Field emission characteristics of InSb patterned nanowires
Filippo Giubileo, Maurizio Passacantando, Francesca Urban, Alessandro Grillo, Laura Iemmo, Aniello Pelella, Curtis Goosney, Ray LaPierre, Antonio Di Bartolomeo
InSb nanowire arrays with different geometrical parameters, diameter and pitch, are fabricated by top-down etching process on Si(100) substrates. Field emission properties of InSb nanowires are investigated by using a nano-manipulated tungsten probe-tip as anode inside the vacuum chamber of a scanning electron microscope. Stable field emission current is reported, with a maximum intensity extracted from a single nanowire of about 1$μA$, corresponding to a current density as high as 10$^4$ A/cm$^2$. Stability and robustness of nanowire is probed by monitoring field emission current for about three hours. By tuning the cathode-anode separation distance in the range 500nm - 1300nm, the field enhancement factor and the turn-on field exhibit a non-monotonic dependence, with a maximum enhancement $β\simeq $ 78 and a minimum turn-on field $E_{ON} \simeq$ 0.033 V/nm for a separation d =900nm. The reduction of spatial separation between nanowires and the increase of diameter cause the reduction of the field emission performance, with reduced field enhancement ($β<$ 60) and increased turn-on field ($E_{ON} \simeq $ 0.050 V/nm). Finally, finite element simulation of the electric field distribution in the system demonstrates that emission is limited to an effective area near the border of the nanowire top surface, with annular shape and maximum width of 10 nm.
Indium antimonide (InSb) nanowires are used as building blocks for quantum devices because of their unique properties, i.e., strong spin-orbit interaction and large Landé g-factor. Integrating InSb nanowires with other materials could potentially unfold novel devices with distinctive functionality. A prominent example is the combination of InSb nanowires with superconductors for the emerging topological particles research. Here, we combine the II-VI cadmium telluride (CdTe) with the III-V InSb in the form of core-shell (InSb-CdTe) nanowires and explore potential applications based on the elect…
We study the low-temperature electron mobility of InSb nanowires. We extract the mobility at 4.2 Kelvin by means of field effect transport measurements using a model consisting of a nanowire-transistor with contact resistances. This model enables an accurate extraction of device parameters, thereby allowing for a systematic study of the nanowire mobility. We identify factors affecting the mobility, and after optimization obtain a field effect mobility of $\sim2.5\mathbin{\times}10^4$ cm$^2$/Vs. We further demonstrate the reproducibility of these mobility values which are among the highest repo…
High quality heteroepitaxial two-dimensional (2D) InSb layers are very difficult to realize owing to the large lattice mismatch with other widespread semiconductor substrates. A way around this problem is to grow free-standing 2D InSb nanostructures on nanowire (NW) stems, thanks to the capability of NWs to efficiently relax elastic strain along the sidewalls when lattice-mismatched semiconductor systems are integrated. In this work, we optimize the morphology of free-standing 2D InSb nanoflags (NFs). In particular, robust NW stems, optimized growth parameters, and the use of reflection high-e…
Epitaxially grown, high quality semiconductor InSb nanowires are emerging material systems for the development of high performance nanoelectronics and quantum information processing and communication devices, and for the studies of new physical phenomena in solid state systems. Here, we report on measurements of a superconductor-normal conductor-superconductor junction device fabricated from an InSb nanowire with aluminum based superconducting contacts. The measurements show a proximity induced supercurrent flowing through the InSb nanowire segment, with a critical current tunable by a gate, i…
Proposals for studying topological superconductivity and Majorana bound states in nanowires proximity coupled to superconductors require that transport in the nanowire is ballistic. Previous work on hybrid nanowire-superconductor systems has shown evidence for Majorana bound states, but these experiments were also marked by disorder, which disrupts ballistic transport. In this letter, we demonstrate ballistic transport in InSb nanowires interfaced directly with superconducting Al by observing quantized conductance at zero-magnetic field. Additionally, we demonstrate that the nanowire is proxim…
Within the framework of Boltzmann equation, we present a $\mathbf{k\cdot p}$ theory based study for the low-field mobilities of InSb nanowires (InSb NWs) with relatively large cross sectional sizes (with diameters up to 51.8 nm). For such type of large size nanowires, the intersubband electron-phonon scattering is of crucial importance to affect the scattering rate and then the mobility. In our simulation, the lowest 15 electron subbands and 50 transverse modes of phonons are carefully accounted for. We find that, up to the 51.84 nm diameter, the mobility monotonously increases with the diamet…
Hybrid InSb nanowire-superconductor devices are promising for investigating Majorana modes and topological quantum computation in solid-state devices. An experimental realisation of ballistic, phase-coherent superconductor-nanowire hybrid devices is a necessary step towards engineering topological superconducting electronics. Here, we report on a low-temperature transport study of Josephson junction devices fabricated from InSb nanowires grown by molecular-beam epitaxy and provide a clear evidence for phase-coherent, ballistic charge transport through the nanowires in the junctions. We demonst…
We use magnetoconductance measurements in dual-gated InSb nanowire devices together with a theoretical analysis of weak antilocalization to accurately extract spin-orbit strength. In particular, we show that magnetoconductance in our three-dimensional wires is very different compared to wires in two-dimensional electron gases. We obtain a large Rashba spin-orbit strength of $0.5 -1\,\text{eVÅ}$ corresponding to a spin-orbit energy of $0.25-1\,\text{meV}$. These values underline the potential of InSb nanowires in the study of Majorana fermions in hybrid semiconductor-superconductor devices.
Majorana Zero Modes (MZMs) are prime candidates for robust topological quantum bits, holding a great promise for quantum computing. Semiconducting nanowires with strong spin orbit coupling offers a promising platform to harness one-dimensional electron transport for Majorana physics. Demonstrating the topological nature of MZMs relies on braiding, accomplished by moving MZMs around each other in a certain sequence. Most of the proposed Majorana braiding circuits require nanowire networks with minimal disorder. Here, the electronic transport across a junction between two merged InSb nanowires i…
We report on realization and transport spectroscopy study of single quantum dots (QDs) made from InSb nanowires grown by molecular beam epitaxy (MBE). The nanowires employed are 50-80 nm in diameter and the QDs are defined in the nanowires between the source and drain contacts on a Si/SiO$_2$ substrate. We show that highly tunable QD devices can be realized with the MBE-grown InSb nanowires and the gate-to-dot capacitance extracted in the many-electron regimes is scaled linearly with the longitudinal dot size, demonstrating that the devices are of single InSb nanowire QDs even with a longitudi…
Semiconductor-superconductor heterostructures represent a promising platform for the detection of Majorana zero modes and subsequently the processing of quantum information using their exotic non-Abelian statistics. Theoretical modeling of such low-dimensional semiconductors is generally based on phenomenological effective models. However, a more microscopic understanding of their band structure and, especially, of the spin-orbit coupling of electrons in these devices is important for optimizing their parameters for applications in quantum computing. In this paper, we approach this problem by …
A longstanding goal of spintronics is to inject, coherently transport, and detect spins in a semiconductor nanowire where a SINGLE quantized subband is occupied at room temperature. Here, we report achieving this goal in 50-nm diameter InSb nanowires by demonstrating both the spin-valve and the Hanle effect. The spin relaxation time in the nanowires was found to have increased by an order of magnitude over what has been reported in bulk and quantum wells due to the suppression of D'yakonov-Perel' spin relaxation as a result of single subband occupancy. These experiments raise hopes for the rea…
We have measured the Zeeman splitting of quantum levels in few-electron quantum dots (QDs) formed in narrow bandgap InSb nanowires via the Schottky barriers at the contacts under application of different spatially orientated magnetic fields. The effective g-factor tensor extracted from the measurements is strongly anisotropic and level-dependent, which can be attributed to the presence of strong spin-orbit interaction (SOI) and asymmetric quantum confinement potentials in the QDs. We have demonstrated a successful determination of the principal values and the principal axis orientations of the…
Ballistic electron transport is a key requirement for existence of a topological phase transition in proximitized InSb nanowires. However, measurements of quantized conductance as direct evidence of ballistic transport have so far been obscured due to the increased chance of backscattering in one dimensional nanowires. We show that by improving the nanowire-metal interface as well as the dielectric environment we can consistently achieve conductance quantization at zero magnetic field. Additionally, studying the sub-band evolution in a rotating magnetic field reveals an orbital degeneracy betw…
We report on a theoretical study of the electronic structures of InSb and GaSb nanowires oriented along the [001] and [111] crystallographic directions. The nanowires are described by atomistic, spin-orbit inteaction included, tight-binding models, and the band structures and the wave functions of the nanowires are calculated by means of a Lanczos iteration algorithm. For the [001]-oriented InSb and GaSb nanowires, the systems with both square and rectangular cross sections are considered. Here, it is found that all the energy bands are double degenerate. Furthermore, although the lowest condu…
We report on the observation of excitation of Majorana fermions in a Nb-InSb nanowire quantum dot-Nb hybrid system. The InSb nanowire quantum dot is formed between the two Nb contacts by weak Schottky barriers and is thus in the regime of strong couplings to the contacts. Due to the proximity effect, the InSb nanowire segments covered by superconductor Nb contacts turn to superconductors with a superconducting energy gap $Δ^*$. Under an applied magnetic field larger than a critical value for which the Zeeman energy in the InSb nanowire is $E_z\sim Δ^*$, the entire InSb nanowire is found to be …
Low-temperature magnetotransport measurements are performed on GaAs/InSb core-shell nanowires. The nanowires were self-catalyzed grown by molecular beam epitaxy. The conductance measurements as a function of back-gate voltage show an ambipolar behavior comprising an insulating range in between the transition from the p-type to the n-type region. Simulations based on a self-consistent Schrödinger--Poisson solver revealed that the ambipolar characteristics originate from a Fermi level dependent occupation of hole and electron states within the approximately circular quantum well formed in the In…
The graphene morphology regulated by nanowires patterned in parallel on a substrate surface is quantitatively determined using energy minimization. The regulated graphene morphology is shown to be governed by the nanowire diameter, the nanowire spacing and the interfacial bonding energies between the graphene and the underlying nanowires and substrate. We demonstrate two representative regulated graphene morphologies and determine critical values of the nanowire spacing, nanowire diameter and interfacial bonding energies at which graphene switches between the two representative morphologies. I…
In this paper, we investigate the impact of gating potential and magnetic field on phonon induced spin relaxation rate and the speed of the electrically driven single-qubit operations inside the InSb nanowire spin qubit. We show that a strong $g$ factor and high magnetic field strength lead to the prevailing influence of electron-phonon scattering due to deformation potential, considered irrelevant for materials with a weak $g$ factor, like GaAs or Si/SiGe. In this regime, we find that spin relaxation between qubit states is significantly suppressed due to the confinement perpendicular to the …
In this study, InSb nanowires have been formed by electrodeposition and integrated into NW-FETs. NWs were formed in porous anodic alumina (PAA) templates, with the PAA pore diameter of approximately 100 nm defining the NW diameter. Following annealing at 125C and 420C respectively, the nanowires exhibited the zinc blende crystalline structure of InSb, as confirmed from x-ray diffraction and high resolution transmission electron microscopy. The annealed nanowires were used to fabricate nanowire field effect transistors (NW-FET) each containing a single NW with 500 nm channel length and gating t…
Understanding of the electrical contact properties of semiconductor nanowire (NW) field effect transistors (FETs) plays a crucial role in employing semiconducting NWs as building blocks for future nanoelectronic devices and in the study of fundamental physics problems. Here, we report on a study of the contact properties of Ti/Au, a widely used contact metal combination, to individual InSb NWs via both two-probe and four-probe transport measurements. We show that a Schottky barrier of height $Φ_{\rm{SB}}\sim20\ \rm{meV}$ is present at the metal-InSb NW interfaces and its effective height is ga…
Strong spin-orbit semiconductor nanowires coupled to a superconductor are predicted to host Majorana zero modes. Exchange (braiding) operations of Majorana modes form the logical gates of a topological quantum computer and require a network of nanowires. Here, we develop an in-plane selective-area growth technique for InSb-Al semiconductor-superconductor nanowire networks with excellent quantum transport properties. Defect-free transport channels in InSb nanowire networks are realized on insulating, but heavily mismatched InP substrates by 1) full relaxation of the lattice mismatch at the nano…
Long nanowires of degenerate semiconductor InSb in asbestos matrix (wire diameter is around 50 Å, length 0.1 - 1 mm) were prepared. Electrical conduction of these nanowires is studied over a temperature range 1.5 - 350 K. It is found that a zero-field electrical conduction is a power function of the temperature $G\propto T^α$ with the typical exponent $α\approx 4$. Current-voltage characteristics of such nanowires are found to be nonlinear and at sufficiently low temperatures follows the power law $I\propto V^β$. It is shown that the electrical conduction of these nanowires cannot be accounted…
We report on transport measurement study of top-gated field effect transistors made out of InSb nanowires grown by chemical vapor deposition. The transistors exhibit ambipolar transport characteristics revealed by three distinguished gate-voltage regions: In the middle region where the fermi level resides within the bandgap, the electrical resistance shows an exponential dependence on temperature and gate voltage. With either more positive or negative gate voltages, the devices enter the electron and hole transport regimes, revealed by a resistance decreasing linearly with decreasing temperatu…
Magnetoresistance in long correlated nanowires of degenerate semiconductor InSb in asbestos matrix (wire diameter of around 5 nm, length 0.1 - 1 mm) is studied over temperature range 2.3 - 300 K. At zero magnetic field the electric conduction $G$ and the current-voltage characteristics of such wires obey the power laws $G\propto T^α$, $I\propto V^β$, expected for one-dimensional electron systems. The effect of magnetic field corresponds to a 20% growth of the exponents $α$, $β$ at H=10 T. The observed magnetoresistance is caused by the magnetic-field-induced breaking of the spin-charge separat…
The electrostatic performance of p-type nanowires (NWs) made of InSb and GaSb, with special focus on their gate capacitance behavior, is analyzed and compared to that achieved by traditional semiconductors usually employed for p-MOS such as Si and Ge. To do so, a self-consistent kp simulator has been implemented to achieve an accurate description of the Valence Band and evaluate the charge behavior as a function of the applied gate bias. The contribution and role of the constituent capacitances, namely the insulator, centroid and quantum ones are assessed. It is demonstrated that the centroid …
We characterize InSb quantum dots induced by bottom finger gates within a nanowire that is grown via the vapor-liquid-solid process. The gates are separated from the nanowire by an exfoliated 35\,nm thin hexagonal BN flake. We probe the Coulomb diamonds of the gate induced quantum dot exhibiting charging energies of $\sim 2.5\,\mathrm{meV}$ and orbital excitation energies up to $0.3\,\mathrm{meV}$. The gate hysteresis for sweeps covering 5 Coulomb diamonds reveals an energy hysteresis of only $60\mathrm{μeV}$ between upwards and downwards sweeps. Charge noise is studied via long-term measureme…
We report an experimental study of one-dimensional (1D) electronic transport in an InSb semiconducting nanowire. Three bottom gates are used to locally deplete the nanowire creating a ballistic quantum point contact with only a few conducting channels. In a magnetic field, the Zeeman splitting of the corresponding 1D subbands is revealed by the emergence of conductance plateaus at multiples of $e^2$/h, yet we find a quantized conductance pattern largely dependent on the configuration of voltages applied to the bottom gates. In particular, we can make the first plateau disappear leaving a first…
We use semiclassical Monte Carlo approach to investigate spin polarized transport in InP and InSb nanowires. Spin dephasing in III-V channels is caused due to D'yakonov- Perel (DP) relaxation and due to Elliott-Yafet (EY) relaxation. The DP relaxation occurs because of bulk inversion asymmetry (Dresselhaus spin-orbit interaction) and structural inversion asymmetry (Rashba spin-orbit interaction). The injection polarization direction studied is that along the length of the channel. The dephasing rate is found to be very strong for InSb as compared to InP which has larger spin dephasing lengths.…
Typical measurements of nanowire devices rely on end-to-end measurements to reveal mesoscopic phenomena such as quantized conductance or Coulomb blockade. However, creating nanoscale tunnel junctions allows one to directly measure other properties such as the density of states or electronic energy distribution functions. In this paper, we demonstrate how to realize uniform tunnel junctions on InSb nanowires, where the low invasiveness preserves ballistic transport in the nanowires. The utility of the tunnel junctions is demonstrated via measurements using a superconducting tunneling probe, whi…
By studying the time-dependent axial and radial growth of InSb nanowires, we map the conditions for the synthesis of single-crystalline InSb nanocrosses by molecular beam epitaxy. Low-temperature electrical measurements of InSb nanocross devices with local gate control on individual terminals exhibit quantized conductance and are used to probe the spatial distribution of the conducting channels. Tuning to a situation where the nanocross junction is connected by few-channel quantum point contacts in the connecting nanowire terminals, we show that transport through the junction is ballistic exce…
We propose a fast and accurate spin initialization method for a single electron trapped in an electrostatic quantum dot. The dot is created in a nanodevice composed of a catalytically grown indium antimonide (InSb) nanowire and nearby gates to which control voltages are applied. Initially we insert a single electron of arbitrary spin into the wire. Operations on spin are performed using the Rashba spin-orbit interaction induced by an electric field. First, a single pulse of voltages applied to lateral gates is used to split the electron wavepacket into two parts with opposite spin orientations…
A systematic numerical investigation of spin-orbit fields in the conduction bands of III-V semiconductor nanowires is performed. Zinc-blende InSb nanowires are considered along [001], [011], and [111] directions, while wurtzite InAs nanowires are studied along [0001] and [10$\overline{1}$0] or [11$\overline{2}$0] directions. Realistic multiband $\vec{k} \cdot \vec{p}\,$ Hamiltonians are solved by using plane-wave expansions of real-space parameters. In all cases the linear and cubic spin-orbit coupling parameters are extracted for nanowire widths from 30 to 100 nm. Typical spin-orbit energies …
Majorana zero modes (MZMs), prime candidates for topological quantum bits, are detected as zero bias conductance peaks (ZBPs) in tunneling spectroscopy measurements. Implementation of a narrow and high tunnel barrier in the next generation of Majorana devices can help to achieve the theoretically predicted quantized height of the ZBP. We propose a material-oriented approach to engineer a sharp and narrow tunnel barrier by synthesizing a thin axial segment of GaxIn1-xSb within an InSb nanowire. By varying the precursor molar fraction and the growth time, we accurately control the composition an…
Semiconductor nanowires such as InAs and InSb are promising materials for studying Majorana zero-modes and demonstrating non-Abelian particle exchange relevant for topological quantum computing. While evidence for Majorana bound states in nanowires has been shown, the majority of these experiments are marked by significant disorder. In particular, the interfacial inhomogeneity between the superconductor and nanowire is strongly believed to be the main culprit for disorder and the resulting soft superconducting gap ubiquitous in tunneling studies of hybrid semiconductor-superconductor systems. …
Hybrid superconductor-semiconducting nanowire devices provide an ideal platform to investigating novel intragap bound states, such as the Andreev bound states (ABSs), Yu-Shiba-Rusinov (YSR) states, and the Majorana bound states. The competition between Kondo correlations and superconductivity in Josephson quantum dot (QD) devices results in two different ground states and the occurrence of a 0-$π$ quantum phase transition. Here we report on transport measurements on hybrid superconductor-InSb nanowire QD devices with different device geometries. We demonstrate a realization of continuous gate-…
We systematically study three-terminal InSb-Al nanowire devices by using radio-frequency reflectometry. Tunneling spectroscopy measurements on both ends of the hybrid nanowires are performed while systematically varying the chemical potential, magnetic field and junction transparencies. Identifying the lowest-energy state allows for the construction of lowest- and zero-energy state diagrams, which show how the states evolve as a function of the aforementioned parameters. Importantly, comparing the diagrams taken for each end of the hybrids enables the identification of states which do not coex…
We report electron transport studies on InSb-Al hybrid semiconductor-superconductor nanowire devices. Tunnelling spectroscopy is used to measure the evolution of subgap states while varying magnetic field and voltages applied to various nearby gates. At magnetic fields between 0.7 and 0.9 T, the differential conductance contains large zero bias peaks (ZBPs) whose height reaches values on the order 2e2/h. We investigate these ZBPs for large ranges of gate voltages in different devices. We discuss possible interpretations in terms of disorder-induced subgap states, Andreev bound states and Major…
Epitaxial semiconductor-superconductor (SM-SC) hybrid nanowires are potential candidates for implementing Majorana qubits. Recent experimental and theoretical works show that charged impurities in SM remain a major problem in all existing hybrid nanowires, in which the SM is either InAs or InSb while the SC is mainly Al. Here, we theoretically validate the recently proposed PbTe-Pb hybrid nanowire as a potential candidate for Majorana devices. By studying the electrostatic and electronic properties of PbTe nanowires, we demonstrate that the huge dielectric constant of PbTe endows itself a high…
Signatures of Majorana zero modes (MZMs), which are the building blocks for fault-tolerant topological quantum computing, have been observed in semiconductor nanowires (NW) with strong spin-orbital-interaction (SOI), such as InSb and InAs NWs with proximity-induced superconductivity. Realizing topological superconductivity and MZMs in this most widely-studied platform also requires eliminating spin degeneracy, which is realized by applying a magnetic field to induce a helical gap. However, the applied field can adversely impact the induced superconducting state in the NWs and also places geome…
We study transport mediated by Andreev bound states formed in InSb nanowire quantum dots. Two kinds of superconducting source and drain contacts are used: epitaxial Al/InSb devices exhibit a doubling of tunneling resonances, while in NbTiN/InSb devices Andreev spectra of the dot appear to be replicated multiple times at increasing source-drain bias voltages. In both devices, a mirage of a crowded spectrum is created. To describe the observations a model is developed that combines the effects of a soft induced gap and of additional Andreev bound states both in the quantum dot and in the finite …
The motion of an electron and its spin are generally not coupled. However in a one dimensional material with strong spin-orbit interaction (SOI) a helical state may emerge at finite magnetic fields, where electrons of opposite spin will have opposite momentum. The existence of this helical state has applications for spin filtering and Cooper pair splitter devices and is an essential ingredient for realizing topologically protected quantum computing using Majorana zero modes. Here we report electrical conductance measurements of a quantum point contact (QPC) formed in an indium antimonide nanow…
Double quantum dot in the few-electron regime is achieved using local gating in an InSb nanowire. The spectrum of two-electron eigenstates is investigated using electric dipole spin resonance. Singlet-triplet level repulsion caused by spin-orbit interaction is observed. The size and the anisotropy of singlet-triplet repulsion are used to determine the magnitude and the orientation of the spin-orbit effective field in an InSb nanowire double dot. The obtained results are confirmed using spin blockade leakage current anisotropy and transport spectroscopy of individual quantum dots.
We use $\vec{k}\cdot\vec{p}$ theory to estimate the Rashba spin-orbit coupling (SOC) in large semiconductor nanowires. We specifically investigate GaAs- and InSb-based devices with different gate configurations to control symmetry and localization of the electron charge density. We explore gate-controlled SOC for wires of different size and doping, and we show that in high carrier density SOC has a non-linear electric field susceptibility, due to large reshaping of the quantum states. We analyze recent experiments with InSb nanowires in light of our calculations. Good agreement is found with S…
Nominally identical permalloy nanowires, with widths down to 150 nm, were fabricated onto a single electron transparent Si$_{3}$N$_{4}$ membrane using electron beam lithography (EBL) and focused ion beam (FIB) milling. Transmission electron microscopy (TEM) experiments were performed to compare the nanostructures produced by these two techniques in what we believe is the first direct comparison of fabrication techniques for nominally identical nanowires. Both EBL and FIB methods produced high quality structures with edge roughness being of the order of the mean grain size 5 -10 nm observed in …
We study hysteretic magnetoresistance in InSb nanowires due to stray magnetic fields from CoFe micromagnets. Devices without any ferromagnetic components show that the magnetoresistance of InSb nanowires commonly exhibits either a local maximum or local minimum at zero magnetic field. Switching of microstrip magnetizations then results in positive or negative hysteretic dependence as conductance maxima or minima shift with respect to the global external field. Stray fields are found to be in the range of tens of millitesla, comparable to the scale over which the nanowire magnetoresistance deve…
We employ first-principles techniques tailored to properly describe semiconductors (modified Becke-Johnson potential added to the exchange-correlation functional), to obtain the electronic band structures of both the zinc-blende and wurtzite phases of GaAs, GaSb, InAs, and InSb. We extract the spin-orbit fields for the relevant valence and conduction bands at zone center, by fitting the spin-splittings resulting from the lack of space inversion symmetry of these bulk crystal structures, to known functional forms---third-order polynomials. We also determine the orientations of the spin-orbit ve…
We study bottom-up grown semiconductor indium antimonide nanowires that are coated with shells of tin. The shells are uniform in thickness. The interface between Sn and InSb is abrupt and without interdiffusion. Devices for transport are prepared by in-situ shadowing of nanowires using nearby nanowires as well as flakes, resulting in etch-free junctions. Tin is found to induce a hard superconducting gap in the range 600-700 micro-eV. Superconductivity persists up to 4 T in magnetic field. A tin island exhibits the coveted two-electron charging effect, a hallmark of charge parity stability. The…
We have studied the magnetotransport through an indium antimonide (InSb) nanowire grown in [111] direction, with a geometric constriction and in an external magnetic field applied along the nanowire axis. We have found that the magnetoresistance is negative for the narrow constriction, nearly zero for the constriction of some intermediate radius, and takes on positive values for the constriction with the radius approaching that of the nanowire. For all magnitudes of the magnetic field, the radius of constriction at which the change of the magnetoresistance sign takes place has been found to be…
Semiconductor quantum dots (QDs) are being regarded as the primary unit for a wide range of advanced and emerging technologies including electronics, optoelectronics, photovoltaics and biosensing applications as well as the domain of q-bits based quantum information processing. Such QDs are suitable for several novel device applications for their unique property of confining carriers 3-dimensionally creating discrete quantum states. However, the realization of such QDs in practice exhibits serious challenge regarding their fabrication in array with desired scalability and repeatability as well…