The strong fascination exerted by the binary compound of FeSe demands reliable engineering protocols and more effective approaches towards inducing superconductivity in FeSe thin films. Our study addresses the peculiarities in pulsed laser deposition which determine FeSe thin film growth and focuses on the film/substrate interface, the tendency for domain matching epitaxial growth but also the disadvantage of chemical heterogeneity. We propose that homogenization of the substrate surface improves the control of stoichiometry, texture, and nanostrain in a way that favors superconductivity even in ultrathin FeSe films. The controlled interface in FeSe/Fe/MgO demonstrates the proof-of-principle.
Interface-enhanced high-temperature superconductivity in one unit-cell (UC) FeSe film on SrTiO3(001) (STO) substrate has recently attracted much attention in condensed matter physics and material science. Here, by ex situ transport measurements, we report on the superconductivity in FeSe ultra-thin films with different thickness on STO substrate. We find that the onset superconducting transition temperature (Tc) decreases with increasing film thickness of FeSe, which is opposite to the behavior usually observed in traditional superconductor films. By systematic post-annealing of 5 UC FeSe film…
To elucidate the mechanisms behind the enhanced $T_c$ in monolayer (1ML) FeSe on SrTiO$_3$ (STO), we grew highly strained 1ML FeSe on the rectangular (100) face of rutile TiO$_2$, and observed the coexistence of replica bands and superconductivity with a $T_c$ of 63 K. From the similar $T_c$ between this system and 1ML FeSe on STO (001), we conclude that strain and dielectric constant are likely unimportant to the enhanced $T_c$ in these systems. A systematic comparison of 1ML FeSe on TiO$_2$ with other systems in the FeSe family shows that while charge transfer alone can enhance $T_c$, it is …
FeSe0.5Te0.5 thin films with PbO-type structure are successfully grown on MgO(100) and LaSrAlO4(001) substrates from FeSe0.5Te0.5 or FeSe0.5Te0.75 polycrystalline targets by pulsed-laser deposition. The film deposited on the MgO substrate (film thickness ~ 55 nm) shows superconductivity at 10.6 K (onset) and 9.2 K (zero resistivity). On the other hand, the film deposited on the LaSrAlO4 substrate (film thickness ~ 250 nm) exhibits superconductivity at 5.4 K (onset) and 2.7 K (zero resistivity). This suggests the strong influence of substrate materials and/or the c-axis length to superconductin…
It was observed recently (K. Shigekawa et al, PNAS 116, 2470 (2019)) that while monolayer iron chalcigenide FeSe on SrTiO3 (STO) substrate has a very high critical temperature, its chemical and structural "twin" material FeS=STO has a very low Tc if any. To explain this the substrate interfacial phonon model of superconductivity in iron chalcogenides is further developed. The main glue is the oxygen ion (60mev) vibrations longitudinal optical (LO) mode. The mode propagates mainly in the TiO2 layer adjacent to the monolayer (and genrally present also in similar highly polarized ionic crystals l…
FeSe0.5Te0.5 thin films were grown by pulsed laser deposition on CaF2, LaAlO3 and MgO substrates and structurally and electro-magnetically characterized in order to study the influence of the substrate on their transport properties. The in-plane lattice mismatch between FeSe0.5Te0.5 bulk and the substrates shows no influence on the lattice parameters of the films, whereas the type of substrates affects the crystalline quality of the films and, therefore, the superconducting properties. The film on MgO showed an extra peak in the angular dependence of critical current density Jc(θ) at θ = 180° …
We perform in-plane optical spectroscopy measurement on (00l) FeSe thin-film grown on SrTiO$_3$ substrate by pulsed laser deposition method. The study indicates that the low frequency conductivity consists of two Drude components, a broad one which takes up most of the spectral weight and a very narrow one roughly below 100-150 \cm. The narrow Drude component locates at so low frequencies that no such behavior was observed in iron pnictides. The overall plasma frequency is found to be smaller than the FeAs based compounds, suggesting a stronger correlation effect. Similar to iron pnictides, a …
Mono- and multilayer FeSe thin films grown on SrTiO$_\mathrm{3}$ and BiTiO$_\mathrm{3}$ substrates exhibit a greatly enhanced superconductivity over that found in bulk FeSe. A number of proposals have been advanced for the mechanism of this enhancement. One possibility is the introduction of a cross-interface electron-phonon ($e$-$ph$) interaction between the FeSe electrons and oxygen phonons in the substrates that is peaked in the forward scattering (small ${\bf q}$) direction due to the two-dimensional nature of the interface system. Motivated by this, we explore the consequences of such an …
We have investigated the crystal structures and superconducting properties of thin films of FeSe$_{0.5}$Te$_{0.5}$ grown on eight different substrates. Superconductivity is not correlated with the lattice mismatch; rather it is correlated with the degree of in-plane orientation and with the lattice parameter ratio $c/a$. The best superconducting properties were observed in films on MgO and LaAlO$_3$ ($T_\mathrm{c}^\mathrm{zero}$ of 9.5 K). TEM observation showed that the presence or absence of an amorphous-like layer at the substrate surface plays a key role in determining the structural and s…
The discovery of higher-temperature superconductivity in FeSe monolayers on SrTiO$_3$ (STO) substrates has sparked a surge of interest in the interface superconductivity. One point of the agreement reached to date is that modulation doping by impurities in the substrate is critical for the enhanced superconductivity. Remarkably, the universal doping of about 0.1 electrons per Fe, \textit{i.e.}, so-called ``magic'' doping, has been observed on a range of Ti oxide substrates, which concludes that there likely is some important interaction limiting the FeSe doping. Our study discovers that the po…
Recently, the signs of both superconducting transition temperature (Tc) beyond 60 K and spin density wave (SDW) have been observed in FeSe thin film on SrTiO3 (STO) substrate, which suggests a strong interplay between superconductivity and magnetism. With the first-principles calculations, we find that the substrate-induced tensile strain tends to stabilize the SDW state in FeSe thin film by enhancing of the next-nearest-neighbor superexchange antiferromagnetic interaction bridged through Se atoms. On the other hand, we find that when there are oxygen vacancies in the substrate, the significan…
Superconducting epitaxial FeSe0.5Te0.5 thin films were prepared on SrTiO3 (001) substrates by pulsed laser deposition. The high purity of the phase, the quality of the growth and the epitaxy were studied with different experimental techniques: X-rays diffraction, reflection high energy electron diffraction, scanning tunnelling microscopy and atomic force microscopy. The substrate temperature during the deposition was found to be the main parameter governing sample morphology and superconducting critical temperature. Films obtained in the optimal conditions show an epitaxial growth with c axis …
Using a microscopic model of lattice vibrations in the STO(001) substrate, an additional 50 mev longitudinal optical (LO) interface mode is identified. The soft mode propagating mainly in the first TiO2 layer ("O chains") has stronger electron - phonon coupling to electron gas in FeSe than a well known 100 mev hard mode. The coupling constant, critical temperature, replica band are calculated. Although there exists a forward in the electron - phonon scattering peak, it is clearly not as sharp as assumed in recent theories (delta function - like). The satellite is broad and its peak appears at …
FeSe$_{1-x}$Te$_{x}$ thin films with PbO-type structure are successfully grown on MgO(100) and LaSrAlO$_{4}$(001) substrates from FeSe$_{1-x}$Te$_{x+d}$ polycrystalline targets by pulsed-laser deposition. The film deposited on the MgO substrate (film thickness $\sim$ 63 nm) shows superconductivity at 6.7 K (onset) and 5.5 K (zero resistivity). On the other hand, the film deposited on the LaSrAlO$_{4}$ substrate (film thickness $\sim$ 52 nm) exhibits only the onset of superconducting transition at 2.6 K, but does not show zero resistivity. This indicates the strong influence of epitaxial strain…
We have fabricated high-quality FeSe1-x superconducting films with a bulk Tc of 11-12 K on different substrates, Al2O3(0001), SrTiO3(100), MgO(100), and LaAlO3(100), by using a pulsed laser deposition technique. All the films were grown at a high substrate temperature of 610 oC, and were preferentially oriented along the (101) direction, the latter being to be a key to fabricating of FeSe1-x superconducting thin films with high Tc. According to the energy dispersive spectroscopy data, the Fe:Se composition ratio was 1:0.90+-0.02. The FeSe1-x film grown on a SrTiO3 substrate showed the best qua…
The discovery of an enhanced superconducting transition temperature $T_c$ in monolayers of FeSe grown on several oxide substrates has opened a new route to high-$T_c$ superconductivity through interface engineering. One proposal for the origin of the observed enhancement is an electron-phonon (e-ph) interaction across the interface that peaked at small momentum transfers. In this paper, we examine the implications of such a coupling on the phononic properties of the system. We show that a strong forward scattering leads to a sizable broadening of phonon lineshape, which may result in charge in…
We study the consequences of an electron-phonon ($e$-$ph$) interaction that is strongly peaked in the forward scattering ($\mathbf{q} = 0$) direction in a two-dimensional superconductor using Migdal-Eliashberg theory. We find that strong forward scattering results in an enhanced $T_c$ that is linearly proportional to the strength of the dimensionless $e$-$ph$ coupling constant $λ_m$ in the weak coupling limit. This interaction also produces distinct replica bands in the single-particle spectral function, similar to those observed in recent angle-resolved photoemission experiments on FeSe monol…
Superconducting FeSe films were electrochemically deposited on rolling-assisted biaxially textured substrate (RABiTS) tape. We observed zero resistivity in the as-electrodeposited FeSe film prepared on the RABiTS when the appropriate voltage was applied while it was dipped into the solution. When the RABiTS tape was dipped in the solution without applying voltage, a thin Se film was deposited on the substrate. The compositional ratio of the FeSe film got closer to the stoichiometric ratio with decreasing the dipping time before applying voltage.
Epitaxial Fe(Se,Te) thin films were prepared by pulsed laser deposition on (La0.18Sr0.82)(Al0.59Ta0.41)O3 (LSAT), CaF2-buffered LSAT and bare CaF2 substrates, which exhibit an almost identical in-plane lattice parameter. The composition of all Fe(Se,Te) films were determined to be FeSe0.7Te0.3 by energy dispersive X-ray spectroscopy, irrespective of the substrate. Albeit the lattice parameters of all templates have comparable values, the in-plane lattice parameter of the FeSe0.7Te0.3 films varies significantly. We found that the superconducting transition temperature (Tc) of FeSe0.7Te0.3 thin …
Monolayer films of FeSe grown on SrTiO$_3$ substrates exhibit significantly higher superconducting transition temperatures than those of bulk FeSe. Interaction of electrons in the FeSe layer with dipolar SrTiO$_3$ phonons has been suggested as the cause of the enhanced transition temperature. In this paper we systematically study the coupling of SrTiO$_3$ longitudinal optical phonons to the FeSe electron, including also electron-electron Coulomb interactions at the random phase approximation level. We find that the electron-phonon interaction between FeSe and SrTiO$_3$ substrate is almost enti…
The significantly enhanced superconducting transition temperature ($T_c$) of an FeSe monolayer on SrTiO$_3$(001) substrate has attracted extensive attention in recent years. Here, based on first-principles electronic structure calculations, we propose another candidate substrate LaO(001) for the epitaxial growth of FeSe monolayer to realize superconductivity. Our calculations show that for the optimal adsorption structure of FeSe monolayer on LaO(001), the stripe antiferromagnetic state and the dimer antiferromagnetic state are almost energetically degenerate, indicating the existence of stron…
Interface enhanced superconductivity at two dimensional limit has become one of most intriguing research directions in condensed matter physics. Here, we report the superconducting properties of ultra-thin FeSe films with the thickness of one unit cell (1-UC) grown on conductive and insulating SrTiO3 (STO) substrates. For the 1-UC FeSe on conductive STO substrate (Nb-STO), the magnetization versus temperature (M-T) measurement shows a diamagnetic signal at 85 K, suggesting the possibility of superconductivity appears at this high temperature. For the FeSe films on insulating STO substrate, sys…
Scanning tunneling microscopy (STM) is a powerful technique for imaging atomic structure and inferring information on local elemental composition, chemical bonding, and electronic excitations. However, traditional methods of visual inspection can be challenging for such determination in multi-component alloys, particularly beyond the dilute limit due to chemical disorder and electronic inhomogeneity. One viable solution is to use machine learning to analyze STM data and identify patterns and correlations that may not be immediately apparent through visual inspection alone. Here, we apply this …
In-situ epitaxial growth of FeSe$_{0.5}$Te$_{0.5}$ thin films is demonstrated on a non-oxide substrate CaF$_2$. Structural analysis reveals that compressive stress is moderately added to 36-nm thick FeSe$_{0.5}$Te$_{0.5}$, which pushes up the critical temperature above 15 K, showing higher values than that of bulk crystals. Critical current density at $T$ = 4.5 K reaches 5.9 x 10$^4$ Acm$^{-2}$ at $μ_0H$ = 10 T, and 4.2 x 10$^4$ Acm$^{-2}$ at $μ_0H$ = 14 T. These results indicate that fluoride substrates have high potential for the growth of iron-based superconductors in comparison with popula…
We used STM to study the tunneling spectra of FeSe0.3Te0.7 films with two orientations of ab-planes and the connection ramp between them. We have discovered that, using pulse laser deposition (PLD) method, the a- and b-axis of the FeSe0.3Te0.7 film deposited on Ar-ion-milled Magnesium Oxide (MgO) substrate are rotated 45 degree with respect to those of MgO, while the a- and b-axis of the film grown on pristine MgO substrate are parallel to those of MgO. With photolithography and this technique, we can prepare FeSe0.3Te0.7 film with two kinds of orientations on the same MgO substrate, and the c…
The presumably unconventional superconductor Beta-FeSe was deposited by radio frequency sputtering and molecular beam epitaxy (MBE) from two elementary sources. Superconducting thin films were grown in (001)-orientation on MgO(100) and YAlO3(010) substrates. The morphology of the samples was studied and directly related to the superconducting properties of the Beta-FeSe thin films. The MBE grown thin films show microcracks down to the substrate and a roughness of about 100~nm. In contrast, sputter deposited superconducting thin films show a smooth surface with almost no precipitates. In both c…
We have synthesized a Ba-doped FeSe superconductor using liquid ammonia, and investigated in detail the structure and composition of the Ba-FeSe phase. In the superconducting phase, both the Tc and the shielding fraction are almost unchanged even if the nominal composition of Ba is varied in the region from 0.3 to 0.7. The optimized Tc is 38.8 K. We have determined the structure of the superconducting phase with X-ray powder diffraction (using synchrotron radiation) and here describe the co-intercalation of Ba and NH3 molecules between the FeSe layers.
Among the recently discovered iron-based superconductors, ultrathin films of FeSe grown on SrTiO3 substrates have uniquely evolved into a high superconducting-transition-temperature (TC) material. The mechanisms for the high-TC superconductivity are ongoing debate mainly with the superconducting gap characterized with in-situ analysis for FeSe films grown by bottom-up molecular-beam epitaxy. Here, we demonstrate the alternative access to investigate the high-TC superconductivity in ultrathin FeSe with top-down electrochemical etching technique in three-terminal transistor configuration. In add…
We report high temperature superconductivity in one unit-cell (1-UC) FeSe films grown on STO(110) substrate by molecular beam epitaxy. By in-situ scanning tunneling spectroscopy measurement, we observed a superconducting gap as large as 17 meV. Transport measurements on 1-UC FeSe/STO(110) capped with FeTe layers reveal superconductivity with an onset TC of 31.6 K and an upper critical magnetic field of 30.2 T. We also find that the TC can be further increased by an external electric field, but the effect is smaller than that on STO(001) substrate. The study points out the important roles of in…
The films of FeSe on substrates have attracted attention because of their unusually high-temperature (Tc) superconducting properties whose origins continue to be debated. To disentangle the competing effects of the substrate and interlayer and intralayer processes, we present here results of density functional theory (DFT)-based analysis of the electronic structure of unsupported FeSe films consisting of 1 to 5 layers (1L-5L). Furthermore, by solving the Bardeen-Schrieffer-Cooper (BCS) equation with spin-wave exchange attraction derived from the Hubbard model, we find the superconducting criti…
We show that electron-phonon coupling can induce strong electron pairing in an FeSe monolayer on a SrTiO3 substrate (experimental indications for superconducting Tc are between 65 and 109K). The role of the SrTiO3 substrate in increasing the coupling is two-fold. First, the interaction of the FeSe and TiO2 terminated face of SrTiO3 prevents the FeSe monolayer from undergoing a shear-type (orthorhombic, nematic) structural phase transition. Second, the substrate allows an anti-ferromagnetic ground state of FeSe which opens electron-phonon coupling channels within the monolayer that are prevente…
We report the Meissner effect studies on an FeSe thin film grown on Nb doped SrTiO3 substrate by molecular beam epitaxy. Two-coil mutual inductance measurement clearly demonstrates the onset of diamagnetic screening at 65 K, which is consistent with the gap opening temperature determined by previous angle resolved photoemission spectroscopy results. The applied magnetic field causes a broadening of the superconducting transition near the onset temperature, which is the typical behavior for quasi-two-dimensional superconductors. Our results provide direct evidence that FeSe thin film grown on N…
We have successfully synthesized FeSe films by the electrochemical deposition in the electrolyte containing FeCl_{2}\cdot4H_{2}O, SeO_{2} and Na_{2}SO_{4}. The composition ratio of Fe and Se was controlled by the synthesis voltage and pH value. The FeSe film with the composition ratio of Fe : Se = 1 : 1 is fabricated at a voltage of -0.9 V and pH 2.1 in our electrochemical deposition. This sample has a highly crystalline tetragonal FeSe structure and exhibits a superconducting transition at 8.1 K, comparable to FeSe synthesized by other methods.
Single unit cell films of iron selenide (1UC FeSe) grown on SrTiO3 (STO) substrates have recently shown superconducting energy gaps opening at temperatures close to the boiling point of liquid nitrogen (77 K), a record for iron-based superconductors. Towards understanding why Cooper pairs form at such high temperatures, a primary question to address is the role, if any, of the STO substrate. Here, we report high resolution angle resolved photoemission spectroscopy (ARPES) results which reveal an unexpected and unique characteristic of the 1UC FeSe/STO system: shake-off bands suggesting the pre…
A high-frequency optical phonon mode of SrTiO3 (STO) was found to assist the high-temperature superconductivity observed recently at the interface between monolayer FeSe and STO substrate. However, the origin of this mode is not clear. Through first-principles calculations, we find that there is a novel polar phonon mode on the surface layers of the STO substrate, which does not exist in the STO crystals. The oxygen vacancies near the FeSe/STO interface drives the dispersion of this phonon mode to be flat and lowers its energy, whereas the charge transfer between STO substrate and FeSe monolay…
FeSe film is successfully fabricated onto Rolling Assisted Biaxially Textured Substrate (RABiTS) tapes by an electrochemical deposition technique. The deposited FeSe films tend to become high crystallinity with a decrease in the applied voltage to -1.0 V, and the compositional ratio of Fe to Se approaches 1:1. The sample deposited at -1.0 V shows a superconducting transition approximately 8.0 K in the magnetic susceptibility.
We have studied the effect of tensile strain on the superconductivity in FeSe films. 50 nm, 100 nm, and 200 nm FeSe films were grown on MgO, SrTiO$_3$, and LaAlO$_3$ substrates by using a pulsed laser deposition technique. X-ray diffraction analysis showed that the tetragonal phase is dominant in all of our FeSe films. The 50 nm FeSe films on MgO and SrTiO$_3$ are under tensile strain, while the 50 nm FeSe film on LaAlO$_3$ and the other thick FeSe films are unstrained. Superconducting transitions have been observed in unstrained FeSe films with T$_{onset}$ $\approx$ 8 K, which is close to the…
In the quest for high temperature superconductors, the interface between a metal and a dielectric was proposed to possibly achieve very high superconducting transition temperature ($T_c$) through interface-assisted pairing. Recently, in single layer FeSe (SLF) films grown on SrTiO$_3$ substrates, signs for $T_c$ up to 65~K have been reported. However, besides doping electrons and imposing strain, whether and how the substrate facilitates the superconductivity are still unclear. Here we report the growth of various SLF films on thick BaTiO$_3$ films atop KTaO$_3$ substrates, with signs for $T_c…
Charge transfer and electron-phonon coupling (EPC) are proposed to be two important constituents associated with enhanced superconductivity in the single unit cell FeSe films on oxide surfaces. Using high-resolution electron energy loss spectroscopy combined with first-principles calculations, we have explored the lattice dynamics of ultrathin FeSe films grown on SrTiO3. We show that, despite the significant effect from the substrate on the electronic structure and superconductivity of the system, the FeSe phonons in the films are unaffected. The energy dispersion and linewidth associated with…
Ultrathin FeSe films grown on SrTiO$_{3}$ substrates are a recent milestone in atomic material engineering due to their important role in understanding unconventional superconductivity in Fe-based materials. Using femtosecond time- and angle-resolved photoelectron spectroscopy, we study phonon frequencies in ultrathin FeSe/SrTiO$_{3}$ films grown by molecular beam epitaxy. After optical excitation, we observe periodic modulations of the photoelectron spectrum as a function of pump-probe delay for 1 unit cell, 3 unit cell, and 60 unit cell thick FeSe films. The frequencies of the coherent inten…
Heterostructure based interface engineering has been proved an effective method for finding new superconducting systems and raising superconductivity transition temperature (TC). In previous work on one unit-cell (UC) thick FeSe films on SrTiO3 (STO) substrate, a superconducting-like energy gap as large as 20 meV, was revealed by in situ scanning tunneling microscopy/spectroscopy (STM/STS). Angle resolved photoemission spectroscopy (ARPES) further revealed a nearly isotropic gap of above 15 meV, which closes at a temperature of ~ 65 K. If this transition is indeed the superconducting transitio…
Superconducting FeSe0.8Te0.2 thin films on SrTiO3, LaAlO3 and CaF2 substrates were electrochemically etched in an ionic liquid DEME-TFSI electrolyte with a gate bias of 5 V. Superconductivity at 38 K was commonly observed on all substrates after etching the films with a thickness above 30 nm, in spite of different Tc of 8 K, 12 K and 19 K before the etching on SrTiO3, LaAlO3 and CaF2 substrates, respectively. Tc returned to the original value by removing the gate bias. The Tc enhancement on the thick film indicates no relationship between the Tc enhancement and any interface effects between th…
We report on the synthesis and physical properties of FeSe$_{1-x}$Te$_x$ single crystals with a low Te content (x = 0.17, 0.21, 0.25), where the replacement of Se with Te partially suppresses superconductivity. Resistivity and Hall effect measurements indicate weak anomalies at elevated temperatures ascribed to nematic transitions. A quasi-classical analysis of transport data, including in a pulsed magnetic field of up to 25 T, confirms the inversion of majority carriers type from holes in FeSe to electrons in FeSe$_{1-x}$Te$_x$ at x $>$ 0.17. The temperature-dependent term in the elastoresist…
Thin film growth of iron chalcogenides by pulsed laser deposition (PLD) is still a delicate issue in terms of simultaneous control of stoichiometry, texture, substrate/film interface properties, and superconducting properties. The high volatility of the constituents sharply limits optimal deposition temperatures to a narrow window and mainly challenges reproducibility for vacuum based methods. In this work we demonstrate the beneficial introduction of a semiconducting FeSe$_{1\text{--}x}$Te$_x$ seed layer for subsequent homoepitaxial growth of superconducting FeSe$_{1\text{--}x}$Te$_x$ thin fi…
In order to investigate the effects of in-plane strain on the superconductivity of FeSe, epitaxial thin films of FeSe were fabricated on CaF$_2$ substrates. The films are compressed along the a-axis and their superconducting transition temperatures $T_{\mathrm c}^{\mathrm {zero}}$ reach 11.4 K, which is approximately 1.5 times higher than that of bulk crystals. The $T_{\mathrm c}$ values are weakly dependent on the ratio of the lattice constants, $c$ / $a$, compared to that of Fe(Se,Te). Our results indicate that even a binary system FeSe has room for improvement, and will open a new route for…
We report the superconductivity evolution of one unit cell (1-UC) and 2-UC FeSe films on SrTiO3(001) substrates with potassium (K) adsorption. By in situ scanning tunneling spectroscopy measurement, we find that the superconductivity in 1-UC FeSe films is continuously suppressed with increasing K coverage, whereas non-superconducting 2-UC FeSe films become superconducting with a gap of ~17 meV or ~11 meV depending on whether the underlying 1-UC films are superconducting or not. This work explicitly reveals that the interface electron-phonon coupling is strongly related to the charge transfer a…
We report on the observation of high-temperature ($T_\textrm{c}$) superconductivity and magnetic vortices in single-unit-cell FeSe films on anatase TiO$_2$(001) substrate by using scanning tunneling microscopy. A systematic study and engineering of interfacial properties has clarified the essential roles of substrate in realizing the high-$T_\textrm{c}$ superconductivity, probably via interface-induced electron-phonon coupling enhancement and charge transfer. By visualizing and tuning the oxygen vacancies at the interface, we find their very limited effect on the superconductivity, which exclu…
We prepared single unit cell FeSe films on GaO$_{2-δ}$ terminated perovskite NdGaO$_{3}$(110) substrates and performed ex situ transport and scanning transmission electron microscopy measurements on the FeTe protected films. Our experimental measurements showed that the single unit cell FeSe films interfaced with GaO$_{2-δ}$ layer are electron doped via interface charge transfer. Most importantly, this type of heterostructure can host interface enhanced superconductivity with an onset temperature of about 28 K, which is much higher than the value of 8 K in bulk FeSe. Our work indicates that Fe…
We report on fully epitaxial FeSe0.5Te0.5 (FST) thin films with high-quality grown on CaF2 (00l) substrate at a low temperature of 300°C by pulsed laser deposition. The transport Jc of thin films is up to 1.36 MA/cm2 in self-field and 0.97 MA/cm2 in 9 T at 4.2 K, indicating very weak field dependence. A nearly isotropy of Jc (γ= Jc(H//ab)/Jc(H//c) as low as 1.09 at 9 T is achieved in the FST thin films. Moreover, no clear amorphous interfacial layer presents between the film and the substrate probably ascribing to low temperature and low laser repetition rate grown, while the thickness of reac…
The superconducting FeSe films were successfully fabricated using the electrochemical synthesis. The composition ratio of Fe and Se can be controlled by the electric potential and pH value. We found that the FeSe films deposited at the electric potential -1.75 V and pH 2.3 show the superconducting transition at 3.5 K. The establishment of this electrochemical synthesis technique will provide many advantages for application.
We report comprehensive angle-resolved photoemission investigations on the electronic structure of single crystal multiple-layer FeSe films grown on CaF2 substrate by pulsed laser deposition (PLD) method. Measurements on FeSe/CaF2 samples with different superconducting transition temperatures Tc of 4 K, 9 K and 14 K reveal electronic difference in their Fermi surface and band structure. Indication of the nematic phase transition is observed from temperature-dependent measurements of these samples; the nematic transition temperature is 140-160 K, much higher than 90 K for the bulk FeSe. Potassi…
Superconductivity was recently found in the simple tetragonal FeSe structure. Recent studies suggest that FeSe is unconventional, with the symmetry of the superconducting pairing state still under debate. To tackle these problems, clean single crystals and thin films are required. Here we report the fabrication of superconducting beta-phase FeSe1-x thin films on different substrates using a pulsed laser deposition (PLD) technique. Quite interestingly, the crystal orientation, and thus, superconductivity in these thin films is sensitive to the growth temperature. At 320C, films grow preferably …
FeSe is a unique superconductor that can be manipulated to enhance its superconductivity using different routes while its monolayer form grown on different substrates reaches a record high temperature for a two-dimensional system. In order to understand the role played by the substrate and the reduced dimensionality on superconductivity, we examine the superconducting properties of exfoliated FeSe thin flakes by reducing the thickness from bulk down towards 9 nm. Magnetotransport measurements performed in magnetic fields up to 16T and temperatures down to 2K help to build up complete supercond…
Since the dramatic interface enhancement of superconducting transition temperature (Tc) was reported in one unit-cell FeSe film grown on SrTiO3 substrate (1-UC FeSe/STO) by molecular beam epitaxy (MBE), related research on this system has become a new frontier in condensed matter physics. In this paper, we present a brief review on this rapidly developing field, mainly focusing on the superconducting properties of 1-UC FeSe/STO. Experimental evidences for the high-temperature superconductivity in 1-UC FeSe/STO, including the direct evidences revealed by transport and diamagnetic measurements, …