Highly sensitive and fast photodetector devices with CdSe quantum nanowires as active elements have been developed exploiting the advantages of electro- and wet-chemical routes. Bismuth nanoparticles electrochemically synthesized directly onto interdigitating platinum electrodes serve as catalysts in the following solution-liquid-solid synthesis of quantum nanowires directly on immersed substrates under mild conditions at low temperature. This fast and simple preparation process leads to a photodetector device with a film of nanowires of limited thickness bridging the electrode gaps, in which a high fraction of individual nanowires are electrically contacted and can be exposed to light at the same time. The high sensitivity of the photodetector device can be expressed by its on/off-ratio or its photosensitivity of more than 107 over a broad wavelength range up to about 700 nm. The specific detectivity and responsivity are determined to D* = 4*10^13 Jones and R = 0.32 A/W, respectively. The speed of the device reflects itself in a 3 dB frequency above 1 MHz corresponding to rise and fall times below 350 ns. The remarkable combination of a high sensitivity and a fast response is attributed to depletion regions inside the nanowires, tunnel-junction barriers between nanowires, as well as Schottky contacts at the electrodes, where all these features are strongly influenced by the number of photo generated charge carriers.
We report the growth of InAs$_{1-x}$Sb$_{x}$ nanowires ($0\leq x \leq 0.15$) grown by catalyst-free molecular beam epitaxy on silicon (111) substrates. We observed a sharp decrease of stacking fault density in the InAs$_{1-x}$Sb$_{x}$ nanowire crystal structure with increasing antimony content. This decrease leads to a significant increase in the field-effect mobility, this being more than three times greater at room temperature for InAs$_{0.85}$Sb$_{0.15}$ nanowires than InAs nanowires.
The addition of boron to GaAs nanowires grown by self-catalyzed molecular beam epitaxy was found to have a strong effect on the nanowire morphology, with axial growth greatly reduced as the nominal boron concentration was increased. Transmission electron microscopy measurements show that the Ga catalyst droplet was unintentionally consumed during growth. Concurrent radial growth, a rough surface morphology and tapering of nanowires grown under boron flux suggest that this droplet consumption is due to reduced Ga adatom diffusion on the nanowire sidewalls in the presence of boron. Modelling of …
Gallium nitride nanowires were grown on c-plane, r-plane and m-plane sapphire substrates in a showerhead metalorganic chemical vapor deposition system using nickel catalyst with trimethylgallium and ammonia as precursors. We studied the influence of carrier gas, growth temperature, reactor pressure, reactant flow rates and substrate orientation in order to obtain thin nanowires. The nanowires grew along the <10-11> and <10-10> axes depending on the substrate orientation. These nanowires were further characterized using x-ray diffraction, electron microscopy, photoluminescence and Raman spectro…
Incorporation of Bi into GaAs-(Ga,Al)As-Ga(As,Bi) core-shell nanowires grown by molecular beam epitaxy is studied with transmission electron microscopy. Nanowires are grown on GaAs(111)B substrates with Au-droplet assisted mode. Bi-doped shells are grown at low temperature (300 °C) with a close to stoichiometric Ga/As flux ratio. At low Bi fluxes, the Ga(As,Bi) shells are smooth, with Bi completely incorporated into the shells. Higher Bi fluxes (Bi/As flux ratio ~ 4%) led to partial segregation of Bi as droplets on the nanowires sidewalls, preferentially located at the nanowire segments with w…
Cuprous oxide (Cu2O) nanowires were grown by a simple, catalyst-free thermal oxidation method starting from a copper foil substrate. Wire growth was performed at different conditions by varying oxygen partial pressure and heating temperature, and produced structural defects such as stacking faults and twin structures of grown nanowires were characterized by transmission electron microscopy. A moderate oxygen partial pressure ~5% with a relatively high temperature at 500 oC is found to be an optimal condition for growing high-quality Cu2O nanowires, while either lowering temperature or enhancin…
We have investigated in-situ Si doping of InAs nanowires grown by molecular beam epitaxy from gold seeds. The effectiveness of n-type doping is confirmed by electrical measurements showing an increase of the electron density with the Si flux. We also observe an increase of the electron density along the nanowires from the tip to the base, attributed to the dopant incorporation on the nanowire facets whereas no detectable incorporation occurs through the seed. Furthermore the Si incorporation strongly influences the lateral growth of the nanowires without giving rise to significant tapering, re…
Bottom up nanowires are attractive for realizing semiconductor devices with extreme heterostructures because strain relaxation through the nanowire sidewalls allows the combination of highly lattice mismatched materials without creating dislocations. The resulting nanowires are used to fabricate light emitting diodes (LEDs), lasers, solar cells and sensors. However, expensive single crystalline substrates are commonly used as substrates for nanowire heterostructures as well as for epitaxial devices, which limits the manufacturability of nanowire devices. Here, we demonstrate nanowire LEDs dire…
Doping of III-nitride based compound semiconductor nanowires is still a challenging issue to have a control over the dopant distribution in precise locations of the nanowire optoelectronic devices. Knowledge of the dopant incorporation and its pathways in nanowires for such devices is limited by the growth methods. We report the direct evidence of incorporation pathway for Mg dopants in p-type nonpolar GaN nanowires grown via vapour-liquid-solid (VLS) method in a chemical vapour deposition technique for the first time. Mg incorporation is confirmed using X-ray photoelectron (XPS) and electron …
The present study elucidates the correlation between the structural and optical properties of GaN nanowires grown on Si(111) substrate by plasma assisted molecular beam epitaxy (PA-MBE) technique under various growth conditions. GaN NWs exhibiting different shapes, sizes and distribution were grown at various substrate temperatures with same Ga-N (III-V) ratio of 0.4. We observe that sample grown at lower substrate temperature (~700 degC) results 2-dimensional island like structure with almost very little (~30%) circularity while increasing substrate temperature (>770 degC) leads to growth of …
Optically active gold-catalyzed ZnTe nanowires have been grown by molecular beam epitaxy, on a ZnTe(111) buffer layer, at low temperature 350\degree under Te rich conditions, and at ultra-low density (from 1 to 5 nanowires per micrometer^{2}. The crystalline structure is zinc blende as identified by transmission electron microscopy. All nanowires are tapered and the majority of them are <111> oriented. Low temperature micro-photoluminescence and cathodoluminescence experiments have been performed on single nanowires. We observe a narrow emission line with a blue-shift of 2 or 3 meV with respec…
SnTe topological crystalline insulator nanowires have been grown by molecular beam epitaxy on graphene/SiC substrates. The nanowires have cubic rock-salt structure, they grow along [001] crystallographic direction and have four sidewalls consisting of {100} crystal planes known to host metallic surface states with Dirac dispersion. Thorough high resolution transmission electron microscopy investigations show that the nanowires grow on graphene in the van der Walls epitaxy mode induced when the catalyzing Au nanoparticle mixes with Sn delivered from SnTe flux, providing liquid Au-Sn alloy. The …
The synthesis, morphology and magneto-transport properties of nanostructure-engineered charge-ordered Pr0.5Ca0.5MnO3 grown on ZnO nanowires are reported. The stability of the charge-ordering can be tuned, but more interestingly the sign of the magnetoresistance is inverted at low temperatures. Coexistence of ferromagnetic clusters on the surface and antiferromagnetic phase in the core of the grains were considered in order to understand these features. This work suggests that such a process of growing on nanowires network can be readily extended to other transition metal oxides and open doors …
Mn-doped GaAs nanowires were grown in the self-catalytic growth mode on oxidized Si(100) surface by molecular beam epitaxy and characterized by scanning and transmission electron microscopy, Raman scattering, photoluminescence, cathodoluminescence, and electron transport measurements. The transmission electron microscopy studies evidenced the substantial accumulation of Mn inside the catalyzing Ga droplets at the top of the nanowires. Optical and transport measurements revealed that the limit of Mn content for self-catalysed growth of GaAs nanowires corresponds to the doping level, i.e., is mu…
Moire based strain analysis in wurtzite GaAs -- rock-salt (Pb,Sn)Te core-shell nanowires grown by molecular beam epitaxy
Institute of Physics, Polish Academy of Sciences（波兰科学院物理研究所）；Faculty of Physics, University of Warsaw（华沙大学物理学院）；Ensemble3 Centre of Excellence（Ensemble3卓越中心）；International Research Center MagTop, Institute of Physics, Polish Academy of Sciences（波兰科学院物理研究所国际研究中心MagTop）
We analyse the morphological, structural and luminescence properties of self-assembled ZnO nanowires grown by chemical vapour transport on Si(001). The examination of nanowire ensembles by scanning electron microscopy reveals that a non-negligible fraction of nanowires merge together forming coalesced aggregates during growth. We show that the coalescence degree can be unambiguously quantified by a statistical analysis of the cross-sectional shape of the nanowires. The examination of the structural properties by X-ray diffraction evidences that the nanowires crystallize in the wurtzite phase, …
We demonstrate a new method to measure absorption coefficients in any family of nanowires, provided they are grown on a substrate having considerable difference in permittivity with the nanowire-air matrix. In the case of high crystal quality, strain-free GaN nanowires, grown on Si (111) substrates with a density of ~1010 cm-2, the extracted absorption coefficients do not exhibit any enhancement compared to bulk GaN values, unlike relevant claims in the literature. This may be attributed to the relatively small diameters, short heights, and high densities of our nanowire arrays.
Structural and magnetic properties of (In,Ga)As-(Ga,Mn)As core-shell nanowires grown by molecular beam epitaxy on GaAs(111)B substrate with gold catalyst have been investigated.(In,Ga)As core nanowires were grown at high temperature (500 °C) whereas (Ga,Mn)As shells were deposited on the {1-100} side facets of the cores at much lower temperature (220 °C). High resolution transmission electron microscopy images and high spectral resolution Raman scattering data show that both the cores and the shells of the nanowires have wurtzite crystalline structure. Scanning and transmission electron micros…
Growth of GaN nanowires are carried out via metal initiated vapor-liquid-solid mechanism, with Au as the catalyst. In chemical vapour deposition technique, GaN nanowires are usually grown at high temperatures in the range of 900-1100 ^oC because of low vapor pressure of Ga below 900 ^oC. In the present study, we have grown the GaN nanowires at a temperature, as low as 700 ^oC. Role of indium in the reduction of growth temperature is discussed in the ambit of Raoult's law. Indium is used to increase the vapor pressure of the Ga sufficiently to evaporate even at low temperature initiating the gr…
Selective area growth (SAG) of nanowires and networks promise a route toward scalable electronics, photonics and quantum devices based on III-V semiconductor materials. The potential of high-mobility SAG nanowires however is not yet fully realized, since interfacial roughness, misfit dislocations at the nanowire/substrate interface and non-uniform composition due to material intermixing all scatter electrons. Here, we explore SAG of highly lattice-mismatched InAs nanowires on insulating GaAs(001) substrates and address these key challenges. Atomically smooth nanowire/substrate interfaces are a…
Nanogenerators based on piezoelectric materials convert ever-present mechanical vibrations into electrical power for energetically autonomous wireless and electronic devices. Nanowires of piezoelectric polymers are particularly attractive for harvesting mechanical energy in this way, as they are flexible, lightweight and sensitive to small vibrations. Previous studies have focused exclusively on nanowires grown by electrospinning, but this involves complex equipment, and high voltages of $\approx$ 10 kV that electrically pole the nanowires and thus render them piezoelectric. Here we demonstrat…
Hexagonal group IV materials like silicon and germanium are expected to display remarkable optoelectronic properties for future development of photonic technologies. However, the fabrication of hexagonal group IV semiconductors within the vapour-liquid-solid method has been obtained using gold as a catalyst thus far. In this letter, we show the synthesis of hexagonal Ge on self-assisted GaAs nanowires using molecular beam epitaxy. With an accurate tuning of the Ga and As molecular beam flux we selected the crystal phase, cubic or hexagonal, of the GaAs NWs during the growth. A 500 nm-long hexa…
We realize growth of self-catalyzed core-shell GaAs/GaAsP nanowires (NWs) on Si substrates using molecular-beam epitaxy. Transmission electron microscopy (TEM) of single GaAs/GaAsP NWs confirms their high crystal quality and shows domination of the zinc-blende phase. This is further confirmed in optics of single NWs, studied using cw and time-resolved photoluminescence (PL). A detailed comparison with uncapped GaAs NWs emphasizes the effect of the GaAsP capping in suppressing the non-radiative surface states: significant PL enhancement in the core-shell structures exceeding 2000 times at 10K i…
Direct evidence of enhanced Ga interdiffusion in InAs vertically aligned free-standing nanowires
我们提出了直接的证据，增强Ga相互扩散的InAs独立的纳米线生长在中等温度下的分子束外延GaAs（111）B。扫描电子显微镜以及共面和掠入射几何形状的X射线衍射测量表明，名义上生长的InAs纳米线实际上是由In $_{0.86}$ Ga $_{0.14}$ As制成的。与典型的气-液-固生长不同，这些纳米线是通过扩散诱导生长结合来自衬底材料的强相互扩散形成的。基于实验结果，一个简单的纳米线生长模型占镓互扩散。该生长模型可普遍应用于III-V族纳米线的分子束异质外延。
GaN nanowires grown by molecular beam epitaxy generally suffer from dominant nonradiative recombination, which is believed to originate from point defects. To suppress the formation of these defects, we explore the synthesis of GaN nanowires at temperatures up to 915 $°C$ enabled by the use of thermally stable TiN$_x$/Al$_2$O$_3$ substrates. These samples exhibit indeed bound exciton decay times approaching those measured for state-of-the-art bulk GaN. However, the decay time is not correlated with the growth temperature, but rather with the nanowire diameter. The inverse dependence of the dec…
We report a detailed magnetic study of a new type of self-organized nanowires disclosed briefly previously [B. Borca et al., Appl. Phys. Lett. 90, 142507 (2007)]. The templates, prepared on sapphire wafers in a kinetically-limited regime, consist of uniaxially-grooved W(110) surfaces, with a lateral period here tuned to 15nm. Fe deposition leads to the formation of (110) 7 nm-wide wires located at the bottom of the grooves. The effect of capping layers (Mo, Pd, Au, Al) and underlayers (Mo, W) on the magnetic anisotropy of the wires was studied. Significant discrepancies with figures known for …
The accurate control of the crystal phase in III-V semiconductor nanowires (NWs) is an important milestone for device applications. In this work, we present a method to select and maintain the wurtzite (WZ) crystal phase in self-assisted NWs. By choosing a specific regime where the NW growth process is a self-regulated system, the main experimental parameter to select the zinc-blende (ZB) or WZ phase is the V/III flux ratio. The latter can be monitored by changing the As flux, and drives the system toward a stationary regime when the wetting angle of the Ga droplet falls in a target interval, …
N-type doping of GaAs nanowires has proven to be difficult because the amphoteric character of silicon impurities is enhanced by the nanowire growth mechanism and growth conditions. The controllable growth of n-type GaAs nanowires with carrier density as high as 1020 electron/cm3 by self-assisted molecular beam epitaxy using Te donors is demonstrated here. Carrier density and electron mobility of highly doped nanowires are extracted through a combination of transport measurement and Kelvin probe force microscopy analysis in single-wire field-effect devices. Low-temperature photoluminescence is…
InAs nanowires were grown on GaAs substrates by the Au-assisted vapour-liquid-solid (VLS) method in a gas source molecular beam epitaxy (GS-MBE) system. Passivation of the InAs nanowires using InP shells proved difficult due to the tendency for the formation of axial rather than core-shell structures. To circumvent this issue, Al$_x$In$_{1-x}$As or Al$_x$In$_{1-x}$P shells with nominal Al composition fraction of x = 0.20, 0.36, or 0.53 were grown by direct vapour-solid deposition on the sidewalls of the InAs nanowires. Characterization by transmission electron microscopy revealed that the addi…
A method of growing mushroom or shell like nanostructured metal convex concave models has been worked out. Silver,copper,nickel,rhodium and Pd-Ni,Pd-Co alloy structures are reproduced as a result of self-assembly of nanowires growing on porous membranes in the course of pulse current electrodeposition. It is shown that the method allows to model not only the shell shape but also the hierarchical structure at the nano, micro and mesolevels. A 1,2 mm sized shell was grown from Pd-Ni alloy. The architecture of the models was studied by fragmentation and chemical etching. The images were obtained …
Significant enhancement of hole mobility in [110] silicon nanowires compared to electrons and bulk silicon
利用sp 3d 5s * 紧束缚能带结构和电子和空穴的波函数，我们证明了在[110]生长的硅纳米线（SiNWs）中声学声子限制的空穴迁移率大于电子迁移率。所考虑的SiNW的室温声学限制的空穴迁移率可以高达2500 cm 2/Vs，这是几乎三倍大于体声学限制的硅空穴迁移率。结果还表明，[110]生长的硅纳米线的电子和空穴迁移率超过了类似直径的[100]硅纳米线，空穴迁移率相差近两个数量级。由于小直径的硅纳米线主要沿[110]方向生长，结果强烈表明这些硅纳米线可能在未来的电子学中有用。我们的研究结果也与最近的实验测量硅纳米线的流动性。
Manipulation of surface architecture of semiconducting nanowires with a control in surface polarity is one of the important objectives for nanowire based electronic and optoelectronic devices for commercialization. We report the growth of exceptionally high structural and optical quality nonpolar GaN nanowires with controlled and uniform surface morphology and size distribution, for large scale production. The role of O contamination (~1-10^5 ppm) in the surface architecture of these nanowires is investigated with the possible mechanism involved. Nonpolar GaN nanowires grown in O rich conditio…
We report on the direct correlation between the structural and optical properties of single, as-grown core-multi-shell GaAs/In$_{0.15}$Ga$_{0.85}$As/GaAs/AlAs/GaAs nanowires. Fabricated by molecular beam epitaxy on a pre-patterned Si(111) substrate, on a row of well separated nucleation sites, it was possible to access individual nanowires in the as-grown geometry. The polytype distribution along the growth axis of the nanowires was revealed by synchrotron-based nanoprobe X-ray diffraction techniques monitoring the axial 111 Bragg reflection. For the same nanowires, the spatially-resolved emis…
Device applications involving topological insulators (TIs) will require the development of scalable methods for fabricating TI samples with sub-micron dimensions, high quality surfaces, and controlled compositions. Here we use Bi-, Se-, and Te-bearing metalorganic precursors to synthesize TIs in the form of nanowires. Single crystal nanowires can be grown with compositions ranging from Bi2Se3 to Bi2Te3, including the ternary compound Bi2Te2Se. These high quality nanostructured TI compounds are suitable platforms for on-going searches for Majorana Fermions.
We develop an InAs nanowire gate-all-around field-effect transistor using a transparent conductive zinc oxide (ZnO) gate electrode, which is in-situ atomic layer deposited after growth of gate insulator of Al2O3. We perform magneto-transport measurements and find a crossover from weak localization to weak antilocalization effect with increasing gate voltage, which demonstrates that the Rashba spin-orbit coupling is tuned by the gate electrode. The efficiency of the gate tuning of the spin-orbit interaction is higher than those obtained for two-dimensional electron gas, and as high as that for …
The incorporation paths of Be in GaAs nanowires grown by the Ga-assisted method in molecular beam epitaxy has been investigated by electrical measurements of nanowires with different doping profiles. We find that Be atoms incorporate preferentially via the nanowire side facets, while the incorporation path through the Ga droplet is negligible. We also demonstrate that Be can diffuse into the volume of the nanowire giving an alternative incorporation path. This work is an important step towards controlled doping of nanowires and will serve as a help for designing future devices based on nanowir…
We report in-situ synthesis of crystalline indium islands on InAs nanowires grown by molecular beam epitaxy. Structural analysis by transmission electron microscopy showed that In crystals grew in a tetragonal body-centred crystal structure within two families of orientations relative to wurtzite InAs. The crystalline islands had lengths < 500 nm and low-energy surfaces, suggesting that growth was driven mainly by surface energy minimization. Electrical transport through In/InAs devices exhibited Cooper pair charging, evidencing charge parity preservation and a pristine In/InAs interface, with…
(Ga,Mn)As in wurtzite crystal structure, is coherently grown by molecular beam epitaxy on the {1100} side facets of wurtizte (Ga,In)As nanowires and further encapsulated by (Ga,Al)As and low temperature GaAs. For the first time a true long-range ferromagnetic magnetic order is observed in non-planar (Ga,Mn)As, which is attributed to a more effective hole confinement in the shell containing Mn by a proper selection/choice of both the core and outer shell materials.
High angle annular dark field scanning transmission electron microscopy is used to analyze the polarity of ZnSe nanowires grown, by molecular beam epitaxy, on GaAs substrates. The experimental results are compared to simulated images in order to verify possible experimental artefacts. In this work we show that for this type of nano-objects, a residual tilt of the specimen below 15 mrad, away from the crystallographic zone axis does not impair the interpretation of the experimental images.
AlN layers with thicknesses between 2 and 14 nm were grown on Si(111) substrates by molecular beam epitaxy. The effect of the AlN layer thickness on the morphology and nucleation time of spontaneously formed GaN nanowires (NWs) was investigated by scanning electron microscopy and line-of-sight quadrupole mass spectrometry, respectively. We observed that the alignment of the NWs grown on these layers improves with increasing layer thickness while their nucleation time decreases. Our results show that 4 nm is the smallest thickness of the AlN layer that allows the growth of well-aligned NWs with…