We report on luminescent centers contained in a few-layer-thick hexagonal boron nitride (h-BN) film grown on Ni by molecular beam epitaxy. After transfer to a SiO$_2$/Si substrate, sharp lines are observed in photo- and cathodoluminescence spectra in both the ultraviolet and the visible range. Spatially resolved measurements reveal that the luminescent centers responsible for these lines are localized within microscopic multi-layer islands that form at the nucleation centers of the h-BN film. The comparison of their energy, polarization and phonon replica emission with previous theoretical predictions suggest that the N$_\mathrm{B}$V$_\mathrm{N}$ anti-site could be one of the light emitters present in our sample. Moreover, we have also observed evidences of other kinds of centers that could be associated to defects containing carbon or oxygen. The characterized luminescent defects could have potential applications as quantum light sources.
We report on silicon delta doping of metalorganic vapor-phase epitaxy-grown \b{eta}-Ga2O3 thin films using silane precursor. Delta-doped \b{eta}-Ga2O3 epitaxial films are characterized using capacitance-voltage profiling and secondary-ion mass spectroscopy. Electron sheet charge density in the range of 2.9e12 cm-2 to 8e12 cm-2 with a half width at half maximum ranging from 6.2 nm to 3.5 nm is measured. We also demonstrate a high density (6.4e12 cm-2) degenerate two-dimensional electron gas using a delta-doped \b{eta}-(Al0.26Ga0.74)2O3/\b{eta}-Ga2O3 heterostructure.The total charge could also i…
N-type doping of GaAs nanowires has proven to be difficult because the amphoteric character of silicon impurities is enhanced by the nanowire growth mechanism and growth conditions. The controllable growth of n-type GaAs nanowires with carrier density as high as 1020 electron/cm3 by self-assisted molecular beam epitaxy using Te donors is demonstrated here. Carrier density and electron mobility of highly doped nanowires are extracted through a combination of transport measurement and Kelvin probe force microscopy analysis in single-wire field-effect devices. Low-temperature photoluminescence is…
Pursuing the confinement of linearly dispersive relativistic fermions is of interest in both fundamental physics and potential applications. Here, we report strong STM evidence for the equally spaced, strikingly sharp, and densely distributed quantum well states (QWSs) near Fermi energy in Pb(111) nanoislands, van-der-Waals epitaxially grown on graphitized 6H-SiC(0001). The observations can be explained as the quantized energies of confined linearly dispersive [111] electrons, which essentially 'simulate' the out-of-plane relativistic quasiparticles. The equally spaced QWSs with an origin of c…
Electron-mediated ferromagnetism and small spin-orbit interaction in a molecular-beam-epitaxy grown n-type $GaAs/Al_{0.3}Ga_{0.7}As$ heterostructure with Mn $δ$-doping
We report on the systematic investigation of the optical properties of a selectively grown quantum dot gain material assisted by block-copolymer lithography for potential applications in active optical devices operating in the wavelength range around 1.55 um and above. We investigated a new type of diblock copolymer PS-b-PDMS (polystyrene-block-polydimethylsiloxane) for the fabrication of silicon oxycarbide hard mask for selective area epitaxy of InAs/InP quantum dots. An array of InAs/InP quantum dots was selectively grown via droplet epitaxy. Our detailed investigation of the quantum dot car…
Nearly localized moire flat bands in momentum space, arising at particular twist angles, are the key to achieve correlated effects in transition-metal dichalcogenides. Here, we use angle-resolved photoemission spectroscopy (ARPES) to visualize the presence of a flat band near the Fermi level of van der Waals (vdW) WSe2/MoSe2 heterobilayer grown by molecular beam epitaxy. This flat band is localized near the K point of the Brillouin zone and has a width of several hundred meVs. By combining ARPES measurements with density functional theory (DFT) calculations, we confirm the coexistence of diffe…
Molecular beam epitaxy is used to fabricate magnetic single and double layer junctions which are deposited in prefabricated nanostencil masks. For all Co | Cu | Co double layer junctions we observe a stable intermediate resistance state which can be reached by current starting from the parallel configuration of the respective ferromagnetic layers. The generation of spin waves is investigated at room temperature in the frequency domain by spectrum analysis, demonstrating both in-plane and out-of-plane precessions of the magnetization of the free magnetic layer. Current-induced magnetization dyn…
Two-dimensional materials (2D) arranged in hybrid van der Waals (vdW) heterostructures provide a route toward the assembly of 2D and conventional III-V semiconductors. Here, we report the structural and electronic properties of single layer WSe2 grown by molecular beam epitaxy on Se-terminated GaAs(111)B. Reflection high-energy electron diffraction images exhibit sharp streaky features indicative of a high-quality WSe2 layer produced via vdW epitaxy. This is confirmed by in-plane x-ray diffraction. The single layer of WSe2 and the absence of interdiffusion at the interface are confirmed by hig…
A novel technique to make Ohmic contact to a buried two-dimensional electron gas in a molecular-beam-epitaxy grown $GaAs/Al_{0.3}Ga_{0.7}As$ heterostructure with Mn $δ$-doping
We report a method for growing rectangular InAs nanofins with deterministic length, width and height by dielectric-templated selective-area epitaxy. These freestanding nanofins can be transferred to lay flat on a separate substrate for device fabrication. A key goal was to regain a spatial dimension for device design compared to nanowires, whilst retaining the benefits of bottom-up epitaxial growth. The transferred nanofins were made into devices featuring multiple contacts for Hall effect and four-terminal resistance studies, as well as a global back-gate and nanoscale local top-gates for den…
We report on an experimental study of the effect of coherent surface-bulk electron scattering on quantum transport in a three-dimensional topological insulator Bi$_2$Te$_3$ nanoplate. The nanoplate is grown via van der Waals epitaxy on a mica substrate and a top-gated Hall-bar device is fabricated from the nanoplate directly on the growth substrate. Top-gate voltage dependent measurements of the sheet resistance of the device reveal that the transport carriers in the nanoplate are of n-type and that, with decreasing top gate voltage, the carrier density in the nanoplate is decreased. However, …
We report on the selective-area chemical beam epitaxial growth of InAs in-plane, one-dimensional (1-D) channels using patterned SiO$_{2}$-coated InP(001), InP(111)B, and InP(110) substrates to establish a scalable platform for topological superconductor networks. Top-view scanning electron micrographs show excellent surface selectivity and dependence of major facet planes on the substrate orientations and ridge directions, and the ratios of the surface energies of the major facet planes were estimated. Detailed structural properties and defects in the InAs nanowires (NWs) were characterized by…
Topological insulators (TIs) are a promising class of materials for manipulating the magnetization of an adjacent ferromagnet (FM) through the spin-orbit torque (SOT) mechanism. However, current studies combining TIs with conventional FMs present large device-to-device variations, resulting in a broad distribution of SOT magnitudes. It has been identified that the interfacial quality between the TI and the FM is of utmost importance in determining the nature and efficiency of the SOT. To optimize the SOT magnitude and enable ultra-low-power magnetization switching, an atomically smooth interfa…
Several of the key issues of planar (Al,Ga)N-based deep-ultraviolet light emitting diodes could potentially be overcome by utilizing nanowire heterostructures, exhibiting high structural perfection and improved light extraction. Here, we study the spontaneous emission of GaN/(Al,Ga)N nanowire ensembles grown on Si(111) by plasma-assisted molecular beam epitaxy. The nanowires contain single GaN quantum disks embedded in long (Al,Ga)N nanowire segments essential for efficient light extraction. These quantum disks are found to exhibit intense emission at unexpectedly high energies, namely, signif…