Optical spectroscopy was used to study the electrodynamics and hidden transport properties of a BaFe$_{1.91}$Ni$_{0.09}$As$_{2}$ thin superconducting film. We analyzed the normal state data using a Drude-Lorentz model with two Drude components: one narrow ($D_1$) and another broad one ($D_2$). In the superconducting state, two gaps with $2Δ_{0}^{(2)}/k_BT_c=1.9$--2.0 and $2Δ_{0}^{(1)}/k_BT_c=4.0$--4.3 are formed from the narrow component $D_1$ while the broad component $D_2$ remains ungapped. The calculated total DC resistivity of the film and the low-temperature scattering rate for the narrow Drude component show a hidden Fermi-liquid behavior. The change of total electron-boson coupling ($λ_{tot}$) and representative energy ($Ω_{0}$) in the normal state with respect to the superconducting state is typical of other iron-based materials as well as high-temperature superconducting (HTSC) cuprates.
We report resistivity, Hall coefficient, current-voltage characteristics, and magneto-optical imaging measurements of epitaxial Co-doped BaFe_{2}As_{2} thin films deposited on MgO(001) substrate. The Hall resistivity of the films has a substantial contribution arising from anomalous Hall effect of ferromagnetic components. The critical current density (J_{c}) of the films is ~2 MA/cm^{2} at low temperatures. Differential magneto-optical images of the remanent state give similar J_{c} values and also exhibit presence of extended defects in the film.
We report the growth of potassium-doped BaFe2As2 thin films, where the major charge carriers are holes, on Al2O3 (0001) and LaAlO3 (001) substrates by using an ex-situ pulsed laser deposition technique. The measured Tc's are 40 and 39 K for the films grown on Al2O3 and LaAlO3, respectively and diamagnetism indicates that the films have good bulk superconducting properties below 36 and 30 K, respectively. The X-ray diffraction patterns for both films indicated a preferred c-axis orientation, regardless of the substrate structures of LaAlO3 and Al2O3. The upper critical field at zero temperature…
Epitaxial growth of Fe-based superconductors such as Co-doped SrFe$_2$As$_2$ (SrFe$_2$As$_2$:Co) was reported recently, but has still insufficient properties for device application because they have rough surfaces and are decomposed by reactions with water vapor in an ambient atmosphere. This letter reports that epitaxial films of Co-doped BaFe$_2$As$_2$ grown at 700 oC show the onset superconducting transition tempearture of 20 K. The transition is sharper than those observed on the SrFe$_2$As$_2$:Co films, which would originate from their improved crystallinity. These films also have atomica…
A low and almost temperature independent resistance in the normal state and an anomalous peak effect within the normal-superconducting transition have been observed in BaFe$_{1.8}$Co$_{0.2}$As$_2$/Fe bilayers, prepared on IBAD-MgO/Y$_2$O$_3$ buffered technical substrates. A resistor network array sufficiently reproduces this effect, assuming an increase of the electrical conductance between tape and film with decreasing buffer layer thickness. Based on this model we evaluated the influence of this effect on the critical current density and successfully reconstructed the superconducting transit…
To investigate the transport properties of iron based superconductors, we prepared planar hybrid superconductor-normal metal-superconductor (SNS') thin film junctions with BaFe1.8Co0.2As2 as base electrode. As counter electrode we used a lead indium alloy, while the normal metal layer was formed by thin gold films. Temperature dependent measurements of the electrical conductivity were strongly influenced by the properties of the electrodes. We developed a junction structure that allows us to characterize the electrodes, too, including the behavior of their normal state resistance in order to c…
Here we report an optical investigation in the terahertz region of a 40 nm ultrathin BaFe$_{1.84}$Co$_{0.16}$As$_2$ superconducting film with superconducting transition temperature T$_c$ = 17.5 K. A detailed analysis of the combined reflectance and transmittance measurements showed that the optical properties of the superconducting system can be described in terms of a two-band, two-gap model. The zero temperature value of the large gap $Δ_B$, which seems to follow a BCS-like behavior, results to be $Δ_B$(0) = 17 cm$^{-1}$. For the small gap, for which $Δ_A$(0) = 8 cm$^{-1}$, the temperature d…
The temperature dependences of the plasma frequency, superfluid density and London penetration depth were determined from terahertz spectra of conductivity and dielectric permittivity of BaFe$_{1.91}$Ni$_{0.09}$As$_{2}$ film with critical temperature $T_c=19.6$~K. Part of experimental data were analyzed within a simple three-band Eliashberg model where the mechanism of superconducting coupling is mediated by antiferromagnetic spin fluctuations, whose characteristic energy $Ω_{0}$ scales with $T_{c}$ according to the empirical law $Ω_{0} = 4.65k_{B}T_{c}$, and with a total electron-boson coupli…
We investigated the complex conductivity spectrum of a Co-doped BaFe$_2$As$_2$ epitaxial thin film in the THz region. In the normal state, the complex conductivity shows a Drude-type frequency dependence, while in the superconducting state, the frequency dependence of the complex conductivity changes to that of a typical superconducting materials. We estimated the magnetic penetration depth at absolute zero to be 710 nm and the superconducting gap energy to be 2.8 meV, which is considered to be the superconducting gap opened at the electron-type Fermi surface near the M point. We succeeded in …
DC superconducting quantum interference devices (dc-SQUIDs) were fabricated in Co-doped BaFe2As2 epitaxial films on (La, Sr)(Al, Ta)O3 bicrystal substrates with 30deg misorientation angles. The 18 x 8 micro-meter^2 SQUID loop with an estimated inductance of 13 pH contained two 3 micro-meter wide grain boundary junctions. The voltage-flux characteristics clearly exhibited periodic modulations with deltaV = 1.4 micro-volt at 14 K, while the intrinsic flux noise of dc-SQUIDs was 7.8 x 10^-5 fai0/Hz^1/2 above 20 Hz. The rather high flux noise is mainly attributed to the small voltage modulation de…
Josephson junctions with iron pnictides open the way for fundamental experiments on superconductivity in these materials and their application in superconducting devices. Here, we present hybrid Josephson junctions with a BaFe_{1.8}Co_{0.2}As_2 thin film electrode, an Au barrier and a PbIn counter electrode. The junctions show RSJ-like current-voltage characteristics up to the critical temperature of the counter electrode of about 7.2K. The temperature dependence of the critical current, IC, does not show an Ambegaokar-Baratoff behavior. Well-pronounced Shapiro steps are observed at microwave …
Whether or not epitaxially grown superconducting films have the same bulk-like superconducting properties is an important concern. We report the structure and the electronic properties of epitaxially grown Ba(Fe1-xCox)2As2 films using scanning tunneling microscopy and scanning tunneling spectroscopy (STS). This film showed a different surface structure, (2sqrtx2sqrt2)R45 reconstruction, from those of as-cleaved surfaces from bulk crystals. The electronic structure of the grown film is different from that in bulk, and it is notable that the film exhibits the same superconducting transport prope…
We measured the THz reflectance properties of a high quality epitaxial thin film of the Fe-based superconductor BaFe$_{1.84}$Co$_{0.16}$As$_2$ with T$_c$=22.5 K. The film was grown by pulsed laser deposition on a DyScO$_3$ substrate with an epitaxial SrTiO$_3$ intermediate layer. The measured $R_S/R_N$ spectrum, i.e. the reflectivity ratio between the superconducting and normal state reflectance, provides clear evidence of a superconducting gap $Δ_A$ close to 15 cm$^{-1}$. A detailed data analysis shows that a two-band, two-gap model is absolutely necessary to obtain a good description of the …
The use of piezoelectric substrates enables a dynamic observation of strain dependent properties of functional materials. Based on studies with La1.85Sr0.15CuO4 we extended this approach to the iron arsenic superconductors represented by BaFe2-xCoxAs2 to investigate strain driven changes in detail. We demonstrate that epitaxial thin films can be prepared on (001)Pb(Mg1/3Nb2/3)0.72Ti0.28O3 substrates using pulsed laser deposition. The structural as well as the electric properties of the grown films were characterized in detail. A reversible shift of the superconducting transition of 0.44 K for …
Electron doping of a 122-type iron pnictide BaFe2As2 by substituting the Ba site with an aliovalent ion (indirect doping), which had been unsuccessful by conventional solid-state synthesis methods, was achieved by a non-equilibrium film growth process. The substitution with La was substantiated by a systematic shrinkage of the c-axis lattice parameter due to the smaller ionic radius of La3+ than that of Ba2+. A negative Hall coefficient indicated that the majority carriers were electrons, as is consistent with this aliovalent ion doping. The La substitution suppressed an antiferromagnetic tran…
We report on imaging of the nonuniform superconducting states in a Pb thin film bridge on top of a ferromagnetic BaFe_{12}O_{19} single crystal with a single straight domain wall along the center of the bridge by low-temperature scanning laser microscopy. We have visualized domain wall superconductivity (DWS) close to the critical temperature of Pb, when the Pb film above the domain wall acts as a superconducting path for the current. The evolution of the DWS signal with temperature and the external-field-driven transition from DWS to reverse domain superconductivity was visualized.
Highly textured NdFeAs(O,F) thin films have been grown on ion beam assisted deposition (IBAD)-MgO/Y2O3/Hastelloy substrates by molecular beam epitaxy. The oxypnictide coated conductors showed a superconducting transition temperature (Tc) of 43 K with a self-field critical current density (Jc) of 7.0 x 104 A/cm2 at 5 K, more than 20 times higher than powder-in-tube processed SmFeAs(O,F) wires. Albeit higher Tc as well as better crystalline quality than Co-doped BaFe2As2 coated conductors, in-field Jc of NdFeAs(O,F) was lower than that of Co-doped BaFe2As2. These results suggest that grain bound…
The iron-based superconductor Ba$_{1-x}$K$_x$Fe$_\text{2}$As$_\text{2}$ is emerging as a key material for high magnetic field applications owing to the recent developments in superconducting wires and bulk permanent magnets. Epitaxial thin films play important roles in investigating and artificially tuning physical properties; nevertheless, the synthesis of Ba$_{1-x}$K$_x$Fe$_2$As$_2$ epitaxial thin films remained challenging because of the high volatility of K. Herein, we report the successful growth of epitaxial Ba$_{1-x}$K$_x$Fe$_\text{2}$As$_\text{2}$ thin films by molecular-beam epitaxy w…
Superconducting nanowire single-photon detectors (SNSPDs) have an absolute advantage over other types of single photon detectors except the low operating temperature. Therefore, many efforts have been devoted to find high-temperature superconducting materials that are suitable for preparing SNSPDs. Copper-based and MgB2 ultra-thin superconducting nanowires have been already reported. However, the transport properties of iron-based ultra-thin superconducting nanowires have not been studied. In this work, a 10 nm thick 200 nm wide 30 μm long high quality superconducting nanowire was fabricated f…
High temperature (high-Tc) superconductors like cuprates have superior critical current properties in magnetic fields over other superconductors. However, superconducting wires for high-field-magnet applications are still dominated by low-Tc Nb3Sn due probably to cost and processing issues. The recent discovery of a second class of high-Tc materials, Fe-based superconductors, may provide another option for high-field-magnet wires. In particular, AEFe2As2 (AE: Alkali earth elements, AE-122) is one of the best candidates for high-field-magnet applications because of its high upper critical field…
In several Fe-based superconductors, slight $C_4$ symmetry breaking occurs at $T^*$, which is tens of Kelvin higher than the structural transition temperature $T_S$. In this "hidden" nematic state at $T_S<T<T^*$, the orthorhombicity is tiny [$ϕ=(a-b)/(a+b) \ll 0.1$%], but clear evidences of bulk phase transition have been accumulated. To explain this long-standing mystery, we propose the emergence of antiferro-bond (AFB) order with the antiferro wavevector ${\bf q}=(0,π)$ at $T=T^*$, by which the characteristic phenomena below $T^*$ are satisfactorily explained. This AFB order originates from …
We have investigated the influence of the superconducting layer thickness, d, on the structural and transport properties of Co-doped BaFe2As2 films deposited on Fe-buffered MgO substrates by pulsed laser deposition. The superconducting transition temperature and the texture quality of Co-doped BaFe2As2 films improve with increasing d due to a gradual relief of the tensile strain. For d>90 nm an additional 110 textured component of Co-doped BaFe2As2 was observed, which leads to an upward shift in the angular dependent critical current density at H // c. These results indicate that the grain bou…
Superconducting and normal state transport properties in iron pnictides are sensitive to disorder and impurity scattering. By investigation of Ba(Fe1-xCox)2As2 thin films with varying Co concentration, we demonstrate that in the dirty limit the superconducting dome in the electronic phase diagram of Ba(Fe1-xCox)2As2 shifts towards lower doping concentrations, which differs significantly from observations in single crystals. We show that especially in the underdoped regime superconducting transition temperatures higher than 27 K are possible.
This paper reports comprehensive results on thin-film growth of 122-type iron-pnictide superconductors, AE(Fe1-xCox)2As2 (AE = Ca, Sr, and Ba, AEFe2As2:Co) by a pulsed laser deposition method using a neodymium-doped yttrium aluminum garnet laser as an excitation source. The most critical parameter to produce the SrFe2As2:Co and BaFe2As2:Co phases is the substrate temperature (Ts). It is difficult to produce highly-pure CaFe2As2:Co phase thin film at any Ts. For BaFe2As2:Co epitaxial films, controlling Ts at 800-850 °C and growth rate to 2.8-3.3 Å/s produced high-quality films with good crystal…
The issue of whether the quantum critical point (QCP) is hidden inside unconventional superconductors is a matter of hot debate. Although a prominent experiment on London penetration depth has demonstrated the existence of the QCP in the isovalent-doped iron-based superconductor BaFe$_2$(As$_{1-x}$P$_x$)$_2$, with the observation of a sharp peak in the penetration depth in the vicinity of the disappearance of magnetic order at zero temperature, the nature of such an emerging QCP remains unclear. Here, we provide a unique picture to understand well the phenomena of the QCP based on the framewor…
For applying tensile or compressive uniaxial strain to functional thin films, we propose a novel approach in combining a piezoelectric-based device and a technical metallic substrate used widely in the 2nd generation coated conductors (i.e. superconducting tapes). A strain-induced shift of the superconducting transition temperature of 0.1 K for Co-doped BaFe2As2 was observed along [100] direction, corresponding to a uniaxial pressure derivative dTc/dp100=-4 K/GPa. For Mn3CuN, a uniaxial strain derivative along [100] direction of the Curie temperature dTC/de100=13 K/% was observed. The current …
We report on the growth of NdFeAs(O,F) thin films on [001]-tilt MgO bicrystal substrates with misorientation angle theta_GB=6°, 12°, 24° and 45°, and their inter- and intra-grain transport properties. X-ray diffraction study confirmed that all our NdFeAs(O,F) films are epitaxially grown on the MgO bicrystals. The theta_GB dependence of the inter-grain critical current density Jc shows that, unlike Co-doped BaFe2As2 and Fe(Se,Te), its decay with theta_GB is rather significant. As a possible reason of this result, fluorine may have diffused preferentially to the grain boundary region and eroded …
We report on electrical transport properties of epitaxial Ba(Fe1-xNix)2As2 thin films grown by pulsed laser deposition in static magnetic fields up to 35 T. The thin film shows a critical temperature of 17.2 K and a critical current density of 5.7x10^5 A/cm^2 in self field at 4.2 K while the pinning is dominated by elastic pinning at two-dimensional nonmagnetic defects. Compared to single-crystal data, we find a higher slope of the upper critical field for the thin film at a similar doping level and a small anisotropy. Also an unusual small vortex liquid phase was observed at low temperatures,…
We demonstrate the growth of Co-doped BaFe2As2 (Ba-122) thin films on AEF2 (001) (AE: Ca, Sr, Ba) single crystal substrates using pulsed laser deposition. All films are grown epitaxially despite of a large misfit of -10.6% for BaF2 substrate. For all films a reaction layer is formed at the interface confirmed by X-ray diffraction and by transmission electron microscopy. The superconducting transition temperature of the film on CaF2 is around 27 K, whereas the corresponding values of the other films are around 21 K. The Ba-122 on CaF2 shows identical crystalline quality and superconducting prop…
The biaxially textured growth of superconducting Co-doped BaFe2As2 (Ba-122) thin films has been realized on ion beam assisted deposition (IBAD) MgO coated conductor templates by employing an iron buffer architecture. The iron pnictide coated conductor showed a superconducting transition temperature of 21.5 K, which is slightly lower than that of Co-doped Ba-122 films on single crystalline MgO substrates. A self-field critical current density of over 10^5 A/cm2 has already been achieved even at 8 K. The current experiment highlights the potential of possible coated conductor applications of the…
We review experimental results, from transport to magnetization measurements, on different graphite samples, from bulk oriented graphite, thin graphite films to transmission electron microscope lamellae, that indicate the existence of granular superconductivity at temperatures above 100 K. The accumulated evidence speaks for a localization of the superconducting phase(s) at certain interfaces embedded in semiconducting crystalline regions with Bernal stacking order.
Surface properties of Co-doped BaFe2As2 epitaxial superconducting thin films were inspected by X-ray photoelectron spectroscopy, scanning spreading resistance microscopy (SSRM), and point contact spectroscopy (PCS). It has been shown that surface of Fe-based superconductors degrades rapidly if being exposed to air, what results in suppression of gap-like structure on PCS spectra. Moreover, SSRM measurements revealed inhomogeneous surface conductivity, what is consistent with strong dependence of PCS spectra on contact position. Presented results suggest that fresh surface and small probing are…
We studied two BaFe2-xNixAs2 (Ni-doped Ba-122) single crystals at two dfferent doping levels (underdoped and optimally doped) using an optical spectroscopic technique. The underdoped sample shows a magnetic phase transition around 80 K. We analyze the data with a Drude-Lorentz model with two Drude components (D1 and D2). It is known that the narrow D1 component originates from electron carriers in the electron-pockets and the broad D2 mode is from hole carriers in the hole-pockets. While the plasma frequencies of both Drude components and the static scattering rate of the broad D2 component sh…
The most effective way to enhance the dissipation-free supercurrent in presence of magnetic field for type II superconductors is the introduction of defects that acts as artificial pinning centres (APCs) for the vortices. For instance, the in-field critical current density of doped BaFe2As2 (Ba122), one of the most technologically important Fe-based superconductors, has been improved over the last decade by APCs created by ion-irradiation. The technique of ion-irradiation has been commonly implemented to determine the ultimate superconducting properties. However, this method is rather complica…
We study the critical charge dynamics of the superconducting to the normal-state transition for LSCO thin films with a wide range of the Sr concentration, by measuring the frequency-dependent excess parts of the complex microwave conductivity, which is induced by the superconducting fluctuations. We present a dynamic scaling analysis of the complex fluctuation conductivity, which includes the information on the universality class and the dimensionality of the critical charge dynamics as a function of the Sr concentration, the film thickness and the magnetic field. In our previous study (H. Kit…