A LiFeAs single crystal with $T_c^{onset}$$\sim$19.7 K was grown successfully in a sealed tungsten crucible using the Bridgeman method. The electrical resistivity experiments revealed a ratio of room temperature to residual resistivity (RRR) of approximately 46 and 18 for the in-plane and out-of plane directions. The estimated anisotropic resistivity, $γ_ρ$=$ρ_c$ / $ρ_{ab}$, was approximately 3.3 at $T_c^{onset}$. The upper critical fields had large $H_{c2} ^{\shortparallel ab}$ and $H_{c2}^{\shortparallel c}$ values of 83.4 T and 72.5 T, respectively, and an anisotropy ratio is $γ_H$=$H_{c2}^{\shortparallel ab}$ / $H_{c2} ^{\shortparallel c}$$\sim$1.15. The high upper critical field value and small anisotropy highlight the potential use of LiFeAs in a variety of applications. The calculated critical current density $(J_c)$ from the $M$-$H$ loop is approximately 10$^3$ A/cm$^2$
The magnetic properties of LiFeAs, as single crystalline and polycrystalline samples, were investigated. The lower critical field deduced from the vortex penetration of two single crystals appears to be almost isotropic with a temperature dependence closer to that of two-gap superconductors. The parameters extracted from the reversible magnetizations of sintered polycrystalline samples are in good agreement with those from the single crystal data.
Miniature Hall-probe arrays were used to measure the critical current densities for the three main directions of vortex motion in the stoichiometric LiFeAs superconductor. These correspond to vortices oriented along the c-axis moving parallel to the ab-plane, and to vortices in the ab-plane moving perpendicular to, and within the plane, respectively. The measurements were carried out in the low-field regime of strong vortex pinning, in which the critical current anisotropy is solely determined by the coherence length anisotropy parameter, ε_ξ. This allows extraction of ε_ξ at magnetic fields f…
The upper critical field $μ_0H_{c2}(T_c)$ of LiFeAs single crystals has been determined by measuring the electrical resistivity using the facilities of pulsed magnetic field at Los Alamos. We found that $μ_0H_{c2}(T_c)$ of LiFeAs shows a moderate anisotropy among the layered iron-based superconductors; its anisotropic parameter $γ$ monotonically decreases with decreasing temperature and approaches $γ\simeq 1.5$ as $T\rightarrow 0$. The upper critical field reaches 15T ($H\parallel c$) and 24.2T ($H\parallel ab$) at $T=$1.4K, which value is much smaller than other iron-based high $T_c$ supercon…
Between the different families of pnictide multiband superconductors, LiFeAs is probably one of the less understood. Indeed, despite the large amount of experiments performed in the last few years on this material, no consensus has been reached yet on the possible pairing mechanism at play in this system. Here we focus on the precursor effects of superconductivity visible in the transport experiments performed above Tc. By analyzing the superconducting fluctuations in a layered multiband model appropriate for this material, we argue that the strong two-dimensional character of the paraconducti…
The superconducting state of LiFeAs single crystals with the maximum critical temperature $T_c\,\approx\,17\,K$ in the 111 family has been studied in detail by multiple Andreev reflections (MAR) spectroscopy implemented by the break-junction technique. The three superconducting gaps, $Δ_Γ\,= (5.1-6.5)\,meV$, $Δ_L\,= (3.8-4.8)\,meV$, and $Δ_S\,= (0.9-1.9)\,meV$ (at $T\,<<\,T_c$), as well as their temperature dependences, have been directly determined in a tunneling experiment with these samples. The anisotropy degrees of the order parameters in the k-space have been estimated as $<\,8$%, $\appr…
The newest homologous series of superconducting As-pnictides, LiFeAs (Li111) and NaFeAs (Na111) have been synthesized and investigated. Both crystallize with the layered tetragonal anti-PbFCl-type structure in P4/nmm space group. Polycrystalline samples and single-crystals of Li111 and Na111 display superconducting transitions at ~ 18 K and 12-25 K, respectively. No magnetic order has been found in either compound, although a weak magnetic background is clearly in evidence. The origin of the carriers and the stoichiometric compositions of Li111 and Na111 were explored.
The in- and out-of-plane lower critical fields and magnetic penetration depths for LiFeAs were examined. The anisotropy ratio $γ_{H_{c1}}(0)$ is smaller than the expected theoretical value, and increased slightly with increasing temperature from 0.6$T_c$ to $T_c$. This small degree of anisotropy was numerically confirmed by considering electron correlation effect. The temperature dependence of the penetration depths followed a power law($\sim$$T^n$) below 0.3$T_c$, with $n$$>$3.5 for both $λ_{ab}$ and $λ_c$. Based on theoretical studies of iron-based superconductors, these results suggest that…
Spectroscopy of vortex bound states can provide valuable information on the structure of the superconducting order parameter. Quasiparticle wavefunctions are expected to leak out in the directions of gap minima or nodes, if they exist, and scanning tunneling spectroscopy (STS) on these low-energy states should probe the momentum dependence of the gap. Anisotropy can also arise from band structure effects, however. We perform a quasiclassical calculation of the density of states of a single vortex in an anisotropic superconductor, and show that if the gap itself is not highly anisotropic, the F…
We have performed high-resolution angle-resolved photoemission spectroscopy on Fe-based superconductor LiFeAs (Tc = 18 K). We reveal multiple nodeless superconducting (SC) gaps with 2D/kBTc ratios varying from 2.8 to 6.4, depending on the Fermi surface (FS). We also succeeded in directly observing a gap anisotropy along the FS with magnitude up to ~30 %. The anisotropy is four-fold symmetric with an antiphase between the hole and electron FSs, suggesting complex anisotropic interactions for the SC pairing. The observed momentum dependence of the SC gap offers an excellent opportunity to invest…
LiFeAs is one of the iron-based superconductors having multiple gaps with the possible sign reversal. To clarify how those novel natures affect the energy dissipation of magnetic vortices, we investigated the microwave surface impedance of LiFeAs single crystals under finite magnetic fields. The flux-flow resistivity enhanced rapidly at low magnetic fields, which is similar to the case of MgB$_{2}$. This is probably the consequence of the multiple-gap nature and the gap anisotropy. This suggest that the sign-reversal is not important for the flux-flow even for multiple-gap superconductors. As …
The synthesis and properties of LiFeAs, a high-Tc Fe-based superconducting stoichiometric compound, are reported. Single crystal x-ray studies reveal that it crystallizes in the tetragonal PbFCl type (P4/nmm) with a=3.7914(7) A and c=6.364(2) A. Unlike the known isoelectronic undoped intrinsic FeAs compounds, LiFeAs does not show any spin-density wave behavior but exhibits superconductivity at ambient pressures without chemical doping. It exhibits a respectable transition temperature of Tc=18 K with electronlike carriers and a very high critical field, Hc2(0)>80 T. LiFeAs appears to be the che…
We report the successful growth of high quality single crystals of LiFeAs with lateral sizes up to 5 x 5 mm2 by the Sn-flux method. Electrical resistivity studies reveal that the superconducting onset temperature is 18.2 K with a transition width less than 1.1 K and the ratio of room temperature to residual resistivity is about 24. Bulk superconductivity is supported by perfect shielding in the magnetic susceptibility and a clear jump in the specific heat Cp, resulting in deltaCp/T ~ 20.0 mJ/mol*K2. Upper critical field slopes of dHc2c/dT ~ -1.39 and dHc2ab/dT ~ -2.99 T/K near Tc predict zero …
The resistivity, Hall effect and transverse magnetoresistance (MR) have been measured in low residual resistivity single crystals of LiFeAs. A comparison with angle resolved photoemission spectroscopy and quantum oscillation data implies that four carrier bands unevenly contribute to the transport. However the scattering rates of the carriers all display the T^2 behavior expected for a Fermi liquid. Near Tc low field deviations of the MR with respect to a H^2 variation permit us to extract the superconducting fluctuation contribution to the conductivity. Though below Tc the anisotropy of super…
We present an inelastic neutron scattering study on single-crystalline LiFeAs devoted to the characterization of the incommensurate antiferromagnetic fluctuations at $\mathbf{Q}=(0.5\pmδ, 0.5\mpδ, q_l)$. Time-of-flight measurements show the presence of these magnetic fluctuations up to an energy transfer of 60 meV, while polarized neutrons in combination with longitudinal polarization analysis on a triple-axis spectrometer prove the pure magnetic origin of this signal. The normalization of the magnetic scattering to an absolute scale yields that magnetic fluctuations in LiFeAs are by a factor …
We utilize a combination of vector magnetic field and scanning tunneling microscopy to elucidate the 3D field-based electronic phase diagram of a correlated iron-based superconductor, LiFeAs. We observe, under a zero-field-cooled method, an ordered hexagonal vortex lattice ground-state in contrast to the disordered lattice observed under a field-cooled method. It transforms into a four-fold-symmetric state by increasing c-axis field and distorts elliptically upon tilting the field in-plane. The vortex lattice transformations correlate with the field dependent superconducting gap that character…
The lack of nesting of the electron and hole Fermi-surface sheets in the Fe-based superconductor LiFeAs, with a critical temperature of 18 K, has led to questions as to whether the origin of superconductivity in this material might be different from other Fe-based superconductors. Both angle-resolved photoemission and quasiparticle interference experiments have reported fully gapped superconducting order parameters with significant anisotropy. The system is also of interest because relatively strong correlations seem to be responsible for significant renormalization of the hole bands. Here we …
We report on the upper critical field B_c2 of a superconducting LiFeAs single crystal with T_c~16 K, determined from magnetic torque measurements in dc-magnetic fields up to 35 T and at temperatures down to 0.3 K. B_c2 at 0.3 K is obtained to be 26.4 T and 15.5 T for the applied field B_a||ab and B_a||c, respectively. The anisotropy parameter $Γ$=$B_c2^ab / B_c2^c$ is ~ 3 at T_c and decreases to 1.7 as $T \rightarrow 0$, showing rather isotropic superconductivity. While B_c2 is orbitally-limited for B_a||c, the spin-paramagnetic effect is evident in the temperature dependence of B_c2 for B_a||…
Performing the first-principles calculations, we investigate the anisotropy in the superconducting state of iron-based superconductors to gain an insight into their potential applications. The anisotropy ratio $γ_λ$ of the c-axis penetration depth to the ab-plane one is relatively small in BaFe2As2 and LiFeAs, i.e., $γ_λ\sim 3$, indicating that the transport applications are promising in these superconductors. On the other hand, in those having perovskite type blocking layers such as Sr2ScFePO3 we find a very large value, $γ_λ\sim 200$, comparable to that in strongly anisotropic high-Tc cuprat…
We have investigated the temperature-dependence of the upper critical field Hc2(T) in a LiFeAs single crystal by direct measurements of resistivity under static magnetic fields up to 36 T. We find in the case of a magnetic field H along the ab-plane that Hc2ab(0) = 30 T is clearly lower than the orbital limiting field Hc2orb,ab (0) = 39.6 T estimated by the |dHc2ab / dT|Tc, suggesting the presence of both Pauli- and orbital-limiting effects in the pair breaking process. The best fit of Hc2ab(T) to the Werthamer-Helfand-Hohenberg formula results in the Maki parameter α = 0.9 and negligible spin…
Measurements of the temperature and angular dependencies of the upper critical fields $H_{c2}$ of a stoichiometric single crystal LiFeAs in pulsed magnetic fields up to 50 T were performed using a tunnel diode resonator. Full $H^{\parallel c}_{c2}(T)$ and $H^{\bot c}_{c2}(T)$ curves with $H^{\parallel c}_{c2}(0)=17 \pm 1$ T, $H^{\bot c}_{c2}(0)=26 \pm 1$ T, and the anisotropy parameter ${γ_H}(T) \equiv H_{c2}^{\bot c}/H_{c2}^{\parallel c}$ decreasing from $\approx 2.5$ at $T_c$ to 1.5 at $T\ll T_c$ were observed. The results for both orientations are in excellent agreement with a theory of $H_…
We report the growth and properties of epitaxial MgB2 thin films on (0001) Al2O3 substrates. The MgB2 thin films were prepared by depositing boron films via RF magnetron sputtering, followed by a post-deposition anneal at 850C in magnesium vapor. X-ray diffraction and cross-sectional TEM reveal that the epitaxial MgB2 films are oriented with their c-axis normal to the (0001) Al2O3 substrate and a 30 degree rotation in the ab-plane with respect to the substrate. The critical temperature was found to be 35 K and the anisotropy ratio, Hc2(parallel to the film) / Hc2(pendicular to the film), about…
The electronic structure and physical properties of the pnictide compound families $RE$OFeAs ($RE$ = La, Ce, Pr, Nd, Sm), $A$Fe$_{2}$As$_{2}$ ($A$ = Ca, Sr, Ba, Eu), LiFeAs and FeSe are quite similar. Here, we focus on the members of the $A$Fe$_{2}$As$_{2}$ family whose sample composition, quality and single crystal growth are better controllable compared to the other systems. Using first principles band structure calculations we focus on understanding the relationship between the crystal structure, charge doping and magnetism in $A$Fe$_{2}$As$_{2}$ systems. We will elaborate on the tetragonal…
Large single crystals of La-doped CaFe2As2 were successfully synthesized by the FeAs self-flux method. The x-ray diffraction patterns suggest high crystalline quality and c-axis orientation. By substitution of trivalent La3+ ions for divalent Ca2+, the resistivity anomaly in the parent compound CaFe2As2 is completely suppressed and a superconducting transition reaches the value of 42.7 K, which is higher than that of about 30 K reported in Saha S. R. et al., arXiv:1105.4798v1. The upper critical field has been determined with the magnetic field along ab-plane and c-axis, yielding an anisotropy…
The transport and superconducting properties of Ba_{1-x}K_xFe_2As_2 single crystals with T_c = 31 K were studied. Both in-plane and out-of plane resistivity was measured by modified Montgomery method. The in-plane resistivity for all studied samples, obtained in the course of the same synthesis, is almost the same, unlike to the out-of plane resistivity, which differ considerably. We have found that the resistivity anisotropy γ=ρ_c /ρ_{ab} is almost temperature independent and lies in the range 10-30 for different samples. This, probably, indicates on the extrinsic nature of high out-of-plane …
In this article we review our studies of the K0.80Fe1.76Se2 superconductor, with an attempt to elucidate the crystal growth details and basic physical properties over a wide range of temperatures and applied magnetic field, including anisotropic magnetic and electrical transport properties, thermodynamic, London penetration depth, magneto-optical imaging and Mossbauer measurements. We find that: (i) Single crystals of similar stoichiometry can be grown both by furnace-cooled and decanted methods; (ii) Single crystalline K0.80Fe1.76Se2 shows moderate anisotropy in both magnetic susceptibility a…
Superconducting properties under high magnetic fields for the novel BiS2-based layered superconductor LaO0.5F0.5BiS2 (polycrystalline sample prepared using the high-pressure synthesis method) have been investigated. The anisotropy of the upper critical field was discussed by analyzing the temperature dependence of the temperature derivative of resistivity. The temperature dependence of upper critical field showed an anomalous behavior with a characteristic magnetic field of 8 T. We revealed that the anomalous behavior was caused by the existence of three kinds of upper critical field, HC2max, …
We discuss the important aspects of synthesis and crystal growth of MgB2 under high pressure (P) and temperature (T) in Mg-B-N system, including the optimisation of P-T conditions for reproducible crystal growth, the role of liquid phases in this process, the temperature dependence of crystal size and the effect of growing instabilities on single crystals morphology. Extensive experiments have been carried out on single crystals with slightly different lattice constants and defects concentration, which revealed and possible effects of Mg-deficiency and lattice strain on the superconducting pro…
The synthesis, structural and physical properties of iron lanthanide oxypnictide superconductors, L4Fe2As2Te1-xO4 (L = Pr, Sm, Gd), with transition temperature at ~ 25 K are reported. Single crystals have been grown at high pressure using cubic anvil technique. The crystal structure consists of layers of L2O2 tetrahedra separated by alternating layers of chains of Te and of Fe2As2 tetrahedra: -L2O2-Te-L2O2-Fe2As2-L2O2-Te-L2O2- (space group: I4/mmm, a ~ 4.0, c ~ 29.6 Å). Substitution of oxygen by fluorine increases the critical temperature, e.g. in Gd4Fe2As2Te1-xOyF4-y up to 45 K. Magnetic torq…
Polycrystalline samples and single crystals of SmFeAs1-xPxO1-y were synthesized and grown employing different synthesis methods and annealing conditions. Depending on the phosphorus and oxygen content, the samples are either magnetic or superconducting. In the fully oxygenated compounds the main impact of phosphorus substitution is to suppress the Néel temperature TN of the spin density wave (SDW) state, and to strongly reduce the local magnetic field in the SDW state, as deduced from muon spin rotation measurements. On the other hand the superconducting state is observed in the oxygen deficie…