Epitaxial perovskite (110) oriented SrIrO3 (SIO) thin films were grown by pulsed laser deposition on (110) oriented DyScO3 (DSO) substrates with various film thickness t (2 nm < t < 50 nm). All the films were produced with stoichiometric composition, orthorhombic phase, and with high crystallinity. The nearly perfect in-plane lattice matching of DSO with respect to SIO and same symmetry result in a full epitaxial inplane alignment, i.e., the c-axis of DSO and SIO are parallel to each other with only slightly enlarged d110 out-of-plane lattice spacing (+0.38%) due to the small in-plane compressive strain caused by the DSO substrate. Measurements of the magnetoresistance MR were carried out for current flow along the [001] and [1-10] direction of SIO and magnetic field perpendicular to the film plane. MR appears to be distinctly different for both directions. The anisotropy MR001/MR1-10 > 1 increases with decreasing T and is especially pronounced for the thinnest films, which likewise display a hysteretic field dependence below T* ~ 3 K. The coercive field Hc amounts to 2-5 T. Both, T* and Hc are very similar to the magnetic ordering temperature and coercivity of DSO which strongly suggests substrate-induced mechanism as a reason for the anisotropic magnetotransport in the SIO films.
We investigate the magnetic and magnetotransport properties of nanostructured Nd0.6Sr0.4MnO3 (NSMO) thin films grown on (100) oriented SrTiO3 (STO) substrates. The thin films fabricated using the pulsed laser deposition technique have been found to possess two distinct surface morphologies: granular and nano rod type. Magnetization measurements have revealed that the films with rod-type morphology exhibit improved in-plane magnetic anisotropy. Magnetotransport studies have revealed that the granular thin films display a characteristic butterfly-shaped low-field magneto-resistive (LFMR) behavio…
We report growth and characterization of epitaxial $α$-Sn thin films grown on CdTe(111)B. Noninvasive techniques verify the film's pseduomorphic growth before fabrication of magnetotransport devices, overcoming ex-situ obstacles on uncapped films for measurement in the Hall bar geometry. We identify a transition to metallic behavior at low temperature with large magnetoresistance, high mobility, and quantum oscillations tentatively suggesting an n-type Dirac semimetallic channel. A parallel p-type dopant channel with high carrier density is seen to dominate at thinner film thicknesses. Careful…
To understand the near-interface magnetism in manganites, uniform, ultra-thin films of La_{0.67}Sr_{0.33}MnO_3 were grown epitaxially on single crystal (001) LaAlO_3 and (110) NdGaO_3 substrates. The temperature and magnetic field dependent film resistance is used to probe the film's structural and magnetic properties. A surface and/or interface related dead-layer is inferred from the thickness dependent resistance and magnetoresistance. The total thickness of the dead layer is estimated to be $\sim 30 Å$ for films on NdGaO_3 and $\sim 50 Å$ for films on LaAlO_3.
We report the magnetoresistance measurements of a highly oriented La0.55Ho0.15Sr0.3MnOz film on LaAlO3 substrate. The film has a metal-insulator transition around 200 K and shows pronounced thermomagnetic history effect in its transport properties below 45 K at 7 Tesla. The irreversibility temperature shifts to lower temperatures when the field is reduced. This behaviour is opposite to the thermomagnetic history effect observed in the magnetisation. At 2.8 K one also observes a significant hysteresis in the resistance versus field curve. We propose a qualitative explanation for these observati…
We show that applying strain on half-doped manganites makes it possible to tune the system to the proximity of a metal-insulator transition and thereby generate a colossal magnetoresistance (CMR) response. This phase competition not only allows control of CMR in ferromagnetic metallic manganites but can be used to generate CMR response in otherwise robust insulators at half-doping. Further, from our realistic microscopic model of strain and magnetotransport calculations within the Kubo formalism, we demonstrate a striking result of strain engineering that, under tensile strain, a ferromagnetic…
Artificial superlattices designed with ferromagnetic Pr0.85Ca0.15MnO3 insulating layer and ferroelectric Ba0.6Sr0.4TiO3 layer were grown on (100) SrTiO3 substrates. The magnetotransport properties were measured with the current perpendicular to the plane geometry. An increase in magnetoresistance (MR), with no significant low field effect, was observed as the number of ferroelectric Ba0.6Sr0.4TiO3 layer thickness increases even up to 9 unit cells. For example, the superlattice [(Pr0.85Ca0.15MnO3)10(Ba0.6Sr0.4TiO3)9]25 shows 35 % MR at 100 K, though the Pr0.85Ca0.15MnO3 film was a robust insula…
We report on the evolution of the average and depth-dependent magnetic order in thin film samples of biaxially stressed and electron-doped EuTiO$_3$ for samples across a doping range $<$0.1 to 7.8 $\times 10^{20}$ cm$^{-3}$. Under an applied in-plane magnetic field, the G-type antiferromagnetic ground state undergoes a continuous spin-flop phase transition into in-plane, field-polarized ferromagnetism. The critical field for ferromagnetism slightly decreases with an increasing number of free carriers, yet the field evolution of the spin-flop transition is qualitatively similar across the dopin…
Highly oriented polycrystalline SSMO thin films deposited on single crystal substrates by ultrasonic nebulized spray pyrolysis have been studied. The film on LAO is under compressive strain while LSAT and STO are under tensile strain. The presence of a metamagnetic state akin to cluster glass formed due to coexisting FM and antiferromagnetic/charge order (AFM/CO) clusters. All the films show colossal magnetoresistance but its temperature and magnetic field dependence are drastically different. In the lower temperature region the magnetic field dependent isothermal resistivity also shows signat…
An important challenge in the field of topological materials is to carefully disentangle the electronic transport contribution of the topological surface states from that of the bulk. For Bi$_2$Te$_3$ topological insulator samples, bulk single crystals and thin films exposed to air during fabrication processes are known to be bulk conducting, with the chemical potential in the bulk conduction band. For Bi$_2$Te$_3$ thin films grown by molecular beam epitaxy, we combine structural characterization (transmission electron microscopy), chemical surface analysis as function of time (x-ray photoelec…
We report a comparative study of the properties of very thin films of La0.67Ca0.33MnO3 grown epitaxially under strain on flat SrTiO3 (STO) and on 1 deg miscut STO. For the films on flat STO the transport properties show well-known behavior, namely values of the metal-insulator transition temperature which are strongly reduced with respect to the bulk value. The reduction in films on miscut STO is significantly less strong than in films on flat STO, even though they appear similar as to strain state. Moreover, the residual resistance at low temperatures is lower than for the case of flat films.…
By pulsed-laser deposition epitaxial thin films of Sr_2FeMoO_6 have been pre- pared on (100) SrTiO_3 substrates. Already for a deposition temperature of 320 C epitaxial growth is achieved. Depending on deposition parameters the films show metallic or semiconducting behavior. At high (low) deposition temperature the Fe,Mo sublattice has a rock-salt (random) structure. The metallic samples have a large negative magnetoresistance which peaks at the Curie temperature. The magnetic moment was determined to 4 mu_B per formula unit (f.u.), in agreement with the expected value for an ideal ferrimagnet…
In this paper, we have studied the effect of strain relaxation on magneto-transport properties of La_0.7Ca_0.3MnO_3 epitaxial films (200 nm thick), which were deposited by pulsed laser deposition technique under identical conditions. All the films are epitaxial and have cubic unit cell. The amount of strain relaxation has been varied by taking three different single crystal substrates of SrTiO_3, LaAlO_3 and MgO. It has been found that for thicker films the strain gets relaxed and produces variable amount of disorder depending on the strength of strain relaxation. The magnitude of lattice rela…
The perovskite manganites of general formula RE_1-xAe_xMnO_3 (RE= rare earth,AE=Ca, Sr, Ba and Pb)have drawn considerable attention, especially following the discovery of colossal magnetoresistance (CMR). They exhibit extraordinary large magnetoresistance pronounced as CMR in the vicinity of insulator-metal/paramagnetic-ferromagnetic transition at a relatively large applied magnetic fields. However, for applied aspectes, occurence of significant CMR at low applied magnetic fields would be required. This review consists of of two sections: In the first section we have extensively reviewed the s…
SmB6 has been predicted and verified as a prototype of topological Kondo insulators (TKIs). Here we report longitudinal magnetoresistance and Hall coefficient measurements on co-sputtered nanocrystalline SmB6 films and try to find possible signatures of their topological properties. The magnetoresistance (MR) at 2 K is positive and linear (LPMR) at low field and becomes negative and quadratic at higher field. While the negative part is known from the reduction of the hybridization gap due to Zeeman splitting, the positive dependence is similar to what has been observed in other topological ins…
We investigated the nature of transport and magnetic properties in SrIr0.5Ru0.5O3, (SIRO) which has characteristics intermediate between a correlated non-Fermi liquid state and an itinerant Fermi liquid state, by growing perovskite thin films on various substrates (SrTiO3 (001), (LaAlO3)0.3(Sr2TaAlO6)0.7 (001) and LaAlO3 (001)). We observed systematic variation of underlying substrate dependent metal-to-insulator transition temperatures at 80 K on SrTiO3, 90 K on (LaAlO3)0.3(Sr2TaAlO6)0.7 and 100 K on LaAlO3) in resistivity. Resistivity in the metallic region follows a T3/2 power law; whereas …
Polycrystalline La$_{2/3}$Sr$_{1/3}$MnO$_{3}$ (LSMO) thin films were synthesized by pulsed laser ablation on single crystal (100) yttria-stabilized zirconia (YSZ) substrates to investigate the mechanism of magneto-transport in a granular manganite. Different degrees of granularity is achieved by using the deposition temperature (T$_{D}$) of 700 and 800 $^{0}$C. Although no significant change in magnetic order temperature (T$_C$) and saturation magnetization is seen for these two types of films, the temperature and magnetic field dependence of their resistivity ($ρ$(T, H)) is strikingly dissimi…
Magnetotransport properties of La0.7Ca0.3MnO3 thin films deposited on (100) LaAlO3 substrate were investigated. The balance between the charge ordered insulating phase and ferromagnetic metallic phase may account for a number of glassy features such as: significant hysteresis, memory effects and long-time resistivity relaxation. It was found that the resistance of La0.7Ca0.3MnO3 thin film decreases significantly upon applying electric current, in a wide temperature range 10 - 220 K. The magnetotransport properties of the strained thin films are discussed in the context of cross-coupling of cha…
Pd$_{3}$Bi$_{2}$Se$_{2}$ has been proposed to be topologically non-trivial in nature. However, evidence of its non-trivial behavior is still unexplored. We report the growth and magneto-transport study of Pd$_{3}$Bi$_{2}$Se$_{2}$ thin films, revealing for the first time the contribution of two-dimensional (2D) topological surface states. We observe exceptional non-saturated linear magnetoresistance which results from Dirac fermions inhabiting the lowest Landau level in the quantum limit. The transverse magnetoresistance changes from a semi-classical weak-field $B^{2}$ dependence to a high-fiel…
Perovskite SrIrO3 (SIO) films epitaxially deposited with a thickness of about 60 nm on various substrate materials display nearly strain-relieved state. Films grown on orthorhombic (110) DyScO3 (DSO) are found to display untwinned bulk-like orthorhombic structure. However, film deposition on cubic (001) SrTiO3 induces a twinned growth of SIO. Resistance measurements on the SIO films reveal only weak temperature dependence, where the resistance R increases with decreasing temperature T. Hall measurements show dominant electron-like transport throughout the temperature range from 2 K to 300 K. A…
We report on the exchange bias between antiferromagnetic and ferroelectric hexagonal YMnO3 epitaxial thin films sandwiched between a metallic electrode (Pt) and a soft ferromagnetic layer (Py). Anisotropic magnetoresistance measurements are performed to monitor the presence of an exchange bias field. When the heteroestructure is biased by an electric field, it turns out that the exchange bias field is suppressed. We discuss the dependence of the observed effect on the amplitude and polarity of the electric field. Particular attention is devoted to the role of current leakage across the ferroel…
We have measured the magnetotransport properties of a strained metallic V2O3 thin film. Most of the properties are similar to V2O3 single crystals that have been submitted to a large pressure. In addition, resistance noise analysis indicates that conductivity fluctuations are freezing out at T\approx 10K. Examination of a range of measurements leads to the conclusion that spins-configuration fluctuations dominate in the low temperature regime.
Understanding the role of spin-orbit coupling (SOC) has been crucial to controlling magnetic anisotropy in magnetic multilayer films. It has been shown that electronic structure can be altered via interface SOC by varying the superlattice structure, resulting in spontaneous magnetization perpendicular or parallel to the plane. In lieu of magnetic thin films, we study the similarly anisotropic helimagnet Cr$_{1/3}$NbS$_2$, where the spin polarization direction, controlled by the applied magnetic field, can modify the electronic structure. As a result, the direction of spin polarization can modu…
We study the properties of Dirac fermions on the surface of a topological insulator in the presence of crossed electric and magnetic fields. We provide an exact solution to this problem and demonstrate that, in contrast to their counterparts in graphene, these Dirac fermions allow relative tuning of the orbital and Zeeman effects of an applied magnetic field by a crossed electric field along the surface. We also elaborate and extend our earlier results on normal metal-magnetic film-normal metal (NMN) and normal metal-barrier-magnetic film (NBM) junctions of topological insulators [Phys. Rev. L…
We present a study on magnetotransport in films of the topological Dirac semimetal Cd$_{3}$As$_{2}$ doped with Sb grown by molecular beam epitaxy. In our weak antilocalization analysis, we find a significant enhancement of the spin-orbit scattering rate, indicating that Sb doping leads to a strong increase of the pristine band-inversion energy. We discuss possible origins of this large enhancement by comparing Sb-doped Cd$_{3}$As$_{2}$ with other compound semiconductors. Sb-doped Cd$_{3}$As$_{2}$ will be a suitable system for further investigations and functionalization of topological Dirac se…
Due to the complex interplay of magnetic, structural, electronic, and orbital degrees of freedom, biaxial strain is known to play an essential role in the doped manganites. For coherently strained La(2/3)Ca(1/3)MnO(3) thin films grown on SrTiO(3) substrates, we measured the magnetotransport properties both parallel and perpendicular to the substrate and found an anomaly of the electrical transport properties. Whereas metallic behavior is found within the plane of biaxial strain, for transport perpendicular to this plane an insulating behavior and non-linear current-voltage characteristics (IVC…
SSMO5347 thin films (thicknesses ~200 nm) were deposited by on-axis dc magnetron sputtering on the single crystal LSAT (001) substrates. These films are oriented along the out of plane c-direction. The ferromagnetic and insulator-metal transition occurs at 96 K and 91 K, respectively. The magnetization easy axis is observed to lie in the plane of the film while the magnetic hard axis is found to be along the normal to this. The magnetotransport of the SSMO films, which was measured as a function of angle (theta) between the magnetic field (H) and plane of the film, shows colossal anisotropy. M…
A new class of materials termed topological insulators have been intensively investigated due to their unique Dirac surface state carrying dissipationless edge spin currents. Recently, it has been theoretically proposed that the three dimensional analogue of this type of band structure, the Weyl Semimetal phase, is materialized in pyrochlore oxides with strong spin-orbit coupling, accompanied by all-in-all-out spin ordering. Here, we report on the fabrication and magnetotransport of Eu2Ir2O7 single crystalline thin films. We reveal that one of the two degenerate all-in-all-out domain structure…
We report the magnetotransport properties of thin polycrystalline films of the recently discovered non-oxide perovskite superconductor MgCNi3. CNi3 precursor films were deposited onto sapphire substrates and subsequently exposed to Mg vapor at 700 C. We report transition temperatures (Tc) and critical field values (Hc2) of MgCNi3 films ranging in thickness from 7.5 nm to 100 nm. Films thicker than ~40 nm have a Tc ~ 8 K, and an upper critical field Hc2 ~ 14 T, which are both comparable to that of polycrystalline powders. Hall measurements in the normal state give a carrier density, n =-4.2 x 1…
The emerging Ni-based superconducting oxide thin films are rather intriguing to the entire condensed matter physics. Here we report some brief experimental results on transport measurements for a 14-nm-thick superconducting Nd0.8Sr0.2NiO2/SrTiO3 thin-film heterostructure with an onset transition temperature of ~9.5 K. Photoluminescence measurements reveal that there is negligible oxygen vacancy creation in the SrTiO3 substrate during thin-film deposition and post chemical reduction for the Nd0.8Sr0.2NiO2/SrTiO3 heterostructure. It was found that the critical current density of the Nd0.8Sr0.2Ni…
We have investigated the dimensionality and origin of the magnetotransport properties of LaAlO3 films epitaxially grown on TiO2-terminated SrTiO3(001) substrates. High mobility conduction is observed at low deposition oxygen pressures (PO2 < 10^-5 mbar) and has a three-dimensional character. However, at higher PO2 the conduction is dramatically suppressed and nonmetallic behavior appears. Experimental data strongly support an interpretation of these properties based on the creation of oxygen vacancies in the SrTiO3 substrates during the growth of the LaAlO3 layer. When grown on SrTiO3 substrat…
We explore the temperature dependent magnetoresistance of bulk insulating topological insulator thin films. Thin films of Bi2Se2Te and BiSbTeSe1.6 were grown using Pulsed Laser Deposition technique and subjected to transport measurements. Magnetotransport measurements indicate a non-saturating linear magnetoresistance (LMR) behavior at high magnetic field values. We present a careful analysis to explain the origin of LMR taking into consideration all the existing models of LMR. Here we consider that the bulk insulating states and the metallic surface states constitute two parallel conduction c…
We report the temperature and magnetic field dependence of transport properties in epitaxial films of the manganite La$_{1-x}$Ca$_{x}$MnO$_{3}$ in the overdoped region of the phase diagram for $x > 0.5$, where a charge--ordered (CO) and an antiferromagnetic (AF) phase are present. Resistivity, magnetoresistance and angular dependence of magnetoresistance were measured in the temperature interval $4.2 ~\mathrm{K} < T < 300 ~\mathrm{K}$, for three concentrations $x = 0.52, 0.58$ and $0.75$ and in magnetic fields up to 5 T. The semiconductor/insulator--like behavior in zero field was observed in …
Strongly correlated iridate pyrochlores with geometrically frustrated spins have been recognized as a potentially interesting group of oxide materials where novel topological phases may appear. A particularly attractive system is the metallic Pr$_2$Ir$_2$O$_7$, as it is known as a Fermi node semimetal characterized by quadratic band touching at the Brillouin zone center, suggesting that the topology of its electronic states can be tuned by moderate lattice strain. In this work we report the growth of epitaxial Pr$_2$Ir$_2$O$_7$ thin films grown by solid-state epitaxy. We show that the strained…
We present magnetotransport evidence for antiferromagnetism in films of the electron-doped cuprates Pr$_{2-x}$Ce$_x$CuO$_4$. Our results show clear signature of static antiferromagnetism up to optimal doping x=0.15, with a quantum phase transition close to x=0.16, and a coexistence of static antiferromagnetism and superconductivity for 0.12$\le$x$\le$0.15.