In this paper the magnetic behaviour of SmFeAsO and SmFeAs(O0.85F0.15) samples is presented and discussed. Molar susceptibility of SmFeAsO exhibits a local peak at T around 140K due to the establishment of a long range antiferromagnetic ordering of the Fe moments in Fe-As layers. This feature has already been observed with different techniques, and frequently ascribed to the onset of a Spin Density Wave (SDW). At TN around 6K another peak, which we attribute to the establishment of antiferromagnetic ordering of Sm ion sublattice, is observed. Furthermore, a temperature independent signal (Pauli paramagnetism, Landau and core diamagnetism...) is also present in the magnetic behaviour of this sample. In SmFeAs(O0.85F0.15) the antiferromagnetic ordering in Fe-As plane is suppressed and superconductivity occurs at T = 52 K, whereas the antiferromagnetic ordering of Sm ions at low temperature persists, leading to the coexistence and competition between superconducting and magnetic orderings. Above the transition temperature, after the subtraction of the Sm ion sublattice paramagnetic contribution and of the temperature independent contribution to the experimental susceptibility data, a Curie-Weiss behaviour for Fe is observed, with a magnetic moment of 1.4 Bohr magneton.
In this paper the magnetic behaviour of undoped and 15% F doped SmFeAsO (Sm-1111) and LaFeAsO (La-1111) samples is presented and discussed. Magnetization measurements are not a simple tool to use for the characterisation of the new family of Fe-based superconductors because magnetic impurities can be easily formed during the preparation procedure and may affect the magnetic signal. In spite of this problem bulk magnetization measurements, properly treated, may give very useful information. In the undoped samples we gathered the main aspects of the physical behavior of the 1111 phase, i.e. the …
High-critical-temperature (Tc) superconductivity at 48 K is reported for hydrogen-doped SmFeAsO epitaxial films on MgO single-crystal substrates. The key processes are pulsed laser deposition to grow undoped SmFeAsO epitaxial films and subsequent topotactic chemical reaction using CaH2 powders under evacuated silica-glass ampule atmosphere. Based on this post-deposition thermal annealing treatment that we have developed, a maximum hydrogen concentration x = ~0.35 was realized in SmFeAs(O1-xHx). Disordered hydrogen-substitution at O sites is experimentally confirmed directly by atomic-scale mic…
We report the iron (Fe) isotope effect on the transition temperature (Tc) in the oxygen-deficient SmFeAsO_{1-y}, a 50 K-class Fe-based superconductor. For the optimally-doped samples with Tc = 54 K, change of the Fe average atomic mass (MFe) causes a negligibly small shift in Tc, with the Fe isotope coefficient (alphaFe) as small as -0.024 \pm 0.015. This result contrasts with the finite, inverse isotope shift observed in optimally-doped (Ba,K)Fe2As2, indicating that the contribution of the electron-phonon interaction markedly differs between these two Fe-based high-Tc superconductors.
Here we report the synthesis and basic characterization of SmFe1-xCoxAsO (x=0.10, 0.15). The parent compound SmFeAsO itself is not superconducting but shows an antiferromagnetic order near 150 K, which must be suppressed by doping before superconductivity emerges. With Co-doping in the FeAs planes, antiferromagnetic order is destroyed and superconductivity occurs at 15 K. Similar to LaFe1-xCoxAsO, the SmFe1-xCoxAsO system appears to tolerate considerable disorder in the FeAs planes. This result is important, which indicates difference between cuprare superconductors and the iron-based arsenide…
We report the resistivity of a series of fluorine-doped SmFeAsO1-xFx polycrystalline superconductors in magnetic fields up to 60T. For underdoped samples (x < 0.15), the low temperature resistive state is characterized by pronounced magneto-resistance and a resistive upturn at low temperatures. The "insulating behavior" is characterized by a log-T divergence observed over a decade in temperature. In contrast, the normal state for samples with doping x > 0.15 display metallic behavior with little magnetoresistance, where intense magnetic fields broaden the superconducting transition rather than…
We report the analysis of pseudogap Delta* derived from resistivity experiments in FeAs-based superconductor SmFeAsO(0.85), having a critical temperature T_c = 55 K. Rather specific dependence Delta*(T) with two representative temperatures followed by a minimum at about 120 K was observed. Below T_s = 147 K, corresponding to the structural transition in SmFeAsO, Delta*(T) decreases linearly down to the temperature T_AFM = 133 K. This last peculiarity can likely be attributed to the antiferromagnetic (AFM) ordering of Fe spins. It is believed that the found behavior can be explained in terms of…
We investigate the quasiparticle relaxation and low-energy electronic structure in undoped SmFeAsO and near-optimally doped SmFeAsO_{0.8}F_{0.2} single crystals - exhibiting spin-density wave (SDW) ordering and superconductivity respectively - using pump-probe femtosecond spectroscopy. In the undoped single crystals a single relaxation process is observed, showing a remarkable critical slowing down of the QP relaxation dynamics at the SDW transition temperature T_{SDW}\simeq125{K}. In the superconducting (SC) crystals multiple relaxation processes are present, with distinct SC state quasiparti…
Ac susceptibility and static magnetization measurements were performed in the optimally doped SmFeAsO$_{0.8}$F$_{0.2}$ superconductor. The field - temperature phase diagram of the superconducting state was drawn and, in particular, the features of the flux line lattice derived. The dependence of the intra-grain depinning energy on the magnetic field intensity was derived in the thermally-activated flux creep framework, enlightening a typical 1/H dependence in the high-field regime. The intra-grain critical current density was extrapolated in the zero temperature and zero magnetic field limit, …
We demonstrate the fabrication of superconducting SmFeAsO1-xFx (Sm-1111) wires by using the ex-situ powder-in-tube technique. Sm-1111 powder and a binder composed of SmF3, samarium arsenide, and iron arsenide were used to synthesize the superconducting core. Although the F content of Sm-1111 is reduced in the process of ex-situ fabrication, the binder compensates by sufficiently supplementing the F content, thereby preventing a decrease in the superconducting transition temperature and a shrinkage of the superconducting volume fraction. Thus, in the superconducting Sm-1111 wire with the binder…
Low temperature specific heat (SH) was measured on the FeAs-based superconducting single crystals Ba$_{0.6}$K$_{0.4}$Fe$_2$As$_2$ and high pressure synthesized polycrystalline samples SmFeAsO$_{0.9}$F$_{0.1}$. It is found that the sharp SH anomaly $ΔC/T|_{T_c}$ in Ba$_{0.6}$K$_{0.4}$Fe$_2$As$_2$ reaches an unexpected high value of 98 mJ/mol K$^2$, about one order of magnitude larger than that of SmFeAsO$_{0.9}$F$_{0.1}$ ($6\sim8$ mJ/mol K$^2$) samples, suggesting very high normal state quasiparticle density of states in FeAs-122 than in FeAs-1111. Furthermore, we found that the electronic SH c…
We studied the effects of isoelectronic Ru substitution at the Fe site on the energy gaps of optimally F-doped SmFeAsO by means of point-contact Andreev reflection spectroscopy. The results show that the SmFe_{1-x}Ru_{x}AsO_{0.85}F_{0.15} system keeps a multigap character at least up to x=0.50, and that the gap amplitudes Delta_1 and Delta_2 scale almost linearly with the local critical temperature TcA. The gap ratios 2Delta_i/(kB Tc) remain approximately constant only as long as Tc > 30 K, but increase dramatically when Tc decreases further. This trend seems to be common to many Fe-based supe…
The magnetic field dependence of the in-plane magnetic penetration depth for optimally doped SmFeAsO_(1-x)F_y was investigated by combining torque magnetometry, SQUID magnetometry, and muon-spin rotation. The results obtained from these techniques show all a pronounced decrease of the superfluid density as the field is increased up to 1.4 T. This behavior is analysed within a two-band model with self-consistently derived coupled gaps, where the superfluid density related to the larger gap is field independent and the superfluid density related to the smaller gap is strongly suppressed with inc…
We measure magnetotransport of F doped SmFeAsO samples up to 28T and we extract the upper critical fields, using different criteria. In order to circumvent the problem of criterion-dependence Hc2 values, we suggest a thermodynamic estimation of the upper critical field slope dHc2/dT based on the analysis of conductivity fluctuations in the critical regime. A high field slope as large as -12T/K is thus extracted for the optimally doped sample. We find evidence of a two-dimensional lowest Landau level (LLL) scaling for applied fields larger than mu_0H_LLL=8T. Finally, we estimate the coherence l…
We report the analysis of fluctuation conductivity (FLC) and pseudogap (D*) in Fe-based superconductor SmFeAsO0.85 with Tc = 55 K derived from resistivity experiments. In the FLC analysis distinct 2D-3D (MT-AL) crossover typical for cuprates but followed by enhanced MT fluctuation contribution was found. Using the crossover temperature To coherence length along c-axis Xc(0) was determined. Rather specific D*(T) dependence with two representative temperatures followed by minimum at about 125 K was observed. Below Ts = 147 K, corresponding to SDW ordering, D*(T) decreases linearly down to TAF = …
In the iron-based high-Tc bulk superconductors, Tc above 50K was only observed in the electron-doped 1111-type compounds. Here we revisit the electron-doped SmFeAsO polycrystals to make a further investigation for the highest T-c in these materials. To introduce more electron carriers and less crystal lattice distortions, we study the Th and F codoping effects into the Sm-O layers with heavy electron doping. Dozens of Sm1-x Th-x FeAsO1-y F-y samples are synthesized through the solid state reaction method, and these samples are carefully characterized by the structural, resistive, and magnetic …
We investigated the temperature dependence of the upper critical field [$H_{c2}(T)$] of fluorine-free SmFeAsO$_{0.85}$ and fluorine-doped SmFeAsO$_{0.8}$F$_{0.2}$ single crystals by measuring the resistive transition in low static magnetic fields and in pulsed fields up to 60 T. Both crystals show that $H_{c2}(T)$'s along the c axis [$H_{c2}^c(T)$] and in an $ab$-planar direction [$H_{c2}^{ab}(T)$] exhibit a linear and a sublinear increase, respectively, with decreasing temperature below the superconducting transition. $H_{c2}(T)$'s in both directions deviate from the conventional one-gap Wert…
Correlation between structural/microstructural and magneto-thermal transport properties of FeAs-based SmFeAsO and SmFeAsO0.85F0.15 has been studied in detail. The Rietveld analysis of room temperature powder X-ray diffraction (XRD) data reveals that both the samples are single phase, with very small amount of rare earth impurity in the F doped compound. Electron microscopic investigations show that compounds have layered morphology and structure, with the individual grains being surrounded by amorphous layers. The average grain boundary thickness is ~5 nm. The F free material is found to be ma…
EXAFS studies at the As K edge as a function of temperature have been carried out in SmFeAsO$_{1-x}$F$_x$ ($x$ = 0 and 0.2) compounds to understand the role of local structural distortions superconductivity observed in F doped compound. A significant correlation between thermal variation of local structural parameters like anion height and superconducting onset is found in the fluorinated compound. Such a variation in anion height is absent in non-superconducting compound. Increase in Fe-As bond distance just below superconducting onset temperature indicates a similarity in distortions observe…
The mechanism of superconductivity in pnictides is discussed through direct doping in superconducting FeAs and also in charge reservoir REO layers. The un-doped SmFeAsO is charge neutral SDW (Spin Density Wave) compound with magnetic ordering below 150 K. The Superconducting FeAs layers are doped with Co and Ni at Fe site, whereas REO layers are doped with F at O site. The electron doping in SmFeAsO through Co results in superconductivity with transition temperature (Tc) maximum up to 15 K, whereas F doping results in Tc upto 47 K in SmFeAsO. All these REFe/Co/NiAsO/F compounds are iso-structu…
Hydrostatic pressure Raman measurements have been carried out on the SmFeAsO series of oxypnictides with varying amount of doping (F substitution for O and Co for Fe) and transition temperature (T_{c}), in order to investigate lattice modifications and their connection to doping and superconductivity. Synchrotron XRD data on some of these compounds indicated that at low doping the lattice constants vary smoothly with pressure, but with increasing F concentration there is a deviation from the normal equation of state and these effects are related with modifications in the superconducting FeAs4 …
Diamond anvil cell using boron-doped metallic diamond electrodes covered with undoped diamond insulating layer have been developed for electrical transport measurements under high pressure. These designed diamonds were grown on a bottom diamond anvil via a nanofabrication process combining microwave plasma-assisted chemical vapor deposition and electron beam lithography. The resistance measurements of high quality FeSe superconducting single crystal under high pressure were successfully demonstrated by just putting the sample and gasket on the bottom diamond anvil directly. The superconducting…
We performed electron energy-loss spectroscopy studies in transmission in order to obtain insight into the electronic properties of potassium intercalated coronene, a recently discovered superconductor with a rather high transition temperature of about 15\,K. A comparison of the loss function of undoped and potassium intercalated coronene shows the appearance of several new peaks in the optical gap upon potassium addition. Furthermore, our core level excitation data clearly signal filling of the conduction bands with electrons.
We have investigated the evolution of the low temperature specific heat anomaly (TN=5.4K in zero field) in polycrystalline SmFeAsO samples with magnetic fields up to 35T. The anomaly remains very sharp up to 16T and becomes rounded with little shift in temperature at higher fields. Doped (superconducting) SmFeAsO0.85F0.15 sample shows a similar behavior up to 16T. The initial slope of the critical field dBc/dT is 160T/K for undoped SmFeAsO and 70T/K for doped SmFeAsO0.85F0.15, with Bc(T) defined at the peak of the specific heat anomaly. The insensitivity to the application of an external magne…
We present a study concerning the partial substitution of yttrium at the lanthanum site of the undoped LaFeAsO and superconducting LaFeAsO0.85F0.15 compounds. We prepared samples with a nominal yttrium content up to 70% producing simultaneous shrinkage of both the a- and c-lattice parameters by 1.8% and 1.7%, respectively. The chemical pressure provided by the partial substitution with this smaller ion size causes a lowering of the spin density wave temperature in the undoped compounds, as well as an increase of the superconducting transition temperatures in the doped ones. The 15% fluorine-do…
We report measurements of resistivity, magnetoresistivity, Hall effect, Seebeck coefficient, infrared reflectivity of undoped SmFeAsO and lightly doped SmFeAs(O0.93F0.07) oxypnictides. All the properties measured on SmFeAsO are characterized by clear signatures of the magnetic instability. A self-consistent picture emerges in which below the magnetic transition carrier condensation occurs due to the opening of spin density wave (SDW) gap. This is accompanied by the mobility increase of not gapped carriers due to the suppression of electron-electron scattering. SmFeAs(O0.93F0.07) exhibits an in…
We report the Hall resistivity, $ρ_{xy}$ of polycrystalline SmFeAsO$_{1-x}$F$_{x}$ for four different fluorine concentrations from the onset of superconductivity through the collapse of the structural phase transition. For the two more highly-doped samples, $ρ_{xy}$ is linear in magnetic field up to 50 T with only weak temperature dependence, reminiscent of a simple Fermi liquid. For the lightly-doped samples with $x<0.15$, we find a low temperature regime characterized $ρ_{xy}(H)$ being both non-linear in magnetic field and strongly temperature dependent even though the Hall angle is small. T…
The fluorine-doped rare-earth iron oxypnictide series SmFeAsO$_{1-x}$F$_x$ (0 $\leq x \leq$ 0.10) was investigated with high resolution powder x-ray scattering. In agreement with previous studies, the parent compound SmFeAsO exhibits a tetragonal-to-orthorhombic structural distortion at T$\rm{_{S}}$~=~130~K which is rapidly suppressed by $x \simeq$ 0.10 deep within the superconducting dome. The change in unit cell symmetry is followed by a previously unreported magnetoelastic distortion at 120~K. The temperature dependence of the thermal expansion coefficient $α_{V}$ reveals a rich phase diagr…
We measured phonon frequencies and linewidths in doped and undoped BaFe2As2 single crystals by inelastic x-ray scattering and compared our results with density functional theory (DFT) calculations. In agreement with previous work, the calculated frequencies of some phonons depended on whether the ground state was magnetic or not and, in the former case, whether phonon wavevector was parallel or perpendicular to the magnetic ordering wavevector. The experimental results agreed better with the magnetic calculation than with zero Fe moment calculations, except the peak splitting expected due to m…
We investigated chemical pressure effects in electron-doped (e-doped) FeSe by fabricating an electric-double-layer structure with single crystalline FeSe films on LaAlO$_3$ with Se substituted by isovalent Te and S. Our method enables transport measurements of e-doped FeSe. Electron doping by applying gate voltage of 5 V increases $T_{\mathrm c}$ of the FeSe$_{1-x}$Te$_x$ and FeSe$_{1-y}$S$_y$ films with $0 \leq x \leq 0.4$ and $0 \leq y \leq 0.25$, while the e-doped $x=0.5$ film showed lower $T_{\mathrm c}$ than that of the undoped one. Both positive and chemical pressure suppress $T_{\mathrm…
A comparative study of thermal properties of SmFeAsO, SmFeAs(O0.93F0.07) and SmFeAs(O0.85F0.15) samples is presented. Specific heat and thermal conductivity show clear evidences of the spin density wave (SDW) ordering below TSDW 135 K in undoped SmFeAsO. At low level of F-doping, SmFeAs(O0.93F0.07), SDW ordering is suppressed and superconducting features are not yet optimally developed in both specific heat and thermal conductivity. At optimal level of F-doping SmFeAs(O0.85F0.15) anomalies related to the superconducting transition are well noticeable. By a compared analysis of doped and undope…
Ac susceptibility and static magnetization measurements were performed in the nearly-optimally doped LaFeAsO$_{0.9}$F$_{0.1}$ and CeFeAsO$_{0.92}$F$_{0.08}$ superconductors, complementing earlier results on SmFeAsO$_{0.8}$F$_{0.2}$ [Phys. Rev. {\bf B 83}, 174514 (2011)]. The magnetic field -- temperature phase diagram of the mixed superconducting state is drawn for the three materials, displaying a sizeable reduction of the liquid phase upon increasing $T_{c}$ in the range of applied fields ($H \leq 5$ T). This result indicates that SmFeAsO$_{0.8}$F$_{0.2}$ is the most interesting compound amo…
We have succeeded in synthesizing electron-doped polycrystalline bulk samples of T'-La1.8Eu0.2CuO4-yFy (y = 0 - 0.15) by the fluorination of undoped (Ce-free) T'-La1.8Eu0.2CuO4 using NH4F. The magnetic susceptibility measurements have revealed that the superconducting transition temperature, Tc, increases with increasing y, exhibits the maximum of 23 K at y = 0.025, and decreases. The dome-like dependence of Tc on the doped carrier concentration in the T'-type (La,Eu)-based cuprates is explained in terms of the pairing mediated by spin fluctuations based on the d-p model calculation [K. Yamaza…
The possibility of superconductivity in doped and undoped triangular antiferromagnets is discussed. Using the Bethe-Salpeter (B-S) equation, it is shown that the exchange of RPA paramagnons on a triangular lattice Hubbard model leads to strong pairing correlations at and near half-filling. The dominant states for this system correspond to d-wave singlet (even-frequency) and s-wave triplet (odd-frequency) pairing. Analytical techniques applied to the hole-doped t-J model yield similar results. A t_1-t_2 Hubbard model interpolating between square (t_1=0) and triangular (t_1=t_2) lattices has a t…
We investigated the superconducting transition and the pinning properties of undoped and Ag-doped FeSe0.94 at magnetic fields up to 14 T. It was established that due to Ag addition the hexagonal phase formation in melted FeSe0.94 samples is suppressed and the grain connectivity is strongly improved. The obtained superconducting zero-field transition becomes sharp (with a transition width below 1 K), Tc and the upper critical field were found to increase, whereas the normal state resistivity significantly reduces becoming comparable with those of FeSe single crystals. In addition, a considerabl…
Tunneling data on MgB_{1.8}C_{0.2} show a reduction in the energy gap of the pi-bands by a factor of two from undoped MgB2 that is consistent with the Tc reduction, but inconsistent with the expectations of the dirty limit. Dirty-limit theory for undoped MgB2 predicts a single gap about three times larger than measured and a reduced Tc comparable to that measured. Our heavily-doped samples exhibit a uniform dispersion of C suggestive of significantly enhanced scattering, and we conclude that the retention of two-band superconductivity in these samples is caused by a selective suppression of in…
In this review article, we show our recent results relating to the undoped (Ce-free) superconductivity in the electron-doped high-Tc cuprates with the so-called T' structure. For an introduction, we briefly mention the characteristics of the electron-doped T'-cuprates, including the reduction annealing, conventional phase diagram and undoped superconductivity. Then, our transport and magnetic results and results relating to the superconducting pairing symmetry of the undoped and underdoped T'-cuprates are shown. Collaborating spectroscopic and nuclear magnetic resonance results are also shown …
A review of high-pressure studies on Fe-pnictide superconductors is given. The pressure effects on the magnetic and superconducting transitions are discussed for different classes of doped and undoped FeAs-compounds, ROFeAs (R = rare earth), AeFe2As2 (Ae = Ca, Sr, Ba), and AFeAs (A = Li, Na). Pressure tends to decrease the magnetic transition temperature in the undoped or only slightly doped compounds. The superconducting Tc increases with pressure for underdoped FeAs-pnictides, remains approximately constant for optimal doping, and decreases linearly in the overdoped range. The undoped LaOFeA…
In order to realize superconductivity in cuprates with the T'-type structure, not only chemical substitution (Ce doping) but also post-growth reduction annealing is necessary. In the case of thin films, however, well-designed reduction annealing alone without Ce doping can induce superconductivity in the T'-type cuprates. In order to unveil the origin of superconductivity in the Ce-undoped T'-type cuprates, we have performed bulk-sensitive hard x-ray photoemission and soft x-ray absorption spectroscopies on superconducting and non-superconducting Nd$_{2-x}$Ce$_x$CuO$_4$ ($x=$ 0, 0.15, and 0.19…
Resistivity, Hall effect and magnetoresistance have been investigated systematically on single crystals of Ba$_{1-x}$K$_x$Fe$_2$As$_2$ ranging from undoped to optimally doped regions. A systematic evolution of the quasiparticle scattering has been observed. It is found that the resistivity in the normal state of Ba$_{1-x}$K$_x$Fe$_2$As$_2$ is insensitive to the potassium doping concentration, which is very different from the electron doped counterpart Ba(Fe$_{1-x}$Co$_{x}$)$_{2}$As$_{2}$, where the resistivity at 300 K reduces to half value of the undoped one when the system is optimally doped…
The magnetoresistivity and critical current density of well characterized Si-nanoparticle doped and undoped Cu-sheathed MgB$_{2}$ tapes have been measured at temperatures $T\geq 28$ K in magnetic fields $B\leq 0.9$ T. The irreversibility line $B_{irr}(T)$ for doped tape shows a stepwise variation with a kink around 0.3 T. Such $B_{irr}(T)$ variation is typical for high-temperature superconductors with columnar defects (a kink occurs near the matching field $% B_ϕ$) and is very different from a smooth $B_{irr}(T)$ variation in undoped MgB$_{2}$ samples. The microstructure studies of nanoparticl…
Low-temperature synthesis is a promising and potentially effective method for improving superconducting properties. We report on the fabrication of polycrystalline samples of SmFeAsO1-xFx with nominal x content varying in a wide range of x = 0-0.35 synthesized at 900 deg C. This synthesis temperature is around 300 deg C lower than the conventional synthesis temperature. The variation in the lattice parameters and transition temperature (Tc) of various F-doped samples indicates that reduction of the unit cell volume (V) seems to be the main reason for the rise of Tc up to 57.8 K. Magnetoresista…
A series of MgB2 thin films were fabricated by pulsed laser deposition (PLD), doped with various amounts of Si up to a level of 18wt%. Si was introduced into the PLD MgB2 films by sequential ablation of a stoichiometric MgB2 target and a Si target. The doped films were deposited at 250 C and annealed in situ at 685 C for 1min. Up to a Si doping level of ~11wt%, the superconducting transition temperature (Tc) of the film does not change significantly, as compared to the control, undoped film. The magnetic critical current density (Jc) of the film at 5K was increased by 50% for a Si doping level…
High-temperature superconductivity has been discovered in La2-xBaxCuO4 [1], a compound that derives from the undoped La2CuO4 crystallizing in the perovskite T-structure. In this structure oxygen octahedra surround the copper ions. It is common knowledge that charge carriers induced by doping in such an undoped antiferromagnetic Mott-insulator lead to high-temperature superconductivity [2- 4]. The undoped material La2CuO4 is also the basis of the electron-doped cuprate superconductors [5] of the form La2-xCexCuO4+y [6,7] which however crystallize in the so called T-prime-structure, i.e. without…
Superconductivity is found in 50% K-doped EuFe2As2 sample below 33 K. Our results of electrical resistivity, magnetic susceptibility and 57Fe and 151Eu Mossbauer spectroscopy provide clear evidence that the ordering of the Fe moments observed at 190 K in undoped EuFe2As2 is completely suppressed in our 50% K doped sample, thus there is no coexistence between the Fe magnetic order and the superconducting state. However, short range ordering of the Eu moments is coexisting with the superconducting state below 15 K. A bump in the susceptibility well below Tc as well as a slight broadening of the …
We have studied the effect of Iridium doping (Rh$_{17-x}$Ir$_{x}$S$_{15}$) in the Rhodium sites of the strongly correlated superconductor Rh$_{17}$S$_{15}$. Even at low levels of doping (x = 1 and 2) we see a drastic change in the superconducting properties as compared to those of the undoped system. We deduce that there is a reduction in the density of states at the Fermi level from reduced Pauli susceptibility and Sommerfeld coefficient in the doped samples. Moreover, the second magnetization peak in the isothermal magnetization scan (`fishtail') which was very prominent in the magnetization…
The effect of doping with Ti, Ta, SiC in complex with synthesis temperature on the amount and distribution of structural inhomogeneities in MgB2 matrix of high-pressuresynthesized-materials (2 GPa) which can influence pining: higher borides (MgB12) and oxygen-enriched Mg-B-O inclusions, was established and a mechanism of doping effect on jc increase different from the generally accepted was proposed. Near theoretically dense SiC-doped material exhibited jc= 1000000 A/sq. cm in 1T field and Hirr =8.5 T at 20 K. The highest jc in fields above 9, 6, and 4 T at 10, 20, and 25 K, respectively, was …
Performing a leading-order renormalization group analysis, here we compute the effects of generic local or short-range electronic interactions in monolayer and Bernal bilayer graphene. Respectively in these two systems chiral quasiparticles display linear and biquadratic band touching, leading to linearly vanishing and constant DOS. Consequently, the former system remains stable for weak enough local interactions, and supports a variety of ordered phases only beyond a critical strength of interactions. By contrast, ordered phases can nucleate for sufficiently weak interactions in bilayer graph…
The recent observation of superconductivity in infinite-layer nickelates has brought intense debate on the established knowledge of unconventional superconductivity based on the cuprates. Despite many similarities, the nickelates differ from the cuprates in many characteristics, the most notable one among which is the magnetism. Instead of a canonical antiferromagnetic Mott insulator as the undoped cuprates, from which the superconductivity is generally believed to arise upon doping, the undoped nickelates show no sign of magnetic ordering in experiments. Through a combined density functional …
We report superconductivity in the SmFe0.9Co0.1AsO system being prepared by most easy and versatile single step solid-state reaction route. The parent compound SmFeAsO is non-superconducting but shows the spin density wave (SDW) like antiferromagnetic ordering at around 140K. To destroy the antiferromagnetic ordering and to induce the superconductivity in the parent system, the Fe2+ is substituted partially by Co3+. Superconductivity appears in SmFe0.9Co0.1AsO system at around 14K. The Co doping suppresses the SDW anomaly in the parent compound and induces the superconductivity. Magnetization …
We have successfully synthesized one member of LnFeAsO (Ln stands for lanthanides) with Ln=Tb. By partial substitution of Tb$^{3+}$ by Th$^{4+}$, superconductivity with onset $T_{c}$ up to 52 K was observed. In the undoped parent compound, the magnetic moments of Tb$^{3+}$ ions order antiferromagnetically (AFM) at $T_N$ of 2.5 K, and there exists an anomaly in the resistivity at $T^*$ of about 124 K which corresponds to the structural phase transition and/or AFM ordering of magnetic moments of Fe$^{2+}$ ions. This anomaly is severely suppressed by Th doping, similar to the cases of F doped LnF…
Using the Density Matrix Renormalization Group and two-leg ladders, we investigate an electronic two-orbital Hubbard model including plaquette diagonal hopping amplitudes. Our goal is to search for regimes where charges added to the undoped state form pairs, presumably a precursor of a superconducting state.For the electronic density $ρ=2$, i.e. the undoped limit, our investigations show a robust $(π,0)$ antiferromagnetic ground state, as in previous investigations. Doping away from $ρ=2$ and for large values of the Hund coupling $J$, a ferromagnetic region is found to be stable. Moreover, whe…
MoSi2 doped MgB2 tapes with different doping levels were prepared through the in-situ powder-in-tube method using Fe as the sheath material. Effect of MoSi2 doping on the MgB2/Fe tapes was investigated. It is found that the highest JC value was achieved in the 2.5 at.% doped samples, more than a factor of 4 higher compared to the undoped tapes at 4.2 K, 10 T, then further increasing the doping ratio caused a reduction of JC. Moreover, all doped tapes exhibited improved magnetic field dependence of Jc. The enhancement of JC-B properties in MoSi2 doped MgB2 tapes is attributed to good grain link…
We report heat capacity measurements of the pnictide materials SmFeAsO$_{1-x}$F$_x$, NdFeAsO, LaFeAsO$_{1-x}$F$_x$ and LiFeAs. For SmFeAsO$_{1-x}$F$_x$, with x close to 0.1, we use 3 He measurements to demonstrate a transfer of entropy from the peak at TN to a previously unidentified ~2 K feature which grows with increasing doping. Our results on the Sm samples are compared with a similarly doped La sample to elucidate the crystal field levels of the Sm3+ ion at 0, 23, and 56 meV which lead to a Schottky-like anomaly, and also show that there is a significant increase in the Sommerfeld coeffic…
The superconducting transition temperature $T_{c}$ of multilayers of electron-doped cuprates, composed of underdoped (or undoped) and overdoped La% $_{2-x}$Ce$_{x}$CuO$_{4}$ (LCCO) and Pr$_{2-x}$Ce$_{x}$CuO$_{4}$ (PCCO) thin films, is found to increase significantly with respect to the $T_{c}$ of the corresponding single-phase films. By investigating the critical current density of superlattices with different doping levels and layer thicknesses, we find that the $T_{c}$ enhancement is caused by a redistribution of charge over an anomalously large distance.
We present first principles calculations of the atomic and electronic structure of electron-doped LaOFeAs. We find that whereas the undoped compound has an antiferromagnetic arrangement of magnetic moments at the Fe atoms, the doped system becomes non magnetic at a critical electron concentration. We have studied the electron-phonon interaction in the doped paramagnetic phase. For the $A_{1g}$ phonon, the separation between the As and Fe planes induces a non-collinear arrangement of the Fe magnetic moments. This arrangement is anti parallel for interactions mediated by As, and perpendicular fo…
The electronic structure of the unoccupied and occupied states of potassium (K)-doped and undoped picene crystalline films has been investigated by using the element-selective and bulk-sensitive photon-detection methods of X-ray absorption and emission spectroscopies. We observed the formation of the doping-induced unoccupied and occupied electronic states in K-doped picene. By applying the inner-shell resonant-excitation experiments, we observed the evidence for the orbital hybridization between K and picene near the Fermi energy. Furthermore, the resonant X-ray emission experiment suggests t…