We have synthesized the novel material Na_2IrO_3 and studied its structure, transport, magnetic, and thermal properties using powder x-ray diffraction (PXRD), electrical resistivity, isothermal magnetization M versus magnetic field H, static χand dynamic χ_ac magnetic susceptibility versus temperature T, and heat capacity C versus T measurements. Na_2IrO_3 crystallizes in the monoclinic C2/c (No. 15) structure which is made up of Na and NaIr_2O_6 layers alternately stacked along the c axis. From a Rietveld refinement of the PXRD pattern we identify atomic disorder arising from a mixing of Ir and Na sites within the NaIr_2O_6 layers. The χdata in H = 1 T shows Curie-Weiss behavior at high T > 100 K with an effective moment μ_eff = 1.82(1) μ_B indicating an effective spin S_eff = 1/2 on the Ir^{4+} moments. A Weiss temperature θ= - 62(1) K indicates substantial antiferromagnetic interactions between these S_eff = 1/2, Ir^{4+} moments. The χdata in low field show a sharp cusp at T_g = 5.5 K and there is a bifurcation between zero-field-cooled (ZFC) and field-cooled (FC) data below this T. The χ_ac data also show a sharp cusp at T_g = 5.5 K at a frequency f = 1 Hz which moves to higher temperatures with increasing f. We did not observe any anomaly at T_g in our C measurements and only a broad shoulder was observed at a much higher T = 12 K. Our results indicate that in Na_2IrO_3, a spin-glass like state occurs below the freezing temperature T_g = 5.5 K and this freezing most likely arises either from structural disorder or geometrical magnetic frustration.
A layered iron oxide \rfeo ($R$: rare-earth elements) is an exotic dielectric material with charge-order (CO) driven electric polarization and magnetoelectric effect caused by spin-charge coupling. In this paper, a theory of electronic structure and dielectric property in \rfeo is presented. Charge frustration in paired-triangular lattices allows a charge imbalance without inversion symmetry. Spin frustration induces reinforcement of this polar CO by a magnetic ordering. We also analyze an orbital model for the Fe ion which does not show a conventional long-range order.
We study a doubly-degenerate orbital model on a honeycomb attice. This is a model for orbital states in multiferroic layered iron oxides. The classical and quantum models are analyzed by spin-wave approximation, Monte-Carlo simulation and Lanczos method. A macroscopic number of degeneracy exists in the classical ground state. In the classical model, a peak in the specific heat appears at a temperature which is much lower than the mean-field ordering one. Below this temperature, angle of orbital pseudo-spin is fixed, but conventional orbital orders are not suggested. The degeneracy in the groun…
We report here a detailed study of AC/DC magnetization and longitudinal/transverse transport properties of La$_{1.2}$Sr$_{1.8}$Mn$_{2}$O$_{7}$ single crystals below $T_{c}$ = 121 K. We find that the resistivity upturn below 40 K is related to the reentrant spin glass phase at the same temperature, accompanied by additional anomalous Hall effects. The carrier concentration from the ordinary Hall effects remains constant during the transition and is close to the nominal doping level (0.4 holes/Mn). The spin glass behavior comes from the competition between ferromagnetic double exchange and antif…
The single layered manganite Pr$_{0.22}$Sr$_{1.78}$MnO$_4$ undergoes structural transition from high temperature tetragonal phase to low temperature orthorhombic phase below room temperature. The orthorhombic phase was reported to have two structural variants with slightly different lattice parameters and Mn-3$d$ levels show orbital ordering within both the variants, albeit having mutually perpendicular ordering axis. In addition to orbital ordering, the orthorhombic variants also order antiferromagnetically with different Néel temperatures. Our magnetic investigation on the polycrystalline sa…
Dielectric and magnetic phenomena in spin and charge frustrated system RFe2O4 (R is a rare-earth metal ion) are studied. An electronic model for charge, spin and orbital degrees in a pair of triangular-lattice planes is derived. We analyze this model by utilizing the mean-field approximation and the Monte-Carlo simulation in a finite size cluster. A three fold-type charge ordered structure with charge imbalance between the planes is stabilized in finite temperatures. This polar charge order is reinforced by spin ordering of Fe ions. This novel magneto-dielectric phenomenon is caused by spin fr…
A new layered iron-oxychalcogenide Na2Fe2OSe2 has been synthesized and structurally characterized by powder X-ray diffraction. The structure is formed by alternate stacking of the newly discovered [Fe2OSe2] blocks and double layers of Na. Conductivity study shows that Na2Fe2OSe2 is a semiconductor with activation energy of 0.26 eV. Magnetic susceptibility and heat capacity measurements reveal an antiferromagnetic phase transition occurs at TN=73 K. A broad maximum of magnetic susceptibility and a slow decay of the specific heat above TN, arises as a result of two-dimensional short-range spin c…
The ac-susceptibility of the electron doped single-layered manganite La$_{1.1}$Sr$_{0.9}$MnO$_4$ is analyzed in detail. A quasi two-dimensional (2$D$) antiferromagnetic (AFM) order with Ising anisotropy is stabilized below $T_N$ $\sim$ 80K. We show that below $T_N$, a rare 2$D$ spin-glass (SG) correlation develops with the same Ising anisotropy as the AFM state. Using simple scaling arguments of the droplet model, we derive a scaling form for the ac-susceptibility data of a 2$D$ SG, which our experimental data follows fairly well. Due to simplifications in this 2$D$ case, the proposed scaling …
A1-xFe2-ySe2 (A = K, Cs, Rb, Tl) are recently discovered iron-based superconductors with critical temperatures (Tc) ranging up to 32 K. Their parent phases have unique properties when compared with other iron-based superconductors; e.g., their crystal structures include ordered Fe vacancies, their normal states are antiferromagnetic (AFM) insulating phases, and they have extremely high Néel transition temperatures. However, control of carrier doping into the parent AFM insulators has been difficult due to their intrinsic phase separation. Here, we fabricated an Fe-vacancy-ordered TlFe1.6Se2 in…
We have successfully synthesized a new layered iron oxychalcogenide BaFe2OSe2 single crystal. This compound is built up of Ba and Fe-Se(O) layers alternatively stacked along the c-axis. The Fe-Se(O) layers contain double chains of edge-shared Fe-Se(O) tetrahedra that propagate along the b-axis and are bridged by oxygen along the a-axis. Physical property measurements indicate that BaFe2OSe2 is a semiconductor without the Curie-Weiss behavior up to 350 K. There is a possible long range antiferromagnetic (AFM) transition at 240 K, corresponding to the peak in specific heat measurement and two gl…
We report the existence of Griffiths phase (GP) and its influence on critical phenomena in layered Sr$_2$IrO$_4$ ferromagnet (T$_C$ = 221.5 K). The power law behavior of inverse magentic susceptibility, 1/$χ$(T) with exponent $λ= 0.18(2)$ confirm the GP in the regime T$_C$ $<$ T $\leq$ T$_G$ = 279.0(5) K. Moreover, the detailed critical analysis via modified Arrott plot method exhibits unrealistic critical exponents $β$ = 0.77(1), $γ$ = 1.59(2) and $δ= 3.06(4)$, in corroboration with magneto-caloric study. The abnormal exponent values have been viewed in context of ferromagnetic-Griffiths phas…
Here, we report an investigation of structural, magnetic and electronic properties in Y-doped layered iridate (Sr$_{1-x}$Y$_x$)$_2$IrO$_4$ ($x$ $\leq$ 0.1). The parent Sr$_2$IrO$_4$ is a well-studied spin-orbit coupling (SOC) induced insulator with an antiferromagnetic ground state. The Y-doping here equivalently acts for electron doping without altering the vital parameters such as, SOC and electron correlation. Experimental results show a minute change in structural parameters and an equivalent charge conversion from Ir$^{4+}$ to Ir$^{3+}$. Unlike similarly other electron-doped system, the l…
To get insight into the nature of the electronic fluid in the frustration-driven charge glasses, we investigate in-plane and out-of-plane charge transport for several quasi-triangular-lattice organic systems, $θ$-(BEDT-TTF)$_2$X [X=RbZn(SCN)$_4$, CsZn(SCN)$_4$ and I$_3$]. These compounds host a charge order, charge glass and Fermi liquid, depending on the strength of charge frustration. We find that the resistivity exhibits extremely two-dimensional (2D) anisotropy and contrasting temperature dependence between in the in-plane and out-of-plane directions in the charge glass phase, qualitativel…
The layered honeycomb magnet $α$-Li$_2$IrO$_3$ has been theoretically proposed as a candidate to display novel magnetic behaviour associated with Kitaev interactions between spin-orbit entangled $j_{\rm eff}=1/2$ magnetic moments on a honeycomb lattice. Here we report single crystal magnetic resonant x-ray diffraction combined with powder magnetic neutron diffraction to reveal an incommensurate magnetic order in the honeycomb layers with Ir magnetic moments counter-rotating on nearest-neighbour sites. This type of magnetic structure has not been reported experimentally before in honeycomb magn…
We report high-resolution photoemission spectroscopy of newly-discovered iron-based layered superconductor La(O$_{0.93}$F$_{0.07}$)FeAs (Tc = 24 K). We found that the superconducting gap shows a marked deviation from the isotropic s-wave symmetry. The estimated gap size at 5 K is 3.6 meV in the s- or axial p-wave case, while it is 4.1 meV in the polar p- or d-wave case. We also found a pseudogap of 15-20 meV above Tc, which is gradually filled-in with increasing temperature and closes at temperature far above Tc similarly to copper-oxide high-temperature superconductors.
The thermal conductivity of polycrystalline samples of (Na,Ca)Co_2O_4 is found to be unusually low, 20 mW/cmK at 280 K. On the assumption of the Wiedemann-Franz law, the lattice thermal conductivity is estimated to be 18 mW/cmK at 280 K, and it does not change appreciably with the substitution of Ca for Na. A quantitative analysis has revealed that the phonon mean free path is comparable with the lattice parameters, where the point-defect scattering plays an important role. Electronically the same samples show a metallic conduction down to 4.2 K, which strongly suggests that NaCo_2O_4 exhibits…
We report the results of neutron diffraction, ac and dc magnetization, heat-capacity, complex permittivity, and pyrocurrent measurements on an oxide, Li3NiRuO5, hitherto not paid much attention in the literature, except for a previous report on its promising electrochemical performance. We emphasize on the following findings: (i) Observation of re-entrant spin-glass behavior; that is, this oxide undergoes ferrilmagnetic ordering below 8- K, entering spin-glass regime around 12 K. (ii) There is no prominent feature in the complex dielectric permittivity (in particular, at the magnetic transitio…
The response of the worldwide scientific community to the discovery in 2008 of superconductivity at Tc = 26 K in the Fe-based compound LaFeAsO_{1-x}F_x has been very enthusiastic. In short order, other Fe-based superconductors with the same or related crystal structures were discovered with Tc up to 56 K. Many experiments were carried out and theories formulated to try to understand the basic properties of these new materials and the mechanism for Tc. In this selective critical review of the experimental literature, we distill some of this extensive body of work, and discuss relationships betw…
Thin films of silver containing 0.3 - 1.5 at % Fe have been prepared by vapor co-deposition. Depending on substrate temperature and iron concentration we could systematically follow the formation of nanometer size clusters of iron from initially dilute iron monomers. samples were characterized via X-ray diffraction, resistivity and Mössbauer spectroscopic measurements. The magnetic behavior derived from Mössbauer data can be best described with an ensemble of ferromagnetic mono-domain particles. The magnetic freezing observed at low temperatures, is controlled via the inter-particle interactio…
We present $^{75}$As nuclear magnetic resonance spin-lattice and spin-spin relaxation rate data in Ba(Fe$_{1-x}$Co$_x$)$_2$As$_2$ and Ba(Fe$_{1-x}$Cu$_x$)$_2$As$_2$ as a function of temperature, doping and magnetic field. The relaxation curves exhibit a broad distribution of relaxation rates, consistent with inhomogeneous glassy behavior up to 100 K. The doping and temperature response of the width of the dynamical heterogeneity is similar to that of the nematic susceptibility measured by elastoresistance measurements. We argue that quenched random fields which couple to the nematic order give…
We investigate interplay between magnetic fluctuations and superconductivity in the effective five-band Hubbard model for iron-oxypnictide superconductors on the basis of the fluctuation-exchange approximation. As for the normal-state properties, we find the pseudogap behavior in the NMR relaxation rate and the spectral weight in the electron-doped region, while we cannot find such behavior in the hole-doped region. The pseudogap behavior originates from the band structure effect, that is, existence of high density of states just below the Fermi level. Solving the superconducting Eliashberg eq…
In the iron--chromium system, Fe$_{x}$Cr$_{1-x}$, a wide dome of spin-glass behavior emerges when the ferromagnetism of iron is suppressed and the antiferromagnetism of chromium emerges as a function of increasing iron content $x$. As both, the high-temperature state and the characteristic cluster size vary as a function of $x$, different regimes of spin-glass behavior may be compared in a single, isostructural material system. Here, we report a study of the spin dynamics across the freezing process into the spin-glass state for different iron concentrations ($x = 0.145$, $0.175$, $0.21$) usin…
We report structural, magnetic and dielectric properties of layered perovskite materials LnBaCuFeO5 (Ln = La and Lu). LaBaCuFeO5 shows magnetic cluster glass behavior below 60 K owing to the competing ferromagnetic and antiferromagnetic exchange interactions. Glassy dynamics of electric dipoles has also been observed in the vicinity of the magnetic glass transition temperature. The presence of significant coupling between spin and polar degrees of freedom results in the multiglass feature in LaBaCuFeO5. The LuBaCuFeO5 compound undergoes YBaCuFeO5 like commensurate to incommensurate antiferroma…
We report ^{31}P and ^{139}La NMR studies of (La_{0.87}Ca_{0.13})FePO, which is a family member of the recently discovered superconductor LaFeAs(O_{1-x}F_x). In the normal state, Knight shift and $1/T_1T$ show that a Fermi-liquid state with moderate ferromagnetic fluctuations emerges below 30K. From 1/T_1T of ^{31}P and ^{139}La, quasi-two dimensional electronic structure is suggested, in which the FeP layer is more conductive than the LaO layer. In the superconducting (SC) state, although a clear Meissner signal was observed, 1/T_1T increases below T_c, in contrast to a decrease of 1/T_1T due…
We report an unusual nearly ferromagnetic, heavy-mass state with a surprisingly large Wilson ratio $R_{\textrm{w}}$ (e.g., $R_{\textrm{w}}\sim$ 700 for $x =$ 0.2) in double layered ruthenates (Sr$_{1-x}$Ca$_{x}$)$_{3}$Ru$_{2}$O$_{7}$ with 0.08 $< x <$ 0.4. This state does not evolve into a long-range ferromagnetically ordered state despite considerably strong ferromagnetic correlations, but freezes into a cluster-spin-glass at low temperatures. In addition, evidence of non-Fermi liquid behavior is observed as the spin freezing temperature of the cluster-spin-glass approaches zero near $x \appr…
Based on the effective four-band model we analyze the spin response in the normal and superconducting states of the Fe-pnictide superconductors. While the normal state spin excitations are dominated by the continuum of the interorbital antiferromagnetic fluctuations and the intraband spin density wave fluctuations, the unconventional superconductivity yields different feedback. The resonance peak in form of the well-defined spin exciton occurs {\it only} for the interband scattering at the antiferromagnetic momentum ${\bf Q}_{AFM}$ for the $s_\pm$ (extended s-wave) superconducting order parame…
Nanoscale Sr$_2$IrO$_4$ Freestanding Thin-Films for Flexible Electronics
Department of Physics and Astronomy, University of Kentucky（肯塔基大学物理与天文学系）；Department of Materials Science and Engineering, The Ohio State University（俄亥俄州立大学材料科学与工程系）；Department of Physics, Pusan National University（釜山国立大学物理系）；Advanced Photon Source, Argonne National Laboratory（阿贡国家实验室先进光子源）
We have investigated the peculiar structure of charge and spin ordering in the half-doped layered perovskite oxide La$_{1.5}$Sr$_{0.5}$CoO$_4$ by elastic neutron scattering. Two samples with different preparation histories were studied. We find that the generic features of the ordered states, such as their short-range, glassy nature and the spin incommensurability, are sample-independent. At the same time, some subtle features of the ordered phases, such as the correlation lengths, differ.
High-temperature superconductivity remains arguably the largest outstanding enigma of condensed matter physics. The discovery of iron-based high-temperature superconductors has renewed the importance of understanding superconductivity in materials susceptible to magnetic order and fluctuations. Intriguingly they show magnetic fluctuations reminiscent of the superconducting (SC) cuprates, including a 'resonance' and an 'hour-glass' shaped dispersion, which provide an opportunity to new insight to the coupling between spin fluctuations and superconductivity. Here we report inelastic neutron scat…
Using resonant x-ray diffraction, we observe an easy c-axis collinear antiferromagnetic structure for the bilayer Sr$_3$Ir$_2$O$_7$, a significant contrast to the single layer Sr$_2$IrO$_4$ with in-plane canted moments. Based on a microscopic model Hamiltonian, we show that the observed spin-flop transition as a function of number of IrO$_2$ layers is due to strong competition among intra- and inter-layer bond-directional pseudo-dipolar interactions of the spin-orbit entangled $J_{eff}$=1/2 moments. With this we unravel the origin of anisotropic exchange interactions in a Mott insulator in the…
The surprising discovery of superconductivity in layered iron-based materials, with transition temperatures climbing as high as 55 K, has lead to thousands of publications on this subject over the past two years. While there is general consensus on the unconventional nature of the Cooper pairing state of these systems, several central questions remain - including the role of magnetism, the nature of chemical and structural tuning, and the resultant pairing symmetry - and the search for universal properties and principles continues. Here we review the progress of research on iron-based supercon…
A new layered perovskite-type oxide Ba$_2$RhO$_4$ was synthesized by a high-pressure technique with the support of convex-hull calculations. The crystal and electronic structure were studied by both experimental and computational tools. Structural refinements for powder x-ray diffraction data showed that Ba$_2$RhO$_4$ crystallizes in a K$_2$NiF$_4$-type structure, isostructural to Sr$_2$RuO$_4$ and Ba$_2$IrO$_4$. Magnetic, resistivity, and specific heat measurements for polycrystalline samples of Ba$_2$RhO$_4$ indicate that the system can be characterized as a correlated metal. Despite the clo…
When suppressing the itinerant antiferromagnetism in chromium by doping with the isostructual itinerant ferromagnet iron, a dome of spin-glass behavior emerges around a putative quantum critical point at an iron concentration $x \approx 0.15$. Here, we report a comprehensive investigation of polycrystalline samples of Fe$_{x}$Cr$_{1-x}$ in the range $0.05 \leq x \leq 0.30$ using x-ray powder diffraction, magnetization, ac susceptibility, and neutron depolarization measurements, complemented by specific heat and electrical resistivity data for $x = 0.15$. Besides antiferromagnetic ($x < 0.15$) …
The infrared transmission measurement was performed for a two-dimensional spin-orbit coupling induced Mott insulator Sr$_{2}$IrO$_{4}$ with a layered-perovskite structure. A phonon-assisted magnon mode was observed at around 1870 cm$^{-1}$ in the absorption spectrum below 180 K. The nearest-neighbor superexchange interaction $J$ was estimated to be 57 meV, which is about a half of the $J$ value of a copper oxide La$_{2}$CuO$_{4}$. Our results indicate the possibility that nontrivial properties such as superconductivity are realized at rather high temperature in iridium oxides.
Coexistence of phases, characterized by different electronic degrees of freedom, commonly occurs in layered superconductors. Among them, alkaline intercalated chalcogenides are model systems showing microscale coexistence of paramagnetic (PAR) and antiferromagnetic (AFM) phases, however, temporal behavior of different phases is still unknown. Here, we report the first visualization of the atomic motion in the granular phase of K$_{x}$Fe$_{2-y}$Se$_2$ using X-ray photon correlation spectroscopy. Unlike the PAR phase, the AFM texture reveals an intermittent dynamics with avalanches as in martens…
$^{75}$As and $^{139}$La field-swept NMR spectra were obtained for the novel weakly itinerant ferromagnet LaCoAsO with 2D layered structure above the Curie temperature of 55 K. By analyzing NMR spectra, temperature dependences of Knight shift $K$ and nuclear quadrupole resonance frequency $ν_Q$ were obtained successfully for each nucleus. We confirmed from the so-called $K$-$χ$ plots that the macroscopic magnetization of our {LaCoAsO} powder sample is intrinsic and does not contain the contribution from impurity phases. We estimated hyperfine coupling constants from the slope of $K$-$χ$ plots …
The recent discovery of superconductivity in the iron-based layered pnictides with T_c ranging between 26 and 56K generated enormous interest in the physics of these materials. Here, we review some of the peculiarities of the antiferromagnetic order in the iron pnictides, including the selection of the stripe magnetic order and the formation of the Ising-nematic state in the unfolded BZ within an itinerant description. In addition we analyze the properties of the quasiparticle interference spectrum in the parent antiferromagnetic phase.
We derive and study a spin one-half Hamiltonian on a honeycomb lattice describing the exchange interactions between Ir$^{4+}$ ions in a family of layered iridates $A_2$IrO$_3$ ($A$=Li,Na). Depending on the microscopic parameters, the Hamiltonian interpolates between the Heisenberg and exactly solvable Kitaev models. Exact diagonalization and a complementary spin-wave analysis reveal the presence of an extended spin-liquid phase near the Kitaev limit and a conventional Néel state close to the Heisenberg limit. The two phases are separated by an unusual stripy antiferromagnetic state, which is t…
57Fe Mössbauer spectroscopy was applied to an iron-based layered compound CeFePO. At temperatures from 9.4 to 293 K, no magnetic splitting was observed in the Mössbauer spectra of CeFePO indicating a paramagnetic phase of the Fe magnetic sublattice. All the spectra were fitted with a small quadrupole splitting, and the Debye temperature of CeFePO was found to be \sim448 K. The isomer shift at room temperature, 0.32 mm/s, was almost equal to those of LnFeAsO (Ln = La, Ce, Sm). Comparing s-electron density using the isomer shifts and unit cell volumes, it was found that the Fe of CeFePO has a si…
Study of superconductivity in layered iron-based materials was initiated in 2006 by Hosono's group, and boosted in 2008 by the superconducting transition temperature, Tc, of 26 K in LaFeAsO1-xFx. Since then, enormous researches have been done on the materials, with Tc reaching as high as 55 K. Here, we review briefly experimental and theoretical results on atomic and electronic structures and magnetic and superconducting properties of FeAs-based superconductors and related compounds. We seek for clues for unconventional superconductivity in the materials.
We show that in layered systems with electronic phase separation tendency, the long-range Coulomb interaction can drive the spontaneous formation of unidirectional superlattices of electronic charge in a completely homogeneous crystalline background. In this self-organized electronic heterostructure, the ratio among the number of crystalline planes in the minority and majority electronic phases corresponds to Farey fractions with the superlattice period controlled by the background charge density and the frustrating Coulomb interaction strength. The phase diagram displays Arnold tongues obeyin…
The structural, magnetic and transport properties of the layered RBaCo$_2$O$_{5.5}$ cobaltites are sensitive to the oxygen stoichiometry. In this present study, we report the presence of a low-temperature magnetic glassy state in electron-doped polycrystalline YBaCo$_2$O$_{5.5}$ cobaltite. The ac magnetization studies show the absence of conventional spin glass features, while the various dc magnetization studies demonstrate the presence of non-equilibrium magnetic glassy state at low temperature. The magnetic glassy state of this sample results from the kinetic arrest of the first order ferro…
By ab initio many-body quantum chemistry calculations, we determine the strength of the symmetric anisotropy in the 5$d^5$ j $\approx$ 1/2 layered material Ba$_2$IrO$_4$. While the calculated anisotropic couplings come out in the range of a few meV, orders of magnitude stronger than in analogous 3d transition-metal compounds, the Heisenberg superexchange still defines the largest energy scale. The ab initio results reveal that individual layers of Ba$_2$IrO$_4$ provide a close realization of the quantum spin-1/2 Heisenberg-compass model on the square lattice. We show that the experimentally ob…
Two-dimensional layered transition-metal-dichalcogenide compound 1T-TaS2 shows the rare coexistence of charge density wave (CDW) and electron correlation driven Mott transition. In addition, atomic-cluster spins on the triangular lattice of the CDW state of 1T-TaS2 give rise to the possibility of the exotic spin-singlet state in which quantum fluctuations of spins are strong enough to prevent any long range magnetic ordering down to absolute zero ( 0 K). We present here the evidences of a glass-like random singlet magnetic state in 1T-TaS2 at low temperatures through a study of temperature and…
We report the successful synthesis of single-crystals of the layered iridate, (Na$_{1-x}$Li$_{x}$)$_2$IrO$_3$, $0\leq x \leq 0.9$, and a thorough study of its structural, magnetic, thermal and transport properties. The new compound allows a controlled interpolation between Na$_2$IrO$_3$ and Li$_2$IrO$_3$, while maintaing the novel quantum magnetism of the honeycomb Ir$^{4+}$ planes. The measured phase diagram demonstrates a dramatic suppression of the Néel temperature, $T_N$, at intermediate $x$ suggesting that the magnetic order in Na$_2$IrO$_3$ and Li$_2$IrO$_3$ are distinct, and that at $x\…
A Ginzburg-Landau approach to fluctuations of a layered superconductor in a magnetic field is used to show that the interlayer coupling can be incorporated within an interacting self-consistent theory of a single layer, in the limit of a large number of neighboring layers. The theory exhibits two phase transitions -- a vortex liquid-to-solid transition is followed by a Bose-Einstein condensation into the Abrikosov lattice -- illustrating the essential role of interlayer coupling. Using this theory, explicit expressions for magnetization, specific heat, and fluctuation conductivity are derived.…
We have synthesized single crystals of Na$_2$(Ir$_{1-x}$Ti$_x$)O$_3$ and polycrystals of Li$_2$(Ir$_{1-x}$Ti$_x$)O$_3$ and studied the effect of magnetic depletion on the magnetic properties by measurements of the magnetic susceptibility, specific heat and magnetocaloric effect at temperatures down to 0.1~K. In both systems, the non-magnetic substitution rapidly changes the magnetically ordered ground state into a spin glass, indicating strong frustration. While for the Li system the Weiss temperature $Θ_{\rm W}$ remains unchanged up to $x=0.55$, a strong decrease $|Θ_{\rm W}|$ is found for th…
Magnetic moments arranged at the corners of a honeycomb lattice are predicted to form a novel state of matter, Kitaev quantum spin liquid, under the influence of frustration effects between bond-dependent Ising interactions. Some layered honeycomb iridates and related materials, such as Na$_{2}$IrO$_{3}$ and $α$-RuCl$_{3}$, are proximate to Kitaev quantum spin liquid, but bosonic spin-wave excitations associated with undesirable antiferromagnetic long-range order mask the inherent properties of Kitaev Hamiltonian. Here, we use $^{63}$Cu nuclear quadrupole resonance to uncover the low energy sp…
By using Nuclear Magnetic Resonance and ac-susceptibility, the characteristic correlation times for the vortex dynamics, in an iron-based superconductor, have been derived. Upon cooling, the vortex dynamics displays a crossover consistent with a vortex glass transition. The correlation times, in the fast motions regime, merge onto a universal curve which is fit by the Vogel-Fulcher law, rather than by an Arrhenius law. Moreover, the pinning barrier shows a weak dependence on the magnetic field which can be heuristically justified within a fragile glass scenario. In addition, the glass freezing…
Spin orbit assisted Mott insulators such as sodium iridate (Na$_2$IrO$_3$) have been an important subject of study in the recent years. In these materials, the interplay of electronic correlations, spin-orbit coupling, crystal field effects and a honeycomb arrangement of ions bring exciting ground states, predicted in the frame of the Kitaev model. The insulating character of Na$_2$IrO$_3$ has hampered its integration to an electronic device, desirable for applications, such as the manipulation of quasiparticles interesting for topological quantum computing. Here we show through electronic tra…