Sr$_{2}$IrO$_{4}$ with strong spin-orbit coupling (SOC) and Hubbard repulsion (U) hosts Mott insulating states. The similar crystal structure, magnetic and electronic properties, particularly the $d$-wave gap observed in Sr$_{2}$IrO$_{4}$ enhanced the analogies to cuprate high-$T_{c}$ superconductor, La$_{2}$CuO$_{4}$. The incomplete analogy was due to the lack of broken inversion symmetry phases observed in Sr$_{2}$IrO$_{4}$. Here, under high pressure and high temperature conditions, we report a non-centrosymmetric Sr$_{2}$IrO$_{4}$. The crystal structure and its noncentrosymmetric character were determined by single crystal X-ray diffraction and high-resolution scanning transmission electron microscopy (HR-STEM). The magnetic characterization confirms the Ir$^{4+}$ with $S$ = 1/2 at low temperature in Sr$_{2}$IrO$_{4}$ with magnetic ordering occurred at around 86 K, where a larger moment is observed than the ambient pressure Sr$_{2}$IrO$_{4}$. Moreover, the resistivity measurement shows three-dimensional Mott variable-range hopping existed in the system. This non-centrosymmetric Sr$_{2}$IrO$_{4}$ phase appears to be a unique material to offer further understanding of high-$T_{c}$ superconductivity.
Synchrotron x-ray diffraction and DFT study of non-centrosymmetric EuRhGe3 under high pressure
Institute of Physics（物理研究所）；Université Paris-Saclay, CNRS, Laboratoire de Physique des Solides（巴黎萨克雷大学、法国国家科学研究中心、固体物理实验室）；Department of Physics, Faculty of Science, University of Zagreb（萨格勒布大学理学院物理系）；Institute of Low Temperature and Structure Research, Polish Academy of Sciences（波兰科学院低温与结构研究所）；Synchrotron SOLEIL（SOLEIL同步辐射中心）；Department of Earth Sciences, Department of Physics and Astronomy, University of Western Ontario（韦斯顿安大略大学地球科学系、物理与天文学系）
Hexagonal LuFe2O4 is a promising charge-order (CO) driven multiferroic material with high charge and spin ordering temperatures. The coexisting charge and spin orders on Fe3+/Fe2+ sites result in novel magnetoelectric behaviors, but the coupling mechanism between the charge and spin orders remains elusive. Here, by tuning external pressure, we reveal three correlated spin-charge ordered phases in LuFe2O4: i) a centrosymmetric incommensurate three-dimensional CO with ferrimagnetism, ii) a non-centrosymmetric incommensurate quasi-two-dimensional CO with ferrimagnetism, and iii) a centrosymmetric…
We report synthesis of non-centrosymmetric BiPd single crystal by self flux method. The BiPd single crystal is crystallized in monoclinic structure with the P21 space group. Detailed SEM (Scanning Electron Microscopy) results show that the crystals are formed in slab like morphology with homogenous distribution of Bi and Pd. The magnetic susceptibility measurement confirmed that the BiPd compound is superconducting below 4K. Further, BiPd exhibits weak ferromagnetism near the superconducting transition temperature in isothermal magnetization (MH) measurements. The temperature dependent electri…
Enhancement of Superconducting Transition Temperature due to the strong Antiferromagnetic Spin Fluctuations in Non-centrosymmetric Heavy-fermion Superconductor CeIrSi3 :A 29Si-NMR Study under Pressure
Honeycomb iridates such as $γ$-Li$_2$IrO$_3$ are argued to realize Kitaev spin-anisotropic magnetic exchange, along with Heisenberg and possibly other couplings. While systems with pure Kitaev interactions are candidates to realize a quantum spin liquid ground state, in $γ$-Li$_2$IrO$_3$ it has been shown that the balance of magnetic interactions leads to the incommensurate spiral spin order at ambient pressure below 38 K. We study the fragility of this state in single crystals of $γ$-Li$_2$IrO$_3$ using resonant x-ray scattering (RXS) under applied hydrostatic pressures of up to 3.0 GPa. RXS …
Protected by the interplay of on-site Coulomb interactions and spin-orbit coupling, Sr$_2$IrO$_4$ at high pressure is a rare example of a Mott insulator with a paramagnetic ground state. Here, using optical Raman scattering, we measure both the phonon and magnon evolution in Sr$_2$IrO$_4$ under pressure, and identify three different magnetically-ordered phases, culminating in a spin-disordered state beyond 18 GPa. A strong first-order structural phase transition drives the magnetic evolution at $\sim$10 GPa with reduced structural anisotropy in the IrO$_6$ cages, leading to increasingly isotro…
The Kitaev model of spin-1/2 on a honeycomb lattice supports degenerate topological ground states and may be useful in topological quantum computation. Na$_{2}$IrO$_{3}$ with honeycomb lattice of Ir ions have been extensively studied as candidates for the realization of the this model, due to the effective $J_{\text{eff}}=1/2$ low-energy excitations produced by spin-orbit and crystal-field effect. As the eventual realization of Kitaev model has remained evasive, it is highly desirable and challenging to tune the candidate materials toward such end. It is well known external pressure often lead…
We studied the effect of external pressure on the electrodynamic properties of $α$-Li$_2$IrO$_3$ single crystals in the frequency range of the phonon modes and the Ir $d$-$d$ transitions. The abrupt hardening of several phonon modes under pressure supports the onset of the dimerized phase at the critical pressure $P_c$=3.8 GPa. With increasing pressure an overall decrease in spectral weight of the Ir $d$-$d$ transitions is found up to $P_c$. Above $P_c$, the local (on-site) $d$-$d$ excitations gain spectral weight with increasing pressure, which hints at a pressure-induced increase in the octa…
Effect of iron-doping on spin-state transition and ferromagnetism in Pr$_{0.5}$Ca$_{0.5}$CoO$_{3-δ}$ cobalt oxides
对多晶Pr $_{0.5}$ Ca $_{0.5}$ Co $_{1-x}$ Fe $_{x}$ O $_{3-δ}$（$x$ = 0、0.05、0.10和0.15）样品进行电阻率和直流磁化测量。所制备的样品表现出铁磁（FM）转变，转变温度随着铁掺杂量的增加而增加。高氧压退火诱导了\emph{iron-free}样品中Co离子的自旋态转变，并且这种转变随着退火氧压的增加而增强，而高氧压退火抑制了铁磁有序。与\emph{iron-free}样品的情况相反，\emph{iron-doped}样品在高氧压下退火没有引起自旋态转变，并且铁磁转变温度几乎与退火过程无关。\emph{iron-free}样品在高氧压下退火后自旋态转变的增强应归因于晶胞体积的减小。Fe掺杂对自旋态跃迁的抑制与晶胞体积的增大以及Fe-O键比Co-O键强有关。铁掺杂对铁磁性的增强可能源于Fe $^{3+}$和Co $^{4+}$之间通过氧的铁磁交换相互作用（Fe $^{3+}$ -O-Co $^{4+}$）。
A skyrmion crystal has internal degrees of freedom in terms of vorticity and helicity, which gives rise to fascinating types of skyrmion phases (Néel, Bloch, and anti-skyrmion). We show how the degeneracy lifting in tetragonal skyrmion crystals occurs in centrosymmetric itinerant magnets by focusing on microscopic interactions through the Fermi surface instability. We demonstrate that four types of skyrmion crystals can be realized according to the signs of the anisotropic Ruderman-Kittel-Kasuya-Yosida interaction, which are sensitive to band structures, electron fillings, atomic orbitals, and…
We have studied the pressure effect on electronic structures and magnetic orders of ternary iron selenide K$_{0.8}$Fe$_{1.6}$Se$_2$ by the first-principles electronic structure calculations. At low pressure, the compound is in the blocked checkerboard antiferromagnetic (AFM) semiconducting phase, as observed by the neutron scatting measurements. Applying pressure induces two phase transitions, first from the blocked checkerboard AFM semiconducting phase to a collinear AFM metallic phase around 12 GPa, and then to a non-magnetic metallic phase around 25 GPa, respectively. Our results help to cl…
We predict that a non-centrosymmetric material NaSnBi locates in a three-dimensional non-trivial topological phase under ambient pressure based on first-principle calculations. By deriving the effective model around $Γ$ point, we find that the topological phase transition is driven by a Rashba spin-orbital coupling through an odd number of pairs of band touch because of a small anisotropic gap caused by quintic dispersion terms. In contrast to conventional topological insulators, the spin texture of surface Dirac cone is right-handed and the surface states are strikingly different for differen…
We present magnetization measurements on polycrystalline $β$-Li$_2$IrO$_3$ under hydrostatic pressures up to 3~GPa and construct the temperature-pressure phase diagram of this material. Our data confirm that magnetic order breaks down in a first-order phase transition at $p_{\rm{c}}$ $\approx$ 1.4~GPa and additionally reveal a step-like feature -- magnetic signature of structural dimerization -- that appears at $p_{\rm{c}}$ and shifts to higher temperatures upon further compression. Following the structural study by L. S. I. Veiga et al. [Phys. Rev. B 100, 064104 (2019)], we suggest that a par…
The non-centrosymmetric Weyl semimetal candidate, MoTe$_2$ was investigated through neutron diffraction and transport measurements at pressures up to 1.5 GPa and at temperatures down to 40 mK. Centrosymmetric and non-centrosymmetric structural phases were found to coexist in the superconducting state. Density Functional Theory (DFT) calculations reveal that the strength of the electron-phonon coupling is similar for both crystal structures. Furthermore, it was found that by controlling non-hydrostatic components of stress, it is possible to mechanically control the ground state crystal structu…
Temperature-pressure phase diagram of the Kitaev hyperhoneycomb iridate $β$-Li$_2$IrO$_3$ is explored using magnetization, thermal expansion, magnetostriction, and muon spin rotation ($μ$SR) measurements, as well as single-crystal x-ray diffraction under pressure and ab initio calculations. The Neel temperature of $β$-Li$_2$IrO$_3$ increases with the slope of 0.9 K/GPa upon initial compression, but the reduction in the polarization field $H_c$ reflects a growing instability of the incommensurate order. At 1.4 GPa, the ordered state breaks down upon a first-order transition giving way to a new …
We report a polarized Raman scattering study of the lattice dynamics of $β$-Li$_2$IrO$_3$ under hydrostatic pressures up to 7.62 GPa. At ambient pressure, $β$-Li$_2$IrO$_3$ exhibits the hyperhoneycomb crystal structure and a magnetically ordered state of spin-orbit entangled Jeff = 1/2 moments that is strongly influenced by bond-directional (Kitaev) exchange interactions. At a critical pressure of ~ 4.1 GPa, the phonon spectrum changes abruptly consistent with the reported structural transition into a monoclinic, dimerized phase. A comparison to the phonon spectra obtained from density functio…
We study the effect of isoelectronic doping and external pressure in tuning the ground state of the honeycomb iridate Na$_2$IrO$_3$ by combining optical spectroscopy with synchrotron x-ray diffraction measurements on single crystals. The obtained optical conductivity of Na$_2$IrO$_3$ is discussed in terms of a Mott insulating picture versus the formation of quasimolecular orbitals and in terms of Kitaev-interactions. With increasing Li content $x$, (Na$_{1-x}$Li$_x$)$_2$IrO$_3$ moves deeper into the Mott insulating regime and there are indications that up to a doping level of 24\% the compound…
The CeFeAsO and CeFePO iron pnictide compounds were studied via electrical transport measurements under high-pressure. In CeFeAsO polycrystals, the magnetic phases involving the Fe and Ce ions coexist up to 15 GPa, with no signs of pressure-induced superconductivity up to 50 GPa. For the CeFePO single crystals, pressure stabilizes the Kondo screening of the Ce 4f-electron magnetic moments.
We present a study of the alloying series of the non-centrosymmetric $f$-electron intermetallic CePt$_3$B$_{1-x}$Si$_x$ by means of muon spin rotation and relaxation measurements. In addition, we include a high pressure magnetization investigation of the stoichiometric parent compound CePt$_3$B. From our data we establish the nature of the magnetic ground state properties of the series, derive the ordered magnetic moment as function of stoichiometry and gain insight into the evolution of the symmetry of the ordered magnetic state with $x$. We thus can verify the notion that the behavior of the…
In this chapter we discuss the physical properties of a particular family of non-centrosymmetric superconductors belonging to the class heavy-fermion compounds. This group includes the ferromagnet UIr and the antiferromagnets CeRhSi3, CeIrSi3, CeCoGe3, CeIrGe3 and CePt3Si, of which all but CePt3Si become superconducting only under pressure. Each of these superconductors has intriguing and interesting properties. We first analyze CePt3Si, then review CeRhSi3, CeIrSi3, CeCoGe3 and CeIrGe3, which are very similar to each other in their magnetic and electrical properties, and finally discuss UIr. …
$\mathrm{Cu_2IrO_3}$ is among the newest layered honeycomb iridates and a promising candidate to harbor a Kitaev quantum spin liquid state. Here, we investigate the pressure and temperature dependence of its structure through a combination of powder x-ray diffraction and x-ray absorption fine structure measurements, as well as $ab$-$initio$ evolutionary structure search. At ambient pressure, we revise the previously proposed $C2/c$ solution with a related but notably more stable $P2_1/c$ structure. Pressures below 8 GPa drive the formation of Ir-Ir dimers at both ambient and low temperatures, …
We study theoretically the variation of the magnetic and the structural transition temperatures of the iron arsenide superconductors with external uniaxial stress. We show that the increase of the transition temperatures reported in recent experiments is compatible with a simple magneto-elastic model in which the physical origin of this variation is linked to the fact that antiferromagnetic bonds are longer than the ferromagnetic ones in the magnetic phase. We make predictions which can be verified in order to test the relevance of this model.
We present magnetization measurements carried out on polycrystalline and single-crystalline samples of $α$-Li$_2$IrO$_3$ under hydrostatic pressures up to 2 GPa and establish the temperature-pressure phase diagram of this material. The Néel temperature ($T_{\rm{N}}$) of $α$-Li$_2$IrO$_3$ is slightly enhanced upon compression with $dT_{\rm{N}}/dp$ = 1.5 K/GPa. Above 1.2 GPa, $α$-Li$_2$IrO$_3$ undergoes a first-order phase transition toward a nonmagnetic dimerized phase, with no traces of the magnetic phase observed above 1.8 GPa at low temperatures. The critical pressure of the structural dimer…
The low-temperature magnetic properties of \tcr{polycrystalline} Na$_2$IrO$_3$, a candidate material for the realization of a quantum spin-liquid state, were investigated by means of muon-spin relaxation and nuclear magnetic resonance methods under chemical and hydrostatic pressure. The Li-for-Na chemical substitution promotes an inhomogeneous magnetic order, whereas hydrostatic pressure (up to 3.9\,GPa) results in an enhancement of the ordering temperature $T_\mathrm{N}$. In the first case, the inhomogeneous magnetic order suggests either short- or long-range correlations of broadly distribut…
Iron-based superconductors are well-known for their intriguing phase diagrams, which manifest a complex interplay of electronic, magnetic and structural degrees of freedom. Among the phase transitions observed are superconducting, magnetic, and several types of structural transitions, including a tetragonal-to-orthorhombic and a collapsed-tetragonal transition. In particular, the widely-observed tetragonal-to-orthorhombic transition is believed to be a result of an electronic order that is coupled to the crystalline lattice and is, thus, referred to as nematic transition. Nematicity is therefo…
We report the synthesis of a new quasi one-dimensional (1D) iron selenide. Ba9Fe3Se15 was synthesized at high temperature and high pressure of 5.5 GPa and systematically studied via structural, magnetic and transport measurements at ambient and at high-pressures. Ba9Fe3Se15 crystallizes in a monoclinic structure and consists of face-sharing FeSe6 octahedral chains along the c axis. At ambient pressure it exhibits an insulating behavior with a band gap ~460 meV and undergoes a ferrimagnet-like phase transition at 14 K. Under high pressure, a complete metallization occurs at ~29 GPa, which is ac…
The effect of compression on the magnetic ground state of Sr$_2$IrO$_4$ is studied with x-ray resonant techniques in the diamond anvil cell. The weak interlayer exchange coupling between square-planar 2D IrO$_2$ layers is readily modified upon compression, with a crossover between magnetic structures around 7 GPa mimicking the effect of an applied magnetic field at ambient pressure. Higher pressures drive an order-disorder magnetic phase transition with no magnetic order detected above 17-20 GPa. The persistence of strong exchange interactions between $\mathrm{J_{eff}}=1/2$ magnetic moments wi…
The New High-entropy Compound RhMnFeCoGe4 with Cubic Non-centrosymmetric B20 Structure
Vereshchagin Institute for High Pressure Physics, RAS（俄罗斯科学院维列夏金高压物理研究所）；Mikheev Institute of Metal Physics, Russian Academy of Sciences（俄罗斯科学院米凯耶夫金属物理研究所）
In the iron-pnictide material CeFeAsO not only the Fe moments, but also the local 4f moments of the Ce order antiferromagnetically at low temperatures. We elucidate on the peculiar role of the Ce on the emergence of superconductivity. While application of pressure suppresses the iron SDW ordering temperature monotonously up to 4 GPa, the Ce-4f magnetism is stabilized, until both types of magnetic orders disappear abruptly and a narrow SC dome develops. With further increasing pressure characteristics of a Kondo-lattice system become more and more apparent in the electrical resistivity. This su…
The magnetic properties of iron-based superconductors $A$Fe$_2$As$_2$ ($A=$K, Cs, and Rb), which are characterized by the V-shaped dependence of the critical temperature ($T_{\rm c}$) on pressure ($P$) were studied by means of the muon spin rotation/relaxation technique. In all three systems studied the magnetism was found to appear for pressures slightly below the critical one ($P_{\rm c}$), i.e. at pressure where $T_{\rm c}(P)$ changes the slope. Rather than competing, magnetism and superconductivity in $A$Fe$_2$As$_2$ are coexisting at $P\gtrsim P_{\rm c}$ pressure region. Our results suppo…
Single-crystal x-ray diffraction studies with synchrotron radiation on the honeycomb iridate $α$-Li$_{2}$IrO$_{3}$ reveal a pressure-induced structural phase transition with symmetry lowering from monoclinic to triclinic at a critical pressure of $P_{c}$ = 3.8 GPa. According to the evolution of the lattice parameters with pressure, the transition mainly affects the $ab$ plane and thereby the Ir hexagon network, leading to the formation of Ir--Ir dimers. These observations are independently predicted and corroborated by our \textit{ab initio} density functional theory calculations where we find…
Electrical-resistivity and magnetic-susceptibility measurements under hydrostatic pressure up to p = 2.75 GPa have been performed on superconducting LiFeP. A broad superconducting (SC) region exists in the temperature - pressure (T-p) phase diagram. No indications for a spin-density-wave transition have been found, but an enhanced resistivity coefficient at low pressures hints at the presence of magnetic fluctuations. Our results show that the superconducting state in LiFeP is more robust than in the isostructural and isoelectronic LiFeAs. We suggest that this finding is related to the nearly …
Hyperhoneycomb iridate $β$-Li$_2$IrO$_3$ is a three-dimensional analogue of two-dimensional honeycomb iridates, such as $α$-Li$_2$IrO$_3$, which recently appeared as another playground for the physics of Kitaev-type spin liquid. $β$-Li$_2$IrO$_3$ shows a non-collinear spiral ordering of spin-orbital-entangled $J_{\rm eff}$ = 1/2 moments at low temperature, which is known to be suppressed under a pressure of $\sim$2 GPa. With further increase of pressure, a structural transition is observed at $P_{\rm S}$ $\sim$ 4 GPa at room temperature. Using the neutron powder diffraction technique, the crys…
Magnetotransport Properties of Iron-Based Ladder Compounds BaFe2S3 and BaFe2Se3 under High Pressure
Graduate School of Advanced Science and Engineering, Hiroshima University（广岛大学高级科学与工程学院）；International Institute for Sustainability with Knotted Chiral Meta Matter (WPI-SKCM2), Hiroshima University（广岛大学螺旋手性超材料可持续性国际研究所）；Department of Physics, Graduate School of Science, Tohoku University（东北大学理学院物理系）
We present a high-pressure NMR study of the overdoped iron pnictide superconductor NaFe$_{0.94}$Co$_{0.06}$As. The low-energy antiferromagnetic spin fluctuations in the normal state, manifest as the Curie-Weiss upturn in the spin-lattice relaxation rate $1/^{75}T_1T$, first increase strongly with pressure but fall again at $P > P_{\rm opt} =$ 2.2 GPa. Neither long-ranged magnetic order nor a structural phase transition is encountered up to 2.5 GPa. The superconducting transition temperature $T_c$ shows a pressure-dependence identical to the spin fluctuations. Our observations demonstrate that …
A pressure-induced collapse of magnetic ordering in $β$-Li$_2$IrO$_3$ at $P_m\sim1.5- 2$ GPa has previously been interpreted as evidence for possible emergence of spin liquid states in this hyperhoneycomb iridate, raising prospects for experimental realizations of the Kitaev model. Based on structural data obtained at \emph{room temperature}, this magnetic transition is believed to originate in small lattice perturbations that preserve crystal symmetry, and related changes in bond-directional anisotropic exchange interactions. Here we report on the evolution of the crystal structure of $β$-Li$…
The recent discovery of superconductivity in BaFe$_2$S$_3$ [Takahashi {\it et al.}, Nat. Mater. {\bf 14}, 1008 (2015)] has stimulated considerable interest in 123-type iron chalcogenides. This material is the first reported iron-based two-leg ladder superconductor, as opposed to the prevailing two-dimensional layered structures of the iron superconductors family. Once the hydrostatic pressure exceeds $11$ GPa, BaFe$_2$S$_3$ changes from a semiconductor to a superconductor below $24$~K. Although previous calculations correctly explained its ground state magnetic state and electronic structure, …
The crystal lattice of Sr$_2$IrO$_4$ is investigated with synchrotron X-ray powder diffraction under hydrostatic pressures up to $P=43$ GPa and temperatures down to $20$ K. The tetragonal unit cell is maintained over the whole investigated pressure range, within our resolution and sensitivity. The $c$-axis compressibility $κ_c(P,T) \equiv -({1} / {c}) ({d c} / {d P})$ presents an anomaly with pressure at $P_1=17$ GPa at fixed $T=20$ K that is not observed at $T=300$ K, whereas $κ_a(P,T)$ is nearly temperature-independent and shows a linear behavior with $P$. The anomaly in $κ_c(P,T)$ is associ…
The layered honeycomb lattice iridate Cu$_2$IrO$_3$ is the closest realization of the Kitaev quantum spin liquid, primarily due to the enhanced interlayer separation and nearly ideal honeycomb lattice. We report pressure-induced structural evolution of Cu$_2$IrO$_3$ by powder x-ray diffraction (PXRD) up to $\sim$17 GPa and Raman scattering measurements up to $\sim$25 GPa. A structural phase transition (monoclinic $C2/c \: \rightarrow$ triclinic $P\bar{1}$) is observed with a broad mixed phase pressure range ($\sim$4 to 15 GPa). The triclinic phase consists of heavily distorted honeycomb lattic…
Hydrogen (H)-doped LaFeAsO is a prototypical iron-based superconductor. However, its phase diagram extends beyond the standard framework, where a superconducting (SC) phase follows an antiferromagnetic (AF) phase upon carrier doping; instead, the SC phase is sandwiched between two AF phases appearing in lightly and heavily H-doped regimes. We performed nuclear magnetic resonance (NMR) measurements under pressure, focusing on the second AF phase in the heavily H-doped regime. The second AF phase is strongly suppressed when a pressure of 3.0 GPa is applied, and apparently shifts to a highly H-do…
In a magnetically driven electronic nematic state, an externally applied uniaxial strain rounds the nematic transition and increases the magnetic transition temperature. We study both effects in a simple classical model of the iron-pnictides expressed in terms of local SO(N) spins (with N = 3) which we solve to leading order in 1=N. The magnetic transition temperature is shown to increase linearly in response to an external strain while a sharp crossover, which is a remnant of the nematic transition, can only be identified for extremely small strain. We show that these results can reasonably a…
The electrical resistivity rho of the iron-arsenide superconductor Ba1-xKxFe2As2 was measured in applied pressures up to 2.6 GPa for four underdoped samples, with x = 0.16, 0.18, 0.19 and 0.21. The antiferromagnetic ordering temperature T_N, detected as a sharp anomaly in rho(T), decreases linearly with pressure. At pressures above around 1.0 GPa, a second sharp anomaly is detected at a lower temperature T_0, which rises with pressure. We attribute this second anomaly to the onset of a phase that causes a reconstruction of the Fermi surface. This new phase expands with increasing x and it comp…
We report a sudden reversal in the pressure dependence of Tc in the iron-based superconductor RbFe2As2, at a critical pressure Pc = 11 kbar. Combined with our prior results on KFe2As2 and CsFe2As2, we find a universal V-shaped phase diagram for Tc vs P in these fully hole-doped 122 materials, when measured relative to the critical point (Pc, Tc). From measurements of the upper critical field Hc2(T) under pressure in KFe2As2 and RbFe2As2, we observe the same two-fold jump in (1/Tc)(-dHc2/dT) across Pc, compelling evidence for a sudden change in the structure of the superconducting gap. We argue…
Properties of iron oxides at the extreme conditions are of essential importance in condensed matter physics and Geophysics. The recent discovery of a new type of iron oxide, Fe4O5, at high pressure and high temperature of Earth's deep interior attracts great interests. In this paper, we report the electronic structure and the magnetic properties of Fe4O5 predicted by the density functional theory plus dynamic mean field theory (DFT+DMFT) approach. We find that Fe4O5 stays metallic from ambient pressure to high pressure. The magnetic moments of iron atoms at the three different crystallographic…
Here, we investigated the interrelationship between pressure and correlation in the LaFeAsO compound by the density functional theory method combined with the dynamical mean field theory (DFT+DMFT) method. The spectral function and the occupation number (ON) of Fe-3d orbitals at different pressures were extracted from the calculations, and the importance of the role of correlation in superconductivity in iron-based compounds was indicated. The measured ON of Fe-3d orbitals demonstrated charge transfer between them and also the crucial role of the Fe-3dxy (xy) orbital in superconductivity in th…