Large magnetocaloric effect has been observed in Mn3O4 around its ferrimagnetic transition at TN = 42.75 K. Field-induced isothermal entropy changes (\DeltaS) were derived from both magnetic and calorimetric techniques. The maximum |\DeltaS| and adiabatic temperature change (ΔTad) at TN are 11 J kg-1 K-1 and 1.9 K, respectively, for a magnetic field change of 20 kOe. Moreover, it is found that the complex magnetic phase transitions taking place below TN produce additional -but smaller- features on \DeltaS(T).
Solid solutions of nominal composition [ZnGa$_2$O$_4$]$_{1-x}$[Fe$_3$O$_4$]$_x$, of the semiconducting spinel ZnGa$_2$O$_4$ with the ferrimagnetic spinel Fe$_3$O$_4$ have been prepared with $x$ = 0.05, 0.10, and 0.15. All samples show evidence for long-range magnetic ordering with ferromagnetic hysteresis at low temperatures. Magnetization as a function of field for the $x$ = 0.15 sample is S-shaped at temperatures as high as 200 K. Mössbauer spectroscopy on the $x$ = 0.15 sample confirms the presence of Fe$^{3+}$, and spontaneous magnetization at 4.2 K. The magnetic behavior is obtained witho…
Spinel Li$_x$Mn$_2$O$_4$ is a key cathode material that is used extensively in commercial Li-ion batteries. A challenge with this material has been that the capacity of the battery fades with cycling, an effect that can be traced to the presence of an anti-ferromagnetic insulator phase in the fully lithiated LiMn$_2$O$_4$ (LMO) and the associated charge disproportionation that drives distortions of the MnO$_6$ octahedra. Here, by combining x-ray magnetic Compton scattering experiments with parallel first-principles computations, we show that the anti-ferromagnetic phase of LMO is surrounded by…
We report a correlation between structural phase stability and magnetic properties of Co2FeO4 spinel oxide. We employed mechanical alloying and subsequent annealing to obtain the desired samples. The particle size of the samples changes from 25 nm to 45 nm. The structural phase separation of samples, except sample annealed at 9000C, into Co rich and Fe rich spinel phase has been examined from XRD spectrum, SEM picture, along with EDAX spectrum, and magnetic measurements. The present study indicated the ferrimagnetic character of Co2FeO4, irrespective of structural phase stability. The observat…
Magnetocaloric effect (MCE) in TbCo2-xFex has been studied by dc magnetization measurements.On substituting Fe in TbCo2, not only the magnetic transition temperature is tuned to room temperature, but also the operating temperature range for MCE is increased from 50 K for TbCo2 to 95 K for TbCo1.9Fe0.1. The maximum magnetic entropy change (-ΔSM) for TbCo1.9Fe0.1 is found to be 3.7 J kg-1 K-1 for a 5 T field change, making it a promising candidate for magnetic refrigeration near room temperature. The temperature dependent neutron diffraction study shows a structural phase transition (from cubic …
We assess the potential of the ferrimagnetic spinel ferrites CoFe2O4 and NiFe2O4 to act as spin filtering barriers in magnetic tunnel junctions. Our study is based on the electronic structure calculated by means of first-principles density functional theory within different approximations for the exchange correlation energy. We show that, in agreement with previous calculations, the densities of states suggest a lower tunneling barrier for minority spin electrons, and thus a negative spin-filter effect. However, a more detailed analysis based on the complex band-structure reveals that both sig…
Sintered samples of a spinel oxide LiFeCr4O8, where Cr3+ and Fe3+ ions have localized moments, were found to show a large magnetic-field-induced volume increase approaching 500 ppm by applying a magnetic field of 9 T. This large volume increase appeared only at around 30 K. At 30 K, a spin-reorientation transition from ferrimagnetic to conical order occurs, giving rise to this large volume increase. The coexistence of ferrimagnetic and conical phases at this transition was found to be important, suggesting that such a large magnetic-field-induced volume change can be realized at various magnet…
We demonstrate that the onset of complex spin orders in ACr$_2$O$_4$ spinels with magnetic A$=$Co, Fe and Cu ions lowers the lattice symmetry. This is clearly indicated by the emergence of anisotropic lattice dynamics -- as evidenced by the pronounced phonon splittings -- even when experiments probing static distortions fail. We show that the crystal symmetry in the magnetic phase is reduced from tetragonal to orthorhombic for FeCr$_2$O$_4$ and CuCr$_2$O$_4$ with Jahn-Teller active A-site ions. The conical spin structure in FeCr$_2$O$_4$ is also manifested in the phonon frequencies. In contras…
We investigate the magnetic properties of the isostructural spinel-spinel interface of NiMn2O4(NMO)-Fe3O4. Although the magnetic transition temperature of the NMO film is preserved, both bulk and interface sensitive measurements demonstrate that the interface exhibits strong interfacial magnetic coupling up to room temperature. While NMO thin films have a ferrimagnetic transition temperature of 60K, both NiFe2O4 and MnFe2O4 are ferrimagnetic at room temperature. Our experimental results suggest that these magnetic properties arise from a thin interdiffused region of (Fe,Mn,Ni)3O4 at the interf…
Structural, magnetic and magnetocaloric properties of Mn2-xCrxSb compounds have been studied. In these compounds a first order magnetic phase transition from the ferrimagnetic to the antiferromagnetic state occurs with decreasing temperature, giving rise to giant inverse magnetocaloric effects that can be tuned over a wide temperature interval through changes in substitution concentration. Entropy changes as high as 7.5 J/kgK have been observed, and a composition independent entropy change is obtained for several different concentrations/working temperatures, making these compounds suitable ca…
The manipulation of mesoscale domain wall phenomena has emerged as a powerful strategy for designing ferroelectric responses in functional devices, but its full potential has not yet been realized in the field of magnetism. We show that mechanically strained samples of Mn$_3$O$_4$ and MnV$_2$O$_4$ exhibit a stripe-like patterning of the bulk magnetization below known magnetostructural transitions, similar to the structural domains reported in ferroelectric materials. Building off our previous magnetic force microscopy data, we use small angle neutron scattering to show that these patterns exte…
Unraveling the Origin of Ferrimagnetic Signatures in (Fe,Mn,Ga)2O3 Bixbyites: The Role of Structurally-Undetectable Spinel Impurities
Kirensky Institute of Physics, Federal Research Center KSC SB RAS（基连斯基物理研究所，俄罗斯科学院西伯利亚分院克拉斯诺亚尔斯克科学中心）；Siberian Federal University（西伯利亚联邦大学）；Far Eastern State Transport University（远东国立交通大学）；National Research Centre “Kurchatov Institute”（库尔恰托夫国家研究中心）；Professor V.F. Voino-Yasenetsky Krasnoyarsk State Medical University（V.F.沃伊诺-亚涅茨基克拉斯诺亚尔斯克国立医科大学）；Institute of Physics, Kazan Federal University（喀山联邦大学物理研究所）；Siberian State University of Science and Technologies（西伯利亚国立科学技术大学）；Federal Research Center "Krasnoyarsk Science Center of the Siberian Branch of the Russian Academy of Sciences"（俄罗斯科学院西伯利亚分院克拉斯诺亚尔斯克科学中心联邦研究中心）；Synchrotron Radiation Facility - Siberian Circular Photon Source "SKlF" Boreskov Institute of Catalysis of Siberian Branch of the Russian Academy of Sciences (SRF "SKIF")（俄罗斯科学院西伯利亚分院博列斯科夫催化研究所同步辐射设施——西伯利亚环形光子源“SKIF”）
The magnetic phase transition and magnetocaloric properties of mineral and synthetic melanostibite Mn$_2$FeSbO$_6$ with ilmenite-type structure have been studied. Mn$_2$FeSbO$_6$ orders ferrimagnetically below 270 K and is found to undergo a second-order magnetic phase transition. The associated magnetic entropy change amounts to 1.7 J/kgK for the mineral and 1.8 J/kgK synthetic melanostibite for 5 T field change. For the synthetic Mn$_2$FeSbO$_6$ the adiabatic temperature change was estimated from magnetic- and specific heat measurements and amounts to 0.2 K in 1 T field change. Perspectives …
Enhancement in Magnetic and Magnetocaloric Properties of CoFe2O4 Nanofibers at Lower Temperatures
Cadi- Ayyad University（卡迪·阿亚德大学）；Jozef Stefan Institute（约瑟夫·斯蒂芬研究所）；University of Picardie Jules Verne（皮卡第朱尔·凡尔纳大学）；Institute of Mathematics, Physics and Mechanics & University of Ljubljana, Faculty of Civil and Geodetic Engineering（卢布尔雅那大学土木与测量工程学院数学、物理与力学研究所）
We report high temperature synchrotron X-ray diffraction (SXRD), dc magnetization and current-voltage (I-V) characteristics for the samples of Co$_{2.75}$Fe$_{0.25}$O$_4$ ferrite. The material was prepared by chemical reaction of the Fe and Co nitrate solutions at pH = 11 and subsequent annealing at temperatures 200 0C, 500 0C and 900 0C. The measurements were performed by cycling the temperature from 300 K to high temperature (warming mode) and return back to 300 K (cooling mode). The SXRD patterns indicated a fine bi-phased cubic spinel structure in the highly Co rich spinel oxide. Magnetiza…
We perform ultrasound velocity measurements on a single crystal of nearly-metallic spinel Co$_{1.21}$V$_{1.79}$O$_4$ which exhibits a ferrimagnetic phase transition at $T_C \sim$ 165 K. The experiments reveal a variety of elastic anomalies in not only the paramagnetic phase above $T_C$ but also the ferrimagnetic phase below $T_C$, which should be driven by the nearly-itinerant character of the orbitally-degenerate V 3$d$ electrons. In the paramagnetic phase above $T_C$, the elastic moduli exhibit elastic-mode-dependent unusual temperature variations, suggesting the existence of a dynamic spin-…
Spinel oxides are an ideal setting to explore the interplay between configurational entropy, site selectivity, and magnetism in high entropy oxides. In this work we characterize the magnetic properties of the spinel (Cr,Mn,Fe,Co,Ni)$_3$O$_4$ and study the evolution of its magnetism as a function of non-magnetic gallium substitution. Across the range of compositions studied here, from 0% to 40% Ga, magnetic susceptibility and powder neutron diffraction measurements show that ferrimagnetic order is robust in the spinel HEO. However, we also find that the ferrimagnetic order is highly tunable, wi…
Origin of magnetically dead layers in spinel ferrites $M\text{Fe}_2\text{O}_4$ grown on $\text{Al}_2\text{O}_3$: Effects of post-deposition annealing studied by XMCD
Multiferroicity in the Presence of Exchange Bias: The Case of Spinel CoMn2O4
School of Physical Science, Jawaharlal Nehru University（贾瓦哈拉尔·尼赫鲁大学物理科学学院）；Special Centre for Nanoscience, Jawaharlal Nehru University（贾瓦哈拉尔·尼赫鲁大学纳米科学特别中心）
Structural, electronic, and magnetic properties of modified cubic spinel compound LiNi$_{0.5}$Mn$_{1.5}$O$_{4}$ are studied via x-ray diffraction, resistivity, DC and AC magnetization, heat capacity, neutron diffraction, $^7$Li nuclear magnetic resonance, magnetocaloric effect, magnetic relaxation, and magnetic memory effect experiments. We stabilized this compound in a cubic structure with space group $P4_{3}32$. It exhibits semiconducting character with an electronic band gap of $Δ/k_{\rm B} \simeq 0.4$ eV. The interaction within each Mn$^{4+}$ and Ni$^{2+}$ sub-lattice and between Mn$^{4+}$…
In this work we present a study of the low temperature magnetic phases of polycrystalline MnCr$_2$O$_4$ spinel through dc magnetization and ferromagnetic resonance spectroscopy (FMR). Through these experiments we determined the main characteristic temperatures: T$_C$ $\sim$41 K and T$_H$ $\sim$18 K corresponding, respectively, to the ferrimagnetic order and to the low temperature helicoidal transitions. The temperature evolution of the system is described by a phenomenological approach that considers the different terms that contribute to the free energy density. Below the Curie temperature th…
Ultra-Soft Ferrimagnetism in a High-Entropy Spinel Oxide Driven by Site-Selective Cation Disorder
Thapar Institute of Engineering and Technology（塔帕尔工程技术学院）；UGC-DAE Consortium for Scientific Research（UGC-DAE科学研究联盟）；Univ. Bordeaux, CNRS, Bordeaux INP, ICMCB, UMR 5026（波尔多大学、法国国家科学研究中心、波尔多国立理工学院、材料与化学研究组合中心）；Laboratory Crismat, UMR6508 CNRS, Normandie University, ENSICAEN, UNICAEN（Crismat实验室、法国国家科学研究中心联合研究实验室6508、诺曼底大学、恩西辛高等学院、卡昂大学）
Varying the substrate temperature changes structural and magnetic properties of spinel ferrite NZFO thin films. XRD of films grown at different temperature display only 004 reflections, without any secondary peaks, showing growth orientation along the c axis. We find an increase in crystalline quality of these thin films with the rise of substrate temperature. The surface topography of the thin films grown on various growth temperatures conditions reveal that these films are smooth with low roughness, however the thin films grown at 800 C exhibit lowest average and rms roughness among all thin…
A comparative study of the non-equilibrium magnetic phenomena (magnetic blocking, memory, exchange bias and aging effect) has been presented for ferrimagnetic Co$_{1.75}$Fe$_{1.25}$O$_4$ (CFO) and its composite with non-magnetic BaTiO$_3$ (BTO). Synchrotron X-Ray diffraction patterns have confirmed coexistence of CFO and BTO structures in composite, but magnetic spin dynamics have been remarkably modified. The blocking phenomenon of ferrimagnetic domains below the room temperature has been studied by different modes of (zero field cooled and field cooled) magnetic measurements in collaboration…
From Chemical Complexity to Tunable Magnetic Ordering in Highly Disordered High-Entropy Spinel Oxides
Thapar Institute of Engineering and Technology（塔帕尔工程技术学院）；UGC-DAE Consortium for Scientific Research（UGC-DAE科学研究联盟）；Freie Universität Berlin（柏林自由大学）；Helmholtz Zentrum Berlin für Materialien und Energie（柏林亥姆霍兹材料与能源中心）；Normandie University（诺曼底大学）
A systematic study using neutron diffraction and magnetic susceptibility are reported on Mn substituted ferrimagnetic inverse spinel Ti$_{1-x}$Mn$_{x}$Co$_2$O$_4$ in the temperature interval 1.6 K $\leq$ $T$ $\leq$ 300 K. Our neutron diffraction study reveals cooperative distortions of the $T$O$_6$ octahedral for all the Jahn-Teller active ions $T$ = Mn$^{3+}$, Ti$^{3+}$ and Co$^{3+}$, which are confirmed by the X-ray photoelectron spectroscopy. Two specific compositions ($x$ = 0.2 and 0.4) have been chosen because of their unique features: noncollinear Yafet-Kittel type ordering, and weak tet…
The 3d-metal chromites ACr$_2$O$_4$ where A is a magnetic ion, show the paramagnetic to ferrimagnetic phase transition at T$_C$ while for non-magnetic A-site ion, ACr$_2$O$_4$ show paramagnetic to antiferromagnetic phase transition at T$_N$. In this report, we present the detailed study of magnetic and the magnetocaloric effect (MCE) of the 3d-metal chromites ACr$_{2}$O$_{4}$ (where A = Mn, Fe, Co, Ni, Cu, and Zn) near T$_C$ and T$_N$. We find the magnitude of MCE (-$Δ$S$_M$) decreases on decreasing the magnetic moment of A-site ion with an exception for CuCr$_{2}$O$_{4} $. Additionally, to kn…
We present the magnetic properties of complete solid solutions of ZnCr$_2$O$_4$ and CoCr$_2$O$_4$: two well-studied oxide spinels with very different magnetic ground states. ZnCr$_2$O$_4$, with non-magnetic $d^{10}$ cations occupying the A site and magnetic $d^3$ cations on the B site, is a highly frustrated antiferromagnet. CoCr$_2$O$_4$, with magnetic $d^7$ cations (three unpaired electrons) on the A site as well, exhibits both Néel ferrimagnetism as well as commensurate and incommensurate non-collinear magnetic order. More recently, CoCr$_2$O$_4$ has been studied extensively for its polar b…
The spinel NiCr$_2$O$_4$ is known to show a ferrimagnetic transition at $T_c = 70$~K, and magneto-structural transitions at $T_s = 30$~K and $T_o = 20$~K\@. We present a detailed magnetic and magnetocaloric effect (MCE $= -ΔS_{M}(T)$) study across these transitions. The $-ΔS_{M}(T)$ shows a positive anomaly at $T_c$, $T_s$, and $T_o$. In addition to these anomalies, we report a new unreported feature at $T \approx 8.5$~K where $-ΔS_{M}(T)$ shows a negative anomaly or the inverse MCE. An Arrot plot of the isothermal magnetization data reveals important information about the nature of the possib…
At 300 K, Y$_{0.9}$Gd$_{0.1}$Fe$_{2}$H$_{x}$ hydrides crystallize sequentially with increasing H concentration in various structures related to a lowering of the cubic MgCu$_{2}$ type structure of the parent alloy: cubic C1, monoclinic M1, cubic C2, monoclinic M2, cubic C3, orthorhombic O. Above 300 K, they undergo a first-order transition at a T$_{O-D}$ temperature driven by order-disorder of hydrogen atoms into interstitial sites. Their magnetic, structural and magnetocaloric properties have been investigated through magnetic measurements, and high-resolution synchrotron diffraction experime…
Disentangling the contributions of individual cations to magnetic order in a spinel high entropy oxide
University of British Columbia（不列颠哥伦比亚大学）；Max Planck Institute for Chemical Physics of Solids（马克斯·普朗克固体化学物理研究所）；University of Saskatchewan（萨斯喀彻温大学）；Canadian Light Source（加拿大光源）
We report the observation of large magnetocaloric effect near room temperature in antipervoskite SnCMn3. The maximal magnetic entropy change at the first-order ferrimagnetic-paramagnetic transition temperature (TC 279 K) is about 80.69mJ/cm3 K and 133mJ/cm3 K under the magnetic field of 20 kOe and 48 kOe, respectively. These values are close to those of typical magnetocaloric materials. The large magnetocaloric effect is associated with the sharp change of lattice, resistivity and magnetization in the vicinity of TC. Through the measurements of Seebeck coefficient and normal Hall effect, the t…
We report electrical resistivity, magnetic and magnetocaloric properties in Sm0.7-xLaxSr0.3MnO3 series for x= 0, 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.65, and 0.7. All the compounds show second order paramagnetic to ferromagnetic transition at T = Tc which is tunable anywhere between 83 K and 373 K with a proper choice of the doping level (x). The insulating ferromagnet x= 0 transforms to ferromagnetic metal below Tc for x= 0.1 and the insulator-metal transition temperature shifts up with increasing x. The magnetization (M) exhibits an interesting behavior as a function of temperature and doping lev…
Motivated by recent experiments, we present a comprehensive theoretical study of the geometrically frustrated strongly correlated magnetic insulator Mn$_3$O$_4$ spinel oxide based on a microscopic Hamiltonian involving lattice, spin and orbital degrees of freedom. Possessing the physics of degenerate e$_g$ orbitals, this system shows a strong Jahn-Teller effect at high temperatures. Further, careful attention is paid to the special nature of the superexchange physics arising from the 90$^o$ Mn-O-Mn bonding angle. The Jahn-Teller and superexchange-based orbital-spin Hamiltonians are then analys…
Cubic spinel CoCr2O4 has attained recent attention due to its multiferroic properties. However, the Co site substitution effect on the structural and magnetic properties has rarely been studied in thin film form. In this work, the structural and magnetic properties of Co1-xNixCr2O4 (x = 0, 0.5) epitaxial thin films deposited on MgAl2O4 (100) and MgO (100) substrates to manipulate the nature of strain in the films using pulsed laser deposition (PLD) technique are presented. The epitaxial nature of the films was confirmed through X-ray diffraction (XRD) and Rutherford backscattering spectrometry…
We report the magnetic properties of mechanically milled Co$_{0.2}$Zn$_{0.8}$Fe$_2$O$_4$ spinel oxide. After 24 hours milling of the bulk sample, the XRD spectra show nanostructure with average particle size $\approx$ 20 nm. The as milled sample shows an enhancement in magnetization and ordering temperature compared to the bulk sample. If the as milled sample is annealed at different temperatures for the same duration, recrystallization process occurs and approaches to the bulk structure on increasing the annealing temperatures. The magnetization of the annealed samples first increases and the…
We examine the effect of small amounts of magnetic substituents in the $A$ sites of the frustrated spinels MgCr$_2$O$_4$ and ZnCr$_2$O$_4$. Specifically we look for the effects of spin and lattice disorder on structural changes accompanying magnetic ordering in these compounds. Substitution of Co$^{2+}$ on the non-magnetic Zn$^{2+}$ site in Zn$_{1-x}$Co$_{x}$Cr$_2$O$_4$ where 0\,$<$\,$x$\,$\leq$\,0.2 completely suppresses the spin-Jahn-Teller distortion of ZnCr$_2$O$_4$ although these systems remain frustrated, and magnetic ordering occurs at very low temperatures of $T$\,$<$\,20\,K. On the ot…
We report magnetic behaviour of MnCr$_2$O$_4$, which belongs to a special class of spinel, known as chromite. Bulk MnCr$_2$O$_4$ shows a sequence of magnetic states, which follows paramagnetic (PM) to collinear ferrimagnetic (FM) state below T$_C$ $\sim$ 45 K and collinear FM state to non-collinear FM state below T$_S$ $\sim$ 18 K. The non-collinear spin structure has been modified on decreasing the particle size, and magnetic transition at T$_S$ decreases in nanoparticle samples. However, ferrimagnetic order is still dominating in nanoparticles, except the observation of superparamagnetic lik…
The search for room-temperature magnetocaloric materials for refrigeration has led to investigations of double perovskites. In particular, a puzzle has appeared in the La$_2$MnNiO$_6$, La$_2$MnCoO$_6$ and La$_2$MnFeO$_6$ family of compounds. They share the same crystal structure, but while La$_2$MnNiO$_6$ and La$_2$MnCoO$_6$ are ferromagnets below room temperature, La$_2$MnFeO$_6$, contrary to simple expectations, is a ferrimagnet. To solve this puzzle, we use density-functional theory calculations to investigate the electronic structure and magnetic exchange interactions of the ordered double…
High-throughput density functional calculations are used to investigate the effect of interstitial B, C and N atoms on 21 alloys reported to crystallize in the cubic Cu$_3$Au structure. It is shown that the interstitials can have a significant impact on the magneto-crystalline anisotropy energy (MAE), the thermodynamic stability and the magnetic ground state structure, making these alloys interesting for hard magnetic, magnetocaloric and other applications. For 29 alloy/interstitial combinations the formation of stable alloys with interstitial concentrations above 5\% is expected. In Ni$_3$Mn …
The inverse spinel ferrimagnetic NiCo$_2$O$_4$ possesses high magnetic Curie temperature $T_C$, high spin polarization, and strain-tunable magnetic anisotropy. Understanding the thickness scaling limit of these intriguing magnetic properties in NiCo$_2$O$_4$ thin films is critical for their implementation in nanoscale spintronic applications. In this work, we report the unconventional magnetotransport properties of epitaxial (001) NiCo$_2$O$_4$ films on MgAl$_2$O$_4$ substrates in the ultrathin limit. Anomalous Hall effect measurements reveal strong perpendicular magnetic anisotropy for films …
The spinel-structured lithium manganese oxide (LiMn$_2$O$_4$) is a material currently used as cathode for secondary lithium-ion batteries, but whose properties are not yet fully understood. Here, we report a computational investigation of the inversion thermodynamics and electronic behaviour of LiMn$_2$O$_4$ derived from spin-polarised density functional theory calculations with a Hubbard Hamiltonian and long-range dispersion corrections (DFT+$U-$D3). Based on the analysis of the configurational free energy, we have elucidated a partially inverse equilibrium cation distribution for the LiMn$_2…
We have investigated the structural, magnetic, thermodynamic, and dielectric properties of polycrystalline CoCr$_2$O$_4$, an insulating spinel exhibiting both ferrimagnetic and spiral magnetic structures. Below $T_c$ = 94 K the sample develops long-range ferrimagnetic order, and we attribute a sharp phase transition at $T_N$ $\approx$ 25 K with the onset of long-range spiral magnetic order. Neutron measurements confirm that while the structure remains cubic at 80 K and at 11 K; there is complex magnetic ordering by 11 K. Density functional theory supports the view of a ferrimagnetic semiconduc…
We have investigated the dielectric anomalies associated with spin ordering transitions in the tetragonal spinel Mn$_3$O$_4$, using thermodynamic, magnetic, and dielectric measurements. We find that two of the three magnetic ordering transitions in Mn$_3$O$_4$ lead to decreases in the temperature dependent dielectric constant at zero applied field. Applying a magnetic field to the polycrystalline sample leaves these two dielectric anomalies practically unchanged, but leads to an increase in the dielectric constant at the intermediate spin-ordering transition. We discuss possible origins for th…
We report on the synthesis and structural characterization of the magnetocaloric FeMnP$_{0.75}$Si$_{0.25}$ compound. Two types of samples (as quenched and annealed) were synthesized and characterized structurally and magnetically. We have found that minute changes in the degree of crystallographic order causes a large change in the magnetic properties. The annealed sample, with higher degree of order is antiferromagnetic with a zero net moment. The as-quenched sample has a net moment of 1.26 $μ_B$/f.u. and ferrimagnetic-like behavior. Theoretical calculations give rather large values for the F…
The ferrimagnetic spinel oxide Zn(x)Fe(3-x)O(4) combines high Curie temperature and spin polarization with tunable electrical and magnetic properties, making it a promising functional material for spintronic devices. We have grown epitaxial thin films with 0<=x<=0.9 on MgO(001) substrates with excellent structural properties both in pure Ar atmosphere and an Ar/O2 mixture by laser molecular beam epitaxy. We find that the electrical conductivity and the saturation magnetization can be tuned over a wide range during growth. Our extensive characterization of the films provides a clear picture of …
Cementite-type carbides are of interest for magnetocaloric applications owing to their temperature- or pressure-induced magnetic phase transition. Here, using first-principles calculations, we investigate the magnetism and the magnetic phase transition in iron carbide (Fe3C) with the substitution of Cr atoms at Fe sites with the strain effect. The presence of Cr atoms is found to give rise to a second-order magnetic phase transition from a ferromagnetic phase for Fe3C to a nonmagnetic phase in chromium carbide (Cr3C).While the ternary Fe2CrC and Cr2FeC compounds prefer the ferrimagnetic ground…
We report on the spin-Hall magnetoresistance (SMR) and spin Seebeck effect (SSE) in multiferroic CoCr2O4 (CCO) spinel thin films with Pt contacts. We observe a large enhancement of both signals below the spin-spiral (Ts = 28 K) and the spin lock-in transitions (T_{lock_in} = 14 K). The SMR and SSE response in the spin lock-in phase are one order of magnitude larger than those observed at the ferrimagnetic transition temperature (Tc = 94 K), which indicates that the interaction between spins at the Pt|CCO interface is more efficient in the non-collinear magnetic state below Ts and T_{lock-in}. …
The field of double perovskites is now advancing to three magnetic elements on the A, B and B$'$ sites. A series of iridium-based double perovskite compounds, $Ln_2$CoIrO$_6$ ($Ln$ = Eu, Tb, Ho) with three magnetic elements were synthesized as polycrystalline samples. The compounds crystalize in monoclinic structures with the space group $P2_1/n$. Magnetic properties of these hetero-tri-spin $3d$-$5d$-$4f$ systems were studied by magnetic susceptibility and field dependent magnetization in both DC and pulsed magnetic fields. All these compounds show ferrimagnetic transitions at temperatures $T…