Mechanical Properties of APbX3 (A=Cs or CH3NH3; X=I or Br) Perovskite Single Crystals
Yevgeny Rakita, Sidney R. Cohen, Nir Klein Kedem, Gary Hodes, David Cahen
备注：
20 pages (including 4 pages of Supporting Information after the references), 3 figures (+3 in the Supporting Information), 2 tables (+1 in the Supporting Information)
The remarkable optoelectronic, and especially photovoltaic performance of hybrid-organic-inorganic perovskite (HOIP) materials drives efforts to connect materials properties to this performance. From nano-indentation experiments on solution-grown single crystals we obtain elastic modulus and nano-hardness values of APbX3 (A = Cs, CH3NH3 and X = I, Br). The Youngs moduli are about 14, 19.5 and 16 GPa, for CH3NH3PbI3, CH3NH3PbBr3 and CsPbBr3, respectively, lending credence to theoretically calculated values. We discuss possible relevance of our results to suggested self-healing, ion diffusion and ease of manufacturing. Using our results, together with literature data on elastic moduli, we classified HOIPs amongst relevant materials groups, based on their elasto-mechanical properties.
Metal halide perovskites have recently emerged as promising materials for the next generation of optoelectronic devices owing to their remarkable intrinsic properties. In the growth of perovskite crystals, the substrates are essential and play a vital role. Herein, substrate engineering in the growth of perovskite crystals have been reviewed. Particularly, various modified strategies and corresponding mechanism based on the substrate engineering applied to the optimization of thickness, nucleation and growth rate are highlighted. Then the alterable adhesion to substrates will also be discussed…
The mechanical properties of formamidinium halide perovskite FABX3(FA = CH(NH2)2; B = Pb, Sn; X = Br, I) were systematically investigated by using the first-principles calculations. Our results reveal that FABX3 perovskites possess excellent mechanical flexibility, ductility and strong anisotropy. It shows that the planar organic cation FA+ has an important effect on the mechanical properties of FABX3 perovskites. In addition, our results indicate that: (i) the moduli (bulk modulus B, Young's modulus E, and shear modulus G) of FABBr3 are larger than those of FABI3 for the same B atom and (ii) …
Twin boundaries (TBs) were identified to show conflicting positive/negative effects on the physical properties of CH3NH3PbI3 perovskite, but their roles on the mechanical properties are pending. Herein, tensile characteristics of a variety of TB-dominated bicrystalline CH3NH3PbI3 perovskites are explored using molecular simulations. TB-contained CH3NH3PbI3 are classified into four types from their tensile ductile detwinning characteristics. Type I is characterized by smooth loading flow stressstrain responses, originating from relatively uniform stress distribution induced gradual amorphizatio…
Halide perovskites are recently emerged as one of the frontline optoelectronic materials for device applications and have been extensively studied in past few years. Among these while, lead-based materials were most widely explored, investigation of optical properties of lead-free perovskites is limited. Being optically active, these materials were expected to show light-induced enhanced photoconductivity and the same was reported for lead halide perovskite single crystals. However, on contrary, herein, light-induced degradation of bismuth halide perovskite Cs3Bi2Cl9 single crystals is reporte…
The single phase polycrystalline Ba1/4Sr3/4MnO3 layered perovskite manganite has been synthesized by combustion method having various crystallite sizes. The room temperature X-ray diffraction patterns reveal that Ba1/4Sr3/4MnO3 crystallizes into hexagonal crystal structure with space group P63/mmc as confirmed by Rietveld refinement. The scanning electron micrographs of Ba1/4Sr3/4MnO3 reveal uniform crystallite size of the samples. Effect of crystallite size on lattice strain and crystal structure has been studied using Rietveld refinement and Williamson-Hall plot, respectively. The structural…
2D layered hybrid organic-inorganic perovskites (HOIPs) have demonstrated improved stability and promising photovoltaic performance. The mechanical properties of such functional materials are both fundamentally and practically important to achieve both high performance and mechanical stable (flexible) devices. Here we report the mechanical properties of a series of 2D layered lead iodide HOIPs and investigate the role of structural sub-units (e.g., variation of the length of the organic spacer molecules -R and the number of inorganic layer -n) on the mechanical properties. While 2D HOIPs have …
2D Ruddlesden Popper perovskites have been extensively studied for their exceptional optical and electronic characteristics while only a few studies have shed light on their mechanical properties. The existing literature mainly discusses the mechanical strength of single crystal perovskites, however a systematic study towards structure tunability of 2D perovskite thin films is still missing. In this study, we report the effect of number of inorganic layers `n' on elastic modulus of Butylammonium based 2D, quasi-2D perovskites and 3D perovskite using nanoindentation technique. The experimental …
Organic-inorganic halide perovskites, especially methylammonium lead halide, have recently led to a remarkable breakthrough in photovoltaic devices. However, due to the environmental and stability concerns of the heavy metal, lead, in these perovskite based solar cells, research in the non-lead perovskite structures have been attracting increasing attention. In this study, a layered perovskite-like architecture, (NH4)3Bi2I9, was prepared in solution and the structure was solved by single crystal X-ray diffraction. The results from DFT calculations showed the significant lone pair effect of the…
Methylammonium lead iodide perovskite has attracted intensive interest for its diverse optoelectronic applications. However, most studies to date have been limited to bulk thin films that are difficult to implement for integrated device arrays because of their incompatibility with typical lithography processes. We report the first patterned growth of regular arrays of perovskite microplate crystals for functional electronics and optoelectronics. We show that large arrays of lead iodide microplates can be grown from an aqueous solution through a seeded growth process and can be further intercal…
Two-dimensional (2D) hybrid organic-inorganic perovskites (HOIPs) are new members of the 2D materials family with wide tunability, highly dynamic structural features and excellent physical properties. Ultrathin 2D HOIPs and their heterostructures with other 2D materials have been exploited for study of new physical phenomena and novel device applications. The in-plane mechanical properties of 2D ultrathin HOIPs are critical for understanding the coupling between mechanical and other physical fields and for integrated devices applications. Here we report for the first time the in-plane mechanic…
The structural, electrical, optical, and mechanical characteristics of the lead-free halide double perovskites Cs2NaTlX6 X = F, Cl, Br are calculated by utilizing PBE functional within generalized gradient approximation GGA under the context of density functional theory DFT.The structural properties such as lattice parameter, cell volume, total energy, bulk modulus, pressure derivative, and tolerance factor are computed at equilibrium.The electronic density of states reveals the semiconducting nature of the compound and the band structure exhibits the nature of the band gap to be direct.HSE06 …
We report the first single crystal growth of the correlated metal LaNiO3 using a high-pressure optical-image floating zone furnace. The crystals were studied using single crystal/powder x-ray diffraction, resistivity, specific heat, and magnetic susceptibility. The availability of bulk LaNiO3 crystals will (i) promote deep understanding in this correlated material, including the mechanism of enhanced paramagnetic susceptibility, and (ii) provide rich opportunities as a substrate for thin film growth such as important ferroelectric and/or multiferroic materials. This study demonstrates the powe…
Single crystals of a new twinned hexagonal perovskite compound Sr8Os6.3O24 have been synthesized, and structural and magnetic properties have been determined. The compound crystallizes in a hexagonal cell with lattice parameters a = 9.6988(3) Å and c = 18.1657(5) Å. The structure is an eight-layered hexagonal B-site deficient perovskite with the layer sequence (ccch)2 and represents the first example of a hexagonal structure among 5d oxides adopting a twin option. The sample shows spontaneous ferromagnetic magnetization below 430 K with a small saturation moment of 0.11 μB/Os ion. This is the …
In this study, different electronic structure evolutions of perovskite single crystals are found via angle-resolved photoelectron spectroscopy (ARPES): (i) unchanged top valence band (VB) dispersions under different temperatures can be found in the CH3NH3PbI3, (ii) phase transitions induced the evolution of top VB dispersions, and even a top VB splitting with Rashba effects can be observed in the CH3NH3PbBr3. Combined with low-energy electron diffraction (LEED), metastable atom electron spectroscopy (MAES), and DFT calculation, we confirm different band structure evolutions observed in these t…
Hybrid metal-organic perovskite solar cells have astounded the solar cell community with their rapid rise in efficiency over the past three years. Despite this success, the basic processes governing the photogeneration of free charges, particularly their dynamics and efficiency, remain unknown. Here we use ultrabroadband pulses of THz frequency light to see the intrinsic photophysical properties of single crystal lead halide perovskite just femtoseconds after a photon is first absorbed. Our spectra reveal the dynamics and efficiencies of free charge creation, the remarkable ease in which they …
We report an investigation of perovskite-type SmScO3 and NdScO3 single crystals by Raman scattering in various scattering configurations and at different wavelengths. The reported Raman spectra, together with the phonon mode assignment, set the basis for the use of Raman scattering for the structural investigation of RE-scandates. Further to the phonon signature, a fluorescence signal is observed for both scandates and is particularly intense for NdScO3 when using a 488 or 514 nm excitation line. A comparison of Raman spectra of RE-scandates with literature Raman data on orthorhombic perovskit…
Two new perovskite oxychalcogenides, Ca2CuFeO3S and Ca2CuFeO3Se, have been synthesized in evacuated quartz tubes. They crystallize in P4/nmm space group with lattice parameters a = 3.8271(1), c = 14.9485(2) Å and a = 3.8605(1), c = 15.3030(2) Å for Ca2CuFeO3S and Ca2CuFeO3Se, respectively. They appear to be the first layered chalcogenide perovskites involving calcium and are structural analogs of the corresponding Sr and Ba compounds. The new compounds exhibit semiconducting properties with energy gap decreasing from the oxysulfide to the oxyselenide. Possibility of introducing Ca2+ into struc…
Using nanoprobe X-ray diffraction microscopy, we investigate the relationship between residual strains from crystal growth in CsPbBr$_3$ thin film crystals, their stability, and local bandgap. We find that out-of-plane compressive strain that arises from cooldown from crystallization is detrimental to material stability under X-ray irradiation. We also find that the optical photoluminescence red shifts as a result of the out-of-plane compressive strain. The sensitivity of bandgap to strain suggests possible applications such as stress-sensitive sensors. Mosaicity, the formation of small misori…
Over the last few years of the heyday of hybrid halide perovskites, so many metal cations additives have been tested to improve their optoelectronic properties that it is already difficult to find an element that has not yet been tried. In general, the variety of these approaches is united under the name "doping", however, there is currently no clear understanding of the mechanisms of the influence of the metal ion additives on the properties of the lead halide perovskite materials. For many ions there is even no consensus on the most fundamental questions: what lattice position does a given i…
The layered perovskite YBaCuFeO5 (YBCFO) is able to adopt chiral magnetic order up to unexpectedly high temperatures, paving the way to strong magnetoelectric coupling at room temperature. In this perovskite A-site cations are fully ordered whereas the occupancy of the B-sites strongly depend on the preparation process. Though the structure is not geometrically frustrated, the presence of partial Fe3+/Cu2+ disorder at the B-sites produces magnetic frustration. In an effort to increase the spin-orbit coupling in the system, we have synthesized and studied YBaCuFe0.95Mn0.05O5 in single crystal f…
Here, we report structural and optical properties of (ALa)(FeMn)O6 (A = Ba and Sr) double perovskite synthesized via auto-combustion followed by a calcination process. Rietveld refinement of the structure using x-ray diffraction data reveals that (BaLa)(FeMn)O6 crystallizes into cubic crystal structure with space group Pm-3m while (SrLa)(FeMn)O6 crystallizes into rhombohedral crystal structure having space group R-3c. The absorption spectrum measurement using UV-Vis spectroscopy reveals that these samples are perfect insulator having an energy band gap between conduction and valence band of th…
Based on the reported ion migration under electric field in hybrid lead halide perovskites we have developed a bright, light emitting electrochemical cell with CH3NH3PbBr3 single crystals directly grown on vertically aligned carbon nanotube (VACNT) forests as contact electrodes. Under the applied electric field, charged ions in the crystal drift and accumulate in the vicinity of the electrodes, resulting in an in operando formed p-i-n heterojunction. The decreased interface energy barrier and the strong charge injection due to the CNT tip enhanced electric field, result in a bright green light…
Based on differential thermal analysis (DTA) and X-ray powder diffraction (XRD), a description of the system Nd$_2$O$_3$--Lu$_2$O$_3$--Sc$_2$O$_3$ was obtained by thermodynamic assessment. Four fields of primary crystallization could be identified; from melt compositions close to the Lu$_2$O$_3$--Sc$_2$O$_3$ edge the rare-earth oxide C-phase crystallizes first, which is stable down to room temperature. From Nd$_2$O$_3$ rich melts the X-phase forms, which is stable only at high temperatures. An additional field, where the alternative high-temperature phase H solidifies as primary product touche…
Organic-inorganic halide perovskites have been intensively re-investigated due to their applications, yet the opto-electronic function of the organic cation remains unclear. Through organic-selective resonant Auger electron spectroscopy measurements on well-defined single crystal surfaces, we find evidence for electronic coupling in the unoccupied states between the organic and inorganic sub-lattices of the prototypical hybrid perovskite, which is contrary to the notion based on previous studies that the organic cation is electronically inert. The coupling is relevant for electron dynamics in …
ABO3 oxides with the perovskite-related structures are attracting significant interest due to their promising physical and chemical properties for many applications requiring tunable chemistry, including fuel cells, catalysis, and electrochemical water splitting. Here we report on the crystal structure of the entire family of perovskite oxides with ABO3 stoichiometry, where A and B are Ba, Sr, Mn, Ce. Given the vast size of this chemically complex material system, exploration for stable perovskite-related structures with respect to its constituent elements and annealing temperature is performe…
Main physical characteristics, crystal, magnetic and electronic structures, of cerium-based perovskites CeTmO3 [Tm3+ = Sc, Ti, V] are systematically investigated via the first-principles computations. Full-potential linear augmented plane-wave with the local density approximation and generalized gradient approximation, under Perdew-Burke-Ernzerh and Wu-Cohen, based on DFT. The optimized crystal parameters indicate that the crystal of compounds can categorized under cubic structure (space group Pm-3m, no. 221), and their obtained lattice constants in good agreement with the available experiment…
Despite soaring performance of organic-inorganic hybrid perovskite materials in recent years, the mechanism of their decomposition at actual operation condition has been elusive. Herein, we elucidated the decrystallization process of CH3NH3PbI3 perovskite crystals via localized charges and identified polarity-dependent degradation pathway by carrying out time-evolution measurements for absorption spectra of perovskite films with underlying different charge transport layers and ab initio molecular dynamics calculations. It was found that the carrier polarity (hole-rich or electron-rich) inside …
Hybrid lead-halide perovskites have emerged as an excellent class of photovoltaic materials. Recent reports suggest that the organic molecular cation is responsible for local polar fluctuations that inhibit carrier recombination. We combine low frequency Raman scattering with first-principles molecular dynamics (MD) to study the fundamental nature of these local polar fluctuations. Our observations of a strong central peak in both hybrid (CH$_3$NH$_3$PbBr$_3$) and all-inorganic (CsPbBr$_3$) lead-halide perovskites show that anharmonic, local polar fluctuations are intrinsic to the general lead…
Methylammonium lead triiodide (CH3NH3PbI3) perovskite solar cell is a gem in the list of photovoltaic semiconductors. Although there are numerous fundamental and technological questions yet to be addressed covering various aspects of this system for its commercialization, this study has employed first-principles DFT to model the [PbI6(CH3NH3)n]m zero-dimensional nanoclusters. Using the calculated binding energy landscapes, it has answered the question: why the corner-sharing PbI6 octahedron is surrounded by eight units of the organic cation in the large-scale supramolecular structures of the C…
The electronic structure of the cleaved perovskite (CH3NH3PbBr3) single crystal was studied in an ultra-high vacuum (UHV) system by angle-resolved photoemission spectroscopy (ARPES) and inverse photoelectron spectroscopy (IPES). Highly reproducible dispersive features of the valence bands were observed with nice symmetry about the Brillouin zone center and boundaries. The largest dispersion width was found to be ~0.73 eV and ~0.98 eV along the ΓX and ΓM directions, respectively. The effective mass of the holes was estimated to be ~0.59 m0. The quality of the surface was verified by atomic forc…
Halide perovskites are promising semiconductor materials for optoelectronics. One of their unique features is the synthesis, that could be performed by the crystallization from the solution. This method is fast, but practically couldn't be optimized due to the strongly non-equilibrium conditions of crystal growth. Another quality limitation is the typical incorporation of organic solvent molecules into crystals when perovskite crystallization is performed from solution with organic solvent. Here we report an alternative method of perovskite single crystal growth based on the counterdiffusion o…
Inorganic metal-halide cubic perovskite semiconductors have become more popular in industrial applications of photovoltaic and optoelectronic devices. Among various perovskites, lead-free materials are currently most explored due to their non-toxic effect on the environment. In this study, the structural, electronic, optical, and mechanical properties of lead-free cubic perovskite materials FrBX3 (B = Ge, Sn; X = Cl, Br, I) are investigated through first-principles density-functional theory (DFT) calculations. These materials are found to exhibit semiconducting behavior with direct bandgap ene…
The structures of the recently reported ordered perovskites SrLa(FeTi)O6 and BaLa(FeTi)O6 have been revisited using Rietveld analysis of the powder x-ray diffraction data. Our studies clearly show that earlier authors have incorrectly reported the tetragonal structure in the I4/m space group for SrLa(FeTi)O6 and the cubic structure in the Fm3m space group for BaLa(FeTi)O6. The correct structure is found to be orthorhombic in the Pnma space group for SrLa(FeTi)O6 while cubic in the Pm3m space group for BaLa(FeTi)O6. Thus the BaLa(FeTi)O6 is not an ordered double perovskite as the occupancies of…
The phonon spectra of calcium, strontium, barium, radium, cadmium, zinc, magnesium, germanium, tin, and lead titanates with the perovskite structure are calculated from first principles within the density functional theory. By analyzing the unstable modes in the phonon spectra, the possible lattice distortions are determined and the energies of the corresponding phases are calculated. From analyzing the phonon spectra, force constants, and eigenvectors of TO phonons, a conclusion is drawn on the origin of the ferroelectricity in considered crystals. It is shown that the main factors determinin…
Two-dimensional (2D) perovskite materials have recently re-attracted intense research interest for applications in photovoltaics and optoelectronics. As a consequence of the dielectric and quantum confinement effect, they show strongly bound and stable excitons at room temperature. In this report, the band-edge exciton fine structure and in particular its exciton and biexciton dynamics in high quality crystals of (PEA)2PbI4 are investigated. A comparison of bulk and surface exciton lifetimes yields a room temperature surface recombination velocity of 2x10^3cm/s and an intrinsic lifetime of 185…
The crystal structures of the Sr1-xCaxRuO3 perovskites are investigated using both long range and local structural probes. High resolution synchrotron powder X-ray diffraction characterization at ambient temperature shows that the materials are orthorhombic to high precision, and we support previous work showing that Ca2+ substitution for Sr2+ primarily changes the tilting of rigid corner-sharing RuO6 octahedra at their shared oxygen vertices. X-ray pair distribution function analysis for SrRuO3, CaRuO3 and one intermediate composition show them to be locally monoclinic, and no long range or l…
We describe a first open-access database of experimentally investigated hybrid organic-inorganic materials with two-dimensional (2D) perovskite-like crystal structure. The database includes 515 compounds, containing 180 different organic cations, 10 metals (Pb, Sn, Bi, Cd, Cu, Fe, Ge, Mn, Pd, Sb) and 3 halogens (I, Br, Cl) known so far and will be regularly updated. The database contains a geometrical and crystal chemical analysis of the structures, which are useful to reveal quantitative structure-property relationships for this class of compounds. We show that the penetration depth of spacer…
Halide perovskites are a versatile class of semiconductors employed for high performance emerging optoelectronic devices, including flexoelectric systems, yet the influence of their ionic nature on their mechanical behaviour is still to be understood. Here, a combination of atomic-force, optical and compositional X-ray microscopy techniques is employed to shed light on the mechanical properties of halide perovskite films at the nanoscale. We reveal mechanical domains within and between morphological grains, enclosed by mechanical boundaries of higher Young's Modulus than the bulk parent materi…
Single crystals of Cs2BiAgBr6 lead-free perovskite were grown by crystallization from supersaturated solution. According to characterization by XRD and EBSD methods the double perovskite single crystal are of the cubic Fm-3m symmetry with the lattice constant a = 11.20 Å. DFT predictions based on the single crystal X-ray diffraction analysis reveal that the material is an indirect band gap semiconductor. Low temperature (1.4 K) photoluminescence spectra demonstrate three broadened bands that correspond to two lowest computed indirect and one direct band-to-band transitions.
We investigate the structural, electronic and optical properties of mixed bromide-iodide lead perovskite solar cell CH$_3$NH$_3$Pb(I$_{1-x}$Br$_x$)$_3$ by means of the virtual crystal approximation (VCA) within density functional theory (DFT). Optimizing the atomic positions and lattice parameters increasing the bromide content $x$ from 0.0 to 1.0, we fit the calculated lattice parameter and energy band gap to the linear and quadratic function of Br content, respectively, which are in good agreement with the experiment, respecting the Vegard's law. With the calculated exciton binding energy an…
Hybrid perovskite thin films have demonstrated impressive performance for solar energy conversion and optoelectronic applications. However, further progress will benefit from a better knowledge of the intrinsic photophysics of materials. Here, the low temperature emission properties of CH3NH3PbI3 single crystals are investigated and compared to those of thin polycrystalline films by means of steady-state and time-resolved photoluminescence spectroscopy. While the emission properties of thin films and crystals appear relatively similar at room temperature, low temperature photoluminescence spec…
We use resonant and non-resonant X-ray diffraction measurements in combination with first-principles electronic structure calculations and Monte Carlo simulations to study the relationship between crystal structure and multiferroic orders in the orthorhombic perovskite manganites, o-$R$MnO$_3$ ($R$ is a rare-earth cation or Y). In particular, we focus on how the internal lattice parameters (Mn-O bond lengths and Mn-O-Mn bond angles) evolve under chemical pressure and epitaxial strain, and the effect of these structural variations on the microscopic exchange interactions and long-range magnetic…
The molybdate oxides SrMoO$_3$, PbMoO$_3$, and LaMoO$_3$ are a class of metallic perovskites that exhibit interesting properties including high mobility, and unusual resistivity behavior. We use first-principles methods based on density functional theory to explore the electronic, crystal, and magnetic structure of these materials. In order to account for the electron correlations in the partially-filled Mo $4d$ shell, a local Hubbard $U$ interaction is included. The value of $U$ is estimated via the constrained random-phase approximation approach, and the dependence of the results on the choi…
Tail state formation in solar cell absorbers leads to a detrimental effect on solar cell performance. Nevertheless, the characterization of the band tailing in experimental semiconductor crystals is generally difficult. In this article, to determine the tail state generation in various solar cell materials, we have developed a quite general theoretical scheme in which the experimental Urbach energy is compared with the absorption edge energy derived from density functional theory (DFT) calculation. For this purpose, the absorption spectra of solar cell materials, including CdTe, CuInSe2 (CISe)…