Atomically flat thin films of topological insulator Bi2Se3 have been grown on double-layer graphene formed on 6H-SiC(0001) substrate by molecular beam epitaxy. By a combined study of reflection high energy electron diffraction and scanning tunneling microscopy, we identified the Se-rich condition and temperature criterion for layer-by-layer growth of epitaxial Bi2Se3 films. The as-grown films without doping exhibit a low defect density of 1.0\pm 0.2x1011/cm2, and become a bulk insulator at a thickness of 10 quintuple layers, as revealed by in situ angle resolved photoemission spectroscopy measurement.
GaMnAs/GaAs films were grown via molecular beam epitaxy using both low and high substrate temperatures. The films were investigated using Hall effect and photoluminescence (PL) measurements from 8 to 300 K. The carrier concentrations in the samples grown at a low substrate temperature are greater than those in the samples grown at a high substrate temperature. The PL spectra show a GaAs exciton peak, a peak involving a carbon acceptor, a substitutional Mn acceptor-related peak and an optical phonon-related peak.
In this report, we demonstrate high spectral responsivity (SR) in MBE grown epitaxial \b{eta}-Ga2O3-based solar blind MSM photodetectors (PD). (-2 0 1)-oriented \b{eta}-Ga2O3 thin film was grown by plasma-assisted MBE on c-plane sapphire substrates. MSM devices fabricated with Ni/Au contacts in an interdigitated geometry were found to exhibit peak SR > 1.5 A/W at 236-240 nm at a bias of 4 V with a UV to visible rejection ratio > 105. The devices exhibited very low dark current < 10 nA at 20 V and showed no persistent photoconductivity (PPC) as evident from the sharp transients with a photo-to-…
We report the first evidence of electron-mediated ferromagnetism in a molecular-beam-epitaxy (MBE) grown $GaAs/Al_{0.3}Ga_{0.7}As$ heterostructure with Mn $δ$-doping. The interaction between the magnetic dopants (Mn) and the Two-Dimensional Electron Gas (2DEG) realizes magnetic ordering when the temperature is below the Curie temperature ($T_{C} \sim 1.7K$) and the 2DEG is brought in close proximity to the Mn layer by gating. The Anomalous Hall Effect (AHE) contribution to the total Hall resistance is shown to be about three to four orders of magnitude smaller than in the case of hole-mediated…
Mn doped GaAs thin films were grown using molecular beam epitaxy at high and low substrate temperatures. The elemental concentration depth profiles in the thin films were determined by using Auger electron spectroscopy combined with ion etching. The Mn concentration is higher near the surface and then decreases with depth for films grown at high substrate temperatures. The Mn concentration profile is much more uniform when films are grown using a low substrate temperature. What was unexpectedly found are high levels of oxygen in the low substrate temperature grown thin films.
Molecular beam epitaxy is used to fabricate magnetic single and double layer junctions which are deposited in prefabricated nanostencil masks. For all Co | Cu | Co double layer junctions we observe a stable intermediate resistance state which can be reached by current starting from the parallel configuration of the respective ferromagnetic layers. The generation of spin waves is investigated at room temperature in the frequency domain by spectrum analysis, demonstrating both in-plane and out-of-plane precessions of the magnetization of the free magnetic layer. Current-induced magnetization dyn…
We report on the growth and characterization of a new Diluted Magnetic Semiconductor (DMS) heterostructure that presents a Two-Dimensional Electron Gas (2DEG) with a carrier density $n \sim 1.08 \times 10^{12} cm^{-2}$ and a mobility $μ\sim 600 cm^{2} / (Vs)$ at T $\sim$ 4.2K. As far as we know this is the highest mobility value reported in the literature for GaMnAs systems. A novel technique was developed to make Ohmic contact to the buried 2DEG without destroying the magnetic properties of our crystal.
We report on realization and transport spectroscopy study of single quantum dots (QDs) made from InSb nanowires grown by molecular beam epitaxy (MBE). The nanowires employed are 50-80 nm in diameter and the QDs are defined in the nanowires between the source and drain contacts on a Si/SiO$_2$ substrate. We show that highly tunable QD devices can be realized with the MBE-grown InSb nanowires and the gate-to-dot capacitance extracted in the many-electron regimes is scaled linearly with the longitudinal dot size, demonstrating that the devices are of single InSb nanowire QDs even with a longitudi…
We report optical orientation experiments in individual, strain free GaAs quantum dots in AlGaAs grown by droplet epitaxy. Circularly polarized optical excitation yields strong circular polarization of the resulting photoluminescence at 4K. Optical injection of spin polarized electrons into a dot gives rise to dynamical nuclear polarization that considerably changes the exciton Zeeman splitting (Overhauser shift). We show that the created nuclear polarization is bistable and present a direct measurement of the build-up time of the nuclear polarization in a single GaAs dot in the order of one s…
We studied the size distribution and its scaling behavior of self-assembled InAlAs/AlGaAs quantum dots (QDs) grown on GaAs with the Stranski-Krastanov (SK) mode by molecular beam epitaxy (MBE), at both 480°C and 510°C, as a function of InAlAs coverage. A scaling function of the volume was found for the first time in ternary alloy QDs. The function was similar to that of InAs/GaAs QDs, which agreed with the scaling function for the two-dimensional submonolayer homoepitaxy simulation with a critical island size of i = 1. However, a character of i = 0 was also found as a tail in the large volume.
We analyze the structural and magnetic characteristics of (111)-oriented lutetium iron garnet (Lu$_3$Fe$_5$O$_{12}$) films grown by molecular-beam epitaxy, for films as thin as 2.8 nm. Thickness-dependent measurements of the in- and out-of-plane ferromagnetic resonance allow us to quantify the effects of two-magnon scattering, along with the surface anisotropy and the saturation magnetization. We achieve effective damping coefficients of $11.1(9) \times 10^{-4}$ for 5.3 nm films and $32(3) \times 10^{-4}$ for 2.8 nm films, among the lowest values reported to date for any insulating ferrimagnet…
GaMnAs thin films with different Mn doping concentrations were grown via molecular beam epitaxy using a substrate temperature of 250 °C. The thin films were investigated using photoluminescence (PL) measurements from 8 to 300 K. Transitions involving Mn acceptors were identified and a binding energy of ~0.1 eV was found. A Mn doping concentration dependent PL spectrum was found to lend insight into the film quality at a local level. Temperature dependent PL studies show that the doping related emissions drop faster in energy than other peaks with increasing temperature, indicating that they ar…
We report resistance versus magnetic field measurements for a La0.65Sr0.35MnO3/SrTiO3/La0.65Sr0.35MnO3 tunnel junction grown by molecular-beam epitaxy, that show a large field window of extremely high tunneling magnetoresistance (TMR) at low temperature. Scanning the in-plane applied field orientation through 360^/circ, the TMR shows 4-fold symmetry, i.e. biaxial anisotropy, aligned with the crystalline axes but not the junction geometrical long axis. The TMR reaches ~ 1900% at 4K, corresponding to an interfacial spin polarization of > 95% assuming identical interfaces. These results show that…
Mn concentration depth profiles in Mn-doped GaAs thin films grown at substrate temperatures of 580 and 250 °C using various Mn cell temperatures have been investigated with dynamic secondary ion mass spectrometry and Auger electron spectroscopy. When the samples are grown at a low substrate temperature of 250 °C, the Mn distributes uniformly. For the samples grown at a high substrate temperature of 580 °C, the concentration depth profiles are easily fitted with a temperature-dependent Fermi function only if the Mn concentration is above the solubility limit. However, when the Mn concentration …
We report on the selective-area chemical beam epitaxial growth of InAs in-plane, one-dimensional (1-D) channels using patterned SiO$_{2}$-coated InP(001), InP(111)B, and InP(110) substrates to establish a scalable platform for topological superconductor networks. Top-view scanning electron micrographs show excellent surface selectivity and dependence of major facet planes on the substrate orientations and ridge directions, and the ratios of the surface energies of the major facet planes were estimated. Detailed structural properties and defects in the InAs nanowires (NWs) were characterized by…
We present an experimental investigation of the magnetic, electrical and structural properties of Ga0.94Mn0.06As1-yPy layers grown by molecular beam epitaxy on GaAs substrates for y less than or equal to 0.3. X-ray diffraction measurements reveal that the layers are under tensile strain which gives rise to a magnetic easy axis perpendicular to the plane of the layers. The strength of the magnetic anisotropy and the coercive field increase as the phosphorous concentration is increased. The resistivity of all samples shows metallic behaviour with the resistivity increasing as y increases. These …
Topological insulators (TIs) are a promising class of materials for manipulating the magnetization of an adjacent ferromagnet (FM) through the spin-orbit torque (SOT) mechanism. However, current studies combining TIs with conventional FMs present large device-to-device variations, resulting in a broad distribution of SOT magnitudes. It has been identified that the interfacial quality between the TI and the FM is of utmost importance in determining the nature and efficiency of the SOT. To optimize the SOT magnitude and enable ultra-low-power magnetization switching, an atomically smooth interfa…
We fabricated GaAs/AlGaAs quantum dots by droplet epitaxy method, and obtained the geometries of the dots from scanning transmission electron microscopy data. Post-thermal annealing is essential for the optical activation of quantum dots grown by droplet epitaxy. We investigated the emission energy shifts of the dots and underlying superlattice by post-thermal annealing with photoluminescence and cathodoluminescence measurements, and specified the emissions from the dots by selectively etching the structure down to a lower layer of quantum dots. We studied the influences of the degree of annea…
The depth distribution of the transport properties as well as the temperature dependence of the low field magneto-conductance for several c-axis oriented GaN nanowall network samples grown with different average wall-widths are investigated. Magneto-conductance recorded at low temperatures shows clear signature of weak localization effect in all nanowall samples studied here. The scattering mean free path and the phase coherence time, are extracted from the magneto-conductance profile. Electron mobility estimated from scattering mean free path is found to be comparable with those estimated pre…
The growth of single layer graphene nanometer size domains by solid carbon source molecular beam epitaxy on hexagonal boron nitride (h-BN) flakes is demonstrated. Formation of single-layer graphene is clearly apparent in Raman spectra which display sharp optical phonon bands. Atomic-force microscope images and Raman maps reveal that the graphene grown depends on the surface morphology of the h-BN substrates. The growth is governed by the high mobility of the carbon atoms on the h-BN surface, in a manner that is consistent with van der Waals epitaxy. The successful growth of graphene layers dep…
We observe a stable intermediate resistance switching state in the current perpendicular to plane geometry for all Co/Cu/Co double layer nanopillar junctions grown by molecular beam epitaxy. This novel state has a resistance between the resistances of the parallel and antiparallel alignment of both Co-layer magnetizations. The state, which originates from an additional in-plane magnetic easy axis, can be reached by spin transfer torque switching or by an external magnetic field. In addition to spin torque-induced coherent small-angle spin wave modes we observe a broad microwave emission spectr…
Reflection high energy electron diffraction (RHEED), scanning tunneling microscopy (STM), vibrating sample magnetometry and other physical property measurements are used to investigate the structure, morphology, magnetic and magneto-transport properties of (001)-oriented Cr$_2$Te$_3$ thin films grown on Al$_2$O$_3$(0001) and Si(111)-(7$\times$7) surfaces by molecular beam epitaxy (MBE). Streaky RHEED patterns indicate flat smooth film growth on both substrates. STM studies show the hexagonal arrangements of surface atoms. Determination of the lattice parameter from atomically resolved STM imag…
N-type doping of GaAs nanowires has proven to be difficult because the amphoteric character of silicon impurities is enhanced by the nanowire growth mechanism and growth conditions. The controllable growth of n-type GaAs nanowires with carrier density as high as 1020 electron/cm3 by self-assisted molecular beam epitaxy using Te donors is demonstrated here. Carrier density and electron mobility of highly doped nanowires are extracted through a combination of transport measurement and Kelvin probe force microscopy analysis in single-wire field-effect devices. Low-temperature photoluminescence is…
We report on silicon delta doping of metalorganic vapor-phase epitaxy-grown \b{eta}-Ga2O3 thin films using silane precursor. Delta-doped \b{eta}-Ga2O3 epitaxial films are characterized using capacitance-voltage profiling and secondary-ion mass spectroscopy. Electron sheet charge density in the range of 2.9e12 cm-2 to 8e12 cm-2 with a half width at half maximum ranging from 6.2 nm to 3.5 nm is measured. We also demonstrate a high density (6.4e12 cm-2) degenerate two-dimensional electron gas using a delta-doped \b{eta}-(Al0.26Ga0.74)2O3/\b{eta}-Ga2O3 heterostructure.The total charge could also i…
We present a systematic study of the morphology of homoepitaxial InP films grown by metalorganic vapor-phase epitaxy which are imaged with ex situ atomic force microscopy. These films show a dramatic range of different surface morphologies as a function of the growth conditions and substrate (growth temperature, V/III ratio, and miscut angle < 0.6deg and orientation toward A or B sites), ranging from stable step flow to previously unreported strong step bunching, over 10 nm in height. These observations suggest a window of growth parameters for optimal quality epitaxial layers. We also present…
We report the successful growth of high-quality SrO films on highly-ordered pyrolytic graphite (HOPG) and single-layer graphene by molecular beam epitaxy. The SrO layers have (001) orientation as confirmed by x-ray diffraction (XRD) while atomic force microscopy measurements show continuous pinhole-free films having rms surface roughness of <1.5 Å. Transport measurements of exfoliated graphene after SrO deposition show a strong dependence between the Dirac point and Sr oxidation. Subsequently, the SrO is leveraged as a buffer layer for more complex oxide integration via the demonstration of (0…
We investigate correlation effects in the regime of a few electrons in uncapped InAs quantum dots by tunneling spectroscopy and wave function (WF) mapping at high tunneling currents where electron-electron interactions become relevant. Four clearly resolved states are found, whose approximate symmetries are roughly s and p, in order of increasing energy. Because the major axes of the p-like states coincide, the WF sequence is inconsistent with the imaging of independent-electron orbitals. The results are explained in terms of many-body tunneling theory, by comparing measured maps with those ca…
We investigate the optical emission and decay dynamics of excitons confined in large strain-free GaAs quantum dots grown by droplet epitaxy. From time-resolved measurements combined with a theoretical model we show that droplet-epitaxy quantum dots have a quantum efficiency of about 75% and an oscillator strength between 8 and 10. The quantum dots are found to be fully described by a model for strongly-confined excitons, in contrast to the theoretical prediction that excitons in large quantum dots exhibit the so-called giant oscillator strength. We attribute these findings to localized ground-…
Pursuing the confinement of linearly dispersive relativistic fermions is of interest in both fundamental physics and potential applications. Here, we report strong STM evidence for the equally spaced, strikingly sharp, and densely distributed quantum well states (QWSs) near Fermi energy in Pb(111) nanoislands, van-der-Waals epitaxially grown on graphitized 6H-SiC(0001). The observations can be explained as the quantized energies of confined linearly dispersive [111] electrons, which essentially 'simulate' the out-of-plane relativistic quasiparticles. The equally spaced QWSs with an origin of c…
Nearly localized moire flat bands in momentum space, arising at particular twist angles, are the key to achieve correlated effects in transition-metal dichalcogenides. Here, we use angle-resolved photoemission spectroscopy (ARPES) to visualize the presence of a flat band near the Fermi level of van der Waals (vdW) WSe2/MoSe2 heterobilayer grown by molecular beam epitaxy. This flat band is localized near the K point of the Brillouin zone and has a width of several hundred meVs. By combining ARPES measurements with density functional theory (DFT) calculations, we confirm the coexistence of diffe…
We report on luminescent centers contained in a few-layer-thick hexagonal boron nitride (h-BN) film grown on Ni by molecular beam epitaxy. After transfer to a SiO$_2$/Si substrate, sharp lines are observed in photo- and cathodoluminescence spectra in both the ultraviolet and the visible range. Spatially resolved measurements reveal that the luminescent centers responsible for these lines are localized within microscopic multi-layer islands that form at the nucleation centers of the h-BN film. The comparison of their energy, polarization and phonon replica emission with previous theoretical pre…
Vertically stacking two dimensional (2D) materials can enable the design of novel electronic and optoelectronic devices and realize complex functionality. However, the fabrication of such artificial heterostructures in wafer scale with an atomically-sharp interface poses an unprecedented challenge. Here, we demonstrate a convenient and controllable approach for the production of wafer-scale 2D GaSe thin films by molecular beam epitaxy. In-situ reflection high-energy electron diffraction oscillations and Raman spectroscopy reveal a layer-by-layer van der Waals epitaxial growth mode. Highly-effi…
Two-dimensional materials (2D) arranged in hybrid van der Waals (vdW) heterostructures provide a route toward the assembly of 2D and conventional III-V semiconductors. Here, we report the structural and electronic properties of single layer WSe2 grown by molecular beam epitaxy on Se-terminated GaAs(111)B. Reflection high-energy electron diffraction images exhibit sharp streaky features indicative of a high-quality WSe2 layer produced via vdW epitaxy. This is confirmed by in-plane x-ray diffraction. The single layer of WSe2 and the absence of interdiffusion at the interface are confirmed by hig…
The emission cascade of a single quantum dot is a promising source of entangled photons. A prerequisite for this source is the use of a symmetric dot analogous to an atom in a vacuum, but the simultaneous achievement of structural symmetry and emission in a telecom band poses a challenge. Here we report the growth and characterization of highly symmetric InAs/InAlAs quantum dots self-assembled on C3v symmetric InP(111)A. The broad emission spectra cover the O (1.3 micron-m), C (1.55 micron-m), and L (1.6 micron-m) telecom bands. The distribution of the fine-structure splittings is considerably…
We report a method for growing rectangular InAs nanofins with deterministic length, width and height by dielectric-templated selective-area epitaxy. These freestanding nanofins can be transferred to lay flat on a separate substrate for device fabrication. A key goal was to regain a spatial dimension for device design compared to nanowires, whilst retaining the benefits of bottom-up epitaxial growth. The transferred nanofins were made into devices featuring multiple contacts for Hall effect and four-terminal resistance studies, as well as a global back-gate and nanoscale local top-gates for den…
Single layer (SL) phosphorus (phosphorene) has drawn considerable research attention recently as a two-dimensional (2D) material for application promises. It is a semiconductor showing superior transport and optical properties. Few-layer or SL black phosphorus has been successfully isolated by exfoliation from bulk crystals and extensively studied thereof for its electronic and optical properties. Blue phosphorus (blueP), an allotrope of black phosphorus where atoms are arranged in a more flat atomic configuration, has been recently suggested by theory to exist in the SL form on some substrate…
Graphene nanoribbon (GNR) field-effect transistors (FETs) with widths down to 12 nm have been fabricated by electron beam lithography using a wafer-scale chemical vapor deposition (CVD) process to form the graphene. The GNR FETs show drain-current modulation of approximately 10 at 300 K, increasing to nearly 106 at 4 K. The strong temperature dependence of the minimum current indicates the opening of a bandgap for CVD-grown GNR-FETs. The extracted bandgap is estimated to be around 0.1 eV by differential conductance methods. This work highlights the development of CVD-grown large-area graphene …
We report on the systematic investigation of the optical properties of a selectively grown quantum dot gain material assisted by block-copolymer lithography for potential applications in active optical devices operating in the wavelength range around 1.55 um and above. We investigated a new type of diblock copolymer PS-b-PDMS (polystyrene-block-polydimethylsiloxane) for the fabrication of silicon oxycarbide hard mask for selective area epitaxy of InAs/InP quantum dots. An array of InAs/InP quantum dots was selectively grown via droplet epitaxy. Our detailed investigation of the quantum dot car…