We report the synthesis and physical properties of single crystals of stoichiometric BaNi2As2 that crystalizes in the ThCr2Si2 structure with lattice parameters a = 4.112(4) Åand c = 11.54(2) Å. Resistivity and heat capacity show a first order phase transition at T_0 = 130 K with a thermal hysteresis of 7 K. The Hall coefficient is weakly temperature dependent from room temperature to 2 K where it has a value of -4x10^{-10} Ω-cm/Oe. Resistivity, ac-susceptibility, and heat capacity find evidence for bulk superconductivity at T_c = 0.7 K. The Sommerfeld coefficient at T_c is 11.6 \pm 0.9 mJ/molK^2. The upper critical field is anisotropic with initial slopes of dH_{c2}^{c}/dT = -0.19 T/K and dH_{c2}^{ab}/dT = -0.40 T/K, as determined by resistivity.
Kagome lattice offers unique opportunities for the exploration of unusual quantum states of correlated electrons. Here, we report on the observation of superconductivity in a kagome single crystal Pd3P2S8 when a semiconducting to metallic transition is driven by pressure. High-pressure resistance measurements show that the metallization and superconductivity are simultaneously observed at about 11 GPa. With increasing pressure, the superconducting critical temperature Tc is monotonously enhanced from 2.6 K to a maximum 7.7 K at ~52 GPa. Interestingly, superconductivity retains when the pressur…
We have studied the intrinsic normal and superconducting properties of the oxypnictide LaFePO. These samples exhibit bulk superconductivity and the evidence suggests that stoichiometric LaFePO is indeed superconducting, in contrast to other reports. We find that superconductivity is independent of the interplane residual resistivity $ρ_0$ and discuss the implications of this on the nature of the superconducting order parameter. Finally we find that, unlike $T_c$, other properties in single-crystal LaFePO including the resistivity and magnetoresistance, can be very sensitive to disorder.
We report pressure-induced superconductivity in a single crystal of CaFe2As2. At atmospheric pressure, this material is antiferromagnetic below 170 K but under an applied pressure of 0.69 GPa becomes superconducting, with a transition temperature Tc exceeding 10 K. The rate of Tc suppression with applied magnetic field is -0.7 K/T, giving an extrapolated zero-temperature upper critical field of 10-14T.
Here we report bulk superconductivity in BaFe1.8Co0.2As2 single crystals below Tc = 22 K, as demonstrated by resistivity, magnetic susceptibility, and specific heat data. Hall data indicate that the dominant carriers are electrons, as expected from simple chemical reasoning. This is the first example of superconductivity induced by electron doping in this family of materials. In contrast to the cuprates, the BaFe2As2 system appears to tolerate considerable disorder in the FeAs planes. First principles calculations for BaFe1.8Co0.2As2 indicate the inter-band scattering due to Co is weak.
We use c-axis resistivity and magnetoresistance measurements to study the interplay between antiferromagnetic (AF) and superconducting (SC) ordering in underdoped RBa_2Cu_3O_{6+x} (R = Lu, Y) single crystals. Both orders are found to emerge from an anisotropic 3D metallic state, upon which antiferromagnetism opposes superconductivity by driving the doped holes towards localization. Despite the competition, the superconductivity sets in before the AF order is completely destroyed and coexists with latter in a certain range of hole doping. We find also that strong magnetic fields affect the AF-S…
Single crystals of SrFe2-xPtxAs2 (0 < x < 0.36) were grown using the self flux solution method and characterized using x-ray crystallography, electrical transport, magnetic susceptibility, and specific heat measurements. The magnetic/structural transition is suppressed with increasing Pt concentration, with superconductivity seen over the range 0.08 < x < 0.36 with a maximum transition temperature Tc of 16 K at x = 0.16. The shape of the phase diagram and the changes to the lattice parameters are similar to the effects of other group VIII elements Ni and Pd, however the higher transition tempe…
We have successfully grown single crystalline NaFeAs with cobalt or phosphor doping. Bulk superconductivity occurs in NaFe$_{0.95}$Co$_{0.05}$As at 19 K while much higher transition temperature is observed in NaFeAs$_{0.8}$P$_{0.2}$, in which the Tc of 33 K is even higher than the highest value realized by applying pressure in NaFeAs and all other isoelectronic element substituted samples. We discuss these behaviours by comparison with 122 and 1111 systems. We hope that our findings will help improve our understanding of iron-based superconductivity.
The crystal structure and physical properties of BaFe2As2, BaCo2As2, and BaNi2As2 single crystals are surveyed. BaFe2As2 gives a magnetic and structural transition at TN = 132(1) K, BaCo2As2 is a paramagnetic metal, while BaNi2As2 has a structural phase transition at T0 = 131 K, followed by superconductivity below Tc = 0.69 K. The bulk superconductivity in Co-doped BaFe2As2 below Tc = 22 K is demonstrated by resistivity, magnetic susceptibility, and specific heat data. In contrast to the cuprates, the Fe-based system appears to tolerate considerable disorder in the transition metal layers. Fir…
The electrical resistivity ρ(T) and heat capacity C(T) on single crystals of SrNi2As2 and EuNi2As2 are reported. While there is no evidence for a structural transition in either compound, SrNi2As2 is found to be a bulk superconductor at T_c=0.62 K with a Sommerfeld coefficient of γ= 8.7 mJ/mol K^2 and a small upper critical field H_{c2} \sim 200 Oe. No superconductivity was found in EuNi2As2 above 0.4 K, but anomalies in ρand C reveal that magnetic order associated with the Eu^{2+} magnetic moments occurs at T_m = 14 K.
We have successfully grown the single crystal of a low carrier density system Y$_3$Ru$_4$Ge$_{13}$ which crystallizes in the cubic crystal structure with the space group Pm3n. Y$_3$Ru$_4$Ge$_{13}$ exhibits super conductivity below 2.85 K as determined from the electrical resistivity, magnetic susceptibility and heat capacity measurements. The bulk measurements indicate multiband superconductivity in this low carrier system. Hall effect measurements show that the Hall coefficient R$_H$ is positive and it decreases rapidly with temperature which is highly unusual. The simple estimation of the ca…
A connection between creation of toroidal moments and breaking of the relativistic crystalline group associated to a given crystal, is presented in this paper. Indeed, if magnetoelectric effects exist, the interaction between electrons and elementary magnetic cells appears in such a way that the resulting local polarization and magnetization break the local relativistic crystalline symmetry. Therefore, Goldstone bosons, also associated to toroidal moments, are created and, as a consequence, corresponding toroidal phases in crystals. The list of the Shubnikov groups compatible with this kind of…
We review magnetic, superconducting and non-Fermi-liquid properties of the structurally layered heavy-fermion compounds Ce$_n$M$_m$In$_{3n+2m}$ (M=Co, Rh, Ir). These properties suggest d-wave superconductivity and proximity to an antiferromagetic quantum-critical point.
The results of inelastic neutron scattering provide a solution for the crystal field level scheme in PrOs4Sb12 in which the ground state in the cubic crystal field potential of Th symmetry is a Gamma_1 singlet. The conduction electron mass enhancement is consistent with inelastic exchange scattering, and we propose that inelastic quadrupolar, or aspherical Coulomb, scattering is responsible for enhancing the superconducting transition temperature. PrOs4Sb12 appears to be the first compound in which aspherical Coulomb scattering is strong enough to overcome magnetic pair-breaking and increase T…
We systematically studied the transport properties of single crystals of $Eu_{1-x}Sr_xFe_{2-y}$Co$_{y}As_2$. Co doping can suppress the spin-density wave (SDW) ordering and induces a superconducting transition, but a resistivity reentrance due to the antiferromagnetic ordering of $Eu^{2+}$ spins is observed, indicating the competition between antiferromagnetism (AFM) and superconductivity. It is striking that the resistivity reentrance can be completely suppressed by external magnetic field (H) because a metamagnetic transition from antiferromagnetism to ferromagnetism for $Eu^{2+}$ spins is i…
The nature of spin-density wave and its relation with superconductivity are crucial issues in the newly discovered Fe-based high temperature superconductors. Particularly it is unclear whether the superconducting phase and spin density wave (SDW) are truly exclusive from each other as suggested by certain experiments. With angle resolved photoemission spectroscopy, we here report exchange splittings of the band structures in Sr1-xKxFe2As2 (x=0,0.1,0.2), and the non-rigid-band behaviors of the splitting. Our data on single crystalline superconducting samples unambiguously prove that SDW and sup…
The suppression of superconductivity by substitution effects has been measured in high quality single crystals of U(Pt_{1-x} Pd_x)_3 with 0 <= x <= 0.002. While the superconducting transition temperature T_c varies linearly with residual resistivity r_0, consistent with pair-breaking by impurity potential scattering, the rate of suppression of T_c with r_0 is much larger for Pd substitution than for other impurity substitutions or by increased defect density. This effect is correlated with an increase in the inelastic scattering coefficient, and may be related to Pd-induced changes in the magn…
BaFe2As2 is the parent compound of the '122' iron arsenide superconductors and crystallizes with the tetragonal ThCr2Si2 type structure, space group I4/mmm. A spin density wave transition at 140 K is accompanied by a symmetry reduction to space group Fmmm and simultaneously by antiferromagnetic ordering. Hole-doping induces superconductivity in Ba1-xKxFe2As2 with a maximum Tc of 38 K at x = 0.4. The upper critical fields approach 75 T with rather small anisotropy of Hc2. At low potassium concentrations (x <= 0.2), superconductivity apparently co-exists with the orthorhombic distorted and magne…
Single crystal of Lu$_2$Fe$_3$Si$_5$ was studied with the tunnel-diode resonator technique in Meissner and mixed states. Temperature dependence of the superfluid density provides strong evidence for the two-gap superconductivity with almost equal contributions from each gap of magnitudes $Δ_1/k_BT_c=1.86$ and $Δ_1/k_BT_c=0.54$. In the vortex state, pinning strength shows unusually strong temperature dependence and is non-monotonic with the magnetic field (peak effect). The irreversibility line is sharply defined and is quite distant from the $H_{c2}(T)$, which hints on to enhanced vortex fluct…
We report superconductivity in single crystals of the new iron-pnictide system BaFe1.9Pt0.1As2 grown by a self-flux solution method and characterized via x-ray, transport, magnetic and thermodynamic measurements. The magnetic ordering associated with a structural transition at 140 K present in BaFe2As2 is completely suppressed by substitution of 5% Fe with Pt and superconductivity is induced at a critical temperature Tc=23 K. Full diamagnetic screening in the magnetic susceptibility and a jump in the specific heat at Tc confirm the bulk nature of the superconducting phase. All properties of th…
High quality single crystals of UPt_3 have been prepared by vertical float-zone refining in ultra-high vacuum. We find that the superconducting transition temperature can be varied systematically by annealing, revealing that the transition temperature intrinsic to UPt_3 is 563 +/- 5 mK. The suppression of the superconducting transition from defects is consistent with a modified Abrikosov-Gor'kov formula that includes anisotropic pairing, Fermi surface anisotropy, and anisotropic scattering by defects.
We report a systematic study on the influence of antiferromagnetic and ferromagnetic phases of Eu^2+ moments on the superconducting phase upon doping the As site by isovalent P, which acts as chemical pressure on EuFe_2As_2. Bulk superconductivity with transition temperatures of 22 K and 28 K are observed for x=0.16 and 0.20 samples respectively. The Eu ions order antiferromagnetically for x<=0.13, while a crossover is observed for x>=0.22 whereupon the Eu ions order ferromagnetically. Density functional theory based calculations reproduce the observed experimental findings consistently. We di…
We observe superconductivity below a critical temperature TC = 1.8 K in single-crystal Ir3Te8, which also exhibits normal-state diamagnetism and a linear temperature dependence of electrical resistivity for a wide temperature interval, 20 K < T < 700 K. Single-crystal Ir3Te8 also undergoes a structural phase transition at TS = 350 K from a cubic (above TS) to a rhombohedral lattice below TS. Our first-principles electronic structure calculations reveal two bands crossing the Fermi level; despite the three-dimensional lattice, one band is quasi-two-dimensional, and is responsible for the observ…
High resolution measurements of the dynamic magnetic susceptibility are reported for ferromagnetic re-entrant superconductor, ErRh$_{4}$B$_{4}$. Detailed investigation of the coexisting regime reveals unusual temperature-asymmetric and magnetically anisotropic behavior. The superconducting phase appears via a series of discontinuous steps upon warming from the ferromagnetic normal phase, whereas the ferromagnetic phase develops via a gradual transition. A model based on local field inhomogeneity is proposed to explain the observations.
Superconducting behavior has been observed in the Sr2RuO4-Sr3Ru2O7 eutectic system as grown by the flux-feeding floating zone technique. A supercurrent flows across a single interface between Sr2RuO4 and Sr3Ru2O7 areas at distances that are far beyond those expected in a conventional proximity scenario. The current-voltage characteristics within the Sr3Ru2O7 macrodomain, as extracted from the eutectic, exhibit signatures of superconductivity in the bilayered ruthenate. Detailed microstructural, morphological and compositional analyses address issues on the concentration and the size of Sr2RuO4…
The complete scenario of high-Tc superconductivity based on experimental data from electron-tunneling spectroscopy on underdoped, overdoped and Ni-doped Bi2212 single crystals using a break-junction technique is presented. There are two different types of superconductivity in cuprates: superconductivity due to pairing of spinons on charged stripes and magnetic superconductivity mediated by spin-waves. The coherent state of the spinon superconductivity is established via the magnetic superconductivity. In NCCO, there is only the spinon superconductivity and the coherent state is established due…
The effects of pressure up to $\sim 20$ kbar, on the structural phase transition of lightly Sn-doped BaFe$_2$As$_2$, as well as on the superconducting transition temperature and upper critical field of (Ba$_{0.55}$K$_{0.45}$)Fe$_2$As$_2$ single crystals have been studied. Both transitions decrease with pressure in an almost linear fashion. Under pressure, the upper critical field curve, $H_{c2}(T)$, shifts down in temperature to follow the zero field $T_c$ with very little change in slope.
We studied the effect of hydrostatic pressure (P) on the structural phase transitions and superconductivity in the ternary and pseudo-ternary iron arsenides CaFe2As2, BaFe2As2, and (Ba0.55K0.45)Fe2As2, by means of measurements of electrical resistivity (rho) in the 1.8 - 300 K temperature (T) range, pressures up to 20 kbar, and magnetic fields up to 9 T. CaFe2As2 and BaFe2As2 (lightly doped with Sn) display structural phase transitions near 170 K and 85 K, respectively, and do not exhibit superconductivity in ambient pressure, while K-doped (Ba0.55K0.45)Fe2As2 is superconducting for T < 30 K. …
The multi-orbital Hubbard model in one dimension is studied using the numerical diagonalization method. Due to the effect of the crystal-field splitting $Δ$, the fully polarized ferromagnetism which is observed in the strong coupling regime becomes unstable against the partially polarized ferromagnetism when the Hund's rule coupling $J$ is smaller than a certain critical value of order of $Δ$. In the vicinity of the partially polarized ferromagnetism, the orbital fluctuation develops due to the competition between the Hund's rule coupling and the crystal-field splitting. The superconducting ph…
We have performed $^{125}$Te NMR on a single crystal of the novel layered superconductor Fe$_{1.04}$Te$_{0.67}$Se$_{0.33}$ for the first time. The spin parts of the Knight shifts for both $H // a$, $H // c$ are suppressed in the superconducting state, indicating the spin singlet superconductivity. At superconducting state, $1/T_{1}$ shows the power-law behavior ($\sim T^{3}$) without any coherent peaks. Observations of the residual density of state and the $T^{3}$-law indicate the presence of the line node in the superconducting gap. In the normal state, $1/T_{1}T$ which probes the \textbf{q}-…
We measure the superconducting transition of YIn$_3$ by resistivity, susceptibility, and specific heat. Despite using high-quality single-crystal samples, the transitions detected by the three techniques are shifted from each other in temperature, suggesting a region of filamentary superconductivity. We discuss the possible implications for filamentary superconductivity in unconventional superconductors.
We report synthesis of Co substitution at Fe site in Fe1-xCoxSe0.5Te0.5 (x=0.0 to 0.10) single crystals via vacuum shield solid state reaction route using flux free method. Single crystal XRD results showed that these crystals grow in (00l) plane i.e., orientation in c-direction. All the crystals possess tetragonal structure having P4/nmm space group. Detailed scanning electron microscopy (SEM) images show that the crystals are grown in slab-like morphology. The EDAX results revealed the final elemental composition to be near stoichiometric. Powder X-Ray diffraction (PXRD) Rietveld analysis re…
We report a doping dependant Electronic Raman Scattering (ERS) study of HgBa$_2$CuO$_{4+δ}$ (Hg-1201) single crystals. We investigate the dynamics of the antinodal and nodal quasiparticles. We show that the dynamical response of the antinodal quasiparticles is strongly reduced towards the underdoped regime in both the normal and superconducting states. When probing the nodal quasiparticles, we are able to distinguish between the energy scale of the pseudogap and that of the superconducting gap. A simple model relating the suppression of the dynamical response of the antinodal quasiparticles to…
Two-dimensional (2D) transition-metal dichalcogenide (TMDs) MoTe2 has attracted much attention due to its predicted Weyl semimetal (WSM) state and a quantum spin Hall insulator in bulk and monolayer form, respectively. We find that the superconductivity in MoTe2 single crystal can be much enhanced by the partial substitution of the Te ions by the S ones. The maximum of the superconducting temperature TC of MoTe1.8S0.2 single crystal is about 1.3 K. Compared with the parent MoTe2 single crystal (TC=0.1 K), nearly 13-fold in TC is improved in MoTe1.8S0.2 one. The superconductivity has been inves…
We report normal and superconducting properties of the Rashba-type noncentrosymmetric com- pound CaIrSi3, using single crystalline samples with nearly 100% superconducting volume fraction. The electronic density of states revealed by the hard x-ray photoemission spectroscopy can be well explained by the relativistic first-principle band calculation. This indicates that strong spin-orbit interaction indeed affects the electronic states of this compound. The obtained H - T phase diagram exhibits only approximately 10% anisotropy, indicating that the superconducting properties are almost three di…
Heat capacity, magnetic susceptibility, NMR, and resistivity of SrNi2P2 single crystals are presented, illustrating a purely structural transition at 325 K with no magnetism. Bulk superconductivity is found at 1.4 K. The magnitude of the transition temperature T_c, fits to the heat capacity data, the small upper critical field $H_{c2}$ = 390 Oe, and Ginzburg-Landau parameter $κ$ = 2.1 suggests a conventional fully gapped superconductor. With applied pressure a second structural phase transition occurs which results in an 8% reduction in the c/a ratio of lattice parameters. We find that superco…
We present superconducting properties of single crystalline Ba(Fe$_{0.9}$Co$_{0.1}$)$_{2}$As$_{2}$ by measuring magnetization, resistivity, upper critical field, Hall coefficient, and magneto-optical images. The magnetization measurements reveal fish-tail hysteresis loop at high temperatures and relatively high critical current density above $J_{c}=10^{5}$ A/cm$^{2}$ at low temperatures. Upper critical field determined by resistive transition is anisotropic with anisotropic parameter $\sim$ 3.5. Hall effect measurements indicate that Ba(Fe$_{0.9}$Co$_{0.1}$)$_{2}$As$_{2}$ is a multiband system…
We report on doping dependencies of structural parameters and superconducting transition temperatures in the solid solution (Ba1-xKx)Fe2As2. As the main effect of doping on the crystal structure, we find linear decreasing As-Fe-As bond angles and Fe-Fe distances, equivalent to an elongation of the FeAs4 tetrahedra along [001]. The structural changes are intimately coupled to the electronic states at the Fermi level, because the most relevant Fe-3dx2-y2 orbitals are strongly affected by the As-Fe-As bond angle. Superconductivity is present over the whole doping range in (Ba1-xKx)Fe2As2 with a m…
We report self flux growth and characterization of FeTe1-xSx (x= 0.00 to 0.25) single crystal series. Surface X-ray diffraction (XRD) exhibited crystalline nature with growth in (00l) plane. Micro-structural (electron microscopy) images of representative crystals showed the slab-like morphology and near stoichiometric composition. Powder XRD analysis (Rietveld) of single crystals exhibited tetragonal structure with P4/nmm space group and decreasing a and c lattice parameters with increase in x. Electrical resistivity measurements (R-T) showed superconductivity with Tconset at 9.5K and 8.5K for…
Many theoretical models of high temperature superconductivity focus only on the doping dependence of the CuO2 plane electronic structure. But such models are manifestly insufficient to explain the strong variations in superconducting critical temperature Tc among cuprates which have identical hole-density but are crystallographically different outside the CuO2 plane. A key challenge, therefore, has been to identify a predominant out-of-plane influence controlling the superconductivity - with much attention focusing on the distance $d_A$ between the apical oxygen and the planar copper atom. Her…
We have successfully observed quantum oscillation (QO) for FeTe_{1-x}Se_{x}. QO measurements were performed using non-superconducting and superconducting thin crystals of FeTe_{0.65}Se_{0.35} fabricated by the scotch-tape method. We show that the Fermi surfaces (FS) of the non-superconducting crystal are in good agreement with the rigid band shift model based on electron doping by excess Fe while that of the superconducting crystal is in good agreement with the calculated FS with no shift. From the FS comparison of both crystals, we demonstrate the change of the cross-sectional area of the FS,…
Recently a new family of Cr-based A2Cr3As3 (A = K, Rb, Cs) superconductors were reported, which own a rare quasi-one-dimensional (Q1D) crystal structure with infinite (Cr3As3)2- chains and exhibit intriguing superconducting characteristics possibly derived from spin-triplet electron pairing. The crystal structure of A2Cr3As3 is actually a slight variation of the hexagonal TlFe3Te3 prototype although they have different lattice symmetry. Here we report superconductivity in a 133-type KCr3As3 compound that belongs to the latter structure. The single crystals of KCr3As3 were prepared by the deint…
Here we report the preparation and superconductivity of the 133-type Cr-based quasi-one-dimensional (Q1D) RbCr3As3 single crystals. The samples were prepared by the deintercalation of Rb+ ions from the 233-type Rb2Cr3As3 crystals which were grown from a high-temperature solution growth method. The RbCr3As3 compound crystallizes in a centrosymmetric structure with the space group of P63/m (No. 176) different with its non-centrosymmetric Rb2Cr3As3 superconducting precursor, and the refined lattice parameters are a = 9.373(3) Å and c = 4.203(7) Å. Electrical resistivity and magnetic susceptibilit…
Mixing of spin singlet and spin triplet superconducting pairing state is expected in noncentrosymmetric superconductors (NCS) due to the inherent presence of Rashba-type antisymmetric spin-orbit coupling. Unlike low symmetry (tetragonal or monoclinic) NCS, parity is isotropicaly broken in space for cubic NCS and can additionally lead to the coexistence of magnetic and superconducting state under certain conditions. Motivated with such enriched possibility of unconventional superconducting phases in cubic NCS we are reporting successful formation of single crystalline cubic noncentrosymmetric P…
The coupling between superconductivity and othorhombic distortion is studied in vapor-grown FeSe single crystals using high-resolution thermal-expansion measurements. In contrast to the Ba122-based (Ba122) superconductors, we find that superconductivity does not reduce the orthorhombicity below Tc. Instead we find that superconductivity couples strongly to the in-plane area, which explains the large hydrostatic pressure effects. We discuss our results in light of the spinnematic scenario and argue that FeSe has many features quite different from the typical Fe-based superconductors.
We investigated the S-doping-driven phase transition from antiferromagnetic to superconducting in FeTe1-xSx single crystals. The partial substitution of Te by S suppresses antiferromagnetism in Fe-square lattice. Superconductivity is induced by oxygen annealing for only FeTe1-xSx in which the long-range magnetic ordering is suppressed. To realize superconductivity in FeTe1-xSx, both S concentration enough to suppress antiferromagnetism and oxygen annealing are required. Anisotropy of superconductivity in oxygen-annealed FeTe0.886S0.114 was estimated to be 1.17.
We report synthesis of high quality Fe1+y(Te1-xSx)z single crystals and a comprehensive study of structural, magnetic and transport properties. There is high sensitivity to material stoichiometry which includes vacancies on the Te(S) site. Our results reveal competition and coexistence of magnetic order and percolative superconductivity for x >= 0.03, while zero resistivity is acheived for x >= 0.1.
Spin-triplet superconductivity is known to be a rare quantum phenomenon. Here we show that nonsymmorphic crystalline symmetries can dramatically assist spin-triplet superconductivity in the presence of spin-orbit coupling. Even with a weak spin-orbit coupling, the spin-triplet pairing can be the leading pairing instability in a lattice with a nonsymmorphic symmetry. The underlining mechanism is the spin-sublattice-momentum lock on electronic bands that are protected by the nonsymmorphic symmetry. We use the nonsymmorphic space group P4/nmm to demonstrate these results and discuss related exper…
Resistivity, magnetic susceptibility and heat capacity measurements are reported for single crystals of Fe1+yTexSe1-x grown via a modified Bridgeman method with 0 < y < 0.15, and x= 1, 0.9, 0.75, 0. 67, 0.55 and 0.5. Although resistivity measurements show traces of superconductivity near 14 K for all x except x=1, only crystals grown with compositions near x=0.5 exhibit bulk superconductivity. The appearance of bulk superconductivity correlates with a reduction in the magnitude of the magnetic susceptibility at room temperature and smaller values of y, the concentration of Fe in the Fe(2) site…
Symmetry of the crystal lattice can be a determining factor for the structure of Cooper pairs in unconventional superconductors. In this study we extend the discussion of superconductivity in non-centrosymmetric materials to the case when inversion symmetry is missing locally, but is present on a global level. Concretely, we investigate the staggered non-centrosymmetricity within a regular sublattice structure, in some analogy to the discussion of superconductivity in antiferromagnetic systems. Three crystal structures are analyzed in detail as illustrative examples for the extended classifica…
The effect of vacuum annealing on superconductivity is investigated in Fe(Se,Te) single crystals. It is found that superconductivity is not enhanced by annealing under high vacuum (~ 10^(-3) Pa) or by annealing in a sealed evacuated quartz tube. In a moderate vacuum atmosphere (~ 1 Pa), iron oxide layers are found to show up on sample surfaces, which would draw excess Fe out of the crystal. Thus, it is suggested that remanent oxygen effectively works to remove excess Fe from the matrix of Fe(Se,Te) crystals, resulting improvement of superconducting transition temperature. Our transport measure…
The effect of Co doping on supercoductivity of FeSe$_{0.4}$Te$_{0.6}$ single crystals is investigated. The superconducting transition temperature decreases linearly for Co doping with the rate -0.75 K/(Co %). On the other hand, the residual resistivity increase is less than 50 $/mu/Omega$cm for 4 % Co doping. These data are consistent with the sign changing interband scattering mechanism of superconductivity ($s_/pm$ symmetry).
Single crystals FeSe_x have been grown in evacuated sealed quartz tube using a NaCl/KCl flux. The products include two crystal structures of tetragon and hexagon. The electronic transport and magnetic properties measurements of FeSe_x single crystal exhibits a superconducting transition at about 10K.
We investigate properties of BaFe2As2 (122) single crystals upon gold doping, which is the transition metal with the highest atomic weight. The Au substitution into the FeAs-planes of 122 crystal structure (Au-122) is only possible up to a small amount of ~3%. We find that 5d is more effective in reducing magnetism in 122 than its counter 3d Cu, and this relates to superconductivity. We provide evidence of short-range magnetic fluctuations and local-lattice inhomogeneities that may prevent strong percolative superconductivity in Ba(Fe1-xAux)2As2.
Layered transition-metal dichalcogenides 1T-TaS2-xSex (0<=x<=2) single crystals have been successfully fabricated by using a chemical vapor transport technique in which Ta locates in octahedral coordination with S and Se atoms. This is the first superconducting example by the substitution of S site, which violates an initial rule based on the fact that superconductivity merely emerges in 1T-TaS2 by applying the high pressure or substitution of Ta site. We demonstrate the appearance of a series of electronic states in 1T-TaS2-xSex with Se content. Namely, the Mott phase melts into a nearly comm…
Polycrystalline La$_{7}$Ir$_{3}$ is reported to show superconductivity breaking time-reversal symmetry while also having an isotropic $s$-wave gap. Single crystals of this noncentrosymmetric superconductor are highly desirable to understand the nature of the electron pairing mechanism in this system. Here we report the growth of high-quality single crystals of La$_{7}$Ir$_{3}$ by the Czochralski method. The structural and superconducting properties of these large crystals have been investigated using x-rays, magnetization, resistivity and heat capacity measurements. We observe a clear anisotro…
The evolution of pressure induced superconductivity in single crystal as well as polycrystalline samples of BaFe2As2 has been investigated through temperature dependent electrical resistivity studies in 0-7 GPa pressure range. While the superconducting transition remains incomplete in polycrystalline sample, a clear pressure induced superconductivity with zero resistivity at the expense of magnetic transition, associated with spin density wave (SDW), is observed in the single crystal sample. The superconducting transition temperature (TC) is seen to increase upto a moderate pressure of about ~…