准一维Cr基材料的磁不稳定性
Magnetic instabilities in quasi-one-dimensional Cr-based material
摘要：
在5 ~ 300 K温度范围内，用直流磁化强度测量方法研究了K2 Cr 3As 3样品的磁响应与磁场（H）的关系。观察磁滞回线m（H），在高于60 K的温度下推断样品的抗磁性行为，而在较低温度下样品显示出与亚铁磁性的存在相容的磁滞回线。此外，在-1000 Oe < H < 1000 Oe的范围内的某些磁场中观察到几个尖峰状磁化跳跃，无论是正的还是负的，与所考虑的温度无关。研究了不同温度下磁化跳变的场位置，其分布可用洛伦兹曲线描述。
英文摘要：
The magnetic response of a K2Cr3As3 sample has been studied by means of dc magnetization measurements as a function of magnetic field (H) at different temperatures ranging from 5 K up to 300 K. Looking at the magnetic hysteresis loops m(H), a diamagnetic behavior of the sample has been inferred at temperatures higher than 60 K, whereas at lower temperatures the sample shows a hysteresis loop compatible with the presence of ferrimagnetism. Moreover, several spike-like magnetization jumps, both positive and negative, have been observed at certain fields in the range -1000 Oe < H < 1000 Oe, regardless of the temperature considered. The field position of the magnetization jumps has been studied at different temperatures, and their distribution can be described by a Lorentzian curve.
机构、总结、中文摘要均由AI分析而来，可能存在错误，请以论文正文为准。