Effect of annealing temperatures on the electrical conductivity and dielectric properties of Ni1.5Fe1.5O4 spinel ferrite prepared by chemical reaction at different pH values
The electrical conductivity and dielectric properties of Ni1.5Fe1.5O4 ferrite has been controlled by varying the annealing temperature of the chemical routed samples. The frequency activated conductivity obeyed Jonschers power law and universal scaling suggested semiconductor nature. An unusual metal like state has been revealed in the measurement temperature scale in between two semiconductor states with different activation energy. The metal like state has been affected by thermal annealing of the material. The analysis of electrical impedance and modulus spectra has confirmed non-Debye dielectric relaxation with contributions from grains and grain boundaries. The dielectric relaxation process is thermally activated in terms of measurement temperature and annealing temperature of the samples. The hole hopping process, due to presence of Ni3+ ions in the present Ni rich ferrite, played a significant role in determining the thermal activated conduction mechanism. This work has successfully applied the technique of a combined variation of annealing temperature and pH value during chemical reaction for tuning electrical parameters in a wide range; for example dc limit of conductivity 10power(-4) -10power(-12) S/cm, and unusually high activation energy 0.17-1.36 eV.
The third order perturbed Heisenberg Hamiltonian was employed to investigate the spinel thick nickel ferrite films. The variation of energy up to N=10000 was studied. At N=75, the energy required to rotate from easy to hard direction is very small. For film with N=10000, the first major maximum and minimum can be observed at 202 and 317 degrees, respectively. This curve shows some abrupt changes after introducing third order perturbation. The maximum energy of this curve is higher than that of spinel thick ferrite films with second order perturbed Heisenberg Hamiltonian. At some values of stre…
Heteroepitaxial spinel ferrites NiFe2O4 and CoFe2O4 films have been prepared by pulsed laser deposition (PLD) at various temperatures (175 - 690 °C) under ozone/oxygen pressure of 10 mTorr. Due to enhanced kinetic energy of ablated species at low pressure and enhanced oxidation power of ozone, epitaxy has been achieved at significantly lower temperatures than previously reported. Films grown at temperature below 550 °C show a novel growth mode, which we term "vertical step-flow" growth mode. Epitaxial spinel ferrite films with atomically flat surface over large areas and enhanced magnetic mome…
We present calculations of magnetostriction constants for the spinel ferrites CoFe2O4 and NiFe2O4 using density functional theory within the GGA+U approach. Special emphasis is devoted to the influence of different possible cation distributions on the B site sublattice of the inverse spinel structure on the calculated elastic and magnetoelastic constants. We show that the resulting symmetry-lowering has only a negligible effect on the elastic constants of both systems as well as on the magnetoelastic response of NiFe2O4, whereas the magnetoelastic response of CoFe2O4 depends more strongly on t…
In this paper we show that spinel ferrite nanocrystals (NiFe2O4, and CoFe2O4) can be texturally embedded inside a ZnO matrix by ion implantation and post-annealing. The two kinds of ferrites show different magnetic properties, e.g. coercivity and magnetization. Anomalous Hall effect and positive magnetoresistance have been observed. Our study suggests a ferrimagnet/semiconductor hybrid system for potential applications in magneto-electronics. This hybrid system can be tuned by selecting different transition metal ions (from Mn to Zn) to obtain various magnetic and electronic properties.
The effect of epitaxial strain on the cation distribution in spinel ferrites CoFe2O4 and NiFe2O4 is investigated by GGA+U total energy calculations. We obtain a very strong (moderate) tendency for cation inversion in NiFe2O4 (CoFe2O4), in agreement with experimental bulk studies. This preference for the inverse spinel structure is reduced by tensile epitaxial strain, which can lead to strong sensitivity of the cation distribution on specific growth conditions in thin films. Furthermore, we obtain significant energy differences between different cation arrangements with the same degree of inver…
We report measurements of magnon spin transport in a spinel ferrite, magnesium aluminum ferrite $\mathrm{MgAl_{0.5}Fe_{1.5}O_4}$ (MAFO), which has a substantial in-plane four-fold magnetic anisotropy. We observe spin diffusion lengths $> 0.8$ $\mathrm{μm}$ at room temperature in 6 nm films, with spin diffusion length 30% longer along the easy axes compared to the hard axes. The sign of this difference is opposite to the effects just of anisotropy in the magnetic energy for a uniform magnetic state. We suggest instead that accounting for anisotropy in exchange stiffness is necessary to explain …
We apply the self-interaction corrected local spin density %(SIC-LSD) approximation to study the electronic structure and magnetic properties of the spinel ferrites MnFe$_{2}$O$_{4}$, Fe$_{3}$O$_{4}$, CoFe$_{2}$O$_{4}$, and NiFe$_{2}$O$_{4}$. We concentrate on establishing the nominal valence of the transition metal elements and the ground state structure, based on the study of various valence scenarios for both the inverse and normal spinel structures for all the systems. For both structures we find all the studied compounds to be insulating, but with smaller gaps in the normal spinel scenari…
The inverse spinels CoFe2O4 and NiFe2O4, which have been of particular interest over the past few years as building blocks of artificial multiferroic heterostructures and as possible spin-filter materials, are investigated by means of density functional theory calculations. We address the effect of epitaxial strain on the magneto-crystalline anisotropy and show that, in agreement with experimental observations, tensile strain favors perpendicular anisotropy, whereas compressive strain favors in-plane orientation of the magnetization. Our calculated magnetostriction constants $λ_{100}$ of about…
Spinel ferrites in general show a rich interplay of structural, electronic, and magnetic properties. Here, we particularly focus on zinc ferrite (ZFO), which has been observed experimentally to crystallise in the cubic $normal$ spinel structure. However, its magnetic ground state is still under dispute. In addition, some unusual magnetic properties in ZFO thin films or nanostructures have been explained by a possible partial cation inversion and a different magnetic interaction between the two cation sublattices of the spinel structure compared to the crystalline bulk material. Here, density f…
Spinel Ferrite-Based Materials for Electrochemical Applications: Synthesis, Applications, and Future Perspectives
Guru Ghasidas Vishwavidyalaya (A Central University)（古鲁·格哈西达斯大学（一所中央大学））；Government Girls Degree College Samadi（萨马迪女子政府学位学院）；Indian Institute of Technology (BHU)（印度理工学院（贝拿勒斯印度教大学））；Indian Institute of Technology Bhilai（印度理工学院比莱分校）
We prepared three ferrite nanocatalysts: (i) copper ferrite (CuFe2O4), (ii) ferrite where cobalt was substituted by nickel (NixCo1-xFe2O4, with x= 0, 0.2, 0.4, 0.6), and (iii) ferrite where nickel was substituted by zinc (ZnyNi1-yFe2O4 with y= 1, 0.7, 0.5, 0.3), by the sol-gel method. The X-ray diffraction patterns show that the ferrite samples have been crystallized in the cubic spinel structural phase. We obtained the grain size by FE-SEM images in the range of 10-70 nm, and their magnetic properties by VSM. Next, carbon nanotubes were grown on these nanocatalysts by the CCVD method. We show…
In this study, a series of nanocrystalline ferrites of Ni0.7Cu0.30AlxFe2-xO4 (x=0.00 to 0.10 with a step of 0.02) has been synthesized through the sol-gel auto combustion technique. The structural, morphological, dielectric, and electrical properties of the Ni-Cu spinel ferrite nanoparticles are analyzed due to the substitution of Al3+ content. The crystalline and structural characteristics of the prepared nanoparticles (NPs) have been studied employing the x-ray diffraction (XRD) spectra and FTIR analysis. The extracted XRD patterns assure the single-phase cubic spinel structure of all sample…
The Raman spectra of single crystals of NiFe2O4 were studied in various scattering configurations in close comparison with the corresponding spectra of Ni0.7Zn0.3Fe2O4 and Fe3O4. The number of experimentally observed Raman modes exceeds significantly that expected for a normal spinel structure and the polarization properties of most of the Raman lines provide evidence for a microscopic symmetry lower than that given by the Fd-3m space group. We argue that the experimental results can be explained by considering the short range 1:1 ordering of Ni2+ and Fe3+ at the B-sites of inverse spinel stru…
The direct liquid injection chemical vapor deposition (DLI-CVD) technique has been used for the growth of cobalt ferrite (CFO) films on (100)-oriented MgAl$_2$O$_4$ (MAO) substrates. Smooth and highly epitaxial cobalt ferrite thin films, with the epitaxial relationship $\mathrm{MAO} (100)\:[001] \parallel \mathrm{CFO} (100)\:[001]$, are obtained under optimized deposition conditions. The films exhibit bulk-like structural and magnetic properties with an out-of-plane lattice constant of $8.370\;\mathrmÅ$ and a saturation magnetization of $420\;\mathrm{kA/m}$ at room temperature. The Raman spect…
This paper presents the results of simulations of the magnetization field {\it ac} response (at $2$ to $12$ GHz) of various submicron ferrite particles (cylindrical dots). The ferrites in the present simulations have the spinel structure, expressed here by M$_{1-n}$Zn$_{n}$Fe$_2$O$_4$ (where M stands for a divalent metal), and the parameters chosen were the following: (a) for $n=0$: M = \{ Fe, Mn, Co, Ni, Mg, Cu \}; (b) for $n=0.1$: M = \{ Fe, Mg \} (mixed ferrites). These runs represent full 3D micromagnetic (one-particle) ferrite simulations. We find evidences of confined spin waves in all s…
Bi3+ Doped Nanocrystalline Ni-Co-Zn Spinel Ferrites: Tuning of Physical, Electrical, Dielectric and Magnetic Properties for Advanced Spintronics Applications
The accumulation of boron within the porous nickel ferrite (NiFe2O4, NFO) deposited on fuel rods is a major technological problem with important safety and economical implications. In this work the electronic structure of nickel ferrite is investigated using first-principles methods, and the results are combined with experimental data to analyze B incorporation into the NFO structure. Under thermodynamic equilibrium the calculations predict that the incorporation of B into the NFO structure is unfavorable. The main limiting factors are the narrow stability domain of NFO and the precipitation o…
Over the past few years, intensive studies of ultrathin epitaxial films of perovskite oxides have often revealed exciting properties like giant magnetoresistive tunnelling and electric field effects. Spinel oxides appear as even more versatile due to their more complex structure and the resulting many degrees of freedom. Here we show that the epitaxial growth of nanometric NiFe2O4 films onto perovskite substrates allows the stabilization of novel ferrite phases with properties dramatically differing from bulk ones. Indeed, NiFe2O4 films few nanometres thick have a saturation magnetization at l…
Varying the substrate temperature changes structural and magnetic properties of spinel ferrite NZFO thin films. XRD of films grown at different temperature display only 004 reflections, without any secondary peaks, showing growth orientation along the c axis. We find an increase in crystalline quality of these thin films with the rise of substrate temperature. The surface topography of the thin films grown on various growth temperatures conditions reveal that these films are smooth with low roughness, however the thin films grown at 800 C exhibit lowest average and rms roughness among all thin…
High-Frequency and Microwave Magnetic Properties of Ni$_{0.5}$Zn$_{0.5}$Fe$_2$O$_4$ Spinel Ferrite Ceramics
Institute of Physics of the Czech Academy of Sciences（捷克科学院物理研究所）；V.I. Vernadsky, Institute of General and Inorganic Chemistry, NAS of Ukraine（乌克兰国家科学院维尔纳茨基普通与无机化学研究所）；NTUU “Igor Sikorsky Kyiv Polytechnic Institute”（国立技术大学伊戈尔·西科尔斯基基辅理工学院）
Spinel ferrite Cu1-xZnxFe2O4 nanofibers over a compositional range 0 < x < 1 were prepared by electrospinning combined with sol-gel method. The influence of Zn2+ ions substitution on morphology, structure, and magnetic properties of copper ferrite has been investigated. The results show that surface of CuFe2O4 nanofibers consists of small open porosity, while surface of doped nanofibers reveals smooth and densified nature. With increasing Zn substitution, saturation magnetization initially increases and then decreases with a maximum value of 58.4 emu/g at x = 0.4, coercivity and square ratio a…
Magnetic, Optoelectronic, and Rietveld refined structural properties of Al3+ substituted nanocrystalline Ni-Cu spinel ferrites: An experimental and DFT based study
Understanding Damping Mechanisms via Spin Diffusion Length in Low-damping Li$_{0.5}$Al$_{1.0}$Fe$_{1.5}$O$_4$ Spinel Ferrite Thin Films
Stanford University（斯坦福大学）；SLAC National Accelerator Laboratory（SLAC国家加速器实验室）；University of California, Irvine（加州大学尔湾分校）；University of California San Diego（加州大学圣地亚哥分校）
Divergence between long- and short-wavelength magnon damping in spinel ferrites
Stanford Institute for Materials and Energy Sciences, SLAC National Accelerator Laboratory（斯坦福材料能源科学研究所，SLAC国家加速器实验室）；Department of Physics and Astronomy, University of Iowa（爱荷华大学物理与天文系）；Department of Physics, Stanford University（斯坦福大学物理系）；Geballe Laboratory for Advanced Materials, Stanford University（斯坦福大学先进材料盖伯实验室）；Department of Applied Physics, Stanford University（斯坦福大学应用物理系）；Department of Materials Science and Engineering, Stanford University（斯坦福大学材料科学与工程系）
Spinel Fe3O4 nanoparticles have been produced through ball milling in methyl-alcohol (CH3OH), aiming to obtain samples with similar average particle sizes <d> and different interparticle interactions. Three samples having Fe3O4/CH3(OH) mass ratios R of 3 %, 10 % and 50 % wt. were milled for several hours until particle size reached a steady value (<d> ~ 7-10 nm). A detailed study of static and dynamic magnetic properties has been undertaken by measuring magnetization, ac susceptibility and Mössbauer data. As expected for small particles, the Verwey transition was not observed, but instead supe…
We have investigated the Vanadium- (V) substituted Ni-Zn-Co ferrites where the samples were prepared using solid-state reaction technique. The impact of V5+ substitution on the structural, magnetic, dielectric and electrical properties of Ni-Zn-Co ferrites has been studied. XRD analysis confirmed the formation of a single-phase cubic spinel structure. The lattice constants have been calculated both theoretically and experimentally along with other structural parameters such as bulk density, X-ray density and porosity. The FESEM images are taken to study the surface morphology. FTIR measurement…
Magnetic nanoparticles of cobalt ferrite have been synthesized by wet chemical method using stable ferric and cobalt salts with oleic acid as the surfactant. X-ray Diffraction (XRD) and Transmission Electron Microscope (TEM) confirmed the formation of single phase cobalt ferrite nanoparticles in the range 15-48nm depending on the annealing temperature and time. The size of the particles increases with annealing temperature and time while the coercivity goes through a maximum, peaking at around 28nm. A very large coercivity (10.5kOe) is observed on cooling down to 77K while typical blocking eff…
Inter-valence charge transfer (IVCT) is electron transfer between two metal $M$ sites differing in oxidation states through a bridging ligand: $M^{n+1} + M'^{m} \rightarrow M^{n} + M'^{m+1}$. It is considered that IVCT is related to the hopping probability of electron (or the electron mobility) in solids. Since controlling the conductivity of ferromagnetic semiconductors (FMSs) is a key subject for the development of spintronic device applications, the manipulation of the conductivity through IVCT may become a new approach of band engineering in FMSs. In Ru-doped cobalt ferrite CoFe$_2$O$_4$ (…
Origin of magnetically dead layers in spinel ferrites $M\text{Fe}_2\text{O}_4$ grown on $\text{Al}_2\text{O}_3$: Effects of post-deposition annealing studied by XMCD
Cobalt ferrite ultrathin films with inverse spinel structure are among the best candidates for spin-filtering at room temperature. We have fabricated high-quality epitaxial ultrathin CoFe2O4 layers on Ag(001) following a three-step method: an ultrathin metallic CoFe2 alloy was first grown in coherent epitaxy on the substrate, and then treated twice with O2, first at RT and then during annealing. The epitaxial orientation, the surface, interface and film structure were resolved combining LEED, STM, Auger and in situ GIXRD. A slight tetragonal distortion was observed, that should drive the easy …
The Sn substituted Ni-Zn ferrites were synthesized by the standard double sintering technique using nano powders of nickel oxide (NiO), zinc oxide (ZnO), iron oxide (Fe2O3) and tin oxide (SnO2). The structural and electrical properties have been investigated by the X-ray diffraction, scanning electron microscopy, DC resistivity and dielectric measurements. Extra intermediate phase has been detected along with the inverse cubic spinel phase of Ni-Zn ferrite. Enhancement of grain size is observed in Sn substituted Ni-Zn ferrites. DC resistivity as a function of temperature has been investigated …
We present the low temperature magnetic properties in Ni1.5Fe1.5O4 ferrite as the function of pH at which the material was prepared by chemical route and post annealing temperature. The material is a ferri or ferromagnet, but showed magnetic blocking and random spin freezing process on lowering the measurement temperature down to 5 K. The sample prepared at pH =12 and annealed at 800 ^C showed a sharp magnetization peak at 105 K, the superparamagnetic blocking temperature of the particles. The magnetization peak remained incomplete within measurement temperature up to 350 K for rest of the sam…
Zinc oxide and Aluminum Ferrite were prepared Chemical route. The samples were characterized by XRD and VSM. Simulation of M-H plots of Co/CoO thin films were performed. Effect of parameters was observed on saturation magnetization.
We report structural, magnetic and dielectric properties of Co1.5Fe1.5O4 nanoparticles and their composites with non-magnetic NaNO3. The samples were derived from metal nitrates solution at different pH values. The chemical routed sample was air heated at 200 0C and 500 0C. Heating of the material showed unusual decrease of crystallite size, but cubic spinel structure is seen in all samples. The samples of Co1.5Fe1.5O4 showed substantially large room temperature ferromagnetic moment, electrical conductivity, dielectric constant, and low dielectric loss. The samples are soft ferromagnet and ele…
We report the synthesis of Y-substituted Mg-Zn ferrites using conventional standard ceramic technique. XRD patterns confirm the single phase cubic spinel structure up to x = 0.03 and appearance of a secondary phase of YFeO3for higher Y contents. FESEM images depict the distribution of grains and EDS spectra confirmed the absence of any unwanted element. Completion of solid state reaction and formation of spinel structure has been revealed from FTIR spectra. The FTIR data along with lattice constant, bulk density and porosity were further used to calculate the stiffness constant (Cij), elastic …
Ferrites with (inverse) spinel structure display a large variety of electronic and magnetic properties making some of them interesting for potential applications in spintronics. We investigate the thermally induced interdiffusion of Ni$^{2+}$ ions out of NiO into Fe$_3$O$_4$ ultrathin films resulting in off-stoichiometric nickelferrite-like thin layers. We synthesized epitaxial Fe$_3$O$_4$/NiO bilayers on Nb-doped SrTiO$_3$(001) substrates by means of reactive molecular beam epitaxy. Subsequently, we performed an annealing cycle comprising three steps at temperatures of 400\,$^{\circ}$C, 600\,…
We report high temperature synchrotron X-ray diffraction (SXRD), dc magnetization and current-voltage (I-V) characteristics for the samples of Co$_{2.75}$Fe$_{0.25}$O$_4$ ferrite. The material was prepared by chemical reaction of the Fe and Co nitrate solutions at pH = 11 and subsequent annealing at temperatures 200 0C, 500 0C and 900 0C. The measurements were performed by cycling the temperature from 300 K to high temperature (warming mode) and return back to 300 K (cooling mode). The SXRD patterns indicated a fine bi-phased cubic spinel structure in the highly Co rich spinel oxide. Magnetiza…
In this work, a successful synthesis of magnetic cobalt ferrite (CoFe2O4) nanoparticles is presented. The synthesized CoFe2O4 nanoparticles have a spherical shape and highly monodisperse in the selected solvent. The effect of different reaction conditions such as temperature, reaction time and varying capping agents on the phase and morphology is studied. Scanning transmission electron microscopy showed that the size of these nanoparticles can be controlled by varying reaction conditions. Both X-ray diffraction and energy dispersive X-ray spectroscopy corroborate the formation of CoFe2O4 spine…
The effect of sintering temperatures (Ts) on the structural and magnetic properties of Ni0.6Zn0.4Fe2O4 (NZFO) ferrites synthesized by conventional double sintering method has been reported. The samples are sintered at 1200, 1250 and 1300 °C. The X-ray diffraction (XRD) analysis reveals the formation of a single phase cubic spinel structure of the sample. The magnetic parameters such as saturation magnetization, Ms; coercive field, Hc; remanent magnetization, Mr and Bohr magneton, μB are determined and well compared with reported values. The obtained values are found to be 71.94 emu/gm and 1.2 …
The observation of strong magnetoelectric effects is reported in thick film bilayers and multilayers of ferrite-lead titanate zirconate (PZT) and lanthanum nanganite-PZT. The ferrites used in our studies included pure and zinc substituted cobalt-, nickel- and lithium ferrites. Samples were prepared by sintering 10-40 mm thick films obtained by tape-casting. Measurements of ME voltage coefficients at 10-1000 Hz indicated a giant ME effect in nickel ferrite-PZT, but a relatively weak coupling in other ferrite-PZT and manganite-PZT systems. Multilayers prepared by hot pressing was found to show a…
CoFe2O4 thin films (5 nm and 20 nm thick) were grown by oxygen assisted molecular beam epitaxy on Pt(111) at 523~K and subsequently annealed at 773 K in vacuum or oxygen. They were characterized in-situ using Auger Electron Spectroscopy, Low-Energy Electron Diffraction, Scanning Tunneling Microscopy and Conversion Electron Mössbauer Spectroscopy. The as-grown films were composed of small, nanometric grains. Annealing of the films produced an increase in the grain size and gave rise to magnetic order at room temperature, although with a fraction of the films remaining in the paramagnetic state.…
Mn-Zn ferrite nanoparticles have been subject of increasing research due to their desired properties for a wide range of applications. These properties include nanometer particle size control, tunable magnetic properties and low toxicity, providing these ferrites with the necessary requirements for cancer treatment via magnetic hyperthermia. During this master thesis, powders of Mn1-xZnxFe2O4 (x=0; 0.5; 0.8; 1) were synthesized via the sol-gel autocombustion and hydrothermal methods, aiming to optimize their structural and magnetic properties for further application in a ferrofluid. Samples we…
The mixed spinel, MgFe2O4 has been synthesized by ball-milling assisted sintering method. X-ray diffraction study confirms formation of cubic MgFe2O4 and the lattice parameter values calculated are a = b = c = 8.369(3) Å. Vibrating sample magnetometer measurements at room temperature shows a soft ferrimagnetic nature. Magneto-Dielectric and Magneto-Restive plots confirm coupling at room temperature in the prepared MgFe2O4. The peak at 500 Oe in the MD plot is due to the canting of Fe3+ ions distributed in octahedral and tetrahedral sites.
The synthesis of layered ferrite-lead titanate zirconate (PZT) and lanthanum nanganite-PZT and the observation of giant magneto-electric interactions are discussed. The ferrites used in our studies included pure and Zn substituted cobalt-, nickel- and lithium ferrites. Ferromagnetic manganites used included both calcium and strontium substituted systems. The samples were prepared from 10-40 mm thick films obtained by tape-casting. Our studies showed strong ME coupling in manganite-PZT and cobalt zinc ferrite-PZT, and a giant ME effect in nickel zinc ferrite-PZT. We found evidence for Zn assist…
A detailed correlative structural, magnetic and chemical analysis of non-stoichiometric cobalt ferrite micrometric crystals was performed by x-ray magnetic circular dichroism combined with photoemission microscopy, low energy electron microscopy, and atomic force microscopy. The vector magnetization at the nanoscale is obtained from magnetic images at different x-ray incidence angles and compared with micromagnetic simulations, revealing the presence of defects which pin the magnetic domain walls. A comparison of different types of defects and the domain walls location suggests that the main s…
A series of Ni0.6-x/2Zn0.4-x/2SnxFe2O4 (x = 0.0, 0.05, 0.1, 0.15, 0.2 and 0.3) (NZSFO) ferrite composites have been synthesized from nano powders using standard solid state reaction technique. The spinel cubic structure of the investigated samples has been observed by the X-ray diffraction (XRD). The magnetic properties such as saturation magnetization (Ms), remanent magnetization (Mr), coercive field (Hc) and Bohr magneton (B) are calculated from the hysteresis loops. The value of Ms is found to decrease with increasing Sn content in the samples. This change has been successfully explained by…
Structural properties, impedance, dielectric and electric modulus spectra have been used to investigate the sintering temperature (Ts) effect on the single phase cubic spinel Ni0.6Zn0.4Fe2O4 (NZFO) ceramics synthesized by standard ceramic technique. Enhancement of dielectric constants is observed with increasing Ts. The collective contribution of n-type and p-type carriers yields a clear peak in notable unusual dielectric behavior is successfully explained by the Rezlescu model. The non-Debye type long range dielectric relaxation phenomena is explained by electric modulus formalism. Fast respo…
Magnetoelectric (ME) coupling at low frequencies and at x-band have been investigated in layered samples containing zinc substituted lithium ferrite and lead zirconate titanate (PZT). Multilayers of Li0.5-x/2ZnxFe2.5-x/2O4 (LZFO) (x=0-0.4) and PZT were prepared by lamination and sintering of thick films. At low frequencies (10-1000 Hz), the ME voltage coefficient for transverse fields is higher than for longitudinal fields. With Zn substitution in the ferrite, transverse coupling increases to a maximum for x=0.3 and then decreases for higher x. Analysis based on our model for a bilayer implies…
The magnetization of thin films of cobalt ferrite frequently falls far below the bulk value of 455 kAm-1, which corresponds to an inverse cation distribution in the spinel structure with a significant orbital moment of about 0.6 muB that is associated with the octahedrally-coordinated Co2+ ions. The orbital moment is responsible for the magnetostriction and magnetocrystalline anisotropy, and its sensitivity to imposed strain. We have systematically investigated the structure and magnetism of films produced by pulsed-laser deposition on different substrates (TiO2, MgO, MgAl2O4, SrTiO3, LSAT, La…
Mg batteries with oxide cathodes have the potential to significantly surpass existing Li-ion technologies in terms of sustainability, abundance, and energy density. However, Mg intercalation at the cathode is often severely hampered by the sluggish kinetics of Mg$^{2+}$ migration within oxides. Here we report a combined theoretical and experimental study addressing routes to identify cathode materials with an improved Mg-ion mobility. Using periodic density functional theory calculations, Mg$^{2+}$ migration in oxide spinels has been studied, revealing key features that influence the activatio…
The mixed ferrite-cobaltites LnFe0.5Co0.5O3, with Ln = Eu & Dy have been prepared by a sol-gel method and the samples have been characterized using X-ray diffraction and electron microscopy. The magnetic investigations reveal that both samples ordered in canted antiferromagnetic structures near room temperature. The Dzyaloshinskii-Moriya or antisymmetric exchange interaction induces weak ferromagnetism due to canting of the antiferromagnetically ordered spins. In the case of Ln-Fe-Co orthoferrites, two magnetic sublattices (Ln3+-4f and Fe3+/Co3+-3d) generally align in opposite directions and i…