Hybrid semiconductor-superconductor InAs-Al nanowires with uniform and defect-free crystal interfaces are one of the most promising candidates used in the quest for Majorana zero modes (MZMs). However, InAs nanowires often exhibit a high density of randomly distributed twin defects and stacking faults, which result in an uncontrolled and non-uniform InAs-Al interface. Furthermore, this type of disorder can create potential inhomogeneity in the wire, destroy the topological gap, and form trivial sub-gap states mimicking MZM in transport experiments. Further study shows that reducing the InAs nanowire diameter from growth can significantly suppress the formation of these defects and stacking faults. Here, we demonstrate the in situ growth of ultra-thin InAs nanowires with epitaxial Al film by molecular-beam epitaxy. Our InAs diameter (~ 30 nm) is only one-third of the diameters (~ 100 nm) commonly used in literatures. The ultra-thin InAs nanowires are pure phase crystals for various different growth directions, suggesting a low level of disorder. Transmission electron microscopy confirms an atomically sharp and uniform interface between the Al shell and the InAs wire. Quantum transport study on these devices resolves a hard induced superconducting gap and $2e^-$ periodic Coulomb blockade at zero magnetic field, a necessary step for future MZM experiments. A large zero bias conductance peak with a peak height reaching 80% of $2e^2/h$ is observed.
We report the growth of InAs$_{1-x}$Sb$_{x}$ nanowires ($0\leq x \leq 0.15$) grown by catalyst-free molecular beam epitaxy on silicon (111) substrates. We observed a sharp decrease of stacking fault density in the InAs$_{1-x}$Sb$_{x}$ nanowire crystal structure with increasing antimony content. This decrease leads to a significant increase in the field-effect mobility, this being more than three times greater at room temperature for InAs$_{0.85}$Sb$_{0.15}$ nanowires than InAs nanowires.
InAs nanowires were grown on GaAs substrates by the Au-assisted vapour-liquid-solid (VLS) method in a gas source molecular beam epitaxy (GS-MBE) system. Passivation of the InAs nanowires using InP shells proved difficult due to the tendency for the formation of axial rather than core-shell structures. To circumvent this issue, Al$_x$In$_{1-x}$As or Al$_x$In$_{1-x}$P shells with nominal Al composition fraction of x = 0.20, 0.36, or 0.53 were grown by direct vapour-solid deposition on the sidewalls of the InAs nanowires. Characterization by transmission electron microscopy revealed that the addi…
Self-assembled InAs quantum dots (QDs) grown on GaAs(001) surface by molecular beam epitaxy under continuous and growth-interruption modes exhibit two families of QDs, quasi-3D (Q3D) and 3D QDs, whose volume density evolution is quantitatively described by a rate-equation kinetic model. The volume density of small Q3D QDs decreases exponentially with time during the interruption, while the single-dot mean volume of the large QDs increases by Ostwald ripening. The kinetics of growth involves conversion of quasi-3D to 3D QDs at a rate determined by superstress and participation of the wetting la…
We have investigated in-situ Si doping of InAs nanowires grown by molecular beam epitaxy from gold seeds. The effectiveness of n-type doping is confirmed by electrical measurements showing an increase of the electron density with the Si flux. We also observe an increase of the electron density along the nanowires from the tip to the base, attributed to the dopant incorporation on the nanowire facets whereas no detectable incorporation occurs through the seed. Furthermore the Si incorporation strongly influences the lateral growth of the nanowires without giving rise to significant tapering, re…
We report on the growth of axial InAs-on-GaAs nanowire heterostructures on silicon by molecular beam epitaxy using 20 nm diameter Au catalysts. First, the growth parameters of the GaAs nanowire segment were optimized to achieve a pure wurtzite crystal structure. Then, we developed a two-step growth procedure to enhance the yield of vertical InAs-on-GaAs nanowires. We achieved 90% of straight InAs-on-GaAs nanowires by further optimizing the growth parameters. We investigated the composition change at the interface by energy dispersive X-ray spectroscopy and the nanowire crystal structure by tra…
InAs nanowires have been actively explored as the channel material for high performance transistors owing to their high electron mobility and ease of ohmic metal contact formation. The catalytic growth of non-epitaxial InAs nanowires, however, has often relied on the use of Au colloids which is non-CMOS compatible. Here, we demonstrate the successful synthesis of high yield of crystalline InAs nanowires with high yield and tunable diameters by using Ni nanoparticles as the catalyst material on amorphous SiO2 substrates. The nanowires show superb electrical properties with field-effect electron…
The article presents a mapping of the residual strain along the axis of InAs/InSb heterostructured nanowires. Using confocal Raman measurements, we observe a gradual shift in the TO phonon mode along the axis of these nanowires. We attribute the observed TO phonon shift to a residual strain arising from the InAs/InSb lattice mismatch. We find that the strain is maximum at the interface and then monotonically relaxes towards the tip of the nanowires. We also analyze the crystal structure of the InSb segment through selected area electron diffraction measurements and electron diffraction tomogra…
We present direct evidence of enhanced Ga interdiffusion in InAs free-standing nanowires grown at moderate temperatures by molecular beam epitaxy on GaAs (111)B. Scanning electron microscopy together with X-ray diffraction measurements in coplanar and grazing incidence geometries show that nominally grown InAs NWs are actually made of In$_{0.86}$Ga$_{0.14}$As. Unlike typical vapor-liquid-solid growth, these nanowires are formed by diffusion-induced growth combined with strong interdiffusion from substrate material. Based on the experimental results, a simple nanowire growth model accounting fo…
Guided growth of semiconductor nanowires in nanotube templates has been considered as a potential platform for reproducible integration of III-Vs on silicon or other mismatched substrates. Herein, we report on the challenges and prospects of molecular beam epitaxy of InAs nanowires on SiO2/Si nanotube templates. We show how and under which conditions the nanowire growth is initiated by In-assisted vapor-liquid-solid growth enabled by the local conditions inside the nanotube template. The conditions for high yield of vertical nanowires are investigated in terms of the nanotube depth, diameter a…
By using a C3v symmetric (111) surface as a growth substrate, we are able to achieve high structural symmetry in self-assembled quantum dots, which are suitable for use as quantum-entangled photon emitters. Here we report on the wavelength controllability of InAs dots on InP(111)A, which we realized by tuning the ternary alloy composition of In(Al,Ga)As barriers that were lattice-matched to InP. We changed the peak emission wavelength systematically from 1.3 to 1.7 micrometer by barrier band gap tuning. The observed spectral shift agreed with the result of numerical simulations that assumed a …
We study band alignment in wurtzite-zincblende polytype InAs heterostructured nanowires using temperature dependent resonance Raman measurements. Nanowires having two different wurtzite fractions are investigated. Using visible excitation wavelengths in resonance Raman measurements, we probe the electronic band alignment of these semiconductor nanowires near a high symmetry point of the Brillouin zone (E$_{1}$ gap). The strain in the crystal structure, as revealed from the shift of the phonon mode, explains the observed band alignment at the wurtzite-zincblende interface. Our experimental resu…
We report the detection of quantum confinement in single InAs-InP core-shell nanowires. The wires having an InAs core with ~25 nm diameter are characterized by emission spectra in which two peaks are identified under high excitation intensity conditions. The peaks are caused by emission from the ground and excited quantized levels, due to the quantum confinement in the plane perpendicular to the nanowire axis. We have identified in the emission spectra different energy contributions related to the wurtzite structure of the wires, the strain between the wurtzite core and shell, and the confinem…
We demonstrate the self-assembled growth of vertically aligned GaN nanowire ensembles on a flexible Ti foil by plasma-assisted molecular beam epitaxy. The analysis of single nanowires by transmission electron microscopy reveals that they are single crystalline. Low-temperature photoluminescence spectroscopy demonstrates that, in comparison to standard GaN nanowires grown on Si, the nanowires prepared on the Ti foil exhibit a equivalent crystalline perfection, a higher density of basal-plane stacking faults, but a reduced density of inversion domain boundaries. The room-temperature photolumines…
SnTe topological crystalline insulator nanowires have been grown by molecular beam epitaxy on graphene/SiC substrates. The nanowires have cubic rock-salt structure, they grow along [001] crystallographic direction and have four sidewalls consisting of {100} crystal planes known to host metallic surface states with Dirac dispersion. Thorough high resolution transmission electron microscopy investigations show that the nanowires grow on graphene in the van der Walls epitaxy mode induced when the catalyzing Au nanoparticle mixes with Sn delivered from SnTe flux, providing liquid Au-Sn alloy. The …
Temperature-dependent I-V and C-V spectroscopy of single InAs nanowire field-effect transistors were utilized to directly shed light on the intrinsic electron transport properties as a function of nanowire radius. From C-V characterizations, the densities of thermally-activated fixed charges and trap states on the surface of untreated (i.e., without any surface functionalization) nanowires are investigated while enabling the accurate measurement of the gate oxide capacitance; therefore, leading to the direct assessment of the field-effect mobility for electrons. The field-effect mobility is fo…
The addition of boron to GaAs nanowires grown by self-catalyzed molecular beam epitaxy was found to have a strong effect on the nanowire morphology, with axial growth greatly reduced as the nominal boron concentration was increased. Transmission electron microscopy measurements show that the Ga catalyst droplet was unintentionally consumed during growth. Concurrent radial growth, a rough surface morphology and tapering of nanowires grown under boron flux suggest that this droplet consumption is due to reduced Ga adatom diffusion on the nanowire sidewalls in the presence of boron. Modelling of …
Selective area growth (SAG) of nanowires and networks promise a route toward scalable electronics, photonics and quantum devices based on III-V semiconductor materials. The potential of high-mobility SAG nanowires however is not yet fully realized, since interfacial roughness, misfit dislocations at the nanowire/substrate interface and non-uniform composition due to material intermixing all scatter electrons. Here, we explore SAG of highly lattice-mismatched InAs nanowires on insulating GaAs(001) substrates and address these key challenges. Atomically smooth nanowire/substrate interfaces are a…
InAs nanowires with Al$_x$In$_{1-x}$P or Al$x$In$_{1-x}$As shells were grown on GaAs substrates by the Au-assisted vapour-liquid-solid (VLS) method in a gas source molecular beam epitaxy (GS-MBE) system. Core diameters and shell thicknesses were measured by transmission electron microscopy (TEM). These measurements were then related to selected area diffraction (SAD) patterns to verify either interface coherency or relaxation through misfit dislocations. A theoretical strain model is presented to determine the critical shell thickness for given core diameters. Zincblende stiffness parameters a…
Time- and spectrally-resolved PL from a periodic array of InP/InAs/InP core-multishell nanowires is presented. InAs layer shows multipeak PL spectra. PL decay is nonexponential and very slow, with decay rate depending on energy.
Mn-doped GaAs nanowires were grown in the self-catalytic growth mode on oxidized Si(100) surface by molecular beam epitaxy and characterized by scanning and transmission electron microscopy, Raman scattering, photoluminescence, cathodoluminescence, and electron transport measurements. The transmission electron microscopy studies evidenced the substantial accumulation of Mn inside the catalyzing Ga droplets at the top of the nanowires. Optical and transport measurements revealed that the limit of Mn content for self-catalysed growth of GaAs nanowires corresponds to the doping level, i.e., is mu…
Using ab initio methods based on the density functional theory, we investigate the segregation and formation energies for various dopants (Si, Be, Zn, Sn), commonly used to obtain p- or ntype conductivity in GaAs and InAs nanowires. The distribution of Au and O atoms, which may be unintentionally incorporated during the wire growth, is also studied. The calculations performed for nanowires of zinc blende and wurtzite structure show that the distribution of most of the impurities depends on the crystal structure of the wires. For example, it is shown that the same growth conditions can lead to …
GaAs:Mn nanowires were obtained on GaAs(001) and GaAs(111)B substrates by molecular beam epitaxial growth of (Ga,Mn)As at conditions leading to MnAs phase separation. Their density is proportional to the density of catalyzing MnAs nanoislands, which can be controlled by the Mn flux and/or the substrate temperature. Being rooted in the ferromagnetic semiconductor (Ga,Mn)As, the nanowires combine one-dimensional properties with the magnetic properties of (Ga,Mn)As and provide natural, self assembled structures for nanospintronics.
We report on growth of Te-doped self-catalyzed InAs nanowires by molecular beam epitaxy on silicon (111) substrates. Changes in the wire morphology, i.e. a decrease in length and an increase in diameter have been observed with rising doping level. Crystal structure analysis based on transmission electron microscopy as well as X-ray diffraction reveals an enhancement of the zinc blende/(wurtzite+zinc blende) segment ratio if Te is provided during the growth process. Furthermore, electrical two-point measurements show that increased Te-doping causes a gain in conductivity. Two comparable growth …
We present a capacitance-voltage study for arrays of vertical InAs nanowires. MOS capacitors are obtained by insulating the nanowires with a conformal 10nm HfO2 layer and using a top Cr/Au metallization as one of the capacitor's electrodes. The described fabrication and characterization technique enables a systematic investigation of the carrier density in the nanowires as well as of the quality of the MOS interface.
Quantum dots realized in InAs are versatile systems to study the effect of spin-orbit interaction on the spin coherence, as well as the possibility to manipulate single spins using an electric field. We present transport measurements on quantum dots realized in InAs nanowires. Lithographically defined top-gates are used to locally deplete the nanowire and to form tunneling barriers. By using three gates, we can form either single quantum dots, or two quantum dots in series along the nanowire. Measurements of the stability diagrams for both cases show that this method is suitable for producing …
Recent theory and experiment have suggested that space-charge-limited transport should be prevalent in high aspect-ratio semiconducting nanowires. We report on InAs nanowires exhibiting this mode of transport and utilize the underlying theory to determine the mobility and effective carrier concentration of individual nanowires, both of which are found to be diameter-dependent. Intentionally induced failure by Joule heating supports the notion of space-charge-limited transport and proposes reduced thermal conductivity due to the nanowires polymorphism.
We present self-assembly of InAs/InAlAs quantum dots by droplet epitaxy technique on vicinal GaAs(111)A substrates. The small miscut angle, while maintaining the symmetries imposed to the quantum dot from the surface, allows fast growth rate thanks to the presence of preferential nucleation sites at the step edges. A 100 nm InAlAs metamorphic layer with In content > 50% is already almost fully relaxed with a very flat surface. The quantum dots emit at the 1.3 μm telecom O-band with the fine structure splitting as low as 16 μeV, thus making them suitable as photon sources in quantum communicati…
The present study elucidates the correlation between the structural and optical properties of GaN nanowires grown on Si(111) substrate by plasma assisted molecular beam epitaxy (PA-MBE) technique under various growth conditions. GaN NWs exhibiting different shapes, sizes and distribution were grown at various substrate temperatures with same Ga-N (III-V) ratio of 0.4. We observe that sample grown at lower substrate temperature (~700 degC) results 2-dimensional island like structure with almost very little (~30%) circularity while increasing substrate temperature (>770 degC) leads to growth of …
The electronic properties and nanostructure of InAs nanowires are correlated by creating multiple field effect transistors (FETs) on nanowires grown to have low and high defect density segments. 4.2 K carrier mobilities are ~4X larger in the nominally defect-free segments of the wire. We also find that dark field optical intensity is correlated with the mobility, suggesting a simple route for selecting wires with a low defect density. At low temperatures, FETs fabricated on high defect density segments of InAs nanowires showed transport properties consistent with single electron charging, even…
Evidence is given for the effectiveness of InAs surface passivation by the growth of an epitaxial InAlAs shell. The electron mobility is measured as a function of temperature for both core-shell and unpassivated nanowires, with the core-shell nanowires showing a monotonic increase in mobility as temperature is lowered, in contrast to a turnover in mobility seen for the unpassivated nanowires. We argue that this signifies a reduction in low temperature ionized impurity scattering for the passivated nanowires, implying a reduction in surface states.
We report on the systematic investigation of the optical properties of a selectively grown quantum dot gain material assisted by block-copolymer lithography for potential applications in active optical devices operating in the wavelength range around 1.55 um and above. We investigated a new type of diblock copolymer PS-b-PDMS (polystyrene-block-polydimethylsiloxane) for the fabrication of silicon oxycarbide hard mask for selective area epitaxy of InAs/InP quantum dots. An array of InAs/InP quantum dots was selectively grown via droplet epitaxy. Our detailed investigation of the quantum dot car…
Self-assisted growth of InAs nanowires on graphene by molecular beam epitaxy is reported. Nanowires with diameter of ~50 nm and aspect ratio of up to 100 were achieved. The morphological and structural properties of the nanowires were carefully studied by changing the substrate from bilayer graphene through buffer layer to quasi-free-standing monolayer graphene. The positional relation of the InAs NWs with the graphene substrate was determined. A 30° orientation configuration of some of the InAs NWs is shown to be related to the surface corrugation of the graphene substrate. InAs NW-based devi…
We observe intense pulses of far-infrared electromagnetic radiation emitted from arrays of InAs nanowires. The THz radiation power efficiency of these structures is about 15 times higher compared to a planar InAs substrate. This is explained by the preferential orientation of coherent plasma motion to the wire surface, which overcomes radiation trapping by total-internal reflection. We present evidence that this radiation originates from a low-energy acoustic surface plasmon mode of the nanowire. This is supported by independent measurements of electronic transport on individual nanowires, ult…
We report tunneling spectroscopy measurements of the Zeeman spin splitting in InAs few-electron quantum dots. The dots are formed between two InP barriers in InAs nanowires with a wurtzite crystal structure grown by chemical beam epitaxy. The values of the electron g-factors of the first few electrons entering the dot are found to strongly depend on dot size and range from close to the InAs bulk value in large dots |g^*|=13 down to |g^*|=2.3 for the smallest dots. These findings are discussed in view of a simple model.
We report on the magnetic and structural properties of Ar and Mn implanted InAs epitaxial films grown on GaAs (100) by Molecular Beam Epitaxy (MBE) and the effect of Rapid Thermal Annealing (RTA) for 30 seconds at 750C. Channeling Particle Induced X- ray Emission (PIXE) experiments reveal that after Mn implantation almost all Mn atoms are subsbtitutional in the In-site of the InAs lattice, like in a diluted magnetic semiconductor (DMS). All of these samples show diamagnetic behavior. But, after RTA treatment the Mn-InAs films exhibit room-temperature magnetism. According to PIXE measurements t…
We report on the heterogeneous nucleation of catalyst-free InAs nanowires on Si (111) substrates by chemical beam epitaxy. We show that nanowire nucleation is enhanced by sputtering the silicon substrate with energetic particles. We argue that particle bombardment introduces lattice defects on the silicon surface that serve as preferential nucleation sites. The formation of these nucleation sites can be controlled by the sputtering parameters, allowing the control of nanowire density in a wide range. Nanowire nucleation is accompanied by unwanted parasitic islands, but by careful choice of ann…
We report a significant and persistent enhancement of the conductivity in free-standing non intentionnaly doped InAs nanowires upon irradiation in ultra high vacuum. Combining four-point probe transport measurements performed on nanowires with different surface chemistries, field-effect based measurements and numerical simulations of the electron density, the change of the conductivity is found to be caused by the increase of the surface free carrier concentration. Although an electron beam of a few keV, typically used for the inspection and the processing of materials, propagates through the …
We demonstrate the Au-assisted growth of semiconductor nanowires on different engineered substrates. Two relevant cases are investigated: GaAs/AlGaAs heterostructures capped by a $50 {\rm nm}$-thick InAs layer grown by molecular beam epitaxy and a $2 {\rm μm}$-thick InAs buffer layer on Si(111) obtained by vapor phase epitaxy. Morphological and structural properties of substrates and nanowires are analyzed by atomic force and transmission electron microscopy. Our results indicate a promising direction for the integration of III-V nanostructures on Si-based electronics as well as for the develo…
We report on low temperature (2-30K) electron transport and magneto-transport measurements of a chemically synthesized InAs nanowire. Both the temperature, T, and transverse magnetic field dependences of the nanowire conductance are consistent with the functional forms predicted in one-dimensional (1D) weak localization theory. By fitting the magneto-conductance data to theory, the phase coherence length of electrons is determined to be tens of nanometers with a T-1/3 dependence. Moreover, as the electron density is increased by a gate voltage, the magneto-conductance shows a possible signatur…
We use polarized photocurrent spectroscopy in a nanowire device to investigate the band structure of hexagonal Wurtzite InAs. Signatures of optical transitions between four valence bands and two conduction bands are observed which are consistent with the symmetries expected from group theory. The ground state transition energy identified from photocurrent spectra is seen to be consistent with photoluminescence emitted from a cluster of nanowires from the same growth substrate. From the energies of the observed bands we determine the spin orbit and crystal field energies in Wurtzite InAs. This …
Ability to understand and model the performance limits of nanowire transistors is the key to design of next generation devices. Here, we report studies on high-mobility junction-less gate-all-around nanowire field effect transistor with carrier mobility reaching 2000 cm2/V.s at room temperature. Temperature-dependent transport measurements reveal activated transport at low temperatures due to surface donors, while at room temperature the transport shows a diffusive behavior. From the conductivity data, the extracted value of sound velocity in InAs nanowires is found to be an order less than th…
We study random telegraph noise in the conductance of InAs nanowire field-effect transistors due to single electron trapping in defects. The electron capture and emission times are measured as functions of temperature and gate voltage for individual traps, and are consistent with traps residing in the few-nanometer-thick native oxide, with a Coulomb barrier to trapping. These results suggest that oxide removal from the nanowire surface, with proper passivation to prevent regrowth, should lead to the reduction or elimination of random telegraph noise, an important obstacle for sensitive experim…
We investigate the influence of modified growth conditions during the spontaneous formation of GaN nanowires on Si(111) in plasma-assisted molecular beam epitaxy. We find that a two-step growth approach, where the substrate temperature is increased during the nucleation stage, is an efficient method to gain control over the area coverage, average diameter, and coalescence degree of GaN nanowire ensembles. Furthermore, we also demonstrate that the growth conditions employed during the incubation time that precedes nanowire nucleation do not influence the properties of the final nanowire ensembl…
The experimental assessment of the strength ($α_R$) of the Rashba spin-orbit coupling is rather indirect and involves the measurement of the spin relaxation length from magnetotransport, together with a model of weak antilocalization. The analysis of the spin relaxation length in nanowires, however, clouds the experimental assessment of the $α_R$ and leads to the prevailing belief that it can be tuned freely with electric field--a central tenant of spintronics. Here, we report direct theory of $α_R$ leading to atomistic calculations of the spin band structure of InAs nanowires upon application…
We report electrical characterization of quantum dots formed by introducing pairs of thin wurtzite (WZ) segments in zinc blende (ZB) InAs nanowires. Regular Coulomb oscillations are observed over a wide gate voltage span, indicating that WZ segments create significant barriers for electron transport. We find a direct correlation of transport properties with quantum dot length and corresponding growth time of the enclosed ZB segment. The correlation is made possible by using a method to extract lengths of nanowire crystal phase segments directly from scanning electron microscopy images, and wit…
N-type doping of GaAs nanowires has proven to be difficult because the amphoteric character of silicon impurities is enhanced by the nanowire growth mechanism and growth conditions. The controllable growth of n-type GaAs nanowires with carrier density as high as 1020 electron/cm3 by self-assisted molecular beam epitaxy using Te donors is demonstrated here. Carrier density and electron mobility of highly doped nanowires are extracted through a combination of transport measurement and Kelvin probe force microscopy analysis in single-wire field-effect devices. Low-temperature photoluminescence is…
We probe the magnetotransport properties of individual InAs nanowires in a field effect transistor geometry. In the low magnetic field regime we observe magnetoresistance that is well described by the weak localization (WL) description in diffusive conductors. The weak localization correction is modified to weak anti-localization (WAL) as the gate voltage is increased. We show that the gate voltage can be used to tune the phase coherence length ($l_ϕ$) and spin-orbit length ($l_{so}$) by a factor of $\sim$ 2. In the high field and low temperature regime we observe the mobility of devices can b…
Effective electron mobilities are obtained by transport measurements on InAs nanowire field-effect transistors at temperatures ranging from 10-200 K. The mobility increases with temperature below ~ 30 - 50 K, and then decreases with temperature above 50 K, consistent with other reports. The magnitude and temperature dependence of the observed mobility can be explained by Coulomb scattering from ionized surface states at typical densities. The behaviour above 50 K is ascribed to the thermally activated increase in the number of scatterers, although nanoscale confinement also plays a role as hig…
We report a method for making epitaxial superconducting contacts to semiconducting nanowires. The temperature and gate characteristics demonstrate barrier-free electrical contact, and the properties in the superconducting state are investigated at low temperature. Half-covering aluminum contacts are realized without the need of lithography and we demonstrate how to controllably insert high-band gap layers in the interface region. These developments are relevant to hybrid superconductor-nanowire devices that support Majorana zero energy states.
We investigate monocrystalline InAs nanowires (NWs) which are grown by molecular beam epitaxy (MBE) and induced by focused ion beam (FIB) implanted Au spots. With this unique combination of methods an increase of the aspect ratio, i.e. the length to width ratio, of the grown NWs up to 300 was achieved. To control the morphology and crystalline structure of the NWs, the growth parameters like temperature, flux ratios and implantation fluence are varied and optimized. Furthermore, the influence of the used molecular arsenic species, in particular the As$_2$ to As$_4$ ratio, is investigated and a…
One-dimensional (1D) sub-bands in cylindrical InAs nanowires (NWs) are electrically mapped as a function of NW diameter in the range of 15-35 nm. At low temperatures, stepwise current increases with the gate voltage are clearly observed and attributed to the electron transport through individual 1D sub-bands. The two-fold degeneracy in certain sub-band energies predicted by simulation due to structural symmetry is experimentally observed for the first time. The experimentally obtained sub-band energies match the simulated results, shedding light on both the energies of the sub-bands as well as…
The pressure dependent phonon modes of predominant wurtzite InAs nanowires has been investigated in a diamond anvil cell under hydrostatic pressure up to 58 GPa. The TO and LO at Gamma point and other optical phonon frequencies increase linearly while the LO TO splitting decreases with pressure. The recorded Raman modes have been used to determine the mode Gruneisen parameters and also the value of Borns transverse effective charge. The calculated Borns transverse effective charge exhibits a linear reduction with increasing pressure implying an increase in covalency of nanowires under compress…
Nanowire (NW)-based opto-electronic devices require certain engineering in the NW geometry to realize polarized-dependent light sources and photodetectors. We present a growth procedure to produce InAs/InP quantum dot-nanowires (QD-NWs) with an elongated top-view cross-section relying on the vapor-liquid-solid method using molecular beam epitaxy. By interrupting the rotation of the sample during the radial growth sequence of the InP shell, hexagonal asymmetric (HA) NWs with long/short cross-section axes were obtained instead of the usual symmetrical shape. Polarization-resolved photoluminescen…