We have investigated the Vanadium- (V) substituted Ni-Zn-Co ferrites where the samples were prepared using solid-state reaction technique. The impact of V5+ substitution on the structural, magnetic, dielectric and electrical properties of Ni-Zn-Co ferrites has been studied. XRD analysis confirmed the formation of a single-phase cubic spinel structure. The lattice constants have been calculated both theoretically and experimentally along with other structural parameters such as bulk density, X-ray density and porosity. The FESEM images are taken to study the surface morphology. FTIR measurement is also performed which confirms spinel structure formation. The saturation magnetization (Ms), coercive field (Hc) and Bohr magneton (B) were calculated from the obtained M-H loops. The temperature dependent permeability is studied to obtain the Curie temperature. Frequency and composition dependence of permeability was also analyzed. Dielectric behavior and ac resistivity are also subjected to investigate the frequency dependency. An inverse relationship was observed between the composition dependence of dielectric constant and ac resistivity. The obtained results such as the electrical resistivity, dielectric constants and magnetic properties suggest the appropriateness of the studied ferrites in microwave device applications.
Spinel ferrite Cu1-xZnxFe2O4 nanofibers over a compositional range 0 < x < 1 were prepared by electrospinning combined with sol-gel method. The influence of Zn2+ ions substitution on morphology, structure, and magnetic properties of copper ferrite has been investigated. The results show that surface of CuFe2O4 nanofibers consists of small open porosity, while surface of doped nanofibers reveals smooth and densified nature. With increasing Zn substitution, saturation magnetization initially increases and then decreases with a maximum value of 58.4 emu/g at x = 0.4, coercivity and square ratio a…
Chromium substituted cobalt ferrite with grain size less than the single domain (approx. 70 nm) has been prepared by the sol-gel method. XRD analysis reveals that the samples crystallize to cubic symmetry with spacegroup number 227. Two transition temperatures (TD (approx. 450 K) and TM (approx. 600 K) have been observed from the impedance verses temperature measurement. TD increases with the increase in frequency due to dipole response to the frequency. TM is comparable with the para-ferrimagnetic transition temperature of cobalt ferrite, which is independent of frequency. This result is well…
We report structural, magnetic and dielectric properties of Co1.5Fe1.5O4 nanoparticles and their composites with non-magnetic NaNO3. The samples were derived from metal nitrates solution at different pH values. The chemical routed sample was air heated at 200 0C and 500 0C. Heating of the material showed unusual decrease of crystallite size, but cubic spinel structure is seen in all samples. The samples of Co1.5Fe1.5O4 showed substantially large room temperature ferromagnetic moment, electrical conductivity, dielectric constant, and low dielectric loss. The samples are soft ferromagnet and ele…
The electrical conductivity and dielectric properties of Ni1.5Fe1.5O4 ferrite has been controlled by varying the annealing temperature of the chemical routed samples. The frequency activated conductivity obeyed Jonschers power law and universal scaling suggested semiconductor nature. An unusual metal like state has been revealed in the measurement temperature scale in between two semiconductor states with different activation energy. The metal like state has been affected by thermal annealing of the material. The analysis of electrical impedance and modulus spectra has confirmed non-Debye diel…
The Sn substituted Ni-Zn ferrites were synthesized by the standard double sintering technique using nano powders of nickel oxide (NiO), zinc oxide (ZnO), iron oxide (Fe2O3) and tin oxide (SnO2). The structural and electrical properties have been investigated by the X-ray diffraction, scanning electron microscopy, DC resistivity and dielectric measurements. Extra intermediate phase has been detected along with the inverse cubic spinel phase of Ni-Zn ferrite. Enhancement of grain size is observed in Sn substituted Ni-Zn ferrites. DC resistivity as a function of temperature has been investigated …
In this study, a series of nanocrystalline ferrites of Ni0.7Cu0.30AlxFe2-xO4 (x=0.00 to 0.10 with a step of 0.02) has been synthesized through the sol-gel auto combustion technique. The structural, morphological, dielectric, and electrical properties of the Ni-Cu spinel ferrite nanoparticles are analyzed due to the substitution of Al3+ content. The crystalline and structural characteristics of the prepared nanoparticles (NPs) have been studied employing the x-ray diffraction (XRD) spectra and FTIR analysis. The extracted XRD patterns assure the single-phase cubic spinel structure of all sample…
Cobalt substitutions were investigated in Ni0.4Zn0.4Cu0.2Fe2O4 ferrites, initial complex permeability was then measured from 1 MHz to 1 GHz. It appears that cobalt substitution led to a decrease in the permeability and an increase in the \mus\timesfr factor. As well, it gave to the permeability spectrum a sharp resonance character. We also observed a spin reorientation occurring at a temperature depending on the cobalt content. Study of the complex permeability versus temperature highlighted that the most resonant character was obtained at this temperature. This shows that cobalt contribution …
Bi3+ Doped Nanocrystalline Ni-Co-Zn Spinel Ferrites: Tuning of Physical, Electrical, Dielectric and Magnetic Properties for Advanced Spintronics Applications
Structural properties, impedance, dielectric and electric modulus spectra have been used to investigate the sintering temperature (Ts) effect on the single phase cubic spinel Ni0.6Zn0.4Fe2O4 (NZFO) ceramics synthesized by standard ceramic technique. Enhancement of dielectric constants is observed with increasing Ts. The collective contribution of n-type and p-type carriers yields a clear peak in notable unusual dielectric behavior is successfully explained by the Rezlescu model. The non-Debye type long range dielectric relaxation phenomena is explained by electric modulus formalism. Fast respo…
The method of microwave assisted hydrothermal synthesis of bismuth ferrite multiferroic nanoflowers, their mechanism of growth, magnetic as well as dielectric properties are presented. The nanoflowers are composed of numerous petals formed by BiFeO3 (BFO) nanocrystals and some amount of amorphous phase. The growth of the nanoflowers begins from the central part of calyx composed of only few petals towards which subsequent petals are successively attached. The nanoflowers exhibit enhanced magnetization due to size effect and lack of spin compensation in the spin cycloid. The dielectric properti…
Yttrium (Y) substituted Mg Zn ferrites with the compositions of Mg0.5Zn0.5YxFe2 xO4 have been synthesized by conventional standard ceramic technique. The effect of Y3+ substitution on the structural, electrical, dielectric and magnetic properties of Mg Zn ferrites has been studied.
The comparative study of the substitution of zinc and lithium for iron in the "114" ferrites, YBaFe4O7 and CaBaFe4O7, shows that these diamagnetic cations play a major role in tuning the competition between ferrimagnetism and magnetic frustration in these oxides. The substitution of Li or Zn for Fe in the cubic phase YBaFe4O7 leads to a structural transition to a hexagonal phase YBaFe4-xMxO7, for M = Li (0.30 < x < 0.75) and for M = Zn (0.40 < x < 1.50). It is seen that for low doping values i.e. x = 0.30 (for Li) and x = 0.40 (for Zn), these diamagnetic cations induce a strong ferrimagnetic c…
A new technique for estimation of magnetic interaction effects of initial magnetization curves has been proposed. It deals with remanence, and initial irreversible magnetization, curves. The method is applied for single-phase polycrystalline Ni0.85-xCu0.15ZnxFe2O4, (x = 0, 0.2, 0.4 and 0.6), which were synthesized by a standard ceramic technology. A study of the initial reversible and irreversible magnetization processes in ferrite materials was carried out. The field dependence of the irreversible, and reversible, magnetizations was determined by magnetic losses of minor hysteresis loops obta…
Layered ferromagnetic-piezoelectric composites show mechanical strain mediated electromagnetic coupling. Here we discuss dielectric and piezoelectric properties of ferrite-lead zirconate titanate (PZT) and lanthanum manganite-PZT samples. Results of our investigations on dielectric and pyroelectric properties of multilayer ferromagnetic-piezoelectric are presented here. Lead zircinate-titanate PbZrxTi1-xO3 (PZT) was used for the piezoelectric phase in all the structures. The following materials were used for the ferromagnetic component: nickel-zinc ferrites Ni0.9Zn 0.1Fe2O4 (NFO1) and Ni0.8Zn0…
We report the analysis of measurements of the complex magnetic permeability ($μ_r$) and dielectric permittivity ($ε_r$) spectra of a rubber radar absorbing material (RAM) with various MnZn ferrite volume fractions. The transmission/reflection measurements were carried out in a vector network analyzer. Optimum conditions for the maximum microwave absorption were determined by substituting the complex permeability and permittivity in the impedance matching equation. Both the MnZn ferrite content and the RAM thickness effects on the microwave absorption properties, in the frequency range of 2 to …
We have carried out the powder x-ray diffraction and dielectric studies on multiferroic particulate composite xNi0.9Zn0.1Fe2O4/(1-x)PbZr0.52Ti0.48O3 with x=0.15, 0.30, 0.45, 0.60, 0.75 and 0.90 to explore the structural and ferroelectric properties. A conventional double sintering method was used to prepare the xNi0.9Zn0.1Fe2O4/(1-x)PbZr0.52Ti0.48O3 composites. The structure of one of the component Ni0.9Zn0.1Fe2O4 is spinel cubic with space group Fd3m, while the other component PbZr0.52Ti0.48O3 is selected around the morphotropic phase boundary region in which the tetragonal and monoclinic pha…
Ferrite nanocrystals are interesting material due to their rich physical properties. Here we add nonmagnetic dopants Zn and Cu to nickel ferrite nanocrystals, Ni1-xMxFe2O4 (0<=x<=1, M{\in}{Cu, Zn}), and characterize how relevant properties of the samples are modified accordingly. Basically, these dopings cause a rearrangement of Fe+3 ions into the two preexisting octahedral and tetrahedral sites. In fact, this, we show, induces pertinent magnetic properties of the doped samples. In the case of the Cu-doping, the Jahn-Teller effect also emerges, which we identify through the FTIR Spectroscopy o…
Magnetic nanomaterials (23-43 nm) of Cu$_x$Co$_{1-x}$Fe$_2$O$_4$\ (x = 0.0, 0.5 and 1.0) were synthesized by auto combustion method. The crystallite sizes of these materials were calculated from X-ray diffraction peaks. The band observed in Fourier transform infrared spectrum near 575 cm$^{-1}$ in these samples confirm the presence of ferrite phase. Conductivity measurement shows the thermal hysteresis and demonstrates the knee points at 475$^o$C, 525$^o$C and 500$^o$C for copper ferrite, cobalt ferrite and copper-cobalt mixed ferrite respectively. The hystersis M-H loops for these materials w…
Magnetic, Optoelectronic, and Rietveld refined structural properties of Al3+ substituted nanocrystalline Ni-Cu spinel ferrites: An experimental and DFT based study
High-Frequency and Microwave Magnetic Properties of Ni$_{0.5}$Zn$_{0.5}$Fe$_2$O$_4$ Spinel Ferrite Ceramics
Institute of Physics of the Czech Academy of Sciences（捷克科学院物理研究所）；V.I. Vernadsky, Institute of General and Inorganic Chemistry, NAS of Ukraine（乌克兰国家科学院维尔纳茨基普通与无机化学研究所）；NTUU “Igor Sikorsky Kyiv Polytechnic Institute”（国立技术大学伊戈尔·西科尔斯基基辅理工学院）
Thick film layered magnetoelectric composites consisting of ferromagnetic and ferroelectric phases have been synthesized with nickel ferrite (NFO), cobalt ferrite (CFO), La0.7Sr0.3MnO3 (LSMO), or La0.7Ca0.3MnO3 (LCMO) and lead zirconate titanate (PZT). Structural, magnetic and ferromagnetic resonance characterization shows evidence for defect free ferrites, but deterioration of manganite parameters. The resistivity and dielectric constants are smaller than expected values. The magnetoelectric effect (ME) is stronger in ferrite-PZT than in manganite-PZT. The ME voltage coefficient aE at room te…
We report the nanoscale electrical imaging results in hexagonal $Lu_{0.6}Sc_{0.4}FeO_3$ single crystals using conductive atomic force microscopy (C-AFM) and scanning microwave impedance microscopy (MIM). While the dc and ac response of the ferroelectric domains can be explained by the surface band bending, the drastic enhancement of domain wall (DW) ac conductivity is clearly dominated by the dielectric loss due to DW vibration rather than mobile-carrier conduction. Our work provides a unified physical picture to describe the local conductivity of ferroelectric domains and domain walls, which …
Results of low temperature dielectric measurements on the mixed (Ca_(1-x)Pb_(x))TiO_(3) system are presented to show that a dielectric anomaly appears for x \geq 0.10. The observed dielectric peak is shown to be due to a thermodynamic phase transition and not due to a relaxor or dipole glass type transition. Curie-Weiss fit to the dielectric constant gives negative Curie temperature which points towards an antiferroelectric transition. Arguments are advanced to propose that CaTiO3 may be an incipient antiferroelectric in which Pb^(2+) substitution stabilises the antiferroelectric phase.
We report the effect of Ba and Zr co-substitution on structural, dielectric, magnetic and magnetoelectric properties of BiFeO3 multiferroics. Polycrystalline nanoceramic samples of Bi1- xBaxFe1-yZryO3 have been synthesized by auto-combustion method. Rietveld refinement result of X-ray diffraction data indicate a contraction of unit cell volume with increase in x and y. Field emission scanning electron micrographs show densely populated grains without any voids or defects with well-defined grain boundary and decrease in grain size with increasing x and y. The result of dielectric measurement di…
We present a combined experimental-theoretical study demonstrating the role of site disorder, off-stoichiometry and strain on the optical behavior of magnetoelectric gallium ferrite. Optical properties such as band-gap, refractive indices and dielectric constants were experimentally obtained by performing ellipsometric studies over the energy range 0.8 eV to 4.2 eV on pulsed laser deposited epitaxial thin films of stoichiometric gallium ferrite with b-axis orientation and the data was compared with theoretical results. Calculations on the ground state structure show that the optical activity i…
A series of Ni0.6-x/2Zn0.4-x/2SnxFe2O4 (x = 0.0, 0.05, 0.1, 0.15, 0.2 and 0.3) (NZSFO) ferrite composites have been synthesized from nano powders using standard solid state reaction technique. The spinel cubic structure of the investigated samples has been observed by the X-ray diffraction (XRD). The magnetic properties such as saturation magnetization (Ms), remanent magnetization (Mr), coercive field (Hc) and Bohr magneton (B) are calculated from the hysteresis loops. The value of Ms is found to decrease with increasing Sn content in the samples. This change has been successfully explained by…
We report the evolution of structural, magnetic and dielectric properties due to partial substitution of Ba by Sr in the high temperature multiferroic YBaCuFeO5. This compound exhibits ferroelectric and antiferromagnetic transitions around 200 K and these two phenomena are presumed to be coupled with each other. Our studies on magnetic and dielectric properties of the YBa1-xSrxCuFeO5 (x = 0.0, 0.25 and 0.5) show that substitution of Sr shifts magnetic transition towards higher temperature whereas dielectric transition to lower temperature. These results points to the fact that magnetic and die…
Polycrystalline La and Ti co-substituted ceramics were synthesized by the tartaric acid modified sol-gel technique. It was observed that the co-substitution of La & Ti at Bi & Fe sites in BiFeO3 suppress the impurity phase formation which is a common problem in bismuth ferrite. The quantitative crystallographic phase analysis was performed with the help of FULLPROF program which suggests the existence of compositional driven crystal structure transition from rhombohederal (space group R3c) to the orthorhombic (space group Pbnm). The changes in the phonon frequencies as well as line widths of A…
A correlation between structure and vibrational properties related to a ferroelectric to paraelectric phase transition in perovskite Pb(1-x)(Na0.5Sm0.5)xTiO3 (PNST - x) polycrystalline powders is discussed. Substitution leads to reduction of tetragonality which is associated with a shift of the phase transition to lower temperatures. The nature of the phase transition gets diffused with increasing substitution.
An electric current flowing around a loop produces a magnetic field and hence a magnetic flux through the loop. The ratio of the magnetic flux to the electric current is called the (magnetic) self inductance. Can there be a dual situation with a magnetic current flowing around a loop and producing an electric field and hence an electric flux through the loop? Following the classical electrodynamics laws an answer to this question should be negative. Nevertheless special spectral properties of magnetic dipolar modes in a quasi-2D ferrite disk show there are the double-valued-function loop magne…
The micromagnetic distribution in a dielectric nanoparticle is theoretically considered. It is shown that the existence of inhomogeneous magnetoelectric interaction in magnetic dielectrics provides the possibility to stabilize the vortex and antivortex state. The estimation of the critical voltage necessary for vortex/antivortex nucleation in bismuth ferrite and iron garnet nanoparticles yields a value of +/-150 V. This system can be considered as electrically switchable two state-logic magnetic element.
Temperature Dependent Magnetic and Structural Properties of Al Substituted Nanostructured Ferrites with Large Coercive Fields
University of Genoa（热那亚大学）；Uppsala University（乌普萨拉大学）；Lomonosov Moscow State University（莫斯科罗蒙诺索夫国立大学）；Le Mans Université（勒芒大学）；Nuclear Physics Institute of the CAS（捷克科学院核物理研究所）；CNR-SPIN（国家研究中心自旋物理研究所）；Università Ca’ Foscari Venezia（威尼斯卡福斯卡里大学）
Divergence between long- and short-wavelength magnon damping in spinel ferrites
Stanford Institute for Materials and Energy Sciences, SLAC National Accelerator Laboratory（斯坦福材料能源科学研究所，SLAC国家加速器实验室）；Department of Physics and Astronomy, University of Iowa（爱荷华大学物理与天文系）；Department of Physics, Stanford University（斯坦福大学物理系）；Geballe Laboratory for Advanced Materials, Stanford University（斯坦福大学先进材料盖伯实验室）；Department of Applied Physics, Stanford University（斯坦福大学应用物理系）；Department of Materials Science and Engineering, Stanford University（斯坦福大学材料科学与工程系）
Bismuth ferrite (BiFeO3) is one of the most promising multiferroics with a sufficiently high ferroelectric (FE) and antiferromagnetic transition temperatures, and magnetoelectric (ME) coupling coefficient at room temperature, and thus it is highly sensitive to the impact of cross-influence of applied electric and magnetic fields. According to the urgent demands of nanotechnology miniaturization for ultra-high density data storage in advanced nonvolatile memory cells, it is very important to reduce the sizes of multiferroic nanoparticles in the self-assembled arrays without serious deterioratio…
Bi1-xLaxFe1-xMnxO3 (x = 0.000 - 0.300) ceramics prepared by the tartaric acid modified sol-gel technique have been studied to analyze the effect of composition driven structural transition on the magnetic properties of bismuth ferrite (BiFeO3). It was found that the co-substitution of La & Mn at Bi & Fe sites leads to suppression of impurity phases (Bi2Fe4O9 and Bi25FeO40) which generally appear in BiFeO3. The quantitative crystallographic phase analysis has been carried out by double phase Rietveld analysis of all the XRD patterns which indicates the existence of compositional driven crystal …
The influence of solubilizing substitutional groups on the electronic and optical properties of functionalized pentacene molecules and crystals have been investigated. Density functional theory is used to calculate the electronic and optical properties of pentacene, TIBS-CF$_{3}$-pentacene, and TIPS-pentacene. The results are compared with experimental absorption spectra of solutions and the complex dielectric function of thin films in the 1 eV to 3 eV energy range. In all cases, the band gaps of the isolated molecules are found to be smaller than those of the crystals. The absorption spectra …
Room temperature dielectric and magnetic properties of BiFeO$_3$ samples, co-doped with magnetic Gd and non-magnetic Ti in place of Bi and Fe, respectively, were reported. The nominal compositions of Bi$_{0.9}$Gd$_{0.1}$Fe$_{1-x}$Ti$_x$O$_3$ (x = 0.00-0.25) ceramics were synthesized by conventional solid state reaction technique. X-ray diffraction patterns revealed that the substitution of Fe by Ti induces a phase transition from rhombohedral to orthorhombic at x $>$ 0.20. Morphological studies demonstrated that the average grain size was reduced from $\sim {~}$1.5 $μm$ to $\sim {~}$200 $nm$ w…
The influence of La and Nd co-substitution on the structural and magnetic properties of BiFeO3 (BFO) thin films was examined. Epitaxial thin films of pure and, La and Nd co-doped BFO on the SrRuO3 buffered single crystal SrTiO3 (001) substrate were deposited using pulsed laser deposition. The structural change in co doped La and Nd BFO thin films which was caused by the changes of force constant in the crystal lattice induced by ionic radii mismatch was investigated. Raman spectroscopy studies manifest the structural change in doped BFO films from rhombohedral to monoclinic distorted phase whi…
The effects of Ni$^{2+}$ substitution on the structure (lattice parameters, cations distribution, average cations radii, cation-cation/anion bond lengths and angles) and the soft magnetic properties of Mg$_{1-x}$Ni$_x$Fe$_2$O$_4$ ($0 \le x \le 1.0$) nanocrystals have been studied by x-ray diffraction with Rietveld refinement, transmittance electron microscopy, Mossbauer spectroscopy and magnetization measurements. The mostly inverse spinel structure was found in MgFe$_2$O$_4$ nanoparticles and the inversion factor is further increased by Ni-substitution up to a complete inversion in NiFe$_2$O$…
In this paper, we reported the effect of Cu doping on the structural and dielectric properties of Ba$_2$Y$_{1-x}$Cu$_x$TaO$_{6-y}$ (0.00 $\leq$ x $\leq$ 0.50) ceramics at room temperature. The Copper for Yttrium substitution reduces the sintering temperature and leads to structural changes in the Ba$_2$YTaO$_6$ rock-salt crystalline structure. Dielectric permittivity and complex impedance spectroscopy measurements suggested enhancement of the dielectric constant and occurrence of interfacial Maxwell-Wagner polarization.
Tetragonal distorted spinel of CuMn2-xTixO4 (x = 0, 0.25 and 0.50) was prepared by solid state reaction method followed by neutron diffraction, FTIR spectroscopy, dielectric spectroscopy and magnetization measurements. The neutron diffraction and FTIR spectroscopy provide the information regarding phase formation. But, the magnetic susceptibility clearly shows the ferri-magnetic order below 76K associated with meta-magnetic state which turns to spin-glass behaviour upon Ti-substitution for Mn in CuMn2O4. In addition, the room temperature M(H) of all the spinels are described by the Arrott's pl…
There have been a large number of papers on bismuth ferrite (BiFeO3) over the past few years, trying to exploit its room-temperature magnetoelectric multiferroic properties. Although these are attractive, BiFeO3 is not the ideal multiferroic, due to weak magnetization and the difficulty in limiting leakage currents. Thus there is an ongoing search for alternatives, including such materials as gallium ferrite (GaFeO3). In the present work we report a comprehensive study of the perovskite PbTi1-xPdxO3 with 0 < x < 0.3. Our study includes dielectric, impedance and magnetization measurements, cond…
Most conventional magnetic materials used in the electronic devices are ferrites, which are composed of micrometer-size grains. But ferrites have small saturation magnetization, therefore the performance at GHz frequencies is rather poor. That is why functionalized nanocomposites comprising magnetic nanoparticles (e.g. Fe, Co) with dimensions ranging from a few nm to 100 nm, and embedded in dielectric matrices (e.g. silicon oxide, aluminium oxide) have a significant potential for the electronics industry. When the size of the nanoparticles is smaller than the critical size for multidomain form…
Composition-driven structural transitions in Bi1-xCaxFe1-xMnxO3 ceramics prepared by the tartaric acid modified sol-gel technique have been studied to analyze its effect on the magnetic properties of bismuth ferrite (BiFeO3). It was observed that the co-substitution of Ca & Mn at Bi & Fe sites in BiFeO3 (BFO) significantly suppress the impurity phases. The quantitative crystallographic phase analysis has been carried out by double phase Rietveld analysis of all the XRD patterns which indicates the existence of compositional driven crystal structure transformation from rhombohederal (R3c space …
Correlations Between the Dielectric Properties, Domain Structure Morphology and Phase State of Bi1-xSmxFeO3 Nanoparticles
Institute of Physics, National Academy of Sciences of Ukraine（乌克兰国家科学院物理研究所）；Taras Shevchenko National University of Kyiv（基辅塔拉斯舍甫琴科国立大学）；Donetsk Institute for Physics and Engineering named after O.O. Galkin of the National Academy of Sciences of Ukraine（乌克兰国家科学院奥·奥·加尔金顿涅茨工程物理学研究所）；Stockholm University, Department of Chemistry（斯德哥尔摩大学化学系）；Ye. O. Paton Institute of Materials Science and Welding, National Technical University of Ukraine “Igor Sikorsky Kyiv Polytechnic Institute”（乌克兰伊戈尔·西科尔斯基基辅理工学院叶·奥·帕顿材料科学与焊接研究所）；Frantsevich Institute for Problems in Materials Science of the National Academy of Sciences of Ukraine（乌克兰国家科学院弗兰采维奇材料科学问题研究所）
In the preceding paper, we have shown analytically that in a source-free subwavelength region of microwave fields there exist the field structures with local coupling between the time-varying electric and magnetic fields differing from the electric-magnetic coupling in regular free-space electromagnetic waves. As a source of such near fields, there is a small quasi-2D ferrite disk with the magnetic-dipolar-mode (MDM) spectra. The near fields originated from a MDM ferrite particle are characterized by topologically distinctive structures of power-flow vortices, non-zero helicity, and a torsion …
Today, spinel ferrite nanoparticles are widely used in the medical field for cancer treatment, drug delivery, and magnetic resonance imaging contrast agent due to their superior magnetic properties and biocompatibility. Due to the strong dependence of magnetic properties on morphology and other structural aspects, the magnetic properties of these nanoparticles depend on their manufacturing process. One of the goals of the researchers is to improve the magnetic properties of these nanoparticles by substituting elements such as manganese, cobalt, zinc, nickel, magnesium and iron. In this researc…
The structural, dielectric, magnetic, and magnetoelectric (ME) properties of particulate composites containing lead-iron niobate and lead titanate piezoelectric 0.94[PbFe$_{0.5}$Nb$_{0.5}$O$_3$]-0.06[PbTi$_{0.5}$O$_3$] (PFN-PT) and Zn-substituted cobalt ferrite magnetostrictive CoFe$_{2-x}$Zn$_{x}$O$_4$ (CF$_{2-x}$Z$_{x}$O); 0.6(PFN-PT)/0.4(CF$_{2-x}$Z$_{x}$O), x=0, 0.025, 0.1, 0.2, 0.3 (with ratio of 60 Wt\% ferroelectric and 40 Wt\% ferrite); have been investigated. We investigated the ME voltage coefficient as a complex quantity for all composite samples using the dynamic piezomagnetic coef…
PbTiO3 has the highest tetragonal distortion (c/a=1.064) and highest spontaneous polarization among perovskite titanates. But, it is hazardous and hence one needs to reduce Pb content by substituting or reducing Pb content for use in applications. Pb(1-x)(K0.5Sm0.5)xTiO3 (0&x&0.5) perovskite powders were synthesized by sol-gel process, where Pb2+ was replaced by a combination of K+10.5Sm+30.5 (equivalent charge and comparable ionic radius) providing an excellent substitution model to study changes in structural and electrical properties. Vibrational properties and dielectric properties are mod…
Single phase, sol-gel prepared Cu1-xFexO (0<x<0.125) are characterized in terms of structural, electronic and magnetic properties. Using dielectric and magnetic studies we investigate the coupling of electron and spin. The electrical conductivities and activation energies are studied with increasing Fe content. Modeling of experimental conductivity data emphasizes on a single hopping mechanism for all samples except x=0.125, which have two activation energies. Hole doping is confirmed from Hall effect [1] and by confirming a majority Fe3+ substitution of Cu2+ in CuO from XPS studies. Such a su…
Phase, microstructural, dielectric and ferroelectric properties investigation clearly reveal that the charge imbalance created due to alio-valent Gd3+-ion substitution at Pb2+ site in lead magnesium niobate should be compensated by changing B-site cation ratio instead of creating A-site or B-site vacancies. Microstructure analysis along with elemental mapping exhibit segregation of magnesium oxide (MgO) and gadolinium niobate (GdNbO4) phase, which is observed to remain invariant to the charge compensation mechanism. Fitting of frequency dependent temperature of dielectric constant maximum Tm (…
Multiferroic bismuth ferrite Bi_2Fe_4O_9 (BFO) ceramic was synthesized by conventional solid state reaction route. X-ray diffraction and Rietveld refinement show formation of single phase ceramic with orthorhombic crystal structure (space group Pbam). The morphological study depicted a well-defined grain of size $\simeq$2μm. The optical studies were carried out by using UV-Vis spectrophotometer which shows a band gap of 1.53 eV and a green emission spectrum at 537 is observed in the Photoluminescence study. The frequency dependent dielectric study at various temperature revealed that the diele…
Manganites exhibit various types of electronic phenomena, and these electronic characteristics can be controlled by carrier doping. Herein, we report the dielectric and magnetic properties of electron-doped manganite Ca$_{1-x}$Sr$_x$Mn$_{0.85}$Sb$_{0.15}$O$_3$ ($x$ = 0, 0.1, 0.2, and 0.3). The temperature dependence of the real part of the dielectric constant exhibits a broad and large peak just below the kink temperature of magnetization and a sharp decrease at lower temperatures, accompanied by an anomaly of the imaginary part. Furthermore, isovalent Sr substitution enhances the temperature …
Multiferroic (Bi1-xLaxFeO3)0.5(PbTiO3)0.5 ceramics was prepared from mechanical synthesized nanopowders. The XRD studies revealed the tetragonal structure and the tetragonality decreased with La content. Dielectric response of the compounds was found to contain three anomalies: 1) relaxor-like behavior due to lattice disorder (below 300 K); 2) dielectric permittivity maxima at~400 K attributed to the presence of oxygen vacancies; 3) grain boundary effect above 475 K. The Curie point at ~500 K was observed for the compound with x=0.5. The composition near the morphotropic boundary: (Bi0.8La0.2F…