In previous work in undoped MFe2As2, partial drops in the resistivity indicative of traces of superconductivity have been observed in some samples of M=Ba (Tc ~ 20 K, up to 25% drop in resistivity) and M=Ca (Tc ~ 10 K, up to 45 % drop in resistivity.) A complete drop in the resistivity to 0, along with a finite fraction of Meissner flux expulsion, has been observed in M=Sr, Tc = 22 K. Using In-flux grown single crystal samples of undoped BaFe2As2, we find a complete drop in the resistivity to 0 in most samples beginning at Tc(onset) = 22.5 K. However, in contrast to the SrFe2As2 results, there is no measurable Meissner effect and no suppression of the resistive superconducting transition with annealing. The current sensitivity of the superconducting resistive transition in our samples of BaFe2As2 is quite strong, with an increase in the current density of a factor of 15 to ~ 1.5 A/cm2 not changing Tc(onset) but broadening the transition significantly and causing the resistivity to remain finite as T approaches 0. To investigate if this unusually low critical current is indicative of filamentary conduction lacking the apparent anisotropy seen in the critical magnetic field, Hc2, measurements of, e. g., the bulk superconductor Co-doped BaFe2As2, Hc2 was measured in both crystalline directions. These BaFe2As2 samples show Hc2(T) values in the ab-plane and along the c-axis comparable to those seen in BaFe2-xCoxAs2, which has a similar Tc. Since the lack of Tc suppression after annealing argues against strain-induced superconductivity as proposed for the other undoped MFe2As2 materials, another possible cause for the superconductivity in BaFe2As2 is discussed.
Undoped cuprates have long been considered to be antiferromagnetic insulators. In this article, however, we report that superconductivity is achieved in undoped T'-RE2CuO4 (RE = Pr, Nd, Sm, Eu, and Gd). Our discovery was performed by using metal-organic decomposition (MOD), an inexpensive and easy-to-implement thin-film process. The keys to prepare the superconducting films are firing with low partial-pressure of oxygen and reduction at low temperatures. The highest Tc of undoped T'-RE2CuO4 is over 30 K, substantially higher than "electron-doped" analogs. Remarkably, Gd2CuO4, even the derivati…
We have recently achieved superconductivity in undoped T'-RE2CuO4 (RE: Pr, Nd, Sm, Eu, and Gd), using epitaxial thin films by metal organic decomposition. The key recipes to achieve superconductivity are low-PO2 firing and subsequent vacuum reduction to minimize the amount of impurity oxygen atoms, which are very harmful to high-Tc superconductivity. In this article, we report our investigation on the reduction dependence of superconductivity of T'-RE2CuO4. For thin films, the amount of remnant Oap atoms is difficult to evaluate but we propose that one good measure for this may be the c-axis l…
In this article, we report the superconductivity in T'-RE2CuO4 (RE = Pr, Nd, Sm, Eu, and Gd), which have been for a long time believed as a Mott insulator. Our discovery was achieved by using metal-organic decomposition (MOD), an inexpensive and easy-to-implement thin-film process. The keys to prepare the superconducting films are firing with low partial-pressure of oxygen and reduction at low temperatures. The highest Tc of undoped T'-RE2CuO4 is over 30 K, substantially higher than "electron-doped" analogs. Remarkably, Gd2CuO4, even the derivatives of which have not shown superconductivity so…
Fe-based superconductors exhibit a diverse interplay between charge, orbital, and magnetic ordering1-4. Variations in atomic geometry affect electron hopping between Fe atoms5,6 and the Fermi surface topology, influencing magnetic frustration and the pairing mechanism through changes of orbital overlap and occupancies7-11. Here, we experimentally demonstrate a systematic approach to realize superconductivity without chemical doping in BaFe2As2, employing geometric design within an epitaxial heterostructure. We control both tetragonality and orthorhombicity in BaFe2As2 through superlattice engi…
The Meissner effect has been directly demonstrated by depth-resolved muon spin rotation measurements in high-quality thin films of the T'-structured cuprate, T'-La$_{1.9}$Y$_{0.1}$CuO$_4$, to confirm bulk superconductivity ($T_c\simeq21$ K) in its {\sl undoped} state. The gradual expelling of an external magnetic field is observed over a depth range of $\sim$100 nm in films with a thickness of 275(15) nm, from which the penetration depth is deduced to be 466(22) nm. Based on this result, we argue that the true ground state of the "parent" compound of the $n$-type cuprates is not a Mott insulat…
Unlike the widely studied ReFeAsO series, the newly discovered iron-based superconductor ThFeAsN exhibits a remarkably high critical temperature of 30 K, without chemical doping or external pressure. Here we investigate in detail its magnetic and superconducting properties via muon-spin rotation/relaxation ($μ$SR) and nuclear magnetic resonance (NMR) techniques and show that ThFeAsN exhibits strong magnetic fluctuations, suppressed below 35 K, but no magnetic order. This contrasts strongly with the ReFeAsO series, where stoichiometric parent materials order antiferromagnetically and supercondu…
We present a study concerning the partial substitution of yttrium at the lanthanum site of the undoped LaFeAsO and superconducting LaFeAsO0.85F0.15 compounds. We prepared samples with a nominal yttrium content up to 70% producing simultaneous shrinkage of both the a- and c-lattice parameters by 1.8% and 1.7%, respectively. The chemical pressure provided by the partial substitution with this smaller ion size causes a lowering of the spin density wave temperature in the undoped compounds, as well as an increase of the superconducting transition temperatures in the doped ones. The 15% fluorine-do…
Single crystals of undoped CaFe2As2 were grown by a FeAs self-flux method, and the crystals were quenched in ice-water rapidly after high temperature growth. The quenched crystal undergoes a collapsed tetragonal structural phase transition around 80 K revealed by the temperature dependent X-ray diffraction measurements. Superconductivity below 25 K was observed in the collapsed phase by resistivity and magnetization measurements. The isothermal magnetization curve measured at 2 K indicates that this is a typical type-II superconductor. For comparison, we systematically characterized the proper…
Bi2Se3 is one of a handful of known topological insulators. Here we show that copper intercalation in the van der Waals gaps between the Bi2Se3 layers, yielding an electron concentration of ~ 2 x 10^20cm-3, results in superconductivity at 3.8 K in CuxBi2Se3 for x between 0.12 and 0.15. This demonstrates that Cooper pairing is possible in Bi2Se3 at accessible temperatures, with implications for study of the physics of topological insulators and potential devices.
The possibility of superconductivity in doped and undoped triangular antiferromagnets is discussed. Using the Bethe-Salpeter (B-S) equation, it is shown that the exchange of RPA paramagnons on a triangular lattice Hubbard model leads to strong pairing correlations at and near half-filling. The dominant states for this system correspond to d-wave singlet (even-frequency) and s-wave triplet (odd-frequency) pairing. Analytical techniques applied to the hole-doped t-J model yield similar results. A t_1-t_2 Hubbard model interpolating between square (t_1=0) and triangular (t_1=t_2) lattices has a t…
We have investigated the effects of magnetic Ni and nonmagnetic Zn impurities on the superconductivity in undoped T'-La$_{1.8}$Eu$_{0.2}$CuO$_4$ (T'-LECO) with the Nd$_2$CuO$_4$-type structure, using the polycrystalline bulk samples, to clarify the pairing symmetry. It has been found that both suppression rates of the superconducting transition temperature $T_\mathrm{c}$ by Ni and Zn impurities are nearly the same and are very similar to those in the optimally doped and overdoped regimes of hole-doped T-La$_{2-x}$Sr$_{x}$CuO$_4$ with the K$_2$NiF$_4$-type structure. These results strongly sugg…
The iron arsenide RbFe_2As_2 with the ThCr_2Si_2-type structure is found to be a bulk superconductor with T_c=2.6 K. The onset of diamagnetism was used to estimate the upper critical field H_c2(T), resulting in dH_c2/dT=-1.4 T/K and an extrapolated H_c2(0)=2.5 T. As a new representative of iron pnictide superconductors, superconducting RbFe_2As_2 contrasts with BaFe_2As_2, where the Fermi level is higher and a magnetic instability is observed. Thus, the solid solution series (Rb,Ba)Fe_2As_2 is a promising system to study the crossover from superconductivity to magnetism.
In this review article, we show our recent results relating to the undoped (Ce-free) superconductivity in the electron-doped high-Tc cuprates with the so-called T' structure. For an introduction, we briefly mention the characteristics of the electron-doped T'-cuprates, including the reduction annealing, conventional phase diagram and undoped superconductivity. Then, our transport and magnetic results and results relating to the superconducting pairing symmetry of the undoped and underdoped T'-cuprates are shown. Collaborating spectroscopic and nuclear magnetic resonance results are also shown …
We have systematically studied the transport properties of the La$_{2-x}$Y$_{x}$CuO$_{4}$(LYCO) films of T'-phase ($0.05\leq x \leq 0.30$). In this nominally "undoped" system, superconductivity was acquired in certain Y doping range ($0.10\leq x \leq 0.20$). Measurements of resistivity, Hall coefficients in normal states and resistive critical field ($H^ρ_{c2}$)in superconducting states of the T'-LYCO films show the similar behavior as the known Ce-doped n-type cuprate superconductors, indicating the intrinsic electron-doping nature. The charge carriers are induced by oxygen deficiency. Non-su…
The Ca10(PtnAs8)(Fe2As2)5 (n=3,4) compounds are a new type of iron pnictide superconductors whose structures consist of stacking Ca-PtnAs8-Ca-Fe2As2 layers in a unit cell. When n=3 (the 10-3-8 phase), the undoped compound is an antiferromagnetic (AFM) semiconductor, while, when n=4 (the 10-4-8 phase), the undoped compound is a superconductor with the transition temperature of 26K. Here we report the results of high-pressure studies on the 10-3-8 compound obtained through a combination of in-situ resistance, magnetic susceptibility, and Hall coefficient measurements. We find that its AFM order …
Tunneling data on MgB_{1.8}C_{0.2} show a reduction in the energy gap of the pi-bands by a factor of two from undoped MgB2 that is consistent with the Tc reduction, but inconsistent with the expectations of the dirty limit. Dirty-limit theory for undoped MgB2 predicts a single gap about three times larger than measured and a reduced Tc comparable to that measured. Our heavily-doped samples exhibit a uniform dispersion of C suggestive of significantly enhanced scattering, and we conclude that the retention of two-band superconductivity in these samples is caused by a selective suppression of in…
Undoped LaFeAsO, parent compound of the newly found high-Tc superconductor, exhibits a sharp decrease in the temperature-dependent resistivity at ~160 K. The anomaly can be suppressed by F doping and the superconductivity appears correspondingly, suggesting a close associate of the anomaly with the superconductivity. We examined the crystal structures, magnetic properties and superconductivity of undoped (normal conductor) and 14 at.% F-doped LaFeAsO (Tc = 20 K) by synchrotron X-ray diffraction, DC magnetic measurements, and ab initio calculations to demonstrate that the anomaly is associated …
Emergent superconductivity is strongly correlated with the symmetry of local atomic configuration in the parent compounds of iron-based superconductors. While chemical doping or hydrostatic pressure can change the local geometry, these conventional approaches do not provide a clear pathway in tuning the detailed atomic arrangement predictably, due to the parent compounds complicated structural deformation in the presence of the tetragonal-to-orthorhombic phase transition. Here, we demonstrate a systematic approach to manipulate the local structural configurations in BaFe2As2 epitaxial thin fil…
In order to realize superconductivity in cuprates with the T'-type structure, not only chemical substitution (Ce doping) but also post-growth reduction annealing is necessary. In the case of thin films, however, well-designed reduction annealing alone without Ce doping can induce superconductivity in the T'-type cuprates. In order to unveil the origin of superconductivity in the Ce-undoped T'-type cuprates, we have performed bulk-sensitive hard x-ray photoemission and soft x-ray absorption spectroscopies on superconducting and non-superconducting Nd$_{2-x}$Ce$_x$CuO$_4$ ($x=$ 0, 0.15, and 0.19…
We have synthesized a novel europium bismuth sulfofluoride, Eu3Bi2S4F4, by solid-state reactions in sealed evacuated quartz ampoules. The compound crystallizes in a tetragonal lattice (space group I4/mmm, a = 4.0771(1) A, c = 32.4330(6) A, and Z = 2), in which CaF2-type Eu3F4 layers and NaCl-like BiS2 bilayers stack alternately along the crystallographic c axis. There are two crystallographically distinct Eu sites, Eu(1) and Eu(2) at the Wyckoff positions 4e and 2a, respectively. Our bond-valence-sum calculation, based on the refined structural data, indicates that Eu(1) is essentially divalen…
It has been considered that FeAs-based high transition temperature (high-Tc) superconductors need electron or hole doping by aliovalent ion substitution or large off-stoichiometry in order to induce superconductivity. We report that exposure of undoped SrFe2As2 epitaxial thin films to water vapor induces a superconducting transition. These films exhibit a higher onset-Tc (25 K) and larger magnetic field anisotropy than those of cobalt-doped SrFe2As2 epitaxial films, suggesting that the mechanism for the observed superconducting transition differs from that of the aliovalent-ion doped SrFe2As2.…
We have systematically investigated the effect of oxygen nonstoichiometry in a nominally undoped superconductor T'-(La,Y)2CuO4+y. In the experiments, the reduction condition was changed after the sample growth by MBE. The superconductivity is very sensitive to the reduction condition. With systematically increasingly reduced atmospheres, resistivity shows a continuous drop and no discontinuity is observed even until the appearance of superconductivity. The absence of the highly insulating state expected for Mott insulators around y ~ 0 suggests that T'-(La,Y)2CuO4 has intrinsic carriers. The r…
We address what seemed to be a contradiction between the lanthanide series REBa$_2$Cu$_3$O$_y$ (RE123) and the charge-compensated series (Ca$_{x}$La$_{1-x}$)(Ba$_{1.75-x}$La$_{0.25+x} $)Cu$_{3}$O$_{y}$ (CLBLCO) regarding the superexchange ($J$) dependence of the maximum superconductivity (SC) critical temperature $T_c^{max}(J)$; RE and $x$ are implicit variables. This is done by measuring the Néel temperature and the temperature dependence of the magnetic order parameter for RE=Nd, Sm, Eu, Gd, Dy, Yb, Y, and for Y(BaSr)Cu$_3$O$_y$, at various very light dopings. The doping is determined by the…
A review of high-pressure studies on Fe-pnictide superconductors is given. The pressure effects on the magnetic and superconducting transitions are discussed for different classes of doped and undoped FeAs-compounds, ROFeAs (R = rare earth), AeFe2As2 (Ae = Ca, Sr, Ba), and AFeAs (A = Li, Na). Pressure tends to decrease the magnetic transition temperature in the undoped or only slightly doped compounds. The superconducting Tc increases with pressure for underdoped FeAs-pnictides, remains approximately constant for optimal doping, and decreases linearly in the overdoped range. The undoped LaOFeA…
Mapping reservoir-enhanced superconductivity to near-long-range magnetic order in the undoped 1D Anderson- and Kondo-lattices
Heriot-Watt University（赫瑞-瓦特大学）；University of Geneva（日内瓦大学）；Weizmann Institute of Science（魏茨曼科学研究所）；Max-Planck-Institut für Physik komplexer Systeme（马克斯·普朗克复杂系统物理研究所）
Since the discovery of superconductivity\cite{1} at 26 K in oxy-pnictide $LaFeAsO_{1-x}F_x$, enormous interests have been stimulated in the fields of condensed matter physics and material sciences. Among the five different structures in this broad type of superconductors\cite{2,3,4,5,6}, the ZrCuSiAs structure has received special attention since the $T_c$ has been quickly promoted to 55-56 K\cite{7,8,9,10,11} in fluorine doped oxy-pnictides REFeAsO (RE = rare earth elements). The superconductivity can also be induced by applying a high pressure to the undoped samples\cite{12,13}. The mechanis…
The resistivity anisotropy unveiled in the study of detwinned single crystals of the undoped 122 pnictides is here studied using the two-dimensional three-orbital Hubbard model in the mean-field approximation. Calculating the Drude weight in the x and y directions at zero temperature for a Q=(π,0) magnetically ordered state, the conductance along the antiferromagnetic direction is shown to be larger than along the ferromagnetic direction. This effect is caused by the suppression of the d_{yz} orbital at the Fermi surface, but additional insight based on the momentum dependence of the transitio…
We have successfully synthesized one member of LnFeAsO (Ln stands for lanthanides) with Ln=Tb. By partial substitution of Tb$^{3+}$ by Th$^{4+}$, superconductivity with onset $T_{c}$ up to 52 K was observed. In the undoped parent compound, the magnetic moments of Tb$^{3+}$ ions order antiferromagnetically (AFM) at $T_N$ of 2.5 K, and there exists an anomaly in the resistivity at $T^*$ of about 124 K which corresponds to the structural phase transition and/or AFM ordering of magnetic moments of Fe$^{2+}$ ions. This anomaly is severely suppressed by Th doping, similar to the cases of F doped LnF…
Superconductivity is found in 50% K-doped EuFe2As2 sample below 33 K. Our results of electrical resistivity, magnetic susceptibility and 57Fe and 151Eu Mossbauer spectroscopy provide clear evidence that the ordering of the Fe moments observed at 190 K in undoped EuFe2As2 is completely suppressed in our 50% K doped sample, thus there is no coexistence between the Fe magnetic order and the superconducting state. However, short range ordering of the Eu moments is coexisting with the superconducting state below 15 K. A bump in the susceptibility well below Tc as well as a slight broadening of the …
Layered transition-metal chalcogenides (Zr,Hf)GeTe$_{4}$ were screened out from database of Atomwork as a candidate for pressure-induced superconductivity due to their narrow band gap and high density of state near the Fermi level. The (Zr,Hf)GeTe$_{4}$ samples were synthesized in single crystal and then the compositional ratio, crystal structures, and valence states were investigated via energy dispersive spectrometry, single crystal X-ray diffraction, and X-ray photoelectron spectroscopy, respectively. The pressure-induced superconductivity in both crystals were first time reported by using …
We use the momentum space renormalization group to study the influence of phonons and the Coulomb interaction on the superconducting response function of armchair single-walled nanotubes. We do not find superconductivity in undoped single nanotubes. When doped, superconducting fluctuations can develop because of the phonons but remain small and are easily destroyed by the Coulomb interaction. The origin of superconductivity in ropes of nanotobes is most likely an intertube effect. Projections to zig-zag nanotubes indicate a more favorable disposition to superconducting fluctuations.
We measure the superconducting transition of YIn$_3$ by resistivity, susceptibility, and specific heat. Despite using high-quality single-crystal samples, the transitions detected by the three techniques are shifted from each other in temperature, suggesting a region of filamentary superconductivity. We discuss the possible implications for filamentary superconductivity in unconventional superconductors.
The possible ground states of the undoped and doped Kitaev-Heisenberg model on a triangular lattice are studied. For the undoped system, a combination of the numerical exact diagonalization calculation and the four-sublattice transformation analysis suggests one possible exotic phase and four magnetically ordered phases including a collinear stripe pattern and a noncollinear spiral pattern in the global phase diagram. The exotic phase near the antiferromagnetic (AF) Kitaev point is further investigated by using the Schwinger-fermion mean-field method, and we obtain an energetically favorable $…
We have successfully observed quantum oscillation (QO) for FeTe_{1-x}Se_{x}. QO measurements were performed using non-superconducting and superconducting thin crystals of FeTe_{0.65}Se_{0.35} fabricated by the scotch-tape method. We show that the Fermi surfaces (FS) of the non-superconducting crystal are in good agreement with the rigid band shift model based on electron doping by excess Fe while that of the superconducting crystal is in good agreement with the calculated FS with no shift. From the FS comparison of both crystals, we demonstrate the change of the cross-sectional area of the FS,…
We investigate the quasiparticle relaxation and low-energy electronic structure in undoped SmFeAsO and near-optimally doped SmFeAsO_{0.8}F_{0.2} single crystals - exhibiting spin-density wave (SDW) ordering and superconductivity respectively - using pump-probe femtosecond spectroscopy. In the undoped single crystals a single relaxation process is observed, showing a remarkable critical slowing down of the QP relaxation dynamics at the SDW transition temperature T_{SDW}\simeq125{K}. In the superconducting (SC) crystals multiple relaxation processes are present, with distinct SC state quasiparti…
The coupling between superconductivity and othorhombic distortion is studied in vapor-grown FeSe single crystals using high-resolution thermal-expansion measurements. In contrast to the Ba122-based (Ba122) superconductors, we find that superconductivity does not reduce the orthorhombicity below Tc. Instead we find that superconductivity couples strongly to the in-plane area, which explains the large hydrostatic pressure effects. We discuss our results in light of the spinnematic scenario and argue that FeSe has many features quite different from the typical Fe-based superconductors.
We investigated the S-doping-driven phase transition from antiferromagnetic to superconducting in FeTe1-xSx single crystals. The partial substitution of Te by S suppresses antiferromagnetism in Fe-square lattice. Superconductivity is induced by oxygen annealing for only FeTe1-xSx in which the long-range magnetic ordering is suppressed. To realize superconductivity in FeTe1-xSx, both S concentration enough to suppress antiferromagnetism and oxygen annealing are required. Anisotropy of superconductivity in oxygen-annealed FeTe0.886S0.114 was estimated to be 1.17.
We report synthesis of high quality Fe1+y(Te1-xSx)z single crystals and a comprehensive study of structural, magnetic and transport properties. There is high sensitivity to material stoichiometry which includes vacancies on the Te(S) site. Our results reveal competition and coexistence of magnetic order and percolative superconductivity for x >= 0.03, while zero resistivity is acheived for x >= 0.1.
Spin-triplet superconductivity is known to be a rare quantum phenomenon. Here we show that nonsymmorphic crystalline symmetries can dramatically assist spin-triplet superconductivity in the presence of spin-orbit coupling. Even with a weak spin-orbit coupling, the spin-triplet pairing can be the leading pairing instability in a lattice with a nonsymmorphic symmetry. The underlining mechanism is the spin-sublattice-momentum lock on electronic bands that are protected by the nonsymmorphic symmetry. We use the nonsymmorphic space group P4/nmm to demonstrate these results and discuss related exper…
We measured phonon frequencies and linewidths in doped and undoped BaFe2As2 single crystals by inelastic x-ray scattering and compared our results with density functional theory (DFT) calculations. In agreement with previous work, the calculated frequencies of some phonons depended on whether the ground state was magnetic or not and, in the former case, whether phonon wavevector was parallel or perpendicular to the magnetic ordering wavevector. The experimental results agreed better with the magnetic calculation than with zero Fe moment calculations, except the peak splitting expected due to m…
High-resolution and high-flux neutron as well as X-ray powder-diffraction experiments were performed on the oxypnictide series LaO(1-x)FxFeAs with 0<x<0.15 in order to study the crystal and magnetic structure. The magnetic symmetry of the undoped compound corresponds to those reported for ReOFeAs (with Re a rare earth) and for AFe2As2 (A=Ba, Sr) materials. We find an ordered magnetic moment of 0.63(1)muB at 2 K in LaOFeAs, which is significantly larger than the values previously reported for this compound. A sizable ordered magnetic moment is observed up to a F-doping of 4.5% whereas there is …
Resistivity, magnetic susceptibility and heat capacity measurements are reported for single crystals of Fe1+yTexSe1-x grown via a modified Bridgeman method with 0 < y < 0.15, and x= 1, 0.9, 0.75, 0. 67, 0.55 and 0.5. Although resistivity measurements show traces of superconductivity near 14 K for all x except x=1, only crystals grown with compositions near x=0.5 exhibit bulk superconductivity. The appearance of bulk superconductivity correlates with a reduction in the magnitude of the magnetic susceptibility at room temperature and smaller values of y, the concentration of Fe in the Fe(2) site…
Symmetry of the crystal lattice can be a determining factor for the structure of Cooper pairs in unconventional superconductors. In this study we extend the discussion of superconductivity in non-centrosymmetric materials to the case when inversion symmetry is missing locally, but is present on a global level. Concretely, we investigate the staggered non-centrosymmetricity within a regular sublattice structure, in some analogy to the discussion of superconductivity in antiferromagnetic systems. Three crystal structures are analyzed in detail as illustrative examples for the extended classifica…
The effect of vacuum annealing on superconductivity is investigated in Fe(Se,Te) single crystals. It is found that superconductivity is not enhanced by annealing under high vacuum (~ 10^(-3) Pa) or by annealing in a sealed evacuated quartz tube. In a moderate vacuum atmosphere (~ 1 Pa), iron oxide layers are found to show up on sample surfaces, which would draw excess Fe out of the crystal. Thus, it is suggested that remanent oxygen effectively works to remove excess Fe from the matrix of Fe(Se,Te) crystals, resulting improvement of superconducting transition temperature. Our transport measure…
The effect of Co doping on supercoductivity of FeSe$_{0.4}$Te$_{0.6}$ single crystals is investigated. The superconducting transition temperature decreases linearly for Co doping with the rate -0.75 K/(Co %). On the other hand, the residual resistivity increase is less than 50 $/mu/Omega$cm for 4 % Co doping. These data are consistent with the sign changing interband scattering mechanism of superconductivity ($s_/pm$ symmetry).
Single crystals FeSe_x have been grown in evacuated sealed quartz tube using a NaCl/KCl flux. The products include two crystal structures of tetragon and hexagon. The electronic transport and magnetic properties measurements of FeSe_x single crystal exhibits a superconducting transition at about 10K.
We investigate properties of BaFe2As2 (122) single crystals upon gold doping, which is the transition metal with the highest atomic weight. The Au substitution into the FeAs-planes of 122 crystal structure (Au-122) is only possible up to a small amount of ~3%. We find that 5d is more effective in reducing magnetism in 122 than its counter 3d Cu, and this relates to superconductivity. We provide evidence of short-range magnetic fluctuations and local-lattice inhomogeneities that may prevent strong percolative superconductivity in Ba(Fe1-xAux)2As2.
Resistivity, Hall effect and magnetoresistance have been investigated systematically on single crystals of Ba$_{1-x}$K$_x$Fe$_2$As$_2$ ranging from undoped to optimally doped regions. A systematic evolution of the quasiparticle scattering has been observed. It is found that the resistivity in the normal state of Ba$_{1-x}$K$_x$Fe$_2$As$_2$ is insensitive to the potassium doping concentration, which is very different from the electron doped counterpart Ba(Fe$_{1-x}$Co$_{x}$)$_{2}$As$_{2}$, where the resistivity at 300 K reduces to half value of the undoped one when the system is optimally doped…
The evolution of pressure induced superconductivity in single crystal as well as polycrystalline samples of BaFe2As2 has been investigated through temperature dependent electrical resistivity studies in 0-7 GPa pressure range. While the superconducting transition remains incomplete in polycrystalline sample, a clear pressure induced superconductivity with zero resistivity at the expense of magnetic transition, associated with spin density wave (SDW), is observed in the single crystal sample. The superconducting transition temperature (TC) is seen to increase upto a moderate pressure of about ~…
Superconductivity was recently found in the simple tetragonal FeSe structure. Recent studies suggest that FeSe is unconventional, with the symmetry of the superconducting pairing state still under debate. To tackle these problems, clean single crystals and thin films are required. Here we report the fabrication of superconducting beta-phase FeSe1-x thin films on different substrates using a pulsed laser deposition (PLD) technique. Quite interestingly, the crystal orientation, and thus, superconductivity in these thin films is sensitive to the growth temperature. At 320C, films grow preferably …
High transition temperature (high-Tc) superconductivity is associated with layered crystal structures. This work considers superconductivity in ultra-thin crystals (of thickness equal to the transverse structural periodicity distance d for one formula unit) of thirty-two cuprate, ruthenate, rutheno-cuprate, iron pnictide, organic, and transuranic compounds, wherein intrinsic optimal (highest) transition temperatures Tc0 (10 - 150 K) are assumed. Sheet transition temperatures Tcs = αTc0, where α < 1, are determined from Kosterlitz-Thouless (KT) theory of phase transitions in two-dimensional sup…
The investigation of the temperature dependences of microwave surface impedance and complex conductivity of V3Si single crystals with different stoichiometry allowed to observe a number of peculiarities which are in remarkable contradiction with single-gap Bardeen-Cooper-Schrieffer theory. At the same time, they can be well described by two-band model of superconductivity, thus strongly evidencing the existence of two distinct energy gaps with zero-temperature values Delta1~1.8Tc and Delta2~0.95Tc in V3Si.
We report the evolution of superconductivity and the phase diagram of the KxFe2-ySe2-zTez (z=0-0.6) crystals grown by a simple one-step synthesis. No structural transition is observed in any crystals, while lattice parameters exhibit a systematic expansion with Te content. The Tc exhibits a gradual decrease with increasing Te content from Tconset = 32.9 K at z = 0 to Tconset = 27.9 K at z = 0.5, followed by a sudden suppression of superconductivity at z = 0.6. Upon approaching a Te concentration of 0.6, the shielding volume fraction decreases and eventually drops to zero. Simultaneously, hump …
We investigated chemical pressure effects in electron-doped (e-doped) FeSe by fabricating an electric-double-layer structure with single crystalline FeSe films on LaAlO$_3$ with Se substituted by isovalent Te and S. Our method enables transport measurements of e-doped FeSe. Electron doping by applying gate voltage of 5 V increases $T_{\mathrm c}$ of the FeSe$_{1-x}$Te$_x$ and FeSe$_{1-y}$S$_y$ films with $0 \leq x \leq 0.4$ and $0 \leq y \leq 0.25$, while the e-doped $x=0.5$ film showed lower $T_{\mathrm c}$ than that of the undoped one. Both positive and chemical pressure suppress $T_{\mathrm…
Iron selenide (FeSex) crystals with lateral dimensions up to millimeters were grown via a vapor self-transport method. The crystals consist of the dominant alpha - phase with trace amounts of beta- phase as identified by powder x-ray diffraction. With four-probe resistance measurements we obtained a zero-resistance critical temperature of 7.5 K and a superconducting onset transition temperature of up to 11.8 K in zero magnetic field as well as an anisotropy of 1.5 +- 0.1 for the critical field. Magnetization measurements on individual crystals reveal the co-existence of superconductivity and f…
In elemental metals the pairing of electrons leading to superconductivity is mediated by the vibrations of the crystal lattice and the pairs have spherical symmetry. For layered organic molecular crystals there is no consensus about the pairing symmetry or the mechanism of the superconductivity. We show theoretically that the mechanism of superconductivity for members of the (BEDT-TTF)2X family with the theta and beta'' crystal structures is mediated by charge fluctuations and the superconducting order parameter has dxy symmetry. This is in contrast to the kappa-(BEDT-TTF)2X family, for which …