We report the synthesis and variation of superconductivity parameters such as transition temperature Tc, upper critical field Hc, critical current density Jc, irreversibility field Hirr and flux pinning parameter (Fp) for the MgB2-xCx system with nano-Carbon doping up to x=0.20. Carbon substitutes successfully on boron site and results in significant enhancement of Hirr and Jc(H). Resistivity measurements reveal a continuous decrease in Tc under zero applied field, while the same improves remarkably at higher fields with an increase in nano-C content for MgB2-xCx system. The irreversibility field value (Hirr) is 7.6 & 6.6 Tesla at 5 and 10K respectively for the pristine sample, which is enhanced to 13.4 and 11.0 Tesla for x = .08 sample at same temperatures. Compared to undoped sample, critical current density (Jc) for the x=0.08 nano-Carbon doped sample is increased by a factor of 24 at 10K at 6 Tesla field.
AC magnetic susceptibilities of electron-doped Pr_{1.85}Ce_{0.15}CuO_4 (PCCO) and Sm_{1.85}Ce_{0.15}CuO_4 (SCCO) granular thin films have been measured as a function of temperature and magnetic-field strength. Depending on the level of homogeneity of our films, two different types of the irreversibility line (IL) defined as the intergrain-loss peak temperature in the imaginary part of susceptibility have been found. The obtained results are described via the critical-state model taking into account the low-field grain-boundary pinning. The extracted pinning-force densities in more granular SCC…
We have measured the isothermal field dependence of magnetization of the Mo$_{100-x}$Re$_x$ (15 $\leq$ x $\leq$ 48) alloys, and have estimated the critical current and pinning force density from these measurements. We have performed structural characterization of the above alloys using standard techniques, and analyzed the field dependence of critical current and pinning force density using existing theories. Our results indicate that dislocation networks and point defects like voids and interstitial imperfections are the main flux line pinning centres in the Mo$_{100-x}$Re$_x$ alloys in the i…
We performed systematic AC susceptibility and magnetic moment measurements to investigate the vortex dynamics and pinning in the $EuRbFe_4As_4$ single crystal as a function of temperature, frequency, and DC magnetic field. The vortex solid-liquid line was determined and it fits well with $H(T_p)=H_0(1-t_p)^β$ using $β$=1.74-1.91, for $H\parallel ab$. It indicates a rather high pinning strength of the vortex system. The activation energy $U_0$ was determined from thermally activated flux creep theory and reached 6700 K at low fields, suggesting strong vortex pinning. A field dependence of $U_0(…
Critical current density was measured at 4.2 K for MgB2 strands with and without SiC additions. In some cases measurements were performed on longer (1 m) samples wound on barrels, and these were compared to magnetic measurements. Most measurements were performed on short samples at higher fields (up to 18 T). It was found that in-situ processed strands with 10% SiC additions HT at 700-800C show improved Hr and Fp values as compared to control samples, with Hr increasing by 1.5 T. At 900C even larger improvements are seen, with Hr reaching 18 T and Fp values maximizing at 20 GN/m3.
We have studied the influence of columnar defects, created by heavy-ion (Kr) irradiation with doses up to 6 10^11 Kr-ions/cm2, on the superconducting critical parameters of single crystalline (YxTm1-x)Ba2Cu3O7. Magnetisation measurements in pulsed fields up to 50 T in the temperature range 4.2 - 90 K revealed that: (i) in fields up to T the critical current Jc(H,T) is considerably enhanced and (ii) down to temperatures T ~ 40 K the irreversibility field Hirr(T) is strongly increased. The field range and magnitude of the Jc(H,T) and Hirr(T) enhancement increase with increasing irradiation dose.…
The magnetic characteristics for superconducting samples of different geometries (plates and films of various widths) and orientation with respect to external field are compared. A similarity is established between the magnetization curves M(H) and the corresponding susceptibilities. A sign reversal is predicted for the 3rd harmonic of the ac susceptibillity when the irreversibility mechanism changes from bulk pinning to edge barrier. A mutual influence of the edge barrier and bulk pinning on the magnetization curves and field-dependent ac susceptibility is studied on the basis of an exactly s…
The $AC$ magnetic penetration depth $λ(T,H,j)$ was measured in presence of a macroscopic $DC$ (Bean) supercurrent, $j$. In single crystal BSCCO below approximately 28 K, $λ(T,H,j)$ exhibits thermal hysteresis. The irreversibility arises from a shift of the vortex position within its pinning well as $j$ changes. It is demonstrated that below a new irreversibility temperature, the nonequilibrium Campbell length depends upon the ratio $j/j_c$. $λ(T,H,j)$ {\it increases} with $j/j_c$ as expected for a non-parabolic potential well whose curvature {\it decreases} with the displacement. Qualitatively…
We report a study of the pinning properties of Fe/MgB2 tapes performed by means of ac magnetic susceptibility measurements. In particular, the third harmonic response has been measured as a function of the dc magnetic field up to 9 T, at different temperatures, for various frequencies and amplitudes of the ac field. The irreversibility line has been determined using the third harmonic onset criterion for samples made with different ball-milled MgB2 powders. The study of the harmonic response allows us to probe the nature of the vortex pinning and to analyse its influence on the enhancement of …
Evidence of how temperature takes part in the magnetic irreversibility in the intermediate state of a cylinder and various disks of pure type-I superconducting lead is presented. Isothermal measurements of first magnetization curves and magnetic hysteresis cycles are analyzed in a reduced representation that defines an equilibrium state for flux penetration in all the samples and reveals that flux expulsion depends on temperature in the disks but not in the cylinder. The magnetic field at which irreversibility sets in along the descending branch of the hysteresis cycle and the remnant magnetiz…
We study finite-size effects at the onset of the irreversible magnetic behaviour of micron-sized Bi$_2$Sr$_2$CaCu$_2$O$_{8+δ}$ single crystals by using silicon micro-oscillators. We find an irreversibility line appearing well below the thermodynamic Bragg-glass melting line at a magnetic field which increases both with increasing the sample radius and with decreasing the temperature. We show that this size-dependent irreversibility line can be identified with the crossover between the Larkin and the random manifold regimes of the vortex lattice transverse roughness. Our method allows to determ…
By scaling isothermal magnetization data measured at different temperatures in the mixed state of high-Tc superconductors, we show that in some cases the sample magnetization, measured in increasing magnetic field below the irreversibility line, is identical with the equilibrium magnetization even in magnetic fields well within the irreversible regime. This surprising behavior can hardly be explained in terms of traditional models of vortex pinning in the bulk of the sample.
Pinning force data, Fp, of a variety of Fe-based high-Tc superconductors (11-, 111-, 122- and 1111-type) were analyzed by means of a scaling approach based on own experimental data and an extensive collection of literature data. The literature data were mostly replotted, but also converted from critical current measurements together with data for the irreversibility line when available from the same authors. Using the scaling approaches of Dew-Hughes and Kramer, we determined the scaling behavior and the best fits to the theory. The data of most experiments analyzed show a good scaling behavio…
We present magnetization studies as a function of time, temperature and magnetic field for $H$ $\parallel$ c-axis, in a hole-doped pnictide superconductor, La$_{0.34}$Na$_{0.66}$Fe$_2$As$_2$, with, $T_c$ $\approx$ 27 K. The obtained vortex phase-diagram shows that the magnetic irreversibility line is very close to the mean-field superconducting transition line, similar to the low $T_c$ superconductors, evidencing a strong pinning behavior. The irreversibility line does not follow a power law behavior with ($T_c$-$T$), however, it is well described using an expression developed in the literatur…
The relationship between irreversibility field, Hirr, and crystallinity of MgB2 bulks including carbon substituted samples was studied. The Hirr was found to increase with an increase of FWHM of MgB2 (110) peak, which corresponds to distortion of honeycomb boron sheet, and their universal correlation was discovered even including carbon substituted samples. Excellent Jc characteristics under high magnetic fields were observed in samples with large FWHM of (110) due to the enhanced intraband scattering and strengthened grain boundary flux pinning. The relationship between crystallinity and Hirr…
The anisotropic irreversibility field B$_{Irr}$ of two $YBa_2Cu_3O_{7-x}$ thin films doped with additional rare earth (RE)=(Gd,Y) and Zr and containing strong correlated pins (splayed BaZrO$_{3}$ nanorods, and $RE_2O_3$ nanoprecipitates), has been measured over a very broad range up to 45T at temperatures 56 K<T<$T_c$. We found that the experimental angular dependence of $B_{Irr}(θ)$ does not follow the mass anisotropy scaling $B_{Irr}(θ)=B_{Irr}(0)(cos^2θ+γ^{-2}sin^2θ)^{-1/2}$, where $γ=(m_c/m_{ab})^{1/2}=5-6$ for the RE-doped $YBa_2Cu_3O_{7-x}$ (REBCO) crystals, m$_{ab}$ and m$_{c}$ are the …
MgB2-diamond nanocomposite superconductors have been synthesized by addition of nano-diamond powder. Microstructural analysis shows that the nanocomposite superconductor consists of tightly-packed MgB2 nano-grains (~50-100 nm) with highly-dispersed and uniformly-distributed diamond nanoparticles (~10-20 nm) inside the grains. The Jc-H and Hiir-T characteristics have been significantly improved in this MgB2-diamond nanocomposite, compared to MgB2 bulk materials prepared by other techniques. Also, the Jc value of 1x104 A/cm2 at 20 K and 4 T and the Hirr value of 6.4 T at 20 K have been achieved
Heterogeneous sonochemical method was applied for synthesis of novel superconducting nanocomposites consisting of magnetic (and/or nonmagnetic) nanoparticles embedded into the bulk of ceramic superconductors. In addition to in-situ production of the efficient pinning centers, this synthesis method considerably improves the interbrain coupling. Significant enhancement of the magnetic irreversibility is reported for Fe2O3 nanoparticles embedded into the bulk of MgB2 superconductor. Nonmagnetic Mo2O5 nanoparticles also increase pinning strength, but less than magnetic Fe2O3. Detailed magnetizatio…
Bulk samples of MgB2 were prepared with 5, 10, and 15% wt.% Y2O3 nanoparticles added using a simple solid-state reaction route. Transmission electron microscopy (TEM) showed a fine nanostructure consisting of ~3-5 nm YB4 nanoparticles embedded within MgB2 grains of ~400 nm size. Compared to an undoped control sample, an improvement in the in-field critical current density Jc was observed, most notably for 10% doping. At 4.2K, the lower bound Jc value was ~2x105A.cm-2 at 2T. At 20K, the corresponding value was ~8x104A.cm-2. Irreversibility fields were ~11.5 T at 4.2K and 5.5T at 20K, compared t…
Doping effect of diamond nanoparticles on the superconducting properties of MgB2 bulk material has been studied. It is found that the superconducting transition temperature Tc of MgB2 is suppressed by the diamond-doping, however, the irreversibility field Hirr and the critical current density Jc are systematically enhanced. Microstructural analysis shows that the diamond-doped MgB2 superconductor consists of tightly-packed MgB2 nano-grains (~50-100 nm) with highly-dispersed and uniformly-distributed diamond nanoparticles (~10-20 nm) inside the grains. High density of dislocations and diamond n…
The upper critical field and flux pinning in MgB2 single crystals were investigated. The implications of these properties for technical applications are discussed and compared with transport properties of polycrystalline bulk samples and wires. In these untextured materials current percolation is important, especially at high magnetic fields. It is shown that the anisotropy of the upper critical field influences the "irreversibility line" and that the application range of MgB2 is limited by the smallest upper critical field (i.e., for the field direction perpendicular to the boron planes). Dis…
It is shown that the large effect of heavy ion-irradiation on the thermodynamical properties of the anisotropic superconductor YBa$_{2}$Cu$_{3}$O$_{7-δ}$ extends well into the superconducting fluctuation regime. The presence of the induced amorphous columnar defects shifts the specific heat maximum at the normal-to-superconducting transition. This effect is similar to that recently put into evidence in cubic K$_{x}$Ba$_{1-x}$BiO$_{3}$ ($x \simeq 0.35$). In both compounds, vortex pinning manifests itself as a sharp angular dependence of the \em equilibrium \rm torque. In YBa$_{2}$Cu$_{3}$O$_{7-…
Enhancement of flux pinning by magnetic nanoparticles embedded into the bulk of type-2 superconductor is studied both theoretically and experimentally. Magnetic part of the pinning force associated with the interaction between a spherical magnetic inclusion and an Abrikosov vortex was calculated in the London approximation. Calculations are supported by the experimental results obtained on sonochemically modified MgB2 superconductor with embedded magnetic Fe2O3 nanoparticles and compared to MgB2 with nonmagnetic Mo2O5 pinning centers of similar concentration and particle size distribution. It …
This paper reports the observation of hysteresis in the vortex pinning in a superconductor / ferromagnetic epitaxial nanocomposite consisting of fcc Gd particles incorporated in a Nb matrix. We show that this hysteretic pinning is associated with magnetic reversal losses in the Gd particles and is fundamentally different in origin to pinning interactions previously observed for ferromagnetic particles or other microstructural features.
We show that for a thin superconducting strip placed in a transverse dc magnetic field - the typical geometry of experiments with high-Tc superconductors - the application of a weak ac magnetic field perpendicular to the dc field generates a dc voltage in the strip. This voltage leads to the decay of the critical currents circulating in the strip, and eventually the equilibrium state of the superconductor is established. This relaxation is not due to thermally activated flux creep but to the "walking" motion of vortices in the two-dimensional critical state of the strip with in-plane ac field.…
We report the high-pressure synthesis of the electron-doped infinite-layer superconductor Sr0.9La0.1CuO2 and its superconducting properties. A Rietveld analysis of X-ray powder diffraction data showed that, within the resolution of the measurement, the sample had purely an infinite-layer structure without any discernible impurities. The superconducting volume fraction and the transition width were greatly improved compared to those in previous reports. The irreversibility field line and the intragranular critical current density were much higher than those of La1.85Sr0.15CuO4 and Nd1.85Ce0.15C…
We have prepared Na-doped YBa2Cu3Oy (YBa1.9Na0.1Cu3Oy +40mol%Y211) (YBNCO) and Na-free YBa2Cu3Oy (YBCO) samples by the Melt-Textured Growth (MTG) method to study the effect of doped Na ion on flux pinning. The ac susceptibility curves (acs) as well as the hysteresis loops were measured for the samples. Then the effective pinning energy (U(T,Hdc,J)), irreversibility line (Hirr(T)) and critical current density (jc(Hdc)) were determined, where T, Hdc and J are temperature, dc magnetic field and current density, respectively. We found that, with Na doping, the Hirr(T) line shifted to lower tempera…
Superconducting MgB2 strands with nanometer-scale SiC additions have been investigated systematically using transport and magnetic measurements. A comparative study of MgB2 strands with different nano-SiC addition levels has shown C-doping-enhanced critical current density Jc through enhancements in the upper critical field, Hc2, and decreased anisotropy. The critical current density and flux pinning force density obtained from magnetic measurements were found to greatly differ from the values obtained through transport measurements, particularly with regards to magnetic field dependence. The …
Nanowires of two-dimensional (2D) crystals of type-II superconductor NbSe$_2$ prepared by electron-beam lithography were studied, focusing on the effect of the motion of Abrikosov vortices. We present magnetoresistance measurements on these nanowires and show features related to vortex crossing, trapping, and pinning. The vortex crossing rate was found to vary non-monotonically with the applied field, which results in non-monotonic magnetoresistance variations in agreement with theoretical calculations in the London approximation. Above the lower critical field, $H_{c1}$, the crossing rate is …
The irreversible magnetization of the layered high-T_{c} superconductor Bi_{2+x}Sr_{2-(x+y)}Cu_{1+y}O_{6 +- delta} (Bi-2201) has been measured by means of a capacitive torquemeter up to B=28 T and down to T=60 mK. No magnetization jumps, peak effects or crossovers between different pinning mechanisms appear to be present. The deduced irreversibility field B_{irr} can not be described by the law B_{irr}(T)=B_{irr}(0)(1-T/T_{c})^n based on flux creep, but an excellent agreement is found with the analytical form of the melting line of the flux lattice as calculated from the Lindemann criterion. T…
We investigated the effect of nanoscale-C doping on the critical current density Jc and irreversibility field Birr of Fe-sheathed MgB2 tapes prepared by the in-situ powder-in-tube method. The tapes were heat treated at 600-950C for 1 h. Higher values of Jc and Birr were seen for 5 at.%C-doped MgB2 tapes at higher sintering temperatures, where substantial substitution of boron for carbon occurred. The C-doped samples sintered at 950C showed the highest Birr, for example, at 4.2 K, the Birr reached 22.9 T. In particular, at 20 K, Birr for the C-doped tape achieved 9 T, which is comparable to the…
We report high-resolution measurements of voltage (V) noise in the mixed state of micrometre-sized thin films of amorphous Nb0.7Ge0.3, which is a good representative of weak-pinning superconductors. There is a remarkable difference between the noise below and above the irreversibility field Birr. Below Birr, in the presence of measurable pinning, the noise at small applied currents resembles shot noise, and in the regime of flux flow at larger currents decreases with increasing voltage due to a progressive ordering of the vortex motion. At magnetic fields B between Birr and the upper critical …
By doping MgB_2 superconductor with SiC nano-particles, we have successfully introduced pinning sites directly into the crystal lattice of MgB_2 grains (intra-grain pinning). It became possible due to the combination of counter-balanced Si and C co-substitution for B, leading to a large number of intra-granular dislocations and the dispersed nano-size impurities induced by the substitution. The magnetic field dependence of the critical current density was significantly improved in a wide temperature range, whereas the transition temperature in the sample MgB_2(SiC)_x having x = 0.34, the highe…
Bulk superconductor samples of YBa2Cu3-xZnxO7-δ with x = 0, 0.01, 0.03 are synthesized by solid-state reaction route. The structural characterisation of all samples has been carried out by x-ray-diffraction (XRD) and transmission electron microscopy (TEM) techniques. The x-ray diffraction patterns indicate that the gross structure/phase of YBa2Cu3-xZnxO7-δ do not change with the substitution of Zn up to x=0.03. In TEM investigations of Zn-doped Y-based cuprates a number of ZnO nano-flower and nano-rod of Y-211 phase are found dispersed in regular YBa2Cu3-xZnxO7 matrix. These dispersed nano-flo…
REBa$_{2}$Cu$_{3}$O$_{x}$ films can achieve remarkably high critical current density values by the incorporation of insulating nanoparticles. A particular interesting case concerns BaZrO$_{3}$ (BZO) nanorods, whose strongly correlated effect is seen at high temperatures. Here we investigate the field, temperature and angular dependence of the critical current density over a wide temperature range from 4.2 K to 77 K, and magnetic fields up to 31 T. We show that the correlated c-axis pinning of BZO nanorods becomes progressively less obvious at lower temperature. Indeed at 4.2 K and fields up to…
The pinning of quantized flux lines, or vortices, in the mixed state is used to quantify the effect of impurities in iron-based superconductors (IBS). Disorder at two length scales is relevant in these materials. Strong flux pinning resulting from nm-scale heterogeneity of the superconducting properties leads to the very disordered vortex ensembles observed in the IBS, and to the pronounced maximum in the critical current density jc at low magnetic fields. Disorder at the atomic scale, most likely induced by the dopant atoms, leads to "weak collective pinning" and a magnetic field-independent …
We investigated the pinning of flux lines in a superconducting film by a regular array of magnetic antidots. The sample consists of a Co/Pt multilayer with perpendicular magnetic anisotropy in which a regular pattern of submicron holes is introduced and which is covered by a type-II superconducting Pb film. The resulting ferromagnetic/superconducting heterostructure shows a pronounced asymmetric magnetization curve with respect to the field polarity. This asymmetry clearly demonstrates that the magnetic contribution dominates the pinning potential imposed by the magnetic antidots on the superc…
We report the synthesis and characterization of graphite (C) doped MgB2-xCx (x = 0.0, 0.1, 0.2 and 0.3) samples. The crystal structure and microstructural characterization have been investigated by x-ray diffractometer and transmission electron microscopic (TEM) analysis. The superconducting properties especially Jc and Hc2 have been measured by employing physical property measurement system. We found that the graphite doping affects the lattice parameters as well as the microstructure of MgB2 superconductor. In case of optimally doped (x=0.1) sample, the critical current density at 5K corresp…
Nb films containing extended arrays of holes with 45-nm diameter and 100-nm spacing have been fabricated using anodized aluminum oxide (AAO) as substrate. Pronounced matching effects in the magnetization and Little-Parks oscillations of the superconducting critical temperature have been observed in fields up to 9 kOe. Flux pinning in the patterned samples is enhanced by two orders of magnitude as compared to unpatterned reference samples in applied fields exceeding 5 kOe. Matching effects are a dominant contribution to vortex pinning at temperatures as low as 4.2 K due to the extremely small s…
Polycrystalline MgB2-xCx samples with x=0.05, 0.1, 0.2, 0.3, 0.4 nano-particle carbon powder were prepared using an in-situ reaction method under well controlled conditions to limit the extent of C substitution. The phases, lattice parameters, microstructures, superconductivity and flux pinning were characterized by XRD, TEM, and magnetic measurements. It was found that both the a-axis lattice parameter and the Tc decreased monotonically with increasing doping level. For the sample doped with the highest nominal composition of x=0.4 the Tc dropped only 2.7K. The nano-C-doped samples showed an …
Epitaxial NdBa2Cu3O7-x films with a hybrid nanoscale defect structure comprised of BaZrO3 nanodot arrays aligned along the c-axis in one half of the film thickness and aligned perpendicular to the c-axis in the other half thickness of the film were fabricated. Transmission electron microscopy images confirm the orientation of the nanoscale defect structures. The angular dependence of critical current density, Jc, at 77 K, 1 T, shows significantly reduced angular variation of Jc. This study nicely demonstrates how pinning characteristics can be tuned by tuning the nanoscale defect structures wi…
The interaction between a straight vortex line in a superconducting film and a soft magnetic nanodisk in the magnetic vortex state in the presence of a magnetic field applied parallel to the film surfaces is studied theoretically. The superconductor is described by London theory and the nanodisk by the Landau-Lifshitz continuum theory of magnetism, using the approximation known as the rigid vortex model. Pinning of the vortex line by the nanodisk is found to result, predominantly, from the interaction between the vortex line and the changes in the nanodisk magnetization induced by the magnetic…
The magnetoresistivity and critical current density of well characterized Si-nanoparticle doped and undoped Cu-sheathed MgB$_{2}$ tapes have been measured at temperatures $T\geq 28$ K in magnetic fields $B\leq 0.9$ T. The irreversibility line $B_{irr}(T)$ for doped tape shows a stepwise variation with a kink around 0.3 T. Such $B_{irr}(T)$ variation is typical for high-temperature superconductors with columnar defects (a kink occurs near the matching field $% B_ϕ$) and is very different from a smooth $B_{irr}(T)$ variation in undoped MgB$_{2}$ samples. The microstructure studies of nanoparticl…
The enhancement of the critical current density (Jc(H)) of carbon and nano-SiC doped MgB2 is presented and compared. The upper critical field (Hc2) being determined from resistivity under magnetic field experiments is though improved for both C substitution and nano-SiC addition the same is more pronounced for the former. In MgB2-xCx carbon is substituted for boron that induces disorder in the boron network and acts as internal pinning centres. The optimal Jc(H) values are obtained for x = 0.1 sample . In case of nano-SiC doped in MgB2, the Jc(H) improves more profoundly and two simultaneous m…
One of the most promising routes for achieving unprecedentedly high critical currents in superconductors is to incorporate dispersed, non-superconducting nanoparticles to control the dissipative motion of vortices. However, these inclusions reduce the overall superconducting volume and can strain the interlaying superconducting matrix, which can detrimentally reduce $T_c$. Consequently, an optimal balance must be achieved between the nanoparticle density $n_p$ and size $d$. Determining this balance requires garnering a better understanding of vortex-nanoparticle interactions, described by stro…
New results of the investigations critical current problems in the high temperature oxide superconductors are presented, basing on an analysis of the flux pinning on nano-sized centers. New model of the interaction pancake vortices with the nano-sized centers is proposed, while comparison of obtained results with others pinning forces approaches presented. The energy balance approach is applied, which leads to the appearance of the potential barrier determining the pancake vortices movement in the flux creep process. Various initial positions of the captured vortex have been analyzed, while va…
We present a microwave study of the angular dependence of the flux-flow resistivity $ρ_{ff}$ and of the pinning constant $k_p$ in YBCO thin films containing BZO nanorods. We find that BZO nanorods are very efficient pinning centers, even in tilted fields. We find that $ρ_{ff}$ is a scaling function of a reduced field $H/f(θ)$. We extend a model for the anisotropic motion of vortices in uniaxially anisotropic superconductor, able to describe the experimental $f(θ)$ on the basis of only the intrinsic anisotropy of YBCO. The pinning constant $k_p$, by contrast, exhibits different field dependence…
Magnesium diboride (MgB2) powder was mechanically alloyed by high energy ball milling with C to a composition of Mg(B0.95C0.05)2 and then sintered at 1000 C in a hot isostatic press. Milling times varied from 1 minute to 3000 minutes. Full C incorporation required only 30-60 min of milling. Grain size of sintered samples decreased with increased milling time to less than 30 nm for 20-50 hrs of milling. Milling had a weak detrimental effect on connectivity. Strong irreversibility field (H*) increase (from 13.3 T to 17.2 T at 4.2 K) due to increased milling time was observed and correlated linea…
Nano-scaled substrate surface roughness is shown to strongly influence the critical current density Jc in YBCO films made by pulse-laser-deposition on the crystalline LaAlO3 substrates consisting of two separate twin-free and twin-rich regions. The nano-scaled corrugated surface was created in the twin-rich region during the deposition process. Using magneto-optical imaging techniques coupled with optical and atomic force microscopy, we observed an enhanced flux pinning in the YBCO films in the twin-rich region, resulted in \~30% increase in Jc, which was unambiguously confirmed by the direct …
We identify a phase transition in the vortex system of a high-temperature superconductor with nano-columnar stacks of precipitates as strong vortex pinning centers. Above a particular, temperature-dependent field $B_X(T)$ the vortex response is no longer determined by the nano-columns, and is instead determined by point-like pinning. This phase transition leads to the change in the measured critical current density as a function of angle between the applied magnetic field and the nano-columns. Below the unbinding, there is a strong maximum in $J_C$ when field is aligned parallel to the columns…
We investigated the effect of SiC nano-particle doping on the crystal lattice structure, critical temperature T_c, critical current density J_c, and flux pinning in MgB_2 superconductor. A series of MgB_{2-x}(SiC)_{x/2} samples with x = 0 to 1.0 were fabricated using in-situ reaction process. The contraction of the lattice and depression of T_c with increasing SiC doping level remained rather small due to the counter-balanced effect of Si and C co-doping. The high level Si and C co-doping allowed the creation of intra-grain defects and highly dispersed nano-inclusions within the grains which c…
Polycrystalline MgB2 samples with 10 wt % silicon powder addition were prepared by an in-situ reaction process. Two different Si powders, one with coarse (44 mm) and the other with nano-size (<100 nm) particles were used for making samples. The phases, microstructures, and flux pinning were characterized by XRD, TEM, and magnetic measurements. It was observed that the samples doped with nano-sized Si powder showed a significantly improved field dependence of the critical current over a wide temperature range compared with both undoped samples and samples with coarse Si added. Jc is as high as …
We study the effect of proton irradiation on Ba(Fe$_{0.96}$Co$_{0.04}$)$_2$As$_2$ superconducting single crystals from combined magnetisation and magnetoresistivity measurements. The study allows the extraction of the values of the apparent pinning energy $U_0$ of the samples prior to and after irradiation, as well as comparison of the values of $U_0$ obtained from the flux-flow reversible region with those from the flux-creep irreversible region. Irradiation reduces $T_c$ modestly, but significantly reduces $U_0$ in both regimes: the critical current density $J_c$ is modified, most strikingly…
We report on the thickness dependence of the superconducting characteristics including critical current Ic, critical current density Jc, transition temperature Tc, irreversibility field Hirr, bulk pinning force plot Fp(H), and the normal state resistivity curve measured after successive ion milling of ~ 1 um thick high Ic YBa2Cu3O7-x films made by an ex situ metal-organic deposition process on Ni-W rolling-assisted biaxially textured substrates (RABiTS). Contrary to many recent data, mostly on in situ pulsed laser deposition (PLD) films, which show strong depression of Jc with increasing film …
The dynamics of quantized magnetic vortices and their pinning by materials defects determine electromagnetic properties of superconductors, particularly their ability to carry non-dissipative currents. Despite recent advances in the understanding of the complex physics of vortex matter, the behavior of vortices driven by current through a multi-scale potential of the actual materials defects is still not well understood, mostly due to the scarcity of appropriate experimental tools capable of tracing vortex trajectories on nanometer scales. Using a novel scanning superconducting quantum interfe…
Superconducting critical currents $j_{c} > 10^{5}$ A/cm$^{2}$ at temperatures $T \sim 50$ K and magnetic fields $B \sim 6$ T are reported for the YBa$_{2}$Cu$_{3-x}$Mo$_{x}$O$_{7+d}$ compound with $x = 0.02$. Clear evidence for the increased pinning force $F_p$ was found from a peak effect present for $j_{c}(B)$. The pinning force was analyzed by a scaling procedure using Kramer's approach. For a wide range of fields and temperatures, we were able to express all $F_p$ data as a single function of a reduced field $b = B/B_k$, where the scaling field $B_{k} << H_{c2}$ was related to the irrevers…
Magneto-optical imaging studies on a high-quality Bi2Sr2CaCu2O8 single crystal partially patterned with a triangular array of holes reveal enhanced flux shielding in the patterned region of the sample. By mapping local magnetic field and shielding current density distributions at different applied magnetic fields and temperatures we determine the regime where pinning from the patterned holes dominates over the intrinsic pinning in the sample. In this regime, the flux density near the center of the patterned region is observed to increase when the applied field is varied from below the matching…
Doping of MgB2 by nano-SiC and its potential for improvement of flux pinning was studied for MgB2-x(SiC)x/2 with x = 0, 0.2 and 0.3 and a 10wt% nano-SiC doped MgB2 samples. Co-substitution of B by Si and C counterbalanced the effects of single-element doping, decreasing Tc by only 1.5K, introducing pinning centres effective at high fields and temperatures and enhancing Jc and Hirr significantly. Compared to the non-doped sample, Jc for the 10wt% doped sample increased by a factor of 32 at 5K and 8T, 42 at 20K and 5T, and 14 at 30K and 2T. At 20K, which is considered to be a benchmark operating…
Hybrid magnetic arrays embedded in superconducting films are ideal systems to study the competition between different physical (such as the coherence length) and structural length scales such as available in artificially produced structures. This interplay leads to oscillation in many magnetically dependent superconducting properties such as the critical currents, resistivity and magnetization. These effects are generally analyzed using two distinct models based on vortex pinning or wire network. In this work, we show that for magnetic dot arrays, as opposed to antidot (i.e holes) arrays, vort…
A series of MgB2 superconducting composite strands co-doped with Dy2O3 and C were prepared via an advanced internal Mg infiltration (AIMI) route.The transport properties and MgB2 layer growth were studied in terms of the Dy2O3 doping level, reaction temperature, and reaction time. Transport studies showed that both critical current densities, Jcs, and irreversibility fields, Birrs, were increased with Dy2O3 doping. The highest layer Jc was 1.35 x 10^5 A/cm2 at 4.2 K, 10 T, 30% higher than that of the best AIMI wires without Dy2O3 doping. The highest "non-barrier" Jc reached 3.6 x 10^4 A/cm2 at…