在Ni_（0：05）TaS_2单晶中发现了超导电性。采用NaCl/KCl助熔剂法成功地生长了Ni 0：05 TaS 2单晶。得到的Ni 0：05 TaS 2的晶格常数c为1.1999nm，明显小于2 H-TaS 2的晶格常数c（1.208nm）。电阻率和磁化强度的测量表明，Ni_（0：05）TaS_2的超导转变温度从0.8K（2 H-TaS_2）提高到3.9K。在Ni_（0：05）TaS_2中，基体化合物2 H-TaS_2的电荷密度波跃迁被抑制。NaCl/KCl助熔剂法生长Ni_（0：05）TaS_2单晶的成功表明，NaCl/KCl助熔剂法是一种可行的层状过渡金属二硫属化合物单晶生长方法。
英文摘要：
Superconductivity was discovered in a Ni0:05TaS2 single crystal. A Ni0:05TaS2 single crystal was successfully grown via the NaCl/KCl flux method. The obtained lattice constant c of Ni0:05TaS2 is 1.1999 nm, which is significantly smaller than that of 2H-TaS2 (1.208 nm). Electrical resistivity and magnetization measurements reveal that the superconductivity transition temperature of Ni0:05TaS2 is enhanced from 0.8 K (2H-TaS2) to 3.9 K. The charge-density-wave transition of the matrix compound 2H-TaS2 is suppressed in Ni0:05TaS2. The success of Ni0:05TaS2 single crystal growth via a NaCl/KCl flux demonstrates that NaCl/KCl flux method will be a feasible method for single crystal growth of the layered transition metal dichalcogenides.
Crystal structure, physical properties and superconductivity in $A_{x}$Fe$_2$Se$_2$ single crystals
我们研究了不同$A_x$ Fe $_2$ Se $_2$单晶（$A$ = K，Rb，Cs）的结构、输运性质和超导电性之间的相关性。在X射线单晶衍射图中观察到两组（00 $l$）反射，并且起因于插入的碱原子的本征不均匀分布。超导电性的发生与{ \sl c}轴晶格常数密切相关，而$A$含量对超导电性至关重要。在电阻率中观察到的驼峰似乎与超导性无关。在$A_x$ Fe $_2$ Se $_2$中的FeSe层内存在许多缺陷，而它们的$T_{\rm c}$变化不大。在这个意义上，超导性对Fe和Se空位是稳健的。在正常状态下，非常高的电阻率应该由导电FeSe层中的这种缺陷引起。$A_x$ Fe $_2$ Se $_2$（$A$ = K、Rb和Cs）单晶在正常状态下显示相同的磁化率行为，并且在电阻率的峰温度下未观察到磁化率的异常。Rb $_x$ Fe $_2$ Se $_2$和K $_x$ Fe $_2$ Se $_2$单晶比热的明显跃变表明这些晶体具有良好的体超导性。
Superconductivity in a Scandium Borocarbide with a Layered Crystal Structure
超导体中近室温超导性的发现激发了对传统超导体材料的进一步研究。为了在含轻元素的材料中实现适度高的临界温度$(T_\mathrm{c})$，我们在钪硼碳化物系统中探索了新的超导相。本文报道了一种新的三元Sc-B-C化合物的超导电性。通过Rietveld分析确定的晶体结构属于四面体空间群$P4/ncc$。通过补充使用密度泛函理论计算，发现化合物的化学式表示为Sc $_{20}$ C $_{8-x}$ B $_x$ C $_{20}$（$x=1\:\mathrm{or}\:2$）。有趣的是，少量的B对稳定目前的结构是必不可少的。我们的实验在$T_\mathrm{c}=7.7\:\mathrm{K}$上揭示了典型的II型超导性。此外，我们计算的状态密度内的第一性原理的方法，发现的贡献的Sc-3d轨道是主要负责的超导性。
Absence of a Competition between Magnetism and Superconductivity in the Layered Nickel Borocarbides: Common Correlation Tc with Crystal Chemical Parameters for Magnetic and Nonmagnetic Compounds
Synthesis, crystal structure and superconductivity in Rb$Ln_2$Fe$_4$As$_4$O$_2$ ($Ln$ = Sm, Tb, Dy and Ho)
本文合成了四种铁基砷氧化物超导体Rb $Ln_2$ Fe $_4$ As $_4$ O $_2$（$Ln$ = Sm，Tb，Dy和Ho），它们是由RbFe $_2$ As $_2$和$Ln$ FeAsO共生而成。发现RbFe $_2$ As $_2$和$Ln$ FeAsO之间的晶格匹配对相的形成至关重要。结构共生导致双不对称的Fe $_2$ As $_2$层，其被绝缘的$Ln_2$ O $_2$板隔开。因此，该材料是本征掺杂在0.25个空穴/Fe原子的水平，体超导性出现在$T_\mathrm{c}$ = 35.8，34.7，34.3和33.8 K，分别为$Ln$ = Sm，Tb，Dy和Ho。对晶体结构和$T_\mathrm{c}$之间相关性的研究表明，层间耦合可能对超导电性的优化起到额外的作用。
Conventional superconductivity in single-crystalline BiPt
McMaster University（麦克马斯特大学）；University of Minnesota（明尼苏达大学）；Technion-Israel Institute of Technology（以色列理工学院）；Simon Fraser University（西蒙菲莎大学）；Indian Institute of Science Education and Research Pune（印度科学教育与研究学院普纳分校）；TRIUMF（特里姆夫实验室）
Coexisting electronic smectic liquid crystal and superconductivity in a Si square-net semimetal
RIKEN Center for Emergent Matter Science（理化学研究所新兴物质科学中心）；Institute for Solid State Physics, The University of Tokyo（东京大学固体物理研究所）；Department of Physics and Center for Theoretical Physics, National Taiwan University（国立台湾大学物理系暨理论物理中心）；Department of Applied Physics, Nagoya University（名古屋大学应用物理系）；Institute of Multidisciplinary Research for Advanced Materials, Tohoku University（东北大学先进材料跨学科研究所）；Physics Division, National Center for Theoretical Sciences（国家理论科学中心物理分部）
Coexistence of superconductivity and antiferromagnetism in single crystals $A_{0.8}Fe_{2-y}Se_2$ (A= K, Rb, Cs, Tl/K and Tl/Rb): evidence from magnetization and resistivity
测量了$A$ Fe $_{2-y}$ Se $_2$（$A$ = KPDMATHABMP，RbPDMATHABMP，$_{0.8}$，$_{0.5}$ $_{0.3}$和$_{0.4}$ $_{0.4}$）单晶在5 ~ 600 K温度范围内的电阻率和磁化率.在低温电阻率和磁化率中观察到了一个急剧的超导转变，磁化率的Meissner体积分数为100%，而在Neel温度（$T_N$）高达500 ~ 540 K（取决于A）时观察到了反铁磁转变。它表明超导性和反铁磁性共存。在略高于$T_{\rm N}$的温度下，由于Fe空位有序化引起的结构转变引起电阻率的急剧增加。在具有如此高的$T_{\rm N}$的反铁磁有序态中出现超导性可能暗示了这种非常规超导体中的新物理。
Weakly anisotropic superconductivity of Pr4Ni3O10 single crystals
ShanghaiTech University（上海科技大学）；Center for High Pressure Science and Technology Advanced Research（高压科学与技术先进研究中心）；Institute for Shanghai Advanced Research in Physical Sciences (SHARPS)（上海物理科学研究院）；Songshan Lake Materials Laboratory（松山湖材料实验室）；Qufu Normal University（曲阜师范大学）；University of Oxford（牛津大学）；Southeast University（东南大学）；Tsinghua University（清华大学）
Anisotropic superconductivity and unusually robust electronic critical field in single crystal La$_{7}$Ir$_{3}$
报道了多晶La $_{7}$ Ir $_{3}$显示超导性破坏时间反演对称性，同时也具有各向同性的$s$ -波隙。这种非中心对称超导体的单晶对于理解该系统中电子配对机制的性质是非常必要的。本文报道了用提拉法生长La $_{7}$ Ir $_{3}$高质量单晶。利用X射线、磁化强度、电阻率和热容测量研究了这些大晶体的结构和超导性质。我们观察到一个明确的各向异性，在较低和较高的临界磁场施加平行和垂直于六角$c$轴的磁场。我们还报告了一个强大的电子临界场的存在下，偏离从热容量，这是表面超导性的标志来自上临界场。
Evidence for Coexistence of Superconductivity and Magnetism in Single Crystals of Co-doped SrFe$_2$As$_2$
为了研究Co掺杂SrFe $_2$ As $_2$中磁性和超导电性是否共存，我们制备了SrFe $_{2-x}$ Co $_x$ As $_2$，$x$ = 0和0.4的单晶，并通过X射线衍射、零场和外加场（最高达9 T）以及常压和外加压力（最高达1.6 GPa）下的电阻率和磁化率对其进行了表征。当$x$ = 0.4时，在120 K下存在自旋密度波跃迁的磁性和电阻证据，而$T_c$ = 19.5 K -表明磁性和超导性共存。讨论这些结果如何与报道的结果相比，无论是在SrFe $_{2-x}$ Co $_x$作为$_2$和其他掺杂122化合物，给出。