我们对超导转变温度为$T_\textrm{c} \sim$ 4.2K的新超导体CeNi $_{0.8}$ Bi $_2$进行了粉末中子衍射。通过Rietveld分析确定了该化合物在室温下的结构参数。在5 K以下，观察到了传播矢量为$q$ =（0 0 0）的清晰的磁布拉格峰.观察到的磁布拉格峰强度可以用晶胞中两个Ce磁矩沿c轴反平行的磁结构来解释。在超导态下观察到磁性布拉格峰，表明该化合物中反铁磁有序和超导电性共存。在$T_\textrm{N}$以下，磁布拉格峰的强度随温度的降低而单调增加，在$T_\textrm{c}$处没有明显的反常现象，这与重费米子超导体中磁有序和超导电性共存的情况（如Cd掺杂的CeCoIn $_5$）明显不同.这些结果表明，Ce原子的4PDMATHABMT电子不与超导载流子耦合，CeNi $_{0.8}$ Bi $_2$的磁有序性几乎与超导性无关.
英文摘要：
We have performed powder neutron diffraction on the new superconductor, CeNi$_{0.8}$Bi$_2$ with a superconducting transtion temperature $T_\textrm{c} \sim$ 4.2 K. The structural parameters of this compound at room temperature are determined by Rietveld analysis. Below about 5 K, the clear magnetic Bragg peaks with propagation vector $q$=(0 0 0) are observed. The observed intensities of magnetic Bragg peaks can be explained by the magnetic structure that the two Ce moments in the unit cell are antiparallel along c axis. The magnetic Bragg peaks are observed in the superconducting state, indicating the coexistence of the antiferromagnetic ordering and the superconductivity in this compound. The intensity of magnetic Bragg peak monotonously increases with decreasing temperature below $T_\textrm{N}$ and does not exhibit apparent anomaly at $T_\textrm{c}$, obviously different from cases of heavy fermion superconductors in which the magnetic ordering and the superconductivity coexist, for example, Cd-doped CeCoIn$_5$. These results suggest that the 4$f$ electron of the Ce atom is not coupled with the superconducting carrier, and the magnetic ordering is almost independent of the superconductivity in CeNi$_{0.8}$Bi$_2$.
We have measured the temperature dependence of resistivity in single-crystalline CeNiGe$_{3}$ under hydrostatic pressure in order to establish the characteristic pressure-temperature phase diagram. The transition temperature to AFM-I phase $T_{\rm N1}$ = 5.5 K at ambient pressure initially increases with increasing pressure and has a maximum at $\sim$ 3.0 GPa. Above 2.3 GPa, a clear zero-resistivity is observed (SC-I phase) and this superconducting (SC) state coexists with AFM-I phase. The SC-I phase suddenly disappears at 3.7 GPa simultaneously with the appearance of an additional kink anomal…
Unconventional superconductivity in locally non-centrosymmetric CeNi$_2$As$_2$
Max Planck Institute for Chemical Physics of Solids（马克斯·普朗克固体化学物理研究所）；Institute for Quantum Materials and Technology, Karlsruhe Institute of Technology（卡尔斯鲁厄理工学院量子材料与技术研究所）
Superconductors have the potential to revolutionize technology due to their ability to have zero electrical resistance. However, superconductor materials require either low temperatures or high pressures to function in a superconductive state. Thus, researchers are now on the search for the first-ever room temperature, ambient pressure superconductor. Yet, recent discoveries have only shown superconductors that work at low temperatures with ambient pressure or room temperature with high pressures. The region between these two extremes has not been identified due to the number of variables that…
We propose to induce a time crystalline state in a high-$T_c$ superconductor, by optically driving a sum resonance of the Higgs mode and a Josephson plasma mode. The generic cubic process that couples these fundamental excitations converts driving of the sum resonance into simultaneous resonant driving of both modes, resulting in an incommensurate subharmonic motion. We use a numerical implementation of a semi-classical driven-dissipative lattice gauge theory on a three-dimensional layered lattice, which models the geometry of cuprate superconductors, to demonstrate the robustness of this moti…
We propose two possible new compounds, Ba$_2$CuO$_2$Fe$_2$As$_2$ and K$_2$CuO$_2$Fe$_2$Se$_2$, which hybridize the building blocks of two high temperature superconductors, cuprates and iron-based superconductors. These compounds consist of square CuO$_2$ layers and antifluorite-type Fe$_2$X$_2$ (X=As,Se) layers separated by Ba/K. The calculations of binding energies and phonon spectrums indicate that they are dynamically stable, which ensures that they may be experimentally synthesized. The Fermi surfaces and electronic structures of the two compounds inherit the characteristics of both cuprat…
Andreev reflection spectroscopy with unpolarized and highly spin-polarized currents has been utilized to study an intermetallic single-crystal superconductor NiBi3. Magnetoresistance at zero bias voltage of point contacts shows the occurrence and suppression of Andreev reflection by unpolarized and polarized current, respectively. The gap value, its symmetry and temperature dependence have been determined using an unpolarized current. The spin state in the NiBi3 sample is determined to be antiparallel using a highly spin-polarized current. The gap value 2Delta/kBT, gap symmetry and its tempera…
A new method to grow very high quality single crystals of the superconducting HgBa2CuO4+δ mercury cuprates is reported. The single crystals are platelet-shaped, with surfaces of high optical quality and good crystallographic properties. Annealing enables optimization of Tc up to Tcmax = 94 K. With adequate treatment, the doping level of the crystalline samples can be finely controlled in a wide under- and over-doped range. Complete structural characterization from single crystal X-ray diffraction data is given for the first time for different doping levels. The role of added gold on the doping…
We report the crystal structure, superconductivity and normal state properties of two iron-based materials, Li0.15(C3H10N2)0.32FeSe(P-4) and Lix(C3H10N2)0.32FeSe(P4/nmm, 0.25<x<0.4) with superconducting transition temperature from 40~46K. The determined crystal structures revealed a coupling between Li concentration and the oritation of 1,2-Diaminopropane molecules within the hyper expanded FeSe layers. Further fitting on resistivity in terms of the Lawence-Doniach model suggests the two superconductors belong to the quasi-two dimonsional system. With increasing temperature, a differences in c…
Mono-arsenide CrAs, endures a helical anti-ferromagnetic order transition at~ 265 K under ambient pressure. Recently, pressure-induced-superconductivity was discovered vicinity to the helical anti-ferromagnetic order in CrAs[Wei Wu et al., Nature Communications 5, 5508 (2014).]. However, the size of crystal grown via tin flux method is as small as 1 mm in longest dimension. In this work, we report the single crystal growth of CrAs with size of 1 * 5 * 1 mm3 via chemical vapor transport method and its physical properties.
Reinterpretation of the equilibrium magnetization of a Tl-based single crystal. Another phase transition in the mixed state of high-Tc superconductors?
Single Crystal Growth and Characterization of the Iron-Based Superconductor KFe2As2 Synthesized by KAs Flux Method
采用自熔法生长了厘米级片状KFe_2As_2单晶。使用商业不锈钢容器的封装技术允许持续超过2周的稳定晶体生长。研究了不同起始组成的K-Fe-As三元体系的最佳生长条件。采用KAs助熔剂生长出典型尺寸为15 mm × 10 mm × 0.4 mm的大单晶，晶体在3.4 K下具有明显的超导转变，转变宽度为0.2 K，剩余电阻率比超过450，表明样品质量良好。
Comparison of crystal structures and effects of Co substitution in a new member of Fe-1111 superconductor family AeFeAsF(Ae = Ca and Sr): a possible candidate for higher Tc superconductor
By varying the parameters controlling the growth of crystals, including the thermodynamic variables, such as temperature, pressure, and reagent composition and the kinetic factors, namely reaction time and cooling rate, we found the most appropriate conditions for the reproducible growth of the nonstoichiometric antiperovskite superconductors MgC1-xNi3-y. Bulk single crystals of MgC1-xNi3-y were grown by a self-flux method at 3 GPa and 1700 C using a mixture of Mg, C, and Ni powders in a molar ratio 1:1.25:3. The as-grown black colored crystals, mechanically extracted from solidified lump, exh…
Single crystals of Nd-substituted LuBa$_2$Cu$_4$O$_8$ were successfully grown by the KOH flux method. The single phase of Lu$_{1-x}$Nd$_x$Ba$_2$Cu$_4$O$_8$ [(Lu,Nd)124] formed at $x = 0.2$. The compound crystallized as orthorhombic Ammm structure with lattice constants of a = 3.835(3) Å, b = 3.879(2) Å and c = 27.195(6) Å. Single crystal structural analysis demonstrated that the Nd ion partially occupied the Lu site. The (Lu,Nd)124 exhibited the superconducting transition at ~75 K in the magnetic susceptibility and resistivity. The $T_c$ and the c-axis of the (Lu,Nd)124 corresponded to Tm124. …
The details of the superconducting to quantum metal transition (SQMT) at T=0 are an open problem that invokes much interest in the nature of this exotic and unexpected ground state1-3. However, the SQMT was not yet investigated in a crystalline 2D superconductor with coexisting and fluctuating quantum orders. Here, we report the observation of a SQMT in 2D ion-gel gated 1T-TiSe24, driven by magnetic field. A field-induced crossover between Bose quantum metal and vortex quantum creeping with increasing field is observed. We discuss the interplay between superconducting and CDW fluctuations (dis…
We report on the first successful growth of single crystals of the noncentrosymmetric superconductor Mo$_3$Al$_2$C obtained by means of a cubic-anvil, high-pressure and high-temperature technique. Composition, structure, and normal-state transport properties of the crystals were studied by means of X-ray diffraction, energy-dispersive X-ray spectroscopy, magnetic susceptibility and resistivity measurements as a function of temperature. Variations in critical temperature ($T_c$) between 8.6 and 9.3 K were observed, probably due to the slightly different carbon stoichiometry of the samples. Sing…
We report single-crystal growth of La$_{0.34}$Na$_{0.66}$Fe$_2$As$_2$ iron-based superconductor with the size of several millimeters. The samples were accidentally obtained in trying to grow LaFeAsO$_{1-y}$F$_y$ ( $y \geq$ 0.8 ) single crystals with NaAs and NaF flux. The sample shows both antiferromagnetic and structural transitions at 106 K. The superconducting transition temperature is about 27 K with the superconducting anisotropy of about 1.9. These values and the temperature dependence of the Hall coefficient suggest that La$_{0.34}$Na$_{0.66}$Fe$_2$As$_2$ belongs to hole-doped "122" fam…
When quasiparticles in a BCS superconductor recombine into Cooper pairs, phonons are emitted within a narrow band of energies above the pairing energy at 2$Δ$. We show that a phonon bandgap restricting the escape of recombination phonons from a superconductor can increase the quasiparticle recombination lifetime by more than an order of magnitude. A phonon bandgap can be realized and matched to the recombination energy with a phononic crystal, a periodically-patterned dielectric membrane. We discuss in detail the non-equilibrium quasiparticle and phonon distributions that arise in a supercondu…
Majorana Kramers pairs emerged on surfaces of time-reversal-invariant topological crystalline superconductors show the Ising anisotropy to an applied magnetic field. We clarify that crystalline symmetry uniquely determines the direction of the Majorana Ising spin for given irreducible representations of pair potential, deriving constraints to topological invariants. Besides, necessary conditions for nontrivial topological invariants protected by the n-fold rotational symmetry are shown.
We have investigated the in-plane anisotropy of the c-axis magnetoresistance for single crystals of a BiCh2-based superconductor LaO0.5F0.5BiSSe under in-plane magnetic fields. We observed two-fold symmetry in the c-axis magnetoresistance in the ab-plane of LaO0.5F0.5BiSSe while the crystal possessed a tetragonal square plane with four-fold symmetry. The observed symmetry lowering in magnetoresistance from the structural symmetry may be related to the nematic states, which have been observed in the superconducting states of several unconventional superconductors.