Synthesis and physical properties of $\rm\bf LaO_{1-x}F_xFeAs$

Agnieszka Kondrat, Jorge Enrique Hamann-Borrero, Norman Leps, Martin Kosmala, Olaf Schumann, Anke Köhler, Jochen Werner, Günter Behr, Markus Braden, Rüdiger Kli… 展开作者

Agnieszka Kondrat, Jorge Enrique Hamann-Borrero, Norman Leps, Martin Kosmala, Olaf Schumann, Anke Köhler, Jochen Werner, Günter Behr, Markus Braden, Rüdiger Klingeler, Bernd Büchner, Christian Hess

发表信息：: Eur. Phys. J. B 70, 461-468 (2009)
DOI：: 10.1140/epjb/e2009-00267-3

阅读 PDF ↗

arXiv 页面 ↗HTML 原文 ↗

英文摘要相关论文

英文摘要：

We have prepared the newly discovered Fe-based superconducting material $\rm LaO_{1-x}F_xFeAs$ ($0\leq x\leq 0.2$) in polycrystalline form and have investigated the samples by means of structural, thermodynamic and transport measurements. Our investigations reveal a non superconducting phase at $0\leq x\lesssim0.04$ which for $x=0$ is characterized by a structural transition towards an orthorhombic distortion at $T_s\approx 160$ K and antiferromagnetic spin order at $T_N\approx138$ K. Both transitions lead to strong anomalies in various transport properties as well as in magnetization and in specific heat. Remarkably, the transition temperatures are only weakly doping dependent up $x\lesssim 0.04$. However, the transitions are abruptly suppressed at $x\geq0.05$ in favour of a superconducting phase with a critical temperature $T_c\gtrsim 20$ K. Upon further increasing the F-doping $T_c$ increases up to a maximum of $T_c=26.8$ K at $x=0.1$ which is followed by a decrease down to $T_c\approx10$ K at $x\geq0.15$.

机构、总结、中文摘要均由AI分析而来，可能存在错误，请以论文正文为准。

阅读原文

阅读 PDF ↗

arXiv 页面 ↗HTML 原文 ↗

本文内容

英文摘要相关论文

机构、总结、中文摘要均由AI分析而来，可能存在错误，请以论文正文为准。

继续探索

相关论文

Strong electron-phonon coupling of the Fe breathing mode of LaO_{1-x}F_xFeAs

The electron-phonon coupling of LaO$_{1-x}$F$_x$FeAs is re-investigated on the basis of density functional theory in local density approximation. The implications of the $(π,π)$ nesting of the Fermi surfaces are carefully studied and found to lead to a non-standard electron-phonon coupling of the corresponding Fe in-plane breathing mode, which might make a strong contribution to the high superconducting transition temperature. The semi-metallic behavior of the undoped material is also further illuminated.

2008-04-11cond-mat.supr-con

Field and Temperature Dependence of the Superfluid Density in LaO_{1-x}F_xFeAs Superconductors: A Muon Spin Relaxation Study

We present zero field and transverse field \muSR experiments on the recently discovered electron doped Fe-based superconductor LaO_{1-x}F_xFeAs. The zero field experiments on underdoped (x=0.075) and optimally doped (x=0.1) samples rule out any static magnetic order above 1.6 K in these superconducting samples. From transverse field experiments in the vortex phase we deduce the temperature and field dependence of the superfluid density. Whereas the temperature dependence is consistent with a weak coupling BCS s-wave or a dirty d-wave gap function scenario, the field dependence strongly evidenc…

2008-04-19cond-mat.supr-con

Synthesis, structural and transport properties of the hole-doped Superconductor Pr_{1-x}Sr_xFeAsO

Superconductivity was achieved in PrFeAsO by partially substituting Pr^{3+} with Sr^{2+}. The electrical transport properties and structure of this new superconductor Pr_{1-x}Sr_xFeAsO at different doping levels (x = 0.05$\sim$ 0.25) were investigated systematically. It was found that the lattice constants (a-axis and c-axis) increase monotonously with Sr or hole concentration. The superconducting transition temperature at about 16.3 K (95% $ρ_n$) was observed around the doping level of 0.20$\sim$ 0.25. A detailed investigation was carried out in the sample with doping level of x = 0.25. The d…

2009-01-13cond-mat.supr-con

Phase Diagram and Quantum Critical Point in Newly Discovered Superconductors: SmO_{1-x}F_xFeAs

The magnetic fluctuations associated with a quantum critical point (QCP) are widely believed to cause the non-Fermi liquid behaviors and unconventional superconductivities, for example, in heavy fermion systems and high temperature cuprate superconductors. Recently, superconductivity has been discovered in iron-based layered compound $LaO_{1-x}F_xFeAs$ with $T_c$=26 K\cite{yoichi}, and it competes with spin-density-wave (SDW) order\cite{dong}. Neutron diffraction shows a long-rang SDW-type antiferromagnetic (AF) order at $\sim 134$ K in LaOFeAs\cite{cruz,mcguire}. Therefore, a possible QCP and…

2008-05-07cond-mat.mtrl-scicond-mat.str-elcond-mat.supr-con

Stabilization of high-Tc phase of BiS2-based superconductor LaO0.5F0.5BiS2 using high-pressure synthesis

High-quality polycrystalline samples of LaO0.5F0.5BiS2 were obtained using high-pressure synthesis technique. The LaO0.5F0.5BiS2 sample prepared by heating at 700 C under 2 GPa showed superconductivity with superconducting transition temperatures (Tc) of Tconset = 11.1 and Tczero = 8.5 K in the electrical resistivity measurements and Tconset = 11.5 and Tcirr = 9.4 K in the magnetic susceptibility measurements, which are obviously higher than those of the LaO0.5F0.5BiS2 polycrystalline samples obtained using conventional solid-state reaction. It was found that the high-Tc phase can be stabilize…

2014-03-10cond-mat.supr-con

Synthesis and Microstructural Studies of Iron Based LaO1-xFxFeAs Superconducting Materials

We report on the synthesis and microstructural studies of fluorine based iron doped superconductors. We have successfully synthesized the fluorine based new superconducting material LaO1-xFxFeAs by choosing comparatively lower temperature and longer synthesis duration. The superconducting transition temperature that we have achieved is 27.5 K which is observed at doping level of x=0.2. The structural microstructural characterizations have been done by employing XRD, SEM and TEM techniques. The SEM and TEM micrographs reveal the layered structure.

2008-06-10cond-mat.mtrl-scicond-mat.supr-con

更多相关论文收起更多论文

Synthesis and Microstructural Studies of Iron Oxypnictide LaO1-xFxFeAs Superconductors

We report on the synthesis and structural/ microstructural studies of iron based fluorine doped LaOFeAs superconductors. We have successfully synthesized fluorine doped superconducting LaO1-xFxFeAs materials by choosing lower temperature (1150^0C) and longer synthesis duration (60 hours) as compared to the standard values of these employed in the pioneering first contribution [Kamihara et al 2008 J Am Chem Soc 130 3296]. Decrease of lattice parameters as determined by x-ray diffraction confirm the substitution of fluorine. The superconducting transition temperature is 27.5 K which is observed …

2008-11-01cond-mat.str-elcond-mat.supr-con

Synthesis and properties of SmO0.5F0.5BiS2 and enhancement in Tc in La1-ySmyO0.5F0.5BiS2

Crystal structure and properties of a new member of oxy-bismuth-sulfide SmO1-xFxBiS2 are reported here. The compounds SmO1-xFxBiS2 (x = 0.0 and 0.5) are found to be isostructural with LaOBiS2 and crystallize in the CeOBiS2 type structure (P4/nmm). Sm substitution in LaO0.5F0.5BiS2, (La1-ySmyO0.5F0.5BiS2), leads to a gradual decrease in a-lattice constant however the c-lattice constant does not show such a gradual trend. Enhancement in Tc is achieved upon partially substituting La by smaller Sm ion. Maximum Tc ~ 4.6 K was observed for composition with y = 0.8. Disobeying this trend Tc disappear…

2015-01-12cond-mat.supr-con

Synthesis, Crystal Structure, and Physical Properties of New Layered Oxychalcogenide La2O2Bi3AgS6

We have synthesized a new layered oxychalcogenide La2O2Bi3AgS6. From synchrotron X-ray diffraction and Rietveld refinement, the crystal structure of La2O2Bi3AgS6 was refined using a model of the P4/nmm space group with a = 4.0644(1) Å and c = 19.412(1) Å, which is similar to the related compound LaOBiPbS3, while the interlayer bonds (M2-S1 bonds) are apparently shorter in La2O2Bi3AgS6. The tunneling electron microscopy (TEM) image confirmed the lattice constant derived from Rietveld refinement (c ~ 20 Å). The electrical resistivity and Seebeck coefficient suggested that the electronic states o…

2017-12-19cond-mat.mtrl-scicond-mat.supr-con

Upper critical field, superconducting energy gaps, and Seebeck coefficient in La0.8Th0.2OFeAs

We report the synthesis and characterization of a new electron-doped La-oxypnictide superconductor by partial substitution of lanthanum by thorium. The superconducting transition temperature at about 30.3 K was observed in La0.8Th0.2OFeAs which is the highest in La-based oxypnictide superconductors synthesized at ambient pressure. We find that the decrease in lattice parameters with Th doping in LaOFeAs is more drastic as compared to that obtained by high pressure (6 GPa) synthesis of oxygen deficient LaOFeAs. The resistivity and magnetic susceptibility measurements yield an upper critical fie…

2009-02-19cond-mat.supr-con

Enhancement in superconducting transition temperature and upper critical field of LaO0.8F0.2FeAs with antimony doping

We report the synthesis and characterization of antimony doped oxypnictide superconductor, LaO0.8F0.2FeAs1-xSbx (x = 0.05 and 0.10). The parent compound LaOFeAs with fluorine doping exhibits superconductivity at maximum transition temperature ~ 28.5 K [11]. Here we partially substitute As by Sb (LaO0.8F0.2FeAs1-xSbx) and observe enhancement of the transition temperature to 30.1 K. This is the only instance so far where Tc increases with doping in the conducting layer (FeAs) and this leads to the highest transition temperature in any La-based oxypnictide. XRD and EDAX measurements confirm phase…

2008-10-14cond-mat.mtrl-scicond-mat.supr-con

New enlargement of the novel class of superconductors

Here we report on synthesis and characterization of a new member LaO1-deltaNiBi in the family of novel superconductors. Though the onset superconducting temperature ~4 K is smaller compared to 55 K that has been achieved already in SmO1-deltaFeAs the similarities in crystalline structure, elec-tronic properties and low-temperature electron transport features give evidence to the common mechanism that seems to underlie the superconducting state in lanthanum nickel oxybismuthides and oxyarsenides.

2008-04-29cond-mat.supr-con

Enhancement of Superconductivity in La$_{1-x}$Sm$_{x}$O$_{0.5}$F$_{0.5}$BiS$_2$

The superconducting and normal-state properties of La$_{1-x}$Sm$_{x}$O$_{0.5}$F$_{0.5}$BiS$_{2}$ (0.1 $\leqslant$ $x$ $\leqslant$ 0.9) have been studied via electrical resistivity, magnetic susceptibility, and specific heat measurements. By using suitable synthesis conditions, Sm exhibits considerable solubility into the CeOBiS$_{2}$-type LaO$_{0.5}$F$_{0.5}$BiS$_{2}$ lattice. In addition to a considerable enhancement of the superconducting volume fraction, it is found that the superconducting transition temperature $T_{c}$ is dramatically enhanced with increasing Sm concentration to 5.4 K at …

2014-09-30cond-mat.supr-con

三维杂化Ruddlesden-Popper镍酸盐单晶的设计与合成

Design and synthesis of three-dimensional hybrid Ruddlesden-Popper nickelate single crystals

本研究设计并合成了由$La_2NiO_4$单层与$La_3Ni_2O_7$双层交替堆叠的三维杂化R-P镍酸盐单晶，表征其结构与140K附近的绝缘体-金属转变，为新型杂化R-P相材料研究开辟了新方向。

2023-12-13cond-mat.mtrl-scicond-mat.str-elcond-mat.supr-con