SmB6 has been predicted and verified as a prototype of topological Kondo insulators (TKIs). Here we report longitudinal magnetoresistance and Hall coefficient measurements on co-sputtered nanocrystalline SmB6 films and try to find possible signatures of their topological properties. The magnetoresistance (MR) at 2 K is positive and linear (LPMR) at low field and becomes negative and quadratic at higher field. While the negative part is known from the reduction of the hybridization gap due to Zeeman splitting, the positive dependence is similar to what has been observed in other topological insulators (TI). We conclude that the LPMR is a characteristic feature of TI and is related to the linear dispersion near the Dirac cone. The Hall resistance shows a sign change around 50 K. It peaks and becomes nonlinear at around 10 K then decreases below 10 K. This indicates that carriers with opposite signs emerge below 50 K. Two films with different geometries (thickness and lateral dimension) show contrasting behavior below and above 50K, which proves the surface origin of the low temperature carriers in these films. The temperature dependence of magnetoresistance and the Hall data indicates that the surface states are likely non-trivial.
We investigate the magnetic and magnetotransport properties of nanostructured Nd0.6Sr0.4MnO3 (NSMO) thin films grown on (100) oriented SrTiO3 (STO) substrates. The thin films fabricated using the pulsed laser deposition technique have been found to possess two distinct surface morphologies: granular and nano rod type. Magnetization measurements have revealed that the films with rod-type morphology exhibit improved in-plane magnetic anisotropy. Magnetotransport studies have revealed that the granular thin films display a characteristic butterfly-shaped low-field magneto-resistive (LFMR) behavio…
We report growth and characterization of epitaxial $α$-Sn thin films grown on CdTe(111)B. Noninvasive techniques verify the film's pseduomorphic growth before fabrication of magnetotransport devices, overcoming ex-situ obstacles on uncapped films for measurement in the Hall bar geometry. We identify a transition to metallic behavior at low temperature with large magnetoresistance, high mobility, and quantum oscillations tentatively suggesting an n-type Dirac semimetallic channel. A parallel p-type dopant channel with high carrier density is seen to dominate at thinner film thicknesses. Careful…
To understand the near-interface magnetism in manganites, uniform, ultra-thin films of La_{0.67}Sr_{0.33}MnO_3 were grown epitaxially on single crystal (001) LaAlO_3 and (110) NdGaO_3 substrates. The temperature and magnetic field dependent film resistance is used to probe the film's structural and magnetic properties. A surface and/or interface related dead-layer is inferred from the thickness dependent resistance and magnetoresistance. The total thickness of the dead layer is estimated to be $\sim 30 Å$ for films on NdGaO_3 and $\sim 50 Å$ for films on LaAlO_3.
We investigated the nature of transport and magnetic properties in SrIr0.5Ru0.5O3, (SIRO) which has characteristics intermediate between a correlated non-Fermi liquid state and an itinerant Fermi liquid state, by growing perovskite thin films on various substrates (SrTiO3 (001), (LaAlO3)0.3(Sr2TaAlO6)0.7 (001) and LaAlO3 (001)). We observed systematic variation of underlying substrate dependent metal-to-insulator transition temperatures at 80 K on SrTiO3, 90 K on (LaAlO3)0.3(Sr2TaAlO6)0.7 and 100 K on LaAlO3) in resistivity. Resistivity in the metallic region follows a T3/2 power law; whereas …
We report the magnetoresistance measurements of a highly oriented La0.55Ho0.15Sr0.3MnOz film on LaAlO3 substrate. The film has a metal-insulator transition around 200 K and shows pronounced thermomagnetic history effect in its transport properties below 45 K at 7 Tesla. The irreversibility temperature shifts to lower temperatures when the field is reduced. This behaviour is opposite to the thermomagnetic history effect observed in the magnetisation. At 2.8 K one also observes a significant hysteresis in the resistance versus field curve. We propose a qualitative explanation for these observati…
We show that applying strain on half-doped manganites makes it possible to tune the system to the proximity of a metal-insulator transition and thereby generate a colossal magnetoresistance (CMR) response. This phase competition not only allows control of CMR in ferromagnetic metallic manganites but can be used to generate CMR response in otherwise robust insulators at half-doping. Further, from our realistic microscopic model of strain and magnetotransport calculations within the Kubo formalism, we demonstrate a striking result of strain engineering that, under tensile strain, a ferromagnetic…
Polycrystalline La$_{2/3}$Sr$_{1/3}$MnO$_{3}$ (LSMO) thin films were synthesized by pulsed laser ablation on single crystal (100) yttria-stabilized zirconia (YSZ) substrates to investigate the mechanism of magneto-transport in a granular manganite. Different degrees of granularity is achieved by using the deposition temperature (T$_{D}$) of 700 and 800 $^{0}$C. Although no significant change in magnetic order temperature (T$_C$) and saturation magnetization is seen for these two types of films, the temperature and magnetic field dependence of their resistivity ($ρ$(T, H)) is strikingly dissimi…
Magnetotransport properties of La0.7Ca0.3MnO3 thin films deposited on (100) LaAlO3 substrate were investigated. The balance between the charge ordered insulating phase and ferromagnetic metallic phase may account for a number of glassy features such as: significant hysteresis, memory effects and long-time resistivity relaxation. It was found that the resistance of La0.7Ca0.3MnO3 thin film decreases significantly upon applying electric current, in a wide temperature range 10 - 220 K. The magnetotransport properties of the strained thin films are discussed in the context of cross-coupling of cha…
Artificial superlattices designed with ferromagnetic Pr0.85Ca0.15MnO3 insulating layer and ferroelectric Ba0.6Sr0.4TiO3 layer were grown on (100) SrTiO3 substrates. The magnetotransport properties were measured with the current perpendicular to the plane geometry. An increase in magnetoresistance (MR), with no significant low field effect, was observed as the number of ferroelectric Ba0.6Sr0.4TiO3 layer thickness increases even up to 9 unit cells. For example, the superlattice [(Pr0.85Ca0.15MnO3)10(Ba0.6Sr0.4TiO3)9]25 shows 35 % MR at 100 K, though the Pr0.85Ca0.15MnO3 film was a robust insula…
Epitaxial perovskite (110) oriented SrIrO3 (SIO) thin films were grown by pulsed laser deposition on (110) oriented DyScO3 (DSO) substrates with various film thickness t (2 nm < t < 50 nm). All the films were produced with stoichiometric composition, orthorhombic phase, and with high crystallinity. The nearly perfect in-plane lattice matching of DSO with respect to SIO and same symmetry result in a full epitaxial inplane alignment, i.e., the c-axis of DSO and SIO are parallel to each other with only slightly enlarged d110 out-of-plane lattice spacing (+0.38%) due to the small in-plane compress…
We report on the evolution of the average and depth-dependent magnetic order in thin film samples of biaxially stressed and electron-doped EuTiO$_3$ for samples across a doping range $<$0.1 to 7.8 $\times 10^{20}$ cm$^{-3}$. Under an applied in-plane magnetic field, the G-type antiferromagnetic ground state undergoes a continuous spin-flop phase transition into in-plane, field-polarized ferromagnetism. The critical field for ferromagnetism slightly decreases with an increasing number of free carriers, yet the field evolution of the spin-flop transition is qualitatively similar across the dopin…
Highly oriented polycrystalline SSMO thin films deposited on single crystal substrates by ultrasonic nebulized spray pyrolysis have been studied. The film on LAO is under compressive strain while LSAT and STO are under tensile strain. The presence of a metamagnetic state akin to cluster glass formed due to coexisting FM and antiferromagnetic/charge order (AFM/CO) clusters. All the films show colossal magnetoresistance but its temperature and magnetic field dependence are drastically different. In the lower temperature region the magnetic field dependent isothermal resistivity also shows signat…
An important challenge in the field of topological materials is to carefully disentangle the electronic transport contribution of the topological surface states from that of the bulk. For Bi$_2$Te$_3$ topological insulator samples, bulk single crystals and thin films exposed to air during fabrication processes are known to be bulk conducting, with the chemical potential in the bulk conduction band. For Bi$_2$Te$_3$ thin films grown by molecular beam epitaxy, we combine structural characterization (transmission electron microscopy), chemical surface analysis as function of time (x-ray photoelec…
We report a comparative study of the properties of very thin films of La0.67Ca0.33MnO3 grown epitaxially under strain on flat SrTiO3 (STO) and on 1 deg miscut STO. For the films on flat STO the transport properties show well-known behavior, namely values of the metal-insulator transition temperature which are strongly reduced with respect to the bulk value. The reduction in films on miscut STO is significantly less strong than in films on flat STO, even though they appear similar as to strain state. Moreover, the residual resistance at low temperatures is lower than for the case of flat films.…
By pulsed-laser deposition epitaxial thin films of Sr_2FeMoO_6 have been pre- pared on (100) SrTiO_3 substrates. Already for a deposition temperature of 320 C epitaxial growth is achieved. Depending on deposition parameters the films show metallic or semiconducting behavior. At high (low) deposition temperature the Fe,Mo sublattice has a rock-salt (random) structure. The metallic samples have a large negative magnetoresistance which peaks at the Curie temperature. The magnetic moment was determined to 4 mu_B per formula unit (f.u.), in agreement with the expected value for an ideal ferrimagnet…
We study the properties of Dirac fermions on the surface of a topological insulator in the presence of crossed electric and magnetic fields. We provide an exact solution to this problem and demonstrate that, in contrast to their counterparts in graphene, these Dirac fermions allow relative tuning of the orbital and Zeeman effects of an applied magnetic field by a crossed electric field along the surface. We also elaborate and extend our earlier results on normal metal-magnetic film-normal metal (NMN) and normal metal-barrier-magnetic film (NBM) junctions of topological insulators [Phys. Rev. L…
Magnetotransport Properties of Iron-Based Ladder Compounds BaFe2S3 and BaFe2Se3 under High Pressure
Graduate School of Advanced Science and Engineering, Hiroshima University（广岛大学高级科学与工程学院）；International Institute for Sustainability with Knotted Chiral Meta Matter (WPI-SKCM2), Hiroshima University（广岛大学螺旋手性超材料可持续性国际研究所）；Department of Physics, Graduate School of Science, Tohoku University（东北大学理学院物理系）
In this paper, we have studied the effect of strain relaxation on magneto-transport properties of La_0.7Ca_0.3MnO_3 epitaxial films (200 nm thick), which were deposited by pulsed laser deposition technique under identical conditions. All the films are epitaxial and have cubic unit cell. The amount of strain relaxation has been varied by taking three different single crystal substrates of SrTiO_3, LaAlO_3 and MgO. It has been found that for thicker films the strain gets relaxed and produces variable amount of disorder depending on the strength of strain relaxation. The magnitude of lattice rela…
The perovskite manganites of general formula RE_1-xAe_xMnO_3 (RE= rare earth,AE=Ca, Sr, Ba and Pb)have drawn considerable attention, especially following the discovery of colossal magnetoresistance (CMR). They exhibit extraordinary large magnetoresistance pronounced as CMR in the vicinity of insulator-metal/paramagnetic-ferromagnetic transition at a relatively large applied magnetic fields. However, for applied aspectes, occurence of significant CMR at low applied magnetic fields would be required. This review consists of of two sections: In the first section we have extensively reviewed the s…
Pd$_{3}$Bi$_{2}$Se$_{2}$ has been proposed to be topologically non-trivial in nature. However, evidence of its non-trivial behavior is still unexplored. We report the growth and magneto-transport study of Pd$_{3}$Bi$_{2}$Se$_{2}$ thin films, revealing for the first time the contribution of two-dimensional (2D) topological surface states. We observe exceptional non-saturated linear magnetoresistance which results from Dirac fermions inhabiting the lowest Landau level in the quantum limit. The transverse magnetoresistance changes from a semi-classical weak-field $B^{2}$ dependence to a high-fiel…
SSMO50 thin films were deposited by DC magnetron sputtering on LAO and STO substrates. The film on LAO is under compressive strain, while the film on STO is under tensile strain. All the magnetic and magnetotransport properties have been discussed in terms of strain controlled metamagnetic state.
The recent conjecture of a topologically-protected surface state in SmB$_6$ and the verification of robust surface conduction below 4 K have prompted a large effort to understand the surface states. Conventional Hall transport measurements allow current to flow on all surfaces of a topological insulator, so such measurements are influenced by contributions from multiple surfaces of varying transport character. Instead, we study magnetotransport of SmB$_6$ using a Corbino geometry, which can directly measure the conductivity of a single, independent surface. Both (011) and (001) crystal surface…
We have measured the magnetotransport properties of a strained metallic V2O3 thin film. Most of the properties are similar to V2O3 single crystals that have been submitted to a large pressure. In addition, resistance noise analysis indicates that conductivity fluctuations are freezing out at T\approx 10K. Examination of a range of measurements leads to the conclusion that spins-configuration fluctuations dominate in the low temperature regime.
Understanding the role of spin-orbit coupling (SOC) has been crucial to controlling magnetic anisotropy in magnetic multilayer films. It has been shown that electronic structure can be altered via interface SOC by varying the superlattice structure, resulting in spontaneous magnetization perpendicular or parallel to the plane. In lieu of magnetic thin films, we study the similarly anisotropic helimagnet Cr$_{1/3}$NbS$_2$, where the spin polarization direction, controlled by the applied magnetic field, can modify the electronic structure. As a result, the direction of spin polarization can modu…
We report the magnetotransport properties of thin polycrystalline films of the recently discovered non-oxide perovskite superconductor MgCNi3. CNi3 precursor films were deposited onto sapphire substrates and subsequently exposed to Mg vapor at 700 C. We report transition temperatures (Tc) and critical field values (Hc2) of MgCNi3 films ranging in thickness from 7.5 nm to 100 nm. Films thicker than ~40 nm have a Tc ~ 8 K, and an upper critical field Hc2 ~ 14 T, which are both comparable to that of polycrystalline powders. Hall measurements in the normal state give a carrier density, n =-4.2 x 1…
We report the temperature and magnetic field dependence of transport properties in epitaxial films of the manganite La$_{1-x}$Ca$_{x}$MnO$_{3}$ in the overdoped region of the phase diagram for $x > 0.5$, where a charge--ordered (CO) and an antiferromagnetic (AF) phase are present. Resistivity, magnetoresistance and angular dependence of magnetoresistance were measured in the temperature interval $4.2 ~\mathrm{K} < T < 300 ~\mathrm{K}$, for three concentrations $x = 0.52, 0.58$ and $0.75$ and in magnetic fields up to 5 T. The semiconductor/insulator--like behavior in zero field was observed in …
This PhD thesis presents a study of the ferromagnetic semiconductor EuO. Chapter 1 gives a general introduction, chapter 2 presents a calculation of the magneto-optical spectrum. Chapter 3 deals with the epitaxial growth of EuO thin films by MBE. In chapter 4 experiments are used to study the spin-resolved band-structure. Chapter 5 discusses the temperature dependent X-ray absorption spectrum of EuO and chapter 6 studies its magenetic circular dichroism spectrum. Chapter 7 discusses magnetotransport and phototransport measurement and theory on EuO. Chapter 8 deals with the nature of doping in …
We present a study on magnetotransport in films of the topological Dirac semimetal Cd$_{3}$As$_{2}$ doped with Sb grown by molecular beam epitaxy. In our weak antilocalization analysis, we find a significant enhancement of the spin-orbit scattering rate, indicating that Sb doping leads to a strong increase of the pristine band-inversion energy. We discuss possible origins of this large enhancement by comparing Sb-doped Cd$_{3}$As$_{2}$ with other compound semiconductors. Sb-doped Cd$_{3}$As$_{2}$ will be a suitable system for further investigations and functionalization of topological Dirac se…
We compare and contrast the low temperature magnetotransport properties of ultra-thin, insulating, Be films with and without spin-orbit scattering (SOS). Beryllium films have very little intrinsic SOS, but by "dusting" them with sub-monolayer coverages of Au, one can introduce a well controlled SOS rate. Pure Be films with sheet resistance R >R_Q exhibit a low-temperature negative magnetoresistance (MR) that saturates to the quantum resistance R_Q = h/e^2. This high-field quantum metal phase is believed to represent a new ground state of the system. In contrast, the corresponding negative MR i…
We report on the temperature and field dependence of resistance of La0.7Sr0.3MnO3 thin films over a wide temperature range and in pulsed magnetic fields up to 60 T. The epitaxial La0.7Sr0.3MnO3 thin films were deposited by laser molecular beam epitaxy. High magnetic field magnetoresistance curves were fitted by the Brillouin function, which indicated the existence of magnetically polarized regions and the underlying hopping mechanism. The unsaturated magnetoconductance was the most striking finding observed in pulsed magnetic fields up to 60 T. These observations can deepen the fundamental und…
We explore the temperature dependent magnetoresistance of bulk insulating topological insulator thin films. Thin films of Bi2Se2Te and BiSbTeSe1.6 were grown using Pulsed Laser Deposition technique and subjected to transport measurements. Magnetotransport measurements indicate a non-saturating linear magnetoresistance (LMR) behavior at high magnetic field values. We present a careful analysis to explain the origin of LMR taking into consideration all the existing models of LMR. Here we consider that the bulk insulating states and the metallic surface states constitute two parallel conduction c…
Mixed-valence perovskite manganites (Re$_{1-x}$A$_{x}$MnO$_{3}$ where Re=rare earth, A=alkaline earth) provide a unique opportunity to study the relationships between the structure and the magnetotransport properties due to an interplay among charge carriers, magnetic coupling, orbital ordering and structural distortion. This makes these compounds very exciting from both the basic research and from the technological view point. As the technology pursued with these materials requires film growth, extensive studies have been made on materials synthesis, structural and physical characterization a…
Due to the complex interplay of magnetic, structural, electronic, and orbital degrees of freedom, biaxial strain is known to play an essential role in the doped manganites. For coherently strained La(2/3)Ca(1/3)MnO(3) thin films grown on SrTiO(3) substrates, we measured the magnetotransport properties both parallel and perpendicular to the substrate and found an anomaly of the electrical transport properties. Whereas metallic behavior is found within the plane of biaxial strain, for transport perpendicular to this plane an insulating behavior and non-linear current-voltage characteristics (IVC…
SSMO5347 thin films (thicknesses ~200 nm) were deposited by on-axis dc magnetron sputtering on the single crystal LSAT (001) substrates. These films are oriented along the out of plane c-direction. The ferromagnetic and insulator-metal transition occurs at 96 K and 91 K, respectively. The magnetization easy axis is observed to lie in the plane of the film while the magnetic hard axis is found to be along the normal to this. The magnetotransport of the SSMO films, which was measured as a function of angle (theta) between the magnetic field (H) and plane of the film, shows colossal anisotropy. M…
Epitaxial films of heavy fermion CeCu2Ge2 and CeFe2Ge2 are grown on DyScO3 and MgO substrates using molecular beam epitaxy. The growth begins via island nucleation leading to a granular morphology. The grains grow flat with c-axis orientation after nucleating, as indicated by in-situ reflection high energy electron diffraction (RHEED) and ex-situ analysis including atomic force microscopy (AFM) and x-ray diffraction (XRD). These single phase films show similar temperature dependent transport to single crystals of the materials indicating that similar collective order occurs in the films as in …
We report the growth and magneto-transport studies of Pd$_{3}$Bi$_{2}$S$_{2}$ (PBS) thin films synthesized by pulsed laser deposition (PLD) technique. The magneto-transport study on pristine and post annealed films show the presence of more than one type of charge carrier with a carrier concentration in the range $0.6$ - $2.26~\times$ 10$^{21}$ cm$^{-3}$ and mobility in the range 0.96 - 1.73 $\times$ 10$^{2}$ cm$^{2}$/Vs. At low temperatures a logarithmic increase in conductivity is observed which indicates the presence of weak anti-localization (WAL). The magnetotransport data is analysed wit…
The newly discovered topological Dirac semimetals host the possibilities of various topological phase transitions through the control of spin-orbit coupling as well as symmetries and dimensionalities. Here, we report a magnetotransport study of high-mobility (Cd1-xZnx)3As2 films, where the topological Dirac semimetal phase can be turned into a trivial insulator via chemical substitution. By high-field measurements with a Hall-bar geometry, magnetoresistance components ascribed to the chiral charge pumping have been distinguished from other extrinsic effects. The negative magnetoresistance exhi…
Room temperature ferromagnetism was observed in n-type Fe-doped In2O3 thin films deposited on c-cut sapphire substrates by pulsed laser deposition. Structure, magnetism, composition, and transport studies indicated that Fe occupied the In sites of the In2O3 lattice rather than formed any metallic Fe or other magnetic impurity phases. Magnetic moments of films were proved to be intrinsic and showed to have a strong dependence on the carrier densities which depended on the Fe concentration and its valance state as well as oxygen pressure.
The emerging Ni-based superconducting oxide thin films are rather intriguing to the entire condensed matter physics. Here we report some brief experimental results on transport measurements for a 14-nm-thick superconducting Nd0.8Sr0.2NiO2/SrTiO3 thin-film heterostructure with an onset transition temperature of ~9.5 K. Photoluminescence measurements reveal that there is negligible oxygen vacancy creation in the SrTiO3 substrate during thin-film deposition and post chemical reduction for the Nd0.8Sr0.2NiO2/SrTiO3 heterostructure. It was found that the critical current density of the Nd0.8Sr0.2Ni…
Rapid progress of quantum transport study in topological Dirac semimetal, including observations of quantum Hall effect in two-dimensional (2D) Cd$_{\mathrm{3}}$As$_{\mathrm{2}}$ samples, has uncovered even more interesting quantum transport properties in high-quality and three-dimensional (3D) samples. However, such 3D Cd$_{\mathrm{3}}$As$_{\mathrm{2}}$ films with low carrier density and high electron mobility have been hardly obtained. Here we report the growth and characterization of 3D thick Cd$_{\mathrm{3}}$As$_{\mathrm{2}}$ films adopting molecular beam epitaxy. The highest electron mobi…
Artificial confinement of electrons by tailoring the layer thickness has turned out to be a powerful tool to harness control over competing phases in nano-layers of complex oxides. We investigate the effect of dimensionality on transport properties of $d$-electron based heavy-fermion metal CaCu$_{3}$Ru$_{4}$O$_{12}$. Transport behavior evolves from metallic to localized regime upon reducing thickness and a metal insulator transition is observed below 3 nm film thickness for which sheet resistance crosses $h/e^{2} \sim 25~$k$Ω$, the quantum resistance in 2D. Magnetotransport study reveals a str…
A new class of materials termed topological insulators have been intensively investigated due to their unique Dirac surface state carrying dissipationless edge spin currents. Recently, it has been theoretically proposed that the three dimensional analogue of this type of band structure, the Weyl Semimetal phase, is materialized in pyrochlore oxides with strong spin-orbit coupling, accompanied by all-in-all-out spin ordering. Here, we report on the fabrication and magnetotransport of Eu2Ir2O7 single crystalline thin films. We reveal that one of the two degenerate all-in-all-out domain structure…
We present magnetotransport evidence for antiferromagnetism in films of the electron-doped cuprates Pr$_{2-x}$Ce$_x$CuO$_4$. Our results show clear signature of static antiferromagnetism up to optimal doping x=0.15, with a quantum phase transition close to x=0.16, and a coexistence of static antiferromagnetism and superconductivity for 0.12$\le$x$\le$0.15.
Transition metal oxides show fascinating physical properties such as high temperature superconductivity, ferro- and antiferromagnetism, ferroelectricity or even multiferroicity. The enormous progress in oxide thin film technology allows us to integrate these materials with semiconducting, normal conducting, dielectric or non-linear optical oxides in complex oxide heterostructures, providing the basis for novel multi-functional materials and various device applications. Here, we report on the combination of ferromagnetic, semiconducting, metallic, and dielectric materials properties in thin fil…
We report a magnetotransport study of spin relaxation in 1.4-21.2 nm epitaxial SrIrO$_3$ thin films coherently strained on SrTiO$_3$ substrates. Fully charge compensated semimetallic transport has been observed in SrIrO$_3$ films thicker than 1.6 nm, where the charge mobility at 10 K increases from 45 cm$^2$/Vs to 150 cm$^2$/Vs with decreasing film thickness. In the two-dimensional regime, the charge dephasing and spin-orbit scattering lengths extracted from the weak localization/anti-localization effects show power-law dependence on temperature, pointing to the important role of electron-elec…