Epitaxial thin films of SrRuO3 with large strain disorder were grown using pulsed laser deposition method which showed two distinct transition temperatures in Magnetic measurements. For the first time, we present visual evolution of magnetic domains across the two transitions using Magnetic force microscopy on these films. The study clearly showed that the magnetic anisotropy corresponding to the two transitions is different. It is observed that the perpendicular magnetic anisotropy is dominating in films which results in domain spin orientation preferably in out of plane direction. The Raman studies showed that the lattice is highly influenced by the magnetic order. The analysis of the phonon spectra around magnetic transition reveals the existence of strong spin-phonon coupling and the calculations resulted in spin-phonon coupling strength (λ) values of λ ~ 5 cm-1 and λ ~ 8.5 cm-1, for SrRuO3 films grown on LSAT and SrTiO3 single crystal substrates, respectively.
Density functional calculations are performed to study the effect of epitaxial strain on PbZrO3. We find a remarkably small energy difference between the epitaxially strained polar R3c and nonpolar Pbam structures over the full range of experimentally accessible epitaxial strains -3% < η< 4%. While ferroelectricity is favored for all compressive strains, for tensile strains the small energy difference between the nonpolar ground state and the alternative polar phase yields a robust antiferroelectric ground state. The coexistence of ferroelectricity and antiferroelectricity observed in thin fil…
Using first-principles computations, we study the effect of epitaxial strains on electronic structure variations across ZnSe/ZnTe nano-heterostructures. Epitaxial strains of various types are modeled using pseudomorphic ZnSe/ZnTe heterostructures. We find that a wide range of band gaps (spanning the visible solar spectrum) and band offsets (0-1.5 eV) is accessible across the heterostructures in a controllable manner via reasonable levels of epitaxial strain. In addition to quantum confinement effects, strain in ZnSe/ZnTe heterostructures may thus be viewed as a powerful degree of freedom that …
Combining effective Hamiltonian and direct $ab$ $initio$ computation, we obtain the phase diagram of SnTiO$_{3}$ with respect to epitaxial strain and temperature, demonstrating the complex features of the phase diagram and providing insight into the epitaxially strained SnTiO$_{3}$, a presumably simple perovskite. In the phase diagram, two triple points are found, which may be exploited to to achieve high-performance piezoelectric effects. On the other hand, despite the inclusion of the degree of freedoms related to oxygen octahedron tilting, it is found that ferroelectric displacements domina…
We report on the effect of epitaxial strain on magnetic and optical properties of perovskite LaCrO3 (LCO) single crystal thin films. Epitaxial LCO thin films are grown by pulsed laser deposition on proper choice of substrates to impose different strain states. A combined experimental and theoretical approach is used to demonstrate the direct correlation between lattice-strain and functional properties. The magnetization results show that the lattice anisotropy plays a critical role in controlling the magnetic behavior of LCO films. The strain induced tetragonality in the film lattice strongly …
We report results from two-dimensional Raman spectroscopy studies of large-area epitaxial graphene grown on SiC. Our work reveals unexpectedly large variation in Raman peak position across the sample resulting from inhomogeneity in the strain of the graphene film, which we show to be correlated with physical topography by coupling Raman spectroscopy with atomic force microscopy. We report that essentially strain free graphene is possible even for epitaxial graphene.
Epitaxial strain can be used to modify the properties of ferroelectric thin films. From the experimental viewpoint, the challenge is to fine-tune the magnitude of the strain. We illustrate how, by using a suitable combination of composition and substrate, the magnitude of the epitaxial strain can be controlled in a continuous manner. The phase diagram of PbxSr1-xTiO3 films grown epitaxially on (110)-DyScO3 is calculated using a Devonshire-Landau approach. A boundary between in-plane and out-of-plane oriented ferroelectric phases is predicted to take place at $x \approx$ 0.8. A series of PbxSr1…
A combined experimental and computational investigation of coupling between polarization and epitaxial strain in highly polar ferroelectric PbZr_0.2Ti_0.8O_3 (PZT) thin films is reported. A comparison of the properties of relaxed (tetragonality c/a = 1.05) and highly-strained (c/a = 1.09) epitaxial films shows that polarization, while being amongst the highest reported for PZT or PbTiO_3 in either film or bulk forms (P_r = 82 microC/cm^2), is almost independent of the epitaxial strain. We attribute this behavior to a suppressed sensitivity of the A-site cations to epitaxial strain in these Pb-…
X-ray analysis of ferroelectric thin layers of Ba1/2Sr1/2TiO3 with different thickness reveals the presence of internal strain gradients across the film thickness and allows us to propose a functional form for the internal strain profile. We use this to calculate the direct influence of strain gradient, through flexoelectric coupling, on the degradation of the ferroelectric properties of thin films with decreasing thickness, in excellent agreement with the observed behaviour. This work highlights the link between strain relaxation and strain gradients in epitaxial films, and shows the pressing…
Temperature dependent structural phase transitions of SrRuO3 thin films epitaxially grown on SrTiO3(001) single crystal substrates have been studied using high-resolution x-ray diffraction. In contrast to bulk SrRuO3, coherently strained epitaxial layers do not display cubic symmetry up to ~730 oC and remain tetragonal. Such behavior is believed to be induced by compressive strain between the SrRuO3 layer and SrTiO3 substrate due to lattice mismatch. The tetragonal symmetry during growth explains the single domain growth on miscut SrTiO3 substrates with step edges running along the [100] or [0…
Strain engineering has attracted great attention, particularly for epitaxial films grown on a different substrate. Residual strains of SiC have been widely employed to form ultra-high frequency and high Q factor resonators. However, to date the highest residual strain of SiC was reported to be limited to approximately 0.6%. Large strains induced into SiC could lead to several interesting physical phenomena, as well as significant improvement of resonant frequencies. We report an unprecedented nano strain-amplifier structure with an ultra-high residual strain up to 8% utilizing the natural resi…
The phase transition behaviour of PbTiO3 and BaTiO3 under (111) epitaxial strain is investigated using density-functional theory calculations. From tensile strains of +0.015 to compressive strains of -0.015, PbTiO3 undergoes phase transitions from C2 through two Cm phases and then to R3m. The total polarisation is found to be almost independent of strain. For the same range of strains BaTiO3 undergoes phase transitions from a single Cm phase, through R3m and then to R-3m. In this case the application of compressive strain inhibits and then completely suppresses the polarisation on transition t…
We investigate energetically favorable structures of ABO$_2$N oxynitrides as functions of pressure and strain via swarm-intelligence-based structure prediction methods, DFT lattice dynamics and first-principles molecular dynamics. We predict several thermodynamically stable polar oxynitride perovskites under high pressures. In addition, we find that ferroelectric polar phases of perovskite-structured oxynitrides can be thermodynamically stable and synthesized at high pressure on appropriate substrates. The dynamical stability of the ferroelectric oxynitrides under epitaxial strain at ambient p…
Biaxial strain in coherent epitaxial thin films can have a pronounced effect on the point defect profile in the film material. Detailed fundamental knowledge of the interaction of strain with point defects is crucial in understanding the stoichiometry and resulting properties of strained thin films. Here we investigate the effect of biaxial strain on the formation energy of cation and anion vacancies using MnO as a model system. Our density functional theory calculations show that, as expected from local volume arguments, compressive strain favours the formation of cation vacancies. Interestin…
The structure and polarization of the as-yet hypothetical Ruddlesden-Popper compound Pb$_2$TiO$_4$ are investigated within density-functional theory. Zone enter phonons of the high-symmetry K$_2$NiF$_4$-type reference structure, space group $I4/mmm$, were calculated. At the theoretical ground-state lattice constants, there is one unstable infrared-active phonon. This phonon freezes in to give the $I2mm$ ferroelectric state. As a function of epitaxial strain, two additional ferroelectric phases are found, with space groups $I4mm$ and $F2mm$ at compressive and tensile strains, respectively.
We investigate the variation of the spontaneous ferroelectric polarization with epitaxial strain for BaTiO$_3$, PbTiO$_3$, LiNbO$_3$, and BiFeO$_3$ using first principles calculations. We find that while the strain dependence of the polarization is very strong in the simple perovskite systems BaTiO$_3$ and PbTiO$_3$ it is only weak in LiNbO$_3$ and BiFeO$_3$. We show that this different behavior can be understood purely in terms of the piezoelectric and elastic constants of the unstrained bulk material, and we discuss several factors that determine the strain behavior of a certain material.
The effect of epitaxial strain on the cation distribution in spinel ferrites CoFe2O4 and NiFe2O4 is investigated by GGA+U total energy calculations. We obtain a very strong (moderate) tendency for cation inversion in NiFe2O4 (CoFe2O4), in agreement with experimental bulk studies. This preference for the inverse spinel structure is reduced by tensile epitaxial strain, which can lead to strong sensitivity of the cation distribution on specific growth conditions in thin films. Furthermore, we obtain significant energy differences between different cation arrangements with the same degree of inver…
The theory of epitaxial strain energy is extended beyond the harmonic approximation to account for large film/substrate lattice mismatch. We find that for fcc noble metals (i) directions <001> and <111> soften under tensile biaxial strain (unlike zincblende semiconductors) while (ii) <110> and <201> soften under compressive biaxial strain. Consequently, (iii) upon sufficient compression <201> becomes the softest direction (lowest elastic energy), but (iv) <110> is the hardest direction for large tensile strain. (v) The dramatic softening of <001> in fcc noble metals upon biaxial tensile strain…
Epitaxial strain has been shown to drive structural phase transitions along with novel functionalities in perovskite-based thin-films. Aliovalent doping at the A-site can drive an insulator-to-metal and magnetic transitions in perovskites along with a variety of interesting structural and electronic phenomena. Using first-principles calculations, we demonstrate here, how coupling epitaxial strain with A-site hole doping in a multiferroic double perovskite, Bi2FeCrO6, could lead to mitigation of issues related to anti-site defects and lowered magnetisation in thin-films of the material. We also…
Epitaxial strain in 4d ferromagnet SrRuO3 films is directly linked to the physical properties through the strong coupling between lattices, electrons, and spins. It provides an excellent opportunity to tune the functionalities of SrRuO3 in electronic and spintronic devices. However, a thorough understanding of the epitaxial strain effect in SrRuO3 has remained elusive due to the lack of systematic studies. This study demonstrates wide-range epitaxial strain control of electrical and magnetic properties in high-quality SrRuO3 films. The epitaxial strain was imposed by cubic or pseudocubic perov…
A current challenge in the field of magnetoelectric multiferroics is to identify systems that allow a controlled tuning of states displaying distinct magnetoelectric responses. Here we show that the multiferroic ground state of the archetypal multiferroic TbMnO3 is dramatically modified by epitaxial strain. Neutron diffraction reveals that in highly strained films the magnetic order changes from the bulk-like incommensurate bc-cycloidal structure to commensurate magnetic order. Concomitant with the modification of the magnetic ground state, optical second-harmonic generation (SHG) and electric…
First-principles calculations of the epitaxial-strain phase diagram of perovskite SrCoO$_{3}$ are presented. Through combination of the large spin-phonon coupling with polarization-strain coupling and coupling of the band gap to the polar distortion, both tensile and compressive epitaxial strain are seen to drive the bulk ferromagnetic-metallic (FM-M) phase to antiferromagnetic-insulating-ferroelectric (AFM-I-FE) phases, the latter having unusually low elastic energy. At these coupled magnetic-ferroelectric metal-insulator phase boundaries, cross responses to applied electric and magnetic fiel…
This work explores the impact of in-plane bi-axial (epitaxial) strain on the cation distribution and electric polarization of the Aurivillius-phase compound Bi$_5$FeTi$_3$O$_{15}$ using first-principles electronic structure calculations. Our calculations indicate that the site preference of the Fe$^{3+}$ cation can be controlled via epitaxial strain. Tensile strain enhances the preference for the inner sites within the perovskite-like layers of the Aurivillius-phase structure, whereas compressive strain favors occupation of the outer sites within the perovskite-layers, i.e., the sites close to…
The phenomenon of ferromagnetic resonance (FMR) provides fundamental information on the physics of magnetic materials and lies at the heart of a variety of signal processing microwave devices. Here we demonstrate theoretically that substrate-induced lattice strains may change the FMR frequency of an epitaxial ferromagnetic film dramatically, leading to ultralow and ultrahigh resonance frequencies at room temperature. Remarkably, the FMR frequency varies with the epitaxial strain nonmonotonically, reaching minimum at a critical strain corresponding to the strain-induced spin reorientation trans…
The interaction of graphene with metallic substrates reveals phenomena and properties of great relevance for applications in nanotechnology. In this review, the vibrational characterization by means of various inelastic scattering spectroscopies are surveyed for graphene epitaxially grown on metals and transition carbides. In particular, the manifestations of electron-phonon interaction, such as Kohn anomalies, the evaluation of elastic properties and the nanoscale control of phonon modes are presented and discussed.
We have investigated the effect of epitaxial strain on the magnetic properties and $B$-site cation ordering in multiferroic Bi$_2$FeCrO$_6$ (001) thin films using a density-functional theory approach. We find that in thin films with rock-salt ordering of Fe and Cr the ground state is characterised by C-type anti-ferromagnetic (AFM) order. This is in contrast to the bulk form of the material which was predicted to be a ferrimagnet with G-type AFM order. Furthermore, the cation ordered thin-films undergo a transition with epitaxial strain from C to A-type AFM order. Other magnetic orders appear …
We present the temperature- and thickness-dependent structural and morphological evolution of strain induced transformations in highly-strained epitaxial BiFeO3 films deposited on LaAlO3 (001) substrates. Using high-resolution X-ray diffraction and temperature-dependent scanning-probe-based studies we observe a complex temperature- and thickness-dependent evolution of phases in this system. A thickness-dependent transformation from a single monoclinically distorted tetragonal-like phase to a complex mixed-phase structure in films with thicknesses up to ~200 nm is the consequence of a strain-in…
Using an extension of a first-principles method developed by King-Smith and Vanderbilt [Phys. Rev. B {\bf 49}, 5828 (1994)], we investigate the effects of in-plane epitaxial strain on the ground-state structure and polarization of eight perovskite oxides: BaTiO$_3$, SrTiO$_3$, CaTiO$_3$, KNbO$_3$, NaNbO$_3$, PbTiO$_3$, PbZrO$_3$, and BaZrO$_3$. In addition, we investigate the effects of a nonzero normal stress. The results are shown to be useful in predicting the structure and polarization of perovskite oxide thin films and superlattices.
High-index Bi2Se3(221) film has been grown on In2Se3-buffered GaAs(001), in which a much retarded strain relaxation dynamics is recorded. The slow strain-relaxation process of in epitaxial Bi2Se3(221) can be attributed to the layered structure of Bi2Se3 crystal, where the epifilm grown along [221] is like a pile of weakly-coupled quintuple layer slabs stacked side-by-side on substrate. Finally, we have revealed the strong chemical bonding at the interface of Bi2Se3 and In2Se3 by plotting differential charge contour calculated by first-principle method. This study points to the feasibility of a…
We showed that a wetting layer in epitaxially strained thin films which decreases with increasing lattice mismatch strain arises due to the variation of nonlinear elastic free energy with film thickness. We calculated how and at what thickness a flat film becomes unstable to perturbations of varying size for films with both isotropic and anisotropic surface tension. We showed that anisotropic surface tension gives rise to a metastable enlarged wetting layer. The perturbation amplitude needed to destabilize this wetting layer decreases with increasing lattice mismatch. We also studied the early…
Effect of biaxial tensile strains on optical functions and band edge transitions of ultra thin epitaxial films was studied using as an example a 13 nm thick SrTiO3 films deposited on KTaO3(100) single-crystal substrates. Optical functions were determined by spectroscopic ellipsometry technique. It was found that tensile strains result in a shift of the low energy band gap optical transitions to higher energies and decrease the refractive index in the visible region. Comparison of the optical spectra for strained SrTiO3 films and for homoepitaxial strain-free SrTiO3:Cr (0.01 %at.) films deposit…
We demonstrate strain-tuning of magnetocrystalline anisotropy over a range of more than one thousand Gauss in epitaxial Y3Fe5O12 films of excellent crystalline quality grown on lattice-mismatched Y3Al5O12 substrates. Ferromagnetic resonance (FMR) measurements reveal a linear dependence of both out-of-plane and in-plane uniaxial anisotropy on the strain-induced tetragonal distortion of Y3Fe5O12. Importantly, we find the spin mixing conductance G_r determined from inverse spin Hall effect and FMR linewidth broadening remains large: G_r = 3.33 x 10^14 Ohm^-1m^-2 in Pt/Y3Fe5O12/Y3Al5O12 heterostru…
Ferroelectric hafnia is being explored for next generation electronics due to its robust ferroelectricity in nanoscale samples and its compatibility with silicon. However, its ferroelectricity is not understood. Other ferroelectrics usually lose their ferroelectricity for nanoscopic samples and thin films, and the hafnia ground state is non-polar baddeleyite. Here we study hafnia with density functional theory (DFT) under epitaxial strain, and find that strain not only stabilizes the ferroelectric phases, but also leads to unstable modes and a downhill path in energy from the high temperature …
Quantum materials, particularly Dirac materials with linearly dispersing bands, can be effectively tuned by strain-induced lattice distortions leading to a pseudo-magnetic field that strongly modulates their electronic properties. Here, we grow kagome magnet FeSn films, consisting of alternatingly stacked Sn$_2$ honeycomb (stanene) and Fe$_3$Sn kagome layers, on SrTiO$_3$(111) substrates by molecular beam epitaxy. Using scanning tunneling microscopy/spectroscopy, we show that the Sn honeycomb layer can be periodically deformed by epitaxial strain for film thickness below 10 nm, resulting in di…
The strain dependence of electric and magnetic properties has been widely investigated, both from a fundamental science perspective and an applications point of view. Electromechanical coupling through field-induced polarization rotation (PRO) and polarization reorientation (PRE) in piezoelectric single crystals can provide an effective strain in film/substrate epitaxial heterostructures. However, the specific pathway of PRO and PRE is a complex thermodynamic process, depending on chemical composition, temperature, electric field and mechanical load. Here, systematic studies of the temperature…
BiFeO3 thin films with various thicknesses were grown epitaxially on (001) LaSrAlO4 single crystal substrates using pulsed laser deposition. High resolution x-ray diffraction measurements revealed that a tetragonal-like phase with c-lattice constant ~4.65 Å is stabilized by a large misfit strain. Besides, a rhombohedral-like phase with c-lattice constant ~3.99 Å was also detected at film thickness of ~50 nm and above to relieve large misfit strains. In-plane piezoelectric force microscopy studies showed clear signals and self-assembled nanoscale stripe domain structure for the tetragonal-like …
The photovoltaic effect in the BiFeO3/TiO2 heterostructures can be tuned by epitaxial strain and an electric field in the visible-light region which is manifested by the enhancement of absorption activity in the heterojunction under tensile strain and an electric field based on the first-principles calculations. It is suggested that there are coupling between photon, spin carrier, charge, orbital, and lattice in the interface of the bilayer film which makes the heterojunction an intriguing candidate towards fabricating the multifunctional photoelectric devices based on spintronics. The microsc…
We revisit the phase diagram of BaTiO$_3$ under biaxial strain using a first principles-based effective Hamiltonian approach. We show that, in addition to the tetragonal ($c$), quasi-rhombohedral ($r$), and quasi-orthorhombic ($aa$) ferroelectric phases, that have been discussed previously, there are temperature and strain regions, in particular under tensile strain, where the system decomposes into multi-domain structures. In such cases, the strained system, at least on a local level, recovers the same phase sequence as the unclamped bulk material. Furthermore, we extend these results from th…
We investigate the effect of epitaxial strain on the electrocaloric effect (ECE) in BaTiO$_3$ by means of ab initio based molecular dynamics simulations. We show that tensile strain can be used to optimize the operation range for ferroic cooling. Strain in the range of $\leq 1$ % can be used to shift the operation temperature by several hundreds of Kelvin both to higher and lower temperatures, depending on the direction of the external field. In addition, the transformation between multi-domain and mono-domain states, induced by an in-plane electric field, results in an additional peak of the …
We investigated the crystal and electronic structures of ferroelectric Bi4Ti3O12 (BiT) single crystalline thin films site-specifically substituted with LaCoO3 (LCO). The epitaxial films were grown by pulsed laser epitaxy on NdGaO3 and SrTiO3 substrates to vary the degree of strain. With increasing the LCO substitution, we observed a systematic increase in the c-axis lattice constant of the Aurivillius phase related with the modification of pseudo-orthorhombic unit cells. These compositional and structural changes resulted in a systematic decrease in the band gap, i.e., the optical transition e…
Perovskite oxynitrides are a promising class of material for photocatalytic water-splitting due to their small band gaps and suitably aligned band edges. Recently, epitaxially strained oxynitrides started to attract interest due to the possibility to engineer the anion order and ferroelectric distortions. However, contrary to oxides there have been no studies on the band-gap evolution in oxynitrides with epitaxial strain. Here, we investigate, using density functional theory calculations, the influence of epitaxial strain on the band gap of two different oxynitrides and compare our results wit…
We study the modification of the electronic structure in the strong spin-orbit coupled Sr$_2$IrO$_4$ by epitaxial strain using density functional methods. Structural optimization shows that strain changes the internal structural parameters such as the Ir-O-Ir bond angle, which has an important effect on the band structure. An interesting prediction is the $Γ- $X crossover of the valence band maximum with strain, while the conduction minimum at M remains unchanged. This in turn suggests strong strain dependence of the transport properties for the hole doped system, but not when the system is el…
Using first-principles density functional theory calculations, we discover an anomalously large bi-axial strain-induced octahedral rotation axis reorientation in orthorhombic perovskites with tendency towards rhombohedral symmetry. The transition between crystallographically equivalent (isosymmetric) structures with different octahedral rotation magnitudes originates from strong strain--octahedral rotation coupling available to perovskites and the energetic hierarchy among competing octahedral tilt patterns. By elucidating these criteria, we suggest many functional perovskites would exhibit th…
The inverse spinels CoFe2O4 and NiFe2O4, which have been of particular interest over the past few years as building blocks of artificial multiferroic heterostructures and as possible spin-filter materials, are investigated by means of density functional theory calculations. We address the effect of epitaxial strain on the magneto-crystalline anisotropy and show that, in agreement with experimental observations, tensile strain favors perpendicular anisotropy, whereas compressive strain favors in-plane orientation of the magnetization. Our calculated magnetostriction constants $λ_{100}$ of about…
Disentangling Strain and Ti3+ Contributions to the Anomalous Hall Effect in Epitaxial RuO2 Films
University of Minnesota−Twin Cities（明尼苏达大学双城分校）；Hankuk University of Foreign Studies（韩国外国语大学）；Kyung Hee University（庆熙大学）；Temple University（天普大学）；Diamond Light Source Ltd.（钻石光源有限公司）；Pacific Northwest National Laboratory（太平洋西北国家实验室）
We report on a strain-induced martensitic transformation, accompanied by a suppression of magnetic order in epitaxial films of chemically disordered FeRh. X-ray diffraction, transmission electron microscopy and electronic structure calculations reveal that the lowering of symmetry (from cubic to tetragonal) imposed by the epitaxial relation leads to a further, unexpected, tetragonal-to-orthorhombic transition, triggered by a band-Jahn-Teller-type lattice instability. The collapse of magnetic order is a direct consequence of this structural change, which upsets the subtle balance between ferrom…
Large area MoS2 and WS2 van der Waals epitaxial thin films with complete control over number of layers including monolayer is grown by pulsed laser deposition utilizing slower growth kinetics. The films grown on c-plane sapphire show stiffening of A1g and E12g phonon modes with decreasing number of layers for both MoS2 and WS2. The observed stiffening translate into the compressive strain of 0.52 % & 0.53 % with accompanying increase in fundamental direct band gap to 1.74 and 1.68 eV for monolayer MoS2 and WS2, respectively. The strain decays with the number of layers. HRTEM imaging directly r…
Stanene, the two-dimensional monolayer form of tin, has been predicted to be a 2D topological insulator due to its large spin--orbit interaction. However, a clear experimental demonstration of stanene's topologically nontrivial properties has eluded observation, in part because of the difficulty of choosing a substrate on which stanene will remain topologically nontrivial. In this paper, we present first-principles density functional theory (DFT) calculations of epitaxial monolayer stanene grown on the (0001) surface of alumina, Al$_{2}$O$_{3}$, as well as free-standing decorated stanene under…
The origin of the large-scale stripe pattern of epitaxial silicene on the ZrB$_2$(0001) surface observed by scanning tunneling microscope experiments is revealed by first-principles calculations. Without stripes, the ($\sqrt{3}\times\sqrt{3}$)-reconstructed, one-atom-thick Si layer is found to exhibit a "zero-frequency" phonon instability at the $M$ point. In order to avoid a divergent response, the relevant phonon mode triggers the spontaneous formation of a new phase with a particular stripe pattern offering a way to lower both the atomic surface density and the total energy of silicene on t…
Morphological properties of strained epitaxial films are examined through a mesoscopic approach developed to incorporate both the film crystalline structure and standard continuum theory. Film surface profiles and properties, such as surface energy, liquid-solid miscibility gap and interface thickness, are determined as a function of misfit strains and film elastic modulus. We analyze the stress-driven instability of film surface morphology that leads to the formation of strained islands. We find a universal scaling relationship between the island size and misfit strain which shows a crossover…
Strain and strain adaption mechanisms in modern functional materials are of crucial importance for their performance. Understanding these mechanisms will advance innovative approaches for material properties engineering. Here we study the strain adaption mechanism in a thin film model system as function of epitaxial strain. Chemically disordered FeRh thin films are deposited on W-V buffer layers, which allow for large variation of the preset lattice constants, e.g. epitaxial boundary condition. It is shown by means of high resolution X-ray reciprocal space maps and transmission electron micros…
In the perovskite oxide SrCrO$_{3}$ the interplay between crystal structure, strain and orbital ordering enables a transition from a metallic to an insulating electronic structure under certain conditions. We identified a narrow window of oxygen partial pressure in which highly strained SrCrO$_{3}$ thin films can be grown using radio-frequency (RF) off-axis magnetron sputtering on three different substrates, (LaAlO$_{3}$)$_{0.3}$-(Sr$_{2}$TaAlO$_{6}$)$_{0.7}$ (LSAT), SrTiO$_{3}$ (STO) and DyScO$_{3}$ (DSO). X-ray diffraction and atomic force microscopy confirmed the quality of the films and a …
The tetragonal states produced by isotropic pseudomorphic epitaxial strain in the (001) plane on a tetragonal phase of a crystal are calculated for V, Ti, Rb, Li, K, Sr from first-principles electronic theory. It is shown that each metal has two tetragonal phases corresponding to minima of the total energy with respect to tetragonal deformations, hence are equilibrium phases, and that the equilibrium phases are separated by a region of inherent instability. The equilibrium phase for any strained tetragonal state can thus be uniquely identified. Lattice constants and relative energies of the tw…
The metal insulator transition (MIT) in VO2 has been an important topic for recent years. It has been generally agreed that the mechanism of the MIT in bulk VO2 is considered to be a collaborative Mott-Peierls transition, however the effect of the strain on the phase transition is much more complicated. In this study the effect of the large strain on the properties of VO2 films was investigated. One remarkable result is that highly strained epitaxial VO2 thin films were rutile in the insulating state as well as in the metallic state. These highly strained VO2 films underwent an electronic phas…
Recently a metallic state was discovered at the interface between insulating oxides, most notably LaAlO3 and SrTiO3. Properties of this two-dimensional electron gas (2DEG) have attracted significant interest due to its potential applications in nanoelectronics. Control over this carrier density and mobility of the 2DEG is essential for applications of these novel systems, and may be achieved by epitaxial strain. However, despite the rich nature of strain effects on oxide materials properties, such as ferroelectricity, magnetism, and superconductivity, the relationship between the strain and el…
The structure and microstrucutre of fully-strained BiCrO3 thin films have been investigated by X-rays diffraction and transmission electron microscopy, at room temperature. Interestingly, three structural variants are simultaneously stabilized within the film. While txo of them are consistent with the existing phases in the bulk-below and above the 420 K structural transition, a different phase is identified. The existence of various structures has been attributed to the inhomogeneous distribution of local strains and oxygens resulting from a minimization of the strain-energy at the interface.…
We report a strong thickness dependence of the complex frequency-dependent optical dielectric function in epitaxial CaMnO3(001) thin films on SrTiO3(001), LaAlO3(001), and SrLaAlO4(001) substrates. A doubling of the peak value of the imaginary part of the dielectric function and spectral shifts of 0.5 eV for a given magnitude of absorption are observed. On the basis of the experimental data and first-principles density functional theory calculations of the dielectric function, its evolution with thickness from 4 to 63 nm has several regimes. In the thinnest, strain-coherent films, the response…
Ferroelectric BaTiO3 films with large polarization have been integrated with Si(001) by pulsed laser deposition. High quality c-oriented epitaxial films are obtained in a substrate temperature range of about 300 deg C wide. The deposition temperature critically affects the growth kinetics and thermodynamics balance, resulting on a high impact in the strain of the BaTiO3 polar axis, which can exceed 2% in films thicker than 100 nm. The ferroelectric polarization scales with the strain and therefore deposition temperature can be used as an efficient tool to tailor ferroelectric polarization. The…
We show that the magnetic anisotropy in spinel-structure CoCr$_2$O$_4$ thin films exhibits a strain dependence in which compressive strain induces an out-of-plane magnetic easy axis and tensile strain an in-plane easy axis, exactly opposite to the behavior reported for the related compound CoFe$_2$O$_4$. We use density functional theory calculations within the LSDA+U approximation to reproduce and explain the observed behavior. Using second-order perturbation theory, we analyse the anisotropy tensor of the Co$^{2+}$ ions in both octahedral and tetrahedral coordination, allowing us to extend ou…
In this work we are investigating the effect of strain in ultrathin Mn-Ga thin films on the magnetic properties at room temperature. Two different Mn-Ga compositions of which one is furthermore doped with Co were grown on Cr buffered MgO (001) substrates. Films with a thickness below 12nm are highly strained and it was observed that the ratio c/a vs. thickness is depending on composition. Using c/a as an order parameter the PMA is shown to be drastically reduced with increasing strain. These findings should be considered when generalizing and downscaling results obtained from films >20nm. Furt…