The common approach to crack dynamics, linear elastic fracture mechanics (LEFM), assumes infinitesimal strains and predicts a $r^{-1/2}$ strain divergence at a crack tip. We extend this framework by deriving a weakly nonlinear fracture mechanics theory incorporating the leading nonlinear elastic corrections that must occur at high strains. This yields strain contributions "more-divergent" than $r^{-1/2}$ at a finite distance from the tip and logarithmic corrections to the parabolic crack tip opening displacement. In addition, a dynamic length-scale, associated with the nonlinear elastic zone, emerges naturally. The theory provides excellent agreement with recent near-tip measurements that can not be described in the LEFM framework.
Material failure by crack propagation essentially involves a concentration of large displacement-gradients near a crack's tip, even at scales where no irreversible deformation and energy dissipation occurs. This physical situation provides the motivation for a systematic gradient expansion of general nonlinear elastic constitutive laws that goes beyond the first order displacement-gradient expansion that is the basis for linear elastic fracture mechanics (LEFM). A weakly nonlinear fracture mechanics theory was recently developed by considering displacement-gradients up to second order. The the…
Soft or weakly-consolidated sand refers to porous materials composed of particles (or grains) weakly held together to form a solid but that can be easily broken when subjected to stress. These materials do not behave as conventional brittle, linear elastic materials and the transition between these two regimes cannot usually be described using poro-elastic models. Furthermore, conventional geotechnical sampling techniques often result in the destruction of the cementation and recovery of sufficient intact core is, therefore, difficult. This paper studies a numerical model that allows us to int…
As is well known, the extrusion rate of polymers from a cylindrical tube or slit (a ``die'') is in practice limited by the appearance of ``melt fracture'' instabilities which give rise to unwanted distortions or even fracture of the extrudate. We present the results of a weakly nonlinear analysis which gives evidence for an intrinsic generic route to melt fracture via a weakly nonlinear subcritical instability of viscoelastic Poiseuille flow. This instability and the onset of associated melt fracture phenomena appear at a fixed ratio of the elastic stresses to viscous stresses of the polymer s…
The dynamics of rapid brittle cracks is commonly studied in the framework of linear elastic fracture mechanics where nonlinearities are neglected. However, recent experimental and theoretical work demonstrated explicitly the importance of elastic nonlinearities in fracture dynamics. We study two simple one-dimensional models of fracture in order to gain insights about the role of elastic nonlinearities and the implications of their exclusion in the common linear elastic approximation. In one model we consider the decohesion of a nonlinear elastic membrane from a substrate. In a second model we…
Microbond tests composed of single fibre and matrix droplet are often used to determine the properties of fibre reinforced composites. Interfacial shear strength is quantified by the maximum pull-out force assuming a uniform stress distribution along the fibre. Here, nonlinear finite element analyses are performed to investigate the validity of this assumption.
We study Mode I fracture in a viscoelastic lattice model with a nonlinear force law, with a focus on the velocity and linear stability of the steady-state propagating solution. This study is a continuation both of the study of the piece-wise linear model in Mode I, and the study of more general nonlinear force laws in Mode III fracture. At small driving, there is a strong dependency of the velocity curve on the dissipation and a strong sensitivity to the smoothness of the force law at large dissipation. At large driving we calculate, via a linear stability analysis, the critical velocity for t…
We study the effect of general nonlinear force laws in viscoelastic lattice models of fracture, focusing on the existence and stability of steady-state Mode III cracks. We show that the hysteretic behavior at small driving is very sensitive to the smoothness of the force law. At large driving, we find a Hopf bifurcation to a straight crack whose velocity is periodic in time. The frequency of the unstable bifurcating mode depends on the smoothness of the potential, but is very close to an exact period-doubling instability. Slightly above the onset of the instability, the system settles into a e…
We present an intuitive physical picture for fractures in nacre-type stratified materials via scaling arguments: strain distributions around a fracture are rather different depending on directions and size of fractures. We thus observe that viscoelastic effects are important for parallel fractures. These effect are taken into account via the simplest viscoelastic model for weakly cross-linked polymer. Within a certain limit, we find a trumpet crack shape similar to that in certain polymers and make predictions for the fracture energy of certain stratified materials in this mode.
It was shown that a material fatigue fracture diagram can be viewed as a locus of points with $σ$ and $\sqrt l$ coordinates' product equal to $K_{1c}/2$, and $σ$ and $l$ product -- to $G_{1c}/2$, where $K_{1c}$ and $G_{1c}$ are non-linear fracture mechanics force and energy criteria. It was established that the average number of interatomic bonds destroyed within one alternate stress $\nabla_{1cs}$ cycle is directly proportional to $σ$ that is twice as large as a peak value of $σ^a$. It was found that low-cycle fatigue is characterized by $σ>σ_{0.2}$ and $σ_{1cs}> 1$, high-cycle fatigue -- by …
This work proposes an investigation on the fracturing behavior of polymer nanocomposites. Towards this end, the study leverages on the analysis of a large bulk of fracture tests from the literature with the goal of critically investigating the effects of the nonlinear Fracture Process Zone (FPZ). It is shown that for most of the fracture tests, the effects of the nonlinear FPZ are not negligible, leading to significant deviations from Linear Elastic Fracture Mechanics (LEFM). As the data indicate, this aspect needs to be taken into serious consideration since the use of LEFM to estimate mode I…
In terms of nonlinear material fracture mechanics, the real (discrete)-structure material fracture model has been developed. The model rests on the demonstration of the fact that crack resistance $K_{1c}=2σ\sqrt l$ and fracture toughness are $G_{1c}=J_{1c}=2σl$ obtained on the basis of energy conservation law and derived without linear material fracture mechanics assumptions can be respectively taken as force and energy criteria for non-linear fracture mechanics. It is shown that $G_{1c}=K_{1c}^2/E$ is the energy criterion of linear fracture mechanics of material and it is sufficiently less th…
We study a planar thin brittle beam subject to elastic deformations and cracks described in terms of a nonlinear Griffith energy functional acting on $SBV$ deformations of the beam. In particular we consider the case in which elastic bulk contributions due to finite bending of the beam are comparable to the surface energy which is necessary to completely break the beam into several large pieces. In the limit of vanishing aspect ratio we rigorously derive an effective Griffith-Euler-Bernoulli functional which acts on piecewise $W^{2,2}$ regular curves representing the midline of the beam. The e…
The recently developed weakly nonlinear theory of dynamic fracture predicts $1/r$ corrections to the standard asymptotic linear elastic $1/\sqrt{r}$ displacement-gradients, where $r$ is measured from the tip of a tensile crack. We show that the $1/r$ singularity does not automatically conform with the notion of autonomy (autonomy means that any crack tip nonlinear solution is uniquely determined by the surrounding linear elastic $1/\sqrt{r}$ fields) and that it does not automatically satisfy the resultant Newton's equation in the crack parallel direction. We show that these two properties are …
A dynamic crack will travel in a straight path up to a material-dependent critical speed beyond which its path becomes erratic. Predicting this critical speed and discovering the origin of this instability are two outstanding problems in fracture mechanics. We recently discovered a simple scaling model based on an effective elastic modulus that gives successful predictions for this critical speed by transforming the nonlinear crack dynamics problem into a linear elasticity representation. We now show that a simple atomic picture based on broken-bond relaxation at the dynamic crack tip provides…
When branching is suppressed, rapid cracks undergo a dynamic instability from a straight to an oscillatory path at a critical velocity $v_c$. In a systematic experimental study using a wide range of different brittle materials, we first show how the opening profiles of straight cracks scale with the size $\ell_{nl}$ of the nonlinear zone surrounding a crack's tip. We then show, for all materials tested, that $v_c$ is both a fixed fraction of the shear speed and, moreover, that the instability wavelength is proportional to $\ell_{nl}$. These findings directly verify recent theoretical predictio…
The failure of materials and interfaces is mediated by cracks, nearly singular dissipative structures that propagate at velocities approaching the speed of sound. Crack initiation and subsequent propagation -- the dynamic process of fracture -- couples a wide range of time and length scales. Crack dynamics challenge our understanding of the fundamental physics processes that take place in the extreme conditions within the nearly singular region where material failure occurs. Here, we first briefly review the classic approach to dynamic fracture, "Linear Elastic Fracture Mechanics" (LEFM), and …
The two-dimensional oscillatory crack instability, experimentally observed in a class of brittle materials under strongly dynamic conditions, has been recently reproduced by a nonlinear phase-field fracture theory. Here we highlight the universal character of this instability by showing that it is present in materials exhibiting widely different near crack tip elastic nonlinearity, and by demonstrating that the oscillations wavelength follows a universal master curve in terms of dissipation-related and nonlinear elastic intrinsic length scales. Moreover, we show that upon increasing the drivin…
A new multiscale modeling approach to unravel the influence of interlayer sp3 bonds on the nonlinear large-deformation and fracture behaviors of 2D carbon nanostructures under tension
Interface cracking is one of the most prominent failure modes in fibre reinforced polymer (FRP) composites. Recent trends in high-tech applications of FRP composites exploit the limits of the load bearing capacity, generally encompassing the development of notable nonlinear effects from geometrical and material signatures. In this investigation, we present a comprehensive assessment of the new Linear Elastic Brittle Interface Model (LEBIM) in geometrically nonlinear applications undergoing mixed-mode fracture conditions. This interface model for triggering fracture events is formulated through…
In this work, we developed a bond-based cohesive peridynamics model (CPDM) and apply it to simulate inelastic fracture by using the meso-scale Xu-Needleman cohesive potential . By doing so, we have successfully developed a bond-based cohesive continuum mechanics model with intrinsic stress/strain measures as well as consistent and built-in macro-scale constitutive relations. The main novelties of this work are: (1) We have shown that the cohesive stress of the proposed nonlocal cohesive continuum mechanics model is exactly the same as the nonlocal peridynamic stress; (2) For the first time, we…
In this paper, we'll answer several abstract, formal questions about the nature of crack growth and nucleation. Bringing a field theory point of view to fracture illuminates things in what I hope will be an entertaining way. Formally, what is the crack nucleation rate? Fracture is an instability of elastic theory under tension. For thermally nucleated cracks, there is an analogy with supercooled liquids. Here the crack nucleation rate can be thought of as an imaginary part of the free energy - giving the decay rate of the metastable, stretched material. As an amusing consequence, we can formal…
Based on atomistic simulations, the nonlinear elastic properties of monolayer graphene nanoribbons under quasistatic uniaxial tension are predicted, emphasizing the effect of edge structures (armchair and zigzag, without and with hydrogen passivation). The results of atomistic simulations are interpreted within a theoretical framework of thermodynamics, which enables determination of the nonlinear functions for the strain-dependent edge energy and the hydrogen adsorption energy, for both zigzag and armchair edges. Due to the edge effects, the initial Young's modulus of graphene nanoribbons und…
The topologies of existing interface elements used to discretize cohesive cracks are such that they can be used to compute the relative displacements (displacement discontinuities) of two opposing segments (in 2D) or of two opposing facets (in 3D) belonging to the opposite crack faces and enforce the cohesive traction-separation relation. In the present work we propose a novel type of interface element for fracture mechanics sharing some analogies with the node-to-segment (in 2D) and with the node-to-surface (in 3D) contact elements. The displacement gap of a node belonging to the finite eleme…
When a frictional interface is subject to a localized shear load, it is often (experimentally) observed that local slip events initiate at the stress concentration and propagate over parts of the interface by arresting naturally before reaching the edge. We develop a theoretical model based on linear elastic fracture mechanics to describe the propagation of such precursory slip. The model's prediction of precursor lengths as a function of external load is in good quantitative agreement with laboratory experiments as well as with dynamic simulations, and provides thereby evidence to recognize f…
Cracks, the major vehicle for material failure, tend to accelerate to high velocities in brittle materials. In three-dimensions, cracks generically undergo a micro-branching instability at about 40% of their sonic limiting velocity. Recent experiments showed that in sufficiently thin systems cracks unprecedentedly accelerate to nearly their limiting velocity without micro-branching, until they undergo an oscillatory instability. Despite their fundamental importance and apparent similarities to other instabilities in condensed-matter physics and materials science, these dynamic fracture instabi…
We briefly review a number of important recent experimental and theoretical developments in the field of dynamic fracture. Topics include experimental validation of the equations of motion for straight tensile cracks (in both infinite media and strip geometries), validation of a new theoretical description of the near-tip fields of dynamic cracks incorporating weak elastic nonlinearities, a new understanding of dynamic instabilities of tensile cracks in both 2D and 3D, crack front dynamics, and the relation between frictional motion and dynamic shear cracks. Related future research directions …
Recent theoretical and computational progress has led to unprecedented understanding of symmetry-breaking instabilities in 2D dynamic fracture. At the heart of this progress resides the identification of two intrinsic, near crack tip length scales -- a nonlinear elastic length scale $\ell$ and a dissipation length scale $ξ$ -- that do not exist in the classical theory of cracks. In particular, it has been shown that at a high propagation velocity $v$, cracks in 2D brittle materials undergo an oscillatory instability whose wavelength varies linearly with $\ell$, and at yet higher propagation ve…
Highly-deformable materials, from synthetic hydrogels to biological tissues, are becoming increasingly important from both fundamental and practical perspectives. Their mechanical behaviors, in particular the dynamics of crack propagation during failure, are not yet fully understood. Here we propose a theoretical framework for the dynamic fracture of highly-deformable materials, in which the effects of a dynamic crack are treated with respect to the nonlinearly deformed (pre-stressed/strained), non-cracked, state of the material. Within this framework, we derive analytic and semi-analytic solu…
On the complementary roles of anisotropic crack density and anisotropic crack driving force in phase-field modeling of mixed-mode fracture
School of Mechanical Engineering, Changwon National University（昌原国立大学机械工程学院）；Department of Smart Shipbuilding Systems, Mokpo National University（木浦国立大学智能造船系统系）
The crack tip mechanics of strain gradient plasticity solids is investigated analytically and numerically. A first-order mechanism-based strain gradient (MSG) plasticity theory based on Taylor's dislocation model is adopted and implemented in the commercial finite element package ANSYS by means of a user subroutine. Two boundary value problems are considered, a single edge tension specimen and a biaxially loaded plate. First, crack tip fields are characterized. Strain gradient effects associated with dislocation hardening mechanisms elevate crack tip stresses relative to conventional plasticit…