The low dielectric losses of an isotropically pure single crystal $^{28}$Si sample were determined at a temperature of 20 mK and at powers equivalent to that of a single photon. Whispering Gallery Mode (WGM) analysis revealed large Quality Factors of order $2\times10^6$ (dielectric loss $\sim 5\times10^{-7}$) at high powers, degrading to $7\times10^5$ (dielectric loss $\sim 1.4\times10^{-6}$) at single photon energy. A very low-loss narrow line width paramagnetic spin flip transition was detected with extreme sensitivity in $^{28}$Si, with very small concentration below $10^{11}$~cm$^{-3}$ (less than 10 parts per trillion) and g-factor of $1.995\pm0.008$. Such determination was only possible due to the low dielectric photonic losses combined with the long lifetime of the spin transition (low magnetic loss), which enhances the magnetic AC susceptibility. Such low photonic loss at single photon energy combined with the narrow line width of the spin ensemble, indicate that single crystal $^{28}$Si could be an important crystal for future cavity QED experiments.
Spin-coherence characterization of boron vacancy defects in hexagonal boron nitride with broadband microwave pulses
The University of Tokyo（东京大学）；National Institute for Materials Science（国立材料研究所）；Tokyo University of Technology（东京都立科学技术大学）；National Institute of Advanced Industrial Science and Technology（产业技术综合研究所）