An extensive comparison of anisotropies in MBE grown (Ga,Mn)As material
C. Gould, S. Mark, K. Pappert, G. Dengel, J. Wenisch, R. P. Campion, A. W. Rushforth, D. Chiba, Z. Li, X. Liu, W. Van Roy, H. Ohno, J. K. Furdyna, B. Gallagher,… 展开作者
C. Gould, S. Mark, K. Pappert, G. Dengel, J. Wenisch, R. P. Campion, A. W. Rushforth, D. Chiba, Z. Li, X. Liu, W. Van Roy, H. Ohno, J. K. Furdyna, B. Gallagher, K. Brunner, G. Schmidt, L. W. Molenkamp
This paper reports on a detailed magnetotransport investigation of the magnetic anisotropies of (Ga,Mn)As layers produced by various sources worldwide. Using anisotropy fingerprints to identify contributions of the various higher order anisotropy terms, we show that the presence of both a [100] and a [110] uniaxial anisotropy in addition to the primary ([100] + [010]) anisotropy is common to all medium doped (Ga,Mn)As layers typically used in transport measurement, with the amplitude of these uniaxial terms being characteristic of the individual layers.
In this report, we demonstrate high spectral responsivity (SR) in MBE grown epitaxial \b{eta}-Ga2O3-based solar blind MSM photodetectors (PD). (-2 0 1)-oriented \b{eta}-Ga2O3 thin film was grown by plasma-assisted MBE on c-plane sapphire substrates. MSM devices fabricated with Ni/Au contacts in an interdigitated geometry were found to exhibit peak SR > 1.5 A/W at 236-240 nm at a bias of 4 V with a UV to visible rejection ratio > 105. The devices exhibited very low dark current < 10 nA at 20 V and showed no persistent photoconductivity (PPC) as evident from the sharp transients with a photo-to-…
(Bi1-xSbx)2Se3 thin films have been prepared using molecular beam epitaxy (MBE). We demonstrate the angle-resolved photoemission spectroscopy (ARPES) and transport evidence for the existence of strong and robust topological surface states in this ternary system. Large tunability in transport properties by varying the Sb doping level has also been observed, where insulating phase could be achieved at x=0.5. Our results reveal the potential of this system for the study of tunable topological insulator and metal-insulator transition based device physics.
This work presents methods of controlling the density of self-assembled CdTe quantum dots (QDs) grown by molecular beam epitaxy. Two approaches are discussed: increasing the deposition temperature of CdTe and the reduction of CdTe layer thickness. Photoluminescence (PL) measurements at low temperature confirms that both methods can be used for significant reduction of QDs density from 10$^{10}$QD/cm$^2$ to 10$^7$-10$^8$QD/cm$^2$. For very low QDs density, identification of all QDs lines observed in the spectrum is possible.
We report on the direct measurement of hot electrons generated in the active region of blue light-emitting diodes grown by ammonia molecular beam epitaxy by electron emission spectroscopy. The external quantum efficiency of these devices is <1% and does not droop; thus, the efficiency losses from the intrinsic, interband, electron-electron-hole, or electron-hole-hole Auger should not be a significant source of hot carriers. The detection of hot electrons in this case suggests that an alternate hot electron generating process is occurring within these devices, likely a trap-assisted Auger recom…
Three different elements, Silicon, Selenium, and Tellurium, are ion-implanted in Gallium arsenide to form a conducting layer that serves as a back-gate to a molecular beam epitaxy (MBE) overgrown two-dimensional electron gas (2DEG). While the heavy ion Tellurium creates too many damages in the gallium arsenide to form a conducting layer, both Silicon and Selenium show promising results combined with MBE-grown high-quality 2DEGs. Similar 2DEG mobility compared to non-implanted reference samples is achieved for both Silicon and Selenium implanted structures. Individual contacts to the back-gate …
We demonstrate first measurements of successful spin generation in crystalline Co$_2$FeSi/MgO/GaAs hybrid structures grown by molecular-beam epitaxy (MBE), with different MgO interlayer thicknesses. Using non-local spin valve and non-local Hanle measurement configurations, we determine spin lifetimes of ${τ\approx 100}$~ns and spin diffusion lengths of ${λ\approx 5.6}$~$μ$m for different MgO layer thicknesses proving the high quality of the GaAs transport channel. For an optimized MgO layer thickness, the bias dependence of the spin valve signals indicates the verification of the half-metallic…
Impact of MBE-grown (In,Ga)As/GaAs metamorphic buffers on excitonic and optical properties of single quantum dots with single-photon emission tuned to the telecom range
The strong light-matter interaction in transition Metal dichalcogenides (TMDs) monolayers (MLs) is governed by robust excitons. Important progress has been made to control the dielectric environment surrounding the MLs, especially through hexagonal boron nitride (hBN) encapsulation, which drastically reduces the inhomogeneous contribution to the exciton linewidth. Most studies use exfoliated hBN from high quality flakes grown under high pressure. In this work, we show that hBN grown by molecular beam epitaxy (MBE) over a large surface area substrate has a similarly positive impact on the optic…
The quest for extremely high mobilities of 2d electron gases in MBE-grown heterostructures is hampered by the available purity of the starting materials, particularly of the gallium. Here we compare the role of different Ga lots having nominally the highest possible quality on the mobility and the photoluminescence (PL) of modulation doped single interface structures and find significant differences. A weak exciton PL reveals that the purity of the Ga is insufficient. No high mobility can be reached with such a lot with a reasonable effort. On the other hand, a strong exciton PL indicates a hi…
The emergence of two-dimensional (2D) materials launched a fascinating frontier of flatland electronics. Most crystalline atomic layer materials are based on layered van der Waals materials with weak interlayer bonding, which naturally leads to thermodynamically stable monolayers. We report the synthesis of a 2D insulator comprised of a single atomic sheet of honeycomb structure BeO (h-BeO), although its bulk counterpart has a wurtzite structure. The h-BeO is grown by molecular beam epitaxy (MBE) on Ag(111) thin films that are conveniently grown on Si(111) wafers. Using scanning tunneling micr…