Bismuth telluride is a low energy bulk band-gap topological system with conducting surface states. Besides its very good thermoelectric properties, it also makes a very good candidate for broadband photodetectors. Here, we report temperature-dependent photo-Seebeck effect in a bulk single crystalline bismuth telluride. On light illumination, an electrically biased sample shows distinguishable contributions in the measured current due to both the Seebeck effect and the normal photo-generated carriers within a narrow layer of the sample. Detailed experiments are performed to elucidate the distinction between the Seebeck contribution and the photogenerated current. The temperature-dependence of the photocurrent without Seebeck contribution shows a sign reversal from negative to positive at a specific temperature depending on the wavelength of photoexcitation light.
We report on graphene-like exfoliation of the large-area crystalline films and ribbons of bismuth telluride with the thicknesses of a few atoms. It is demonstrated that bismuth telluride, the most important material for thermoelectric industry, can be mechanically separated into its building blocks -[Te-Bi-Te-Bi-Te]- atomic five-folds with the thickness of ~1 nm and even further - to subunits with smaller thicknesses. The atomically-thin crystals can be structured into suspended crystalline ribbons providing quantum confinement in two dimensions. The quasi two-dimensional (2-D) crystals of bis…
Hetero-epitaxial films based on bismuth telluride with excess of Te were grown by hat wall technique at the surface of the mica (muscovite). Galvanomagnetic properties of the thin films were measured, and quantum oscillations of the magnetoresistance were found at the temperatures below 10 K in the magnetic field from 6 to 14 T. From analysis of magnetoresistance oscillations the main surface state parameters of the films were determined. Expementally obtained Landau level index shift and its temperature dependence are consistent with Berry phase specific for topological Dirac surface states. …
Bismuth telluride (Bi2Te3) and its alloys are the best bulk thermoelectric materials known today. The stacked quasi-two-dimensional (2D) layers of Bi2Te3 were also identified as topological insulators. In this paper we describe a method for graphene-inspired exfoliation of crystalline bismuth telluride films with a thickness of a few atoms. The atomically thin films were suspended across trenches in Si/SiO2 substrates, and subjected to detail characterization. The presence of the van der Waals gaps allowed us to disassemble Bi2Te3 crystal into its quintuple building blocks - five mono-atomic s…
We study the electrical transport properties of ensembles of bismuth telluride (Bi2Te3) nanoplates grown by solution based chemical synthesis. Devices consisting of Bi2Te3 nanoplates are fabricated by surface treatment after dropping the solution on the structured gold plates and the temperature dependence of resistance shows a nonmetallic behavior. Symmetric tunneling behavior in I-V was observed in both our experimental results and theoretical calculation of surface conductance based on a simple Hamiltonian, which excludes carrier-carrier interactions. Here, we present two devices: one showi…
We theoretically studied the effect of the perpendicular electric field on the thermoelectric properties of the intrinsic, n-type and p-type bismuth telluride nanowires with the growth direction [110]. The electronic structure and the wave functions were calculated by solving self-consistently the system of the Schrodinger and Poisson equations using the spectral method. The Poisson equation was solved in terms of the Newton - Raphson method within the predictor-corrector approach. The electron - electron exchange - correlation interactions were taken into account in our analysis. In the tempe…
Potential applications in spintronics and quantum computing have motivated much recent research in epitaxial films of bismuth telluride. This system is also an example of van der Waals (vdW) epitaxy where the interface coherence between film and substrate is based on vdW bonds instead of strong ionic or covalent bonds. Effects of lattice mismatch on electrical properties and film structure are more difficult to control due to the weakness of the vdW forces. Here we present a general x-ray diffraction method to investigate in-plane atomic displacements and lateral lattice coherence length in vd…
Electronic structure of bismuth telluride nanowires with the growth directions [110] and [015] is studied in the framework of anisotropic effective mass method using the parabolic band approximation. The components of the electron and hole effective mass tensor for six valleys are calculated for both growth directions. For a square nanowire, in the temperature range from 77 K to 500 K, the dependence of the Seebeck coefficient, the electron thermal and electrical conductivity as well as the figure of merit ZT on the nanowire thickness and on the excess hole concentration are investigated in th…
Metallic Bi2Te3 crystalline sheets with the room-temperature resistivity of above 10 mΩ cm were prepared and their magnetoresistive transport was measured in a field of up to 9 Tesla. The Shubnikov de Haas oscillations were identified from the secondly-derived magnetoresistance curves. While changing the angle between the field and normal axis of the sheets, we find that the oscillation periods present a cosine dependence on the angle. This indicates a two-dimensional transport due to the surface state. The work reveals a resolvable surface contribution to the overall conduction even in a meta…
We report on "graphene-like" mechanical exfoliation of single-crystal Bi2Te3 films and thermoelectric characterization of the stacks of such films. Thermal conductivity of the resulting "pseudo-superlattices" was measured by the "hot disk" and "laser flash" techniques. The room-temperature in-plane (cross-plane) thermal conductivity of the stacks decreases by a factor of ~2.4 (3.5) as compared to bulk. The thermal conductivity reduction with preserved electrical properties leads to strong increase in the thermoelectric figure of merit. It is suggested that the film thinning to few-quintuples a…
Since 2017, epitaxial graphene has been the base material for the US national standard for resistance. A future avenue of research within electrical metrology is to remove the need for strong magnetic fields, as is currently the case for devices exhibiting the quantum Hall effect. The quantum Hall effect is just one of many research endeavours that revolve around recent quantum physical phenomena like composite fermions, charge density waves, and topological properties [1-2]. New materials, like magnetically doped topological insulators (MTIs), offer access to the quantum anomalous Hall effect…
We demonstrate that the charge-spin conversion efficiency of topological insulators (TI) can be experimentally determined by injecting spin-polarized tunneling electrons into a TI. Through a comparative study between bismuth selenide and bismuth antimony telluride, we verified the topological-surface-state origin of the observed giant spin signals. By injecting energetic electrons into bismuth selenide, we further studied the energy dependence of the effective spin polarization at the TI surface. The experimentally verified large spin polarization, as well as our calculations, provides new ins…
The Weyl semi-metal candidate MoTe$_{2}$ is expected to exhibit a range of exotic electronic transport properties. It exhibits a structural phase transition near room temperature that is evident in the thermal hysteresis in resistivity and thermopower (Seebeck coefficient) as well as large spin-orbit interaction. Here, we also document a resistivity anomaly of up to 13% in the temperature window between 25 and 50 K, which is found to be strongly anisotropic. Based on the experimental data in conjunction with density functional theory calculations, we conjecture that the anomaly can be related …
We calculate the phonon-drag contribution to the transverse (Nernst) thermoelectric power $S_{yx}$ in a bismuth single crystal subjected to a quantizing magnetic field. The calculated heights of the Nernst peaks originating from the hole Landau levels and their temperature dependence reproduce the right order of magnitude for those of the pronounced magneto-oscillations recently reported by Behnia et al [Phys.Rev.Lett. 98, 166602 (2007)]. A striking experimental finding that $S_{yx}$ is much larger than the longitudinal (Seebeck) thermoelectric power $S_{xx}$ can be naturally explained as the …
Te NMR studies were carried out for the bismuth telluride topological insulator in a wide range from room temperature down to 12.5 K. The measurements were made on a Bruker Avance 400 pulse spectrometer. The NMR spectra were collected for the mortar and pestle powder sample and for single crystalline stacks with orientations c parallel and perpendicular to field. The activation energy responsible for thermal activation. The spectra for the stack with c parallel to field showed some particular behavior below 91 K.
A 125Te NMR study of bismuth telluride nanoparticles as function of particle size revealed that the spin-lattice relaxation is enhanced below 33 nm, accompanied by a transition of NMR spectra from single to bimodal regime. The satellite peak features a negative Knight shift and higher relaxivity, consistent with core polarization from p-band carriers. Whereas nanocrystals follow a Korringa law in the range 140-420K, micrometer particles do so only below 200K. The results reveal increased metallicity of these nanoscale topological insulators in the limit of higher surface-to-volume ratios.
Bismuth chalcogenides and lead telluride/selenide alloys exhibit exceptional thermoelectric properties which could be harnessed for power generation and device applications. Since phonons play a significant role in achieving these desired properties, quantifying the interaction between phonons and electrons, which is encoded in the Eliashberg function of a material, is of immense importance. However, its precise extraction has in part been limited due to the lack of local experimental probes. Here we construct a method to directly extract the Eliashberg function using Landau level spectroscopy…
Bismuth telluride - Bi(2)Te(3)- and related compounds have recently attracted strong interest owing to the discovery of the topological insulator properties in many members of this family of materials. The few-quintuple films of these materials are particularly interesting from the physics point of view. We report results of the micro-Raman spectroscopy study of the "graphene-like" exfoliated few-quintuple layers of Bi(2)Te(3), Bi(2)Se(3) and Sb(2)Te(3). It is found that crystal symmetry breaking in few-quintuple films results in appearance of A1u-symmetry Raman peaks, which are not active in …
Considerable evidence suggests that variations in the properties of topological insulators (TIs) at the nanoscale and at interfaces can strongly affect the physics of topological materials. Therefore, a detailed understanding of surface states and interface coupling is crucial to the search for and applications of new topological phases of matter. Currently, no methods can provide depth profiling near surfaces or at interfaces of topologically inequivalent materials. Such a method could advance the study of interactions. Herein we present a non-invasive depth-profiling technique based on $β$-N…