Dynamic radiative cooling with variable emissive power is experimentally demonstrated in this study by a wavelength-selective tunable metafilm emitter, which consists of an opaque aluminum film, a sputtered silicon spacer, and a thermochromic vanadium dioxide (VO2) layer fabricated by a furnace oxidation method. The temperature-dependent spectral emittance, experimentally obtained from spectral reflectance measurements, clearly shows a pronounced emission peak around 10 um wavelength when the VO2 experiences an insulator-to-metal phase transition near 65C. The tunable metafilm emitter achieves a significant total emittance increase from 0.14 at room temperature to 0.6 at 100C. Theoretical modeling based on thin-film optics indicates that the emission enhancement at high temperatures is realized by Fabry-Perot cavity resonance with the metallic VO2 film. Moreover, a calorimetry-based thermal vacuum experiment was conducted and the enhanced thermal emission of the fabricated tunable metafilm sample was experimentally demonstrated at temperatures higher than the phase transition temperature, compared to black, aluminum and doped silicon samples, whose emittance changes little near room temperatures. The developed tunable metafilm emitter with variable spectrally-selective emittance in the mid-infrared holds great promise for both terrestrial and extraterrestrial dynamic radiative cooling applications.
We present an electro-optic modulator exploiting an array of Vanadium dioxide nanorods operating in the epsilon near regime as the active switching material integrated in a silicon waveguide. The modulator takes advantage of the insulator-to-metal transition of Vanadium dioxide to achieve a robust modulation depth of 19.7 dB/micron with a broad wavelength of operation. Using simulations, we demonstrate how the effective permittivity of the metamaterial can be tuned to a near-zero value by varying the nanorod geometry. The paper also proposes a novel hexagonal array design which achieves low in…
We demonstrate the broadband operation of a switchable terahertz quarter-wave plate achieved with an active metasurface employing vanadium dioxide. For this purpose, we utilize anisotropically deformed checkerboard structures, which present broadband characteristics compatible with deep modulation. Moreover, the metasurface is integrated with a current injection circuit to achieve state switching; this injection circuit can also be employed to monitor the electric state of vanadium dioxide. We estimate the Stokes parameters derived from the experimental transmission spectra of the fabricated m…
We present a plasmonic modulator based on hybrid orthogonal silver junctions using vanadium dioxide as the modulating material on the silicon on insulator. The modulator has an ultra-compact footprint of 1.8μm x 1μm with a 100nm x 100nm modulating section based on the orthogonal geometry. We take advantage of large change in the refractive index of vanadium dioxide during its phase transition to achieve a high modulation depth of 46.89dB/μm. We also provide a fabrication strategy for the development of this device. The device geometry has potential applications in the development of next gener…
We present an experimental demonstration of passive, dynamic thermal regulation in a solid-state system with temperature-dependent thermal emissivity switching. We achieve this effect using a multilayered device, comprised of a vanadium dioxide (VO2) thin film on a silicon substrate with a gold back reflector. We experimentally characterize the optical properties of the VO2 film and use the results to optimize device design. Using a calibrated, transient calorimetry experiment we directly measure the temperature fluctuations arising from a time-varying heat load. Under laboratory conditions, w…
A limiting optical diode is an asymmetric nonlinear device that is bidirectionally transparent at low power, but becomes opaque when illuminated by sufficiently intense light incident from a particular direction. We explore the use of a phase-transition material, vanadium dioxide (VO2), as an active element of limiting optical diodes. The VO2 phase transition can be triggered by optical absorption, resulting in a change in refractive index orders of magnitude larger than what can be achieved with conventional nonlinearities. As a result, a limiting optical diode based on incident-direction-dep…
High performance metasurfaces for thermal radiative cooling applications can be identified using computational optimization methods. This work has identified an easy-to-fabricate temperature phase transition VO2 nanowire array laid atop dielectric BaF2 Fabry-Perot cavity-on-metal with total coating thickness of 2 um. This optimized structure has ability to self-adaptively switch between high reflectance at low temperature to high emissivity at high temperature in the broad thermal infrared spectrum. This design demonstrates exceptional turn-down figure-of-merit compared to previously realized …
We conceptualized three-array scalable metasurfaces comprising only three thin strip grids and numerically demonstrated their characteristics in the mid-infrared spectral regime for switchable polarization manipulation and related asymmetric diodelike transmission (AT). A few or all of the grids were taken to be made of VO$_2$, a phase-change material. For each proposed metasurface, two effective structures and, therefore, two different functionalities exist, corresponding to the metallic and insulating phases of VO$_2$. The achieved scenarios of functionality switching that depend on the VO$_…
Resonant optical phased arrays are a promising way to reach fully reconfigurable metasurfaces in the optical and NIR regimes with low energy consumption, low footprint and high reliability. Continuously tunable resonant structures suffer from inherent drawbacks such as low phase range, amplitude-phase correlation or extreme sensitivity that makes precise control at the individual element level very challenging. In order to bypass these issues, we use 1-bit (binary) control for beam steering for an innovative nano-resonator antenna and explore the theoretical capabilities of such phased arrays.…
One route to create tunable metamaterials is through integration with "on-demand" dynamic quantum materials, such as vanadium dioxide (VO2). This enables new modalities to create high performance devices for historically challenging applications. Indeed, dynamic materials have often been integrated with metamaterials to imbue artificial structures with some degree of tunability. Conversely, metamaterials can be used to enhance and extend the natural tuning range of dynamic materials. Utilizing a complementary split ring resonator array deposited on a VO2 film, we demonstrate enhanced terahertz…
Abstract: An induced-transmission filter (ITF) uses an ultrathin layer of metal positioned at an electric-field node within a dielectric thin-film bandpass filter to select one transmission band while suppressing other transmission bands that would have been present without the metal layer. Here, we introduce a switchable mid-infrared ITF where the metal film can be "switched on and off", enabling the modulation of the filter response from single-band to multiband. The switching is enabled by a deeply subwavelength film of vanadium dioxide (VO2), which undergoes a reversible insulator-to-metal…
Tuning of Localized Surface Plasmons in Vanadium Dioxide Nanoparticles via Size and Insulator-Metal Transition
Brno University of Technology（布尔诺理工大学）；Central European Institute of Technology（中欧技术研究所）；Center for Nanophase Materials Sciences, Oak Ridge National Laboratory（橡树岭国家实验室纳米材料科学中心）
This paper proposes a reconfigurable planar metamaterial that can be switched between capacitive and inductive responses using local changes in the electrical conductivity of its constituent material. The proposed device is based on Babinet's principle and exploits the singular electromagnetic responses of metallic checkerboard structures, which are dependent on the local electrical conductivity. Utilizing the heating-induced metal-insulator transition of vanadium dioxide ($\mathrm{VO}_2$), the proposed metamaterial is designed to compensate for the effect of the substrate and is experimentall…
The insulator-to-metal transition (IMT) in vanadium dioxide (VO2) can enable a variety of optics applications, including switching and modulation, optical limiting, and tuning of optical resonators. Despite the widespread interest in optics, the optical properties of VO2 across its IMT are scattered throughout the literature, and are not available in some wavelength regions. We characterized the complex refractive index of VO2 thin films across the IMT for free-space wavelengths from 300 nm to 30 μm, using broadband spectroscopic ellipsometry, reflection spectroscopy, and the application of ef…
We address the propagation of laser beams in Si02-VO2 nanocomposite waveguides with thermo-optical nonlinearity. We show that the large modifications of the absorption coefficient as well as notable changes of refractive index of VO2 nanoparticles embedded into the SiO2 host media that accompany the semiconductor-to-metal phase transition may lead to optical limiting in the near-infrared wave range.
Sub-milliwatt threshold power and tunable-bias all-optical nonlinear activation function using vanadium dioxide for wavelength-division multiplexing photonic neural networks
Subwavelength modulators play an indispensable role in integrated photonic-electronic circuits. Due to weak light-matter interactions, it is always a challenge to develop a modulator with a nanometer scale footprint, low switching energy, low insertion loss and large modulation depth. In this paper, we propose the design of a vanadium dioxide dual-mode plasmonic waveguide electroabsorption modulator using a metal-insulator-VO$_2$-insulator-metal (MIVIM) waveguide platform. By varying the index of vanadium dioxide, the modulator can route plasmonic waves through the low-loss dielectric insulato…
We experimentally demonstrate that a thin (~150 nm) film of vanadium dioxide (VO2) deposited on sapphire has an anomalous thermal emittance profile when heated, which arises due to the optical interaction between the film and the substrate when the VO2 is at an intermediate state of its insulator-metal transition (IMT). Within the IMT region, the VO2 film comprises nanoscale islands of metal- and dielectric-phase, and can thus be viewed as a natural, disordered metamaterial. This structure displays "perfect" blackbody-like thermal emissivity over a narrow wavelength range (~40 cm-1), surpassin…
We propose and analyze theoretically an approach for realizing a tunable optical phased-array antenna utilizing the properties of VO2 for electronic beam steering applications in the near-IR spectral range. The device is based on a 1D array of slot nano-antennas engraved in a thin Au film grown over VO2 layer. The tuning is obtained by inducing a temperature gradient over the device, which changes the refractive index of the VO2, and hence modifies the phase response of the elements comprising the array, by producing a thermal gradient within the underlying PCM layer. Using a 10-element array,…
Vanadium dioxide (VO2) transforms from purely monoclinic to purely tetragonal on being heated from 58 deg C to 72 deg C, the transformation being reversible but hysteretic. Electromagnetically, VO2 transforms from a dissipative dielectric to another dissipative dielectric if the free-space wavelength is less than 1100 nm, but from a dissipative dielectric to a plasmonic metal (or vice versa) if the free-space wavelength exceeds 1100 nm. Calculating the extinction, total scattering, absorption, radiation-pressure, back-scattering, and forward-scattering efficiencies of a VO2 sphere, we found cl…
Surface plasmon polaritons can substantially reduce the sizes of optical devices, since they can concentrate light to (sub)wavelength scales. However, (sub)wavelength-scale electro-optic plasmonic switches or modulators with high efficiency, low insertion loss, and high extinction ratios remain a challenge due to their small active volumes. Here, we use the insulator-metal phase transition of a correlated-electron material, vanadium dioxide, to overcome this limitation and demonstrate compact, broadband, and efficient plasmonic switches with integrated electrical control. The devices are micro…
Nonlinear spectroscopy in the extreme ultraviolet (EUV) and soft x-ray spectral range offers the opportunity for element selective probing of ultrafast dynamics using core-valence transitions (Mukamel et al., Acc. Chem. Res. 42, 553 (2009)). We demonstrate a step on this path showing core-valence sensitivity in transient grating spectroscopy with EUV probing. We study the optically induced insulator-to-metal transition (IMT) of a VO2 film with EUV diffraction from the optically excited sample. The VO2 exhibits a change in the 3p-3d resonance of V accompanied by an acoustic response. Due to the…
We use apertureless scattering near-field optical microscopy (SNOM) to investigate the nanoscale optical response of vanadium dioxide (VO2) thin films through a temperature-induced insulator-to-metal transition (IMT). We compare images of the transition at both mid-infrared (MIR) and terahertz (THz) frequencies, using a custom-built broadband THz-SNOM compatible with both cryogenic and elevated temperatures. We observe that the character of spatial inhomogeneities in the VO2 film strongly depends on the probing frequency. In addition, we find that individual insulating (or metallic) domains ha…
Phase transition materials are promising for realization of switchable optics. In this work, we show reflectance resonances in the near-infrared and long-wave infrared wavelengths in highly subwavelength partially oxidized Vanadium thin films. These partially oxidized films consist of a multilayer of Vanadium dioxide and Vanadium as shown using Raman spectroscopy and four-probe measurements. As Vanadium dioxide is a phase transition material that shows insulator to metal phase transition at 68 C, the observed infra-red resonances can be switched with temperature into a high-reflectance state. …
We demonstrate spatial modification of the optical properties of thin-film metal oxides, zinc oxide and vanadium dioxide as representatives, using a commercial focused ion beam (FIB) system. Using a Ga+ FIB and thermal annealing, we demonstrated variable doping of a band semiconductor, zinc oxide (ZnO), achieving carrier concentrations from 10^18 cm-3 to 10^20 cm-3. Using the same FIB without subsequent thermal annealing, we defect-engineered a correlated semiconductor, vanadium dioxide (VO2), locally modifying its insulator-to-metal transition (IMT) temperature by range of ~25 degrees C. Such…
Vanadium Dioxide (VO2) is a strongly correlated material, which exhibits insulator to metal transition at ~68 C along with large resistivity and infrared optical reflectance modulation. In this work, we use atmospheric pressure thermal oxidation of Vanadium to synthesize VO2 films on glass and ITO coated glass substrates. With the optimized short oxidation durations of 2 min and 4 min, the synthesized VO2 film shows high optical reflectance switching in long-wavelength infrared on glass substrates and mid-wavelength infrared on ITO coated glass substrates, respectively. Peak reflectance switch…
Vanadium dioxide (VO2) as a phase-change material controls the transferred heat during phase transition process between metal and insulator states. At temperature above 68C, the rutile structure VO2 keeps the heat out and increases the IR radiation reflectivity, while at the lower temperature the monoclinic structure VO2 acts as the transparent material and increase the transmission radiation. In this paper, we first present the metal-insulator phase transition (MIT) of the VO2 in high and low temperatures. Then we simulate the meta-surface VO2 of metamaterial reflector by Ansys HFSS to show t…
We present the model of an ultrasensitive mid-infrared (mid-IR) photodetector operating in the mid-wavelength infrared (MWIR) and long-wavelength infrared (LWIR) domains consisting of a hybrid heterostructure made of nanopatterned graphene (NPG) and vanadium dioxide (VO$_2$) which exhibits a large responsivity of $R\sim 10^4$ V/W, a detectivity exceeding $D^*\sim 10^{10}$ J, and a sensitivity in terms of noise-equivalent power $\mathrm{NEP}\sim 100$ fW/$\sqrt{\rm Hz}$ close to room temperature by taking advantage of the phase change of a thin VO$_2$ film. Our proposed photodetector can reach a…
Vanadium dioxide (VO2) is one of the most promising materials for developing hybrid photonic integrated devices (PICs). However, despite switching times as low as a few femtoseconds have been reported, the all-optical temporal dynamics of VO2 embedded in a waveguide using an in-plane optical signal remain still hidden. Here, we experimentally investigate this behavior in hybrid VO2/Si waveguides by using pump-probe measurements at telecom wavelengths. Our results show switching times in the micro and nanosecond range, suggesting that the phase transition is triggered thermally from the light a…
Recently, metalenses which consist of metasurface arrays, have attracted attention due to their more condensed size in comparison with conventional lenses. In this paper, we propose a reconfigurable coding metasurface hybridized with vanadium dioxide (VO2) for wavefront manipulation at terahertz (THz) frequencies. At room temperature, the unit-cell can reflect as a "1" bit under linearly y polarized illuminated waves. Besides, when the temperature is increased, VO2 would be in a fully metallic state; therefore, unit-cell can act as a "0" reflection phase. Furthermore, by changing the unit-cell…
We propose a mechanism to substantially rectify radiative heat flow by matching thin films of metal-to-insulator transition materials and polar dielectrics in the electromagnetic near field. By leveraging the distinct scaling behaviors of the local density of states with film thickness for metals and insulators, we theoretically achieve rectification ratios over 140-a 10-fold improvement over the state of the art-with nanofilms of vanadium dioxide and cubic boron nitride in the parallel-plane geometry at experimentally feasible gap sizes (~100 nm). Our rational design offers relative ease of f…
We study terahertz transmission through nano-patterned vanadium dioxide thin film. It is found that the patterning allows the lowering of the apparent transition temperature. For the case of the smallest width nano antennas, the transition temperature is lower by as many as ten degrees relative to the bare film, so that the nano patterned hysteresis curves completely separate themselves from their bare film counterparts. This early transition comes from the one order of magnitude enhanced effective dielectric constants by nano antennas. This phenomenon opens up the possibility of transition te…
In this work, we report the design of a wavelength-tunable infrared metamaterial by exciting magnetic resonance with phase transition of vanadium dioxide (VO2). Numerical simulation shows a broad absorption peak at the wavelength of 10.9 um when VO2 is a metal, but it shifts to 15.1 um when VO2 changes to dielectric phase below its phase transition temperature of 68degC. The large tunability of 38.5% in the resonance wavelength stems from the different excitation conditions of magnetic resonance assisted by plasmon in metallic VO2 but optical phonons in dielectric VO2. The physical mechanism i…