Using isothermal and temperature-dependent electrical measurements, we investigated the resistive switching mechanism of amorphous titanium oxide thin films deposited by a plasma-enhanced atomic layer deposition method between two aluminum electrodes. We found a bipolar resistive switching behavior in the high temperature region (> 140 K), and two activation energies of shallow traps, 0.055 eV and 0.126 eV in the ohmic current regime. We also proposed that the bipolar resistive switching of amorphous TiO2 thin films is governed by the transition of conduction mode from a bulk-limited SCLC model (Off state) to an interface-limited Schottky emission (On state), generated by the ionic movement of oxygen vacancies.
We report a direct observation of the microscopic origin of the bipolar resistive switching behavior in nanoscale titanium oxide films. Through a high-resolution transmission electron microscopy, an analytical TEM technique using energy-filtering transmission electron microscopy and an in situ x-ray photoelectron spectroscopy, we demonstrated that the oxygen ions piled up at top interface by an oxidation-reduction reaction between the titanium oxide layer and the top Al metal electrode. We also found that the drift of oxygen ions during the on/off switching induced the bipolar resistive switch…
Nonvolatile bipolar resistive switching has been observed in an Au/BiFeO3/Pt structure, where a Schottky contact and a quasi-Ohmic contact were formed at the Au/BiFeO3 and BiFeO3/Pt interface, respectively. By changing the polarity of the external voltage, the Au/BiFeO3/Pt is switched between two stable resistance states without an electroforming process. The resistance ratio is larger than two orders of magnitude. The resistive switching is understood by the electric field - induced carriers trapping and detrapping, which changes the depletion layer thickness at the Au/BiFeO3 interface.
We investigated electroforming-free bipolar resistive switching behavior in Pt/Ti/Al2O3/Al tunnel junctions where the Al2O3 tunnel barrier was naturally formed on Al in air. Various compliance current values for the junction's set switching successfully lead to various resistance values in its low resistance state, suggesting the possibility for multi-level-operation. A mechanism for the bipolar switching is qualitatively discussed in terms of the modulation of the tunnel barrier by the reactive Ti layer on top of the barrier.
We introduce a model that accounts for the bipolar resistive switching phenomenom observed in transition metal oxides. It qualitatively describes the electric field-enhanced migration of oxygen vacancies at the nano-scale. The numerical study of the model predicts that strong electric fields develop in the highly resistive dielectric-electrode interfaces, leading to a spatially inhomogeneous oxygen vacancies distribution and a concomitant resistive switching effect. The theoretical results qualitatively reproduce non-trivial resistance hysteresis experiments that we also report, providing key …
Empowering conventional materials with unexpected magnetoelectric properties is appealing to the multi-functionalization of existing devices and the exploration of future electronics. Recently, owing to its unique effect in modulating a matter's properties, ultra-small dopants, e.g. H, D, and Li, attract enormous attention in creating emergent functionalities, such as superconductivity, and metal-insulator transition. Here, we report an observation of bipolar conduction accompanied by a giant positive magnetoresistance in D-doped metallic Ti oxide (TiOxDy) films. To overcome the challenges in …
Reverse and stable bipolar resistive switching effect was observed in planar NdCeCuO - NdCeO - Ag heterostructures. It was shown that the current voltage charactereriscs of the BRSE observed has a diode character. Simulations were used to consider the influence of the nonuniform distribution of an electric field at the interface of a heterojunction on the effect of bipolar resistive switching in investigated structures. The inhomogeneous distribution of the electric field near the contact edge creates regions of higher electric field strength which, in turn, stimulates motion and redistributio…
Controlled bipolar resistive switching (BRS) has been observed in nanostructured CoFe2O4 films using Al(aluminum)/CoFe2O4/FTO(fluorine-doped tin oxide) device. The fabricated device shows electroforming-free uniform BRS with two clearly distinguished and stable resistance states without any application of compliance current (CC), with a resistance ratio of high resistance state (HRS) and low resistance state (LRS) > 102. Small switching voltage (< 1 volt) and lower current in both the resistance states confirms the fabrication of low power consumption device. In the LRS, the conduction mechani…
BiFeO3 thin films are deposited on FTO coated glass substrates using a simple sol-gel deposition technique, limiting thickness about 70 nm and Ag/BiFeO3/FTO RRAM devices are prepared. The devices showed low-voltage bipolar switching with the maximum Ion/Ioff ~ 450, and low set and reset voltages ~ 1.1 V and -1.5 V, respectively. The devices are stable against on-off cycles with ~ 104 s retention time without any significant degradation. The variations in the set and reset voltages are 0.4 V and 0.6 V, respectively. We found that ohmic and trap-controlled space charge limited conductions are re…
Bipolar resistive switching (BRS) phenomenon has been demonstrated in Mn3O4 using Al (Aluminum)/Mn3O4/FTO (Fluorine doped Tin Oxide) Resistive Random Access Memory (RRAM) device. The fabricated RRAM device shows good retention, non volatile behavior and forming free BRS. The Current-Voltage (I-V) characteristics and the temperature dependence of the resistance (R-T) measurements were used to explore conduction mechanisms and the thermal activation energy (Ea). The resistance ratio of high resistance state (HRS) to low resistance state (LRS) is ~102. The fabricated RRAM device shows different c…
Complementary resistive switches (CRS) are considered as a potential solution for the sneak path problem in large-scale integration of passive crossbar resistive memory arrays. A typical CRS is composed of two bipolar memory cells that are connected anti-serially. Here we report a tantalum-oxide based resistive memory that achieves the complementary switching functionality within a single memory cell. The complementary switching effect is accompanied by switching polarity reversal in different voltage bias regimes. These effects were explained by the redistribution of oxygen vacancies inside t…
For the clear understanding of the role of interface reaction between top metal electrode and titanium oxide layer, we investigated the effects of various top metals on the resistive switching in Metal/a-TiO2/Al devices. The top Al device with the highest oxygen affinity showed the best memory performance, which is attributed to the fast formation of interfacial layer (Al-Ti-O), as confirmed by high resolution transmission electron microscopy and electron dispersive spectroscopy. Hence, we concluded that the interface layer, created by the redox reaction between top metal electrode and TiO2 la…
We investigated the reversible resistive switching of poly(3,4-ethylenedioxythiophene):polystyrenesulfonate (PEDOT:PSS) thin films sandwiched between Al electrodes. The J-V sweep curve showed a hysteretic behavior which depends on the polarity of the applied voltage bias. From the analysis of I-V curves, it was revealed that the charge transport through the junction was governed by the bulk space-charge-limited conduction (SCLC) model. Using transmission electron microscopy (TEM) analysis, it was confirmed that the initial high resistance state of PEDOT:PSS films is related with the segregatio…
Metallic oxides encased within Metal-Insulator-Metal (MIM) structures can demonstrate both unipolar and bipolar switching mechanisms, rendering them the capability to exhibit a multitude of resistive states and ultimately function as memory elements. Identifying the vital physical mechanisms behind resistive switching can enable these devices to be utilized more efficiently, reliably and in the long-term. In this paper, we present a new approach for analysing resistive switching by modelling the active core of two terminal devices as 2D and 3D grid circuit breaker networks. This model is emplo…
We have studied the effects of accumulating cyclic electrical pulses of increasing amplitude on the non-volatile resistance state of interfaces made by sputtering a metal (Au, Pt) on top of the surface of a cuprate superconductor YBa$_2$Cu$_3$O$_{7-δ}$ (YBCO). We have analyzed the influence of the number of applied pulses $N$ on the relative amplitude of the remnant resistance change between the high ($R_H$) and the low ($R_L$) state [$α=(R_{H}-R_{L})/R_{L}$] at different temperatures ($T$). We show that the critical voltage ($V_c$) needed to produce a resistive switching (RS, i.e. $α>0$) decr…
Flexible solution processed memristors show different behaviour dependent on the choice of electrode material. Use of gold for both electrodes leads to switchable WORM (Write Once Read Many times) resistive devices. Use of aluminium for both electrodes increases the richness of behaviour allowing both curved and triangular memristive switching resistance memories. A comparison device with an aluminium bottom electrode and gold top electrode only exhibited significant memristive resistance switching when the aluminium electrode was the cathode, suggesting that the electrode is acting as a sourc…
We studied the resistive memory switching in pulsed laser deposited amorphous LaHoO3 (LHO) thin films for non-volatile resistive random access memory (RRAM) applications. Nonpolar resistive switching (RS) was achieved in PtLHOPt memory cells with all four possible RS modes ( positive unipolar, positive bipolar, negative unipolar, and negative bipolar) having high RON and ROFF ratios (in the range of 104 to 105) and non-overlapping switching voltages (set voltage, VON 3.6 to 4.2 V and reset voltage, VOFF 1.3 to 1.6 V) with a small variation of about 5 to 8 percent. X ray photoelectron spectrosc…
Bipolar resistive switching using organic molecule is very promising for memory application owing to their advantages like simple device structure, low manufacturing cost, their stability and flexibility etc. Herein we report Langmuir-Blodgett and spin-coated film based bipolar resistive switching devices using organic material indole derivative. Pressure - area per molecule isotherm, Brewster Angle Microscopy, Atomic Force Microscopy and Scanning Electron Microscopy were used to have an idea about organization and morphology of the organic material onto thin film. Based on device structure an…
Superlattices may play an important role in next generation electronic and spintronic devices if the key-challenge of the reading and writing data can be solved. This challenge emerges from the coupling of low dimensional individual layers with macroscopic world. Here we report the study of the resistive switching characteristics of a of hybrid structure made out of a superlattice with ultrathin layers of two ferromagnetic metallic oxides, La0.7Sr0.3MnO3 (LSMO) and SrRuO3 (SRO). Bipolar resistive switching memory effects are measured on these LSMO/SRO superlattices, and the observed switching …
The resistive switching phenomena of HfO2 films grown by metalorganic chemical vapor deposition was studied for the application of ReRAM devices. In the fabricated Pt/HfO2/TiN memory cells, the bipolar resistive switching characteristics were observed, and the set and reset states were measured to be as low as 7 uA and 4 uA, respectively, at VREAD = 1 V. Regarding the resistive switching performance, the stable RS performance was observed under 40 repetitive dc cycling test with the small variations of set/reset voltages and currents, and good retention characteristics over 105 s in both LRS a…
Recent renewal of the highest transition temperature in a conventional superconductor of the sulfer hydride attracts much attention to exploring simple compounds with the lighter elements, situated in unconventional conditions. We report the discovery of superconductivity in simple oxides of Ti4O7 and g-Ti3O5 in a thin-film form having deliberately tuned epitaxial structures and off-stoichiometry. These higher titanium oxides join in a class of simple-oxide superconductors, and g-Ti3O5 now holds the highest superconducting transition temperature of 7.1 kelvin among them. The mechanism behind t…
Synaptic devices with linear high-speed switching can accelerate learning in artificial neural networks (ANNs) embodied in hardware. Conventional resistive memories however suffer from high write noise and asymmetric conductance tuning, preventing parallel programming of ANN arrays as needed to surpass conventional computing efficiency. Electrochemical random-access memories (ECRAMs), where resistive switching occurs by ion insertion into a redox-active channel address these challenges due to their linear switching and low noise. ECRAMs using two-dimensional (2D) materials and metal oxides suf…
The memristor is the fundamental non-linear circuit element, with uses in computing and computer memory. ReRAM (Resistive Random Access Memory) is a resistive switching memory proposed as a non-volatile memory. In this review we shall summarise the state of the art for these closely-related fields, concentrating on titanium dioxide, the well-utilised and archetypal material for both. We shall cover material properties, switching mechanisms and models to demonstrate what ReRAM and memristor scientists can learn from each other and examine the outlook for these technologies.
We report on resistive switching (RS) characteristics of W/WO3-x/Pt-based thin film memristors modulated by precisely controlled oxygen non-stoichiometry. RS properties of the devices with varied oxygen vacancy (VO) concentration have been studied by measuring their DC current voltage properties. Switchability of the resistance states in the memristors have been found to depend strongly on the VOs concentration in the WO3-x layer. Depending on x, the memristors exhibited forming-free bipolar, forming-required bipolar and non-formable characteristics. Devices with high VOs concentration (~1*102…
We investigate ferroelectric- and resistive switching behavior in 18-nm-thick epitaxial BaTiO$_3$ (BTO) films in a model electrolyte-ferroelectric-semiconductor (EFS) configuration. The system is explored for its potential as a ferroelectric microelectrode in bioelectronics. The BTO films are grown by pulsed laser deposition (PLD) on semiconducting Nb-doped (0.5 wt\%) SrTiO$_{3}$ (Nb:STO) single crystal substrates. The ferroelectric properties of the bare BTO films are demonstrated by piezoresponse force microscopy (PFM) measurements. Cyclic voltammetry (CV) measurements in EFS configuration, …
Here we demonstrate that both, tunnel magneto resistance (TMR) and resistive switching (RS), can be observed simultaneously in nano-scale magnetic tunnel junctions. The devices show bipolar RS of 6 % and TMR ratios of about 100 %. For each magnetic state, multiple resistive sates are created depending on the bias history which provides a method for multi-bit data storage and logic. The electronic transport measurements are discussed in the framework of a memristive system. Differently prepared MgO barriers are compared to gain insight into the switching mechanism.
The development prospects of memristive elements for non-volatile memory with use of the metal-dielectric-metal sandwich structures with a thin oxide layer are due to the possibility of reliable forming the sustained functional states with quantized resistance. In the paper we study the properties of fabricated memristors based on the non-stoichiometric $ZrO_2$ nanotubes in different resistive switching modes. Anodic oxidation of the $Zr$ foil has been used to synthesize a zirconia layer of $1.7$ $μ$$m$ thickness, consisting of an ordered array of vertically oriented nanotubes with outer diame…
Self-ordered nanotubular titania TiO2-NT with outer tube diameter of 45 nm are synthesized using the anodic oxidation of titanium foil. Four sets of memristors with 100 $μm$ diameter based on Ti/TiO2-NT/Au sandwich structures with an oxide layer thickness of 80, 120, 160 and 200 nm are fabricated. Current-voltage (CV) characteristics for the obtained samples in the static and dynamic operation modes are studied. Resistance in high and low resistance states is estimated. Basing on the analysis of the CV characteristics in dynamic mode (> 14 000 switchings) a prospective of use for synthesized T…
High-performance non-volatile resistive random access memories (ReRAM) and their small stimuli control are of immense interest for high-speed computation and big-data processing in the emergent Internet of Things (IOT) arena. Here, we examine the resistive switching (RS) behavior in growth controlled HfO2/La0.67Sr0.33MnO3 heterostructures and their tunability under low magnetic field. It is demonstrated that oxygen-deficient HfO2 films show bipolar switching with high on/off ratio, stable retention, as well as good endurance owing to the orthorhombic-rich phase constitution and charge (de)-tra…
Understanding electronic properties of sub-stoichiometric phases of titanium oxide such as Magnéli phase Ti4O7 is crucial in designing and modeling resistive switching devices. Here we present our study on Magnéli phase Ti4O7 together with rutile TiO2 and Ti2O3 using density functional theory methods with atomic-orbital-based self-interaction correction (ASIC). We predict a new antiferromagnetic ground state in the low temperature phase (or LT phase), and we explain energy difference with a competing antiferromagnetic state using a Heisenberg model. The predicted energy ordering of these state…
Here we report the design and synthesis of an imidazole derivative namely 1-benzyl-2,4,5-triaryl imidazole and its switching behaviour assembled onto Langmuir-Blodgett films. Monolayer characteristic of imidazole at the air-water interface has been studied by surface pressure vs area per molecule isotherm, hysteresis analysis and insitu Brewster Angle Microscopy . These studies indicated the formation of stable floating Langmuir film at the water subphase. Atomic Force Microscopy investigation confirmed the successful deposition of the Langmuir film onto solid substrate. Device consisted of 60…
Multiferroic (MF) devices based on simultaneous ferroelectric and ferromagnetic phenomena are considered to be promising candidates for future bi-functional micro/nano-electronics. The multiferroic phenomena in two-dimensional materials is rarely reported in literature. We reported a simple approach to reveal frequency-dependent ferroelectricity and mutiferroicity in Ti$_3$C$_2$T$_x$ MXene film at room-temperature. To study the frequency and poling effect on ferroelectricity as well as multiferroicity, we performed electric polarization vs. electric field measurement at different external freq…
Transition metal oxide memristors, or resistive random-access memory (RRAM) switches, are under intense development for storage-class memory because of their favorable operating power, endurance, speed, and density. Their commercial deployment critically depends on predictive compact models based on understanding nanoscale physico-chemical forces, which remains elusive and controversial owing to the difficulties in directly observing atomic motions during resistive switching, Here, using scanning transmission synchrotron x-ray spectromicroscopy to study in-situ switching of hafnium oxide memri…
Using memristive properties common for the titanium dioxide thin film devices, we designed a simple write algorithm to tune device conductance at a specific bias point to 1% relative accuracy (which is roughly equivalent to 7-bit precision) within its dynamic range even in the presence of large variations in switching behavior. The high precision state is nonvolatile and the results are likely to be sustained for nanoscale memristive devices because of the inherent filamentary nature of the resistive switching. The proposed functionality of memristive devices is especially attractive for analo…
The thermal radiative near field transport between vanadium dioxide and silicon oxide at submicron distances is expected to exhibit a strong dependence on the state of vanadium dioxide which undergoes a metal-insulator transition near room temperature. We report the measurement of near field thermal transport between a heated silicon oxide micro-sphere and a vanadium dioxide thin film on a titanium oxide (rutile) substrate. The temperatures of the 15 nm vanadium dioxide thin film varied to be below and above the metal-insulator-transition, the sphere temperatures were varied in a range between…
Thin films of amorphous (a)-TiO2 are ubiquitous as photocatalysts, protective coatings, photoanodes and in memory application, where they are exposed to excess electrons and holes. We investigate trapping of excess electrons and holes in the bulk of pure amorphous titanium dioxide, a-TiO2, using hybrid density functional theory (h-DFT) calculations. Fifty 270-atom a-TiO2 structures were produced using classical molecular dynamics and their geometries fully optimised using h-DFT simulations. They have the density, distribution of atomic coordination numbers and radial pair-distribution function…