Significant insights for critical current density (Jc) improvement in Bi-2212 super- conductor wires can be obtained by an accurate analysis of the structural and mi- crostructural properties evolving during the so-called partial-melt process, a heat treatment needed to improve grain connectivity and therefore gain high Jc. Here, we report an in-situ analysis by means of synchrotron X-ray and neutron diffraction performed, for the first time, during the heat treatment carried out with the very same temperature profile and reacting oxygen atmosphere in which the Bi-2212 wires are usually treated for practical applications. The obtained results show the thermal evolution of the Bi-2212 structure, focusing in particular on texturing and secondary phases formation. The role of the oxygen is discussed as well. Hence, the present investigation marks a significant advance for the comprehension of the phenomena involved in the wire fabrication process and provides useful insights for the process optimization as well.
Seven-core Ag/Fe sheathed Sr0.6K0.4Fe2As2 (Sr-122) superconducting wires were produced by the ex situ powder-in-tube (PIT) method. The relationship between the cold-work deformation process and the superconducting properties of wires were systematically studied. It was found that flat rolling can efficiently increase the density of the superconducting core and largely improve the transport critical current density (Jc) of as-drawn wires. The Jc of the best sample achieved 21.1 kA/cm^2 at 4.2 K in self field, and showed very weak magnetic field dependence in high fields. Our result suggested a …
A comparative study of magnetic behavior in a DC magnetic field up to 19 Tesla has been undertaken on different Nb3Sn samples, i.e. single crystals, polycrystal samples and multifilamentary wires. From the 1st and 3rd harmonics of the AC magnetic susceptibility a peak effect was experimentally observed in the single crystal and in the polycrystal, whereas this phenomenon is absent in the measured wires. The corresponding H vs T phase diagram reveals a different behavior between wires on one hand and polycrystalline and single crystal samples on the other. In particular, from the 3rd harmonics …
Bi2Sr2CaCu2O8+x is the only cuprate superconductor that can be made into a round-wire conductor form with a high enough critical current density Jc for applications. Here we show that the Jc(5 T,4.2 K) of such Ag-sheathed filamentary wires can be doubled to more than 1.4x10^5 A/cm^2 by low temperature oxygenation. Careful analysis shows that the improved performance is associated with a 12 K reduction in transition temperature Tc to 80 K and a significant enhancement in intergranular connectivity. In spite of the macroscopically untextured nature of the wire, overdoping is highly effective in …
We have fabricated prototype Bi,Pb(2223)/Ag superconduting multifilamentary wires with a square cross-section. The AC losses of these wires were measured, compared with those of tapes and also compared with the theory. Wires show largely reduced AC magnetic field losses at 47 Hz, compared to those of tapes in a perpendicular magnetic field. The effects of the twist pitch and of the use of the high resisitive barriers were also investigated. The results show that the use of a twist pitch of about 10 mm is sufficient for decoupling the filaments, and that the use of very short twist pitches does…
Transport critical current densities and n-values were measured at 4.2 K in fields up to 15 T on 7, 19, and 37-stack multifilamentary MgB2 strands made using an in-situ route. Some strands included SiC additions (particle size 30 nm), while in others Mg-rich compositions were used. Two basic multifilamentary variants were measured, the first had Nb filamentary barriers, the second had Fe filamentary barriers. All samples incorporated stabilizer in the form of Cu 101. Simple, one-step heat treatments were used, with temperatures ranging from 700-800C, and times from 10-30 minutes. Transport cri…
The MgB2 superconductor has already demonstrated its applicative potential, in particular for DC applications such as MRI magnets, thanks to the low costs of the raw materials and to its simple production process. However further efforts have still to be made in order to broaden its employment also towards the AC applications such as SFCL, motors, transformers. The main issues are related to the reduction of the AC losses. Some of these can be faced by obtaining multifilamentary conductors with a large number of very fine filaments and, in this context, the powders granulometry can play a cruc…
Multifilamentary MgB2/Fe wires and tapes with high transport critical current densities have been fabricated using a straightforward powder-in-tube (PIT) process. After annealing, we measured transport jc values up to 1.1 * 105 A/cm2 at 4.2 K and in a field of 2 T in a MgB2/Fe square wire with 7 filaments fabricated by two-axial rolling, and up to 5 * 104 A/cm2 at 4.2 K in 1 T in a MgB2/Fe tape with 7 filaments. For higher currents these multifilamentary wires and tapes quenched due to insufficient thermal stability of filaments. Both the processing routes and deformation methods were found to…
In DC and AC practical applications of MgB2 superconducting wires an important role is represented by the material sheath which has to provide, among other things, a suitable electrical and thermal stabilization. A way to obtain a large enough amount of low resistivity material in to the conductor architecture is to use it as external sheath. In this paper we study ex-situ multifilamentary MgB2 wires using oxide-dispersion-strengthened copper (GlidCop) as external sheath in order to reach a good compromise between critical current density and thermal properties. We prepared three GlidCop sampl…
Iron-based superconductors have been considered to be very promising in high-field applications, for which multifilamentary wire and tape conductors with high mechanical strength are essential. In this work, 7-,19- and 114-filament Sr0.6K0.4Fe2As2 (Sr-122) superconducting wires and tapes with silver as matrix and iron as outer reinforcing sheath were produced by the ex situ powder-in-tube method. The mass densities of Sr-122 phase in 7- and 19-filament conductors were investigated by microhardness characterization, which revealed a positive correlation between hardness and transport critical c…
Mono- and multifilamentary MgB2/Fe tapes and wires with high transport critical current densities have been prepared using the powder-in-tube (PIT) process. The fabrication details are described. The effect of powder grain sizes and recrystallization temperature on jc has been investigated. At 25K and 1 T, jc values close to 105 A/cm2 were measured, while jc of 106 A/cm2 were extrapolated for 4.2K/0T in our monofilamentary tape. MgB2/Fe tapes exhibit high exponential n factors for the resistive transition: n ~ 80 and 40 were found at 5 T and 7 T, respectively. The highest transport jc values o…
We report non-Cu critical current densities of 4.09 * 10^9 A/m^2 at 12 T and 2.27 * 10^9 A/m^2 at 15 T obtained from transport measurements on a Ti-alloyed RRP Nb3Sn wire after irradiation to a fast neutron fluence of 8.9 * 10^21 m^-2. These values are to our knowledge unprecedented in multifilamentary Nb3Sn, and they correspond to a Jc enhancement of approximately 60% relative to the unirradiated state. Our magnetometry data obtained on short wire samples irradiated to fast neutron fluences of up to 2.5 * 10^22 m^-2 indicate the possibility of an even better performance, whereas earlier irrad…
We present two magnetometry-based methods suitable for assessing gradients in the critical temperature and hence the composition of multifilamentary superconductors: AC magnetometry and Scanning Hall Probe Microscopy. The novelty of the former technique lies in the iterative evaluation procedure we developed, whereas the strength of the latter is the direct visualization of the temperature dependent penetration of a magnetic field into the superconductor. Using the example of a PIT Nb3Sn wire, we demonstrate the application of these techniques, and compare the respective results to each other …
MgB2 tapes and wires were fabricated by the Powder-In-Tube method. Stainless steel and Cu-Ni tubes were used as sheath materials, and no heat treatment was applied. The tapes made of stainless steel showed transport critical current density Jc of about 10,000A/cm2 at 4.2K and 5T. A high Jc of about 300,000A/cm2 was obtained by extrapolating the Jc-B curves to zero field. Multifilamentary(7-core) MgB2 wire was successfully fabricated using Cu-Ni tubes. For both tapes and wires the grain connectivity of MgB2 was as good as a high-pressure sintered bulk sample. However, the Jc of the Cu-Ni sheath…
Recently the interest about Bi-2212 round wire superconductor for high magnetic field use has been enhancing despite the fact that an increase of the critical current is still needed to boost its successful use in such applications. Recent studies have demonstrated that the main obstacle to current flow, especially in long wires, is the residual porosity inside these Powder-In-Tube processed conductors which develops in bubbles-agglomeration when the Bi-2212 melts. Through this work we tried to overcome this issue acting on the wire densification by changing the deformation process. Here we sh…
We have fabricated a series of iron-sheathed superconducting wires prepared by the powder-in-tube technique from (MgB_2)_{1-x}:(Mg+2B)_x initial powder mixtures taken with different proportions, so that x varies from 0 to 1. It turned out that "ex-situ" prepared wire (x = 0) has considerable disadvantages compared to all the other wires in which "in-situ" assisted (0 < x < 1) or pure "in-situ" (x = 1) preparation was used due to weaker inter-grain connectivity. As a result, higher critical current densities J_c were measured over the entire range of applied magnetic fields B_a for all the samp…
We fabricated FeTe0.5Se0.5 superconducting wires using ex-situ Powder-in-tube method with an Fe sheath. It was amazing that superconducting current was observed in the as-drawn wire without any heat treatments. By heat treatment at 200C for 2 hours, Tczero and Jc at 4.2 K were enhanced up to 9.1 K and 64.1 A/cm2 (Ic = 182.6 mA), respectively. Furthermore, the Jc of FeTe0.5Se0.5 wire heat treated at 200C for 2 hours was not much sensitive to the applied magnetic fields. Therefore, FeTe0.5Se0.5 wires have a great potential for applications.
MgB2 wires and tapes suffer from a limitation of the transport current densities, especially at low field, due to an unsufficient thermal stabilization caused by hot spots from a non-homogeneous microstructure, the presence of secondary phases and voids. For the preparation of MgB2 wires and tapes two different precursor routes, using MgB2 (ex-situ process) or Mg + B (in-situ process) are applied. The in-situ approach allows variation of many parameters in the wire preparation and the improvement of this approach is the central topic of this paper. We present an improved in-situ approach, the …
We demonstrate the fabrication of superconducting SmFeAsO1-xFx (Sm-1111) wires by using the ex-situ powder-in-tube technique. Sm-1111 powder and a binder composed of SmF3, samarium arsenide, and iron arsenide were used to synthesize the superconducting core. Although the F content of Sm-1111 is reduced in the process of ex-situ fabrication, the binder compensates by sufficiently supplementing the F content, thereby preventing a decrease in the superconducting transition temperature and a shrinking of the superconducting volume fraction. Thus, in the superconducting Sm-1111 wire with the binder…
We report large transport critical current densities observed in Ag-added (Ba,K)Fe2As2 superconducting wires prepared by an ex-situ powder-in-tube (PIT) process. The wire has a simple composite structure sheathed only by Ag. A precursor bulk material prepared by a melting process was ground into powder and put into a Ag tube. The composite was then cold worked into a wire and heat treated at 850$^\circ$C for sintering. Transport critical current densities, Jc, at 4.2 K are 1.0\times104 A/cm2 (Ic = 60.7 A) in self field and 1.1\times103 A/cm2 (Ic = 6.6 A) in 10 T. These are the highest values r…
We demonstrate the fabrication of superconducting SmFeAsO1-xFx (Sm-1111) wires by using the ex-situ powder-in-tube technique. Sm-1111 powder and a binder composed of SmF3, samarium arsenide, and iron arsenide were used to synthesize the superconducting core. Although the F content of Sm-1111 is reduced in the process of ex-situ fabrication, the binder compensates by sufficiently supplementing the F content, thereby preventing a decrease in the superconducting transition temperature and a shrinkage of the superconducting volume fraction. Thus, in the superconducting Sm-1111 wire with the binder…
The superconducting properties of copper-sheathed MgB2 wires fabricated by conventional powder-in-tube techniques and the in-situ reaction procedure are analysed. The influence of the processing conditions and initial (1+x)Mg + 2B (x = 0, 0.1, 0.2) proportions of the precursors on the critical current values of the wires have been studied. In particular, the limits of the available temperatures and times for heat treatments imposed by the chemical reaction between Mg and Cu, and their effect on the superconducting properties of the wires, are discussed. The analysis includes the study of the s…
We found that the transport Jc of the ex-situ PIT processed (Ba,K)Fe2As2 (Ba-122) wire with single Ag sheath can be significantly enhanced by repeating the combined process of rolling and heat treatment. The transport Jc (4.2 K and 10 T) of 4.4 x 103 A/cm2 (Ic =15.7 A) was obtained for a thin tape of 0.3 mm in thickness, which is the highest value reported so far for the PIT processed 122 wires and tapes with a Ag sheath and processed by a conventional route. The measurement by a hybrid magnet showed that Jc-H curve maintains very small field dependence up to the strong magnetic field of 28 T …
We report successful fabrication of multi- and mono-core FeSe wires with high transport critical current density Jc using a simple in-situ Fe-diffusion process based on the powder-in-tube (Fe-diffusion PIT) method. The seven-core wire showed transport Jc of as high as 1027 A/cm2 at 4.2 K. The superconducting transition temperature Tczero was observed at 10.5 K in the wire-samples, which is about 2 K higher than that of bulk FeSe. The Fe-diffusion PIT method is suitable for fabricating multi-core wires of the binary FeSe superconductors with superior properties.
MgB2 monofilamentary nickel-sheated tapes and wires were fabricated by means of the ex-situ powder-in-tube method using either high-energy ball milled and low temperature synthesized powders. All sample were sintered at 920 C in Ar flow. The milling time and the revolution speed were tuned in order to maximize the critical current density in field (Jc): the maximum Jc value of 6 x 10e4 A/cm2 at 5 K and 4 T was obtained corresponding to the tape prepared with powders milled for 144h at 180rpm. Vorious synthesis temperature were also investigated (730-900 C) finding a best Jc value for the wire …
Superconducting Ag or Cu sheathed MgB2 wires have been fabricated by conventional powder-in-tube techniques. The in-situ reaction of Mg and B powders with atomic proportions of 1:2 and 1.33:2 inside Ag or Cu tubes at low temperatures have been searched. An active alloying of Mg with Ag or Cu sheaths at temperatures below 660 C has been observed. For Ag sheaths, there is a strong diffusion of Mg, which does not allow the formation of large amounts of MgB2 at the core. For Cu sheaths, the diffusion of Mg is stopped by the formation of a MgCu2 layer around the superconducting core and an appropri…
In this letter, we report the results of transport Jc of solenoid coils upto 100 turns fabricated with Cu-sheathed MgB2 wires using a wind-reaction in-situ technique. Despite the low density of single core and some reaction between Mg and Cu-sheath, our results demonstrate the decrease in transport Jc with increasing length of MgB2 wires is insignificant. Solenoid coils with diameter as small as 10 mm can be readily fabricated using a wind-reaction in-situ technique. The Jc of coils is essentially the same as in the form of straight wires. A Jc of 133,000 A/cm2 and 125,000 A/cm2 at 4 K and sel…
In this work, the feasibility condition of Powder-In-Tube (PIT) processed wires of Fe(Se,Te) superconductor has been investigated. We faced several technical issues that are extensively described and discussed. In particular, we tested different metals and alloys as external sheaths (Cu, Ag, Nb, Ta, Ni, Fe, cupronickel, brass) concluding that the only sheath that does not affect substantially the Fe(Se,Te) phase is Fe. On the other hand, Fe sheath introduces excess iron in the Fe(Se,Te) phase, which affects the superconducting properties; we investigated the effects of the thermal treatments a…
FeTe0.5Se0.5 superconducting wires have been fabricated using ex-situ PIT method with an Fe sheath. Among the other FeAs-based superconductor, FeTe0.5Se0.5 has great advantage for application due to binary composition and less toxic. Surprisingly, superconducting current was observed in the as-fabricated wire without any heat treatments. Zero resistivity and transport critical current density (Jc) were 3.2 K and 2.8 A/cm2, respectively. In addition, by annealing at 200 degC for 2 h, critical temperature Tczero and Jc were enhanced up to 9.1 K, and 64.1 A/cm2, respectively. This suggests that t…
Among the recently discovered Fe-based superconducting compounds, the (K,Ba)Fe2As2 phase is attracting large interest within the scientific community interested in conductor developments. In fact, after some years of development, critical current densities Jc of about 105 A/cm2 at fields up to more than 10 T have been obtained in powder in tube (PIT) processed wires and tapes. Here we explore the crucial points in the wire/tape fabrication by means of the ex-situ PIT method. We focus on scaling up processes which are crucial for the industrial fabrication. We analyzed the effects on the micros…
The new class of Mg-B superconducting conductors was prepared using the standard in-situ powder-in-tube, PIT, method where Mg+2B mixture was used to fill the copper and silver tubes. Study of the intergranular current, grain connectivity and superconducting phases in wires were conducted by AC susceptibility measurements and direct four point transport measurements. Using SQUID magnetometer, magnetisation versus magnetic field (M-H) curves of the round wires after reactive diffusion were measured at temperatures 5K and magnetic field up to 5T to define the Jcmag . The direct current density me…