Employing density-functional calculations we study single and double graphene layers on Si- and C-terminated 1x1-6H-SiC surfaces. We show that, in contrast to earlier assumptions, the first carbon layer is covalently bonded to the substrate, and cannot be responsible for the graphene-type electronic spectrum observed experimentally. The characteristic spectrum of free-standing graphene appears with the second carbon layer, which exhibits a weak van der Waals bonding to the underlying structure. For Si-terminated substrate, the interface is metallic, whereas on C-face it is semiconducting or semimetallic for single or double graphene coverage, respectively.
We report the growth of high-quality triangular GaN nanomesas, 30-nm thick, on the C-face of 4H-SiC using nano selective area growth (NSAG) with patterned epitaxial graphene grown on SiC as an embedded mask. NSAG alleviates the problems of defective crystals in the heteroepitaxial growth of nitrides, and the high mobility graphene film can readily provide the back low-dissipative electrode in GaN-based optoelectronic devices. The process consists in first growing a 5-8 graphene layers film on the C-face of 4H- SiC by confinement-controlled sublimation of silicon carbide. The graphene film is t…
We investigated the electroluminescent properties of the epitaxial graphene/SiC junction. The temperature and current dependence of electroluminescence from the epitaxial graphene/SiC is measured within a temperature range of 50-300 K. The result of electroluminescence at 300~K is compared with the electroluminescent spectra from aluminium/SiC junction. The difference between the spectra is explained by the different band bending, which could lead to the tunable LED due to the semi-metal character of the graphene. We observed the electroluminescence at both bias polarities and we described the…
The Seebeck coefficient in multilayer graphene is investigated within the density-functional theory, using the semiclassical Boltzmann equations and interpolating the bands in a maximally-localized Wannier functions basis set. We compare various graphene stackings (AA, AB and ABC) both free-standing and deposited on a $4H$-SiC(0001) C-terminated substrate. We find that the presence of the SiC substrate can significantly affect the thermopower properties of graphene layers, depending on the stacking, providing a promising way to tailor efficient graphene-based devices.
We have measured optical absorption in mid-infrared spectral range on hydrogen intercalated epitaxial graphene grown on silicon face of SiC. We have used attenuated total reflection geometry to enhance absorption related to the surface and SiC/graphene interface. The samples of epitaxial graphene have been intercalated in the temperature range of 790 to 1250$^\circ$C and compared to the reference samples of hydrogen etched SiC. We have found that although the Si-H bonds form at as low temperatures as 790$^\circ$C, the well developed bond order has been reached only for epitaxial graphene inter…
Using highly controlled coverages of graphene on SiC(0001), we have studied the structure of the first graphene layer that grows on the SiC interface. This layer, known as the buffer layer, is semiconducting. Using x-ray reflectivity and x-ray standing waves analysis we have performed a comparative study of the buffer layer structure with and without an additional monolayer graphene layer above it. We show that no more than 26\% of the buffer carbon is covalently bonded to Si in the SiC interface. We also show that the top SiC bilayer is Si depleted and is the likely the cause of the incommens…
We present a new fabrication method for epitaxial graphene on SiC which enables the growth of ultra-smooth defect- and bilayer-free graphene sheets with an unprecedented reproducibility, a necessary prerequisite for wafer-scale fabrication of high quality graphene-based electronic devices. The inherent but unfavorable formation of high SiC surface terrace steps during high temperature sublimation growth is suppressed by rapid formation of the graphene buffer layer which stabilizes the SiC surface. The enhanced nucleation is enforced by decomposition of polymer adsorbates which act as a carbon …
The quasi-free-standing nature of graphene on H-saturated SiC(0001)
我们报道了在6 H-SiC（0001）上通过在缓冲层下嵌入氢制备的准独立石墨烯的研究。利用红外吸收光谱，我们证明了SiC（0001）表面是饱和的氢。拉曼光谱表明缓冲层转化为石墨烯，石墨烯表现出轻微的拉伸应变和短程缺陷。这些层是空穴掺杂的（p = 5.0-6.5 x 10^12 cm^（-2）），室温下载流子迁移率为3，100 cm ^2/Vs。与缓冲层上的石墨烯相比，对于H-封端的SiC（0001）上的石墨烯，观察到迁移率的温度依赖性大大降低，这证明了术语“准自立”的合理性。
Low temperature transport properties of multigraphene structures on 6H-SiC obtained by thermal graphitization: evidences of a presence of nearly perfect graphene layer
We measure the adsorption height of hydrogen-intercalated quasi-free-standing monolayer graphene on the (0001) face of 6H silicon carbide by the normal incidence x-ray standing wave technique. A density functional calculation for the full ($6 \sqrt{3} \times 6 \sqrt{3}$)-R30$^\circ$ unit cell, based on a van der Waals corrected exchange correlation functional, finds a purely physisorptive adsorption height in excellent agreement with experiments, a very low buckling of the graphene layer, a very homogeneous electron density at the interface and the lowest known adsorption energy per atom for g…
We have investigated the atomic structure of superconducting Ca-intercalated bilayer graphene on a SiC(0001) substrate using total-reflection high-energy positron diffraction. By comparing the experimental rocking-curves with ones calculated for various structural models using a full-dynamical theory, we have found that Ca atoms are intercalated in the graphene-buffer interlayer, rather than between the two graphene layers. From transport measurements, the superconducting transition was observed to be at Tc_onset = 4K for this structure. This study is the first to clearly identify the relation…
We report on the charge spill-out and work function of epitaxial few-layer graphene on 6H-SiC(0001). Experiments from high-resolution, energy-filtered X-ray photoelectron emission microscopy (XPEEM) are combined with ab initio Density Functional Theory calculations using a relaxed interface model. Work function values obtained from theory and experiments are in qualitative agreement, reproducing the previously observed trend of increasing work function with each additional graphene plane. Electrons transfer at the SiC/graphene interface through a buffer layer causes an interface dipole moment …
Heterostructures made of stacked 2D materials with different electronic properties are studied for their potential in creating multifunctional devices. Graphene (G) and hexagonal boron nitride (h-BN) van der Waals (vdW) systems have been extensively researched, including recent studies on synthesizing h-BN on graphene/SiC(0001) templates. These studies suggest that h-BN encapsulation could occur in addition to vdW epitaxy. This work presents theoretical research on G/h-BN heterostructures on SiC(0001) with a carbon buffer layer. The results show an energetic preference for h-BN encapsulation b…
We demonstrate hydrogen assisted growth of high quality epitaxial graphene on the C-face of 4H-SiC. Compared with the conventional thermal decomposition technique, the size of the growth domain by this method is substantially increased and the thickness variation is reduced. Based on the morphology of epitaxial graphene, the role of hydrogen is revealed. It is found that hydrogen acts as a carbon etchant. It suppresses the defect formation and nucleation of graphene. It also improves the kinetics of carbon atoms via hydrocarbon species. These effects lead to increase of the domain size and the…
We report the use of a surfactant molecule during the epitaxy of graphene on SiC(0001) that leads to the growth in an unconventional orientation, namely $R0^\circ$ rotation with respect to the SiC lattice. It yields a very high-quality single-layer graphene with a uniform orientation with respect to the substrate, on the wafer scale. We find an increased quality and homogeneity compared to the approach based on the use of a pre-oriented template to induce the unconventional orientation. Using spot profile analysis low energy electron diffraction, angle-resolved photoelectron spectroscopy, and …
We investigate electronic band-structure images in reciprocal space of few layer graphene epitaxially grown on SiC(000-1). In addition to the observation of commensurate rotation angles of the graphene layers, the k-space images recorded near the Fermi edge highlight structures originating from diffraction of the Dirac cones due to the relative rotation of adjacent layers. The 21.9° and 27° rotation angles between two sheets of graphene are responsible for a periodic pattern that can be described with a superlattice unit cells. The superlattice generates replicas of Dirac cones with smaller wa…
The Moiré structure of epitaxial graphene mono layer grown on 6H-SiC(0001) has been investigated recently by grazing incidence fast atom diffraction, and the results were compared with the calculation of the structure \textit{ab initio} and exact diffraction codes. We review these results and present a complementary approach using the Hard Wall Model to extract information without any \textit{a priori}. Reversely, taking advantage of previous exact calculations we evaluate quantitatively the performance of this simplified approach by comparing predictions using the same potential energy surfac…
Predictive first-principles calculations suggest graphitic-like GaN to be theoretically possible. Thus far, it has not been experimentally reported. We report on GaN monolayer in a buckled geometry obtained in confinement at graphene/SiC interface by metalorganic chemical vapor deposition (MOCVD). Conductive atomic force microscopy (C-AFM) has been employed to probe vertical current injection through the graphene/SiC interface and to establish the uniformity of the intercalated areas. Scanning transmission electron microscopy (S/TEM) has been employed for atomic resolution imaging and spectros…
Interfacial Coupling Controls Molecular Epitaxy of HMTP on Graphene/SiC