A magnetic tunnel junction Fe3O4/MgO/Fe with (001) layer orientation is considered. The junction magnetic energy is analyzed as a function of the angle between the layer magnetization vectors under various magnetic fields. The tunnel magnetoresistance is calculated as a function of the external magnetic field. In contrast with junctions with unidirectional anisotropy, a substantially lower magnetic field is required for the junction switching.
We created epitaxial magnetic tunnel junctions of FeCo/MgO/EuS on MgO buffered Si (100). Tunnel magnetoresistance reached up to 64% at 4.2 K. An unexpected fast drop of magnetoresistance was recorded for MgO thickness above 1 nm, which is attributed to the forced nonspecular conductance across the EuS conduction band minimum located at the X point, rather than the desired Delta_1 conductance centered around the Gamma point.
We investigated dependence of tunnel magnetoresistance effect in CoFeB/MgO/CoFeB magnetic tunnel junctions on Ar pressure during MgO-barrier sputtering. Sputter deposition of MgO-barrier at high Ar pressure of 10 mTorr resulted in smooth surface and highly (001) oriented MgO. Using this MgO as a tunnel barrier, tunnel magnetoresistance (TMR) ratio as high as 355% at room temperature (578% at 5K) was realized after annealing at 325 C or higher, which appears to be related to a highly (001) oriented CoFeB texture promoted by the smooth and highly oriented MgO. Electron-beam lithography defined d…
By use of first-principles electronic structure calculations, we predict that the magnetoresistance of the bcc Co(100)/MgO(100)/bcc Co(100) and FeCo(100)/MgO(100)/FeCo(100) tunneling junctions can be several times larger than the very large magnetoresistance predicted for the Fe(100)/MgO(100)/Fe(100) system. The origin of this large magnetoresistance can be understood using simple physical arguments by considering the electrons at the Fermi energy travelling perpendicular to the interfaces. For the minority spins there is no state with $Δ_1$ symmetry whereas for the majority spins there is onl…
We report tunnel magnetoresistance (TMR) ratios as high as 472% at room temperature and 804% at 5 K in pseudo-spin valve (SV) CoFeB/MgO/CoFeB magnetic tunnel junctions (MTJs) annealed at 450oC, which is approaching the theoretically predicted value. By contrast, the TMR ratios for exchange-biased (EB) SV MTJs with a MnIr antiferromagnetic layer are found to drop when they are annealed at 450oC. Energy dispersive X-ray analysis shows that annealing at 450oC induces interdiffusion of Mn and Ru atoms into the MgO barrier and ferromagnetic layers in EB-SV MTJs. Mechanisms behind the different anne…
Magnetic tunnel junctions with the layer sequence Co$_2$Cr$_{0.6}$Fe$_{0.4}$Al/MgO/CoFe were fabricated by magnetron sputtering at room temperature (RT). The samples exhibit a large inverse tunneling magnetoresistance (TMR) effect of up to -66% at RT. The largest value of -84% at 20 K reflects a rather weak influence of temperature. The dependence on the voltage drop shows an unusual behavior with two almost symmetric peaks at $\pm600$ mV with large inverse TMR ratios and small positive values around zero bias.
We investigated the relationship between the tunnel magnetoresistance (TMR) ratio and the electrode structure in MgO-barrier magnetic tunnel junctions (MTJs). The TMR ratio in a MTJ with Co40Fe40B20 reference and free layers reached 355% at the post-deposition annealing temperature of Ta=400 degree C. When Co50Fe50 or Co90Fe10 is used for the reference layer material, no high TMR ratio was observed. The key to have high TMR ratio is to have highly oriented (001) MgO barrier/CoFeB crystalline electrodes. The highest TMR ratio obtained so far is 450% at Ta = 450 degree C in a pseudo spin-valve M…
We report on systematic ab-initio investigations of Co and Cr interlayers embedded in Fe(001)/MgO/Fe(001) magnetic tunnel junctions, focusing on the changes of the electronic structure and the transport properties with interlayer thickness. The results of spin-dependent ballistic transport calculations reveal options to specifically manipulate the tunnel magnetoresistance ratio. The resistance area products and the tunnel magnetoresistance ratios show a monotonous trend with distinct oscillations as a function of the Cr thickness. These modulations are directly addressed and interpreted by mea…
Giant tunnel magnetoresistance (TMR) ratios of 417% at room temperature (RT) and 914% at 3 K were demonstrated in epitaxial Fe/MgO/Fe(001) exchanged-biased spin-valve magnetic tunnel junctions (MTJs) by tuning growth conditions for each layer, combining sputter deposition for the Fe layers, electron-beam evaporation of the MgO barrier, and barrier interface tuning. Clear TMR oscillation as a function of the MgO thickness with a large peak-to-valley difference of ~80% was observed when the layers were grown on a highly (001)-oriented Cr buffer layer. Specific features of the observed MTJs are s…
By carrying out density functional theory analysis within the Keldysh non-equilibrium Green's functional formalism, we have calculated the nonlinear and non-equilibrium quantum transport properties of Fe/MgO/Fe trilayer structures as a function of external bias voltage. For well relaxed atomic structures of the trilayer, the equilibrium tunnel magnetoresistance ratio (TMR) is found to be very large and also fairly stable against small variations in the atomic structure. As a function of external bias voltage, the TMR reduces monotonically to zero with a voltage scale of about 1V, in agreement …
The knowledge of chemical and magnetic conditions at the Co40Fe40B20 / MgO interface is important to interpret the strong annealing temperature dependence of tunnel magnetoresistance of Co-Fe-B / MgO / Co-Fe-B magnetic tunnel junctions, which increases with annealing temperature from 20% after annealing at 200C up to a maximum value of 112% after annealing at 350C. While the well defined nearest neighbor ordering indicating crystallinity of the MgO barrier does not change by the annealing, a small amount of interfacial Fe-O at the lower Co-Fe-B / MgO interface is found in the as grown samples,…
Group-IV-based ferromagnetic semiconductor Ge1-xFex (GeFe) is one of the most promising materials for efficient spin injectors and detectors for Si and Ge. Recent first principles calculations (Sakamoto et al., Ref. 9) suggested that the Fermi level is located in two overlapping largely spin-polarized bands formed in the bandgap of GeFe; spin-down d(e) band and spin-up p-d(t2) band. Thus, it is important to clarify how these bands contribute to spin injection and detection. In this study, we show the first successful observation of the tunneling magnetoresistance (TMR) in magnetic tunnel junct…
The formation of patterned nanostructure in AgCo/Pt/MgO(001) thin film is simulated by a technique of combining molecular dynamics and phase-field theory. The dislocation (strain) network existing in Pt/MgO is used as a template whose pattern is transferred to AgCo phase in spinodal decomposition, resulting in regular arrays of Co islands that are attracted by the dislocations. The influence of various factors, such as component concentration and film thickness, is studied. It is found that the spinodal decomposition of AgCo in this system is mainly characterized by a competition between a sur…
Room temperature local magnetoresistance in two-terminal scheme is reported. By employing 1.6 nm-thick MgO tunnel barrier, spin injection efficiency is increased, resulting in large non-local magnetoresistance. The magnitude of the non-local magnetoresistance is estimated to be 0.0057 ohm at room temperature. As a result, a clear rectangle signal is observed in local magnetoresistance measurement even at room temperature. We also investigate the origin of local magnetoresistance by measuring the spin accumulation voltage of each contact separately.
We investigated the dependence of giant tunnel magnetoresistance (TMR) on the thickness of an MgO barrier and on the annealing temperature of sputtered CoFeB/MgO/CoFeB magnetic tunnel junctions deposited on SiO2/Si wafers. The resistance-area product exponentially increases with MgO thickness, indicating that the quality of MgO barriers is high in the investigated thickness range of 1.15-2.4 nm. High-resolution transmission electron microscope images show that annealing at 375 C results in the formation of crystalline CoFeB/MgO/CoFeB structures, even though CoFeB electrodes are amorphous in th…
An unusual crystallographic orientation of hexagonal Ru with a 4-fold symmetry emerging in epitaxial MgO/Ru/Co2FeAl/MgO heterostructures is reported, in which an approximately Ru(02-23) growth attributes to the lattice matching among MgO, Ru, and Co2FeAl. Perpendicular magnetic anisotropy of the Co2FeAl/MgO interface is substantially enhanced as compared with those with a Cr(001) layer. The MTJs incorporating this structure gave rise to the largest tunnel magnetoresistance for perpendicular MTJs using low damping Heusler alloys. The 4-fold-symmetry hexagonal Ru arises from an epitaxial growth …
Magnetite (Fe3O4) is an eligible candidate for magnetic tunnel junctions (MTJs) since it shows a high spin polarization at the Fermi level as well as a high Curie temperature of 585°C. In this study, Fe3O4/MgO/Co-Fe-B MTJs were manufactured. A sign change in the TMR is observed after annealing the MTJs at temperatures between 200°C and 280°C. Our findings suggest an Mg interdiffusion from the MgO barrier into the Fe3O4 as the reason for the change of the TMR. Additionally, different treatments of the magnetite interface (argon bombardment, annealing at 200°C in oxygen atmosphere) during the pr…
Spin-valve is a microelectronic device in which high and low resistance states are realized by utilizing both charge and spin of carriers. Spin-valve structures used in modern hard drive read-heads and magnetic random access memories comprise two ferromagnetic (FM) electrodes whose relative magnetization orientations can be switched between parallel and antiparallel configurations, yielding the desired giant or tunneling magnetoresistance effect. In this paper we demonstrate >100$% spin-valve-like signal in a NiFe/IrMn/MgO/Pt stack with an antiferromagnet (AFM) on one side and a non-magnetic m…
Alloying Fe electrodes with V, through reduced FeV/MgO interface mismatch in epitaxial magnetic tunnel junctions with MgO barriers, notably suppresses both nonmagnetic (parallel) and magnetic (antiparallel) state 1/f noise and enhances tunnelling magnetoresistance (TMR). A comparative study of the room temperature electron transport and low frequency noise in Fe1-xVx/MgO/Fe and Fe/MgO/Fe1-xVx MTJs with 0 <= x <= 0.25 reveals that V doping of the bottom electrode for x < 0.1 reduces in nearly 2 orders of magnitude the normalized nonmagnetic and magnetic 1/f noise. We attribute the enhanced TMR …
We examine the spin torque (ST) response of magnetic tunnel junctions (MTJs) with ultra-thin MgO tunnel barrier layers to investigate the relationship between the spin-transfer torque and the tunnel magnetoresistance (TMR) under finite bias. We find that the spin torque per unit current exerted on the free layer decreases by less than 10% over a bias range where the TMR decreases by over 40%. We examine the implications of this result for various spin-polarized tunneling models and find that it is consistent with magnetic-state-dependent effective tunnel decay lengths.
The influence of insertion of an ultra-thin NiO layer between the MgO barrier and ferromagnetic electrode in magnetic tunnel junctions has been investigated by measuring the tunneling magnetoresistance and the X-ray magnetic circular dichroism (XMCD). The magnetoresistance shows a high asymmetry with respect to bias voltage, giving rise to a negative value of -16% at 2.8 K. We attribute this to the formation of non-collinear spin structures in the NiO layer as observed by XMCD. The magnetic moments of the interface Ni atoms tilt from the easy axis due to exchange interaction and the tilting an…
Recently, it has been shown that magnetic tunnel junctions with thin MgO tunnel barriers exhibit extraordinarily high tunneling magnetoresistance (TMR) values at room temperature1, 2. However, the physics of spin dependent tunneling through MgO barriers is only beginning to be unravelled. Using planar magnetic tunnel junctions in which ultra-thin layers of magnetic metals are deposited in the middle of a MgO tunnel barrier here we demonstrate that the TMR is strongly modified when these layers are discontinuous and composed of small pancake shaped nanodots. At low temperatures, in the Coulomb …
We fabricate fully epitaxial Fe/ZnO/MgO/Fe magnetic tunnel junctions (MTJs) with a bilayer tunnel barrier, in which ZnO has a metastable rock-salt crystal structure. We observe a high magnetoresistance ratio up to 96% at room temperature (RT) and find that these MTJs have asymmetric current-voltage characteristics, and their rectifying performances are largely dependent on the magnetization alignments of the Fe electrodes. Diode responsibilities at a zero-bias voltage ($β_{0}$), which is an important performance index for harvesting applications, are observed up to 1.3 A/W at RT in the antipar…
We investigated the relationship between tunnel magnetoresistance (TMR) ratio and the crystallization of CoFeB layers through annealing in magnetic tunnel junctions (MTJs) with MgO barriers that had CoFe/Ru/CoFeB synthetic ferrimagnet pinned layers with varying Ru spacer thickness (tRu). The TMR ratio increased with increasing annealing temperature (Ta) and tRu, reaching 361% at Ta = 425C, whereas the TMR ratio of the MTJs with pinned layers without Ru spacers decreased at Ta over 325C. Ruthenium spacers play an important role in forming an (001)-oriented bcc CoFeB pinned layer, resulting in a…
Magnetic phase transition tunnel magnetoresistance (MPT-TMR) effect with a single magnetic electrode has been investigated by first-principles calculations. The calculations show that the MPT-TMR of FeRh/MgO/Cu tunnel junction can be as high as hundreds of percent when the magnetic structure of FeRh changes from G-type antiferromagnetic (GAFM) to ferromagnetic order. This new type of MPT-TMR may be superior to the tunnel anisotropic magnetoresistance because of its huge magneto-resistance effect and similar structural simplicity. The main mechanism for the giant MPT-TMR can be attributed to th…
The spin-orbit interaction in heavy metal/ferromagnet/oxide structures has been extensively investigated because it can be employed in manipulation of the magnetization direction by in-plane current. This implies the existence of an inverse effect, in which the conductivity in such structures should depend on the magnetization orientation. In this work, we report a systematic study of the magnetoresistance (MR) of the W/CoFeB/MgO structures and its correlation to the current-induced torque to the magnetization. We observe that the MR is independent of the angle between magnetization and curren…
We investigate bias voltage effects on the spin-dependent transport properties of Fe/MgAl${}_2$O${}_4$/Fe(001) magnetic tunneling junctions (MTJs) by comparing them with those of Fe/MgO/Fe(001) MTJs. By means of the nonequilibrium Green's function method and the density functional theory, we calculate bias voltage dependences of magnetoresistance (MR) ratios in both the MTJs. We find that in both the MTJs, the MR ratio decreases as the bias voltage increases and finally vanishes at a critical bias voltage $V_{\rm c}$. We also find that the critical bias voltage $V_{\rm c}$ of the MgAl${}_2$O${…
While the effects of lattice mismatch-induced strain, mechanical strain, as well as the intrinsic strain of thin films are sometimes detrimental, resulting in mechanical deformation and failure, strain can also be usefully harnessed for applications such as data storage, transistors, solar cells, and strain gauges, among other things. Here, we demonstrate that quantum transport across magnetic tunnel junctions (MTJs) can be significantly affected by the introduction of controllable mechanical strain, achieving an enhancement factor of ~2 in the experimental tunneling magnetoresistance (TMR) ra…
We theoretically study the tunnel magnetoresistance (TMR) effect in (111)-oriented junctions Co/MgO/Co(111) and Ni/MgO/Ni(111). The Co-based junction is shown to have a TMR ratio over 2000$\%$, which is one order higher than that of the Ni-based one. The high TMR ratio is attributed to the interfacial resonance effect: The interfacial $d$-$p$ antibonding states are formed close to the Fermi level in the majority-spin channel and these states in both interfaces resonate with each other. This differs essentially from the conventional coherent tunneling mechanism of high TMR ratios in Fe(Co)/MgO/…
We theoretically studied spin dependent electron transport perpendicular-to-plain (CPP) in magnetic laminated multilayered structures by using Kubo formalism. We took into account not only bulk scattering, but the interface resistance due to both specular and diffuse reflection and also spin conserving and spin-flip processes. It was shown that spin-flip scattering at interfaces substantially reduces the value of GMR. This can explain the experimental observations that the CPP GMR ratio for laminated structures only slightly increases as compared to non-laminated ones despite lamination induce…
The ferrimagnetic Heusler compound Mn2VGa is predicted to have a pseudogap in the majority spin channel, which should lead to a negative tunnel magnetoresistance. We synthesized epitaxial Mn2VGa thin films on MgO(001) substrates by dc and rf magnetron co-sputtering, resulting in nearly stoichiometric films. XRD analysis revealed a mostly B2-ordered structure for the films deposited at substrate temperatures of 350°C, 450°C, and 550°C. Magnetic tunnel junctions with MgO barrier and CoFe counter-electrodes were fabricated. After post-annealing at up to T_a=425°C negative TMR was obtained around …
Spintronics exploits the magnetoresistance effects to store or sense the magnetic information. Since the magnetoresistance strictly depends on the magnetic anisotropy of the system, it is fundamental to set a defined anisotropy to the system. Here, we investigate by means of vectorial Magneto-Optical Kerr Magnetometry (v-MOKE), half-metallic La0.67Sr0.33MnO3 (LSMO) thin films that exhibit at room temperature pure biaxial magnetic anisotropy if grown onto MgO (001) substrate with a thin SrTiO3 (STO) buffer. In this way, we can avoid unwanted uniaxial magnetic anisotropy contributions that may b…
The independent control of two magnetic electrodes and spin-coherent transport in magnetic tunnel junctions are strictly required for tunneling magnetoresistance, while junctions with only one ferromagnetic electrode exhibit tunneling anisotropic magnetoresistance dependent on the anisotropic density of states with no room temperature performance so far. Here we report an alternative approach to obtaining tunneling anisotropic magnetoresistance in alfa-FeRh-based junctions driven by the magnetic phase transition of alfa-FeRh and resultantly large variation of the density of states in the vicin…
The tunnel magnetoresistance (TMR) effect observed in magnetic tunnel junctions (MTJs) is commonly used in many spintronic applications because the effect can easily convert from local magnetic states to electric signals in a wide range of device resistances. In this study, we demonstrated TMR ratios of up to 631% at room temperature (RT), which is two or more times larger than those used currently for magnetoresistive random access memory (MRAM) devices, using CoFe/MgO/CoFe(001) epitaxial MTJs. The TMR ratio increased up to 1143% at 10 K, which corresponds to an effective tunneling spin polar…
We studied polycrystalline B2-type Co2FeAl (CFA) full-Heusler alloy based magnetic tunnel junctions (MTJs) fabricated on a Si/SiO2 amorphous substrate. Polycrystalline CFA films with a (001) orientation, a high B2 ordering, and a flat surface were achieved using a MgO buffer layer. A tunnel magnetoresistance (TMR) ratio up to 175% was obtained for an MTJ with a CFA/MgO/CoFe structure on a 7.5-nm-thick MgO buffer. Spin-transfer torque induced magnetization switching was achieved in the MTJs with a 2-nm-thick polycrystalline CFA film as a switching layer. Using a thermal activation model, the in…
Spin-resolved electron symmetry filtering is a key mechanism behind giant tunneling magnetoresistance (TMR) in Fe/MgO/Fe and similar magnetic tunnel junctions (MTJs), providing room temperature functionality in modern spin electronics. However, the core process of the electron symmetry filtering breaks down under applied bias, dramatically reducing the TMR above 0.5 V. This strongly hampers the application range of MTJs. To circumvent the problem, resonant tunneling between ferromagnetic electrodes through quantum well states in thin layers has been used so far. This mechanism, however, is mai…
Recent studies on the electrical switching of tetragonal antiferromagnet (AFM) via N{é}el spin-orbit torque have paved the way for the economic use of antiferromagnetic materials. The most difficult obstacle that presently limits the application of antiferromagnetic materials in spintronics, especially in memory storage applications, could be the small and fragile magnetoresistance (MR) in the AFM-based nanostructure. In this study, we investigated the spin transports in Mn$_2$Au-based tunnel junctions based onthe first-principle scattering theory. Giant MRs more than $1000\%$ are predicted in…
Ab initio study of magnetoresistance effect in $\mathrm{Mn_{3}Sn}/\mathrm{MgO}/\mathrm{Mn_{3}Sn}$ antiferromagnetic tunnel junction
University of Tokyo（东京大学）；JSR Corporation（JSR公司）；Kyoto University（京都大学）；Johns Hopkins University（约翰斯·霍普金斯大学）；Tokyo Metropolitan University（东京都立大学）；Tohoku University（东北大学）；RIKEN（理化学研究所）
The Fe/MgO interface is an essential ingredient in spintronics as it shows giant tunneling magnetoresistance and strong perpendicular magnetic anisotropy (PMA). A recent study demonstrated that the insertion of an ultra-thin LiF layer between the Fe and MgO layers enhances PMA significantly. In this study, we perform x-ray magnetic circular dichroism measurements on Fe/LiF/MgO multilayers to reveal the origin of the PMA enhancement. We find that the LiF insertion increases the orbital-magnetic-moment anisotropy and thus the magnetic anisotropy energy. We attribute the origin of this orbital-ma…
The electronic structure and spin-dependent tunneling in epitaxial Fe/MgO/Fe(001) tunnel junctions are studied using first-principles calculations. For small MgO barrier thickness the minority-spin resonant bands at the two interfaces make a significant contribution to the tunneling conductance for the antiparallel magnetization, whereas these bands are, in practice, mismatched by disorder and/or small applied bias for the parallel magnetization. This explains the experimentally observed decrease in tunneling magnetoresistance (TMR) for thin MgO barriers. We predict that a monolayer of Ag epit…
Future generations of magnetic random access memory demand magnetic tunnel junctions that can provide simultaneously high magnetoresistance, strong retention, low switching energy and small cell size below 10nm. Here we study perpendicular magnetic tunnel junctions with composite free layers where multiple ferromagnet/nonmagnet interfaces can contribute to the thermal stability. Different nonmagnetic materials (MgO, Ta, Mo) have been employed as the coupling layers in these multi-interface free layers. The evolution of junction properties under different annealing conditions is investigated. A…
Ultra-thin magnetic tunnel junctions with low resistive MgO tunnel barriers are prepared to examine their stability under large current stress. The devices show magnetoresistance ratios of up to 110 % and an area resistance product of down to 4.4 ohm micrometer squared. If a large current is applied, a reversible resistance change is observed, which can be attributed to two different processes during stressing and one relaxation process afterwards. Here, we analyze the time dependence of the resistance and use a simple model to explain the observed behavior. The explanation is further supporte…
Perpendicular magnetic tunnel junction with MgAl2O4 barrier is investigated. It is found that reactive RF sputtering with O2 is essential to obtain strong perpendicular magnetic anisotropy and large tunneling magnetoresistance in MgAl2O4-based junctions. An interfacial perpendicular magnetic anisotropy energy density of 2.25 mJ/m2 is obtained for the samples annealed at 400C. An enhanced magnetoresistance of 60% has also been achieved. The Vhalf, bias voltage at which tunneling magnetoresistance drops to half of the zero-bias value, is found to be about 1V, which is substantially higher than t…
In a number of current experiments in the field of spin-caloritronics a temperature gradient across a nanostructured interface is applied and spin-dependent transport phenomena are observed. However, a lack in the interpretation and knowledge let it unclear how the temperature drop across a magnetic nanostructured interface looks like where both phonons and electrons may contribute to thermal transport. We answer this question for the case of a magnetic tunnel junction (MTJ) where the tunneling magneto Seebeck effect occurs. Nevertheless, our results can be extended to other nanostructured int…
The authors studied an effect of ferromagnetic (Co20Fe60B20 or Fe) layer insertion on tunnel magnetoresistance (TMR) properties of MgO-barrier magnetic tunnel junctions (MTJs) with CoFe/Pd multilayer electrodes. TMR ratio in MTJs with CoFeB/MgO/Fe stack reached 67% at an-nealing temperature (Ta) of 200 degree C and then decreased rapidly at Ta over 250 degree C. The degradation of the TMR ratio may be related to crystallization of CoFe(B) into fcc(111) or bcc(011) texture result-ing from diffusion of B into Pd layers. MTJs which were in-situ annealed at 350oC just after depo-siting bottom CoFe…
We study IrCrMnZ (Z=Al, Ga, Si, Ge) systems using first-principles calculations from the perspective of their application as the electrode materials of MgO-based MTJs. These materials have highly spin-polarized conduction electrons with partially occupied $Δ_1$ band, which is important for coherent tunneling in parallel magnetization configuration. The Curie temperatures of IrCrMnAl and IrCrMnGa are very high (above 1300 K) as predicted from mean-field-approximation. The stability of ordered phase against various antisite disorders has been investigated. We discuss here the effect of "spin-orb…
Flexible electronic devices require the integration of multiple crucial components on soft substrates to achieve their functions. In particular, memory devices are the fundamental component for data storage and processing in flexible electronics. Here, we present flexible MgO barrier magnetic tunnel junction (MTJ) devices fabricated using a transfer printing process, which exhibit reliable and stable operation under substantial deformation of the device substrates. In addition, the flexible MTJ devices yield significantly enhanced tunneling magnetoresistance (TMR) of ~300 % and improved abrupt…
We report on spin polarization reduction by incoherent tunneling in realistic single crystal Co2FeAl/MgO/Co50Fe50 magnetic tunnel junctions (MTJ) compared to reference Fe/MgO/Fe. A large density of misfit dislocations in the Heusler based MTJs has been insured by a thick MgO barrier and its 3.8% lattice mismatch with the Co2FeAl electrode. Our analysis implicates a correlated structural-transport approach. The crystallographic coherence, in the real space, is investigated using High Resolution Transmission Electron Microscopy phase analysis. The electronic transport experiments in variable tem…
The interface structure of Fe/MgO(100) magnetic tunnel junctions predicted by density functional theory (DFT) depends significantly on the choice of exchange and correlation functional. Bader analysis reveals that structures obtained by relaxing the cell with the local spin-density approximation (LSDA) display a different charge transfer than those relaxed with the generalized gradient approximation (GGA). As a consequence, the electronic transport is found to be extremely sensitive to the interface structure. In particular, the conductance for the LSDA-relaxed geometry is about one order of m…
We study the local and non-local magnetoresistance of thin Pt strips deposited onto yttrium iron garnet. The local magnetoresistive response, inferred from the voltage drop measured along one given Pt strip upon current-biasing it, shows the characteristic magnetization orientation dependence of the spin Hall magnetoresistance. We simultaneously also record the non-local voltage appearing along a second, electrically isolated, Pt strip, separated from the current carrying one by a gap of a few 100 nm. The corresponding non-local magnetoresistance exhibits the symmetry expected for a magnon spi…
A number of recent studies indicate that the charge conduction of the LaAlO$_3$/SrTiO$_3$ interface at low temperature is confined to filaments which are linked to structural domain walls in the SrTiO$_3$ with drastic consequences for example for the temperature dependence of local transport properties. We demonstrate that as a consequences of this current carrying filaments on the nano-scale the magnetotransport properties of the interface are highly anisotropic. Our magnetoresistance measurements reveal that the magnetoresistance in different nanostructures ($<500nm$) is random in magnitude …
Current-driven magnetization switching in low-resistance Co40Fe40B20/MgO/Co40Fe40B20 magnetic tunnel junctions (MTJs) is reported. The critical-current densities Jc required for current-driven switching in samples annealed at 270C and 300C are found to be as low as 7.8 x 10^5 A/cm^2 and 8.8 x 10^5 A/cm^2 with accompanying tunnel magnetoresistance (TMR) ratios of 49% and 73 %, respectively. Further annealing of the samples at 350C increases TMR ratio to 160 %, while accompanying Jc increases to 2.5 x 10^6 A/cm^2. We attribute the low Jc to the high spin-polarization of tunnel current and small …
We prepared magnetic tunnel junctions with one ferromagnetic and one superconducting Al-Si electrode. Pure cobalt electrodes were compared with a Co-Fe-B alloy and the Heusler compound Co2FeAl. The polarization of the tunneling electrons was determined using the Maki-Fulde-model and is discussed along with the spin-orbit scattering and the total pair-breaking parameters. The junctions were post-annealed at different temperatures to investigate the symmetry filtering mechanism responsible for the giant tunneling magnetoresistance ratios in Co-Fe-B/ MgO/ Co-Fe-B junctions.
The capacitance of MgO based magnetic tunnel junctions (MTJs) has been observed to be magnetic field dependent. We propose an equivalent circuit for the MTJs with a parallel-leaky capacitance (Cl) across the series combination of geometric and interfacial capacitance. The analysis of junctions with different tunneling magnetoresistance values suggests higher Cl for low TMR junctions. Using Cole-Cole plots the capacitive nature of MTJs is manifested. Fitting with Maxwell-Wagner capacitance model validates the RC parallel network model for MTJs and the extracted field dependent parameters match …
We observed spin injection into silicon through Fe/MgO tunnel barrier by using non-local magnetoresistance measurement technique. Fe/MgO tunnel barrier contacts with a lateral spin valve structure were fabricated on phosphorous doped silicon-on-insulator substrate. Spin injection signals in the non-local scheme were observed up to 120K, which is the highest value where band transferred spins in Si have ever been reported, and spin diffusion length was estimated to be about 2.25um at 8K. Temperature dependence and injection current dependence of the non-local voltage were also investigated. It …
In this study we investigate magnetic properties, surface morphology and crystal structure in iron nanoclusters electrodeposited on lightly-doped (100) n-type silicon substrates. Our goal is to investigate the spin injection and detection in the Fe/Si lateral structures. The samples obtained under electric percolation were characterized by magnetoresistive and magnetic resonance measurements with cycling the sweeping applied field in order to understand the spin dynamics in the as-produced samples. The observed hysteresis in the magnetic resonance spectra, plus the presence of a broad peak in …