The evolution of pressure induced superconductivity in single crystal as well as polycrystalline samples of BaFe2As2 has been investigated through temperature dependent electrical resistivity studies in 0-7 GPa pressure range. While the superconducting transition remains incomplete in polycrystalline sample, a clear pressure induced superconductivity with zero resistivity at the expense of magnetic transition, associated with spin density wave (SDW), is observed in the single crystal sample. The superconducting transition temperature (TC) is seen to increase upto a moderate pressure of about ~1.5 GPa and decreases monotonically beyond this pressure. The SDW transition temperature TSDW decreases rapidly with increasing pressure and vanishes above ~1.5 GPa.
The long-sought goal of room-temperature superconductivity has reportedly recently been realized in a carbonaceous sulfur hydride compound under high pressure, as reported by Snider et al. [1]. The evidence presented in that paper is stronger than in other similar recent reports of high temperature superconductivity in hydrides under high pressure [2-7], and has been received with universal acclaim [8-10]. Here we point out that features of the experimental data shown in Ref. [1] indicate that the phenomenon observed in that material is not superconductivity. This observation calls into questi…
Very recently, NiTe2 has been reported to be a type II Dirac semimetal with Dirac nodes near the Fermi surface. Furthermore, it is unveiled that NiTe2 presents the Hall Effect, which is ascribed to orbital magnetoresistance. The physical properties behavior of NiTe2 under high pressure attracts us. In this paper, we investigate the electrical properties of polycrystalline NiTe2 by application of pressure ranging from 3.4GPa to 54.45Gpa. Superconductivity emerges at critical pressure 12GPa with a transition temperature of 3.7K, and Tc reaches its maximum, 6.4 K, at the pressure of 52.8GPa. Comp…
We report the effect of pressure on the electrical transport properties of the four-layer-type bismuth chalcogenide semiconductors LaOPbBiS$_{3}$ and La$_{2}$O$_{2}$Bi$_{3}$AgS$_{6}$ and present the discovery of a pressure-induced superconductivity. In both compounds, the semiconductorlike behavior concomitant with an anomaly in the more insulating state is gradually suppressed with increasing pressure while the superconductivity develops. The obtained phase diagrams, in sharp contrast with the interplay between the conventional charge density waves and superconductivity, suggest that the enha…
One approach to discovering topological superconductor is establishing superconductivity based on well-identified topological insulators. However, the coexistence of superconductivity and topological state is always arcane. In this paper, we report how pressure tunes the crystal structure, electronic structure, and superconductivity in topological insulator Bi2Te2.1Se0.9. The first pressure-induced structure transition start from 8.4 GPa, followed by the structure sequence of R-3m - C2/m - C2/c - Im-3m up to 37 GPa. Superconductivity starts to present at 2.4 GPa with the Tc around 6.6 K. Moreo…
Over the past six years, superconductivity at high temperatures has been reported in a variety of hydrogen-rich compounds under high pressure. That high-temperature superconductivity should exist in these materials is expected according to the conventional theory of superconductivity, as shown by detailed calculations. However here we argue that experimental observations rule out conventional superconductivity in these materials. Our results indicate that either these materials are unconventional superconductors of a novel kind, which we term `nonstandard superconductors', or alternatively tha…
Superconductivity in the doped topological insulator Cu$_x$Bi$_2$Se$_3$ under high pressure
本文报道了拓扑超导体Cu $_x$ Bi $_2$ Se $_3$的高压单晶研究。压力下的电阻率测量表明超导性被平滑地抑制。同时，金属性能逐渐丧失。压力下的上临界场数据$B_{c2}(T)$塌陷到一条通用曲线上。泡利极限的缺乏和$B_{c2}(T)$与极性态函数的比较表明自旋三重态超导性，但各向异性的自旋单重态不能被完全丢弃。
The Meissner effect, magnetic field expulsion, is a hallmark of superconductivity. Associated with it, superconductors exclude applied magnetic fields. Recently Minkov et al. presented experimental results reportedly showing "definitive evidence of the Meissner effect" in sulfur hydride and lanthanum hydride under high pressure [1], and more recently Eremets et al. argued that "the arguments against superconductivity (in hydrides) can be either refuted or explained" [2]. Instead, we show here that the evidence presented in those papers does not support the case for superconductivity in these m…
Hydrides offer an opportunity to study high-temperature (Tc) superconductivity at experimentally achievable pressures. However, they remained extremely high. Using density functional theory calculations, herein we demonstrated that a newly rare earth hydride, namely bulk ErH2, could be superconducting with a Tc around 80 K at 14.5 GPa. To date, the drived pressure is the lowest reported value for compressed hydrides. Besides superconductivity, Fermi Surface nesting and Kondo effect were manifested at this pressure. Intriguingly, due to Kondo destruction, superconductivity was prone to exist at…
We have investigated uniaxial and hydrostatic pressure effects on superconductivity in Fe1.07Te0.88S0.12 through magnetic-susceptibility measurements down to 1.8 K. The superconducting transition temperature Tc is enhanced by out-of-plane pressure (uniaxial pressure along the c-axis); the onset temperature of the superconductivity reaches 11.8 K at 0.4 GPa. In contrast, Tc is reduced by in-plane pressure (uniaxial pressure along the ab-plane) and hydrostatic pressure. Taking into account these results, it is inferred that the superconductivity of Fe1+yTe1-xSx is enhanced when the lattice const…
Pressure induced superconductivity in non-centrosymmetric CeRhSi$_{3}$ and CeIrSi$_{3}$ compounds has attracted significant attention of the scientific community since its discovery 15 years ago. Up-to-date, all reported experimental results were obtained employing the hybrid-cylinder piston pressure cells with a maximum reachable pressure of 3 GPa. Present study focuses on the superconducting state at higher, so far unreported, pressures using the Bridgman anvil cell and a CeRhSi$_{3}$ single crystal synthesized by the Sn-true-flux method. The initial increase of superconducting critical temp…
The recent discovery of superconductivity in heavy Fermion compound UTe2, a candidate topological and triplet-paired superconductor, has aroused widespread interest. However, to date, there is no consensus on whether the stoichiometric sample of UTe2 is superconducting or not due to lack of reliable evidence to distinguish the difference between the nominal and real compositions of samples. Here, we are the first to clarify that the stoichiometric UT2 is non-superconducting at ambient pressure and under hydrostatic pressure up to 6 GPa, however we find that it can be compressed into supercondu…
By performing high-pressure single-crystal neutron diffraction measurements, the evolution of structure and magnetic ordering in EuFe2As2 under hydrostatic pressure were investigated. Both the tetragonal-toorthorhombic structural transition and the Fe spin-density-wave (SDW) transition are gradually suppressed and become decoupled with increasing pressure. The antiferromagnetic order of the Eu sublattice is, however, robust against the applied pressure up to 24.7 kbar, without showing any change of the ordering temperature. Under the pressure of 24.7 kbar, the lattice parameters of EuFe2As2 di…
Here we report the observation of superconductivity in pressurized type-II Weyl semimetal (WSM) candidate TaIrTe4 by means of complementary high-pressure transport and synchrotron X-ray diffraction measurements. We find that TaIrTe4 shows superconductivity with transition temperature (TC) of 0.57 K at the pressure of ~23.8 GPa. Then, the TC value increases with pressure and reaches ~2.1 K at 65.7 GPa. In situ high-pressure Hall coefficient (RH) measurements at low temperatures demonstrate that the positive RH increases with pressure until the critical pressure of the superconducting transition…
The rich phenomena in the FeSe and related compounds have attracted great interests as it provides fertile material to gain further insight into the mechanism of high temperature superconductivity. A natural follow-up work was to look into the possibility of superconductivity in MnSe. It was shown that MnP becomes superconducting with Tc ~ 1 K under pressure. We demonstrated in this work that high pressure can effectively suppress the complex magnetic characters of MnSe crystal when observed at ambient condition. MnSe under pressure is found to undergo several structural transformations: the c…
The Ca10(PtnAs8)(Fe2As2)5 (n=3,4) compounds are a new type of iron pnictide superconductors whose structures consist of stacking Ca-PtnAs8-Ca-Fe2As2 layers in a unit cell. When n=3 (the 10-3-8 phase), the undoped compound is an antiferromagnetic (AFM) semiconductor, while, when n=4 (the 10-4-8 phase), the undoped compound is a superconductor with the transition temperature of 26K. Here we report the results of high-pressure studies on the 10-3-8 compound obtained through a combination of in-situ resistance, magnetic susceptibility, and Hall coefficient measurements. We find that its AFM order …
Quasi-two-dimensional kagome metals AV3Sb5 (A = K, Rb, and Cs) have attracted much recent interest due to exotic quantum phenomena such as unconventional superconductivity, topological charge order and giant anomalous Hall effect. Here we report pressure-induced reemergent superconductivity in CsV3Sb5 by electrical transport measurements under high pressures up to 47.9 GPa. We show that the superconducting critical temperature Tc is first enhanced by pressure and reaches its first maximum ~ 8.9 K at 0.8 GPa, then the Tc is suppressed by pressure and cannot be detected above 7.5 GPa, forming a …
Superconductivity in RbH$_{12}$ at low pressures: an \emph{ab initio} study
University of the Basque Country (UPV/EHU)（巴斯克大学）；Centro de Física de Materiales (CFM-MPC), CSIC-UPV/EHU（材料物理中心，西班牙国家研究委员会-巴斯克大学）；Donostia International Physics Center (DIPC)（圣塞巴斯蒂安国际物理中心）