We report the synthesis and basic physical properties of single crystals of CaFe2As2, an isostructural compound to BaFe2As2 which has been recently doped to produce superconductivity. CaFe2As2 crystalizes in the ThCr2Si2 structure with lattice parameters a = 3.907(4) A and c = 11.69(2) A. Magnetic susceptibility, resistivity, and heat capacity all show a first order phase transition at T_0 171 K. The magnetic susceptibility is nearly isotropic from 2 K to 350 K. The heat capacity data gives a Sommerfeld coefficient of 8.2 +- 0.3 mJ/molK2, and does not reveal any evidence for the presence of high frequency (> 300 K) optical phonon modes. The Hall coefficient is negative below the transition indicating dominant n-type carriers.
We report a combined study of the Nernst coefficient (v), Hall effect and thermoelectric power of CaFe2As2 and CaFe1.92Co0.08As2 single crystals. The absolute value of v in both samples is enhanced, probably due to ambipolar flow of electron- and hole-like quasiparticles. The onset of spin-density-wave order in CaFe2As2 causes further rapid rise of the Nernst coefficient. On the contrary, in the CaFe1.92Co0.08As2 crystal we do not see any feature of v(T), which could be clearly associated with SDW fluctuations. In this Co-doped sample there is also no noticeable increase in of v in the vicinit…
We report pressure-induced superconductivity in a single crystal of CaFe2As2. At atmospheric pressure, this material is antiferromagnetic below 170 K but under an applied pressure of 0.69 GPa becomes superconducting, with a transition temperature Tc exceeding 10 K. The rate of Tc suppression with applied magnetic field is -0.7 K/T, giving an extrapolated zero-temperature upper critical field of 10-14T.
The effects of pressure generated in a liquid medium, clamp, pressure cell on the in-plane and c-axis resistance, temperature-dependent Hall coefficient and low temperature, magnetoresistance in CaFe2As2 are presented. The T - P phase diagram, including the observation of a complete superconducting transition in resistivity, delineated in earlier studies is found to be highly reproducible. The Hall resistivity and low temperature magnetoresistance are sensitive to different states/phases observed in CaFe2As2. Auxiliary measurements under uniaxial, c-axis, pressure are in general agreement with…
We report the synthesis, and structural and physical properties of CaFe4As3 single crystals. Needle-like single crystals of CaFe4As3 were grown out of Sn flux and the compound adopts an orthorhombic structure as determined by X-ray diffraction measurements. Electrical, magnetic, and thermal properties indicate that the system undergoes two successive phase transitions occurring at TN1 ~ 90 K and TN2 ~ 26 K. At TN1, electrical resistivities (ρ(b) and ρ(ac)) are enhanced while magnetic susceptibilities (χ(b) and χ(ac)) are reduced in both directions parallel and perpendicular to the b-axis, cons…
We report anisotropic dc magnetic susceptibility $χ(T)$, electrical resistivity $ρ(T)$, and heat capacity $C(T)$ measurements on the single crystals of CaFe$_{2-x}$Co$_x$As$_2$ for $x$ = 0 and 0.06. Large sized single crystals were grown by the high temperature solution method with Sn as the solvent. For the pure compound with $x$ = 0, a high temperature transition at 170 K is observed which is attributed to a combined spin density wave (SDW) ordering and a structural phase transition. On the other hand, for the Co-doped samples for $x$ = 0.06, the SDW transition is suppressed while supercondu…
We studied the effect of hydrostatic pressure (P) on the structural phase transitions and superconductivity in the ternary and pseudo-ternary iron arsenides CaFe2As2, BaFe2As2, and (Ba0.55K0.45)Fe2As2, by means of measurements of electrical resistivity (rho) in the 1.8 - 300 K temperature (T) range, pressures up to 20 kbar, and magnetic fields up to 9 T. CaFe2As2 and BaFe2As2 (lightly doped with Sn) display structural phase transitions near 170 K and 85 K, respectively, and do not exhibit superconductivity in ambient pressure, while K-doped (Ba0.55K0.45)Fe2As2 is superconducting for T < 30 K. …
Single crystals of CaFe$_2$(As$_{1-x}$P$_x$)$_2$ are found to exhibit the tetragonal (T) to collapsed-tetragonal (cT) transition at $T_{\rm cT} \lesssim100$\,K for $x>0.05$. The c-axis shrinks by $\sim9$% below $T_{\rm cT}$, which substantially diminishes the interband nesting between the hole and electron bands. In sharp contrast to the superconducting T phase of $A$Fe$_2$(As$_{1-x}$P$_x$)$_2$ ($A=$ Ba, Sr), where the anomalous non-Fermi liquid transport properties are observed, the resistivity, Hall coefficient, and magnetoresistance data in the Ca-based system all indicate that the standard…
Superconductivity in Iron-Arsenic based pnictides emerges in close proximity to an antiferromagnetic (AFM)ordered parent state and the AFM phase overlaps with superconducting (SC) phase in some pnictides for certain range of doping. CaFe2-xNixAs2 belongs to this category, where both the phases overlap. Here we use scanning tunneling microscopy and spectroscopy to investigate the local electronic properties of uderdoped CaFe1.96Ni0.04As2 single crystals in the vicinity of the boundary of the two phases. Both resistivity and magnetic measurements show that a tiny portion (~ 1.2 %) of this compou…
Here we investigate single crystals of CaCo$_{5}$As$_{3}$ by means of single crystal X-ray diffraction, microprobe, magnetic susceptibility, heat capacity, and pressure-dependent transport measurements. CaCo$_{5}$As$_{3}$ shares the same structure of CaFe$_{4}$As$_{3}$ with an additional Co atom filling a lattice vacancy and undergoes a magnetic transition at $T_{M} = 16$ K associated with a frustrated magnetic order. CaCo$_{5}$As$_{3}$ displays metallic behavior and its Sommerfeld coefficient ($γ= 70$ mJ/mol.K$^{2}$) indicates a moderate enhancement of electron-electron correlations. Transpor…
Single crystal neutron and high-energy x-ray diffraction have identified the phase lines corresponding to transitions between the ambient-pressure tetragonal (T), the antiferromagnetic orthorhombic (O) and the non-magnetic collapsed tetragonal (cT) phases of CaFe2As2. We find no evidence of additional structures for pressures up to 2.5 GPa (at 300 K). Both the T-cT and O-cT transitions exhibit significant hysteresis effects and we demonstrate that coexistence of the O and cT phases can occur if a non-hydrostatic component of pressure is present. Measurements of the magnetic diffraction peaks s…
We report $^{75}$As Nuclear Magnetic Resonance data in a single crystal of CaFe$_2$As$_2$. The Knight shift, electric field gradient, and spin-lattice relaxation rate are strongly temperature dependent in the paramagnetic state, and change discontinuously at the structural transition temperature, $T_S=T_N=167$ K. Immediately below, the NMR spectra reveal an internal field at the As site associated with the presence of a commensurate magnetic order. These results indicate that the structural and magnetic transitions in CaFe$_2$As$_2$ are first order and strongly coupled, and that the electron d…
Temperature dependent measurements of 57Fe Mossbauer spectra on CaFe2As2 single crystals in the tetragonal and collapsed tetragonal phases are reported. Clear features in the temperature dependencies of the isomer shift, relative spectra area and quadrupole splitting are observed at the transition from the tetragonal to the collapsed tetragonal phase. From the temperature dependent isomer shift and spectral area data, an average stiffening of the phonon modes in the collapsed tetragonal phase is inferred. The quadrupole splitting increases by ~25% on cooling from room temperature to ~100 K in …
The interplay between magnetism and crystal structures in three CaFe$_{2}$As$_{2}$ samples is studied. For the nonmagnetic quenched crystals, different crystalline domains with varying lattice parameters are found, and three phases (orthorhombic, tetragonal, and collapsed tetragonal) coexist between T$_{S}$ = 95 K and 45 K. Annealing of the quenched crystals at 350°C leads to a strain relief through a large (~1.3 %) expansion of the c-parameter and a small (~0.2 %) contraction of the a-parameter, and to local ~0.2 Å displacements at the atomic-level. This annealing procedure results in the mos…
The antiferromagnet CaFe$_2$As$_2$ does not become superconducting when subject to ideal hydrostatic pressure conditions, where crystallographic and magnetic states also are well defined. By measuring electrical resistivity and magnetic susceptibility under quasi-hydrostatic pressure, however, we find that a substantial volume fraction of the sample is superconducting in a narrow pressure range where collapsed tetragonal and orthorhombic structures coexist. At higher pressures, the collapsed tetragonal structure is stabilized, with the boundary between this structure and the phase of coexistin…
Neutron scattering measurements of the magnetic excitations in single crystals of antiferromagnetic CaFe2As2 reveal steeply dispersive and well-defined spin waves up to an energy of 100 meV. Magnetic excitations above 100 meV and up to the maximum energy of 200 meV are however broader in energy and momentum than the experimental resolution. While the low energy modes can be fit to a Heisenberg model, the total spectrum cannot be described as arising from excitations of a local moment system. Ab-initio calculations of the dynamic magnetic susceptibility suggest that the high energy behavior is …
We present 75As nuclear magnetic resonance data in the paramagnetic and magnetic states of single crystal CaFe2As2. The electric field gradient and the internal magnetic field at the As sites change discontinuously below the first order structural transition at T0 = 169 K. In the magnetic state, we find a single value of the internal hyperfine field consistent with commensurate antiferromagnetic order of Fe moments pointing in the ab plane. The spin lattice relaxation rate shows Korringa behavior for T<T0/3, reflecting the metallic nature of the ordered state. Surprisingly, 1/T1 exhibits a sma…
Aliovalent rare earth substitution into the alkaline earth site of CaFe2As2 single-crystals is used to fine-tune structural, magnetic and electronic properties of this iron-based superconducting system. Neutron and single crystal x-ray scattering experiments indicate that an isostructural collapse of the tetragonal unit cell can be controllably induced at ambient pressures by choice of substituent ion size. This instability is driven by the interlayer As-As anion separation, resulting in an unprecedented thermal expansion coefficient of $180\times 10^{-6}$ K$^{-1}$. Electrical transport and ma…
We report ultrafast quasiparticle (QP) dynamics and coherent acoustic phonons in undoped CaFe_2As_2 iron pnictide single crystals exhibiting spin-density wave (SDW) and concurrent structural phase transition at temperature TSDW ~ 165 K using femtosecond time-resolved pump-probe spectroscopy. The contributions in transient differential reflectivity arising from exponentially decaying QP relaxation and oscillatory coherent acoustic phonon mode show large variations in the vicinity of T_SDW. From the temperature-dependence of the QP recombination dynamics in the SDW phase, we evaluate a BCS-like …
We measured the transport properties and susceptibility of single crystals Ca$_{1-x}$La$_x$Fe$_2$As$_2$(x=0, 0.05, 0.1, 0.15, 0.19 and 0.25). Large in-plane resistivity anisotropy similar to that in Co-doped 122 iron-pnictides is observed although no transition metals were introduced in the FeAs-plane. The in-plane resistivity anisotropy gradually increases with La doping below T$_{SDW}$, being different from the hole-doped 122 superconductors. The susceptibilities of the samples show that La doping leads to suppression of SDW and induces a Curie-Weiss-like behavior at low temperature, which i…
Magnetism in the orthorhombic metal CaFe$_4$As$_3$ was examined through neutron diffraction for powder and single crystalline samples. Incommensurate (${\bm q}_{\rm m}\approx (0.37-0.39)\times{\bm b}^{\ast}$) and predominantly longitudinally ($\parallel b$) modulated order develops through a 2nd order phase transition at $T_{\rm N}=89.63(6)$ K with a 3D Heisenberg-like critical exponent $β=0.365(6)$. A 1st order transition at $T_2=25.6(9)$ K is associated with the development of a transverse component, locking ${\bm q}_{\rm m}$ to $0.375(2){\bm b}^{\ast}$, and increasing the moments from 2.1(1…
TThe parent compounds of iron-arsenide superconductors, $A$Fe$_{2}$As$_{2}$ ($A$=Ca, Sr, Ba), undergo a tetragonal to orthorhombic structural transition at a temperature $T_{\mathrm{TO}}$ in the range 135 to 205K depending on the alkaline earth element. Below $T_{\mathrm{TO}}$ the free standing crystals split into equally populated structural domains, which mask intrinsic, in-plane, anisotropic properties of the materials. Here we demonstrate a way of mechanically detwinning CaFe$_{2}$As$_{2}$ and BaFe$_{2}$As$_{2}$. The detwinning is nearly complete, as demonstrated by polarized light imaging…
Starting from the orthorhombic magnetically ordered phase, we investigate the effects of uniaxial tensile and compressive stresses along a, b, and the diagonal a+b directions in BaFe2As2 and CaFe2As2 in the framework of ab initio density functional theory (DFT) and a phenomonological Ginzburg-Landau model. While -contrary to the application of hydrostatic or c-axis uniaxial pressure- both systems remain in the orthorhombic phase with a pressure-dependent nonzero magnetic moment, we observe a sign-changing jump in the orthorhombicity at a critical uniaxial pressure, accompanied by a reversal of…
At ambient pressure CaFe2As2 has been found to undergo a first order phase transition from a high temperature, tetragonal phase to a low temperature orthorhombic / antiferromagnetic phase upon cooling through T ~ 170 K. With the application of pressure this phase transition is rapidly suppressed and by ~ 0.35 GPa it is replaced by a first order phase transition to a low temperature collapsed tetragonal, non-magnetic phase. Further application of pressure leads to an increase of the tetragonal to collapsed tetragonal phase transition temperature, with it crossing room temperature by ~ 1.7 GPa. …
Single crystals of Ca(Fe1-xRux)2As2 (0<x<0.065) and Ca1-yLay(Fe0.973Ru0.027)2As2 (0<y<0.2) have been synthesized and studied with respect to their structural, electronic and magnetic properties. The partial substitution of Fe by Ru induces a decrease of the c-axis constant leading for x<0.023 to a suppression of the coupled magnetic and structural (tetragonal to orthorhombic) transitions. At x_cr=0.023 a first order transition to a collapsed tetragonal (CT) phase is found, which behaves like a Fermi liquid and which is stabilized by further increase of x. The absence of superconductivity near …
Using a combination of muon-spin relaxation ($μ$SR), inelastic neutron scattering (INS) and nuclear magnetic resonance (NMR), we investigated the novel iron-based superconductor with a triclinic crystal structure (CaFe$_{1-x}$Pt$_x$As)$_{10}$Pt$_3$As$_8$ (T$_{\rm c}$ = 13 K), containing platinum-arsenide intermediary layers. The temperature dependence of the superfluid density obtained from the $μ$SR relaxation-rate measurements indicates the presence of two superconducting gaps, $Δ_\text{1}\ggΔ_\text{2}$. According to our INS measurements, commensurate spin fluctuations are centered at the ($…
The transport properties, phase diagram, and dopant distribution are investigated in systematically Nd doped CaFe_2As_2 single crystals. Coexistence of two superconducting (SC) phases with different critical transition temperature (T_c) is observed. The low-T_c phase emerges as x >= 0.031, and the T_c value increases to its maximum value of about 20 K at x = 0.083, the maximum doping level in our study. As x >= 0.060, the high-T_c phase with a T_c value of about 40 K is observed. The structure transition (STr) from tetragonal to orthorhombic phase vanishes suddenly around x = 0.060, where a ne…
The sodium rhodate NaRh2O4 was synthesized for the first time and characterized by neutron and x-ray diffraction studies, measurements of magnetic susceptibility, specific heat, electrical resistivity, and the Seebeck coefficient. NaRh2O4 crystallizes in the CaFe2O4-type structure, which is comprised of a characteristic RhO6 octahedra network. The compound is metallic in nature, probably reflecting the 1 to 1 mixed valence character of Rh(III) and Rh(IV) in the network. For further studies of the compound, the Rh valence was varied significantly by means of an aliovalent substitution: the full…
The recent discovery and subsequent developments of FeAs-based superconductors have presented novel challenges and opportunities in the quest for superconducting mechanisms in correlated-electron systems. Central issues of ongoing studies include interplay between superconductivity and magnetism as well as the nature of the pairing symmetry reflected in the superconducting energy gap. In the cuprate and RE(O,F)FeAs (RE = rare earth) systems, the superconducting phase appears without being accompanied by static magnetic order, except for narrow phase-separated regions at the border of phase bou…
Platelet-like single crystals of the Ca(Fe1-xCox)2As2 series having lateral dimensions up to 15 mm and thickness up to 0.5 mm were obtained from the high temperature solution growth technique using Sn flux. Upon Co doping, the c-axis of the tetragonal unit cell decreases, while the a-axis shows a less significant variation. Pristine CaFe2As2 shows a combined spin-density-wave and structural transition near T = 166 K which gradually shifts to lower temperatures and splits with increasing Co-doping. Both transitions terminate abruptly at a critical Co-concentration of xc = 0.075. For x \geq 0.05…
Intercalation of organic cations in superconducting iron selenide can significantly increase the critical temperature (Tc). We present an electrochemical method using beta-FeSe crystals (Tc ~ 8 K) floating on a mercury cathode to intercalate tetramethylammonium ions (TMA+) quantitatively to obtain bulk samples of (TMA)0.5Fe2Se2 with Tc = 43 K. The layered crystal structure is closely related to the ThCr2Si2-type with disordered TMA+ ions between the FeSe layers. Although the organic ions are not detectable by X-ray diffraction, packing requirements as well as first principle DFT calculations c…
Fluorides in general are characterized by big variety of crystal structures, whereas those containing transition metals also often show sizable magnetic properties. The tendency of fluorine to form linear chain structures in many cases results in low-dimensional magnetism. Despite the plethora of magnetic phenomena in fluorides, their magnetoelectric properties are less studied than those of oxides. In the present work we theoretically study the magnetic and magnetoelectric properties of spin-chain compounds CaFeF$_5$ and SrFeF$_5$. The density functional theory is employed for determination o…
Single crystalline CaFe2As2 and (Ca1-xNax)Fe2As2 polycrystals (0 < x < 0.66) are synthesized and characterized using structural, magnetic, electronic transport, and heat capacity measurements. These measurements show that the structural/magnetic phase transition in CaFe2As2 at 165 K is monotonically suppressed by the Na doping and that superconductivity can be realized over a wide doping region. For 0.3 < x < 0.36, the magnetic susceptibilities indicate the possible coexistence of the spin density wave (SDW) and superconductivity. Superconducting phases corresponding to the Na doping level in …
NMR measurements have been performed on single crystals of Ba$_{1-x}$K$_{x}$Fe$_2$As$_2$ (x = 0, 0.45) and CaFe$_2$As$_2$ grown from Sn flux. The Ba-based pnictide crystals contain significant amounts of Sn in their structure, $\sim 1$%, giving rise to magnetic impurity effects evident in the NMR spectrum and in the magnetization. Our experiments show that the large impurity magnetization is broadly distributed on a microscopic scale, generating substantial magnetic field gradients. There is a concomitant 20% reduction in the transition temperature which is most likely due to magnetic electron…
The new quaternary iron arsenide-fluoride SrFeAsF with the tetragonal ZrCuSiAs-type structure was synthesized and the crystal structure was determined by X-ray powder diffraction (P4/nmm, a = 399.30(1), c = 895.46(1) pm). SrFeAsF undergoes a structural and magnetic phase transition at 175 K, accompanied by strong anomalies in the specific heat, electrical resistance and magnetic susceptibility. In the course of this transition, the space group symmetry changes from tetragonal (P4/nmm) to orthorhombic (Cmme). 57Fe Moessbauer spectroscopy experiments show a single signal at room temperature at a…
We report on synthesis of single crystals of BaFe2Se3 and study of their crystal and magnetic structures by means of synchrotron single crystal X-ray and neutron powder diffraction. The crystal structure has orthorhombic symmetry and consists of double chains of FeSe4 edge connected tetrahedra intercalated by barium. Below 240 K long range block-spin checkerboard antiferromagnetic (AFM) order is developed. The magnetic structure is similar to one observed in A0.8Fe1.6Se2 (A=K, Rb or Cs) superconductors. The crystals exhibit a transition to the diamagnetic state with an onset transition tempera…
A new Cr-based quasi-one-dimensional superconductor Na2Cr3As3 was synthesized by an ion-exchange method in sodium naphthalenide solution. The crystals are thread-like and the structure was analyzed by X-ray diffraction with a noncentrosymmetric hexagonal space group P-6m2 (No. 187), in which the (Cr3As3)2- linear chains are separated by Na+ ions, and the refined lattice parameters are a = 9.239(2) Å and c = 4.209(6) Å. The measurements for electrical resistivity, magnetic susceptibility, and heat capacity reveal a superconducting transition with unconventional characteristic at the Tc of 8.6 K…
Infinite-layer (IL) nickelates are an emerging family of superconductors whose similarities and differences to cuprate superconductors are under intense debate. To date, the IL phase of nickelates can only be reached via topotactic oxygen reduction of the perovskite phase, using H$_2$ gas or reducing agents such as CaH$_2$. While the topotactic reduction method has been widely employed on thin film and polycrystalline powder samples, the reduction of La$_{1-x}$Ca$_x$NiO$_3$ single-crystals with lateral dimensions up to 150 $μ$m was achieved only recently, using an indirect contact method with …
Layered bismuthides of the family ATM2Bi2 are showing very interesting structural and physical properties. Here, we report crystal growth and characterization of new ternary layered bismuthides: RbCd2Bi2, RbZn2Bi2 and KZn2Bi2. Single crystals were grown by self-flux technique. As grown crystals were characterized by combination of powder X-ray diffraction, scanning electron microscopy, energy-dispersive X-ray spectroscopy and single crystal X-ray diffraction. All novel compounds crystallize in layered ThCr2Si2 structure type with plate-like morphology with weak bonding between layers. Signific…
We report the successful synthesis of FeSe$_{1-x}$S$_{x}$ single crystals with $x$ ranging from 0 to 1 via a hydrothermal method. A complete phase diagram of FeSe$_{1-x}$S$_{x}$ has been obtained based on resistivity and magnetization measurements. The nematicity is suppressed with increasing $x$, and a small superconducting dome appears within the nematic phase. Outside the nematic phase, the superconductivity is continuously suppressed and reaches a minimum $T_c$ at $x$ = 0.45; beyond this point, $T_c$ slowly increases until $x$ = 1. Intriguingly, an anomalous resistivity upturn with a chara…
A macroscopic single crystal of $γ_{\rm II}$-Li\(_2\)FeSiO\(_4\) has been grown by means of the high-pressure optical floating-zone technique. Static magnetic susceptibility $χ$ implies that the tetrahedrally-coordinated Fe$^{2+}$ ions are in the high-spin, $S=2$, state. While a sharp decrease in $χ$ implies long-range antiferromagnetic order below \tn\ = 17.0(5)~K, the presence of a broad maximum at $T_{\rm m} = 28$~K suggests quasi-low-dimensional magnetism. Applying magnetic fields along the easy magnetic $a$-axis yields additional contributions to the susceptibility $\partial M/\partial B$…
Recently, new Cr-based superconductors, A$_2$Cr$_3$As$_3$ (A = K, Rb, Cs), have gained a strong interest because of their one-dimensional crystal structures and electron correlations. Here we report the crystal structure and physical properties of two related materials ACr$_3$As$_3$ (A = Rb, Cs) which are synthesized via a soft-chemical A+ deintercalation in A$_2$Cr$_3$As$_3$. The new compounds remain one-dimensional (Cr$_3$As$_3$)$_{\infty}$ linear chains, and the interchain distance can be tuned by the incorporation of the alkali-metal cations with different sizes. The physical-property meas…
Single crystal growth is a widely explored method of synthesizing materials in the solid state. The last few decades have seen significant improvements in the techniques used to synthesize single crystals, but there has been comparatively little discussion on ways to disseminate this knowledge. We aim to change that. Here we describe the principles of known single crystal growth techniques as well as lesser-known variations that have assisted in the optimization of defect control in known materials. We offer a perspective on how to think about these synthesis methods in a grand scheme. We cons…
The iron arsenide Eu3Fe2O5Fe2As2 was synthesized at 1173-1373 K in a resistance furnace and characterized by X-ray powder diffraction with Rietveld analysis: Sr3Fe2O5Cu2S2-type, I4/mmm, a = 406.40(1) pm, c = 2646.9(1) pm. Layers of edge-sharing FeAs4/4 tetrahedra are separated by perovskite-like oxide blocks. No structural transition occurs in the temperature range from 10 to 300 K. Magnetic measurements have revealed Curie-Weiss behavior with an effective magnetic moment of 7.79 muB per europium atom in agreement with the theoretical value of 7.94 muB for Eu2+. A drop in the magnetic suscepti…
The novel spin-chain cobalt oxide Sr5Pb3CoO12 [P-62m, a = 10.1093(2) A and c = 3.562 51(9) A at 295 K] is reported. Polycrystalline sample of the compound was studied by neutron diffraction (at 6 and 295 K) and magnetic susceptibility measurements (5 to 390 K). The cobalt oxide was found to be analogous to the copper oxide Sr5Pb3CoO12, which is comprised of magnetic-linear chains at inter-chain distance of 10 A. Although the cobalt oxide chains (mu_eff of 3.64 mu_B per Co) are substantially antiferromagnetic (theta_W = -38.8 K), neither low-dimensional magnetism nor long-range ordering has bee…
The Zn-paratacamite family, Zn$_{x}$Cu$_{4-x}$(OH)$_{6}$Cl$_{2}$ for $x \, \geq$ 0.33, is an ideal system for studying spin-1/2 frustrated magnetism in the form of antiferromagnetic Cu$^{2+}$ kagome planes. Here we report a new synthesis method by which high quality millimeter-sized single crystals of Zn-paratacamite have been produced. These crystals have been characterized by metal analysis, x-ray diffraction, neutron diffraction, and thermodynamic measurements. The $x$ = 1 member of the series displays a magnetic susceptibility that is slightly anisotropic at high temperatures with $χ_{c} \…
In this study, we synthesized single crystals of Na$_{x}$CoO$_{2}$ with $x\sim0.8$ using the optical floating zone technique. A thorough electrochemical treatment of the samples permitted us to control the de-intercalation of Na to obtain single crystal samples of stable Na ordered phases with $x=0.5-0.8$. Comparisons of the bulk magnetic properties with those observed in the Na ordered powder samples confirmed the high quality of these single crystal phases. The ab plane resistivity was measured for the Na ordered samples and it was quite reproducible for different sample batches. The data we…
A new class of materials, Topological Crystalline Insulators (TCIs) have been shown to possess exotic surface state properties that are protected by mirror symmetry. These surface features can be enhanced if the surface-area-to-volume ratio of the material increases, or the signal arising from the bulk of the material can be suppressed. We report the experimental procedures to obtain high quality crystal boules of the TCI, SnTe, from which nanowires and microcrystals can be produced by the vapour-liquid-solid (VLS) technique. Detailed characterisation measurements of the bulk crystals as well …
Numerous contemporary investigations in condensed matter physics are devoted to high temperature (high-$T_c$ ) cuprate superconductors. Despite its unique effulgence among research subjects, the enigma of the high-$T_c$ mechanism still persists. One way to advance its understanding is to discover and study new analogous systems. Here we begin a novel exploration of the natural mineral murunskite, K$_2$FeCu$_3$S$_4$, as an interpolation compound between cuprates and ferropnictides, the only known high-$T_c$ superconductors at ambient pressure. Because in-depth studies can be carried out only on…
We present the crystal structures and magnetic properties of RE3Sb3Mg2O14 (La3Sb3Mg2O14, Pr3Sb3Mg2O14, Sm3Sb3Mg2O14, Eu3Sb3Mg2O14, Tb3Sb3Mg2O14, and Ho3Sb3Mg2O14), a family of novel materials based on a perfect geometry 2D rare earth Kagome lattice. Structure refinements were performed by the Rietveld method using X-ray diffraction data, indicating that the layered compounds are fully structurally ordered. The compounds crystallize in a rhombohedral supercell of the cubic pyrochlore structure, in the space group R-3m. As indicated by magnetic susceptibility measurements, they exhibit predomina…