In this article, we report the superconductivity in T'-RE2CuO4 (RE = Pr, Nd, Sm, Eu, and Gd), which have been for a long time believed as a Mott insulator. Our discovery was achieved by using metal-organic decomposition (MOD), an inexpensive and easy-to-implement thin-film process. The keys to prepare the superconducting films are firing with low partial-pressure of oxygen and reduction at low temperatures. The highest Tc of undoped T'-RE2CuO4 is over 30 K, substantially higher than "electron-doped" analogs. Remarkably, Gd2CuO4, even the derivatives of which have not shown superconductivity so far, gets superconducting with Tconset as high as 20 K. The implication of our discovery is briefly discussed.
Undoped cuprates have long been considered to be antiferromagnetic insulators. In this article, however, we report that superconductivity is achieved in undoped T'-RE2CuO4 (RE = Pr, Nd, Sm, Eu, and Gd). Our discovery was performed by using metal-organic decomposition (MOD), an inexpensive and easy-to-implement thin-film process. The keys to prepare the superconducting films are firing with low partial-pressure of oxygen and reduction at low temperatures. The highest Tc of undoped T'-RE2CuO4 is over 30 K, substantially higher than "electron-doped" analogs. Remarkably, Gd2CuO4, even the derivati…
We have recently achieved superconductivity in undoped T'-RE2CuO4 (RE: Pr, Nd, Sm, Eu, and Gd), using epitaxial thin films by metal organic decomposition. The key recipes to achieve superconductivity are low-PO2 firing and subsequent vacuum reduction to minimize the amount of impurity oxygen atoms, which are very harmful to high-Tc superconductivity. In this article, we report our investigation on the reduction dependence of superconductivity of T'-RE2CuO4. For thin films, the amount of remnant Oap atoms is difficult to evaluate but we propose that one good measure for this may be the c-axis l…
Fe-based superconductors exhibit a diverse interplay between charge, orbital, and magnetic ordering1-4. Variations in atomic geometry affect electron hopping between Fe atoms5,6 and the Fermi surface topology, influencing magnetic frustration and the pairing mechanism through changes of orbital overlap and occupancies7-11. Here, we experimentally demonstrate a systematic approach to realize superconductivity without chemical doping in BaFe2As2, employing geometric design within an epitaxial heterostructure. We control both tetragonality and orthorhombicity in BaFe2As2 through superlattice engi…
The Meissner effect has been directly demonstrated by depth-resolved muon spin rotation measurements in high-quality thin films of the T'-structured cuprate, T'-La$_{1.9}$Y$_{0.1}$CuO$_4$, to confirm bulk superconductivity ($T_c\simeq21$ K) in its {\sl undoped} state. The gradual expelling of an external magnetic field is observed over a depth range of $\sim$100 nm in films with a thickness of 275(15) nm, from which the penetration depth is deduced to be 466(22) nm. Based on this result, we argue that the true ground state of the "parent" compound of the $n$-type cuprates is not a Mott insulat…
Unlike the widely studied ReFeAsO series, the newly discovered iron-based superconductor ThFeAsN exhibits a remarkably high critical temperature of 30 K, without chemical doping or external pressure. Here we investigate in detail its magnetic and superconducting properties via muon-spin rotation/relaxation ($μ$SR) and nuclear magnetic resonance (NMR) techniques and show that ThFeAsN exhibits strong magnetic fluctuations, suppressed below 35 K, but no magnetic order. This contrasts strongly with the ReFeAsO series, where stoichiometric parent materials order antiferromagnetically and supercondu…
We present a study concerning the partial substitution of yttrium at the lanthanum site of the undoped LaFeAsO and superconducting LaFeAsO0.85F0.15 compounds. We prepared samples with a nominal yttrium content up to 70% producing simultaneous shrinkage of both the a- and c-lattice parameters by 1.8% and 1.7%, respectively. The chemical pressure provided by the partial substitution with this smaller ion size causes a lowering of the spin density wave temperature in the undoped compounds, as well as an increase of the superconducting transition temperatures in the doped ones. The 15% fluorine-do…
In previous work in undoped MFe2As2, partial drops in the resistivity indicative of traces of superconductivity have been observed in some samples of M=Ba (Tc ~ 20 K, up to 25% drop in resistivity) and M=Ca (Tc ~ 10 K, up to 45 % drop in resistivity.) A complete drop in the resistivity to 0, along with a finite fraction of Meissner flux expulsion, has been observed in M=Sr, Tc = 22 K. Using In-flux grown single crystal samples of undoped BaFe2As2, we find a complete drop in the resistivity to 0 in most samples beginning at Tc(onset) = 22.5 K. However, in contrast to the SrFe2As2 results, there…
Single crystals of undoped CaFe2As2 were grown by a FeAs self-flux method, and the crystals were quenched in ice-water rapidly after high temperature growth. The quenched crystal undergoes a collapsed tetragonal structural phase transition around 80 K revealed by the temperature dependent X-ray diffraction measurements. Superconductivity below 25 K was observed in the collapsed phase by resistivity and magnetization measurements. The isothermal magnetization curve measured at 2 K indicates that this is a typical type-II superconductor. For comparison, we systematically characterized the proper…
Bi2Se3 is one of a handful of known topological insulators. Here we show that copper intercalation in the van der Waals gaps between the Bi2Se3 layers, yielding an electron concentration of ~ 2 x 10^20cm-3, results in superconductivity at 3.8 K in CuxBi2Se3 for x between 0.12 and 0.15. This demonstrates that Cooper pairing is possible in Bi2Se3 at accessible temperatures, with implications for study of the physics of topological insulators and potential devices.
The possibility of superconductivity in doped and undoped triangular antiferromagnets is discussed. Using the Bethe-Salpeter (B-S) equation, it is shown that the exchange of RPA paramagnons on a triangular lattice Hubbard model leads to strong pairing correlations at and near half-filling. The dominant states for this system correspond to d-wave singlet (even-frequency) and s-wave triplet (odd-frequency) pairing. Analytical techniques applied to the hole-doped t-J model yield similar results. A t_1-t_2 Hubbard model interpolating between square (t_1=0) and triangular (t_1=t_2) lattices has a t…
We have investigated the effects of magnetic Ni and nonmagnetic Zn impurities on the superconductivity in undoped T'-La$_{1.8}$Eu$_{0.2}$CuO$_4$ (T'-LECO) with the Nd$_2$CuO$_4$-type structure, using the polycrystalline bulk samples, to clarify the pairing symmetry. It has been found that both suppression rates of the superconducting transition temperature $T_\mathrm{c}$ by Ni and Zn impurities are nearly the same and are very similar to those in the optimally doped and overdoped regimes of hole-doped T-La$_{2-x}$Sr$_{x}$CuO$_4$ with the K$_2$NiF$_4$-type structure. These results strongly sugg…
The iron arsenide RbFe_2As_2 with the ThCr_2Si_2-type structure is found to be a bulk superconductor with T_c=2.6 K. The onset of diamagnetism was used to estimate the upper critical field H_c2(T), resulting in dH_c2/dT=-1.4 T/K and an extrapolated H_c2(0)=2.5 T. As a new representative of iron pnictide superconductors, superconducting RbFe_2As_2 contrasts with BaFe_2As_2, where the Fermi level is higher and a magnetic instability is observed. Thus, the solid solution series (Rb,Ba)Fe_2As_2 is a promising system to study the crossover from superconductivity to magnetism.
In this review article, we show our recent results relating to the undoped (Ce-free) superconductivity in the electron-doped high-Tc cuprates with the so-called T' structure. For an introduction, we briefly mention the characteristics of the electron-doped T'-cuprates, including the reduction annealing, conventional phase diagram and undoped superconductivity. Then, our transport and magnetic results and results relating to the superconducting pairing symmetry of the undoped and underdoped T'-cuprates are shown. Collaborating spectroscopic and nuclear magnetic resonance results are also shown …
We have systematically studied the transport properties of the La$_{2-x}$Y$_{x}$CuO$_{4}$(LYCO) films of T'-phase ($0.05\leq x \leq 0.30$). In this nominally "undoped" system, superconductivity was acquired in certain Y doping range ($0.10\leq x \leq 0.20$). Measurements of resistivity, Hall coefficients in normal states and resistive critical field ($H^ρ_{c2}$)in superconducting states of the T'-LYCO films show the similar behavior as the known Ce-doped n-type cuprate superconductors, indicating the intrinsic electron-doping nature. The charge carriers are induced by oxygen deficiency. Non-su…
The Ca10(PtnAs8)(Fe2As2)5 (n=3,4) compounds are a new type of iron pnictide superconductors whose structures consist of stacking Ca-PtnAs8-Ca-Fe2As2 layers in a unit cell. When n=3 (the 10-3-8 phase), the undoped compound is an antiferromagnetic (AFM) semiconductor, while, when n=4 (the 10-4-8 phase), the undoped compound is a superconductor with the transition temperature of 26K. Here we report the results of high-pressure studies on the 10-3-8 compound obtained through a combination of in-situ resistance, magnetic susceptibility, and Hall coefficient measurements. We find that its AFM order …
Tunneling data on MgB_{1.8}C_{0.2} show a reduction in the energy gap of the pi-bands by a factor of two from undoped MgB2 that is consistent with the Tc reduction, but inconsistent with the expectations of the dirty limit. Dirty-limit theory for undoped MgB2 predicts a single gap about three times larger than measured and a reduced Tc comparable to that measured. Our heavily-doped samples exhibit a uniform dispersion of C suggestive of significantly enhanced scattering, and we conclude that the retention of two-band superconductivity in these samples is caused by a selective suppression of in…
Undoped LaFeAsO, parent compound of the newly found high-Tc superconductor, exhibits a sharp decrease in the temperature-dependent resistivity at ~160 K. The anomaly can be suppressed by F doping and the superconductivity appears correspondingly, suggesting a close associate of the anomaly with the superconductivity. We examined the crystal structures, magnetic properties and superconductivity of undoped (normal conductor) and 14 at.% F-doped LaFeAsO (Tc = 20 K) by synchrotron X-ray diffraction, DC magnetic measurements, and ab initio calculations to demonstrate that the anomaly is associated …
Emergent superconductivity is strongly correlated with the symmetry of local atomic configuration in the parent compounds of iron-based superconductors. While chemical doping or hydrostatic pressure can change the local geometry, these conventional approaches do not provide a clear pathway in tuning the detailed atomic arrangement predictably, due to the parent compounds complicated structural deformation in the presence of the tetragonal-to-orthorhombic phase transition. Here, we demonstrate a systematic approach to manipulate the local structural configurations in BaFe2As2 epitaxial thin fil…
It is shown that charge ordering in layered crystalline metals causes an increase in the normal state energy of the conducting layers. If this increase in the energy exceeds the difference between the superconducting state energy and the normal state energy of the metal, then the superconducting transition occurs. A relation between the charge gap in the superconducting phase and the bandgap width in the undoped insulating phase of high-temperature superconductors is obtained.
In order to realize superconductivity in cuprates with the T'-type structure, not only chemical substitution (Ce doping) but also post-growth reduction annealing is necessary. In the case of thin films, however, well-designed reduction annealing alone without Ce doping can induce superconductivity in the T'-type cuprates. In order to unveil the origin of superconductivity in the Ce-undoped T'-type cuprates, we have performed bulk-sensitive hard x-ray photoemission and soft x-ray absorption spectroscopies on superconducting and non-superconducting Nd$_{2-x}$Ce$_x$CuO$_4$ ($x=$ 0, 0.15, and 0.19…
We have synthesized a novel europium bismuth sulfofluoride, Eu3Bi2S4F4, by solid-state reactions in sealed evacuated quartz ampoules. The compound crystallizes in a tetragonal lattice (space group I4/mmm, a = 4.0771(1) A, c = 32.4330(6) A, and Z = 2), in which CaF2-type Eu3F4 layers and NaCl-like BiS2 bilayers stack alternately along the crystallographic c axis. There are two crystallographically distinct Eu sites, Eu(1) and Eu(2) at the Wyckoff positions 4e and 2a, respectively. Our bond-valence-sum calculation, based on the refined structural data, indicates that Eu(1) is essentially divalen…
It has been considered that FeAs-based high transition temperature (high-Tc) superconductors need electron or hole doping by aliovalent ion substitution or large off-stoichiometry in order to induce superconductivity. We report that exposure of undoped SrFe2As2 epitaxial thin films to water vapor induces a superconducting transition. These films exhibit a higher onset-Tc (25 K) and larger magnetic field anisotropy than those of cobalt-doped SrFe2As2 epitaxial films, suggesting that the mechanism for the observed superconducting transition differs from that of the aliovalent-ion doped SrFe2As2.…
A theoretical analysis is presented on possible effects of disorder by dopants in high-temperature superconducting cuprate perovskites, to define their basic spectra of spin and electronic excitations, and the subsequent observable properties, especially doping dependence of superconducting order parameter. The central point in the proposed physical picture is formation of specific impurity subband within the insulating bandgap of initial undoped material, serving as a source for the system metallization and further transition into superconducting state with anisotropic order parameter.
With the discovery of Tc s over 100K, continuously biased hole-doped semiconductive C60+y has joined the family of high-temperature superconductors (HTSC) previously dominated by the ceramic cuprates. The phase diagrams of these two quite different materials are remarkably similar, despite the absence from undoped C60+y of magnetic order. This supports percolative models of HTSC based on strong electron-phonon interactions. These models explain observed fine structure in the C60+y phase diagrams, and furthermore suggest novel paths to still higher Tc s.
A review of high-pressure studies on Fe-pnictide superconductors is given. The pressure effects on the magnetic and superconducting transitions are discussed for different classes of doped and undoped FeAs-compounds, ROFeAs (R = rare earth), AeFe2As2 (Ae = Ca, Sr, Ba), and AFeAs (A = Li, Na). Pressure tends to decrease the magnetic transition temperature in the undoped or only slightly doped compounds. The superconducting Tc increases with pressure for underdoped FeAs-pnictides, remains approximately constant for optimal doping, and decreases linearly in the overdoped range. The undoped LaOFeA…
Mapping reservoir-enhanced superconductivity to near-long-range magnetic order in the undoped 1D Anderson- and Kondo-lattices
Heriot-Watt University（赫瑞-瓦特大学）；University of Geneva（日内瓦大学）；Weizmann Institute of Science（魏茨曼科学研究所）；Max-Planck-Institut für Physik komplexer Systeme（马克斯·普朗克复杂系统物理研究所）
Since the discovery of superconductivity\cite{1} at 26 K in oxy-pnictide $LaFeAsO_{1-x}F_x$, enormous interests have been stimulated in the fields of condensed matter physics and material sciences. Among the five different structures in this broad type of superconductors\cite{2,3,4,5,6}, the ZrCuSiAs structure has received special attention since the $T_c$ has been quickly promoted to 55-56 K\cite{7,8,9,10,11} in fluorine doped oxy-pnictides REFeAsO (RE = rare earth elements). The superconductivity can also be induced by applying a high pressure to the undoped samples\cite{12,13}. The mechanis…
We have successfully synthesized one member of LnFeAsO (Ln stands for lanthanides) with Ln=Tb. By partial substitution of Tb$^{3+}$ by Th$^{4+}$, superconductivity with onset $T_{c}$ up to 52 K was observed. In the undoped parent compound, the magnetic moments of Tb$^{3+}$ ions order antiferromagnetically (AFM) at $T_N$ of 2.5 K, and there exists an anomaly in the resistivity at $T^*$ of about 124 K which corresponds to the structural phase transition and/or AFM ordering of magnetic moments of Fe$^{2+}$ ions. This anomaly is severely suppressed by Th doping, similar to the cases of F doped LnF…
Superconductivity is found in 50% K-doped EuFe2As2 sample below 33 K. Our results of electrical resistivity, magnetic susceptibility and 57Fe and 151Eu Mossbauer spectroscopy provide clear evidence that the ordering of the Fe moments observed at 190 K in undoped EuFe2As2 is completely suppressed in our 50% K doped sample, thus there is no coexistence between the Fe magnetic order and the superconducting state. However, short range ordering of the Eu moments is coexisting with the superconducting state below 15 K. A bump in the susceptibility well below Tc as well as a slight broadening of the …
High-critical-temperature (Tc) superconductivity at 48 K is reported for hydrogen-doped SmFeAsO epitaxial films on MgO single-crystal substrates. The key processes are pulsed laser deposition to grow undoped SmFeAsO epitaxial films and subsequent topotactic chemical reaction using CaH2 powders under evacuated silica-glass ampule atmosphere. Based on this post-deposition thermal annealing treatment that we have developed, a maximum hydrogen concentration x = ~0.35 was realized in SmFeAs(O1-xHx). Disordered hydrogen-substitution at O sites is experimentally confirmed directly by atomic-scale mic…
We systematically investigated the superconducting properties and the interplay between charge-density-waves (CDW) and superconductivity in lithium-intercalated 2H-TaS2. By gradually increasing the lithium content x, the CDW formation temperature is continuously suppressed, and the onset temperature of superconductivity is increased with a maximum transition temperature Tc = 3.5 K for x = 0.096. The bulk nature of superconductivity is confirmed by a superconducting shielding fraction of the order of unity for this composition. The electronic contribution to the specific heat and Hall resistivi…
We use the momentum space renormalization group to study the influence of phonons and the Coulomb interaction on the superconducting response function of armchair single-walled nanotubes. We do not find superconductivity in undoped single nanotubes. When doped, superconducting fluctuations can develop because of the phonons but remain small and are easily destroyed by the Coulomb interaction. The origin of superconductivity in ropes of nanotobes is most likely an intertube effect. Projections to zig-zag nanotubes indicate a more favorable disposition to superconducting fluctuations.
The possible ground states of the undoped and doped Kitaev-Heisenberg model on a triangular lattice are studied. For the undoped system, a combination of the numerical exact diagonalization calculation and the four-sublattice transformation analysis suggests one possible exotic phase and four magnetically ordered phases including a collinear stripe pattern and a noncollinear spiral pattern in the global phase diagram. The exotic phase near the antiferromagnetic (AF) Kitaev point is further investigated by using the Schwinger-fermion mean-field method, and we obtain an energetically favorable $…
We investigated chemical pressure effects in electron-doped (e-doped) FeSe by fabricating an electric-double-layer structure with single crystalline FeSe films on LaAlO$_3$ with Se substituted by isovalent Te and S. Our method enables transport measurements of e-doped FeSe. Electron doping by applying gate voltage of 5 V increases $T_{\mathrm c}$ of the FeSe$_{1-x}$Te$_x$ and FeSe$_{1-y}$S$_y$ films with $0 \leq x \leq 0.4$ and $0 \leq y \leq 0.25$, while the e-doped $x=0.5$ film showed lower $T_{\mathrm c}$ than that of the undoped one. Both positive and chemical pressure suppress $T_{\mathrm…
RbFe2As2 has recently been reported to be a bulk superconductor with Tc = 2.6 K in the undoped state, in contrast to undoped BaFe2As2 with a magnetic ground state. We present here the results of the first-principles calculations of the structural, elastic and electronic properties for this newest superconductor and discuss its behaviour in relation to other related systems. Keywords: RbFe2As2, Electronic structure; Elastic constant; Superconductivity. PACS: 74.70.Dd, 74.10.+v, 74.20.Pq, 75.25.Ld
Resistivity, Hall effect and magnetoresistance have been investigated systematically on single crystals of Ba$_{1-x}$K$_x$Fe$_2$As$_2$ ranging from undoped to optimally doped regions. A systematic evolution of the quasiparticle scattering has been observed. It is found that the resistivity in the normal state of Ba$_{1-x}$K$_x$Fe$_2$As$_2$ is insensitive to the potassium doping concentration, which is very different from the electron doped counterpart Ba(Fe$_{1-x}$Co$_{x}$)$_{2}$As$_{2}$, where the resistivity at 300 K reduces to half value of the undoped one when the system is optimally doped…
We report the characterization of layered, 2H-type CuxTaS2, for x between 0 and 0.12. The charge density wave (CDW), at 70 K for TaS2, is destabilized with Cu doping. The sub-1K superconducting transition in undoped 2H-TaS2 jumps quickly to 2.5 K at low x, increases to 4.5 K at the optimal composition Cu0.04TaS2, and then decreases at higher x. The electronic contribution to the specific heat, first increasing and then decreasing as a function of Cu content, is 12 mJ mol-1 K-2 at Cu0.04TaS2. Electron diffraction studies show that the CDW remains present at the optimal superconducting compositi…
The superconductivity of the 4-angstrom single-walled carbon nanotubes (SWCNTs) was discovered more than a decade ago, and marked the breakthrough of finding superconductivity in pure elemental undoped carbon compounds. The van Hove singularities in the electronic density of states at the Fermi level in combination with a large Debye temperature of the SWCNTs are expected to cause an impressively large superconducting gap. We have developed an innovative computational algorithm specially tailored for the investigation of superconductivity in ultrathin SWCNTs. We predict the superconducting tra…
The discovery of superconducting materials has led to their use in technological marvels such as magnetic-field sensors in MRI machines, powerful research magnets, short transmission cables, and high-speed trains. Despite such applications, the uses of superconductors are not widespread because they function much below room-temperature, hence the costly cooling. Since the discovery of Cu- and Fe-based high-temperature superconductors (HTS), much intense effort has tried to explain and understand the superconducting phenomenon. While no exact explanations are given, several trends are reported …
We have carried out detailed magnetic and transport studies of the new Sr0.5Ce0.5FBiS2-xSex (x = 0.5, 1) superconductors derived by doping Se in Sr0.5Ce0.5FBiS2. Se-doping produces several effects: it suppresses semiconducting like behavior observed in the undoped Sr0.5Ce0.5FBiS2, ferromagnetic ordering temperature, TFM, decreases considerably from 7.5 K (in Sr0.5Ce0.5FBiS2) to 3.5 K and superconducting transition temperature, Tc, gets enhanced slightly to 2.9 - 3.3 K. Thus in these Se-doped materials, TFM is just marginally higher than Tc. Magnetization studies provide an evidence of bulk sup…
We investigate theoretically the superconducting state of the undoped Fe-based superconductor ThFeAsN. Using input from $ab~initio$ calculations, we solve the Fermi-surface based, multichannel Eliashberg equations for Cooper-pair formation mediated by spin and charge fluctuations, and by the electron-phonon interaction (EPI). Our results reveal that spin fluctuations alone, when coupling only hole-like with electron-like energy bands, can account for a critical temperature $T_c$ up to $\sim7.5\,\mathrm{K}$ with an $s_{\pm}$-wave superconducting gap symmetry, which is a comparatively low $T_c$ …
The origin of unconventional superconductivity and its relationship to a T=0 K continuous quantum phase transition (a quantum critical point, QCP), which is hidden inside the dome of a superconducting state, have long been an outstanding puzzle in correlated superconductors. The observation and tuning of the hidden QCP, which is critical in resolving the mystery, however, has been rarely reported due to lack of ideal systems. The helical antiferromagnet CrAs provides an example in which a dome of superconductivity appears at a pressure where its magnetic transition goes to zero temperature. He…
Strontium titanate is a low-temperature, non-Bardeen-Cooper-Schrieffer superconductor that superconducts to carrier concentrations lower than in any other system and exhibits avoided ferroelectricity at low temperatures. Neither the mechanism of superconductivity in strontium titanate nor the importance of the structure and dielectric properties for the superconductivity are well understood. We studied the effects of twin structure on superconductivity in a 5.5-nm-thick layer of niobium-doped SrTiO$_{3}$ embedded in undoped SrTiO$_{3}$. We used a scanning superconducting quantum interference d…
We derive an effective Hamiltonian for spin polarons forming in weakly doped antiferromagnets and demonstrate that the system becomes superconducting at finite doping. We argue that the driving mechanism which gives rise to superconductivity is lowering of the kinetic energy by formation of mobile antiferromagnetic spin bipolarons. That source of attraction between holes is by definition effective if the antiferromagnetic correlation length is longer than the radius of forming polarons. Notwithstanding that the attraction is strongest in the undoped system with long range order, the supercondu…
We demonstrate that Mn-doping in the layered sulfides Bi_4O_4S_3 leads to stable Bi_4-x Mn_x O_4 S_3 compounds that exhibit both long-range ferromagnetism and enhanced superconductivity for 0.075 < = x < = 0.15, with a possible record superconducting transition temperature (T_c) = 15 K among all BiS_2-based superconductors. We conjecture that the coexistence of superconductivity and ferromagnetism may be attributed to Mn-doping in the spacer Bi2O2 layers away from the superconducting BiS_2 layers, whereas the enhancement of T_c may be due to excess electron transfer to BiS_2 from the Mn4+/Mn3+…
We investigate the possibility of multi-band superconductivity in SrTiO$_{3}$ films and interfaces using a two-dimensional two-band model. In the undoped compound, one of the bands is occupied whereas the other is empty. As the chemical potential shifts due to doping by negative charge carriers or application of an electric field, the second band becomes occupied, giving rise to a strong enhancement of the transition temperature and a sharp feature in the gap functions, which is manifested in the local density of states spectrum. By comparing our results with tunneling experiments in Nb-doped …
The discovery of a new family of high Tc materials, the iron arsenides (FeAs), has led to a resurgence of interest in superconductivity. Several important traits of these materials are now apparent, for example, layers of iron tetrahedrally coordinated by arsenic are crucial structural ingredients. It is also now well established that the parent non-superconducting phases are itinerant magnets, and that superconductivity can be induced by either chemical substitution or application of pressure, in sharp contrast to the cuprate family of materials. The structure and properties of chemically sub…
We investigate the quasiparticle relaxation and low-energy electronic structure in undoped SmFeAsO and near-optimally doped SmFeAsO_{0.8}F_{0.2} single crystals - exhibiting spin-density wave (SDW) ordering and superconductivity respectively - using pump-probe femtosecond spectroscopy. In the undoped single crystals a single relaxation process is observed, showing a remarkable critical slowing down of the QP relaxation dynamics at the SDW transition temperature T_{SDW}\simeq125{K}. In the superconducting (SC) crystals multiple relaxation processes are present, with distinct SC state quasiparti…
The observation of superconductivity in infinite layer nickelate (Nd,Sr)NiO$_{2}$ thin films has led to rapid theoretical and experimental investigations of these copper-oxide-analogue systems [1-15]. Superconductivity has also been found in (Pr,Sr)NiO$_{2}$ [16,17], but not previously in (La,Sr)NiO$_{2}$ [2], raising a fundamental question whether superconductivity is associated with the presence of rare-earth moments [18,19]. Here we show that with significant materials optimization, substantial portions of the La$_{1-x}$Sr$_{x}$NiO$_{2}$ phase diagram can enter the regime of coherent low-te…
We use elastic and inelastic neutron scattering to systematically investigate the evolution of the low-energy spin excitations of the iron arsenide superconductor BaFe2-xNixAs2 as a function of nickel doping x. In the undoped state, BaFe2As2 exhibits a tetragonal-to-orthorhombic structural phase transition and simultaneously develops a collinear antiferromagnetic (AF) order below TN = 143 K. Upon electron-doping of x = 0.075 to induce bulk superconductivity with Tc = 12.3 K, the AF ordering temperature reduces to TN = 58 K.We show that the appearance of bulk superconductivity in BaFe1.925Ni0.0…
Granular superconductivity occurs when microscopic superconducting grains are separated by non-superconducting regions through which they communicate by Josephson tunneling to establish the macroscopic superconducting state [1]. Although crystals of the cuprate high-Tc superconductors are not granular in a structural sense, theory indicates that at low hole densities the holes can become concentrated at some locations resulting in hole-rich superconducting domains [2-5]. Granular superconductivity due to Josephson tunneling through 'undoped' regions between such domains would represent a new p…
We have studied the electron-phonon and superconducting properties of the Mg{1-x}AlxB2 and MgB{2(1-y)}C{2y} alloys within the framework of density functional theory using the self-consistent virtual-crystal approximation. For both alloys, the Eliashberg spectral functions and the electron-phonon coupling constants have been calculated in the two-band model for several concentrations up to x(Al)=0.55 and y(C)=0.175. We solved numerically the two-band Eliashberg gap equations without considering interband scattering. Using a single parameter for the Coulomb pseudopotential, which was determined …
One of the most intensely studied scenarios of high-temperature superconductivity (HTS) postulates pairing by exchange of magnetic excitations [1]. Indeed, such excitations have been observed up to around optimal doping in the cuprates [2-7]. In the heavily overdoped regime neutron scattering measurements indicate that magnetic excitations have effectively disappeared [8-10], and this was argued to cause the demise of HTS with overdoping [1, 8, 10]. Here we use resonant inelastic x-ray scattering (RIXS), which is sensitive to complementary parts of reciprocal space, to measure the evolution of…
We have performed an angle-resolved photoemission spectroscopy (ARPES) study of the undoped and electron-doped iron pnictides BaFe2\_{-x}CoxAs2 (Ba122) (x=0, 0.14) and studied the Fermi surfaces (FSs) and band dispersions near the Fermi level. The FS sheets we observed are consistent with the shrinkage of the hole-like pockets around the Brillouin Zone (BZ) center and the expansion of the electron pockets around the BZ corner in the electron-doped compound as compared to the undoped parent compound. Band dispersions and FSs around the BZ center strongly depend on the photon energy, indicating …
Superconducting bismuthates (Ba,K)BiO$_{3}$ (BKBO) constitute an interesting class of superconductors in that superconductivity with a remarkably high $T_\mathrm{c}$ of 30 K arises in proximity to charge density wave (CDW) order. Prior understanding on the driving mechanism of the CDW and superconductivity emphasizes the role of either bismuth (negative $U$ model) or oxygen ions (ligand hole model). While holes in BKBO presumably reside on oxygen owing to their negative charge transfer energy, so far there has been no other comparative material studied. Here, we introduce (Ba,K)SbO$_{3}$ (BKSO…
It is well established that the occurrence of superconductivity in iron pnictides is closely related to the tetragonal to orthorhombic structural and antiferromagnetic (AFM) phase transitions. It, however, has not been clear whether the same scenario is appropriate for iron chalcogenide counterparts due to the absence of parent compounds for the latter family of superconductors. Here, we report the synthesis and structure determination of two novel phases in ethylenediamine intercalated FeSe, one is tetragonal and the other orthorhombic in room temperature, which can be stabilized with neutral…