Room-temperature multiferroic hexagonal LuFeO$_3$ films
Wenbin Wang, Jun Zhao, Wenbo Wang, Zheng Gai, Nina Balke, Miaofang Chi, Ho Nyung Lee, Wei Tian, Leyi Zhu, Xuemei Cheng, David J. Keavney, Jieyu Yi, Thomas Z. Wa… 展开作者
Wenbin Wang, Jun Zhao, Wenbo Wang, Zheng Gai, Nina Balke, Miaofang Chi, Ho Nyung Lee, Wei Tian, Leyi Zhu, Xuemei Cheng, David J. Keavney, Jieyu Yi, Thomas Z. Ward, Paul C. Snijders, Hans M. Christen, Weida Wu, Jian Shen, Xiaoshan Xu
The crystal and magnetic structures of single-crystalline hexagonal LuFeO$_3$ films have been studied using x-ray, electron and neutron diffraction methods. The polar structure of these films are found to persist up to 1050 K; and the switchability of the polar behavior is observed at room temperature, indicating ferroelectricity. An antiferromagnetic order was shown to occur below 440 K, followed by a spin reorientation resulting in a weak ferromagnetic order below 130 K. This observation of coexisting multiple ferroic orders demonstrates that hexagonal LuFeO$_3$ films are room-temperature multiferroics.
The structural transition at about 1000 °C, from the hexagonal to the orthorhombic phase of LuFeO3, has been investigated in thin films of LuFeO3. Separation of the two structural phases of LuFeO3 occurs on a length scale of micrometer, as visualized in real space using X-ray photoemission electron microscopy (X-PEEM). The results are consistent with X-ray diffraction and atomic force microscopy obtained from LuFeO3 thin films undergoing the irreversible structural transition from the hexagonal to the orthorhombic phase of LuFeO3, at elevated temperatures. The sharp phase boundaries between th…
Multiferroicity in the two-dimensional limit in hexagonal LuFeO3 films
Fudan University（复旦大学）；University of Science and Technology Beijing（北京科技大学）；Brookhaven National Laboratory（布鲁克海文国家实验室）；Hefei National Laboratory（合肥国家实验室）；Shanghai Research Center for Quantum Sciences（上海量子科学研究中心）；Zhangjiang Fudan International Innovation Center（张江复旦国际创新中心）；University of Nebraska, Lincoln（内布拉斯加大学林肯分校）
From the measurement of dielectric, ferroelectric, and magnetic properties we observe simultaneous ferroelectric and magnetic transitions around $\sim$600 K in orthorhombic LuFeO$_3$. We also observe suppression of the remanent polarization by $\sim$95\% under a magnetic field of $\sim$15 kOe at room temperature. The extent of suppression of the polarization under magnetic field increases monotonically with the field. These results show that even the orthorhombic LuFeO$_3$ is a room temperature multiferroic of type-II variety exhibiting quite a strong coupling between magnetization and polariz…
Neutron scattering techniques are used to investigate the crystalline and magnetic structure of LuFe$_{0.75}$Mn$_{0.25}$O$_{3}$ in bulk polycrystalline form. We find that the crystalline structure is described by the hexagonal P6$_{3}$cm space group similar to that of thin-film LuFeO$_{3}$, and that the system orders antiferromagnetically below T$_{N}$ = 134 K. Inelastic neutron scattering reveals nearest-neighbor superexchange parameters that are enhanced relative to LuMnO$_{3}$. The observation of significant diffuse scattering above T$_{N}$ demonstrates the frustrated nature of the system; …
We report on the magnetic structure and ordering of hexagonal LuFeO3 films grown by molecular-beam epitaxy (MBE) on YSZ (111) and Al2O3 (0001) substrates. Using a set of complementary probes including neutron diffraction, we find that the system magnetically orders into a ferromagnetically-canted antiferromagnetic state via a single transition between 138-155 K, while a paraelectric to ferroelectric transition occurs above 1000 K. The symmetry of the magnetic structure in the ferroelectric state implies that this material is a strong candidate for linear magnetoelectric coupling and control of…
We construct ferroelectric (LuFeO3)m/(LuFe2O4) superlattices with varying index m to study the effect of confinement on topological defects. We observe a thickness-dependent transition from neutral to charged domain walls and the emergence of fractional vortices. In thin LuFeO3 layers, the volume fraction of domain walls grows, lowering the symmetry from P63cm to P3c1 before reaching the non-polar P63/mmc state, analogous to the high-temperature ferroelectric to paraelectric transition. Our study shows how dimensional confinement stabilizes textures beyond those in bulk ferroelectric systems.
Hexagonal LuFeO$_3$ films have been studied using x-ray absorption and optical spectroscopy. The crystal splittings of Fe$^{3+}$ are extracted as $E_{e'}-E_{e"}$=0.7 eV and $E_{a_1'}-E_{e'}$=0.9 eV and a 2.0 eV optical band gap is determined assuming a direct gap. First-principles calculations confirm the experiments that the relative energies of crystal field splitting states do follow $E_{a_1'}>E_{e'}>E_{e"}$ with slightly underestimated values and a band gap of 1.35 eV.
Hexagonal LuFeO$_3$ has drawn a lot of research attention due to its contentious room-temperature multiferroicity. Due to the unstability of hexagonal phase in the bulk form, most experimental studies focused on LuFeO$_3$ thin films which can be stabilized by strain using proper substrates. Here we report on the hexagonal phase stabilization, magnetism, and magnetoelectric coupling of bulk LuFeO$_3$ by partial Sc-substitution of Lu. First, our first-principles calculations show that the hexagonal structure can be stabilized by partial Sc substitution, while the multiferroic properties includin…
Using combined theoretical and experimental approaches, we studied the structural and electronic origin of the magnetic structure in hexagonal LuFeO$_3$. Besides showing the strong exchange coupling that is consistent with the high magnetic ordering temperature, the previously observed spin reorientation transition is explained by the theoretically calculated magnetic phase diagram. The structural origin of this spin reorientation that is responsible for the appearance of spontaneous magnetization, is identified by theory and verified by x-ray diffraction and absorption experiments.
Electronic structures for the conduction bands of both hexagonal and orthorhombic LuFeO3 thin films have been measured using x-ray absorption spectroscopy at oxygen K (O K) edge. Dramatic differences in both the spectra shape and the linear dichroism are observed. These differences in the spectra can be explained using the differences in crystal field splitting of the metal (Fe and Lu) electronic states and the differences in O 2p-Fe 3d and O 2p-Lu 5d hybridizations. While the oxidation states has not changed, the spectra are sensitive to the changes in the local environments of the Fe3+ and L…
The magnetic interaction between rare-earth and Fe ions in hexagonal rare-earth ferrites (h-REFeO3), may amplify the weak ferromagnetic moment on Fe, making these materials more appealing as multiferroics. To elucidate the interaction strength between the rare-earth and Fe ions as well as the magnetic moment of the rare-earth ions, element specific magnetic characterization is needed. Using X-ray magnetic circular dichroism, we have studied the ferrimagnetism in h-YbFeO3 by measuring the magnetization of Fe and Yb separately. The results directly show anti-alignment of magnetization of Yb and …
We have observed enhancement and shift in the spin reorientation transition temperature as a consequence of coexistence of orthorhombic and hexagonal phases and higher aspect ratio in nanoscale LuFeO3. Nanoparticles and nanofibers of LuFeO3 are considered for this work. Nanoparticles have 75 % orthorhombic phase and 25 % hexagonal phase, while nanofibers have 23% orthorhombic phase and 77%-hexagonal phase. Larger aspect ratio in case of nanofibers is seen to help strain-stabilize the hexagonal phase in the material. Magnetic measurements show significant difference in the magnetic behavior and…
Hexagonal ferrites (h-RFeO$_3$, R=Y, Dy-Lu) have recently been identified as a new family of multiferroic complex oxides. The coexisting spontaneous electric and magnetic polarizations make h-RFeO$_3$ rare-case ferroelectric ferromagnets at low temperature. Plus the room-temperature multiferroicity and predicted magnetoelectric effect, h-RFeO$_3$ are promising materials for multiferroic applications. Here we review the structural, ferroelectric, magnetic, and magnetoelectric properties of h-RFeO$_3$. The thin film growth is also discussed because it is critical in making high quality single cr…
We report a study of magnetic dynamics in multiferroic hexagonal manganite HoMnO3 by far-infrared spectroscopy. Low-temperature magnetic excitation spectrum of HoMnO3 consists of magnetic-dipole transitions of Ho ions within the crystal-field split J=8 manifold and of the triangular antiferromagnetic resonance of Mn ions. We determine the effective spin Hamiltonian for the Ho ion ground state. The magnetic-field splitting of the Mn antiferromagnetic resonance allows us to measure the magnetic exchange coupling between the rare-earth and Mn ions.
Hexagonal RMnO3 manganites are improper ferroelectrics in which the electric polarization is a by-product of the tripling of the unit cell. In YMnO3, there is a second transition at ~ 920K whose nature remains unexplained. We argue that this transition can be seen as a sort of hidden order in which a residual symmetry displayed by the trimerization order parameter is spontaneously broken. This additional order gives rise to twelve structural domains instead of six, and structural domain boundaries that can be either ferroelectric or non-ferroelectric domain walls.
Using first-principles calculations we examine the band structures of ferromagnetic hexagonal manganites $\mathrm{YXO_3}$ (X=V, Cr, Mn, Fe and Co) in the nonpolar nonsymmorphic $P6_3/mmc$ space group. For $\mathrm{YVO_3}$ and $\mathrm{YCrO_3}$ we find a band inversion near the Fermi energy that generates a nodal ring in the $k_z=0$ mirror plane. We perform a more detailed analysis for these compounds and predict the existence of the topological "drumhead" surface states. Finally, we briefly discuss the low-symmetry polar phases (space group $P6_3cm$) of these systems, and show they can undergo…
We fabricated epitaxial thin films of hexagonal DyMnO3, which otherwise form in a bulk perovskite structure, via deposition on Pt(111)//Al2O3 (0001) and YSZ(111) substrates: each of which has in-plane hexagonal symmetry. The polarization hysteresis loop demonstrated the existence of ferroelectricity in our hexagonal DyMnO3 films at least below 70 K. The observed 2.2 uC/cm^2 remnant polarization at 25 K corresponded to a polarization enhancement by a factor of 10 compared to that of the bulk orthorhombic DyMnO3. Interestingly, this system showed an antiferroelectric-like feature in its hysteres…
Spectra of transmission and reflection coefficients of single crystalline Y-type hexaferrite Ba_(2)Mg_(2)Fe_(12)O_(22) are measured at Terahertz and infrared frequencies, 3 - 4500 c--1, and at temperatures 10 to 300 K, for polarization E prp c. Oscillator parameters of nineteen phonon lines allowed by the R3m crystal lattice symmetry are determined. Absorption lines assignment to vibrational modes of the lattice structural fragments is performed. Below the temperatures of 195 K and 50 K, corresponding to the zero field phase transitions to the proper screw and to the longitudinal-conical spin …
The spontaneous transformations associated with symmetry-breaking phase transitions generate domain structures and defects that may be topological in nature. The formation of these defects can be described according to the Kibble-Zurek mechanism, which provides a generic relation that applies from cosmological to interatomic lengthscales. Its verification is challenging, however, in particular at the cosmological scale where experiments are impractical. While it has been demonstrated for selected condensed-matter systems, major questions remain regarding e.g. its degree of universality. Here w…
Hexagonal rare-earth ferrite RFeO$_3$ family represents a unique class of multiferroics exhibiting weak ferromagnetism, and a strong coupling between magnetism and structural trimerization is predicted. However, the hexagonal structure for RFeO$_3$ remains metastable in conventional condition. We have succeeded in stabilizing the hexagonal structure of polycrystalline YbFeO$_3$ by partial Sc substitution of Yb. Using bulk magnetometry and neutron diffraction, we find that Yb$_{0.42}$Sc$_{0.58}$FeO$_3$ orders into a canted antiferromagnetic state with the Neel temperature $T_N$ ~ 165 K, below w…
We use a combination of symmetry analysis, phenomenological modelling and first-principles density functional theory to explore the interplay between the magnetic ground state and the detailed atomic structure in the hexagonal rare-earth manganites. We find that the magnetic ordering is sensitive to a breathing mode distortion of the Mn and O ions in the $ab$ plane, which is described by the K\textsubscript{1} mode of the high-symmetry structure. Our density functional calculations of the magnetic interactions indicate that this mode particularly affects the single-ion anisotropy and the inter…
Structural changes in REMnO3 (RE= Y, Ho, Lu) under high pressure were examined by synchrotron x-ray diffraction methods at room temperature. Compression occurs more readily in the ab plane than along the c-axis. Under hydrostatic pressure (~11 GPa), the atoms hold their approximate ambient fractional positions in the unit cell and the spontaneous polarization shows no significant change. With increased pressure, a pressure-induced hexagonal to orthorhombic phase transition was observed starting at ~ 22GPa for Lu(Y)MnO3. A small volume fraction of Lu(Y)MnO3 is converted to the orthorhombic phas…
We report an investigation of hexagonal Y_(1-x)Eu_xMnO_3 ceramics with x=0, 0.1 and 0.2 using infrared and THz spectroscopies in the temperature range between 5 and 900 K. The temperature dependence of the THz permittivity reveals a kink near the antiferromagnetic phase transition temperature T_N ~ 70 K giving evidence of a strong spin-lattice coupling. Below T_N two absorption peaks were revealed in the THz spectra close to 43 and 73 cm-1. While the first peak corresponds to a sharp antiferromagnetic resonance exhibiting softening on heating towards TN, the second one may be attributed to an …
We have investigated the effects of substituting In for Mn on the antiferromagnetic phase transition in YMnO3 using magnetic, dielectric, and specific heat measurements. We prepared a set of isostructural phase pure hexagonal YMn$_{1-x}$In$_{x}$O$_{3}$ samples having x=0 to x=0.9, which exhibit a systematic decrease of the antiferromagnetic ordering temperature with increasing In content. The multiferroic phase, which develops below TN, appears to be completely suppressed for x$\geq$0.5 in the temperature range investigated, which can be attributed solely to the dilution of magnetic interactio…
PbFe12O19 (PFO) powders in hexagonal structure have been synthesized by sol-gel process using lead acetate, glycerin and ferric acetylacetonate as the precursor. PbFe12O19 ceramics were obtained by sintering the PbFe12O19 powders at 1000\degree C for 1 hour. Distorted flaky hexahedron grains are frequently observed in the SEM images of sintered PbFe12O19 ceramics. Large spontaneous polarization was observed in PbFe12O19 ceramic at room temperature, exhibiting a clear ferroelectric hysteresis loop. The remnant polarization of PbFe12O19 ceramic is estimated to be Pr~21μC/cm2. The distortion of h…
We show that the improper ferroelectric phase transition in the multiferroic hexagonal manganites displays the same symmetry-breaking characteristics as those proposed in early-universe theories. We present an analysis of the Kibble-Zurek theory of topological defect formation applied to the hexagonal manganites, discuss the conditions determining the range of cooling rates in which Kibble-Zurek behavior is expected, and show that recent literature data are consistent with our predictions. We explore experimentally for the first time to our knowledge the cross-over out of the Kibble-Zurek regi…
A growth diagram of Lu-Fe-O compounds on MgO (111) substrates using pulsed laser deposition is constructed based on extensive growth experiments. The LuFe$_2$O$_4$ phase can only be grown in a small range of temperature and O$_2$ pressure conditions. An understanding of the growth mechanism of Lu-Fe-O compound films is offered in terms of the thermochemistry at the surface. Superparamagnetism is observed in LuFe$_2$O$_4$ film and is explained in terms of the effect of the impurity h-LuFeO$_3$ phase and structural defects .
Hexagonal YMnO_3 with space group P63cm is one of the rare examples of multiferroic materials that exhibit co-dependence of a robust ferroelectric phase along with antiferromagnetic ordering. This is primarily ascribed to tilting of the MnO_5 polyhedra driven by magnetoelectric coupling. We report on the effect of magnetic field at the atomic level in YMnO_3 by utilizing magnetic field and temperature dependent neutron diffraction measurements. We show that near the Néel temperature the lattice parameters, effective magnetic moment per site, Mn-O bond lengths and O-Mn-O bond angles show large …
Antisymmetric Dzyaloshinskii-Moriya (DM) interactions generating from the spin-orbit coupling induce various fascinating properties, like magnetoelectric (ME) effect, weak ferromagnetism and non-trivial topological spin textures like skyrmions, in real materials. Compared to their symmetric isotropic exchange counterpart, these interactions are generally of a weaker order of strength, creating modest twisting in the spin structure which results in weak ferromagntism or weak linear ME effect. Our proposed two-sublattice model, in contrast, predicts a hitherto unobserved, charge ordered non-coll…
Multiferroic hexagonal RMnO3 (R=rare earths) crystals exhibit dense networks of vortex lines at which six domain walls merge. While the domain walls can be readily moved with an applied electric field, the vortex cores were so far impossible to control. Our experiments demonstrate that shear strain induces a Magnus-type force pulling vortices and antivortices in opposite directions and unfolding them into a topological stripe domain state. We discuss the analogy between this effect and the current-driven dynamics of vortices in superconductors and superfluids.
Multiferroic materials have received an astonishing attention in the last decades due to expectations that potential coupling between distinct ferroic orders could inspire new applications and new device concepts. As a result, a new knowledge on coupling mechanisms and materials science has dramatically emerged. Multiferroic RMnO3 perovskites are central to this progress providing a suitable platform to tailor spin-spin and spin-lattice interactions. With views towards applications, development of thin films of multiferroic materials have also progressed enormously and nowadays thin film manga…
We report on optical studies of the thin films of multiferroic hexagonal (P.G. 6mm) rare-earth orthoferrites RFeO3 (R=Ho, Er, Lu) grown epitaxially on a (111)-surface of ZrO2(Y2O3) substrate. The optical absorption study in the range of 0.6-5.6 eV shows that the films are transparent below 1.9 eV; above this energy four broad intense absorption bands are distinguished. The absorption spectra are analyzed taking into account the unusual fivefold coordination of the Fe(3+) ion. Temperature dependence of the optical absorption at 4.9 eV shows anomaly at 124 K, which we attribute to magnetic order…
The complex interplay between the 3d and 4f moments in hexagonal ErMnO3 is investigated by magnetization, optical second harmonic generation, and neutron-diffraction measurements. We revise the phase diagram and provide a microscopic model for the emergent spin structures with a special focus on the intermediary phase transitions. Our measurements reveal that the 3d exchange between Mn^{3+} ions dominates the magnetic symmetry at 10 K < T < T_N with Mn^3+ order according to the Gamma_4 representation triggering 4f ordering according to the same representation on the Er^{3+}(4b) site. Below 10 …
We deduce the intrinsic conductivity properties of the ferroelectric domain walls around the topologically protected domain vortex cores in multiferroic YMnO3. This is achieved by performing a careful equivalent-circuit analysis of dielectric spectra measured in single-crystalline samples with different vortex densities. The conductivity contrast between the bulk domains and the less conducting domain boundaries is revealed to reach up to a factor 500 at room temperature, depending on sample preparation. Tunneling of localized defect charge carriers is the dominant charge-transport process in …
We report on epitaxial growth of single-phase [Pb(Zr0.57Ti0.43)O3]0.8[Pb(Fe2/3W1/3)O3]0.2 (PZT-PFW) solid-solution thin films using pulsed laser deposition. X-ray diffraction measurements reveal that the films have a tetragonal structure. The films exhibit ferroelectric properties and weak ferromagnetic responses at room temperature. Magnetoelectric effects were investigated; the nonlinear magnetoelectric coefficient was measured and found to be comparable to those of multiferroic hexagonal manganites, but at least two orders of magnitude smaller than that for polycrystalline PZT-PFW films.
Simultaneous co-existence of room-temperature(T) ferromagnetism and ferroelectricity in Fe doped BaTiO$_3$ (BTO) is intriguing, as such Fe doping into tetragonal BTO, a room-T ferroelectric (FE), results in the stabilization of its hexagonal polymorph which is FE only below $\sim$80K. Here, we investigate its origin and show that Fe-doped BTO has a mixed-phase room-temperature multiferroicity, where the ferromagnetism comes from the majority hexagonal phase and a minority tetragonal phase gives rise to the observed weak ferroelectricity. In order to achieve majority tetragonal phase (responsib…
Local structural measurements have been performed on hexagonal HoMnO3 in order to ascertain the specific changes in bond distances which accompany magnetic ordering transitions. The transition from paramagnetic to the antiferromagetic (noncollinear) phase near ~70 K is dominated by changes in the a-b plane Mn-Mn bond distances. The spin rotation transition near ~40 K involves both Mn-Mn and nearest neighbor Ho-Mn interactions while the low temperature transition below 10 K involves all interactions, Mn-Mn, Ho-Mn (nearest and next nearest) and Ho-Ho correlations. These changes in bond distances…
Hexagonal LuFe2O4 is a promising charge-order (CO) driven multiferroic material with high charge and spin ordering temperatures. The coexisting charge and spin orders on Fe3+/Fe2+ sites result in novel magnetoelectric behaviors, but the coupling mechanism between the charge and spin orders remains elusive. Here, by tuning external pressure, we reveal three correlated spin-charge ordered phases in LuFe2O4: i) a centrosymmetric incommensurate three-dimensional CO with ferrimagnetism, ii) a non-centrosymmetric incommensurate quasi-two-dimensional CO with ferrimagnetism, and iii) a centrosymmetric…
In the multiferroic hexagonal manganite HoMnO3, inelastic neutron scattering and synchrotron based THz spectroscopy have been used to investigate the spin waves associated to the Mn order together with Ho crystal field excitations. While the Mn order sets in first below 80 K, a spin reorientation occurs below 37 K, a rare feature in the rare earth manganites. We show that severalHo crystal field excitations are present in the same energy range as the magnons, and that they are all affected by the spin reorientation. Moreover, several anomalous features are observed in the excitations at low te…
To tune the magnetic properties of hexagonal ferrites, a family of magnetoelectric multiferroic materials, by atomic-scale structural engineering, we studied the effect of structural distortion on the magnetic ordering temperature (TN). Using the symmetry analysis, we show that unlike most antiferromagnetic rare-earth transition-metal perovskites, a larger structural distortion leads to a higher TN in hexagonal ferrites and manganites, because the K3 structural distortion induces the three-dimensional magnetic ordering, which is forbidden in the undistorted structure by symmetry. We also revea…
Hexagonal RMnO3 is a multiferroic compound with a giant spin-lattice coupling at an antiferromagnetic transition temperature [1]. Despite extensive studies over the past two decades, however, the origin and underlying microscopic mechanism of the strong spin-lattice coupling remain still very much elusive. In this study, we have tried to address this problem by measuring the thermal expansion and dielectric constant of doped single crystals Y1-xLuxMnO3 with x = 0, 0.25, 0.5, 0.75, and 1.0. From these measurements, we confirm that there is a progressive change in the physical properties with do…
We have carried out temperature-dependent inelastic neutron scattering measurements of YMnO3 over the temperature range 50 - 1303 K, covering both the antiferromagnetic to paramagnetic transition (70 K), as well as the ferroelectric to paraelectric transition (1258 K). Measurements are accompanied by first principles calculations of phonon spectra for the sake of interpretation and analysis of the measured phonon spectra in the room temperature ferroelectric (P63cm) and high temperature paraelectric (P63/mmc) hexagonal phases of YMnO3. The comparison of the experimental and first-principles ca…
Magnetic structure evolution of multiferroic hexagonal $YMn_{1-x}Fe_{x}O_{3}$ (${x} = 0, 0.05,$ and $0.1$) has been studied by carrying out detailed temperature-dependent neutron diffraction at zero- and 5T-fields. Thermodynamic data confirm antiferromagnetic ordering at $T_{N}$ in all the compositions. Our sub-$T_{N}$ neutron diffraction results assign the magnetic structure of pure $YMnO_3$ to $Γ_{1}$ irreducible representation. Over the perturbative-doping range, the magnetic configuration changes via $Γ_{1}+Γ_{2}$ for $YMn_{0.95}Fe_{0.05}O_{3}$ on to $Γ_{2}$ for $YMn_{0.9}Fe_{0.1}O_{3}$, a…
Hexagonal manganites REMnO3 (RE, rare earths) have attracted significant attention due to their potential applications as multiferroic materials and the intriguing physics associated with the topological defects. The two-dimensional (2D) and 3D domain and vortex structure evolution of REMnO3 is predicted using the phase-field method based on a thermodynamic potential constructed from first-principles calculations. In 3D spaces, vortex lines show three types of topological changes, i.e. shrinking, coalescence, and splitting, with the latter two caused by the interaction and exchange of vortex l…
Using x-ray resonant magnetic scattering and x-ray magnetic circular dichroism, techniques that are element specific, we have elucidated the role of Ho3+ in multiferroic HoMnO3. In zero field, Ho3+ orders antiferromagnetically with moments aligned along the hexagonal c direction below 40 K, and undergoes a transition to another magnetic structure below 4.5 K. In applied electric fields of up to 1x10^7 V/m, the magnetic structure of Ho3+ remains unchanged.
We present a systematic first-principles study of the phonon spectrum of hexagonal YMnO3 in ferroelectric (multiferroic) phase. We investigated in detail the low-energy phonon modes, their dispersion, symmetry, as well as the infrared optical properties of the crystal and determined the phonon density of states.
The improper ferroelectricity in YMnO$_3$ and other related multiferroic hexagonal manganites are known to cause topologically protected ferroelectric domains that give rise to rich and diverse physical phenomena. The local structure and structural coherence across the ferroelectric transition, however, were previously not well understood. Here we reveal the evolution of the local structure with temperature in YMnO$_3$ using neutron total scattering techniques, and interpret them with the help of first-principles calculations. The results show that, at room temperature, the local and average s…
We report a detailed high-resolution powder neutron diffraction investigation of the structural behaviour of the multiferroic hexagonal polymorph of YMnO3 between room temperature and 1403 K. The study was aimed at resolving previous uncertainties regarding the nature of the paraelectric- ferroelectric transition and the possibilities of any secondary structural transitions. We observe a clear transition at 1258 +/- 14 K corresponding to a unit cell tripling and a change in space group from centrosymmetric P6_3/mmc to polar P6_3cm. Despite the fact that this symmetry permits ferroelectricity, …
Multiferroic rare earth manganites attracted recent attention because of the coexistence of different types of magnetic and ferroelectric orders resulting in complex phase diagrams and a wealth of physical phenomena. The coupling and mutual interference of the different orders and the large magnetoelectric effect observed in several compounds are of fundamental interest and bear the potential for future applications in which the dielectric (magnetic) properties can be modified by the onset of a magnetic (dielectric) transition or the application of a magnetic (electric) field. The physical mec…
We investigate partially disordered antiferromagnetism in CoCl$_2$-2SC(NH$_2$)$_2$, in which a-b plane hexagonal layers are staggered along the c-axis, rather than stacked. A robust 1/3 state forms in applied magnetic fields which the spins are locked, varying neither as a function of temperature nor field. By contrast, in zero field, partial antiferromagnetic order occurs, in which free spins are available to create a Curie-like magnetic susceptibility. We report measurements of the crystallographic structure, and the specific heat, magnetization, and electric polarization down to $T$ = 50 mK…