We describe a method for scalable synthesis of epoxy composites with graphene and few-layer graphene fillers, and report on the electromagnetic interference (EMI) shielding and thermal properties of such composites at elevated temperatures. The tested materials reveal excellent total EMI shielding of ~65 dB (~105 dB) at a thickness of 1 mm(~2 mm) in the X-band frequency range of f=8.2 GHz - 12.4 GHz. The room-temperature cross-plane thermal conductivity of the composite with ~19.5 vol.% of fillers was determined to be ~11.2 W/mK, which is a factor of x41 larger than that of the pristine epoxy. Interestingly, the EMI shielding efficiency improves further as the temperature increases to 520 K while the thermal conductivity remains approximately constant. The excellent EMI shielding and heat conduction characteristics of such multifunctional graphene composites at elevated temperatures are promising for packaging applications of microwave components where EMI shielding and thermal management are important design considerations.
We report on the investigation of thermal transport in non-cured silicone composites with graphene fillers of different lateral dimensions. Graphene fillers are comprised of few-layer graphene flakes with lateral sizes in the range from 400 nm to 1200 nm and number of atomic planes from one to ~100. The distribution of the lateral dimensions and thicknesses of graphene fillers has been determined via atomic force microscopy statistics. It was found that in the examined range of the lateral dimensions the thermal conductivity of the composites increases with the increasing size of the graphene …
Natural fibers composites are considered as sustainable alternative to synthetic composites due to their environmental and economic benefits. However, they suffer from poor mechanical and interfacial properties due to a random fiber orientation and weak fiber-matrix interface. Here we report nano-engineered graphene-based natural jute fiber preforms with a new fiber architecture (NFA) which significantly improves their properties and performances. Our graphene-based NFA of jute fiber perform enhances Young modulus of jute-epoxy composites by ~324% and tensile strength by ~110% more than untrea…
Inkjet-printed wearable electronic textiles (e-textiles) are considered to be very promising due to excellent processing and environmental benefits offered by digital fabrication technique. Inkjet-printing of conductive metallic inks such as silver (Ag) nanoparticles (NPs) are well-established and that of graphene-based inks is of great interest due to multi-functional properties of graphene-based materials. However, poor ink stability at higher graphene concentration and the cost associated with the higher Ag loading in metal inks have limited their wider use. Moreover, graphene-based e-texti…
Accumulative Roll Bonding(ARB) process was used to develop few-layer graphene nano platelets reinforced aluminum matrix (GNPs/Al) composite in the form of sheets. Annealed Al sheets were ARB processed up to 6 pass along with coating of graphene between stacked sheets in first and second pass. Another set was prepared with same process parameter in the absence of graphene coating. Properties of these two set of samples were analyzed on the basis of film theory of ARB process which enables micro-level mixing of material on stacked layer interface. Hence the problem of graphene agglomeration was …
We demonstrate that polymer composites with a low loading of graphene, below 1.2 wt. %, are efficient as electromagnetic absorbers in the THz frequency range. The epoxy-based graphene composites were tested at frequencies from 0.25 THz to 4 THz, revealing total shielding effectiveness of 85 dB (1 mm thickness) with graphene loading of 1.2 wt. % at the frequency f=1.6 THz. The THz radiation is mostly blocked by absorption rather than reflection. The efficiency of the THz radiation shielding by the lightweight, electrically insulating composites, increases with increasing frequency. Our results …
In this work, we demonstrate that edge-oxidation of graphene can enable larger enhancement in thermal conductivity (k) of graphene-nanoplatelet (GnP)/polyetherimide (PEI) composites relative to oxidation of the basal plane of graphene. Edge oxidation (EGO) offers the advantage of leaving the basal plane of graphene intact, preserving its high in-plane thermal conductivity (kin > 2000 Wm-1K-1), while, simultaneously, the oxygen groups introduced on graphene edge enhance interfacial thermal conductance through hydrogen bonding with oxygen groups of polyetherimide (PEI), enhancing overall polymer…
The thermal properties of an epoxy-based binary composites comprised of graphene and copper nanoparticles are reported. It is found that the "synergistic" filler effect, revealed as a strong enhancement of the thermal conductivity of composites with the size-dissimilar fillers, has a well-defined filler loading threshold. The thermal conductivity of composites with a moderate graphene concentration of ~15 wt% exhibits an abrupt increase as the loading of copper nanoparticles approaches ~40 wt%, followed by saturation. The effect is attributed to intercalation of spherical copper nanoparticles …
This study investigates the prospect of using reduced graphene oxide encapsulated between thin wood membranes as a composite filter for water filtration. Graphene oxide (GO) with a volume range of 0.2 to 0.5 mL was deposited on a 95 mm2 area of thin sheets of Balsa wood with a thickness range of 2.20 - 3.50 mm. The dried GO deposits were laser treated in reduced oxygen environment to prepare a reduced graphene oxide-wood composite (rGO-wood). The rGO substrate of the composite was sandwiched between 2 wood sheets which were glued using polydimethylsiloxane (PDMS) to give a stable membrane. Fab…
Proximity-induced magnetism (PIM) in graphene (Gr) adjacent to magnetic specimen has raised great fundamental interests. The subject is under debate and yet no application is proposed and granted. In this paper, toward accomplishment of fundamental facts, we first explore the effect of particle size and clustering in the PIM in Gr nanoplates (GNPs)/yttrium iron garnet (YIG) magnetic nanoparticle (MNP) composite. Microscopic analyzes suggest that fine MNPs distributed uniformly on the GNPs have higher saturation magnetization due to the PIM in Gr. We propose that such magnetic plates can thus b…
We report on the synthesis of the epoxy-based composites with graphene fillers and testing their electromagnetic shielding efficiency by the quasi-optic free-space method in the extremely high frequency (EHF) band (220 - 325 GHz). The curing adhesive composites were produced by a scalable technique with a mixture of single-layer and few-layer graphene layers of a few-micron lateral dimensions. It was found that the electromagnetic transmission, T, is low even at small concentrations of graphene fillers: T<1% at frequency of 300 GHz for a composite with only 1 wt% of graphene. The main shieldin…
We report on the synthesis and characterization of the epoxy-based composites with the few-layer graphene fillers, which are capable of the duel functional applications. It was found that composites with the certain types of few-layer graphene fillers reveal an efficient total electromagnetic interference shielding, SE~45 dB, in the important X-band frequency range, f=8.2 GHz - 12.4 GHz, while simultaneously providing the high thermal conductivity, K = 8 W/mK, which is a factor of x35 larger than that of the base matrix material. The efficiency of the dual functional application depends on the…
Institute for Basic Science (IBS)（韩国基础科学研究院）；University of Trento（特伦托大学）；Queen Mary University of London（伦敦玛丽女王大学）；Ulsan National Institute of Science and Technology (UNIST)（蔚山科学技术院）
We report on the thermal and electrical properties of hybrid epoxy composites with graphene and boron nitride fillers. The thicknesses, lateral dimensions, and aspect ratios of each filler material were intentionally selected for geometric similarity to one another, in contrast to prior studies that utilized dissimilar filler geometries to achieve a "synergistic" effect. We demonstrate that the electrically-conductive graphene and electrically-insulating boron nitride fillers allow one to effectively engineer the thermal and electrical conductivities of their resulting composites. By varying t…
Graphite has been one of the promising materials in diverse application domains owing to its high conductivity, tunability into different structures and mechanical strength its. The effectiveness of graphite and its derivatives has been studied for electromagnetic domains as well. Pencil strokes on paper create a film of graphite composites which is reported to be useful for fabrication of electronic components. In our study, we extend use of pencil traces on paper for studying its electromagnetic properties. The pencil traces on paper is facile method of coating graphite composite films with …
The effective dispersion of Graphene Nanosheet (GNS) as reinforcement was studied with various morphology of Copper (Cu) powder as matrix. High energy milling was used for modifying the morphology of the Cu powders. The Cu powder with Spherical and dentric shape was used in this study. Using high energy milling both the powders were milled for 8 h and 16 h respectively. The morphology of Cu powders was altered as flake shape upon milling. GNS (2 wt. %) was added as reinforcement uniformly with various morphology Cu powder used as matrix. The effect of size and shape of Cu as matrix on Cu/GNS c…
Few layer graphene/carbon (FLG/C) composites are prepared directly via the rapid and simple exfoliation of expanded graphite in the presence of carbon based natural precursors (i.e. protein, polysaccharide) in water, followed by carbonization process. Several parameters such as nature of C-precursor, FLG/C ratio and carbonization conditions (gas, temperature) are modified in order to optimize the morphology, composition and porosity of FLG/C and thereby investigate their impact on gravimetric and volumetric capacitance, their stability and contribution of pseudocapacitance (Ps) vs. double-laye…
In order to realise the potential of graphene nanocomposites it is vital to control the degree of dispersion and achieve a strong graphene polymer interface. Herein, we developed a facile grafting to functionalisation approach for graphene nanoplatelets. NH2-terminated graphene nanoplatelets, NH2 GNPs, prepared by a diazonium coupling were used as a platform to covalently graft PMMA chains to the surface of graphene through an amidation between the NH2 groups and PMMA chains, PMMA NH GNPs. A degree of PMMA grafting of 3.8 wt, one chain per 40 carbon atoms, was found to both improve the dispers…
Electromagnetic (EM) composites have stimulated tremendous fundamental and practical interests owing to their flexible electromagnetic properties and extensive potential engineering applications. Hence, it is necessary to systematically understand the physical mechanisms and design principles controlling EM composites. In this tutorial, we first provide an overview of the basic theory of electromagnetism about electromagnetic constitutive parameters that can represent the electromagnetic properties of materials. We show how this corpus allows a consistent construction of effective medium theor…
The effect of graphene orientation on permeability and corrosion initiation under composite coatings
Chongqing 2D Materials Institute（重庆二维材料研究院）；Faculty of Materials Science and Engineering, K. N. Toosi University of Technology（德黑兰理工大学材料科学与工程学院）；Key Laboratory of Optoelectronic Technology & System Ministry of Education, Chongqing University（重庆大学光电系统及技术教育部重点实验室）；College of Materials Science and Engineering, Beijing University of Chemical Technology（北京化工大学材料科学与工程学部）
Rational combination holds the key for non-precious metal oxides and economic carbon materials to the creation of high performance air electrode materials. Carbon nanotubes (CNTs)-supported manganese oxides composite catalysts (CMnCs) were obtained by reacting commercial CNTs with MnO$_4^-$ in diluted H$_2$SO$_4$ with cancelling conventional hydrothermal processing or adding surfantant templates. CMnCs were then assembled into commercial air cathodes equipped in metal air fuel cells. CNTs demonstrated structurally much defective. Outer CNT walls were cracked into graphene nano pieces yet remai…
Graphene possesses unique features that make it attractive for nanotechnology. Functional devices often require combination of several materials with specific functions, and graphene-polymer composites are one of them. Herein, we report on the preparation of PEDOT:Graphene bilayers by in situ polymerization of EDOT on covalently functionalized graphene. The polymerization proceeds exclusively on the grafted graphene, and patterned structures with high spatial resolution down to 3 μm could have been prepared. The composite exhibits enhanced efficiency of electrochemical doping compared to prist…
The reliability and safety of lithium-ion batteries can be affected by overheating issues. Phase change materials like paraffin due to their large heat capacities are among the best solutions for the thermal management of batteries. In this investigation, multiscale modelling techniques were developed to explore the efficiency in the thermal management of rechargeable batteries through employing the paraffin composite structures. A combined atomistic-continuum multiscale modelling was conducted to evaluate the thermal conductivity of paraffin reinforced with graphene or hexagonal boron-nitride…
This report introduces the electromagnetic absorption of the catalyst as a novel knob in optimizing chemical vapor deposition of graphene. A chromium film initially deposited at one side of a catalyst copper foil absorbs radiative thermal energy several times higher than the plain copper foil and migrates to the other side of the foil in the form of microscale grains. The process involves local melting of the copper which together with the increased operation temperature, improves the crystalline quality of growing graphene. Local melting of copper replaces the otherwise-necessary annealing pr…
The incorporation of graphene-related materials as nanofiller can produce multifunctional foams with enhanced specific properties and density reduction. Herein we report on the preparation of microcellular thermoplastic polyurethane/graphene foams by batch foaming. Solution blending was first adopted to disperse graphene nanoplatelets (GNP) in the elastomeric matrix. Then, a foaming process based on the use of supercritical CO2 was adopted to produce the microcellular TPU/GNP composite foams with graphene content up to 1 wt%. The EMI shielding behaviour of the TPU/GNP foams has been assessed i…
Electromagnetically induced transparency (EIT) analogue in all-dielectric metamaterials with a high quality factor provides an effective route to enhance light-matter interaction at the nanoscale. In particular, the active control applied to it enables great degree of freedom for spatial light modulation and thus promises functional device applications with high flexible tunability. Here we load graphene into all-dielectric metamaterials and realize the remarkably high modulation depth in the transmission amplitude of the EIT resonance with the manipulation of graphene conductivity, via shifti…
Electromagnetic interference (EMI) shielding coating materials with thicknesses in the microscale are required in many sectors, including communications, medical, aerospace and electronics, to isolate the electromagnetic radiation emitted from electronic equipment. We report a spray, layer-by-layer (LbL) coating approach to fabricate micron thick, highly-ordered and electrically-conductive coatings with exceptional EMI shielding effectiveness (EMI SE >4830 dB/mm), through the alternating self-assembly of negatively-charged reduced graphene oxide (RGO) and a positively-charged polyelectrolyte (…
This paper presents illustrative electromagnetic modelling and simulation of graphene antenna using a two-dimensional graphene sheet of zero thickness and a three-dimensional graphene slab of finite thickness. The properties of the antenna are analyzed in terms of the S11 parameter, input impedance, VSWR, radiation pattern, and frequency reconfiguration using the full-wave electromagnetic simulator. Furthermore, this work numerically studies the modelling of graphene antenna using a three-dimensional graphene thin slab and the impact of graphene slab thickness on the performance of graphene an…
The use of graphene in a form of discontinuous flakes in polymer composites limits the full exploitation of the unique properties of graphene, thus requiring high filler loadings for achieving - for example - satisfactory electrical and mechanical properties. Herein centimetre-scale CVD graphene/polymer nanolaminates have been produced by using an iterative 'lift-off/float-on' process and have been found to outperform, for the same graphene content, state-of-the-art flake-based graphene polymer composites in terms of mechanical reinforcement and electrical properties. Most importantly these th…
Composites are ideally suited to achieve desirable multifunctional effective properties since the best properties of different materials can be judiciously combined with designed microstructures. Here we establish cross-property relations for two-phase composite media that link effective elastic and electromagnetic wave characteristics to one another, including the respective effective wave speeds and attenuation coefficients, which facilitate multifunctional material design. This is achieved by deriving accurate formulas for the effective electromagnetic and elastodynamic properties that depe…