A deeply modulated, regular, continuous, oscillating current waveform is reliably and repeatably achieved during electropolishing of niobium single-cell elliptical radiofrequency cavities. Details of the technique and cavity test results are reported here. The method is applicable for cavity frequencies in the range 500 MHz to 3.9 GHz and can be extended to multicell structures.
The PIP II linear accelerator includes different types of niobium SRF cavities including 650 MHz elliptical low (0.61) and high (0.92) beta cavities. The elliptical cavity surface is processed with the electropolishing method. The elliptical cavities especially the low-$β$ 650 MHz cavities showed a rough equator surface after the EP was per-formed with the standard EP conditions. This work was focused to study the effect of different EP parameters, including cathode surface area, temperature and voltage, and optimize them to improve the cavity surface.
As a result of a collaboration between Jefferson Lab and niobium manufacturer CBMM, ingot niobium was explored as a possible material for superconducting radiofrequency (SRF) cavity fabrication. The first single cell cavity from large grain high purity niobium was fabricated and successfully tested at Jefferson Lab in 2004. This pioneering work triggered research activities in other SRF laboratories around the world. Large grain niobium became not only an interesting alternative material for cavity builders, but also material scientists and surface scientists were eager to participate in the d…
We report a surface treatment that systematically improves the quality factor of niobium radio frequency cavities beyond the expected limit for niobium. A combination of annealing in a partial pressure of nitrogen or argon gas and subsequent electropolishing of the niobium cavity surface leads to unprecedented low values of the microwave surface resistance, and an improvement in the efficiency of the accelerating structures up to a factor of 3, reducing the cryogenic load of superconducting cavities for both pulsed and continuous duty cycles. The field dependence of the surface resistance is r…
Nitrogen doping treatment with the subsequent electropolishing (EP) of the niobium superconducting cavity can significantly increase the cavity's quality factor up to a factor of 3. But the process of the EP removal may reintroduce hydrogen in the cavity surface, which may influence the cavity's radio frequency performance. Plasma cleaning study on niobium samples with gas mixtures of argon and oxgen intended to remove contaminations (hydrocarbons and micronicdust particles) from cavity surface to avoid field emission, was performed in Peking University. The niobium samples have been analyzed …
A new surface treatment technique for niobium (Nb) Superconducting Radio Frequency (SRF) cavities called Buffered Electropolishing (BEP) has been developed at JLab. It was found that BEP could produce the smoothest surface finish on Nb samples ever reported in the literature. Experimental results revealed that the Nb removal rate of BEP could reach as high as 4.09 um/min. This is significantly faster1 than that of the conventional electropolishing technique employing an acid mixture of HF and H2SO4. An investigation is underway to determine the optimum values for all relevant BEP parameters so…
In this paper we present the discovery of a new surface treatment applied to superconducting radio frequency (SRF) niobium cavities, leading to unprecedented accelerating fields of 49 MV/m in TESLA-shaped cavities, in continuous wave (CW); the corresponding peak magnetic fields are the highest ever measured in CW, about 210 mT. For TESLA-shape cavities the maximum quench field ever achieved was ~45 MV/m - reached very rarely- with most typical values being below 40 MV/m. These values are reached for niobium surfaces treated with electropolishing followed by the so called mild bake, a 120C vacu…
An increase in the quality factor of superconducting radiofrequency cavities is achieved by minimizing the surface resistance during processing steps. The surface resistance is the sum of temperature independent residual resistance and temperature/material dependent Bardeen-Cooper-Schrieffer (BCS) resistance. High temperature heat treatment usually reduces the impurities concentration from the bulk niobium, lowering the residual resistance. The BCS part can be reduced by selectively doping non-magnetic impurities. The increase in quality factor, termed as Q-rise, was observed in cavities when …
We present the results of from DC magnetization and penetration depth measurements of cylindrical bulk large-grain (LG) and fine-grain (FG) niobium samples used for the fabrication of superconducting radio frequency (SRF) cavities. The surface treatment consisted of electropolishing and low temperature baking as they are typically applied to SRF cavities. The magnetization data were fitted using a modified critical state model. The critical current density Jc and pinning force Fp are calculated from the magnetization data and their temperature dependence and field dependence are presented. The…
The Standing Wave (SW) TESLA niobium-based superconducting radio frequency structure is limited to an accelerating gradient of about 50 MV/m by the critical RF magnetic field. To break through this barrier, we explore the option of niobium-based traveling wave (TW) structures. Optimization of TW structures was done considering experimentally known limiting electric and magnetic fields. It is shown that a TW structure can have an accelerating gradient above 70 MeV/m that is about 1.5 times higher than contemporary standing wave structures with the same critical magnetic field. The other benefit…
Nitrogen doping study on niobium (Nb) samples used for the fabrication of superconducting radio frequency (SRF) cavities was carried out. The samples' surface treatment was attempted to replicate that of the Nb SRF cavities, which includes heavy electropolishing (EP), nitrogen doping and the subsequent EP with different amounts of material removal. The surface chemical composition of Nb samples with different post treatments has been studied by XPS. The chemical composition of Nb, O, C and N was presented before and after Gas Cluster Ion Beam (GCIB) etching. No signals of poorly superconductin…
We report a strong effect of the cooling dynamics through $T_\mathrm{c}$ on the amount of trapped external magnetic flux in superconducting niobium cavities. The effect is similar for fine grain and single crystal niobium and all surface treatments including electropolishing with and without 120$^\circ$C baking and nitrogen doping. Direct magnetic field measurements on the cavity walls show that the effect stems from changes in the flux trapping efficiency: slow cooling leads to almost complete flux trapping and higher residual resistance while fast cooling leads to the much more efficient flu…
We report the rf performance of a single-cell superconducting radiofrequency cavity after low temperature baking in a nitrogen environment. A significant increase in quality factor has been observed when the cavity was heat treated in the temperature range of 120-160 °C with a nitrogen partial pressure of ~25 mTorr. This increase in quality factor as well as the Q-rise phenomenon (anti-Q-slope) is similar to those previously obtained with high temperature nitrogen doping as well as titanium doping. In this study, a cavity N2-treated at 120 °C and at140 °C, showed no degradation in accelerating…
The technological and metallurgical requirements of material for highgradient superconducting cavities are described. High-purity niobium, as the preferred metal for the fabrication of superconducting accelerating cavities, should meet exact specifications. The content of interstitial impurities such as oxygen, nitrogen, and carbon must be below 10μg/g. The hydrogen content should be kept below 2μg/g to prevent degradation of the Q-value under certain cool-down conditions. The material should be free of flaws (foreign material inclusions or cracks and laminations) that can initiate a thermal b…
Nb$_3$Sn is a promising advanced material under development for superconducting radiofrequency (SRF) cavities. Past efforts have been focused primarily on small development-scale cavities, but large, often multi-celled cavities, are needed for particle accelerator applications. In this work, we report on successful Nb$_3$Sn coatings on Nb in a 1 m-long 9-cell Nb sample-host cavity at Fermilab. The geometry of the first coating with only one Sn source made it possible to study the influence of Sn flux on the microstructure. Based on these results, we postulate a connection between recently obse…
The Tera Electronvolt Superconducting Linear Accelerator TESLA is the only linear electron-positron collider project based on superconductor technology for particle acceleration. In the first stage with 500 GeV center-of-mass energy an accelerating field of 23.4 MV/m is needed in the superconducting niobium cavities which are operated at a temperature of 2 K and a quality factor Q0 of 10 to the 10. This performance has been reliably achieved in the cavities of the TESLA Test Facility (TTF) accelerator. The upgrade of TESLA to 800 GeV requires accelerating gradients of 35 MV/m. Using an improve…
A Three-Fluid Model of Dissipation at Surfaces in Superconducting Radiofrequency Cavities
Laboratory of Atomic and Solid State Physics, Cornell University（康奈尔大学原子与固态物理实验室）；Cornell Laboratory for Accelerator-Based Sciences and Education, Cornell University（康奈尔大学加速器科学与教育实验室）