High-resolution synchrotron XRD study of Zr-rich compositions of Pb(Zr_xTi_1-x)O_3 (0.525\leq x \leq 0.60): evidence for the absence of the rhombohedral phase
Results of Rietveld analysis of the synchrotron XRD data on Pb(Zr_xTi_1-x)O_3 (PZT) for 0.525\leqx\leq0.60 are presented to show the absence of rhombohedral phase on the Zr-rich side of the morphotropic phase boundary (MPB). Our results reveal that the structure of PZT is monoclinic in the Cm space group for 0.525\leq x\leq 0.60. The nature of the monoclinic distortion changes from pseudo-tetragonal for 0.525\leqx\leq0.54 to pseudo-rhombohedral for x>0.54.
Raman spectra of PbZr1-xTixO3 ceramics with titanium concentration varying between 0.40 and 0.60 were measured at 7 K. By observing the concentration-frequency dependence of vibrational modes, we identified the boundaries among rhombohedral, monoclinic, and tetragonal ferroelectric phases. The analysis of the spectra was made in the view of theory group analysis making possible the assignment of some modes for the monoclinic phase.
Neutron diffraction data obtained on single crystals of PbZr1-xTixO3 with x = 0.325 and x = 0.460, which lie on the pseudorhombohedral side of the morphotropic phase boundary, suggest a coexistence of rhombohedral (R3m/R3c) and monoclinic (Cm) domains and that monoclinic order is enhanced by Ti substitution. A monoclinic phase with a doubled unit cell (Cc) is ruled out as the ground state.
The results are presented of anelastic and dielectric spectroscopy measurements on large grain ceramic PZT with compositions near the two morphotropic phase boundaries (MPBs) that the ferroelectric (FE) rhombohedral phase has with the Zr-rich antiferroelectric and Ti-rich FE tetragonal phases. These results are discussed together with similar data from previous series of samples, and reveal new features of the phase diagram of PZT, mainly connected with octahedral tilting and its coupling with the polar modes. Additional evidence is provided of what we interpret as the onset of the tilt instab…
The historic de Haas van Alphen effect observed in the late 1950s in CSIR-NPL by J.S. Dhillon and D. Shoenberg in pure bismuth and zinc metal is revisited in this article hrough a single crystalline phase of bismuth crystal, which is observed in terms of resistivity as predicted by Shubnikov de Haas oscillations. The occurrence of oscillations in the transverse magnetic field confirms the presence of the Fermi surface. The single crystal of bismuth is grown through solid-state reaction under an optimized heat treatment whose purity and structural phase are confirmed through XRD, SEM, and EDAX.
A nanometric Sb2Te3 rhombohedral phase was produced from Sb and Te by mechanical alloying for 3 hours and its structural stability was studied by synchrotron X-ray diffraction (XRD) and Raman spectroscopy (RS) measurements as a function of pressure. A phase transformation from the ambient pressure rhombohedral phase into a β-Sb2Te3 monoclinic structure between 9.8 and 13.2 GPa is observed by XRD. This phase transformation is confirmed by the Raman spectroscopy measurements. The pressure dependence of the volume fited to a Birch-Murnaghan equation of state gives a bulk modulus B0 = 40.6 +- 1.5 …
An approach combining the Rietveld method and pairs distribution function analysis to study crystalline materials under high pressure or temperature was early proposed by us, and in this study, it was applied to investigate de effect of high pressure on the rhombohedral Bi2Te3 phase. The refined structural parameters obtained from the Rietveld refinement of the XRD patterns measured for pressures up to 9.1 GPa were used as input data to simulate the partial and total structure factors SBiBi, SBiTe, STeTe, and SBi2Te3. Fourier transformation of the Sij factors permitted to obtain the partial an…
We review some of the current research on two of the ultra-high piezoelectric relaxors Pb(Mg1/3Nb2/3)O3 (PMN) and Pb(Zn1/3Nb2/3)O3 (PZN). The discovery of a monoclinic phase in Pb(Zr1-xTix)O3 (PZT) in 1999 by Noheda et al. forced a reassessment of the structural symmetries found near the morphotropic phase boundary in PZT, as well as in the PbTiO3 (PT) doped systems PZN-PT, and PMN-PT. All three systems are now known to have nearly identical phase diagrams that exhibit a rhombohedral-monoclinic-tetragonal structural sequence with increasing PbTiO3 concentration. The dynamical properties of the…
Polycrystalline ceramic samples and a single crystal of EuTiO3 have been investigated by Raman spectroscopy in the temperature range 80-300 K. Although synchrotron XRD data clearly indicated the cubic to tetragonal phase transition around 282 K, no mode from the symmetry allowed Raman active phonons was found in the tetragonal phase, contrary to the case of the homologous SrTiO3. In order to study the evolution of this unique characteristic, ceramics of EuxSr1-xTiO3 (x=0.03-1.0) characterized by synchrotron XRD for the structural phase transition have been also investigated by Raman spectrosco…
The structural phase transformations of 0.7Pb(Mg1/3Nb2/3)O3-0.3PbTiO3 (PMN-30%PT) have been studied using x-ray diffraction (XRD) and neutron scattering as a function of temperature and electric field. We observe the phase transformational sequence (i) cubic (C)-> tetragonal (T)-> rhombohedral (R) in the zero-field-cooled (or ZFC) condition; (ii) C->T-> monoclinic (MC)-> monoclinic (MA) in the field-cooled (or FC) condition; and (iii) R->MA->MC->T with increasing field at fixed temperature beginning from the ZFC condition. Upon removal of the field, the MA phase is stable at room temperature i…
Piezoelectric and ferroelectric ceramics with a high Curie temperature (Tc) have attracted a growing attention owning to their applications under severe environments. In this work, phase structure, dielectric, ferroelectric and piezoelectric properties of (0.975-x)BiScO3-xPbTiO3-0.025Pb(Cd1/3Nb2/3)O3 ceramics (x = 0.58-0.64) were studied. A composition-induced structural transformation occurs from rhombohedral phase to tetragonal phase through an intermediate monoclinic phase with the increasing PT concentration. The relationship between structure and electrical properties of the system were d…
Single phase barium titanate-bismuth ferrite ((1-x)BaTi$_3$-(x)BiFe$_3$, BTO-BFO) solid solutions were prepared using citric acid and ethylene glycol assisted sol-gel synthesis method. Depending on the dopant content the samples are characterized by tetragonal, tetragonal-pseudocubic, pseudocubic and rhombohedral structure as confirmed by Raman spectroscopy and XRD measurements. An increase of the BFO content leads to a reduction in the cell parameters accompanied by a decrease in polar distortion of the unit cell wherein an average particle size increases from 60 up to 350 nm. Non zero piezor…
Coatings of (Al1-xVx)2O3, with x ranging from 0 to 1, were deposited by pulsed DC reactive sputter deposition on Si(100) at a temperature of 550 °C. XRD showed three different crystal structures depending on V-metal fraction in the coating: α-V2O3 rhombohedral structure for 100 at.% V, a defect spinel structure for the intermediate region, 63 - 42 at.% V. At lower V-content, 18 and 7 at.%, a gamma-alumina-like solid solution was observed, shifted to larger d-spacing compared to pure γ-Al2O3. The microstructure changes from large columnar faceted grains for α-V2O3 to smaller equiaxed grains whe…
Twinning is a common crystallographic phenomenon, which usually occurs in crystals during symmetry-lowering phase transition. Once formed, twin domains play an important role in defining physical properties: for example, twin domains underpin the giant piezoelectric effect in ferroelectrics, superelasticity in ferroelastics and the shape-memory effect in martensitic alloys. Unfortunately, there is still a lack of experimental methods for imaging and characterization of twin domain patterns. Here, we propose a theoretical framework and an algorithm for the recognition of twinned pairs of ferroe…
There is a general perception that large piezoelectric response in ferroelectric alloys requires tuning the system towards a morphotropic phase boundary (MPB), i.e., a composition driven inter-ferroelectric instability. Here we show that high piezoelectric response can be realized even in non-MPB alloy systems. This is demonstrated on (1-x)PbTiO3-(x)Bi(Zr0.5Ni0.5)O3 (PT-BNZ) by a comprehensive study involving electric-field and temperature dependent XRD, Raman spectroscopy, dielectric, piezoelectric and high field electrostrain measurements. We found that poling-field irreversibly suppresses t…