A detailed investigation of first order ferrimagnetic (FRI) to antiferromagnetic (AFM) transition in Co (15%) doped $Mn_2Sb$ is carried out. These measurements demonstrate anomalous thermomagnetic irreversibility and glass-like frozen FRI phase at low temperatures. The irreversibility arising between the supercooling and superheating spinodals is distinguised in an ingenious way from the irreversibility arising due to kinetic arrest. Field annealing measurements shows reentrant FRI-AFM-FRI transition with increasing temperature. These measurements also show that kinetic arrest band and supercooling band are anitcorrelated i.e regions which are kinetically arrested at higher temperature have lower supercooling temperature and vice versa.
Thermally quenched metastability in metal-insulator transitions via elemental substitution
The University of Tokyo（东京大学）；National Institute of Advanced Industrial Science and Technology（产业技术综合研究所）；Graduate School of Engineering and Science, Shibaura Institute of Technology（芝浦工业大学研究生院理工学研究科）；RIKEN Center for Emergent Matter Science（理化学研究所新兴物质科学研究中心）；University of Tsukuba（筑波大学）；Institute of Science Tokyo（东京科学大学）；National Institute for Materials Science（国立材料研究所）
Frustration induced inversion of magnetocaloric effect and enhanced cooling power in substituted Pyrochlore Iridates
我们研究了局部3d Cr 3+磁矩部分取代5d Ir 4+位置对Y2 Ir 2 O 7（YIO）烧绿石铱酸盐磁热性能的影响。我们发现，Y2 Ir 2-xCrxO 7（YICO）发生团簇玻璃化转变，可能是由于RKKY一样的本地化的Cr 3+时刻占据烧绿石网络中的随机站点之间的相互作用，介导的5d Ir传导电子。铁磁团簇和反铁磁团簇的共存导致了常规磁热效应和逆磁热效应。我们观察到显着增强传统以及逆MCE与替代。虽然传统的MCE和反MCE在取代的铱酸盐的值不大，效果跨越一个巨大的工作温度窗口，从而导致数量级的增强冷却功率，该值是可比的标准磁热材料。
Doping-induced redistribution of magnetic spectral weight in substituted hexaborides Ce$_{1-x}$La$_x$B$_6$ and Ce$_{1-x}$Nd$_x$B$_6$
利用中子漫散射研究了掺杂对Ce B $_6$在一系列Ce $_{1-x}R_x$ B $_6$（$R$ = La，Nd）取代样品上电子结构的影响.我们观察到整个布里渊区的磁谱权重的重新分配，我们与修改后的载流子浓度相关的费米表面嵌套特性的变化。特别是，在布里渊区的角落（$R$点），这符合难以捉摸的反铁四极（AFQ）的传播矢量CEB $_6$秩序的强扩散峰，迅速抑制La和Nd掺杂，像AFQ秩序本身。相应的光谱权重被转移到$X(00\frac{1}{2})$点，最终稳定在该波矢量在富钕侧的相图的长程AFM秩序。在中间Nd浓度下，在$X$点周围观察到具有多个局部强度最大值的宽扩散峰，证明产生多个有序相的巡回挫折，其中Ce $_{1-x}$ Nd $_x$ B $_6$是已知的。然而，在相图的富镧侧，磁矩的稀释阻止了类似的$(00\frac{1}{2})$型顺序的形成，尽管存在嵌套。我们的研究结果表明，如何扩散中子散射可以用来探测嵌套矢量在复杂的f-电子系统直接，而不参考单粒子的能带结构，并强调费米表面几何形状的作用，在稳定稀土六硼化物的磁秩序。
Evolution of a metastable phase with a magnetic phase coexistence phenomenon and its unusual sensitivity to magnetic field cycling in the alloys Tb5-xLuxSi3 (x <= 0.7)
Emergent magnetism, heavy electrons and pressure-induced reentrant superconductivity in the iron substituted 4d transition-metal sulfides
Zhejiang University of Technology（浙江工业大学）；Fudan University（复旦大学）；Qufu Normal University（曲阜师范大学）；Nanjing University of Posts and Telecommunications（南京邮电大学）；Suzhou University of Technology（苏州科技大学）；Hangzhou Dianzi University（杭州电子科技大学）；National Taiwan Normal University（台湾师范大学）；Academia Sinica（中央研究院）；Zhejiang University（浙江大学）；Ningbo University（宁波大学）；Hangzhou Normal University（杭州师范大学）；Shanghai Jiao Tong University（上海交通大学）
Room-temperature multistage metastability in a moiré superstructure
Tsung-Dao Lee Institute, School of Physics and Astronomy, Shanghai Jiao Tong University（上海交大李政道理论与计算科学中心，物理与天文学院）；Massachusetts Institute of Technology（麻省理工学院）；Stanford University（斯坦福大学）；Peking University（北京大学）；Beijing Academy of Quantum Information Sciences（北京量子信息科学研究院）；Tianjin University of Technology（天津理工大学）
Field-induced magnetic phase transitions and memory effect in bilayer ruthenate Ca$_3$Ru$_2$O$_7$ with Fe substitution
双层复合材料Ca $_3$（Ru $_{1-x}$ Fe $_x$）$_2$ O $_7$（$x$ = 0.05）具有由Dzyaloshinskii-Moriya相互作用驱动的非公度磁孤子晶格.本文通过单晶中子衍射和磁输运测量，研究了该体系中复杂的场致磁相变和记忆效应。我们观察到一阶的inexualate到公度的磁性转变时，施加磁场沿和垂直于传播轴的无公度自旋结构。此外，我们还发现降低磁场后形成的亚稳态依赖于温度和外加磁场的方向。我们认为，所观察到的场致亚稳态可能是由于在低温下的淬火动力学。
Comment on "Tuning low-energy scales in YbRh$_2$Si$_2$ by non-isoelectronic substitution and pressure"
在参考文献1中，Schubert等人[Phys. Rev. Research 1，032004（2019）]报告了Fe和Ni取代的YbRh $_2$ Si $_2$的等温磁阻测量结果，基于此，他们对原始YbRh $_2$ Si $_2$的磁场诱导量子临界点（QCP）的Kondo破坏描述提出了质疑。在此，我们提出三点。首先，如Paschen等人和Friedemann等人对原始YbRh $_2$ Si $_2$的研究所示，等温交叉场和单场霍尔效应测量是必要的，以确定费米表面在该QCP上的演变。由于Schubert等人没有进行这样的测量，因此他们对Fe和Ni取代的YbRh $_2$ Si $_2$的结果不能用于评估近藤破坏图对取代或原始YbRh $_2$ Si $_2$的有效性。第二，当参考Friedemann等人关于YbRh $_2$ Si $_2$的等温交叉的数据时，他们没有认识到交叉宽度的含义，交叉宽度由半峰全宽（FWHM）量化，在温度上是线性的，具有零偏移，在温度上大约$1.5$几十年，从30 mK到1 K。最后，在要求Friedemann等人的霍尔交叉FWHM数据与上述$T$线性相关性的偏差时，他们忽略了这些测量的误差条，并丢弃了一些数据点。因此，Schubert等人的主张没有数据支持，既没有以前发表的数据，也没有新的数据（参考文献1）。因此，它们不能使YbRh $_2$ Si…
Emergence of weak pyrochlore phase and signature of field induced spin ice ground state in Dy$_{2-x}$La$_{x}$Zr$_{2}$O$_{7}$; x = 0, 0.15, 0.3
烧绿石氧化物Dy $_{2}$ Ti $_{2}$ O $_{7}$和Ho $_{2}$ Ti $_{2}$ O $_{7}$是研究得很好的自旋冰体系，并显示出磁共振激发的证据。与这些不同，Dy $_{2}$ Zr $_{2}$ O $_{7}$被报道以扭曲的萤石结构结晶。本文研究了La取代Dy $_{2}$ Zr $_{2}$ O $_{7}$的磁性和热容量。我们的研究结果表明，在Dy $_{2}$ Zr $_{2}$ O $_{7}$中不存在自旋冰态，但在T $\approx$ 10 K附近出现了磁场诱导的自旋冻结，这与Dy $_{2}$ Ti $_{2}$ O $_{7}$相似。Dy $_{2}$ Zr $_{2}$ O $_{7}$的磁热容量显示出峰值位置从零磁场中的1.2 K向磁场中的更高温度的移动，并且相应地磁熵减小。在5 kOe场下，低温磁熵为Rln ~ 2-（1/2）Rln（3/2），与自旋冰态相同。用非磁性的等价La $^{3+}$取代Dy $^{3+}$，可使结构由高度无序的萤石相逐渐转变为弱有序的烧绿石相。La $^{3+}$取代的化合物在较低的磁场下表现出自旋冻结，而在磁场作用下自旋冻结进一步加强。结果表明，Dy $_{2}$ Zr $_{2}$ O $_{7}$中的自旋冰态可以通过降低自旋动力学或通过适当的取代强化烧绿石相来稳定.
Cu Nuclear Quadrupole Resonance Study of La_{2-x}Sr_xCu_{1-y}Zn_yO_4 (x=0.10, 0.15 and 0.20): Zn-induced Wipeout Effect near the Magnetic and Electric Instability