We have studied the structural, magnetic and electronic properties of Co-implanted ZnO (0001) films grown on Al2O3 (1120) substrates for different implantation doses and over a wide temperature range. Strong room temperature ferromagnetism is observed with magnetic parameters depending on the cobalt implantation dose. A detailed analysis of the structural and magnetic properties indicates that there are two magnetic phases in Co-implanted ZnO films. One is a ferromagnetic phase due to the formation of long range ferromagnetic ordering between implanted magnetic cobalt ions in the ZnO layer, the second one is a superparamagnetic phase, which occurs due to the formation of metallic cobalt clusters in the Al2O3 substrate. Using x-ray resonant magnetic scattering, the element specific magnetization of cobalt, oxygen and Zn was investigated. Magnetic dichroism was observed at the Co L2,3 edges as well as at the O K edge. In addition, the anomalous Hall effect is also observed, supporting the intrinsic nature of ferromagnetism in Co-implanted ZnO films.
Magnetic anisotropies of Co-implanted ZnO (0001) films grown on single-crystalline Al2O3 (11-20) substrates have been studied by ferromagnetic resonance (FMR) technique for different cobalt implantation doses. The FMR data show that the easy and hard axes have a periodicity of 60 degrees in the film plane, in agreement with the hexagonal structure of the ZnO films. This six-fold in-plane magnetic anisotropy, which is observed for the first time in ZnO-based diluted magnetic semiconductors, is attributed to the substitution of cobalt on Zn sites in the ZnO structure, and a clear indication for …
We report on the structural and magnetic properties of a cobalt-implanted ZnO film grown on a sapphire substrate. X-ray diffraction and transmission electron microscopy reveal the presence of a (10-10)-oriented hexagonal Co phase in the Al2O3 sapphire substrate, but not in the ZnO film. Co clusters, with a diameter of is about 5-6 nm, form a Co rich layer in the substrate close to the ZnO/Al2O3 interface. Magnetization measurements indicate that there exist two different magnetic phases in the implanted region. One originates from the Co clusters in Al2O3, the other one belongs to a homogeneou…
We report structural and magnetic properties of pure ZnO rods using X-ray diffraction (XRD), magnetization hysteresis (M-H) loop and near edge x-ray fine structure spectroscopy (NEXAFS) study at O K edge. Sample of ZnO was prepared by co-precipitation method. XRD and selective area electron diffraction measurements infer that ZnO rods exhibit a single phase polycrystalline nature with wurtzite lattice. Field emission transmission electron microscopy, field emission scanning electron microscopy micrographs infers that ZnO have rod type microstructures with dimension 200 nm in diameter and 550 n…
We report the structural and magnetic properties of ZnO single crystals implanted at 623 K with up to 10 at. % of Ni. As revealed by X-ray diffraction, crystalline fcc-Ni nanoparticles were formed inside ZnO. The magnetic behavior (magnetization with field reversal and with different temperature protocol) of all samples is well explained by a magnetic Ni-nanoparticle system. Although the formation of Ni:ZnO based diluted magnetic semiconductor cannot be ruled out, the major contribution to the magnetic properties stems from crystalline nanoparticles synthesized under these implantation conditi…
The magneto-transport properties of single proton-implanted ZnO and of Li(7\%)-doped ZnO microwires have been studied. The as-grown microwires were highly insulating and not magnetic. After proton implantation the Li(7\%) doped ZnO microwires showed a non monotonous behavior of the negative magneto-resistance (MR) at temperature above 150 K. This is in contrast to the monotonous NMR observed below 50 K for proton-implanted ZnO. The observed difference in the transport properties of the wires is related to the amount of stable Zn vacancies created at the near surface region by the proton implan…
Unwanted secondary phases are one of the major problems in diluted magnetic semiconductor creation. Here, the authors show possibilities to avoid such phases in Fe implanted and postannealed ZnO(0001) single crystals. While -Fe nanoparticles are formed after such doping in as-polished crystals, high temperature (1273 K) annealing in O2 or high vacuum before implantation suppresses these phases. Thus, the residual saturation magnetization in the preannealed ZnO single crystals is about 20 times lower than for the as-polished ones and assigned to indirect coupling between isolated Fe ions rather…
We present superparamagnetic clusters of structurally highly disordered Co-Zn-O created by high fluence Co ion implantation into ZnO (0001) single crystals at low temperatures. This secondary phase cannot be detected by common x-ray diffraction but is observed by high-resolution transmission electron microscopy. In contrast to many other secondary phases in a ZnO matrix it induces low-field anomalous Hall effect and thus is a candidate for magneto-electronics applications.
Unexpected ferromagnetism has been observed in carbon doped ZnO films grown by pulsed laser deposition [Phys. Rev. Lett. 99, 127201 (2007)]. In this letter, we introduce carbon into ZnO films by ion implantation. Room temperature ferromagnetism has been observed. Our analysis demonstrates that (1) C-doped ferromagnetic ZnO can be achieved by an alternative method, i.e. ion implantation, and (2) the chemical involvement of carbon in the ferromagnetism is indirectly proven.
Room-temperature ferromagnetism has been induced within ZnO single crystals by implant-doping with Fe ions. For an implantation temperature of 620 K and an ion fluence of 4x10^16 cm^-2, very tiny Fe particles, formed inside the host matrix, are responsible for the ferromagnetic properties. They were identified using synchrotron X-ray diffraction and Moessbauer spectroscopy. On the other hand, Fe ions implanted at a temperature of 253 K and an ion fluence of 4x10^15 cm^-2 are incorporated into the host matrix and develop a room temperature diluted magnetic semiconductor (DMS).
We report room temperature ferromagnetism in as-implanted Eu doped ZnO (ZnO:Eu). To address the origin of ferromagnetism ab initio calculations of ZnO:Eu system are performed. Results show that the ferromagnetism is induced by ZnO point defects as Eu ions in perfect ZnO tend to align antiferromagnetically.
We investigated ZnO(0001) single crystals annealed in high vacuum with respect to their magnetic properties and cluster formation tendency after implant-doping with Fe. While metallic Fe cluster formation is suppressed, no evidence for the relevance of the Fe magnetic moment for the observed ferromagnetism was found. The latter along with the cluster suppression is discussed with respect to defects in the ZnO host matrix, since the crystalline quality of the substrates was lowered due to the preparation as observed by x-ray diffraction.
Recently theoretical works predict that some semiconductors (e.g. ZnO) doped with magnetic ions are diluted magnetic semiconductors (DMS). In DMS magnetic ions substitute cation sites of the host semiconductor and are coupled by free carriers resulting in ferromagnetism. One of the main obstacles in creating DMS materials is the formation of secondary phases because of the solid-solubility limit of magnetic ions in semiconductor host. In our study transition metal ions were implanted into ZnO single crystals with the peak concentrations of 0.5-10 at.%. We established a correlation between stru…
The structural and magnetic properties of V doped ZnO are presented. V ions were introduced into hydrothermal ZnO single crystals by ion implantation with fluences of 1.2*10^16 to 6*10^16 cm^-2. Post-implantation annealing was performed in high vacuum from 823 K to 1023 K. The ZnO host material still partly remains in a crystalline state after irradiation, and is partly recovered by annealing. The V ions show a thermal mobility as revealed by depth profile Auger electron spectroscopy. Synchrotron radiation x-ray diffraction revealed no secondary phase formation which indicates the substitution…
We simulated and experimentally investigated the sputter yield of ZnO and GaAs nanowires, which were implanted with energetic Mn ions at room temperature. The resulting thinning of the nanowires and the dopant concentration with increasing Mn ion fluency were measured by accurate scanning electron microscopy (SEM) and nano-X-Ray Fluorescence (nanoXRF) quantification, respectively. We observed a clear enhanced sputter yield for the irradiated nanowires compared to bulk, which is also corroborated by iradina simulations. These show a maximum if the ion range matches the nanowire diameter. As a c…
We report on structural, magnetic and electronic properties of Co-implanted TiO2 rutile single crystals for different implantation doses. Strong ferromagnetism at room temperature and above is observed in TiO2 rutile plates after cobalt ion implantation, with magnetic parameters depending on the cobalt implantation dose. While the structural data indicate the presence of metallic cobalt clusters, the multiplet structure of the Co L3 edge in the XAS spectra gives clear evidence for a substitutional Co 2+ state. The detailed analysis of the structural and magnetic properties indicates that there…
Ion implantation is an interesting method to dope semiconducting materials such as zinc oxide provided that the implantation-induced defects can be subsequently removed. Nitrogen implantation followed by anneals under O2 were carried out on zinc oxide nanowires in the same conditions as in a previous study on bulk ZnO [J. Appl.Phys. 109, 023513 (2011)], allowing a direct comparison of the defect recovery mechanisms. Transmission electron microscopy and cathodoluminescence were carried out to assess the effects of nitrogen implantation and of subsequent anneals on the structural and optical pro…
A close link between the charge transfer electronic structures and polarity dependent high-TC ferromagnetism of TM2+:ZnO DMSs (TM2+ = 3d ions) is demonstrated. Trends in ferromagnetism across the 3d series of TM2+:ZnO DMSs predicted from their charge transfer energies reproduce experimental trends well. These results provide a unified basis for understanding both n- and p-type ferromagnetic oxide DMSs.
The adsorption of hydrogen on the polar Zn-ended ZnO(0001) surface has been investigated by density functional {\it ab-initio} calculations. An on top H(1x1) ordered overlayer with genuine H-Zn chemical bonds is shown to be energetically favorable. The H covered surface is metallic and spin-polarized, with a noticeable magnetic moment at the surface region. Lower hydrogen coverages lead to strengthening of the H-Zn bonds, corrugation of the surface layer and to an insulating surface. Our results explain experimental observations of hydrogen adsorption on this surface, and not only predict a me…
We have investigated electronic structures and magnetic properties of potential ZnO based diluted magnetic semiconductors: (Fe, Co) and (Fe, Cu) codoped ZnO. The origins of ferromagnetism are shown to be different between two. (Fe, Co) codoped ZnO does not have a tendency of Fe-O-Co ferromagnetic cluster formation, and so the double exchange mechanism will not be effective. In contrast, (Fe, Cu) codoped ZnO has a tendency of the Fe-O-Cu ferromagnetic cluster formation with the charge transfer between Fe and Cu, which would lead to the ferromagnetism through the double-exchange mechanism. The f…
Structural and magnetic properties have been studied for polycrystalline Zn_1-xMn_xO (x=0.02, 0.03, 0.05). Low-temperature (~500 oC) synthesis leaves unreacted starting ZnO and manganese oxides. Contrary to a recent report, no bulk ferromagnetism was observed for single-phase materials synthesized in air at temperatures above 900 oC. Single-phase samples show paramagnetic Curie-Weiss behavior.
We report a surfactant assisted synthesis of Mn doped ZnO polycrystalline samples showing robust room temperature ferromagnetism as characterized by X-ray diffraction analysis, Transmission Electron Microscopy, Electron Paramagnetic Resonance and DC magnetization mearurements. This surfactant assisted synthesis method, developed by us, is found to be highly reproducible. Further, it can also be extended to the synthesis of other transition metal doped ZnO.
Nowadays ferromagnetism is often found in potential diluted magnetic semiconductor systems. However, many authors argue that the observed ferromagnetism stems from ferromagnetic precipitates or spinodal decomposition rather than from carrier mediated magnetic impurities, as required for a diluted magnetic semiconductor. In the present paper we answer this question for Fe-implanted ZnO single crystals comprehensively. Different implantation fluences and temperatures and post-implantation annealing temperatures have been chosen in order to evaluate the structural and magnetic properties over a w…
Following the theoretical predictions of ferromagnetism in Mn- and Co-doped ZnO, several workers reported ferromagnetism in thin films as well as in bulk samples of these materials. While some observe room-temperature ferromagnetism, others find magnetization at low temperatures. Some of the reports, however, cast considerable doubt on the magnetism of Mn- and Co-doped ZnO. In order to conclusively establish the properties of Mn- and Co-doped ZnO, samples with 6 percent and 2 percent dopant concentrations, have been prepared by the low-temperature decomposition of acetate solid solutions. The …
We report on the stability and magnetic state of ion implanted $^8$Li in single crystals of the semiconductor ZnO using $β$-detected nuclear magnetic resonance. At ultradilute concentrations, the spectra reveal distinct Li sites from 7.6 to 400 K. Ionized shallow donor interstitial Li is stable across the entire temperature range, confirming its ability to self-compensate the acceptor character of its (Zn) substitutional counterpart. Above 300 K, spin-lattice relaxation indicates the onset of correlated local motion of interacting defects, and the spectra show a site change transition from dis…
We present the results of a computational study of ZnO in the presence of Co and Mn substitutional impurities. The goal of our work is to identify potential ferromagnetic ground states within the (Zn,Co)O or (Zn,Mn)O material systems that are also good candidates for piezoelectricity. We find that, in contrast to previous results, robust ferromagnetism is not obtained by substitution of Co or Mn on the Zn site, unless additional carriers (holes) are also incorporated. We propose a practical scheme for achieving such $p$-type doping in ZnO.
We report here enhancement of ferromagnetism in pure ZnO upon thermal annealing with the ferromagnetic transition temperature Tc above room temperature. We observe a finite coercive field upto 300K and a finite thermoremanent magnetization upto 340K for the annealed sample. We propose that magnetic moments can form at anionic vacancy clusters. Ferromagnetism can occur due to either superexchange between vacancy clusters via isolated F+ centers, or through a limited electron delocalization between vacancy clusters. Isolated vacancy clusters or isolated F+ centers give rise to a strong paramagne…
We report room temperature ferromagnetism in boron-doped ZnO both experimentally and theoretically. The single phase Zn1-xBxO films deposited under high oxygen pressure by pulsed-laser deposition show ferromagnetic behavior at room temperature. The saturation magnetization increases monotonously from 0 to 1.5 emu/cm3 with the increasing of B component x from 0 to 6.8%. The first-principles calculations based on density functional theory demonstrate that the ferromagnetism in B-doped ZnO originates from the induced magnetic moments of oxygen atoms in the nearest neighbor sites to the B-Zn vacan…
We report on the magnetic properties of thoroughly characterized Zn1-xCoxO epitaxial thin films, with low Co concentration, x=0.003-0.005. Magnetic and EPR measurements, combined with crystal field theory, reveal that isolated Co2+ ions in ZnO possess a strong single ion anisotropy which leads to an "easy plane" ferromagnetic state when the ferromagnetic Co-Co interaction is considered. We suggest that the peculiarities of the magnetization process of this state can be viewed as a signature of intrinsic ferromagnetism in ZnO:Co materials.
We have developed a simple, surfactant assisted synthesis route for the preparation, in gram quantities, of Co and Li doped ZnO nanocrystalline samples showing robust room temperature ferromagnetism. Our studies show that RTF is intrinsic to Zn0.85Co0.05Li0.10O and not due to any segregated secondary phases. In addition, it has been shown that the defects play an important role in activating RTF in these oxide systems. This also provide an explanation for the widely varying results observed in the literature. The method can also be extended for the synthesis of other transition metal doped ZnO…
Magnetic 3d-ions doped into wide-gap oxides show signatures of room temperature ferromagnetism, although their concentration is two orders of magnitude smaller than that in conventional magnets. The prototype of these exceptional materials is Co-doped ZnO, for which an explanation of the room temperature ferromagnetism is still elusive. Here we demonstrate that magnetism originates from Co2+ oxygen-vacancy pairs with a partially filled level close to the ZnO conduction band minimum. The magnetic interaction between these pairs is sufficiently long-ranged to cause percolation at moderate concen…
The prediction of ferromagnetism at room temperature in Co-ZnO thin films has generated a large interest in the community due to the possible applications. However, the results are controversial, going from ferromagnetism to non-ferromagnetism, leading to a large debate about its origin (secondary phase, Co clusters or not). By carefully studying the micro-structure of various Co-ZnO films, we show that the Co2+ partly substitutes the ZnO wurtzite matrix without forming Co clusters. Surprisingly, the ferromagnetism nature of the films disappears as the Co content increases. In addition, our re…
Nitrogen embedded ZnO:N films prepared by pulsed laser deposition exhibit significant ferromagnetism. The nitrogen ions contained in ZnO confirmed by Secondary Ion Microscopic Spectrum and Raman experiments and the embedded nitrogen ions can be regarded as defects. According to the experiment results, a mechanism is proposed based on one of the electrons in the completely filled d-orbits of Zn that compensates the dangling bonds of nitrogen ions and leads to a net spin of one half in the Zn orbits. These one half spins strongly correlate with localized electrons that are captured by defects to…
Fe-doped ZnO nanocrystals are successfully synthesized and structurally characterized by using x-ray diffraction and transmission electron microscopy. Magnetization measurements on the same system reveal a ferromagnetic to paramagnetic transition temperature > 450 K with a low-temperature transition from ferromagnetic to spin-glass state due to canting of the disordered surface spins in the nanoparticle system. Local magnetic probes like EPR and Mossbauer indicate the presence of Fe in both valence states Fe2+ and Fe3+. We argue that the presence of Fe3+ is due to the possible hole doping in t…
We report here on the magnetic properties of ZnO:Mn and ZnO:Co doped nanoparticles. We have found that the ferromagnetism of ZnO:Mn can be switched on and off by consecutive low-temperature annealings in O2 and N2 respectively, while the opposite phenomenology was observed for ZnO:Co. These results suggest that different defects (presumably n-type for ZnO:Co and p-type for ZnO:Mn) are required to induce a ferromagnetic coupling in each case. We will argue that ferromagnetism is likely to be restricted to a very thin, nanometric layer, at the grain surface. These findings reveal and give insigh…
Cobalt and silver co-doping has been undertaken in ZnO thin films grown by pulsed laser deposition in order to investigate the ferromagnetic properties in ZnO-based diluted magnetic materials and to understand the eventual relation between ferromagnetism and charge carriers. Hall transport measurements reveal that Ag doping up to 5% leads to a progressive compensation of the native n-type carriers. The magnetization curves show ferromagnetic contributions for all samples at both 5 K and room temperature, decreasing with increasing the Ag concentration. First principles modeling of the possible…
The electronic structure and magnetic coupling properties of rare-earth metals (Gd, Nd) doped ZnO have been investigated using first-principles methods. We show that the magnetic coupling between Gd or Nd ions in the nearest neighbor sites is ferromagnetic. The stability of the ferromagnetic coupling between Gd ions can be enhanced by appropriate electron doping into ZnO:Gd system and the room-temperature ferromagnetism can be achieved. However, for ZnO:Nd system, the ferromagnetism between Nd ions can be enhanced by appropriate holes doping into the sample. The room-temperature ferromagnetism…
Several experimental studies have referred to the grain boundary (GB) defect as the origin of the ferromagnetism in ZnO. However, the mechanism of this hypothesis has never been confirmed. Present study investigates the atomic structure and the effect of point defects in a ZnO GB using the GGA+U approximation. The relaxed GB possesses large periodicity and channels with 8 and 10 numbered atoms having 4 and 3 fold coordination. Unlike O vacancy (VO), Zn vacancy (VZn) is preferentially aggregated at the GB, relative to the bulk-like region, indicating the possibility of obtaining p-type conducti…
Although zinc oxide is a promising material for the fabrication of short wavelength optoelectronic devices, p-type doping is a step that remains challenging for the realization of diodes. Out of equilibrium methods such as ion implantation are expected to dope ZnO successfully provided that the non-radiative defects introduced by implantation can be annealed out. In this study, ZnO substrates are implanted with nitrogen ions, and the extended defects induced by implantation are studied by transmission electron microscopy and X-ray diffraction (XRD), before and after annealing at 900^{\circ}C. …
A density functional theory study of substitutional carbon impurities in ZnO has been performed, using both the generalized gradient approximation (GGA) and a hybrid functional (HSE06) as exchange-correlation functional. It is found that the non-spinpolarized C$_\mathrm{Zn}$ impurity is under almost all conditions thermodynamically more stable than the C$_\mathrm{O}$ impurity which has a magnetic moment of $2μ_{\mathrm{B}}$, with the exception of very O-poor and C-rich conditions. This explains the experimental difficulties in sample preparation in order to realize $d^{0}$-ferromagnetism in C-…
We have investigated the electronic structure of ZnO:Mn and ZnO:Mn,N thin films using x-ray magnetic circular dichroism (XMCD) and resonance-photoemission spectroscopy. From the Mn 2$p$$\rightarrow3d$ XMCD results, it is shown that, while XMCD signals only due to paramagnetic Mn$^{2+}$ ions were observed in ZnO:Mn, nonmagnetic, paramagnetic and ferromagnetic Mn$^{2+}$ ions coexist in ZnO:Mn,N. XMCD signals of ZnO:Mn,N revealed that the localized Mn$^{2+}$ ground state and Mn$^{2+}$ state hybridized with ligand hole coexisted, implying $p$-$d$ exchange coupling. In the valence-band spectra, spe…
In the last decade, transition-metal-doped ZnO has been intensively investigated as a route to room-temperature diluted magnetic semiconductors (DMSs). However, the origin for the reported ferromagnetism in ZnO-based DMS remains questionable. Possible options are diluted magnetic semiconductors, spinodal decomposition, or secondary phases. In order to clarify this question, we have performed a thorough characterization of the structural and magnetic properties of Co- and Ni-implanted ZnO single crystals. Our measurements reveal that Co or Ni nanocrystals (NCs) are the major contribution of the…
The nature of the often reported room temperature ferromagnetism in transition metal doped oxides is still a matter of huge debate. Herein we report on room temperature ferromagnetism in high quality Co-doped ZnO (Zn1-xCoxO) bulk samples synthesized via standard solid-state reaction route. Reference paramagnetic Co-doped ZnO samples with low level of structural defects are subjected to heat treatments in a reductive atmosphere in order to introduce defects in the samples in a controlled way. A detailed structural analysis is carried out in order to characterize the induced defects and their co…
Successful synthesis of room-temperature ferromagnetic semiconductors, Zn$_{1-x}$Fe$_{x}$O, is reported. The essential ingredient in achieving room-temperature ferromagnetism in bulk Zn$_{1-x}$Fe$_{x}$O was found to be additional Cu doping. A transition temperature as high as 550 K was obtained in Zn$_{0.94}$Fe$_{0.05}$Cu$_{0.01}$O; the saturation magnetization at room temperature reached a value of $0.75 μ_{\rm B}$ per Fe. Large magnetoresistance was also observed below $100 $K.
During the past years there has been renewed interest in the wide-bandgap II-VI semiconductor ZnO, triggered by promising prospects for spintronic applications. First, ferromagnetism was predicted for dilute magnetic doping. In comprehensive investigation of ZnO:Co thin films based on the combined measurement of macroscopic and microscopic properties, we find no evidence for carrier-mediated itinerant ferromagnetism. Phase-pure, crystallographically excellent ZnO:Co is uniformly paramagnetic. Superparamagnetism arises when phase separation or defect formation occurs, due to nanometer-sized met…
We discuss the properties of semiconducting bulk ZnO when substituted with the magnetic transition metal ions Mn and Co, with substituent fraction ranging from $x$ = 0.02 to $x$ = 0.15. The magnetic properties were measured as a function of magnetic field and temperature and we find no evidence for magnetic ordering in these systems down to $T$ = 2 K. The magnetization can be fit by the sum of a Curie-Weiss term with a Weiss temperature of $Θ\gg$100 K and a Curie term. We attribute this behavior to contributions from both \textit{t}M ions with \textit{t}M nearest neighbors and from isolated sp…
The origin of room temperature (RT) ferromagnetism (FM) in Ni doped ZnO samples are systematically investigated through physical, optical, and magnetic properties of nanostructure, prepared by simple low-temperature wet chemical method. Reitveld refinement of X-ray diffraction pattern displays an increase in lattice parameters with strain relaxation and contraction in Zn/O occupancy ratio by means of Ni-doping. Similarly scanning electron microscope demonstrates modification in the morphology from nanorods to nanoflakes with Ni doping, suggests incorporation of Ni ions in ZnO. More interesting…
The results of XPS core-level and valence band measurements, photoluminescence spectra of a-SiO2 implanted by Zn-ions (E=30 keV, D=1*1017 cm^-2) and Density Functional Theory calculations of electronic structure as well as formation energies of structural defects in silica glass induced by Zn-ion implantation are presented. Both theory and experiment show that it is energetically more favorable for implanted zinc ions to occupy the interstitial positions instead of cation substitution. As a result, the Zn-ions embedded to interstitials, form chemical bonds with the surrounding oxygen atoms, fo…
We studied structural, optical and magnetic properties of high-quality 5 and 15% Co-doped ZnO films grown by plasma-assisted molecular beam epitaxy (MBE) on (0001)-sapphire substrates. Magnetic force microscopy (MFM) and magnetic measurements with SQUID magnetometer show clear ferromagnetic behavior of the films up to room temperature whereas they are antiferromagnetic below 200 K approximately. Temperature dependence of the carrier mobility was determined using Raman line shape analysis of the longitudinal-optical-phonon-plasmon coupled modes. It shows that the microscopic mechanism for ferro…
Single phase Mn doped (2 at %) ZnO samples have been synthesized by solid-state reaction technique. Before the final sintering at 500 C, the mixed powders have been milled for different milling periods (6, 24, 48 and 96 hours). The grain sizes of the samples are very close to each other (~ 32 \pm 4 nm). However, the defective state of the samples is different from each other as manifested from the variation of magnetic properties and electrical resistivity with milling time. All the samples have been found to be ferromagnetic with clear hysteresis loops at room temperature. The maximum value f…
We have investigated the magnetic properties of non-doped ZnO nanostructures by using {\it ab initio} total energy calculations. Contrary to many proposals that ferromagnetism in non-doped semiconductors should be induced by intrinsic point defects, we show that ferromagnetism in nanostructured materials should be mediated by extended defects such as surfaces and grain boundaries. This kind of defects create delocalized, spin polarized states that should be able to warrant long-range magnetic interactions.
II-oxide and III-nitride semiconductors doped by nonmagnetic 2p light elements are investigated as potential dilute magnetic semiconductors (DMS). Based on our first-principle calculations, nitrogen doped ZnO, carbon doped ZnO, and carbon doped AlN are predicted to be ferromagnetic. The ferromagnetism of such DMS materials can be attributed to a p-d exchange-like p-p coupling interaction which is derived from the similar symmetry and wave function between the impurity (p-like t_2) and valence (p) states. We also propose a co-doping mechanism, using beryllium and nitrogen as dopants in ZnO, to …
The effect of hydrogenation on magnetic properties of Zn0.85Co0.05Li0.10O nanoparticles is presented. It was found that the sample hydrided at room temperature (RT) showed weak ferromagnetism (FM) while that hydrided at 400oC showed robust ferromagnetism at room temperature. In both cases reheating the sample at 400oC in air converts it back into paramagnetic state (P) completely. The characterization of samples by X-ray and electron diffraction (ED) showed that room temperature ferromagnetism observed in the samples hydrogenated at RT is intrinsic in nature whereas that observed in the sample…
Recently, d0 ferromagnetic materials have been projected as one of the promising novel materials for spintronics applications. In this work, we have studied Li-doped ZnO compounds, i.e. Zn1-xLixO (x=0, 0.02, 0.04, and 0.06) samples, prepared by the solid-state reaction route method. From the study of crystal structure using X-ray diffraction (XRD) patterns, it is evident that the prepared materials have been formed in a single-phase of the hexagonal wurtzite structure. The refinement of the XRD patterns suggests that there are very small changes in the lattice parameters upon Li-incorporation …
ZnO nanoparticles with Wurtzite structure were prepared by chemical methods at low temperature in aqueous solution. Nanoparticles are in the range from about 10 to 30 nm. Ferromagnetic properties were observed from 2 K to room temperature and above. Magnetization vs temperature, M(T) and isothermal measurements M(H) were determined. The coercive field clearly shows ferromagnetism above room temperature. The chemical synthesis, structural defects in the bulk related to oxygen vacancies are the main factors for the observed magnetic behavior. PACS numbers: 61.46.Hk Nanocrystals, 75.50.Pp Magneti…
We recently reported the observation of room temperature ferromagnetism in mixtures of ZnO and Co3O4 despite the diamagnetic and antiferromagnetic character of these oxides respectively. Here we present a detailed study on the electronic structure of this material in order to account for this unexpected ferromagnetism. Electrostatic interactions between both oxides lead to a dispersion of Co3O4 particles over the surface of ZnO larger ones. As a consequence, the reduction of Co+3 to Co2+ at the particle surface takes place as evidenced by XAS measurements and optical spectrocopy. This reductio…
The possibility that the apparent room temperature ferromagnetism, often measured in Co-doped ZnO, is due to uncompensated spins at the surface of wurtzite CoO nanoclusters is investigated by means of a combination of density functional theory and Monte Carlo simulations. We find that the critical temperature extracted from the specific heat systematically drops as the cluster size is reduced, regardless of the particular cluster shape. Furthermore the presence of defects, in the form of missing magnetic sites, further reduces $T_\mathrm{C}$. This suggests that even a spinodal decomposed phase…
Ion implantation of Mn ions into hole-doped GaP has been used to induce ferromagnetic behavior above room temperature for optimized Mn concentrations near 3 at.%. The magnetism is suppressed when the Mn dose is increased or decreased away from the 3 at.% value, or when n-type GaP substrates are used. At low temperatures the saturated moment is on the order of one Bohr magneton, and the spin wave stiffness inferred from the Bloch-law T^3/2 dependence of the magnetization provides an estimate Tc = 385K of the Curie temperature that exceeds the experimental value, Tc = 270K. The presence of ferro…
Experimental studies of Zn1-xCoxO as thin films or nanocrystals have found ferromagnetism and Curie temperatures above room temperature and that p- or n-type doping of Zn1-xCoxO can change its magnetic state. Bulk Zn1-xCoxO with a low defect density and x in the range used in experimental thin film studies exhibits ferromagnetism only at very low temperatures. Therefore defects in thin film samples or nanocrystals may play an important role in promoting magnetic interactions between Co ions in Zn1-xCoxO. The electronic structures of Co substituted for Zn in ZnO, Zn and O vacancies, substituted…
It is shown that substitution of C or N for O recently proposed as a way to create ferromagnetism in otherwise nonmagnetic oxide insulators is curtailed by formation of impurity pairs, and the resultant C2 spin=1 dimers as well as the isoelectronic N2^{2+} interact antiferromagneticallly in p-type MgO. For C-doped ZnO, however, we demonstrate using the HSE hybrid functional that a resonance of the spin-polarized C2 ppπ* states with the host conduction band results in a long-range ferromagnetic interaction. Magnetism of open-shell impurity molecules is proposed as a possible route to d0-ferroma…
Recently the point defect responsible for the intra-3$d$ luminescence of cobalt in doped ZnO samples has been indentified\,\cite{pssb2019}. In this work we further extend our investigation to other point defects in Co-doped ZnO. We use density-functional theory and GW calculations to determined the orbital-resolved band structure of cobalt doped zinc oxide (ZnO). We show that mainly O-p and Co-d orbitals take part in the process and confirm that an oxygen interstitial nearby a cobalt atom is a likely defect to occur in Co-implanted ZnO samples. We also rule out that other common point defects …