Irreproducibility is a serious issue in thin film organic photovoltaic (OPV) devices, as smallest local inhomogeneities can change the entire behaviour of identically built devices without showing obvious failure. Inhomogeneities can occur at various steps of device preparation and appear in all layers with different length scales and impact. The hole-transport interlayer (HTL) in OPV devices blocks unwanted electron diffusion to the anode and corrects energetic mismatch between oxide electrode and organic semiconductor. Most commonly used is commercial ink based on poly(3,4-ethylenedioxythiophene) poly(styrenesulfonate) (PEDOT PSS) colloidal particles. However, exactly these are suspected to cause microscopic inhomogeneities, causing known irreproducibility of device characteristics. Considering PEDOT:PSS acidity-caused electrode corrosion, it is questionable how much impact colloids have on device homogeneity. In this report, we give proof that a colloidal HTL does not necessarily cause device inhomogeneity and decreased efficiency, by comparing OPV devices with different HTLs, namely from commercial PEDOT:PSS ink and from MoO3, obtained from two liquid precursors, leading to quasi-continuous or colloidal layers. With a combination of X-ray diffraction, atomic force and Kelvin probe microscopy, photoelectron and ambient air photoemission spectroscopy, we discuss the layers properties from nano- to macroscale and demonstrate their impact upon implementation into OPV devices, via spatially-resolved characterization.
After the efficiency of organic photovoltaic (OPV) cells achieved more than 10%, the control of stability and degradation mechanisms of solar cells became a prominent task. The improvement of device efficiency due to incorporation of a hole-transport layer (HTL) in bulk-heterojunction solar cells has been extensively reported. However, the most widely used HTL material, PEDOT:PSS is frequently suspected to be the dominating source for devices instability under environmental conditions. Thereby effects like photooxidation and electrode corrosion are often reported to shorten device lifetime. Ho…
Here, we focus on induced degradation and spatial inhomogeneity of organic photovoltaic devices under different environmental conditions, uncoupled from the influence of a hole-transport (HT) layer. During testing of devices comprising the standard photoactive layer of P3HT as donor, blended with PCBM as acceptor, a comparison was made between the nonencapsulated devices upon exposure to dry air, dry air with illumination and humid air. The impact on the active layer's photophysics is discussed, along with the device physics in terms of integral solar cell performance and spatially resolved ph…
The thermodynamic limit for the efficiency of solar cells is predominantly defined by the energy bandgap of the used semiconductor. In case of organic solar cells both energetics and kinetics of three different species play role: excitons, charge transfer states and charge separated states. In this work, we clarify the effect of the relative energetics and kinetics of these species on the recombination and generation dynamics. Making use of detailed balance, we develop an analytical framework describing how the intricate interplay between the different species influence the photocurrent genera…
Charge transfer in polymer devices represents a crucial, though highly inaccessible stage of photocurrent generation. In this article we propose studying the properties and behaviour of organic solar cells through the modification of photocurrent generation when an external magnetic field is applied. By allowing the parameters of our theoretical model not to be constrained to any specific material, we are able to show that not only a modest external magnetic field leads to a significant increase in photocurrent intensity, but also how such magnetic field can be used to study in detail the ener…
Solution-processable interlayers are an important building block for the commercialization of organic electronic devices such as organic solar cells. Here, the potential of cross-linking to provide an insoluble, stable and versatile charge transport layer based on soluble organic semiconductors is studied. For this purpose, a photo-reactive tris-azide cross-linker is synthesized. The capability of the small molecular cross-linker is illustrated by applying it to a p-doped polymer used as a hole transport layer in organic solar cells. High cross-linking efficiency and excellent charge extractio…
In this article the Wells-Dawson polyoxometalate K6[P2W18O62] is grown as an interfacial layer between indium tin oxide and bulk heterojunction of poly(3-hexylthiophene) (P3HT) and [6,6]-phenyl-C61-butyric acid methyl ester (PCBM). The structure of the POM layers depends on the thickness and shows a highly anisotropic surface organization. The films have been characterized by atomic force microscopy and X-ray photoelectron spectroscopy (XPS) to gain insight into their macroscopic organization and better understand their electronic properties. Then, they were put at the anodic interface of a P3…
Surface recombination has a major impact on the open-circuit voltage ($V_\text{oc}$) of organic photovoltaics. Here, we study how this loss mechanism is influenced by imbalanced charge transport in the photoactive layer. As a model system, we use organic solar cells with a two orders of magnitude higher electron than hole mobility. We find that small variations in the work function of the anode have a strong effect on the light intensity dependence of $V_\text{oc}$. Transient measurements and drift-diffusion simulations reveal that this is due to a change in the surface recombination rather th…
We report a charge based model to establish the analytical equation, describing the nature of capacitance-voltage ($C$-$V$) characteristics of organic solar cells under dark condition (or organic diodes) over a wide range of voltage, extending from deep reverse bias to well above the built-in potential. The present model enables to explain the unusual peak in $C$-$V$ characteristics of these devices, as observed experimentally by various groups. The results are further validated using self-consistent numerical simulation. Finally, we discuss the discrepancy and limitation of using Mott-Schottk…
Energetic disorder has been known for decades to limit the performance of structurally disordered semiconductors such as amorphous silicon and organic semiconductors. However, in the past years, high performance organic solar cells have emerged showing a continuously reduced amount of energetic disorder. While searching for future high efficiency material systems, it is therefore important to correctly characterize this energetic disorder. While there are several techniques in literature, the most common approaches to probe the density of defect states are using optical excitation as in extern…
Among the parameters determining the efficiency of an organic solar cell, the open-circuit voltage ($V_\text{OC}$) is the one with most room for improvement. Existing models for the description of $V_\text{OC}$ assume that photogenerated charge carriers are thermalized. Here, we demonstrate that quasi-equilibrium concepts cannot fully describe $V_\text{OC}$ of disordered organic devices. For two representative donor:acceptor blends it is shown that $V_\text{OC}$ is actually 0.1-0.2 V higher than it would be if the system was in thermodynamic equilibrium. Extensive numerical modeling reveals th…
Non-fullerene acceptors based on perylenediimides (PDIs) have garnered significant interest as an alternative to fullerene acceptors in organic photovoltaics (OPVs), but their charge transport phenomena are not well understood, especially in bulk heterojunctions (BHJs). Here, we investigate charge transport and current fluctuations by performing correlated low-frequency noise and impedance spectroscopy measurements on two BHJ OPV systems, one employing a fullerene acceptor and the other employing a dimeric PDI acceptor. In the dark, these measurements reveal that PDI-based OPVs have a greater …
For almost sixty years, solar energy for space applications has relied on inorganic photovoltaics, evolving from solar cells made of single crystalline silicon to triple junctions based on germanium and III-V alloys. The class of organic-based photovoltaics, which ranges from all-organic to hybrid perovskites, has the potential of becoming a disruptive technology in space applications, thanks to the unique combination of appealing intrinsic properties (e.g. record high specific power, tunable absorption window) and processing possibilities. Here, we report on the launch of the stratospheric mi…
Understanding the role that exciton diffusion plays in organic solar cells is a crucial to understanding the recent rise in power conversion effciencies brought about by non-fullerene acceptors (NFA). Established methods for measuring exciton diffusion lengths in organic solar cells require specialized equipment designed for measuring high-resolution time-resolved photoluminescence (TRPL). Here we introduce a technique, coined pulsed-PLQY, to measure the diffusion length of organic solar cells without any temporal measurements. Using a Monte-Carlo model we simulate the dynamics within a thin f…
The performance of organic solar cells strongly depends on the bulk heterojunction (BHJ) morphology of the photoactive layer. This BHJ forms during the drying of the wet-deposited solution, because of physical processes such as crystallization and/or liquid liquid phase separation (LLPS). However, the process-structure relationship remains insufficiently understood. In this work, a recently developed, coupled phase field fluid mechanics framework is used to simulate the BHJ formation upon drying. For the first time, this allows to investigate the interplay between all the relevant physical pro…
Kinetic Monte Carlo (KMC) simulations are a powerful tool to study the dynamics of charge carriers in organic photovoltaics. However, the key characteristic of any photovoltaic device, its current-voltage ($J$-$V$) curve under solar illumination, has proven challenging to simulate using KMC. The main challenges arise from the presence of injecting contacts and the importance of charge recombination when the internal electric field is low, i.e., close to open-circuit conditions. In this work, an experimentally calibrated KMC model is presented that can fully predict the $J$-$V$ curve of a disor…
We investigate nongeminate recombination in organic solar cells based on copper phthalocyanine (CuPc) and C$_{60}$. Two device architectures, the planar heterojunction (PHJ) and the bulk heterojunction (BHJ), are directly compared in view of differences in charge carrier decay dynamics. We apply a combination of transient photovoltage (TPV) experiments, yielding the small perturbation charge carrier lifetime, and charge extraction measurements, providing the charge carrier density. In organic solar cells, charge photogeneration and recombination primarily occur at the donor--acceptor heteroint…
Hybrid conjugated polymer/fullerene filaments based on MEH-PPV/PVP/PCBM are prepared by electrospinning, and their properties assessed by scanning electron, atomic and lateral force, tunnelling, and confocal microscopy, as well as by attenuated total reflection Fourier transform-infrared spectroscopy, photoluminescence quantum yield and spatially-resolved fluorescence. Highlighted features include ribbon-shape of the realized fibers, and the persistence of a network serving as a template for heterogeneous active layers in solar cell devices. A set of favorable characteristics is evidenced in t…
We have demonstrated a high-performance low temperature solution processed electron selective contact consisting of 10 at% antimony doped tin oxide (ATO) and the neutral polymer polyethylenimine (PEI). Inverted organic photovoltaics (OPVs) utilizing ATO/PEI as electron selective contact exhibited high power conversion efficiencies for both the reference P3HT: PCBM and the non-fullerene based P3HT- IDTBR active layer OPV material systems. Importantly it is shown that the proposed ATO/PEI carrier selective contact provides light soaking-free inverted OPVs. Furthermore, by increasing the thicknes…
Despite many advances towards improving the stability of organic photovoltaic devices, environmental degradation under ambient conditions remains a challenging obstacle for future application. Particularly conventional systems employing fullerene derivatives are prone to oxidise under illumination, limiting their applicability. Herein, we report on the environmental stability of the small molecule donor DRCN5T together with the fullerene acceptor PC70BM. We find that this system exhibits exceptional device stability, mainly due to almost constant short-circuit current. By employing ultrafast f…
Ternary organic solar cells (TOSC) are currently under intensive investigation, recently reaching a record efficiency of 17.1%. The origin of the device open-circuit voltage (VOC), already a multifaceted issue in binary OSC, is even more complex in TOSCs. Herein, we investigate two ternary systems with one donor (D) and two acceptor materials (A1, A2) including fullerene and non-fullerene acceptors. By varying the ratio between the two acceptors, we find the VOC to be gradually tuned between those of the two binary systems, D:A1 and D:A2. To investigate the origin of this change, we employ ult…
The paper proposes a model of an organic solar cell based on Tamm plasmon polariton localized at the boundary of the active layer doped with plasmon nanoparticles and a multilayer mirror. It is shown that the integral absorption in the active layer can be increased by 10% compared to the optimized planar solar cell.
Bulk-heterojunction (BHJ) non-fullerene organic solar cells prepared from sequentially deposited donor and acceptor layers (sq-BHJ) have recently been promising to be highly efficient, environmentally friendly, and compatible with large area and roll-to-toll fabrication. However, the related photophysics at donor-acceptor interface and the vertical heterogeneity of donor-acceptor distribution, critical for exciton dissociation and device performance, are largely unexplored. Herein, steady-state and time-resolved optical and electrical techniques are employed to characterize the interfacial tra…
Space charge effects can significantly degrade charge collection in organic photovoltaics (OPVs), especially in thick-film devices. The two main causes of space charge are doping and imbalanced transport. Although these are completely different phenomena, they lead to the same voltage dependence of the photocurrent, making them difficult to distinguish. In this work, a method is introduced how the build-up of space charge due to imbalanced transport can be monitored in a real operating organic solar cell. The method is based on the reconstruction of quantum efficiency spectra and requires only…
In organic solar cells, photogenerated singlet excitons form charge transfer (CT) complexes, which subsequently split into free charge carriers. Here, we consider the contributions of excess energy and molecular quadrupole moments to the charge separation process. We investigate charge photogeneration in two separate bulk heterojunction systems consisting of the polymer donor PTB7-Th and two non-fullerene acceptors, ITIC and h-ITIC. CT state dissociation in these donor-acceptor systems is monitored by charge density decay dynamics obtained from transient absorption experiments. We study the el…
Organic solar cells (OSCs) have recently shown a rapid improvement in their performance, bringing power conversion efficiencies (PCEs) closer to the point where commercial applications of the technology become viable. However, the low open-circuit voltage (Voc) of OSCs relative to their optical gap still limits PCEs to below 20%. A key factor contributing to the large Voc deficit in OSCs is non-radiative recombination to spin-triplet excitons, which is widely, but not universally, observed in blends using both fullerene and non-fullerene electron acceptors. Here, we present an experimental fra…
Non-fullerene acceptor (NFA)-based ternary bulk heterojunction solar cells (TSC) are the most efficient organic solar cells (OSCs) today due to their broader absorption and quantum efficiencies (QE) often surpassing those of corresponding binary blends. We study how the energetics driving charge transfer at the electron donor:electron acceptor (D/A) interfaces impact the QE in blends of PBDB-T-2F donor with several pairs of lower bandgap NFAs. As in binary blends, the ionization energy offset between donor and acceptor (ΔIE) controls the QE and maximizes for ΔIE > 0.5 eV. However, ΔIE is not c…
Driven by the rapid development of non-fullerene electron acceptors (NFAs), the power conversion efficiencies of organic solar cells (OSCs) have reached levels suitable for commercial applications. However, the poor operational stability of high-performance NFA OSCs is a remaining fundamental challenge that must be addressed. Whilst previous studies have primarily focused on the NFA component, we consider here the degradation pathways of both the donor and acceptor materials in the benchmark PM6:Y6 blend. Here, we show that light soaking greatly increases the energetic disorder and trap state …
Non-radiative losses to the open-circuit voltage are a primary factor in limiting the power conversion efficiency of organic photovoltaic devices. The dominant non-radiative loss is intrinsic to the active layer and can be determined from the quasi-Fermi level splitting (QFLS) and the radiative thermodynamic limit of the photovoltage. Quantification of the QFLS in thin film devices with low mobility is challenging due to the excitonic nature of photoexcitation and additional sources of nonradiative loss associated with the device structure. This work outlines an experimental approach based on …
Transparent electronics offer exciting light harvesting solutions for generation of electrical power via demonstration of "see-through" optoelectronic devices. The wireless energy harvesting ability can empower unplugged and battery-free operations for Internet of Things (IoT) devices. In this study, we report a transparent, luminescent, and elastomeric optical waveguide incorporating quantum dots that is in-situ coupled with organic solar cell array made of P3HT:PC61BM bulk heterojunction. CdSe@ZnS QDs have a photoluminescence quantum yield (PLQY) of 91% and are synthetically engineered to ma…
Organic solar cells (OSCs) have received a special attention over the past years due to their solution processability, low cost, flexibility and capability of role-to-role production. The power conversion efficiency of these devices has been significantly increased over the past decades from 1% in 1986 to 5% in 2005 and to up to 13% in 2017 thanks to the molecular optimization and the use of non-fullerene acceptors in their active materials. Despite such interesting efficiency, their applications remain limited so far because of instability and short life time of their active layers. It is exp…
Suppressing charge recombination is key for organic solar cells to become commercial reality. However, there is still no conclusive picture of how recombination losses are influenced by the complex nanoscale morphology. Here, new insight is provided by revisiting the P3HT:PCBM blend, which is still one of the best performers regarding reduced recombination. By changing small details in the annealing procedure, two model morphologies were prepared that vary in phase separation, molecular order and phase purity, as revealed by electron tomography and optical spectroscopy. Both systems behave ver…
Polymer solar cells are considered as very promising candidates for development of photovoltaics of the future. They are cheap and easy to fabricate, however, up to now, they possess fundamental drawback, low effectiveness. In the most popular BHJ (bulk heterojunction) architecture the actual record of efficiency is about 13 percent. One ask the question how fundamental this limitation is. In our paper we propose the simple model which examines the limitations of efficiency by analysis of geometrical aspects of the BHJ architecture. In this paper we considered two dimensional model. We calcula…
Parameter estimation procedures provide valuable guidance in the understanding and improvement of organic solar cells and other devices. They often rely on one-dimensional models, but in the case of bulk-heterojunction (BHJ) designs, it is not straightforward that these models' parameters have a consistent physical interpretation. Indeed, contrarily to two- or three-dimensional models, the BHJ morphology is not explicitly described in one-dimensional models and must be implicitly expressed through effective parameters. In order to inform experimental decisions, a helpful parameter estimation m…
The power conversion efficiencies (PCEs) of organic solar cells (OSCs) using non-fullerene acceptors (NFAs) have now reached 18%. However, this is still lower than inorganic solar cells, for which PCEs >20% are commonplace. A key reason is that OSCs still show low open-circuit voltages (Voc) relative to their optical band gaps, attributed to non-radiative recombination. For OSCs to compete with inorganics in efficiency, all non-radiative loss pathways must be identified and where possible, removed. Here, we show that in most NFA OSCs, the majority of charge recombination at open-circuit procee…
The ideal band gap for a photovoltaic active layer for the solar spectrum is around 1.3 eV. However oxides with such values are rare. One of the most studied oxides to date as a photovoltaic active layer is the cuprous oxide Cu2O. Its band gap is around 2.1 eV and is therefore not ideal for the solar spectrum. Power Conversion Efficiency generally do not exceed 4%. In this paper we propose to study an emerging type of solar cell that is based on ferroelectricity. In this type of solar cell, a p-n junction is not necessarily required, unlike conventional solar cells. Interesting conversion effi…
We study the radiative decay, or fluorescence, of excitons in organic solar cells as a function of its geometrical parameters. Contrary to their non-radiative counterpart, fluorescence losses strongly depend on the environment. By properly tuning the thicknesses of the buffer layers between the active regions of the cell and the electrodes, the exciton lifetime and, hence, the exciton diffusion length can be increased. The importance of this phenomenon depends on the radiative quantum efficiency, which is the fraction of the exciton decay that is intrinsically due to fluorescence. Besides this…
The energetic landscape of charge transfer (CT) states at the interface of electron donating and electron accepting domains in organic optoelectronic devices is crucial for their performance. Central questions -- such as the role of static energetic disorder and vibrational effects -- are under ongoing dispute. This study provides an in-depth analysis of temperature dependent broadening of the spectroscopic absorption and emission features of CT states in devices with small molecule-fullerene blends. We confirm the validity of the electro-optical reciprocity relation between the photovoltaic e…
Organic solar cells (OSCs) based on non-fullerene acceptors can show high charge generation yields despite near-zero donor-acceptor energy offsets to drive charge separation and overcome the mutual Coulomb attraction between electron and hole. Here we use time-resolved optical spectroscopy to show that free charges in these systems are generated by thermally activated dissociation of interfacial charge-transfer excitons (CTEs) that occurs over hundreds of picoseconds at room temperature, three orders of magnitude slower than comparable fullerene-based systems. Upon free electron-hole encounter…
Low temperature solution combustion synthesis emerges as a facile method for synthesis of functional metal oxides thin films for electronic applications. We study the solution combustion synthesis process of Cu:NiOx using different molar ratios (w/o, 0.1 and 1.5) of fuel acetylacetone (Acac) to oxidizer (Cu, Ni Nitrates) as a function of thermal annealing tempera-tures 150, 200 and 300 oC. The solution combustion synthesis process, in both thin films and bulk Cu:NiOx, is investigated. Thermal analysis studies using TGA and DTA reveal that the Cu:NiOx thin films show a more gradual mass loss wh…
State of the art organic solar cells exhibit power conversion efficiencies of 18 % and above. These devices benefit from the suppression of free charge recombination with regard to the Langevin-limit of charge encounter in a homogeneous medium. It has been recognized that the main cause of suppressed free charge recombination is the reformation and resplitting of charge transfer states at the interface between donor and acceptor domains. Here, we use kinetic Monte Carlo simulations to understand the interplay between free charge motion and recombination in an energetically-disordered phase-sep…
In this article we address the theoretical study of a multiscale drift-diffusion (DD) model for the description of photoconversion mechanisms in organic solar cells. The multiscale nature of the formulation is based on the co-presence of light absorption, conversion and diffusion phenomena that occur in the three-dimensional material bulk, of charge photoconversion phenomena that occur at the two-dimensional material interface separating acceptor and donor material phases, and of charge separation and subsequent charge transport in each three-dimensional material phase to device terminals that…
Low-gap conjugated polymers have enabled an impressive increase in the efficiencies of organic solar cells, primarily due to their red absorption which allows harvesting of that part of the solar spectrum. Here, we report that the true optical gap of one prototypical material, PTB7, is in fact at significantly higher energy than has previously been reported, indicating that the red absorption utilized in these materials in solar cells is entirely due to chain aggregation. Using single-molecule spectroscopy we find that PL from isolated nanoscale aggregates consists of multiple independently em…
The outstanding performance of organic-inorganic metal trihalide solar cells benefits from the exceptional photo-physical properties of both electrons and holes in the material. Here, we directly probe the free-carrier dynamics in Cs-doped FAPbI3 thin films by spatiotemporal photoconductivity imaging. Using charge transport layers to selectively quench one type of carriers, we show that the two relaxation times on the order of 1 microsecond and 10 microseconds correspond to the lifetimes of electrons and holes in FACsPbI3, respectively. Strikingly, the diffusion mapping indicates that the diff…
Polymer solar cells are considered as very promising candidates for development of photovoltaics of the future. They are cheap and easy to fabricate. However, up to now, they possess fundamental drawback: low effectiveness. In the most popular BHJ (bulk heterojunction) architecture the actual long-standing top efficiency is about 12\% (recent achievements about 15\%). One ask the question how fundamental this limitation is, as certain theoretical considerations suggest that it should be about two times higher. In our paper we analyze the `geometric factor' as one of possible explanation of rel…