Nanoscale Fe3O4 epitaxial thin film has been synthesized on MgO/GaAs(100) spintronic heterostructure, and studied with X-ray magnetic circular dichroism (XMCD). We have observed a total magnetic moment of (3.32 +- 0.1) uB/f.u., retaining 83% of the bulk value. Unquenched orbital moment of (0.47 +- 0.05) uB/f.u. has been confirmed by carefully applying the sum rule. The results offer direct experimental evidence of the bulk-like total magnetic moment and a large orbital moment in the nanoscale fully epitaxial Fe3O4/MgO/GaAs(100) heterostructure, which is significant for spintronics applications.
The electronic band structure in the epitaxial Fe/MgO/GaAs(001) tunnel junction has been studied by X-ray and ultraviolet photoelectron spectroscopy measurements. The Schottky barrier height (SBH) of Fe on MgO/GaAs heterostructure is determined to be 3.3+-0.1eV, which sets the Fe Fermi level about 0.3eV above the GaAs valence band maximum. This SBH is also exactly the same as that measured from Fe on MgO monocrystal. After Fe deposition, no band bending change is observed in MgO and GaAs underlayers. On the contrary, Au and Al deposition lead to clear variation of the band bending in both MgO …
We created epitaxial magnetic tunnel junctions of FeCo/MgO/EuS on MgO buffered Si (100). Tunnel magnetoresistance reached up to 64% at 4.2 K. An unexpected fast drop of magnetoresistance was recorded for MgO thickness above 1 nm, which is attributed to the forced nonspecular conductance across the EuS conduction band minimum located at the X point, rather than the desired Delta_1 conductance centered around the Gamma point.
The structures of epitaxial ultrathin Co2FeAl/MgO(001) heterostructures relating to the interface-induced perpendicular magnetic anisotropy (PMA) were investigated using scanning transmission electron microscopy, energy dispersive x-ray spectroscopy, and x-ray magnetic circular dichroism. We found that Al atoms from the Co2FeAl layer significantly interdiffuse into MgO, forming an Al-deficient Co-Fe-Al/Mg-Al-O structure near the Co2FeAl/MgO interface. This atomic replacement may play an additional role for enhancing PMA, which is consistent with the observed large perpendicular orbital magneti…
We report on the structural properties of epitaxial FeO layers grown by molecular beam epitaxy on MgO(111). The successful stabilization of polar FeO films as thick as 16 monolayers (ML), obtained by deposition and subsequent oxidation of single Fe layers, is presented. FeO/MgO(111) thin films were chemically and structurally characterized using low-energy electron diffraction, Auger electron spectroscopy and conversion electron Mossbauer spectroscopy (CEMS). Detailed in situ CEMS measurements as a function of the film thickness demonstrated a size-effect-induced evolution of the hyperfine par…
We investigate the initial growth modes and the role of interfacial electrostatic interactions of EuO epitaxy on MgO(001) by reactive molecular beam epitaxy. A TiO2 interfacial layer is employed to produce high quality epitaxial growth of EuO on MgO(001) with a 45° in plane rotation. For comparison, direct deposition of EuO on MgO, without the TiO2 layer shows a much slower time evolution in producing a single crystal film. Conceptual arguments of electrostatic repulsion of like-ions are introduced to explain the increased EuO quality at the interface with the TiO2 layer. It is shown that ultr…
We report the successful electrical creation of spin polarization in p-type Si at room temperature by using an epitaxial MgO(001) tunnel barrier and Fe(001) electrode. Reflection high-energy electron diffraction observations revealed that epitaxial Fe/MgO(001) tunnel contacts can be grown on a (2 x 1) reconstructed Si surface whereas tunnel contacts grown on the (1 x 1) Si surface were polycrystalline. Transmission electron microscopy images showed a more flat interface for the epitaxial Fe/MgO/Si compared to that of the polycrystalline structure. For the Fe/MgO/p-Si devices, the Hanle and inv…
The Empirical Tight Binding(ETB) method is widely used in atomistic device simulations. The reliability of such simulations depends very strongly on the choice of basis sets and the ETB parameters. The traditional way of obtaining the ETB parameters is by fitting to experiment data, or critical theoretical bandedges and symmetries rather than a foundational mapping. A further shortcoming of traditional ETB is the lack of an explicit basis. In this work, a DFT mapping process which constructs TB parameters and explicit basis from DFT calculations is developed. The method is applied to two mater…
Giant tunnel magnetoresistance (TMR) ratios of 417% at room temperature (RT) and 914% at 3 K were demonstrated in epitaxial Fe/MgO/Fe(001) exchanged-biased spin-valve magnetic tunnel junctions (MTJs) by tuning growth conditions for each layer, combining sputter deposition for the Fe layers, electron-beam evaporation of the MgO barrier, and barrier interface tuning. Clear TMR oscillation as a function of the MgO thickness with a large peak-to-valley difference of ~80% was observed when the layers were grown on a highly (001)-oriented Cr buffer layer. Specific features of the observed MTJs are s…
Epitaxial semiconducting NiYBi thin films were directly prepared on MgO(100) substrates by magnetron sputtering. The intensity ratio of the (200) and (400) diffraction peaks, I(200)/I(400) = 2.93, was close to the theoretical value (3.03). The electronic structure of NiYBi was calculated using WIEN2k and a narrow indirect band gap of width 210 meV was found. The valence band spectra of the films obtained by linear dichroism in hard X-ray photoelectron spectroscopy exhibit clear structures that are in good agreement with the calculated band structure of NiYBi.
The spin and orbital magnetic moments of the Fe3O4 epitaxial ultrathin film synthesized by plasma assisted simultaneous oxidization on MgO(100) have been studied with X-ray magnetic circular dichroism (XMCD). The ultrathin film retains a rather large total magnetic moment, i.e. (2.7+-0.15) uB/f.u., which is ~ 70% of that for the bulk-like Fe3O4. A significant unquenched orbital moment up to (0.54+-0.05) uB/f.u. was observed, which could come from the symmetry breaking at the Fe3O4/MgO interface. Such sizable orbital moment will add capacities to the Fe3O4-based spintronics devices in the magne…
We demonstrate a large electrical spin injection into GaAs at zero magnetic field thanks to an ultrathin perpendicularly magnetized CoFeB contact of a few atomic planes (1.2 nm). The spin-polarization of electrons injected into GaAs was examined by the circular polarization of electroluminescence from a Spin Light Emitting Diode with embedded InGaAs/GaAs quantum wells. The electroluminescence polarization as a function of the magnetic field closely traces the out-of-plane magnetization of the CoFeB/MgO injector. A circular polarization degree of the emitted light as large as 20% at 25 K is ach…
An efficient electrical spin injection into an InGaAs/GaAs quantum well light emitting diode is demonstrated thanks to a CoFeB/MgO spin injector. The textured MgO tunnel barrier is fabricated by two different techniques: sputtering and molecular beam epitaxy (MBE). The maximal spin injection efficiency is comparable for both methods. Additionally, the effect of annealing is also investigated for the two types of samples. Both samples show the same trend: an increase of the electroluminescence circular polarization (Pc) with the increase of annealing temperature, followed by a saturation of Pc …
Magnetite thin fims have been grown epitaxially on ZnO and MgO substrates using molecular beam epitaxy. The film quality was found to be strongly dependent on the oxygen partial pressure during growth. Structural, electronic, and magnetic properties were analyzed utilizing Low Energy Electron Diffraction (LEED), HArd X-ray PhotoElectron Spectroscopy (HAXPES), Magneto Optical Kerr Effect (MOKE), and X-ray Magnetic Circular Dichroism (XMCD). Diffraction patterns show clear indication for growth in the (111) direction on ZnO. Vertical structure analysis by HAXPES depth profiling revealed uniform …
Voltage control of magnetic anisotropy (VCMA) in magnetic heterostructures is a key technology for achieving energy-efficiency electronic devices with ultralow power consumption. Here, we report the first demonstration of the VCMA effect in novel epitaxial Ru/Co2FeAl(CFA)/MgO heterostructures with interfacial perpendicular magnetic anisotropy (PMA). Perpendicularly magnetized tunnel junctions with the structure of Ru/CFA/MgO were fabricated and exhibited an effective voltage control on switching fields for the CFA free layer. A large VCMA coefficient of 108 (139) fJ/Vm for the CFA film was ach…
Thin films of the proposed topological insulator PdLuBi - a Heusler compound with the C1b structure - were prepared on Ta-Mo-buffered MgO(100) substrates by co-sputtering from PdBi2 and Lu targets. Epitaxial growth of high-quality PdLuBi films was confirmed by X-ray spectrometry and reflection high-energy electron diffraction. The root-mean-square roughness of the films was as low as 1.45 nm, although the films were deposited at high temperature. The film composition is close to the ideal stoichiometric ratio. The valence band spectra of the PdLuBi films, observed by hard X-ray photoelectron s…
We demonstrate first measurements of successful spin generation in crystalline Co$_2$FeSi/MgO/GaAs hybrid structures grown by molecular-beam epitaxy (MBE), with different MgO interlayer thicknesses. Using non-local spin valve and non-local Hanle measurement configurations, we determine spin lifetimes of ${τ\approx 100}$~ns and spin diffusion lengths of ${λ\approx 5.6}$~$μ$m for different MgO layer thicknesses proving the high quality of the GaAs transport channel. For an optimized MgO layer thickness, the bias dependence of the spin valve signals indicates the verification of the half-metallic…
We study the spin-orbit torque (SOT) effective fields in Cr/CoFeAl/MgO and Ru/CoFeAl/MgO magnetic heterostructures using the adiabatic harmonic Hall measurement. High-quality perpendicular-magnetic-anisotropy CoFeAl layers were grown on Cr and Ru layers. The magnitudes of the SOT effective fields were found to significantly depend on the underlayer material (Cr or Ru) as well as their thicknesses. The damping-like longitudinal effective field (ΔH_L) increases with increasing underlayer thickness for all heterostructures. In contrast, the field-like transverse effective field (ΔH_T) increases w…
Anti-phase boundaries (APBs) normally form as a consequence of the initial growth conditions in all spinel ferrite thin films. The presence of APBs in epitaxial films of the inverse spinel Fe3O4 alters their electronic and magnetic properties due to strong antiferromagnetic (AF) interactions across these boundaries. The effect of using in-situ electric field assisted growth on the migration of APBs in hetero epitaxial Fe3O4(100)/MgO(100) thin films have been explored in the present work. The electric field assisted growth is found to reduce the AF interactions across APBs and as a consequence …
Thin epitaxial GaAs films, with thickness varying from 140 to 1000 nm and different Si doping levels, were grown at 650C by organometallic vapor phase epitaxy (OMVPE) on Ge substrates and extensively analyzed by low-temperature photoluminescence (PL) spectroscopy.
Although both theoretical predications and experimental observations demonstrated that the damping factor is anisotropic at ferromagnet/semiconductor interface with robust interfacial spin-orbit coupling, it is not well understood whether non-local Gilbert damping driven by spin currents in heavy metal/ferromagnetic metal (HM/FM) bilayers is anisotropic or not. Here, we investigated the in-plane angular- and frequency- dependence of magnetic relaxation of epitaxial Fe/MgO(001) films with different capping layers of Pd and Cu. After disentangling the parasitic contributions, such as two-magnon …
We fabricate fully epitaxial Fe/ZnO/MgO/Fe magnetic tunnel junctions (MTJs) with a bilayer tunnel barrier, in which ZnO has a metastable rock-salt crystal structure. We observe a high magnetoresistance ratio up to 96% at room temperature (RT) and find that these MTJs have asymmetric current-voltage characteristics, and their rectifying performances are largely dependent on the magnetization alignments of the Fe electrodes. Diode responsibilities at a zero-bias voltage ($β_{0}$), which is an important performance index for harvesting applications, are observed up to 1.3 A/W at RT in the antipar…
The electronic transport and spincaloric properties of epitaxial magnetic tunnel junctions with half-metallic Co$_2$MnSi Heusler electrodes, MgO tunneling barriers, and different interface terminations are investigated by using first-principles calculations. A new approach to spincaloric properties is presented that circumvents the linear response approximation inherent in the Seebeck coefficient and compared to the method of Sivan and Imry. This approach supports two different temperatures in the two electrodes and provides the exact current and/or voltage response of the system. Moreover, it…
We investigate the magnetization reversal in Fe/MgO(001) films with fourfold in-plane magnetic anisotropy and an additional uniaxial anisotropy whose orientation and strength are tuned using different growth geometries and post growth treatments. The previously adopted mechanism of 180^{o} domain wall nucleation clearly fails to explain the observed 180^{o} magnetization reversal. A new reversal mechanism with two successive domain wall nucleations consistently predicts the switching fields for all field orientations. Our results are relevant for a correct interpretation of magnetization rever…
The electronic structure and spin-dependent tunneling in epitaxial Fe/MgO/Fe(001) tunnel junctions are studied using first-principles calculations. For small MgO barrier thickness the minority-spin resonant bands at the two interfaces make a significant contribution to the tunneling conductance for the antiparallel magnetization, whereas these bands are, in practice, mismatched by disorder and/or small applied bias for the parallel magnetization. This explains the experimentally observed decrease in tunneling magnetoresistance (TMR) for thin MgO barriers. We predict that a monolayer of Ag epit…
We demonstrate the epitaxial growth of EuO on GaAs by reactive molecular beam epitaxy. Thin films are grown in an adsorption-controlled regime with the aid of an MgO diffusion barrier. Despite the large lattice mismatch, it is shown that EuO grows well on MgO(001) with excellent magnetic properties. Epitaxy on GaAs is cube-on-cube and longitudinal magneto-optic Kerr effect measurements demonstrate a large Kerr rotation of 0.57°, a significant remanent magnetization, and a Curie temperature of 69 K.
Alloying Fe electrodes with V, through reduced FeV/MgO interface mismatch in epitaxial magnetic tunnel junctions with MgO barriers, notably suppresses both nonmagnetic (parallel) and magnetic (antiparallel) state 1/f noise and enhances tunnelling magnetoresistance (TMR). A comparative study of the room temperature electron transport and low frequency noise in Fe1-xVx/MgO/Fe and Fe/MgO/Fe1-xVx MTJs with 0 <= x <= 0.25 reveals that V doping of the bottom electrode for x < 0.1 reduces in nearly 2 orders of magnitude the normalized nonmagnetic and magnetic 1/f noise. We attribute the enhanced TMR …
Low-temperature epitaxial growth of refractory transition-metal nitride thin films by means of physical vapor deposition has been a recurring theme in advanced thin-film technology for several years. In the present study, 150-nm-thick epitaxial HfN layers are grown on MgO(001) by reactive high-impulse magnetron sputtering (HiPIMS) with no external substrate heating. Maximum film growth temperatures Ts due to plasma heating range from 70-150 °C, corresponding to Ts/Tm = 0.10-0.12 (in which Tm is the HfN melting point in K). During HiPIMS, gas and sputtered-metal ion fluxes incident at the growi…
We report the growth of MgO[001]//Fe(6 nm)/MgO(7 nm) and MgO[001]//Fe(6 nm)/Pt(6 nm) by molecular beam epitaxy and show that the full characterization by spin-orbit ferromagnetic resonance (SO-FMR) allows the determination of magnetic anisotropies as by classical FMR-only studies. The spin mixing conductance of epitaxial Fe/Pt interface was measured to be (1.5 +- 0.5)x10^19 m^2, and the effective spin Hall angle (SHA), was estimated at different in-plane crystalline directions. It was found that SHA is the same in all directions. When taking into account high enough excitation frequencies to a…
Whether αdouble prime-Fe16N2 possesses a giant saturation magnetization (Ms) has been a daunting problem among magnetic researchers for almost 40 years, mainly due to the unshakable faith of famous Slater-Pauling (SP) curve and poor consistency on evaluating its Ms. Here we demonstrate that, using epitaxy and mis-fit strain imposed by an underlying substrate, the in-plane lattice constant of Fe16N2 thin films can be fine tuned to create favorable conditions for exceptionally large saturation magnetization. Combined study using polarized neutron reflectometry and X-ray diffraction shows that wi…
A new acousto-electrical method making use of transient transverse acoustoelectric voltage (TAV) to study solid state structures is reported. This voltage arises after a surface acoustic wave (SAW) generating the signal is switched off. Related measurements consist in detecting the shape of transient voltage and its spectral and temperature dependence. Both theory and experiment show that this method is an effective tool to characterize trapping centers in the bulk as well as at surfaces or interfaces of epitaxial semiconductor structures.
Epitaxial growth of BaBiO3 thin films on SrTiO3(001) and MgO(001) substrates using molecular beam epitaxy and controlling their crystal orientations competition
We report the epitaxial growth of CdCr2Se4, an n-type ferromagnetic semiconductor, on both GaAs and GaP(001) substrates, and describe the structural, magnetic and electronic properties. Magnetometry data confirm ferromagnetic order with a Curie temperature of 130 K, as in the bulk material. The magnetization exhibits hysteretic behavior with significant remanence, and an in-plane easy axis with a coercive field of ~125 Oe. Temperature dependent transport data show that the films are semiconducting in character and n-type as grown, with room temperature carrier concentrations of n ~ 1 x 10^18 c…
We have selectively grown thin epitaxial GaAs films on Ge substrates with the aid of a 200 nm thin SiO2 mask layer. The selectively grown structures have lateral sizes ranging from 1 um width up to large areas of 1 by 1 mm2. The growth is fully selective, thanks to an optimized growth procedure, consisting of a 13 nm thin nucleation layer grown at high pressure, followed by low pressure growth of GaAs. This growth procedure inhibits the nucleation of GaAs on the mask area and is a good compromise between reduction of loading effects and inhibition of anti phase domain growth in the GaAs. Never…
We have selectively grown thin epitaxial GaAs films on Ge substrates with the aid of a 200 nm thin SiO2 mask layer. The selectively grown structures have lateral sizes ranging from 1 um width up to large areas of 1 by 1 mm2. The growth with the standard growth procedure for GaAs growth on Ge substrates reveals a limited amount of GaAs nucleation on the mask area and strong loading effects caused by diffusion of group III precursors over the mask area and in the gas phase. Reduction of the growth pressure inhibits GaAs nucleation on the mask area and reduces the loading effects strongly, but fa…
BaZn2As2 is expected for a good p-type semiconductor and has two crystalline phases of an orthorhombic alpha phase and a higher-symmetry tetragonal beta phase. Here, we report high-quality epitaxial films of the tetragonal beta-BaZn2As2 were grown on single-crystal MgO (001) substrates by a reactive solid-phase epitaxy technique. Out-of-plane and in-plane epitaxial relationships between the film and the substrate were BaZn2As2 (00l)//MgO (001) and BaZn2As2 [200]//MgO [200], respectively. The full-widths at half maximum were 0.082o for a 008 out-of-plane rocking curve and 0.342o for a 200 in-pl…
The biaxially textured growth of superconducting Co-doped BaFe2As2 (Ba-122) thin films has been realized on ion beam assisted deposition (IBAD) MgO coated conductor templates by employing an iron buffer architecture. The iron pnictide coated conductor showed a superconducting transition temperature of 21.5 K, which is slightly lower than that of Co-doped Ba-122 films on single crystalline MgO substrates. A self-field critical current density of over 10^5 A/cm2 has already been achieved even at 8 K. The current experiment highlights the potential of possible coated conductor applications of the…
Epitaxial growth of III-V semiconductors on Si is a promising route for silicon photonics. Threading dislocations and the residual thermal stress generated during growth are expected to affect the thermal conductivity of the III-V semiconductors, which is crucial for efficient heat dissipation from photonic devices built on this platform. In this work, we combine a non-contact laser-induced transient thermal grating technique with ab initio phonon simulations to investigate the in-plane thermal transport of epitaxial GaAs-based buffer layers on Si, employed in the fabrication of III-V quantum …
Single-phase Ni0.46Mn0.54As films with strained C1b symmetry have been successfully grown on GaAs (001) substrates by molecular-beam epitaxy. The epitaxial relationship between the film and the substrate has been studied using synchrotron radiation, and a preferred configuration of (110)-orientated Ni0.46Mn0.54As on (001)-orientated GaAs was revealed. In addition, the magnetic properties of the films were found to be significantly influenced by the growth temperature. The optimized growth temperature is determined to be ~370 degree Celsius , for which relatively high Curie temperature, large s…
The Fe/MgO magnetic tunnel junction is a classic spintronic system, with current importance technologically, and interest for future innovation. The key magnetic properties are linked directly to the structure of hard-to-access buried interfaces, and the Fe and MgO components near the surface are unstable when exposed to air, making a deeper probing, non-destructive, in-situ measurement ideal for this system. We have thus applied hard x-ray photoemission spectroscopy (HXPS) and standing-wave (SW) HXPS in the few keV energy range to probe the structure of an epitaxially-grown MgO/Fe superlattic…
The diffusion length of minority carriers L p,n is an important characterisation parameter in semiconductor materials and is of particular interest when constructing devices such as solar cells (Hovel 1975), double hetero junction lasers (Casey and Panish 1978) and bipolar transistors. Their efficiency depends primarily on the ability of minority carriers to diffuse through neutral material to a p-n junction or Schottky barrier where they recombine with majority carriers. For this reason diffusion lengths have been measured in a variety of semiconductor materials. The GaAs material was grown b…
The exchange bias effect is commonly used to shift the coercive field of a ferromagnet. This technique is crucial for the use of magnetic tunnel junctions as logic or memory devices. Therefore, an independent switching of the two ferromagnetic electrodes is necessary to guarantee a reliable readout. Here, we demonstrate that the intrinsic exchange bias effect of Ni-Mn-Sn can be used to apply a unidirectional anisotropy to magnetic tunnel junctions. For this, we use epitaxial Ni-Mn-Sn films as pinning layers for microfabricated CoFeB/MgO/CoFeB magnetic tunnel junctions. We compare the exchange …
We study the underlying chemical, electronic and magnetic properties of a number of magnetite based thin films. The main focus is placed onto NiO/Fe$_3$O$_4$(001) bilayers grown on MgO(001) and Nb-SrTiO$_3$(001) substrates. We compare the results with those obtained on pure Fe$_3$O$_4$(001) thin films. It is found that the magnetite layers are oxidized and Fe$^{3+}$ dominates at the surfaces due to maghemite ($γ$-Fe$_2$O$_3$) formation, which decreases with increasing magnetite layer thickness. From a layer thickness of around 20 nm on the cationic distribution is close to that of stoichiometr…
The exploration of electric field controlled magnetism has come under scrutiny for its intriguing magnetoelectric phenomenon as well as technological advances in spintronics. Herein, the tremendous effect of an epitaxial strain on voltage-controlled perpendicular magnetic anisotropy (VPMA) is demonstrated in a transition-metal/ferromagnet/MgO (TM/FM/MgO) heterostructure from first-principles electronic structure computation. By tuning the epitaxial strain in Ta/Fe/MgO as a model system of TM/FM/MgO, we find distinctly different behaviours of VPMA from V- to Λ-shape trends with a substantially …
Electronic and structural properties of ultrathin MgO layers grown on epitaxial Fe(110) films were investigated at room temperature by means of spin-resolved photoelectron spectroscopy, Auger-electron spectroscopy, and low energy electron diffraction. The spin polarization at the Fermi level of the Fe(110) film decreases abruptly with increasing thickness of MgO layer up to 7 Å. This behavior is attributed to the formation of a thin FeO layer at the MgO(111)/Fe(110) interface, attenuating the intrinsic spin polarization.
The present study is dedicated to the influence of different substrate and buffer layer materials on the martensitic transformation in sputter deposited epitaxial shape memory Heusler alloys. For this, the magnetocaloric Heusler alloy Ni-Co-Mn-Al \cite{Teichert2015b} is grown on MgO(001), MgAl$_{2}$O$_{4}$(001), and MgO(001)/V substrates, which exhibit a lattice misfit to the Ni-Co-Mn-Al between $-1.2\%$ and $3.6\%$. By temperature dependent X-ray diffraction measurements it is shown that the optimum buffer layer for shape memory Heusler films is not one with minimum lattice misfit, but one wi…
Epitaxial growth of Co20Fe50Ge30 thin film on single crystal MgO (001) substrate is reported. Structure characterization revealed (001)-oriented B2 order of CoFeGe well lattice matched with the MgO barrier. Perpendicular magnetic anisotropy (PMA) was achieved in the MgO/CoFeGe/MgO structure with an optimized magnetic anisotropy energy density (K) of 3 106 erg/cm3. The magnetic anisotropy is found to depend strongly on the thickness of the MgO and CoFeGe layers, indicating that the PMA of CoFeGe is contributed by the interfacial anisotropy between CoFeGe and MgO. With reported low damping const…
Single-crystal Heusler atomic-scale superlattices that have been predicted to exhibit perpendicular magnetic anisotropy and half-metallicity have been successfully grown by molecular beam epitaxy. Superlattices consisting of full-Heusler Co$_2$MnAl and Fe$_2$MnAl with one to three unit cell periodicity were grown on GaAs (001), MgO (001), and Cr (001)/MgO (001). Electron energy loss spectroscopy maps confirmed clearly segregated epitaxial Heusler layers with high cobalt or high iron concentrations for samples grown near room temperature on GaAs (001). Superlattice structures grown with an exce…
In this work we present a study of the structural properties of Fe$_{100-x}$ Ga$_x$ grown by Molecular Beam Epitaxy on Mg0(100). We combine long range and local/chemically selective X-ray probes (X-ray Diffraction and X-ray absorption spectroscopy) together with real space imaging by means of Transmission Electron Microscopy and surface sensitive $in situ$ Reflected High Energy Electron Diffraction. For substrate temperature $T_s$ below 400 $^o$C we obtain $bcc$ films while, for $x \approx$ 24 and $T_s \geq$ 400$^o$C the nucleation of the $fcc$ phase is observed. For both systems a Ga anticlus…
We have investigated the nonlinear microwave properties of electron-beam coevaporated YBaCuO films on MgO, using stripline resonators at 2.3 GHz and temperatures 1.7-80 K. The oxygen content of the films ranged from strongly underdoped to overdoped. Above 20 K, the nonlinear response of the resonators was dominated by the superconductor. We could establish clear correlations between the nonlinear surface resistance, two-tone intermodulation (IMD), and oxygen content of the films, which indicate that the superconducting order parameter is important for the nonlinearities. An exponential rather …
An unusual crystallographic orientation of hexagonal Ru with a 4-fold symmetry emerging in epitaxial MgO/Ru/Co2FeAl/MgO heterostructures is reported, in which an approximately Ru(02-23) growth attributes to the lattice matching among MgO, Ru, and Co2FeAl. Perpendicular magnetic anisotropy of the Co2FeAl/MgO interface is substantially enhanced as compared with those with a Cr(001) layer. The MTJs incorporating this structure gave rise to the largest tunnel magnetoresistance for perpendicular MTJs using low damping Heusler alloys. The 4-fold-symmetry hexagonal Ru arises from an epitaxial growth …
Epitaxial Al/GaAs/Al structures having controlled thickness of high-quality GaAs and pristine interfaces have been fabricated using a wafer-bonding technique. III-V semiconductor/Al structures are grown by molecular beam epitaxy on III-V semiconductor substrates and bonded to silicon and sapphire. Selective etching is used to remove the III-V substrate followed by surface cleaning and superconductor regrowth, resulting in epitaxial Al/GaAs/Al tri-layers on sapphire or silicon substrates. Structures are characterized with reflection high energy electron diffraction, atomic force microscopy, X-r…
I present here theory of PZT thin film - MgO substrate system thermal expansion effect. I show that elastic properties of the substrate have to be taken into account to describe this effect.