Ferroelectric oxides have attracted much attention due to their wide range of applications, especially in electronic devices such as nonvolatile memories and tunnel junctions. As a result, the monolithic integration of these materials into silicon technology and its nanostructuration to develop alternative cost-effective processes are among the central points in current technology. In this work, we used a chemical route to obtain nanowire thin films of a novel Sr1+δMn8O16 (SMO) hollandite-type manganese oxide on silicon. Scanning transmission electron microscopy combined with crystallographic computing reveals a crystal structure comprising hollandite and pyrolusite units sharing the edges of their MnO6 octahedra, resulting in three types of tunnels arranged along the c axis, where ordering of the Sr atoms produces a natural symmetry breaking. The novel structure gives rise to a ferroelectricity and piezoelectricity, as revealed by local Direct Piezoelectric Force Microscopy measurements, which confirmed the ferroelectric nature of SMO nanowire thin films at room temperature and showed a piezoelectric coefficient d33 value of 22,6 pC/N. Moreover, we proved that flexible vertical SMO nanowires can be harvested and converted into electric output energy through the piezoelectric effect, showing an excellent deformability and high interface recombination. This work indicates the possibility of engineering the integration of 1D manganese oxides on silicon, a step which precedes the production of microelectronic devices.
Ferroelectric hafnia is being explored for next generation electronics due to its robust ferroelectricity in nanoscale samples and its compatibility with silicon. However, its ferroelectricity is not understood. Other ferroelectrics usually lose their ferroelectricity for nanoscopic samples and thin films, and the hafnia ground state is non-polar baddeleyite. Here we study hafnia with density functional theory (DFT) under epitaxial strain, and find that strain not only stabilizes the ferroelectric phases, but also leads to unstable modes and a downhill path in energy from the high temperature …
First principles investigation of ferroelectricity in epitaxially strained Pb$_2$TiO$_4$
本文用密度泛函理论研究了假设的Ruddlesden-Popper化合物Pb $_2$ TiO $_4$的结构和极化。计算了空间群为$I4/mmm$的高对称性K-$_2$-NiF-$_4$-型参考结构的带内声子.在理论基态晶格常数下，存在一个不稳定的红外激活声子。该声子冻结以产生$I2mm$铁电态。作为外延应变的函数，两个额外的铁电相被发现，与空间群$I4mm$和$F2mm$在压缩和拉伸应变，分别。
Epitaxial orthorhombic Hf0.5Zr0.5O2 (HZO) films on La0.67Sr0.33MnO3 (LSMO) electrodes show robust ferroelectricity, with high polarization, endurance and retention. However, no similar results have been achieved using other perovskite electrodes so far. Here, LSMO and other perovskite electrodes are compared. A small amount of orthorhombic phase and low polarization is found in HZO films grown on La-doped BaSnO3 and Nb-doped SrTiO3, while null amounts of orthorhombic phase and polarization are detected in films on LaNiO3 and SrRuO3. The critical effect of the electrode on the stabilized phases…
Zirconia and hafnia based thin films have attracted tremendous attention in the last decade due to their unexpected ferroelectric behavior at the nanoscale, which facilitates the downscaling of ferroelectric devices. The present work reports a novel ferroelectric rhombohedral phase of ZrO2 that can be achieved in thin films grown on (111)- Nb:SrTiO3 substrates by ion-beam sputtering. Structural and ferroelectric characterizations reveal that the (111)-oriented ZrO2 films are under epitaxial compressive strain and display a switchable ferroelectric polarization of about 20.2 μC/cm2 with a coerc…
Room temperature ferroelectricity is observed in lattice-matched ~18% ScAlN/GaN heterostructures grown by molecular beam epitaxy on single-crystal GaN substrates. The epitaxial films have smooth surface morphologies and high crystallinity. Pulsed current-voltage measurements confirm stable and repeatable polarization switching in such ferroelectric/semiconductor structures at several measurement conditions, and in multiple samples. The measured coercive field values are Ec~0.7 MV/cm at room temperature, with remnant polarization Pr~10 μC/cm2 for ~100 nm thick ScAlN layers. These values are sub…
The unconventional Si-compatible ferroelectricity in hafnia-based systems, which becomes robust only at nanoscopic sizes, has attracted a lot of interest. While a metastable polar orthorhombic (o-) phase (Pca21) is widely regarded as the responsible phase for ferroelectricity, a higher energy polar rhombohedral (r-) phase is recently reported on epitaxial HfZrO4 (HZO) films grown on (001) SrTiO3 (R3m or R3), (0001) GaN (R3), and Si (111). Armed with results on these systems, here we report a systematic study leading towards identifying comprehensive global trends for stabilizing r-phase polymo…
Single-phase multiferroic materials that allow the coexistence of ferroelectric and magnetic ordering above room temperature are highly desirable, motivating an ongoing search for mechanisms for unconventional ferroelectricity in magnetic oxides. Here, we report an antisite defect mechanism for room temperature ferroelectricity in epitaxial thin films of yttrium orthoferrite, YFeO3, a perovskite-structured canted antiferromagnet. A combination of piezoresponse force microscopy, atomically resolved elemental mapping with aberration corrected scanning transmission electron microscopy and density…
Hafnia (HfO$_2$)-based thin films have promising applications in nanoscale electronic devices due to their robust ferroelectricity and integration with silicon. However, HfO$_2$ has various stable and metastable polymorphs with quite similar structures and energies. Identifying and stabilizing the ferroelectric functional phases of HfO$_2$ have attracted intensive research interest in recent years. In this work, first-principles calculations on (111)-oriented HfO$_2$ are used to discover that imposing an in-plane shear strain on the tetragonal phase induces a nonpolar to polar phase transition…
Two-dimensional (2D) ferroelectricity has attracted extensive attention since its discovery in the monolayers of van der Waals materials. Here we show that 2D ferroelectricity induced by octahedral rotation distortion is widely present in the perovskite bilayer system through first-principles calculations. The perovskite tolerance factor plays a crucial role in the lattice dynamics and ground-state structure of the perovskite monolayers and bilayers, thus providing an important indicator for screening this hybrid improper ferroelectricity. Generally, the ferroelectric switching via an orthorho…
About ten years after ferroelectricity was first reported in doped HfO2 polycrystalline films, there is tremendous interest in this material and ferroelectric oxides are once again in the spotlight of the memories industry. Great efforts are being made to understand and control ferroelectric properties. Epitaxial films, which have fewer defects and a more controlled microstructure than polycrystalline films, can be very useful for this purpose. Epitaxial films of ferroelectric HfO2 have been much less investigated, but after the first report in 2015 significant progress has been achieved. This…
We investigate the effect of polar Sr-O vacancy pairs on the electric polarization of SrMnO$_3$ (SMO) thin films using density functional theory (DFT) calculations. This is motivated by indications that ferroelectricity in complex oxides can be engineered by epitaxial strain but also \textit{via} the defect chemistry. Our results suggest that intrinsic doping by cation and anion divacancies can induce a local polarization in unstrained non-polar SMO thin films and that a ferroelectric state can be stabilized below the critical strain of the stoichiometric material. This polarity is promoted by…
We report on multiple fundamental qualitative improvements in the growth of improper ferroelectric hexagonal YMnO$_3$ (YMO) thin films and heterostructures by pulsed laser deposition (PLD). By a combination of pre-growth substrate annealing and low-energy-fluence PLD, we obtain a two-dimensional growth mode of the YMO films on yttria-stabilized zirconia (YSZ) with ultralow roughness and devoid of misoriented nanocrystalline inclusions. By inserting a sacrificial manganite layer capped with conducting indium-tin oxide between the substrate and the final film, the latter is grown in a fully latt…
Thickness scaling of ferroelectricity in AlScN is a determining factor for its potential application in neuromorphic computing and memory devices. In this letter, we report on ultrathin (10 nm) Al0.72Sc0.28N films that are ferroelectrically switchable at room temperature. All-epitaxial Al0.72Sc0.28N/Pt heterostructures are grown by magnetron sputtering onto GaN/sapphire substrates followed by an in situ Pt capping approach to avoid oxidation of the Al0.72Sc0.28N film surface. Structural characterization by X-ray diffraction and transmission electron microscopy reveals the established epitaxy. …
Reducing the dimensions of ferroelectric materials down to the nanoscale has strong implications on the ferroelectric polarization pattern and on the ability to switch the polarization. As the size of ferroelectric domains shrinks to nanometer scale, the heterogeneity of the polarization pattern becomes increasingly pronounced, enabling a large variety of possible polar textures in nanocrystalline and nanocomposite materials. Critical to the understanding of fundamental physics of such materials and hence their applications in electronic nanodevices, is the ability to investigate their ferroel…
Unconventional ferroelectricity, robust at reduced nanoscale sizes, exhibited by hafnia-based thin-films presents tremendous opportunities in nanoelectronics. However, the exact nature of polarization switching remains controversial. Here, we investigate epitaxial Hf0.5Zr0.5O2 (HZO) capacitors, interfaced with oxygen conducting metals (La0.67Sr0.33MnO3, LSMO) as electrodes, using atomic resolution electron microscopy while in situ electrical biasing. By direct oxygen imaging, we observe reversible oxygen vacancy migration from the bottom to the top electrode through HZO and reveal associated r…
We investigate ferroelectric- and resistive switching behavior in 18-nm-thick epitaxial BaTiO$_3$ (BTO) films in a model electrolyte-ferroelectric-semiconductor (EFS) configuration. The system is explored for its potential as a ferroelectric microelectrode in bioelectronics. The BTO films are grown by pulsed laser deposition (PLD) on semiconducting Nb-doped (0.5 wt\%) SrTiO$_{3}$ (Nb:STO) single crystal substrates. The ferroelectric properties of the bare BTO films are demonstrated by piezoresponse force microscopy (PFM) measurements. Cyclic voltammetry (CV) measurements in EFS configuration, …
Epitaxy of Fe3O4 on Si(001) by pulsed laser deposition using a TiN/MgO buffer layer
氧化物材料在硅（Si）衬底上的外延对于使用氧化物的各种物理性质如铁电性、铁磁性或超导性的未来功能器件具有极大的兴趣。最近，具有高自旋极化的载流子的材料已经成为自旋电子学中的氧化物-氧化物混合器件的关注点。在这里，我们报告的脉冲激光沉积磁铁矿（Fe 3 O 4）在Si（001）衬底上清洁的原位激光束高温处理。在沉积氮化钛（TiN）和氧化镁（MgO）的双缓冲层之后，可以生长高质量的外延磁铁矿层，如通过RHEED强度振荡和高分辨率X射线衍射所验证的。