Probing charge transport and background doping in MOCVD grown (010) $β$-Ga$_{2}$O$_{3}$
Zixuan Feng, A F M Anhar Uddin Bhuiyan, Zhanbo Xia, Wyatt Moore, Zhaoying Chen, Joe F. McGlone, David R. Daughton, Aaron R. Arehart, Steven A. Ringel, Siddharth… 展开作者
Zixuan Feng, A F M Anhar Uddin Bhuiyan, Zhanbo Xia, Wyatt Moore, Zhaoying Chen, Joe F. McGlone, David R. Daughton, Aaron R. Arehart, Steven A. Ringel, Siddharth Rajan, Hongping Zhao
A new record-high room temperature electron Hall mobility ($μ_{RT} = 194\space cm^{2}/V\space s$ at $n\sim 8\times 10^{15}\space cm^{-3}$) for $β$-Ga2O3 is demonstrated in the unintentionally doped thin film grown on (010) semi-insulating substrate via metalorganic chemical vapor deposition (MOCVD). A peak electron mobility of $\sim 9500\space cm^{2}/V\space s$ is achieved at 45 K. Further investigation on the transport properties indicate the existence of sheet charges near the epi-layer/substrate interface. Si is identified as the primary contributor to the background carrier in both the epi-layer and the interface, originated from both surface contamination as well as growth environment. Pre-growth hydrofluoric acid cleaning of the substrate lead to an obvious decrease of Si impurity both at interface and in epi-layer. In addition, the effect of MOCVD growth condition, particularly the chamber pressure, on the Si impurity incorporation is studied. A positive correlation between the background charge concentration and the MOCVD growth pressure is confirmed. It is noteworthy that in a $β$-Ga2O3 film with very low bulk charge concentration, even a reduced sheet charge density can play an important role in the charge transport properties.
In this letter, we design and demonstrate an improved MOCVD grown reverse Al-composition graded contact layer to achieve low resistance contact to MOCVD grown ultra-wide bandgap (UWBG) Al0.70Ga0.30N channel metal semiconductor field-effect transistors (MESFETs). Increasing the thickness of the reverse graded layer was found to improve contact layer resistance significantly, leading to contact resistance of 3.3x10^-5 Ohm.cm2. Devices with gate length, LG, of 0.6 microns and source-drain spacing, LSD, of 1.5 microns displayed a maximum current density, IDSMAX, of 635 mA/mm with an applied gate v…
Ammonia (NH3) is commonly used as group V precursor in gallium nitride (GaN) metalorganic chemical vapor deposition (MOCVD). The high background carbon (C) impurity in MOCVD GaN is related to the low pyrolysis efficiency of NH3, which represents one of the fundamental challenges hindering the development of high purity thick GaN for vertical high power device applications. This work uses a laser-assisted MOCVD (LA-MOCVD) growth technique to address the high-C issue in MOCVD GaN. Carbon dioxide (CO2) laser with wavelength of 9.219 um was utilized to facilitate NH3 decomposition via resonant vib…
We report on the growth and characterization of Ge-doped \b{eta}-Ga2O3 thin films using a solid germanium source. \b{eta}-Ga2O3 thin films were grown using a low-pressure chemical vapor deposition (LPCVD) reactor with either an oxygen or gallium delivery tube. Films were grown on 6 degree offcut sapphire and (010) \b{eta}-Ga2O3 substrates with growth rates between 0.5 - 22 μm/hr. By controlling the germanium vapor pressure, a wide range of Hall carrier concentrations between 10^17 - 10^19 cm-3 were achieved. Low-temperature Hall data revealed a difference in donor incorporation depending on th…
The integration of MOCVD grown group III-A nitride device stacks on Si (111) substrates is critically dependent on the quality of the first AlN buffer layer grown. A Si surface that is both oxide-free and smooth is a primary requirement for nucleating such layers. A single parameter, the AlN layer growth stress, is shown to be an early (within 50 nm), clear (<0.5 GPa versus >1 GPa) and fail-safe indicator of the pre-growth surface, and the AlN quality required for successful epitaxy. Grain coalescence model for stress generation is used to correlate growth stress, the AlN-Si interface and crys…
This work demonstrates the first nonpolar vertical GaN on GaN pn power diodes grown on m-plane free standing substrates by MOCVD. The SEM and HRXRD results showed the good crystal quality of the homoepitaxial nonpolar structure with low defect densities. The CL result confirmed the nonpolar p GaN was of high quality with considerably reduced deep level states. At forward bias, the device showed good rectifying behaviors with a turn-on voltage of 4.0 V, an on-resistance of 2.3 mohmcm2, and a high on off ratio of 1e10. At reverse bias, the current leakage and breakdown were described by the trap…
N type conductivity of \b{eta}-Ga2O3 grown from the melt is typically achieved using Sn and Si. In this paper, we experimentally and computationally investigate Hf doping of \b{eta}-Ga2O3 single crystals using UV-Vis-NIR absorption and Hall Effect measurements and hybrid functional calculations. Unintentionally-doped and Hf-doped samples with a nominal concentration of 0.5at% were grown from the melt using vertical gradient freeze (VGF) and Czochralski method in mixed Ar+O2 atmosphere. We demonstrate Hf dopants, predicted to incorporate on the octahedral GaII site as a shallow donor, achieve d…
Si- and C-Induced Modifications in Vapor-Solid-Grown InGaAs Nanowires: From Crystal Structure to Carrier Dynamics
Walter Schottky Institute, TUM School of Natural Sciences, Technical University of Munich（沃尔特·肖特基研究所，慕尼黑工业大学自然科学学院）；Institute of Physics and Astronomy, Technical University Berlin（柏林工业大学物理与天文研究所）
Two-dimensional (2D) indium monoselenide (InSe) has attracted significant attention as a III-VI two-dimensional semiconductor (2D) with a combination of favorable attributes from III-V semiconductors as well as van der Waals 2D transition metal dichalcogenides. Nevertheless, the large-area synthesis of phase-pure 2D InSe remains unattained due to the complexity of the binary In-Se system and the difficulties in promoting lateral growth. Here, we report the first polymorph-selective synthesis of epitaxial 2D InSe by metal-organic chemical deposition (MOCVD) over 2 inch diameter sapphire wafers.…
We report on n-type degenerate doping in MOVPE grown \b{eta}-(Al0.26Ga0.74)2O3 epitaxial thin films and modulation doping in \b{eta}-(Al0.26Ga0.74)2O3/\b{eta}-Ga2O3 heterostructure. Alloy composition is confirmed using HRXRD measurements. Carrier concentration in the thin films is proportional to the silane molar flow. Room temperature hall measurements showed a high carrier concentration of 6x1018-7.3x1019 cm-3 with a corresponding electron mobility of 53-27 cm2/V.s in uniformly-doped \b{eta}-(Al0.26Ga0.74)2O3 layers. Modulation doping is used to realize a total electron sheet charge of 2.3x1…
In this work, we report on the growth of high-mobility $β$-Ga$_2$O$_3$ homoepitaxial thin films grown at a temperature much lower than the conventional growth temperature window for metalorganic vapor phase epitaxy. Low-temperature $β$-Ga$_2$O$_3$ thin films grown at 600$^{\circ}$C on Fe-doped (010) bulk substrates exhibits remarkable crystalline quality which is evident from the measured room temperature Hall mobility of 186 cm$^2$/Vs for the unintentionally doped films. N-type doping is achieved by using Si as a dopant and controllable doping in the range of 2$\times$10$^{16}$ - 2$\times$10$…
We show evidence that tunnel junctions (TJs) in GaN grown by metal-organic vapor phase epitaxy are dominated by trap-assisted (Poole-Frenkel) tunneling. This stems from observations of the careful optimized doping for the TJs. Especially the p$^{++}$ and the n$^{++}$ layers are far from ideal. The n$^{++}$ layer induces 3D growth, which can be seen by a rising oxygen signal in Secondary Ions Mass Spectroscopy (SIMS). Furthermore, Mg segregation observed by SIMS indicates a depletion region of more than 10 nm. Still, we could realize TJ based LEDs with a low penalty voltage of 1.1 V and a speci…
We report on low-temperature MOVPE growth of silicon delta-doped \b{eta}-Ga2O3 films with low FWHM. The as-grown films are characterized using Secondary-ion mass spectroscopy, Capacitance-Voltage and Hall techniques. SIMS measurements show that surface segregation is the chief cause of large FWHM in MOVPE-grown films. The surface segregation coefficient (R) is observed to reduce with reduction in the growth temperature. Films grown at 600 °C show an electron concentration of 9.7 x 1012 cm-2 and a FWHM of 3.2 nm. High resolution scanning/transmission electron microscopy of the epitaxial film di…
We report on silicon delta doping of metalorganic vapor-phase epitaxy-grown \b{eta}-Ga2O3 thin films using silane precursor. Delta-doped \b{eta}-Ga2O3 epitaxial films are characterized using capacitance-voltage profiling and secondary-ion mass spectroscopy. Electron sheet charge density in the range of 2.9e12 cm-2 to 8e12 cm-2 with a half width at half maximum ranging from 6.2 nm to 3.5 nm is measured. We also demonstrate a high density (6.4e12 cm-2) degenerate two-dimensional electron gas using a delta-doped \b{eta}-(Al0.26Ga0.74)2O3/\b{eta}-Ga2O3 heterostructure.The total charge could also i…