We demonstrate spin-valve magnetoresistance with a current-in-plane (CIP) configuration in (Ga,Fe)Sb / InAs (thickness $t_\mathrm{InAs}$ nm) / (Ga,Fe)Sb trilayer heterostructures, where (Ga,Fe)Sb is a ferromagnetic semiconductor (FMS) with high Curie temperature ($T_\mathrm{C}$). An MR curve with an open minor loop is clearly observed at 3.7 K in a sample with $t_\mathrm{InAs}$ = 3 nm, which originates from the parallel - antiparallel magnetization switching of the (Ga,Fe)Sb layers and spin-dependent scattering at the (Ga,Fe)Sb / InAs interfaces. The MR ratio increases (from 0.03 to 1.6%) with decreasing $t_\mathrm{InAs}$ (from 9 to 3 nm) due to the enhancement of the interface scattering. This is the first demonstration of the spin-valve effect in Fe-doped FMS heterostructures, paving the way for device applications of these high- $T_\mathrm{C}$ FMSs.
Room temperature local magnetoresistance in two-terminal scheme is reported. By employing 1.6 nm-thick MgO tunnel barrier, spin injection efficiency is increased, resulting in large non-local magnetoresistance. The magnitude of the non-local magnetoresistance is estimated to be 0.0057 ohm at room temperature. As a result, a clear rectangle signal is observed in local magnetoresistance measurement even at room temperature. We also investigate the origin of local magnetoresistance by measuring the spin accumulation voltage of each contact separately.
We study the magnetoresistance of spin-valve devices using graphene as a non-magnetic material to connect ferromagnetic leads. As a preliminary step we first study the conductivity of a graphene strip connected to metallic contacts for a variety of lead parameters, and demonstrate that the resulting conductivity is rather insensitive to them. We then compute the conductivity of the spin-valve device in the parallel and antiparallel spin polarization configurations, and find that it depends only weakly on the relative spin orientations of the leads, so that the magnetoresistance $MR$ of the sys…
We demonstrate an electric-field control of tunneling magnetoresistance (TMR) effect in a semiconductor quantum-dot (QD) spin-valve device. By using ferromagnetic Ni nano-gap electrodes, we observe the Coulomb blockade oscillations at a small bias voltage. In the vicinity of the Coulomb blockade peak, the TMR effect is significantly modulated and even its sign is switched by changing the gate voltage, where the sign of the TMR value changes at the resonant condition.
We report the successful fabrication of lateral organic spin valves with a channel length in the sub $100\,nm$ regime. The fabication process is based on in-situ shadow evaporation under UHV conditions and therefore yields clean and oxygen-free interfaces between the ferromagnetic metallic electrodes and the organic semiconductor. The spin valve devices consist of Nickel and Cobalt-iron electrodes and the high mobility \emph{n}-type organic semiconductor $N,N'$-bis(heptafluorobutyl)-$3,4:9,10$-perylene diimide. Our studies comprise fundamental investigations of the process' and materials' suit…
A fabrication process for vertical organic spin-valve devices has been developed which offers the possibility to achieve active device areas of less than 500x500 nm^2 and is flexible in terms of material choice for the active layers. Characterization of the resulting devices shows a large magnetoresistance of sometimes more than 100%, however with equally large variation from device to device. Comparison with large-area spin-valves indicates that the magnetoresistance of both, large and small devices most likely originates from tunneling through pinholes and tunneling magnetoresistance.
We investigate theoretically the effects of surface states over the magnetoresistance of Ni-based organic spin-valves. In particular we perform {\it ab initio} electronic transport calculations for a benzene-thiolate molecule chemically attached to a Ni [001] surface and contacted either by Te to another Ni [001] surface, or terminated by a thiol group and probed by a Ni STM tip. In the case of S- and Te-bonded molecules we find a large asymmetry in the spin-currents as a function of the bias, although the $I$-$V$ is rather symmetric. This leads to a smooth although not monotonic dependence of…
We report on a highly efficient spin diode effect in an exchange-biased spin-valve giant magnetoresistance (GMR) strips. In such multilayer structures, symmetry of the current distribution along the vertical direction is broken and, as a result, a non-compensated Oersted field acting on the magnetic free layer appears. This field, in turn, is a driving force of magnetization precessions. Due to the GMR effect, resistance of the strip oscillates following the magnetization dynamics. This leads to rectification of the applied radio frequency current and induces a direct current voltage $V_{DC}$.…
Due to its two dimensional nature, ferromagnetism and charge doping can be induced by proximity and electric field effects in graphene. Taking advantage of these features, we propose an electrically engineered spin valve by combining two magnetic insulators (using EuO, EuS, or YIG) and three coating gates. Two top gates are used to cancel the heavy electron doping's in these magnets and one back gate is used to utilize the normal or half-metallic ferromagnetisms. We demonstrate that, when the second top gate is tuned to utilize the insulating or spin insulating states, huge giant magnetoresist…
We report magnetoresistance curves of CoFe nano-oxide specular spin valves of MnIr/CoFe/nano-oxidized CoFe/CoFe/Cu/CoFe/nano-oxidized CoFe/Ta at different temperatures from 300 to 20 K. We extend the Stoner-Wolfarth model of a common spin valve to a specular spin valve, introducing the separation of the pinned layer into two sublayers and their magnetic coupling across the nano-oxide. We study the effect of different coupling/exchange (between the antiferromagnetic layer and the bottom sublayer) field ratios on the magnetization and magnetoresistance, corresponding with the experimentally obse…
We investigated the spin-dependent transport properties of a lateral spin-valve device with a 600 nm-long GaAs channel and ferromagnetic MnGa electrodes with perpendicular magnetization. Its current-voltage characteristics show nonlinear behavior below 50 K, indicating that tunnel transport through the MnGa/GaAs Schottky barrier is dominant at low temperatures. We observed clear magnetoresistance (MR) ratio up to 12% at 4 K when applying a magnetic field perpendicular to the film plane. Furthermore, a large spin-dependent output voltage of 33 mV is obtained. These values are the highest in lat…
We report on the combination of current-induced spin-orbit torques and giant magnetoresistance in a single device to achieve all-electrical write and read out of the magnetization. The device consists of perpendicularly magnetized TbCo and Co layers separated by a Pt or Cu spacer. Current injection through such layers exerts spin-orbit torques and switches the magnetization of the Co layer while the TbCo magnetization remains fixed. Subsequent current injection of lower amplitude senses the relative orientation of the magnetization of the Co and TbCo layers, which results in two distinct resis…
Thermal control of exchange coupling between two strongly ferromagnetic layers through a weakly ferromagnetic Ni-Cu spacer and the associated magnetoresistance is investigated. The spacer, having a Curie point slightly above room temperature, can be cycled between its paramagnetic and ferromagnetic states by varying the temperature externally or using joule heating. It is shown that the giant magnetoresistance vanishes due to a strong reduction of the mean free path in the spacer at above ~30 % Ni concentration -- before the onset of ferromagnetism. Finally, a device is proposed and demonstrat…
The electrical resistance of ferromagnetic/normal-metal (F/N) heterostructures depends on the nature of the junctions which may be tunnel barriers, point contacts, or intermetallic interfaces. For all junction types, the resistance of disordered F/N/F perpendicular spin valves as a function of the angle between magnetization vectors is shown to obey a simple universal law. The spin-current induced magnetization torque can be measured by the angular magnetoresistance of these spin valves. The results are generalized to arbitrary magnetoelectronic circuits.
Magnetoelectric coupling has been a trending research topic in both organic and inorganic materials and hybrids. The concept of controlling magnetism using an electric field is particularly appealing in energy efficient applications. In this spirit, ferroelectricity has been introduced to organic spin valves to manipulate the magneto transport, where the spin transport through the ferromagnet/organic spacer interfaces (spinterface) are under intensive study. The ferroelectric materials in the organic spin valves provide a knob to vary the interfacial energy alignment and the interfacial crysta…
We report the observation of tunneling anisotropic magnetoresistance (TAMR) in an organic spin-valve-like structure with only one ferromagnetic electrode. The device is based on a new high mobility perylene diimide-based n-type organic semiconductor. The effect originates from the tunneling injection from the LSMO contact and can thus occur even for organic layers which are too thick to support the assumption of tunneling through the layer. Magnetoresistance measurements show a clear spin-valve signal, with the typical two step switching pattern caused by the magnetocrystalline anisotropy of t…
We have observed distinct temperature-dependent magnetization reversal modes in a perpendicular (Co/Pd)4/Co/Cu/(Co/Ni)4/Co pseudo-spin-valve, which are correlated with spin-transport properties. At 300 K, magnetization reversal occurs by vertically correlated domains. Below 200 K the hysteresis loop becomes bifurcated due to laterally correlated reversal of the individual stacks. The magnetic configuration change also leads to higher spin disorders and a significant increase in the giant magnetoresistance effect. First order reversal curve measurements reveal that the coupled state can be re-e…
We report the observation of the spin valve effect in (Ga,Mn)As/p-GaAs/(Ga,Mn)As trilayer devices. Magnetoresistance measurements carried out in the current in plane geometry reveal positive magnetoresistance peaks when the two ferromagnetic layers are magnetized orthogonal to each other. Measurements carried out for different post-growth annealing conditions and spacer layer thickness suggest that the positive magnetoresistance peaks originate in a noncollinear spin valve effect due to spin-dependent scattering that is believed to occur primarily at interfaces.
To augment the magnetoresistance (MR) ratio of n-type non-degenerate Si-based lateral spin valves (Si-LSVs), we modify the doping profile in the Si layer and introduce a larger local strain into the Si channel by changing a capping insulator. The highest MR ratio of 1.4% is achieved in the Si-LSVs through these improvements, with significant roles played by a reduction in the resistance-area product of the ferromagnetic contacts and an enhancement of the momentum relaxation time in the Si channel.
We use a previously proposed theory for the temperature dependence of tunneling magnetoresistance to shed light on ongoing efforts to optimize spin valves. First we show that a mechanism in which spin valve performance at finite temperatures is limited by uncorrelated thermal fluctuations of magnetization orientations on opposite sides of a tunnel junction is in good agreement with recent studies of the temperature-dependent magnetoresistance of high quality tunnel junctions with MgO barriers. Using this insight, we propose a simple formula which captures the advantages for spin-valve optimiza…
Spin-valve is a microelectronic device in which high and low resistance states are realized by utilizing both charge and spin of carriers. Spin-valve structures used in modern hard drive read-heads and magnetic random access memories comprise two ferromagnetic (FM) electrodes whose relative magnetization orientations can be switched between parallel and antiparallel configurations, yielding the desired giant or tunneling magnetoresistance effect. In this paper we demonstrate >100$% spin-valve-like signal in a NiFe/IrMn/MgO/Pt stack with an antiferromagnet (AFM) on one side and a non-magnetic m…
We determine from first-principles the Curie temperature Tc for bulk Co in the hcp, fcc, bcc, and tetragonalized bct phases, for FeCo alloys, and for bcc and bct Fe. For bcc-Co, Tc=1420 K is predicted. This would be the highest Curie temperature among the Co phases, suggesting that bcc-Co/MgO/bcc-Co tunnel junctions offer high magnetoresistance ratios even at room temperature. The Curie temperatures are calculated by mapping ab initio results to a Heisenberg model, which is solved by a Monte Carlo method.
Defects ubiquitously exist in crystal materials and usually exhibit a very different nature than the bulk matrix, and hence, their presence can have significant impacts on the properties of devices. Although it is well accepted that the properties of defects are determined by their unique atomic environments, the precise knowledge of such relationships is far from clear for most oxides due to the complexity of defects and difficulties in characterization. Here, we fabricate a 36.8° SrRuO3 grain boundary of which the transport measurements show a spin-valve magnetoresistance. We identify its at…
We present a study of the effects of inelastic scattering on the transport properties of various nanoscale devices, namely H$_2$ molecules sandwiched between Pt contacts, and a spin-valve made by an organic molecule attached to model half-metal ferromagnetic current/voltage probes. In both cases we use a tight-binding Su-Schrieffer-Heeger Hamiltonian and the inelastic effects are treated with a multi-channel method, including Pauli exclusion principle. In the case of the H$_2$ molecule, we find that inelastic backscattering is responsible for the drop of the differential conductance at biases …
We report the results of magnetoresistance measurements in vertical organic spin valves with the magnetic field oriented perpendicular to the layer stack. The magnetoresistance measurements were performed after carefully preparing either parallel or antiparallel in-plane magnetization states of the magnetic electrodes in order to observe traces of Hanle precession. Due to the low mobility in organic semiconductors the transit time of spin polarized carriers should allow for precession of the spins in perpendicular fields which in statistical average would quench the magnetoresistance. However,…
We report giant magnetoresistance up to 150 percent at low bias current and low temperature as well as room temperature magnetoresistance in polymeric spin-valves having the structure LSMO/conjugated polymer/Co. The conjugated polymers, regiorandom and regioregular P3HT were used as the spacer materials. We observed an asymmetric bias voltage dependence of different devices and additional, hitherto unseen, peaks in MR vs. magnetic field plot with low bias currents measurements that we attribute to local magnetic moments due to spin-trapping in the defects in the spacer material. Also, various …
Naturally occurring spin-valve-type magnetoresistance (SVMR), recently observed in Sr2FeMoO6 samples, suggests the possibility of decoupling the maximal resistance from the coercivity of the sample. Here we present the evidence that SVMR can be engineered in specifically designed and fabricated core-shell nanoparticle systems, realized here in terms of soft magnetic Fe3O4 as the core and hard magnetic insulator CoFe2O4 as the shell materials. We show that this provides a magnetically switchable tunnel barrier that controls the magnetoresistance of the system, instead of the magnetic properties…
We report the current-perpendicular-to-plane giant magnetoresistance of a spin valve with Co2MnSi (CMS) Heusler alloy ferromagnetic electrodes. A multilayer stack of Cr/Ag/Cr/CMS/Cu/CMS/Fe25Co75/Ir28Mn72/Ru was deposited on a MgO (001) single crystal substrate. The bottom CMS layer was epitaxially grown on the Cr/Ag/Cr buffer layers and was ordered to the L21 structure after annealing at 673 K. The upper CMS layer was found to grow epitaxially on the Cu spacer layer despite the large lattice mismatch between Cu and CMS. The highest MR ratios of 8.6% and 30.7% for CPP-GMR were recorded at room …
Magnetic molecules possess a high potential as building blocks for the design of spintronic devices. Moreover, the use of molecular materials opens the way for the controlled use of bottom-up, e.g. supramolecular, processing techniques combining massively parallel self-fabrication with conventional top-down nanostructuring techniques. The development of solid state spintronic devices based on the giant magnetoresistance (GMR), tunnel magnetoresistance (TMR), and spin valve effects has revolutionized the field of magnetic memory applications. Recently, organic semiconductors were inserted into …
Organic spintronic devices have been appealing because of the long spin life time of the charge carriers in the organic materials and their low cost, flexibility and chemical diversity. In previous studies, the control of resistance of organic spin valves is generally achieved by the alignment of the magnetization directions of the two ferromagnetic electrodes, generating magnetoresistance.1 Here we employ a new knob to tune the resistance of organic spin valves by adding a thin ferroelectric interfacial layer between the ferromagnetic electrode and the organic spacer. We show that the resista…
Vanadium based dichalcogenides, VSe$_2$, are two-dimensional materials in which magnetic Vanadium atoms are arranged in a hexagonal lattice and are coupled ferromagnetically within the plane. However, adjacent atomic planes are coupled antiferromagnetically. This provides new and interesting opportunities for application in spintronics and data storage and processing technologies. A spin valve magnetoresistance may be achieved when magnetic moments of both atomic planes are driven to parallel alignment by an external magnetic field. The resistance change associated with the transition from ant…
The impact of in-plane alternating currents on the exchange bias, resistance, and magnetoresistance of a CoFe/NiCoO/CoFe/Cu/CoFe spin-valve is studied. With increasing current, the resistance is increased while the maximum magnetoresistance ratio decreases. Noticeably, the reversal of the pinned layer is systematically suppressed in both field sweeping directions. Since the NiCoO oxide is a good insulator, it is expected that the ac current flows only in the CoFe/Cu/CoFe top layers, thus ruling out any presence of spin-transfer torque acting on the spins in the antiferromagnetic layer. Instead…
We report on a local spin valve effect observed unambiguously in lateral all-semiconductor all-electrical spin injection devices, employing p+-(Ga,Mn)As/n+-GaAs Esaki diode structures as spin aligning contacts. We discuss the observed local spin-valve signal as a result of interplay between spin-transport-related contribution and tunneling anisotropic magnetoresistance of magnetic contacts. The magnitude of the spin-related magnetoresistance change is equal to 30 Ohm which is twice the magnitude of the measured non-local signal.
Giant tunnel magnetoresistance (TMR) ratios of 417% at room temperature (RT) and 914% at 3 K were demonstrated in epitaxial Fe/MgO/Fe(001) exchanged-biased spin-valve magnetic tunnel junctions (MTJs) by tuning growth conditions for each layer, combining sputter deposition for the Fe layers, electron-beam evaporation of the MgO barrier, and barrier interface tuning. Clear TMR oscillation as a function of the MgO thickness with a large peak-to-valley difference of ~80% was observed when the layers were grown on a highly (001)-oriented Cr buffer layer. Specific features of the observed MTJs are s…
The layered compound La2-2xSr1+2xMn2O7 (x=0.3) consists of bilayers of metallic MnO2 sheets separated by insulating material. The compound exhibits markedly anisotropic magnetoresistance at temperatures well below the three-dimensional magnetic ordering temperature TC=90 K in addition to colossal magnetoresistance around TC. We present neutron diffraction data which show that the magnetic structure of this material switches from antiferromagnetic stacking of the (ferromagnetically ordered) sheets in zero field to ferromagnetic stacking in a field of 1.5 Tesla. The data are the first to be coll…
Electric-field control of magnetism via inverse magnetostrictive effect is an efficient path towards improving energy-efficient storage and sensing devices based on giant magnetoresistance effect. In this letter, we report on lateral electric-field driven strain-mediated modulation of magnetic properties in Co$/$Cu$/$Py pseudo spin valve grown on ferroelectric PMN-PT substrate. We show a decrease of the giant magnetoresistance ratio of the pseudo spin valve with increasing electric field, which is attributed to the deviation of the Co layer magnetization from the initial direction due to strai…
We demonstrate pseudo spin valves with a (112)-textured DO_22 MnGa (MnGa) tilted magnetization fixed layer and an in-plane CoFe free layer. Single D0_22 MnGa films exhibit a small magnetoresistance (MR) typically observed in metals. In MnGa/Cu/ CoFe spin valves a transition from a negative (-0.08%) to positive (3.88%) MR is realized by introducing a thin spin polarizing CoFe insertion layer at the MnGa/Cu interface and tailoring the MnGa thickness. Finally, the exchange coupling between the MnGa and CoFe insertion layer is studied using a first-order reversal curve (FORC) technique.
Nonlinear current-voltage characteristics and magnetoresistance of point contacts between a normal metal (N) and films of amorphous ferromagnet (F) Co40Fe40B20 of different thickness, exchange-biased by antiferromagnetic Mn80Ir20 are studied. A surface spin valve effect in the conductance of such F-N contacts is observed. The effect of exchange bias is found to be inversely proportional to the Co40Fe40B20 film thickness. This behavior as well as other magneto-transport effects we observe on single exchange-pinned ferromagnetic films are similar in nature to those found in conventional three-la…
Using resonant soft x-ray scattering as a function of both temperature and magnetic field, we reveal a large number of almost degenerate magnetic orders in SrCo6O11. The Ising-like spins in this frustrated material in fact exhibit a so-called magnetic devil's staircase. It is demonstrated how a magnetic field induces transitions between different microscopic spin configurations, which is responsible for the magnetoresistance of SrCo6O11. This material therefore constitutes a unique combination of a magnetic devil's staircase and spin valve effects, yielding a novel type of magnetoresistance sy…
We have studied microwave emission from a current-perpendicular-to-plane pseudo spin valve nanopillars with Heusler alloy Co2Fe(Ga0.5Ge0.5) electrodes. Large emission amplitude exceeding 150 nV/Hz^0.5, partly owing to the large magnetoresistance, and narrow generation linewidth below 10 MHz are observed. We also find that the linewidth shows significant dependence on the applied field magnitude and its angle within the film plane. A minimum in the linewidth is observed when the slope of the frequency versus current becomes near zero. This agrees with theoretical prediction that takes into acco…
The unusual magnetoresistance (MR) behavior in Sr2FeMoO6, recently termed as spin-valve type MR (SVMR), presents several anomalies that are little understood so far. The difficulty in probing the origin of this phenomenon, arising from the magnetic property of only a small volume fraction of the ferromagnetic bulk, is circumvented in the present study by the use of ac susceptibility measurements that are sensitive to the slope rather than the magnitude of the magnetization. The present study unravels a spin-glass (SG) like surface layer around each soft ferromagnetic (FM) grain of Sr2FeMoO6. I…
Spin accumulation and spin precession in single-layer graphene are studied by non-local spin valve measurements at room temperature. The dependence of the non-local magnetoresistance on electrode spacing is investigated and the results indicate a spin diffusion length of ~1.6 microns and a spin injection/detection efficiency of 0.013. Electrical detection of the spin precession confirms that the non-local signal originates from spin injection and transport. Fitting of the Hanle spin precession data yields a spin relaxation time of ~84 ps and a spin diffusion length of ~1.5 microns, which is co…
We observe magnetization dynamics induced by spin momentum transfer in the noise spectra of current perpendicular to the plane giant magnetoresistance spin valves. The dynamics are observable only for those combinations of current direction and magnetic configuration in which spin transfer acts to reorient the free layer magnetization away from the direction set by the net magnetic field. Detailed measurements as a function of magnetic configuration reveal an evolution of the noise spectra, going from a spectrum with a well-defined noise peak when the free layer is roughly collinear with the p…
We have investigated the influence of anisotropic magnetoresistance (AMR) on nonlocal signals in Si-based multi-terminal devices with ferromagnetic Fe electrodes. The AMR of the Fe electrodes was found to have a significant influence on nonlocal signals when the in-plane device structure is not optimized. Moreover, realization of a pure spin current by spin diffusion was found to be virtually impossible because of the electric potential distribution in the depth direction in the Si channel. Although apparent signals indicating the spin-valve effect were not detected, we mainly present structur…
Colossal negative magnetoresistance Δρ(T,B) observed in La(0.6)Y(0.1)Ca(0.3)MnO(3) at B=1T shows a nearly perfect symmetry around T_0=160K suggesting a universal field-induced transport mechanism in this material. Attributing this symmetry to strong magnetic fluctuations (triggered by the Y substitution and further enhanced by magnetic field, both above and below the field-dependent Curie temperature T_C(B)=T_0), the data are interpreted in terms of the nonthermal spin hopping and magnetization M dependent charge carrier localization scenario leading to Δρ(T,B)= -ρ_s(1-exp(-γM^2)) with M(T,B)=…
A large spin-dependent and electric field-tunable magnetoresistance of a two-dimensional electron system (2DES) is a key ingredient for the realization of many novel concepts for spin-based electronic devices. The low magnetoresistance observed during the last decades in devices with lateral semiconducting (SC) transport channels between ferromagnetic (FM) source (S) and drain (D) contacts has been the main obstacle for realizing spin field effect transistor proposals. Here, we show both, a large two terminal magnetoresistance in lateral 2DES-based spin valve geometry, with up to 80% resistanc…
Two-dimensional (2D) layered transition metal dichalcogenides (TMDs) have been recently proposed as appealing candidate materials for spintronic applications owing to their distinctive atomic crystal structure and exotic physical properties arising from the large bonding anisotropy. Here we introduce the first MoS2-based spin-valves that employ monolayer MoS2 as the nonmagnetic spacer. In contrast with what expected from the semiconducting band-structure of MoS2, the vertically sandwiched-MoS2 layers exhibit metallic behavior. This originates from their strong hybridization with the Ni and Fe …
We present a theoretical study on the spin-dependent transport through a spin valve consisting of graphene sandwiched between two magnetic leads with an arbitrary orientation of the lead magnetization. No gate voltage is applied. Using Keldysh's nonequilibrium Green's function method we show that, in absence of external magnetic fields, the current-voltage curves are nonlinear. Around zero bias the differential conductance versus bias voltage possesses a strong dip. The zero-bias anomaly in the tunnel magnetoresistance (TMR) is affected strongly by the leads spin polarization. Depending on the…
To study spin flipping within the antiferromagnet IrMn, we extended prior Current-Perpendicular-to-Plane (CPP) Giant Magnetoresistance (GMR) studies of Py-based exchange-biased-spin-valves containing IrMn inserts to thicker IrMn layers-5 nm less than or equal to t(IrMn) less than or equal to 30 nm. Unexpectedly, AΔR = A[R(AP) - R(P)]--the difference in specific resistance between the anti-parallel (AP) and parallel (P) magnetic states of the two Py layers-did not decrease with increasing t(IrMn), for t(IrMn) greater than 5 nm, but rather became constant to within our measuring uncertainty. Thi…
The chirality-induced spin selectivity (CISS) effect enables the detection of chirality as electrical charge signals. It is often studied using a two-terminal circuit geometry where a ferromagnet is connected to a chiral component, and a change of electrical resistance is reported upon magnetization reversal. This is however not expected in the linear response regime because of compensating reciprocal processes, limiting the interpretation of experimental results. Here we show that magnetoresistance effects can indeed appear even in the linear response regime, either by changing the magnitude …
The propagation of a domain wall in a submicron ferromagnetic spin-valve stripe is investigated using giant magnetoresistance. A notch in the stripe efficiently traps an injected wall stopping the domain propagation. The authors show that the magnetic field at which the wall is depinned displays a stochastic nature. Moreover, the depinning statistics are significantly different for head to head and tail-to-tail domain walls. This is attributed to the dipolar field generated in the vicinity of the notch by the pinned layer of the spin-valve.
We demonstrate the spin valve effect by ballistic transport in fully epitaxial MnAs ferromagnetic metal / GaAs semiconductor / GaAs:MnAs granular hybrid heterostructures. The GaAs:MnAs material contains ferromagnetic MnAs nanoparticles in a GaAs matrix, and acts as a spin injector and a spin detector. Although the barrier height of the GaAs/MnAs interface was found to be very small, relatively large magnetoresistance was observed. This result shows that by using ballistic transport, we can realize a large spin valve effect without inserting a high tunnel barrier at the ferromagnetic metal / se…
The charge and spin diffusion equations taking into account spin-flip and spin-transfer torque were numerically solved using a finite element method in complex non-collinear geometry with strongly inhomogeneous current flow. As an illustration, spin-dependent transport through a non-magnetic nanoconstriction separating two magnetic layers was investigated. Unexpected results such as vortices of spin-currents in the vicinity of the nanoconstriction were obtained. The angular variations of magnetoresistance and spin-transfer torque are strongly influenced by the structure geometry.
We report ab initio calculations of spin-dependent transport in single atomic carbon chains bridging two zigzag graphene nanoribbon electrodes. Our calculations show that carbon atomic chains coupled to graphene electrodes are perfect spin-filters with almost 100 % spin polarization. Moreover, carbon atomic chains can also show a very large bias-dependent magnetoresistance up to 1000000 % as perfect spin-valves. These two spin-related properties are independent on the length of carbon chains. Our report, the spin-filter and spin-valve are conserved in a single device simultaneously, opens a ne…
Noncollinear frustrated magnets are proposed as a new class of spintronic materials with high magnetoresistance which can be controlled with relatively small applied voltages. It is demonstrated that their magnetic configuration strongly depends on position of the Fermi energy and applied voltage. The voltage induced control of noncollinear frustrated materials (VCFM) can be seen as a way to intrinsic control of colossal magnetoresistance (CMR) and is the bulk material counterpart of spin transfer torque concept used to control giant magnetoresistance in layered spin-valve structures.
Thin van der Waals (vdW) layered magnetic materials disclose the possibility to realize vdW heterostructures with new functionalities. Here we report on the realization and investigation of tunneling spin valves based on van der Waals heterostructures consisting of an atomically thin hBN layer acting as tunnel barrier and two exfoliated Fe3GeTe2 crystals acting as ferromagnetic electrodes. Low-temperature anomalous Hall effect measurements show that thin Fe3GeTe2 crystals are metallic ferromagnets with an easy axis perpendicular to the layers, and a very sharp magnetization switching at magnet…
We report magnetization and magetoresistance measurements in hybrid ferromagnetic metal/semiconductor heterostructures comprised of MnAs/(Ga,Mn)As bilayers. Our measurements show that the (metallic) MnAs and (semiconducting) (Ga,Mn)As layers are exchange coupled, re- sulting in an exchange biasing of the magnetically softer (Ga,Mn)As layer that weakens with layer thickness. Magnetoresistance measurements in the current-perpendicular-to-the-plane geometry show a spin valve effect in these self-exchange biased bilayers. Similar measurements in MnAs/p- GaAs/(Ga,Mn)As trilayers show that the excha…