To investigate the normal-state magnetic properties of UTe2 under pressure, we perform 125Te nuclear magnetic resonance (NMR) measurements up to 2 GPa. Below 1.2 GPa, the b-axis NMR Knight shift shows a broad maximum at the so-called T_chimax on cooling, which is consistent with the magnetization measurement under pressure. T_chimax decreases with increasing pressure and disappears at the critical pressure Pc = 1.7 GPa, above which superconductivity is destroyed. This tendency is also observed in the temperature dependence of the nuclear spin-lattice relaxation rate 1/T1. At low pressures, 1/T1 shows a conventional Fermi-liquid behavior (1/T1T = constant) at low temperatures, indicating the formation of the heavy-fermion state. Above Pc, 1/T1T follows a 1/T behavior without any crossover to the heavy-fermion state down to the lowest temperature (~3 K). In addition, the NMR signals disappear below 3~K, due to the influence of the magnetically ordered moments. From the pressure dependence of the T_chimax and Knight shift, it was found that the Fermi surface character is abruptly changed at Pc, and that superconductivity is observed only in the heavy-fermion state.
Temperature independent pseudogap from $^{17}$O and $^{89}$Y NMR and the single component picture
核磁共振（NMR）是一种强有力的材料电子结构局域量子探针，但在缺乏可靠理论的情况下，NMR数据的解释可能具有挑战性。对于铜氧化物高温超导体尤其如此。多年来，大量的核磁共振数据变得可用，这使得对早期解释的审查成为可能。最近，它表明，所有的平面$^{17}$ O NMR位移和弛豫数据在文献中指向一个温度无关，但掺杂依赖的赝能隙，非常类似于所提出的电子熵。在这里，我们分析的平面O的位移和弛豫的各向异性，以建立一个单一的电子自旋组件是否适用，因为平面铜位移各向异性显然失败这样的描述。我们发现，从数据中推导出的轨道位移项与第一性原理计算一致，位移数据显示出与温度无关的各向异性也与第一性原理预测的超精细系数一致，这也解释了弛豫各向异性。此外，我们表明，原来的$^{89}$ Y位移和弛豫数据与建议的温度无关的赝能隙。这个赝能隙取决于掺杂，但也取决于材料的家族，并且在能隙之外或没有能隙的情况下的态密度对于铜酸盐是普遍的;这表明熵对于所有的铜酸盐也应该是相似的。将讨论进一步的后果。
A magnetization and $^{11}$B NMR study of Mg$_{1-x}$Al$_x$B$_2$ superconductors
本文首次用$^{11}$ B NMR在23.5和47 kOe的磁场下研究了轻掺杂Mg $_{1-x}$ Al $_x$ B $_2$（$x\leq 0.025$）粉末样品中纯涡旋态的磁场分布。在T=5 K时的磁场分布是Al掺杂依赖的，揭示了相对于纯MgB $_2$的各向异性的相当大的减少。这一结果与磁化测量结果很好地相关，并且与MgB $_2$的$σ$带空穴驱动超导性一致.
NMR and NQR studies on transition-metal arsenide superconductors LaRu2As2, KCa2Fe4As4F2, and A2Cr3As3
我们报告75 As-核磁共振（NMR）和核四极共振（NQR）测量过渡金属砷化物LaRu 2 As 2，KCa 2 Fe 4 As 4 F2，和A2 Cr 3 As 3。在LaRu_2As_2的超导态中，自旋-晶格弛豫速率~（-1）/T_1的温度依赖关系在T_c以下出现一个Hebel-Slichter相干峰，表明LaRu_2As_2是一个全带隙超导体。对于KCa_2Fe_4As_4F_2，在正常态下观察到反铁磁自旋涨落。我们进一步发现各向异性率RAF = Tc 1/Tab 1很小且与温度无关，这意味着低能自旋涨落在自旋空间中是各向同性的.我们的研究结果表明，KCa_2Fe_4As_4F_2是一种适度过掺杂的铁砷化物高温超导体，具有化学计量组成。对于A_2Cr_3As_3，我们用第一性原理方法计算了电场梯度，并将75 As-NQR峰归属于两个晶体学上不同的As位，为进一步的NMR研究铺平了道路。
Breaking of Ginzburg-Landau description in the temperature dependence of the anisotropy in the nematic superconductor
向列相超导体的特征在于明显的晶体对称性破缺，这导致面内上临界磁场$H_{c2}$的各向异性。对称性破缺通常归因于晶格的应变。该菌株的性质和价值是有争议的。在1.8~K $<T<T_c\approx 2.7$~K温度范围内，利用温度稳定技术对高质量的Sr $_x$ Bi $_2$ Se $_3$单晶中的$H_{c2}$各向异性进行了系统的测量，测量精度为0.0001 K。我们观察到，在所有测试样品的各向异性是弱的温度依赖时，$T<0.8\,T_c$和平稳地降低在较高的温度下，没有任何迹象的奇异性时，$T\rightarrow T_c$。这种行为与金-朗道理论对超导体的预言是完全矛盾的。我们讨论这种差异的可能原因。
Pressure Induced Stripe-order Antiferromagnetism and First-order Phase Transition in FeSe
为了阐明FeSe的磁结构和向列性的起源，我们对FeSe单晶进行了高压$^{77}$ Se NMR研究。我们发现，抑制的结构转变温度与压力高达约2 GPa的各向异性的奈特位移。在2GPa以上，打破空间四重旋转对称性的条序反铁磁性由不同场取向下的NMR谱确定，温度低至50 mK。磁相变是一级相变，这意味着存在一个伴随的结构转变通过自旋-晶格耦合。条纹型自旋波动在高温下观察到，并保持强大的压力。这些结果为FeSe中向列性和磁性之间的强耦合提供了明确的证据，从而支持了铁基超导体中磁驱动向列性的普遍假设。
Enhanced superconducting transition temperature in hyper-interlayer-expanded FeSe despite the suppressed electronic nematic order and spin fluctuations
通过插入分子间隔层可以显著提高FeSe的超导临界温度$T_{\rm c}$。本文报道了粉末状超层间膨胀Li的$^{77}$ Se、$^7$ Li和$^1$ H核磁共振（NMR）研究。在$^7$ Li和$^1$ H NMR谱中没有任何位移表明FeSe层中的传导电子与层间单元完全解耦，而几乎与温度无关的$^7$ Li和$^1$ H自旋晶格弛豫速率与绝缘层间空间中存在的Fe杂质的不可忽略的浓度一致。另一方面，$^{77}$ Se NMR位移和自旋-晶格弛豫速率$1/^{77}T_1$的强温度依赖性归因于接近费米能的类空穴带。$1/^{77}T_1$没有显示出额外的各向异性，这将导致电子有序下降到$T_{\rm c}$。类似地，在正常状态下，没有发现由于自旋涨落引起的$1/^{77}T_1$的增强。然而，一个特征的幂律依赖性$1/^{77}T_1\propto T^{4.5}$仍然符合库珀配对介导的自旋波动。