Doping-insensitive density-of-states suppression in polycrystalline iron-based superconductor SmO$_{1-x}$F$_{x}$FeAs
H. W. Ou, Y. Zhang, J. F. Zhao, J. Wei, D. W. Shen, B. Zhou, L. X. Yang, F. Chen, M. Xu, C. He, R. H. Liu, M. Arita, K. Shimada, H. Namatame, M. Taniguchi, Y. C… 展开作者
H. W. Ou, Y. Zhang, J. F. Zhao, J. Wei, D. W. Shen, B. Zhou, L. X. Yang, F. Chen, M. Xu, C. He, R. H. Liu, M. Arita, K. Shimada, H. Namatame, M. Taniguchi, Y. Chen, X. H. Chen, D. L. Feng
We investigated the temperature dependence of the density-of-states in the iron-based superconductor SmO_1-xF_xFeAs (x=0, 0.12, 0.15, 0.2) with high resolution angle-integrated photoemission spectroscopy. The density-of-states suppression is observed with decreasing temperature in all samples, revealing two characteristic energy scales (10meV and 80meV). However, no obvious doping dependence is observed. We argue that the 10meV suppression is due to an anomalously doping-independent normal state pseudogap, which becomes the superconducting gap once in the superconducting state; and alert the possibility that the 80meV-scale suppression might be an artifact of the polycrystalline samples.
A series of polycrystalline SmO1-xFxFeAs bulks (x=0.15, 0.2, 0.3 and 0.4) were prepared by the conventional solid state reaction. Resistivity, susceptibility, magnetic hysteresis, critical current density and microstructure of these samples have been investigated. It is found that critical transition temperature Tc increases steadily with increasing fluorine content, with the highest onset Tc=53 K at x=0.4. On the other hand, the superconductivity seems correlated with lattice constants; that is, Tc rises with the shrinkage of a-axis while resistivity increases with the enlargement of c-axis. …
We prepared polycrystalline SmFeAsO1-xFx (Sm1111) bulk samples by sintering and hot isostatic pressing (HIP) in order to study the effects of phase purity and relative density on the intergranular current density. Sintered and HIPped Sm1111 samples are denser with fewer impurity phases, such as SmOF and the grain boundary wetting phase, FeAs. We found quite complex magnetization behavior due to variations of both the inter and intragranular current densities. Removing porosity and reducing second phase content enhanced the intergranular current density, but HIPping reduced Tc and the intragran…
We report the influence of atomic disorder introduced by sequential neutron irradiation on the basic superconducting properties, flux pinning and grain connectivity. Two different polycrystalline Sm-1111 samples (SmFeAsO_{1-x}F_x) and two Ba-122 single crystals (BaFe_{1.8}Co_{0.2}As_2) were investigated. The monotonous decrease of the transition temperature with neutron fluence degrades the upper critical field, at least in the investigated temperature region. Pinning on the other hand is largely improved, with a different optimal defect concentration (fluence) in the two materials. The analys…
We report on successful synthesis under high pressure of a series of polycrystalline GdFeAs O_{1-x}F_x high-Tc superconductors with different oxygen deficiency x=0.12 - 0.16 and also with no fluorine. We have found that the high-pressure synthesis technique is crucial for obtaining almost single-phase superconducting materials: by synthesizing the same compounds with no pressure in ampoules we obtained non-superconducting materials with an admixture of incidental phases. Critical temperature for all the materials was in the range 40 to 53K. The temperature derivative of the critical field dHc2…
We report far-infrared reflectance measurements on polycrystalline superconducting samples of SmO$_{1-x}$F$_{x}$FeAs ($x$ = 0.12, 0.15 and 0.2). We clearly observe superconductivity induced changes of reflectivity in a broad range of energies, which resembles earlier optical measurements on high $T_{c}$ cuprates. The superconducting-to-normal reflectivity ratio $R_{s}/R_{n}$ grows for the photon energies below 18 meV and shows a complicated structure due to the presence of a strong infrared-active phonon at about 10 meV.
The electronic structure of the new superconductor, SmO$_{1-x}$F$_x$FeAs ($x=0.15$), has been studied by angle-integrated photoemission spectroscopy. Our data show a sharp feature very close to the Fermi energy, and a relative flat distribution of the density of states between 0.5 eV and 3 eV binding energy, which agrees best with band structure calculations considering an antiferromagnetic ground state. No noticeable gap opening was observed at 12 Kelvin below the superconducting transition temperature, indicating the existence of large ungapped regions in the Brillouin zone.
Raman spectra of polycrystalline NdFeAsO1-xFx (x=0.0, 0.1, 0.2) compound have been systematically investigated as functions of temperature and fluorine concentration. Scanning electron microscopic and Raman microscopic characterization demonstrates that the polycrystalline samples mainly contain two phases, i.e. superconductor NdFeAsO1-xFx compound and a MnP-type FeAs phase, with dissimilar characteristic Raman bands. It was found that fluorine doping leads to structure disorder in the insulator Nd-O layers and high temperature coefficient of Fe-As vibrational mode.
We have studied current-voltage characteristics of Andreev contacts in polycrystalline GdO$_{0.88}$F$_{0.12}$FeAs samples with bulk critical temperature ${T_c}$ = (52.5 \pm 1)K using break-junction technique. The data obtained cannot be described within the single-gap approach and suggests the existence of a multi-gap superconductivity in this compound. The large and small superconducting gap values estimated at T = 4.2K are ΔL = 10.5 \pm 2 meV and ΔS = 2.3 \pm 0.4 meV, respectively.
We report superconductivity in polycrystalline samples of the 1038-type compounds (Ca$_{1-x}$RE$_x$)$_{10}$(FeAs)$_{10}$(Pt$_3$As$_8$) up to T$_c$ = 35 K with RE = Y, La-Nd, Sm, Gd-Lu. The critical temperatures are independent of the trivalent rare earth element used, yielding an universal T$_c$($x$) phase diagram for electron doping in all these systems. The absence of superconductivity in Eu$^{2+}$ doped samples, as well as the close resemblance of (Ca$_{1-x}$RE$_x$)$_{10}$(FeAs)$_{10}$(Pt$_3$As$_8$) to the 1048 compound substantiate that the electron doping scenario in the RE-1038 and 1048 …
The specific heat $C(T)$ of new iron-based high-$T_c$ superconductor SmO$_{1-x}$F$_x$FeAs ($0 \leq x \leq 0.2$) was systematically studied. For undoped $x$ = 0 sample, a specific heat jump was observed at 130 K. This is attributed to the structural or spin-density-wave (SDW) transition, which also manifests on resistivity as a rapid drop. However, this jump disappears with slight F doping in $x$ = 0.05 sample, although the resistivity drop still exists. The specific heat $C/T$ shows clear anomaly near $T_c$ for $x$ = 0.15 and 0.20 superconducting samples. Such anomaly has been absent in LaO$_{…
Superconducting properties of Co-co-doped (Ca,RE)FeAs2 ((Ca,RE)112: RE = La, Pr) were investigated. Co-co-doping increased Tc of (Ca,Pr)112 while Mn-co-doping suppressed superconductivity of (Ca,RE)112. Co-co-doped (Ca,La)112 showed large diamagnetic screening and sharper superconducting transition than Co-free (Ca,La)112. Tczero observed in resistivity measurements increased from 14 K to 30 K by Co-co-doping, while Tconset was not increased. The critical current density (Jc) of Co-co-doped (Ca,La)112 were approximately 2.1 x 104 Acm-2 and 3.2 x 103 Acm-2 at 2 K and 25 K, respectively, near ze…
Current-voltage characteristics and dynamic conductance of the superconductor - constriction - superconductor junctions in GdO(F)FeAs polycrystalline samples with critical temperatures Tc^local = 46 - 53 K were investigated. Two superconducting gaps, the large Delta_L = 10.5 +- 2 meV, and the small one Delta_S = 2.3 +- 0.4 meV were clearly observed at T = 4.2 K. The 2Delta_L/kTc^local = 5.5 +- 1 ratio gives support to the strong coupling mechanism which is responsible for the high Tc value. Temperature dependence of the large gap Delta_L(T) indicates the presence of intrinsic proximity effect …
Polycrystalline samples of RO1-xFxFeAs (0 < x < 0.25) (R = La, Sm, Gd) were investigated by wavelength-dispersive X-ray spectroscopy (WDX) in the electron microscope to determine the composition of the samples, in particular the fluorine content. It was found that the measured fluorine content can deviate considerably from the initial weight. In the lanthanum compound LaO1-xFxFeAs, we found good agreement mainly for x > 0.05, but for x < 0.05 the fluorine hardly goes into the sample. For the samarium compound we measured less than half the fluorine in the sample as initially weighed at all flu…
Polycrystalline samples of Sr2Mn2CuAs2O2, Sr2Mn3As2O2, and Sr2Zn2MnAs2O2 were synthesized. Their temperature- and applied magnetic field-dependent structural, transport, thermal, and magnetic properties were characterized by means of x-ray and neutron diffraction, electrical resistivity rho, heat capacity, magnetization and magnetic susceptibility measurements. These compounds have a body-centered-tetragonal crystal structure (space group I4/mmm) that consists of MO2 (M = Zn and/or Mn) oxide layers similar to the CuO2 layers in high superconducting transition temperature Tc cuprate superconduc…
In two recent articles (cond-mat/0606177 and arXiv:0804.1615), we have suggested a unified theory of superconductivity based on the real-space spin-parallel electron pairing and superconducting mechanism and have shown that the stable hexagonal and tetragonal vortex lattices (the optimal doping phases) can be expected in the newly discovered LaO{1-x}F{x}FeAs (x0=1/7=0.1428) and SmO{1-x}F{x}FeAs (x0=1/6=0.1667), respectively. In this paper, we present a theoretical study of the effects of hydrostatic and anisotropic pressure on the superconducting transition temperature Tc of the Fe-based layer…
Polycrystalline Sr1-xNdxFeAsF samples were prepared at various Nd-doping levels using both a stoichiometric mixture of the starting materials and in slight excess amounts of FeAs. Susceptibility and resistivity of the samples were studied down to 4 K revealing a probable coexistence of superconductivity and a magnetic ordering. Temperature dependence of resistivity for all the Nd-doped samples shows the presence of a transition below 15 K most likely originating from the magnetic ordering of Nd moments, while the spin-density-wave anomaly at 175 K survives up to 0.35 Nd-doping. Superconductivi…
The densities of the valence and conduction band electronic states of the newly discovered layered superconductors LaOFeAs, LaO$_{0.87}$F$_{0.13}$FeAs (Tc=26 K), SmO$_{0.95}$F$_{0.05}$FeAs and SmO$_{0.85}$F$_{0.15}$FeAs (Tc=43 K) are studied using soft X-ray absorption and emission spectroscopy combined with FP LAPW calculations of LaOFeAs, LaO$_{0.875}$FeAs and LaO$_{0.875}$F${0.125}$FeAs. The Fe 3d-states are localized in energy near the top of the valence band and are partially hybridized with p-type O (2p), As (4p), and La (6p) states approximately 3 eV below the Fermi energy. The Fe L3 X-…
The study of excess conductivity $σ'(T)$ in the textured polycrystalline FeAs-based superconductor $EuFeAsO_{0.85}F_{0.15}$ ($T_c = 11\, K$) prepared by the solid state synthesis is reported. The $σ'(T)$ analysis has been performed within the Local Pair (LP) model based on the assumption of the LP formation in cuprate high-$T_c$ superconductors (cuprates) below the pseudogap (PG) temperature $T^*\gg T_c$. Similarly to the cuprates, near $T_c$ $σ'(T)$ is adequately described by the 3D term of the Aslamasov-Larkin (AL) theory but the range of the 3D-AL fluctuations, $ΔT_{3D}$, is relatively shor…
High resolution photoemission measurements have been carried out on non-superconducting SmOFeAs parent compound and superconducting Sm(O$_{1-x}$F$_x$)FeAs (x=0.12, and 0.15) compounds. The momentum-integrated spectra exhibit a clear Fermi cutoff that shows little leading-edge shift in the superconducting state which suggests the Fermi surface sheet(s) around the $Γ$ point may not be gapped in this multiband superconductors. A robust feature at 13 meV is identified in all these samples. Spectral weight suppression near E$_F$ with decreasing temperature is observed in both undoped and doped samp…
The recent discovery of iron-based superconductors challenges the existing paradigm of high-temperature superconductivity. Owing to their unusual multi-orbital band structure, magnetism, and electron correlation, theories propose a unique sign reversed s-wave pairing state, with the order parameter changing sign between the electron and hole Fermi pockets. However, because of the complex Fermi surface topology and material related issues, the predicted sign reversal remains unconfirmed. Here we report a novel phase-sensitive technique for probing unconventional pairing symmetry in the polycrys…
Using the "break-junction" technique we prepared and studied superconductor - constriction - superconductor nanocontacts in polycrystalline samples of Fe-based superconductors CeO$_{0.88}$F$_{0.12}$FeAs (Ce-1111; $T_C^{\rm bulk} = 41 \pm 1 K$), LaO$_{0.9}$F$_{0.1}$FeAs (La-1111; $T_C^{\rm bulk} = 28 \pm 1 K$), and FeSe ($T_C^{\rm bulk} = 12 \pm 1 K$). We detected two subharmonic gap structures related with multiple Andreev reflections, indicating the presence of two superconducting gaps with the BCS-ratios $2Δ_L/k_BT_C = 4.2 ÷5.9$ and $2Δ_S/k_BT_C\sim 1 \ll 3.52$, respectively. Temperature dep…
Low temperature specific heat (SH) was measured on the FeAs-based superconducting single crystals Ba$_{0.6}$K$_{0.4}$Fe$_2$As$_2$ and high pressure synthesized polycrystalline samples SmFeAsO$_{0.9}$F$_{0.1}$. It is found that the sharp SH anomaly $ΔC/T|_{T_c}$ in Ba$_{0.6}$K$_{0.4}$Fe$_2$As$_2$ reaches an unexpected high value of 98 mJ/mol K$^2$, about one order of magnitude larger than that of SmFeAsO$_{0.9}$F$_{0.1}$ ($6\sim8$ mJ/mol K$^2$) samples, suggesting very high normal state quasiparticle density of states in FeAs-122 than in FeAs-1111. Furthermore, we found that the electronic SH c…
Temperature dependent resistivity of the iron-based superconductor NdFeAsO0.88F0.12 was measured under different applied fields and excitation currents. Arrhenius plot shows an anomalous tail effect, which contains obvious two resistivity dropping stages. The first is caused by the normal superconducting transition, and the second is supposed to be related to the weak-link between the grains. A model for the resistivity dropping related to the weak-link behavior is proposed, which is based on the Josephson junctions formed by the impurities in grain boundaries like FeAs, Sm2O3 and cracks toget…
The effect of atomic disorder induced by neutron irradiation on the crystal structure and electronic states near $E_F$ of the lightly overdoped LaFeAsO$_{0.85}$F$_{0.15}$ ($T_c=21K$) was studied by X-ray diffraction and $^{75}$As NMR. The irradiation of the polycrystalline sample by "moderate" neutron fluence of $Φ=(0;0.5;1.6)\cdot10^{19}cm^{-2}$ at $T=50^{\circ}C$ leads to the suppression of superconductivity. It is shown that neutron irradiation produces an anisotropic expansion of the tetragonal lattice almost due to an increase of the Fe-As distance. A partial loss of the 2D character of t…
We have investigated the fluorine-doping dependence of lattice constants, transports and specific heat for polycrystalline LaFePO1-xFx. F doping slightly and monotonically decreases the in-plane lattice parameter. In the normal state, electrical resistivity at low temperature is proportional to the square of temperature and the electronic specific heat coefficient has large value, indicating the existence of moderate electron-electron correlation in this system. Hall coefficient has large magnitude, and shows large temperature dependence, indicating the low carrier density and multiple carrier…